WO2019125490A1 - Encre de catalyseur contenant un alcool en c5-c10 ou un acide carboxylique, et procédé de fabrication de mea - Google Patents

Encre de catalyseur contenant un alcool en c5-c10 ou un acide carboxylique, et procédé de fabrication de mea Download PDF

Info

Publication number
WO2019125490A1
WO2019125490A1 PCT/US2017/068252 US2017068252W WO2019125490A1 WO 2019125490 A1 WO2019125490 A1 WO 2019125490A1 US 2017068252 W US2017068252 W US 2017068252W WO 2019125490 A1 WO2019125490 A1 WO 2019125490A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
aqueous mixture
ionomer
optionally
substrate
Prior art date
Application number
PCT/US2017/068252
Other languages
English (en)
Inventor
Mark EDMUNDSON
F. Colin Busby
Original Assignee
W. L. Gore & Associates, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by W. L. Gore & Associates, Inc. filed Critical W. L. Gore & Associates, Inc.
Priority to KR1020217031979A priority Critical patent/KR102463959B1/ko
Priority to CA3045521A priority patent/CA3045521C/fr
Priority to KR1020197021676A priority patent/KR102311777B1/ko
Priority to JP2019534221A priority patent/JP7102412B2/ja
Priority to PCT/US2017/068252 priority patent/WO2019125490A1/fr
Priority to US16/092,440 priority patent/US11251453B2/en
Priority to CN201780082861.0A priority patent/CN110521039B/zh
Priority to EP17832665.8A priority patent/EP3673528A1/fr
Publication of WO2019125490A1 publication Critical patent/WO2019125490A1/fr

Abstract

L'invention concerne des procédés et des compositions pour fabriquer des composants de pile à combustible Dans un mode de réalisation, le procédé comprend la fourniture d'un substrat, et la formation ou l'adhésion d'une électrode sur le substrat, la formation comprenant le dépôt d'un mélange aqueux en tant qu'encre de catalyseur comprenant de l'eau, un composant insoluble dans l'eau, un catalyseur et un ionomère. Le composant insoluble dans l'eau comprend un alcool en C5-C10 insoluble dans l'eau, un acide carboxylique insoluble dans l'eau en C5-C10, ou une combinaison de ceux-ci. L'utilisation de tels composants insolubles dans l'eau permet d'obtenir un milieu liquide stable présentant une réticulation réduite lors du séchage, une dissolution réduite du substrat et une pénétration réduite des pores du substrat.
PCT/US2017/068252 2016-12-23 2017-12-22 Encre de catalyseur contenant un alcool en c5-c10 ou un acide carboxylique, et procédé de fabrication de mea WO2019125490A1 (fr)

Priority Applications (8)

Application Number Priority Date Filing Date Title
KR1020217031979A KR102463959B1 (ko) 2017-12-22 2017-12-22 C5-c10 알코올 또는 카르복실산을 함유하는 촉매 잉크 및 mea 제조 방법
CA3045521A CA3045521C (fr) 2016-12-23 2017-12-22 Procede de fabrication d'un dispositif d'electrode a membrane
KR1020197021676A KR102311777B1 (ko) 2017-12-22 2017-12-22 C5-c10 알코올 또는 카르복실산을 함유하는 촉매 잉크 및 mea 제조 방법
JP2019534221A JP7102412B2 (ja) 2017-12-22 2017-12-22 膜電極接合体の製造方法
PCT/US2017/068252 WO2019125490A1 (fr) 2017-12-22 2017-12-22 Encre de catalyseur contenant un alcool en c5-c10 ou un acide carboxylique, et procédé de fabrication de mea
US16/092,440 US11251453B2 (en) 2016-12-23 2017-12-22 Membrane electrode assembly manufacturing process
CN201780082861.0A CN110521039B (zh) 2017-12-22 2017-12-22 含c5-c10醇或羧酸的催化剂油墨以及膜电极组件制造方法
EP17832665.8A EP3673528A1 (fr) 2017-12-22 2017-12-22 Encre de catalyseur contenant un alcool en c5-c10 ou un acide carboxylique, et procédé de fabrication de mea

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2017/068252 WO2019125490A1 (fr) 2017-12-22 2017-12-22 Encre de catalyseur contenant un alcool en c5-c10 ou un acide carboxylique, et procédé de fabrication de mea

Publications (1)

Publication Number Publication Date
WO2019125490A1 true WO2019125490A1 (fr) 2019-06-27

Family

ID=61007820

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2017/068252 WO2019125490A1 (fr) 2016-12-23 2017-12-22 Encre de catalyseur contenant un alcool en c5-c10 ou un acide carboxylique, et procédé de fabrication de mea

Country Status (5)

Country Link
EP (1) EP3673528A1 (fr)
JP (1) JP7102412B2 (fr)
KR (2) KR102311777B1 (fr)
CN (1) CN110521039B (fr)
WO (1) WO2019125490A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7131524B2 (ja) * 2019-10-18 2022-09-06 トヨタ自動車株式会社 膜電極ガス拡散層接合体の製造方法

