WO2019220114A1 - Matériaux catalytiques destinés au traitement d'eaux usées - Google Patents

Matériaux catalytiques destinés au traitement d'eaux usées Download PDF

Info

Publication number
WO2019220114A1
WO2019220114A1 PCT/GB2019/051335 GB2019051335W WO2019220114A1 WO 2019220114 A1 WO2019220114 A1 WO 2019220114A1 GB 2019051335 W GB2019051335 W GB 2019051335W WO 2019220114 A1 WO2019220114 A1 WO 2019220114A1
Authority
WO
WIPO (PCT)
Prior art keywords
catalytic material
catalyst
organic compound
waste stream
metal
Prior art date
Application number
PCT/GB2019/051335
Other languages
English (en)
Inventor
Daniel MALKO
Anthony R. J. KUCERNAK
Javier Rubio-Garcia
Original Assignee
Imperial College Of Science, Technology And Medicine
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Imperial College Of Science, Technology And Medicine filed Critical Imperial College Of Science, Technology And Medicine
Priority to EP19726085.4A priority Critical patent/EP3793951A1/fr
Publication of WO2019220114A1 publication Critical patent/WO2019220114A1/fr

Abstract

La présente invention concerne des matériaux catalytiques et des procédés de traitement d'un flux d'eaux usées à l'aide des matériaux catalytiques. En particulier, la présente invention concerne des matériaux et des procédés servant à réduire les contaminants organiques dans des flux d'eaux usées. L'invention concerne un procédé de traitement d'un flux de déchets comprenant les étapes consistant à : fournir un matériau catalytique ; fournir un flux de déchets comprenant un composé organique qui est un liquide ou dissous dans un solvant, et mettre en contact le matériau catalytique avec le flux de déchets ; fournir de l'oxygène au flux de déchets ; et oxyder le composé organique à la surface du matériau catalytique avec une réduction simultanée de l'oxygène. L'invention concerne également de nouveaux matériaux catalytiques et des procédés de préparation des matériaux catalytiques et des dispositifs qui comprennent les matériaux catalytiques.
PCT/GB2019/051335 2018-05-15 2019-05-15 Matériaux catalytiques destinés au traitement d'eaux usées WO2019220114A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP19726085.4A EP3793951A1 (fr) 2018-05-15 2019-05-15 Matériaux catalytiques destinés au traitement d'eaux usées

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GBGB1807860.0A GB201807860D0 (en) 2018-05-15 2018-05-15 Catalytic material for wastewater treatment
GB1807860.0 2018-05-15

Publications (1)

Publication Number Publication Date
WO2019220114A1 true WO2019220114A1 (fr) 2019-11-21

Family

ID=62623410

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2019/051335 WO2019220114A1 (fr) 2018-05-15 2019-05-15 Matériaux catalytiques destinés au traitement d'eaux usées

Country Status (3)

Country Link
EP (1) EP3793951A1 (fr)
GB (1) GB201807860D0 (fr)
WO (1) WO2019220114A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110898825A (zh) * 2019-12-13 2020-03-24 南京农业大学 一种重金属超富集生物质炭催化剂及其制备方法与应用
WO2022101629A1 (fr) * 2020-11-13 2022-05-19 Sweetgen Ltd Traitement de liquide catalytique à l'aide d'un aldéhyde
CN117401958A (zh) * 2023-10-16 2024-01-16 舒兰市鑫源建筑工程有限公司 一种日用陶瓷及其制备方法与应用

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112916027A (zh) * 2019-12-06 2021-06-08 四川大学 一种酵母生物质制备磷化铁/碳复合材料的方法
CN115722219B (zh) * 2022-11-14 2024-05-28 浙江工业大学 一种颗粒炭材料负载金催化剂及其制备方法和在乙炔氢氯化制氯乙烯反应中的应用

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5389325A (en) 1993-09-24 1995-02-14 Corning Incorporated Activated carbon bodies having phenolic resin binder
EP0913193A2 (fr) * 1997-10-21 1999-05-06 Karsten Pedersen Catalysateur, procédé et dispositif pour la destruction de composés nocifs contenus dans l'eau
WO2004101442A1 (fr) * 2003-05-19 2004-11-25 Ntu Ventures Private Limited Procede et systeme de degradation de composes halogenes
EP1484285A1 (fr) * 2002-03-11 2004-12-08 Nippon Shokubai Co., Ltd. Procede de traitement des eaux usees
WO2015049318A1 (fr) 2013-10-01 2015-04-09 Imperial Innovations Limited Catalyseurs de réduction d'oxygène
WO2017049375A1 (fr) 2015-09-25 2017-03-30 Cylzer S.A. Anneau de mélange pour dissoudre une partie de soluté dans une partie de solvant, système et procédé pour dissoudre une partie de soluté dans une partie de solvant
WO2017093754A1 (fr) * 2015-12-02 2017-06-08 Imperial Innovations Limited Pile à combustible destinée au traitement d'eaux usées

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5389325A (en) 1993-09-24 1995-02-14 Corning Incorporated Activated carbon bodies having phenolic resin binder
EP0913193A2 (fr) * 1997-10-21 1999-05-06 Karsten Pedersen Catalysateur, procédé et dispositif pour la destruction de composés nocifs contenus dans l'eau
EP1484285A1 (fr) * 2002-03-11 2004-12-08 Nippon Shokubai Co., Ltd. Procede de traitement des eaux usees
WO2004101442A1 (fr) * 2003-05-19 2004-11-25 Ntu Ventures Private Limited Procede et systeme de degradation de composes halogenes
WO2015049318A1 (fr) 2013-10-01 2015-04-09 Imperial Innovations Limited Catalyseurs de réduction d'oxygène
WO2017049375A1 (fr) 2015-09-25 2017-03-30 Cylzer S.A. Anneau de mélange pour dissoudre une partie de soluté dans une partie de solvant, système et procédé pour dissoudre une partie de soluté dans une partie de solvant
WO2017093754A1 (fr) * 2015-12-02 2017-06-08 Imperial Innovations Limited Pile à combustible destinée au traitement d'eaux usées

Non-Patent Citations (5)

* Cited by examiner, † Cited by third party
Title
J. HYDROGEN ENERGY, vol. 36, 2011, pages 15731 - 15738
J. PHYS. CHEM., vol. 97, 1993, pages 12020 - 12029
MALKO, D.KUCERNAK, A.LOPES, T., NATURE COMMUNICATIONS, vol. 7, 2016, pages 13285
MALKO, D.LOPES, T.SYMIANAKIS, E.KUCERNAK, A. R., J. MATER. CHEM. A, vol. 4, 2015, pages 142 - 152
PARK JIN-YOUNG ET AL: "Enhanced oxygen reduction reaction of Pt deposited Fe/N-doped bimodal porous carbon nanostructure catalysts", JOURNAL OF CATALYSIS, ACADEMIC PRESS, DULUTH, MN, US, vol. 359, 3 February 2018 (2018-02-03), pages 46 - 54, XP085348887, ISSN: 0021-9517, DOI: 10.1016/J.JCAT.2017.12.033 *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110898825A (zh) * 2019-12-13 2020-03-24 南京农业大学 一种重金属超富集生物质炭催化剂及其制备方法与应用
WO2022101629A1 (fr) * 2020-11-13 2022-05-19 Sweetgen Ltd Traitement de liquide catalytique à l'aide d'un aldéhyde
CN117401958A (zh) * 2023-10-16 2024-01-16 舒兰市鑫源建筑工程有限公司 一种日用陶瓷及其制备方法与应用

Also Published As

Publication number Publication date
GB201807860D0 (en) 2018-06-27
EP3793951A1 (fr) 2021-03-24

Similar Documents

Publication Publication Date Title
WO2019220114A1 (fr) Matériaux catalytiques destinés au traitement d'eaux usées
Wang et al. Surface strategies for catalytic CO 2 reduction: from two-dimensional materials to nanoclusters to single atoms
JP6517316B2 (ja) 炭素担持触媒を生成するための方法
US20180354819A1 (en) Fuel Cell For Wastewater Treatment
Cui et al. PtRu catalysts supported on heteropolyacid and chitosan functionalized carbon nanotubes for methanol oxidation reaction of fuel cells
KR101797782B1 (ko) 연료 전지를 위한 금속 산화물 도핑을 갖는 촉매
EP1758678B1 (fr) Procede de preparation de catalyseurs de platine obtenus par reduction de dioxyde de platine forme in-situ
Luksirikul et al. Electron promotion by surface functional groups of single wall carbon nanotubes to overlying metal particles in a fuel‐cell catalyst
US8372781B2 (en) Carbon catalyst and use thereof
KR100688428B1 (ko) 금속 나노입자가 분산된 콜로이드를 이용한 촉매물질 및 연료전지 전극재료 제조 방법
KR20170100581A (ko) 개질제를 포함하는 탄소 지지형 촉매 및 이의 제조 방법
JP5665743B2 (ja) 触媒の連続的な製造方法
CN1966144A (zh) 一种由胶体溶液制备负载型纳米Pd/C催化剂的方法
Silva et al. The effect of antimony-tin and indium-tin oxide supports on the catalytic activity of Pt nanoparticles for ammonia electro-oxidation
Ye et al. Catalytic oxidation of hydroquinone in aqueous solution over bimetallic PdCo catalyst supported on carbon: effect of interferents and electrochemical measurement
CN108970608A (zh) 具有包覆结构的负载型贵金属催化剂及其制备方法和在Cu(II)液相催化还原中的应用
US20030100443A1 (en) Oxidation-insensitive polymer-stabilized noble metal colloids
CN117352760B (zh) 多级孔、氮掺杂、石墨化炭负载铂基催化剂的制备方法
Moreira et al. Rhodium effects on Pt anode materials in a direct alkaline ethanol fuel cell
WO2008009742A1 (fr) Catalyseurs anodiques constitués de métaux nobles spontanément déposés sur des catalyseurs nanostructurés composés de métaux de transition, leur synthèse et leur utilisation dans des piles à combustible
CN114345324A (zh) 生物质碳基金属单原子复合催化剂、制备方法及其应用
Pech-Rodríguez et al. Cost-effective functionalization of Vulcan XC-72 by using the intermittent microwave heating process as nanocatalyst support for ethanol electrooxidation in acid media
CN111204848B (zh) 一种导电基底负载金属的非均匀阴极电还原去除污染物的方法
RU2446009C1 (ru) Способ приготовления платино-рутениевых электрокатализаторов
JP5142258B2 (ja) 炭素担持貴金属ナノ粒子触媒の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19726085

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2019726085

Country of ref document: EP

Effective date: 20201215