WO2019117112A1 - 電極フィルムおよび電気化学測定システム - Google Patents
電極フィルムおよび電気化学測定システム Download PDFInfo
- Publication number
- WO2019117112A1 WO2019117112A1 PCT/JP2018/045394 JP2018045394W WO2019117112A1 WO 2019117112 A1 WO2019117112 A1 WO 2019117112A1 JP 2018045394 W JP2018045394 W JP 2018045394W WO 2019117112 A1 WO2019117112 A1 WO 2019117112A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- electrode film
- electrode
- functional layer
- conductive carbon
- Prior art date
Abstract
電極フィルムは、可撓性基材と、可撓性基材の厚み方向一方側に配置される機能層と、機能層の厚み方向一方側に配置され、sp2結合およびsp3結合を有する導電性カーボン層とを備える。
Description
本発明は、電極フィルム、および、電気化学測定システムに関する。
従来、電気化学反応を利用して、溶液中の微量なイオンや残留物質を定性分析または定量分析する電気化学測定法が知られている。電気化学測定法は、容器中の電位差を測定する方法や、電流を測定する方法などが挙げられる。
電気化学測定法に用いる電気化学測定システムは、一般的に、電極として、少なくとも作用電極および参照電極を備えており、作用電極で測定対象を検出する。この作用電極としては、白金、金、グラッシーカーボン、ボロンドープダイヤモンドなどが使用されている。しかし、白金などの貴金属は、希少であり、グラッシーカーボンは、成膜性に劣り電極として使用しにくく、また、ボロンドープダイヤモンドは、非常に高温で製造する必要がある。
そこで、近年、作用電極として、sp2結合およびsp3結合からなる微結晶ドメインから構成される炭素電極が検討されている(特許文献1参照。)。
特許文献1の炭素電極は、比較的低温で容易に製膜することができるため、高温処理が必要な生産設備を必要としない。また、電位窓が広いため、多種の物質を検出することができる。
ところで、特許文献1の炭素電極は、バッチ式などの製造方法によって、シリコン基板などの硬質基板の上に成膜されている。そのため、生産性に劣る。
そこで、生産性を向上するために、ロールトゥロール法を採用することが検討される。その際に、高分子フィルムなどの可撓性基材を用いることになる。しかしながら、可撓性基材上に、炭素電極を成膜すると、炭素電極の抵抗値が著しく向上する不具合が発生する。すなわち、炭素電極の導電性(低抵抗)などの電極として必要な特性が損なわれる。
本発明は、生産性に優れ、電極特性が良好な電極フィルムおよび電気化学測定システムを提供することにある。
本発明[1]は、可撓性基材と、前記可撓性基材の厚み方向一方側に配置される機能層と、前記機能層の厚み方向一方側に配置され、sp2結合およびsp3結合を有する導電性カーボン層とを備える、電極フィルムを含んでいる。
本発明[2]は、前記機能層が、ガスバリア層である、[1]に記載の電極フィルムを含んでいる。
本発明[3]は、前記機能層が、金属層である、[1]または[2]に記載の電極フィルムを含んでいる。
本発明[4]は、前記機能層の厚みが、5nm以上である、[1]~[3]のいずれか一項に記載の電極フィルムを含んでいる。
本発明[5]は、前記機能層内の厚み方向一方面に形成される酸化膜の厚みが、3nm未満である、[1]~[4]のいずれか一項に記載の電極フィルムを含んでいる。
本発明[6]は、前記可撓性基材が、高分子フィルムである、[1]~[5]のいずれか一項に記載の電極フィルムを含んでいる。
本発明[7]は、電気化学測定用の電極である、[1]~[6]のいずれか一項に記載の電極フィルムを含んでいる。
本発明[8]は、[7]に記載の電極フィルムを備える、電気化学測定システムを含んでいる。
本発明の電極フィルムによれば、基材として可撓性基材を使用しているので、ロールトゥロール工程で製造することができる。そのため、生産性に優れる。また、可撓性基材と導電性カーボン層との間に機能層を備えているため、可撓性基材が導電性カーボン層の成膜時に与える悪影響を抑制できる。そのため、導電性などの電極特性を良好にすることができる。
本発明の電気化学測定システムは、電極特性に優れる電極フィルムを備えるため、精度よく電気化学測定を実施することができる。
図1を参照して、本発明の電極フィルムの一実施形態を説明する。図1において、紙面上下方向は、上下方向(厚み方向、第1方向)であって、紙面上側が、上側(厚み方向一方側、第1方向一方側)、紙面下側が、下側(厚み方向他方側、第1方向他方側)である。また、紙面左右方向および奥行き方向は、上下方向に直交する面方向である。具体的には、各図の方向矢印に準拠する。
1.電極フィルム
電極フィルム1は、所定の厚みを有するフィルム形状(シート形状を含む)を有し、厚み方向と直交する所定方向(面方向)に延び、平坦な上面(厚み方向一方面)および平坦な下面(厚み方向他方面)を有する。
電極フィルム1は、所定の厚みを有するフィルム形状(シート形状を含む)を有し、厚み方向と直交する所定方向(面方向)に延び、平坦な上面(厚み方向一方面)および平坦な下面(厚み方向他方面)を有する。
具体的には、図1に示すように、電極フィルム1は、可撓性基材2と、可撓性基材2の上側(厚み方向一方側)に配置される機能層3と、機能層3の上側に配置される導電性カーボン層4とを備える。すなわち、電極フィルム1は、可撓性基材2と、機能層3と、導電性カーボン層4とをこの順に備える。好ましくは、電極フィルム1は、可撓性基材2、機能層3および導電性カーボン層4からなる。以下、各層を詳述する。
2.可撓性基材
可撓性基材2は、可撓性を有し、機能層3および導電性カーボン層4を支持する基材である。可撓性基材2は、電極フィルム1の最下層であって、フィルム形状を有する。可撓性基材2は、機能層3の下面と接触するように、機能層3の下面全面に配置されている。
可撓性基材2は、可撓性を有し、機能層3および導電性カーボン層4を支持する基材である。可撓性基材2は、電極フィルム1の最下層であって、フィルム形状を有する。可撓性基材2は、機能層3の下面と接触するように、機能層3の下面全面に配置されている。
可撓性基材2としては、例えば、高分子フィルム、薄型ガラスフィルムなどが挙げられる。高分子フィルムの材料として、例えば、ポリエステル樹脂(例えば、ポリエチレンテレフタレート、ポリエチレンナフタレート)、アセテート樹脂、ポリエーテルスルホン樹脂、ポリカーボネート樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリオレフィン樹脂(例えば、ポリシクロオレフィンポリマー)、(メタ)アクリル樹脂、ポリ塩化ビニル樹脂、ポリ塩化ビニリデン樹脂、ポリスチレン樹脂、ポリビニルアルコール樹脂、ポリアリレート樹脂、ポリフェニレンサルファイド樹脂などが挙げられる。好ましくは、ポリエステル樹脂、ポリカーボネート樹脂、ポリオレフィン樹脂が挙げられ、より好ましくは、ポリエステル樹脂が挙げられる。
可撓性基材2としては、耐熱性、機械的強度、可撓性などの観点から、好ましくは、ポリエステルフィルム、薄型ガラスフィルムが挙げられ、より好ましくは、ポリエステルフィルムが挙げられ、さらに好ましくは、ポリエチレンテレフタレートフィルムなどが挙げられる。
可撓性基材の厚みは、例えば、2μm以上、好ましくは、20μm以上であり、また、例えば、200μm以下、好ましくは、120μm以下、より好ましくは、100μm以下である。
3.機能層
機能層3は、可撓性基材2が導電性カーボン層4に与える悪影響を抑制する層である。機能層3は、フィルム形状を有する。機能層3は、可撓性基材2の上面に接触するように、可撓性基材2の上面全面に配置されている。より具体的には、機能層3は、可撓性基材2の上面および導電性カーボン層4の下面に接触するように、可撓性基材2と導電性カーボン層4との間に配置されている。
機能層3は、可撓性基材2が導電性カーボン層4に与える悪影響を抑制する層である。機能層3は、フィルム形状を有する。機能層3は、可撓性基材2の上面に接触するように、可撓性基材2の上面全面に配置されている。より具体的には、機能層3は、可撓性基材2の上面および導電性カーボン層4の下面に接触するように、可撓性基材2と導電性カーボン層4との間に配置されている。
機能層3としては、例えば、ガスバリア層、導電層、密着層、表面平滑層などが挙げられる。
ガスバリア層は、水や有機ガスの透過を遮断する層である。機能層3がガスバリア層である場合、導電性カーボン層4の形成時において、機能層3が、可撓性基材2から放出される不純物ガス(水、有機ガスなど)が導電性カーボン層4に取り込まれることを抑制することができる。そのため、導電性カーボン層4の不純物含有量の低減することができ、導電性カーボン層4本来の特性の低下を抑制することができる。
導電層は、導電性を有する層である。機能層3が導電層である場合、導電性カーボン層4の導電性を補助するため、電極フィルム1(導電性カーボン層4表面)の導電性を向上させることができる。導電層の表面抵抗値は、例えば、10kΩ/□以下である。表面抵抗値は、JIS K 7194に準じて、4端子法により測定することができる。
密着層は、導電性カーボン層4と可撓性基材2との密着性を向上させる層である。機能層3が密着層である場合、導電性カーボン層4の剥離・脱落を抑制することができ、電極フィルム1の耐久性を向上させることができる。
表面平滑層は、可撓性基材2の上面を平滑にする層である。機能層3が表面平滑層である場合、導電性カーボン層4の表面(上面および下面)を平滑にすることができるため、導電性カーボン層4の凹凸に起因するノイズを抑制することができる。
機能層3としては、好ましくは、少なくともガスバリア層であり、より好ましくは、ガスバリア層と導電層とを兼ねる層である。
具体的には、機能層3としては、例えば、無機物層、有機物層が挙げられる。ガスバリア層としては、好ましくは、無機物層が挙げられる。ガスバリア層は、有機物層と無機物層とを交互に複数積層する層であってもよい。導電層としては、好ましくは、導電性の無機物層が挙げられる。密着層としては、好ましくは、無機物層や、シランカップリング剤含有の有機物層が挙げられる。表面平滑層としては、好ましくは、薄膜の無機物層または有機物層が挙げられる。
無機物層としては、例えば、金属層、無機物化合物層などが挙げられる。
金属層は、例えば、チタン、クロム、タングステン、アルミニウム、銅、銀、シリコン、または、これらの合金から形成されている。好ましくは、金属層は、チタン層が挙げられる。
無機化合物層は、例えば、NaF、Na3AlF6、LiF、MgF2、CaF2、BaF2、BaF2、SiO2、LaF3、CeF、Al2O3、または、これらの混合物などから形成されている。
無機物層としては、好ましくは、金属層が挙げられる。機能層3が金属層である場合、ガスバリア層および導電層の両方の役割を担う。すなわち、導電性カーボン層4の形成時において、可撓性基材2から放出される不純物ガスを金属層が遮断して、導電性カーボン層4内の不純物ガスの取り込みを抑制することができ、その結果、導電性カーボン層4本来の特性(特に導電性)の低下を抑制することができる。また、金属層が導電層として導電性カーボン層4の導電性を補助する。これらの役割によって、電極フィルム1の導電性を顕著に向上させることができる。
機能層3が金属層である場合、その上面には、金属酸化層(酸化膜の一例)を有していてもよく、また、有していなくてもよい。好ましくは、金属酸化層を有していないか、厚さ3nm未満の金属酸化層を有する。すなわち、好ましくは、機能層3内の上面に形成される金属酸化層の厚みが、3nm未満であり、より好ましくは、1nm以下である。最も好ましくは、機能層3は、金属酸化層を有しない。
これにより、機能層3と導電性カーボン層4との密着性に優れ、電極使用時における導電性カーボン層4の剥離を抑制することができる。例えば、カーボン層形成時の真空度が低い場合や、可撓性基材2が水分などの脱ガス成分を含む場合には、金属層(機能層3)の上面に金属酸化層が形成されて、導電性カーボン層4に対する密着性を低下することがあるが、金属酸化層の厚みを上記範囲とすることにより、密着性を良好に維持することができる。
機能層3が無機物層である場合、その厚みは、例えば、2nm以上、好ましくは、3nm以上、より好ましくは、4nm以上、さらに好ましくは、7nm以上であり、また、例えば、700nm以下、好ましくは、100nm以下、より好ましくは、50nm以下、さらに好ましくは、30nm以下、とりわけ好ましくは、20nm以下である。無機物層の厚みを上記範囲とすることにより、ガスバリア性、密着性を向上させることができる。
有機物層は、例えば、アクリル樹脂、ウレタン樹脂、メラミン樹脂、アルキド樹脂、シロキサン樹脂、有機シラン縮合物などの樹脂組成物から形成されている。有機物層は、上記材料に加えて、無機粒子および有機粒子などの粒子を含有していてもよい。
機能層3が有機物層である場合、その厚みは、例えば、15nm以上、好ましくは、20nm以上であり、また、例えば、1500nm以下、好ましくは、1000nm以下、より好ましくは、800nm以下である。有機物層の厚みを上記範囲とすることにより、電極フィルム1の上面をより確実に平滑にすることができる。
機能層3の上面(厚み方向一方面)の表面粗さRa(算術平均粗さ)は、例えば、5.0nm以下、好ましくは、3.0nm以下、より好ましくは、2.0nm以下であり、また、例えば、0.1nm以上である。機能層3の上面の表面粗さを上記上限以下とすることにより、電極フィルム1の表面粗さを低減することができ、その結果、電極フィルム1を電気化学測定用の電極として用いた場合に、ノイズを抑制することができる。
表面粗さは、走査型プローブ顕微鏡(Digetal Instruments社製、「NanoscopeIV」)を用いて、機能層3の上面において、500nm角の範囲を観察することにより、測定することができる。
なお、機能層3は、無機物層または有機物層の単層から構成されていてもよく、無機物層の複層または有機物層の複層から構成されていてもよく、また、無機物層および有機物層の混合からなる複層であってもよい。
4.導電性カーボン層
導電性カーボン層4は、電極特性(電位窓の広さ、導電性など)を有し、電極としての役割を担う層である。
導電性カーボン層4は、電極特性(電位窓の広さ、導電性など)を有し、電極としての役割を担う層である。
導電性カーボン層4は、sp2結合およびsp3結合を有する炭素から形成されている。すなわち、導電性カーボン層4は、グラファイト型構造およびダイヤモンド構造を有する層である。これにより、導電性カーボン層4は、電位窓を広くしつつ、良好な導電性を備える。また、低温での成膜性に優れる。
sp3の、sp2に対する比率(sp3/sp2)は、例えば、0.05以上、好ましくは、 0.10以上であり、また、例えば、2.00以下、好ましくは、1.50以下である。
上記比率は、X線光電子分光分析装置(アルバック・ファイ社製、「Quantum2000」)を用いて、導電性カーボン層4の結合エネルギー(単位:eV、横軸)および強度(単位:CPS、縦軸)を測定し、測定グラフにおいて、sp3のピーク高さおよびsp2のピーク高さを算出することにより、得ることができる。測定条件は、実施例にて後述する。
導電性カーボン層4の厚みは、例えば、1nm以上、好ましくは、2nm以上、より好ましくは、5nm以上であり、また、例えば、500nm以下、好ましくは、100nm以下、より好ましくは、50nm以下である。
なお、導電性カーボン層4は、炭素以外にもその他の添加剤を含有していてもよい。また、導電性カーボン層は、構造、組成、添加剤濃度などが異なる複数の層から構成であってもよく、また、導電性カーボン層4は、構造、組成、添加剤濃度などが段階的に(グラデーション状に)変化する構成であってもよい。
5.電極フィルムの製造方法
電極フィルム1は、例えば、可撓性基材2を用意する工程、可撓性基材2に機能層3を設ける工程、および、機能層3に導電性カーボン層4を設ける工程により、製造される。
電極フィルム1は、例えば、可撓性基材2を用意する工程、可撓性基材2に機能層3を設ける工程、および、機能層3に導電性カーボン層4を設ける工程により、製造される。
まず、公知または市販の可撓性基材2を用意する。
その後、必要に応じて、可撓性基材2と機能層3との密着性の観点から、可撓性基材2の上面に、例えば、スパッタ、コロナ放電、火炎、紫外線照射、電子線照射、化成、酸化などの下地処理を実施することができる。また、溶剤洗浄、超音波洗浄などにより、可撓性基材2を除塵、清浄化することができる。
次いで、可撓性基材2の上面に、機能層3を設ける。
機能層3が無機物層である場合、好ましくは、乾式方法により、可撓性基材2の上面に無機物層である機能層3を形成する。
乾式方法としては、例えば、PVD法(物理蒸着法)、CVD法(化学蒸着法)が挙げられ、好ましくは、PVD法が挙げられる。
PVD法としては、例えば、スパッタ法、真空蒸着法、レーザー蒸着法、イオンプレーティング法(アーク蒸着法など)などが挙げられる。好ましくは、スパッタ法が挙げられる。この方法を採用することにより、薄膜の無機物層を形成することができる。
スパッタ法としては、大電力パルススパッタ法、電子サイクロトロン共鳴スパッタ法、アンバランストマグネトロンスパッタ法、RFスパッタ法、DCスパッタ法(DCマグネトロンスパッタ法など)、DCパルススパッタ法、イオンビームスパッタ法などが挙げられる。ロールトゥロール生産における成膜レート、膜厚均一性の観点から、好ましくは、DCスパッタ法が挙げられる。
スパッタ法を採用する場合、ターゲット材としては、無機物層を構成する上述の無機物が挙げられ、好ましくは、チタンが挙げられる。
スパッタ法の成膜チャンバーに導入するスパッタガスとしては、例えば、Arなどの不活性ガスが挙げられる。また、必要に応じて、酸素ガスなどの反応性ガスを併用することができる。反応性ガスを併用する場合において、反応性ガスの流量比は特に限定しないが、スパッタガスおよび反応性ガスの合計流量比に対して、例えば、0.1流量%以上5流量%以下である。
スパッタ法は、真空下で実施される。具体的には、スパッタ時の気圧は、スパッタリングレートの低下抑制、放電安定性などの観点から、例えば、1Pa以下、好ましくは、0.7Pa以下である。
成膜温度(基材温度)は、例えば、200℃以下、好ましくは、150℃以下、より好ましくは、70℃以下であり、また、例えば、-40℃以上、好ましくは、0℃以上、より好ましくは、30℃以上である。
また、所望厚みの機能層3を形成するために、ターゲット材やスパッタの条件などを適宜設定して複数回スパッタを実施してもよい。
機能層3が有機物層である場合、好ましくは、湿式方法により、可撓性基材2の上面に有機物層である機能層3を形成する。
具体的には、可撓性基材2の上面に、有機物層を形成する樹脂組成物を湿式塗工することにより、可撓性基材2の上面に機能層3を形成する。
具体的には、例えば、樹脂組成物を溶媒で希釈した希釈液(ワニス)を調製し、続いて、希釈液を可撓性基材2の上面に塗布して、希釈液を乾燥する。
塗布方法としては、希釈液および可撓性基材2に応じて適宜選択することができ、例えば、グラビアコート法、ディップコート法、エアーナイフコート法、カーテンコート法、ローラーコート法、ワイヤーバーコート法、エクストルージョンコート法などが挙げられる。
乾燥温度は、例えば、50℃以上、好ましくは、70℃以上であり、例えば、200℃以下、好ましくは、100℃以下である。乾燥時間は、例えば、0.5分以上、好ましくは、1分以上であり、例えば、60分以下、好ましくは、20分以下である。
その後、樹脂組成物が活性エネルギー線硬化性樹脂を含有する場合は、希釈液の乾燥後に、活性エネルギー線を照射することにより、活性エネルギー線硬化性樹脂を硬化させる。
これにより、可撓性基材2と、その上面に配置された機能層3とを備える中間体が得られる。
次いで、機能層3の上面に、導電性カーボン層4を設ける。好ましくは、乾式方法により、機能層3の上面に導電性カーボン層4を形成する。
乾式方法としては、機能層3で上述した方法が挙げられる。導電性カーボン層4に含まれる水素を低減して、より確実に導電性カーボン層4を成膜できる観点から、好ましくは、スパッタ法が挙げられる。sp3結合およびsp2結合の比が所望範囲である導電性カーボンを容易に成膜でき、また、成膜レートを向上させることができ、さらに、ロールトゥロール法を採用できる観点から、より好ましくは、大電力パルススパッタ法が挙げられる。
スパッタ法を採用する場合、ターゲット材としては、カーボンが挙げられる。なお、ターゲット材は、膜質調整やプロセス安定の観点から、公知の添加剤を含有していてもよい。
スパッタ法の成膜チャンバーに導入するスパッタガスとしては、例えば、Ar、Xeなどの不活性ガスが挙げられる。なお、導電性カーボン層4のスパッタ時では、反応性ガスとして酸素ガスなどを併用しない。
スパッタ法は、真空下で実施される。具体的には、スパッタ時の気圧は、スパッタリングレートの低下抑制、放電安定性などの観点から、例えば、1Pa以下、好ましくは、0.7Pa以下である。
成膜温度(基材温度)は、例えば、200℃以下、好ましくは、150℃以下、より好ましくは、70℃以下であり、また、例えば、-40℃以上、好ましくは、0℃以上、より好ましくは、30℃以上である。
また、所望厚みの導電性カーボン層4を形成するために、ターゲット材やスパッタの条件などを適宜設定して複数回スパッタ法を実施してもよい。
これにより、電極フィルム1が得られる。
得られる電極フィルム1の総厚みは、例えば、2μm以上、好ましくは、20μm以上であり、また、例えば、200μm以下、好ましくは、120μm以下、より好ましくは、100μm以下である。
電極フィルム1における導電性カーボン層4(すなわち、電極フィルム1の上面)の表面粗さRaは、例えば、5.0nm以下、好ましくは、2.0nm以下である。電極フィルム1の表面粗さを上記上限以下とすることにより、電気化学測定用の電極として用いた場合に、ノイズを抑制することができる。
電極フィルム1の上面(導電性カーボン層4の表面)における表面抵抗値は、例えば、1.0×104Ω/□以下、好ましくは、1.0×103Ω/□以下、より好ましくは、5.0×102Ω/□以下である。
表面抵抗値は、JIS K 7194に準じて、4端子法により測定することができる。
また、上記製造方法では、ロールトゥロール方式にて、可撓性基材2を搬送させながら、その可撓性基材2に、機能層3および導電性カーボン層4をこの順に形成してもよく、また、これらの層の一部または全部をバッチ方式(枚葉方式)にて形成してもよい。生産性の観点から、好ましくは、ロールトゥロール方式にて、可撓性基材2を搬送させながら、その可撓性基材2に、各層を形成する。
6.電気化学測定用電極フィルム、および、電気化学測定システム
この電極フィルム1は、各種の電極として用いることができ、好ましくは、電気化学測定法を実施する電気化学測定用の電極(好ましくは、作用電極)として用いることができる。
この電極フィルム1は、各種の電極として用いることができ、好ましくは、電気化学測定法を実施する電気化学測定用の電極(好ましくは、作用電極)として用いることができる。
電極フィルム1を電極として用いる場合、電極フィルム1の上面には、導電性カーボン層4の露出面を調整する観点から、絶縁層が設けられていてもよい。また、電極フィルム1全体、または、導電性カーボン層4および機能層3は、所望の形状にパターニングされていてもよい。
絶縁層としては、可撓性基材2で上述した高分子フィルムなどが挙げられる。
電気化学測定法としては、例えば、電位差測定法などの電位差測定手法、例えば、電気伝導度測定法、アンペロメトリー・ボルタンメトリー法、交流インピーダンス法などの電流測定手法などが挙げられる。
本発明の電気化学測定システムは、作用電極として電極フィルム1を用いる。
具体的には、電位差測定手法における電気化学測定システムは、電極フィルム1と、参照電極と、これら電極間の起電力を測定する電位差計を備える。また、電流測定手法における電気化学測定システムは、電極フィルム1と、参照電極と、対極と、これらの電極電位を制御するポテンショスタットと、電極フィルム1および対極の間に流れる電流を測定する電流検出素子とを備える。
参照電極としては、例えば、銀/塩化銀などが挙げられ、対極としては、例えば、白金、金、ニッケルなどが挙げられる。
7.作用効果
この電極フィルム1によれば、基材として可撓性基材2を使用しているので、ロールトゥロール工程で製造することができる。そのため、生産性に優れる。また、可撓性基材2と導電性カーボン層4との間に機能層3を備えているため、可撓性基材2が導電性カーボン層4の成膜時に与える悪影響を抑制できる。
この電極フィルム1によれば、基材として可撓性基材2を使用しているので、ロールトゥロール工程で製造することができる。そのため、生産性に優れる。また、可撓性基材2と導電性カーボン層4との間に機能層3を備えているため、可撓性基材2が導電性カーボン層4の成膜時に与える悪影響を抑制できる。
具体的には、機能層3がガスバリア層である場合は、ロールトゥロール工程により、導電性カーボン層4を可撓性基材2の上側に製膜する際に、可撓性基材2から放出される不純物ガスが、ガスバリア層によって、導電性カーボン層4内に到達することを抑制することができる。そのため、sp2結合およびsp3結合を有する導電性カーボン層4の内部に不純物が侵入することを抑制でき、導電性カーボン層4が備える導電性、電位窓の広さなどの電極特性を好適に発揮することができる。さらには、可撓性基材2および機能層3からなる中間体に対する成膜性に優れる。
また、機能層3が金属層である場合は、ガスバリア性および導電性を備える。そのため、ガスバリア層として、導電性カーボン層4の内部に不純物が侵入することを抑制でき、導電性カーボン層4が備える導電性、電位窓の広さなどの電極特性を好適に発揮することができる。また、導電層として、導電性カーボン層4の導電性を補完または補助することができる。これらによって、電極フィルム1の導電性(すなわち、低い表面抵抗値)を顕著に良好にさせることができる。
また、この電極フィルム1を備える電気化学測定システムは、生産性に優れ、導電性、電位窓の広さなどの電極特性を好適に発揮することができる。そのため、被測定対象の検知精度を向上させることができるとともに、多種の物質を測定することができる。
8.変形例
電極フィルム1は、可撓性基材2、機能層3および導電性カーボン層4からなるが、例えば、図示しないが、可撓性基材2と機能層3との間に、厚み1~100nmのアンダーコート層をさらに備えていてもよい。これにより、機能層3との密着性をより一層向上させたり、または、表面粗さを調整することができる。
電極フィルム1は、可撓性基材2、機能層3および導電性カーボン層4からなるが、例えば、図示しないが、可撓性基材2と機能層3との間に、厚み1~100nmのアンダーコート層をさらに備えていてもよい。これにより、機能層3との密着性をより一層向上させたり、または、表面粗さを調整することができる。
以下に実施例および比較例を示し、本発明をさらに具体的に説明する。なお、本発明は、何ら実施例および比較例に限定されない。また、以下の記載において用いられる配合割合(含有割合)、物性値、パラメータなどの具体的数値は、上記の「発明を実施するための形態」において記載されている、それらに対応する配合割合(含有割合)、物性値、パラメータなど該当記載の上限値(「以下」、「未満」として定義されている数値)または下限値(「以上」、「超過」として定義されている数値)に代替することができる。
実施例1
可撓性基材として、厚みが50μmであるポリエチレンテレフタレートフィルム(PETフィルム)を用意した。DCマグネトロンスパッタ法により、不活性ガスが存在する環境下で、PETフィルムの上面に、ガスバリア層(機能層)として、厚みが10nmであるチタン層(金属層)を形成した。なお、ターゲット材としてチタンを用い、基材温度を40℃、成膜時の真空度を0.6Paとした。
可撓性基材として、厚みが50μmであるポリエチレンテレフタレートフィルム(PETフィルム)を用意した。DCマグネトロンスパッタ法により、不活性ガスが存在する環境下で、PETフィルムの上面に、ガスバリア層(機能層)として、厚みが10nmであるチタン層(金属層)を形成した。なお、ターゲット材としてチタンを用い、基材温度を40℃、成膜時の真空度を0.6Paとした。
続いて、大電力パルススパッタ法により、不活性ガスが存在する環境下で、チタン層の上面に、厚みが35nmであるカーボン層を形成した。なお、ターゲット材としてカーボンを用い、基材温度を40℃、成膜時の真空度を0.6Paとした。
これにより、可撓性基材、機能層および導電性カーボン層を順に備える電極フィルムを製造した。
実施例2
チタン層の厚みを15nmとした以外は、実施例1と同様にして電極フィルムを作製した。
チタン層の厚みを15nmとした以外は、実施例1と同様にして電極フィルムを作製した。
実施例3
チタン層の厚みを5nmとした以外は、実施例1と同様にして電極フィルムを作製した。
チタン層の厚みを5nmとした以外は、実施例1と同様にして電極フィルムを作製した。
実施例4
実施例3において、チタン層を形成した後、スパッタ装置から電極フィルムを取り出し、大気圧下で24時間放置し、チタン層の上面を酸化させて、金属酸化層(酸化チタン層)を形成した。続いて、実施例3と同様にしてカーボン層を形成して、電極フィルムを製造した。
実施例3において、チタン層を形成した後、スパッタ装置から電極フィルムを取り出し、大気圧下で24時間放置し、チタン層の上面を酸化させて、金属酸化層(酸化チタン層)を形成した。続いて、実施例3と同様にしてカーボン層を形成して、電極フィルムを製造した。
比較例1
チタン層を形成しなかった以外は、実施例1と同様にして、電極フィルムを製造した。
チタン層を形成しなかった以外は、実施例1と同様にして、電極フィルムを製造した。
比較例2
PETフィルムの代わりにシリコン基板を用いて、そのシリコン基板の上面に実施例1と同様の条件でカーボン層を形成することにより、電極基板を製造した。
PETフィルムの代わりにシリコン基板を用いて、そのシリコン基板の上面に実施例1と同様の条件でカーボン層を形成することにより、電極基板を製造した。
(1)厚みの測定
各実施例および各実施例の電極フィルムおよび電極基板を用いて、FIBマイクロサンプリング法によりTEM用断面試料を作製し、電界放射型透過電子顕微鏡(FE-TEM、JOEL社製、「JEM-2800」)を用いて断面観察して、各層の厚みを測定した。
各実施例および各実施例の電極フィルムおよび電極基板を用いて、FIBマイクロサンプリング法によりTEM用断面試料を作製し、電界放射型透過電子顕微鏡(FE-TEM、JOEL社製、「JEM-2800」)を用いて断面観察して、各層の厚みを測定した。
また、エネルギー分散型X線分析装置(EDX、Thermo Fisher Scientific社製、「NORAN system 7」)を用いて元素分析を実施して、該当金属と検出限界以上の酸素とが観測された層を金属酸化層とし、該当金属が検出され酸素が検出限界以下であった層を金属層とした。結果を表1に示す。
(2)sp3、sp2の測定
各実施例および各実施例において、X線光電子分光分析装置(ESCA)を用いて、各導電性カーボン層の表面に、X線を照射することにより、結合エネルギー(単位:eV、横軸)および強度(単位:CPS、縦軸)を測定し、これらに基づいて、グラフを作成した。
各実施例および各実施例において、X線光電子分光分析装置(ESCA)を用いて、各導電性カーボン層の表面に、X線を照射することにより、結合エネルギー(単位:eV、横軸)および強度(単位:CPS、縦軸)を測定し、これらに基づいて、グラフを作成した。
装置 :アルバック・ファイ社製、「Quantum2000」
X線源 :モノクロAlKα
X線設定 :200μmφ[15kV、30W]
光電子取出し角 :試料表面に対して45°
帯電中和条件 :電子中和銃とArイオン銃(中和モード)の併用
結合エネルギー :C-C結合に由来するピークを285.0eVに設定
各実施例および各比較例の導電性カーボン層のグラフのいずれにおいても、sp3のピークおよびsp2のピークが確認されたので、sp2結合およびsp3結合の両方を有していることが分かった。
X線源 :モノクロAlKα
X線設定 :200μmφ[15kV、30W]
光電子取出し角 :試料表面に対して45°
帯電中和条件 :電子中和銃とArイオン銃(中和モード)の併用
結合エネルギー :C-C結合に由来するピークを285.0eVに設定
各実施例および各比較例の導電性カーボン層のグラフのいずれにおいても、sp3のピークおよびsp2のピークが確認されたので、sp2結合およびsp3結合の両方を有していることが分かった。
(3)表面抵抗値の測定
各実施例および各比較例において、導電性カーボン層側の表面(上面)を、JIS K 7194に準じて、4端子法により測定した。結果を表1に示す。
各実施例および各比較例において、導電性カーボン層側の表面(上面)を、JIS K 7194に準じて、4端子法により測定した。結果を表1に示す。
(4)密着性の評価
各実施例および各比較例に対して、JISK5400に準じて、碁盤目剥離試験(各マス1mm□、合計100マス)を実施し、下記の基準にて密着性を評価した。結果を表1に示す。
剥がれが0マスであった場合を○と評価した。
剥がれが1マス以上10マス以下であった場合を△と評価した。
剥がれが11マス以上であった場合を×と評価した。
各実施例および各比較例に対して、JISK5400に準じて、碁盤目剥離試験(各マス1mm□、合計100マス)を実施し、下記の基準にて密着性を評価した。結果を表1に示す。
剥がれが0マスであった場合を○と評価した。
剥がれが1マス以上10マス以下であった場合を△と評価した。
剥がれが11マス以上であった場合を×と評価した。
なお、上記発明は、本発明の例示の実施形態として提供したが、これは単なる例示に過ぎず、限定的に解釈してはならない。当該技術分野の当業者によって明らかな本発明の変形例は、後記請求の範囲に含まれる。
本発明の電極フィルムは、各種の工業製品に適用することができ、例えば、電気化学測定システム用電極などの各種の電極として用いることができる。
1 電極フィルム
2 可撓性基材
3 機能層
4 導電性カーボン層
2 可撓性基材
3 機能層
4 導電性カーボン層
Claims (8)
- 可撓性基材と、
前記可撓性基材の厚み方向一方側に配置される機能層と、
前記機能層の厚み方向一方側に配置され、sp2結合およびsp3結合を有する導電性カーボン層と
を備えることを特徴とする、電極フィルム。 - 前記機能層が、ガスバリア層であることを特徴とする、請求項1に記載の電極フィルム。
- 前記機能層が、金属層であることを特徴とする、請求項1または2に記載の電極フィルム。
- 前記機能層の厚みが、5nm以上であることを特徴とする、請求項1~3のいずれか一項に記載の電極フィルム。
- 前記機能層内の厚み方向一方面に形成される酸化膜の厚みが、3nm未満であることを特徴とする、請求項1~4のいずれか一項に記載の電極フィルム。
- 前記可撓性基材が、高分子フィルムであることを特徴とする、請求項1~5のいずれか一項に記載の電極フィルム。
- 電気化学測定用の電極であることを特徴とする、請求項1~6のいずれか一項に記載の電極フィルム。
- 請求項7に記載の電極フィルムを備えることを特徴とする、電気化学測定システム。