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3953566A (en) 1970-05-21 1976-04-27 W. L. Gore & Associates, Inc. Process for producing porous products
USRE37307E1 (en) 1994-11-14 2001-08-07 W. L. Gore & Associates, Inc. Ultra-thin integral composite membrane
US20050067345A1 (en) * 2002-02-26 2005-03-31 Prugh David Neville Production of catalyst coated membranes
US20060229194A1 (en) * 2000-08-04 2006-10-12 Makoto Uchida Method for manufacturing polymer electrolyte fuel cell
US7306729B2 (en) 2005-07-18 2007-12-11 Gore Enterprise Holdings, Inc. Porous PTFE materials and articles produced therefrom
US20110166009A1 (en) * 2005-03-30 2011-07-07 Umicore Ag & Co. Kg Ink For Producing Catalyst Layers
US20130040222A1 (en) * 2011-08-11 2013-02-14 Samsung Sdi Co., Ltd. Catalyst layer composition for fuel cell, electrode for fuel cell, method of preparing electrode for fuel cell, membrane-electrode assembly for fuel cell, and fuel cell system using the membrane-electrode assembly
US20130202986A1 (en) * 2008-01-11 2013-08-08 GM Global Technology Operations LLC Reinforced electrode assembly
US20160126560A1 (en) 2013-05-10 2016-05-05 W.L. Gore & Associates, Co. Ltd. Fuel cell electrode catalyst and method for activating catalyst
US20160233532A1 (en) 2015-02-09 2016-08-11 W. L. Gore & Associates, Inc. Membrane Electrode Assembly Manufacturing Process

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8652705B2 (en) * 2005-09-26 2014-02-18 W.L. Gore & Associates, Inc. Solid polymer electrolyte and process for making same
EP2475034B1 (fr) * 2010-12-23 2020-11-25 Greenerity GmbH Ensembles électrode-membrane pour piles à combustible pem

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3953566A (en) 1970-05-21 1976-04-27 W. L. Gore & Associates, Inc. Process for producing porous products
USRE37307E1 (en) 1994-11-14 2001-08-07 W. L. Gore & Associates, Inc. Ultra-thin integral composite membrane
US20060229194A1 (en) * 2000-08-04 2006-10-12 Makoto Uchida Method for manufacturing polymer electrolyte fuel cell
US20050067345A1 (en) * 2002-02-26 2005-03-31 Prugh David Neville Production of catalyst coated membranes
US20110166009A1 (en) * 2005-03-30 2011-07-07 Umicore Ag & Co. Kg Ink For Producing Catalyst Layers
US7306729B2 (en) 2005-07-18 2007-12-11 Gore Enterprise Holdings, Inc. Porous PTFE materials and articles produced therefrom
US20130202986A1 (en) * 2008-01-11 2013-08-08 GM Global Technology Operations LLC Reinforced electrode assembly
US20130040222A1 (en) * 2011-08-11 2013-02-14 Samsung Sdi Co., Ltd. Catalyst layer composition for fuel cell, electrode for fuel cell, method of preparing electrode for fuel cell, membrane-electrode assembly for fuel cell, and fuel cell system using the membrane-electrode assembly
US20160126560A1 (en) 2013-05-10 2016-05-05 W.L. Gore & Associates, Co. Ltd. Fuel cell electrode catalyst and method for activating catalyst
US20160233532A1 (en) 2015-02-09 2016-08-11 W. L. Gore & Associates, Inc. Membrane Electrode Assembly Manufacturing Process
WO2016130529A1 (fr) * 2015-02-09 2016-08-18 W. L. Gore & Associates, Inc. Procédé de fabrication d'ensemble électrode-membrane

Also Published As

Publication number Publication date
CN110521039A (zh) 2019-11-29
JP7102412B2 (ja) 2022-07-19
KR102311777B1 (ko) 2021-10-13
CN110521039B (zh) 2022-11-18
KR20210125607A (ko) 2021-10-18
EP3673528A1 (fr) 2020-07-01
JP2020514965A (ja) 2020-05-21
KR102463959B1 (ko) 2022-11-04
KR20190128046A (ko) 2019-11-14

Similar Documents

Publication Publication Date Title
US11251453B2 (en) Membrane electrode assembly manufacturing process
CA2983076C (fr) Procede de fabrication d'ensemble electrode-membrane
US8586264B2 (en) Gas diffusion electrode material and production method thereof
US9722269B2 (en) Reinforced electrode assembly
US20110262828A1 (en) Electrode catalyst dispersion and ink composition
US8142957B2 (en) Method for preparing a membrane electrode of a fuel cell
US20140315121A1 (en) Method for the preparation of catalyst-coated membranes method for the preparation of catalyst-coated membranes
KR102311777B1 (ko) C5-c10 알코올 또는 카르복실산을 함유하는 촉매 잉크 및 mea 제조 방법
CN104051745B (zh) 燃料电池部件的同时涂覆
US20220149408A1 (en) Membrane electrode assembly manufacturing process
CA3206074A1 (fr) Procede de fabrication d'un dispositif d'electrode a membrane
JP2007184140A (ja) 電解質膜−電極接合体の製造方法
JP5634013B2 (ja) 燃料電池用触媒層の製造方法、触媒層転写シート及び触媒層−電解質膜積層体
JP2010033897A (ja) 固体高分子形燃料電池用触媒層の製造方法及び触媒層−電解質膜積層体
JP4893704B2 (ja) 固体高分子形燃料電池用触媒層の製造方法及び触媒層−電解質膜積層体
JP2006294267A (ja) 燃料電池電極形成用触媒インク
JP2022543189A (ja) 触媒膜

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2017832665

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2017832665

Country of ref document: EP

Effective date: 20181009

ENP Entry into the national phase

Ref document number: 3045521

Country of ref document: CA

ENP Entry into the national phase

Ref document number: 2019534221

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20197021676

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE