WO2019047387A1 - Pigment nacré photochromique à base d'oxyde de tungstène-mica et procédé de préparation d'un liquide de dispersion de celui-ci - Google Patents

Pigment nacré photochromique à base d'oxyde de tungstène-mica et procédé de préparation d'un liquide de dispersion de celui-ci Download PDF

Info

Publication number
WO2019047387A1
WO2019047387A1 PCT/CN2017/113060 CN2017113060W WO2019047387A1 WO 2019047387 A1 WO2019047387 A1 WO 2019047387A1 CN 2017113060 W CN2017113060 W CN 2017113060W WO 2019047387 A1 WO2019047387 A1 WO 2019047387A1
Authority
WO
WIPO (PCT)
Prior art keywords
mica
photochromic
tungsten oxide
pearlescent pigment
suspension
Prior art date
Application number
PCT/CN2017/113060
Other languages
English (en)
Chinese (zh)
Inventor
吴昌梓
蒋绪川
王淑芬
余艾冰
Original Assignee
瑞彩科技股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 瑞彩科技股份有限公司 filed Critical 瑞彩科技股份有限公司
Publication of WO2019047387A1 publication Critical patent/WO2019047387A1/fr

Abstract

La présente invention concerne un pigment nacré photochromique d'oxyde de tungstène-mica et un procédé de préparation d'un liquide de dispersion de celui-ci, appartenant au domaine de la préparation de nouveaux matériaux fonctionnels. Dans la présente invention, afin de surmonter les déficiences de l'état de la technique, de l'oxyde de tungstène est uniformément revêtu sur la surface du mica au moyen de l'assistance d'un matériau organique soluble dans l'eau et de l'ajustement du pH, ce qui permet de préparer un pigment nacré photochromique d'oxyde de tungstène-mica. La poudre obtenue ou un liquide de dispersion de celle-ci sont directement exposés à une lumière ultraviolette pendant différentes durées pour observer des effets photochromiques, et on a remarqué que la poudre et le liquide de dispersion préparés présentent tous deux de bons effets photochromiques sous irradiation de lumière ultraviolette, la vitesse de réponse à la lumière et la réversibilité photochromique étant bonnes. Le procédé selon la présente invention est un procédé de synthèse chimique à basse température, et est un procédé à conditions modérées qui est simple, efficace et facile à adapter à une production industrielle.
PCT/CN2017/113060 2017-09-06 2017-11-27 Pigment nacré photochromique à base d'oxyde de tungstène-mica et procédé de préparation d'un liquide de dispersion de celui-ci WO2019047387A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201710795004.7A CN107629782B (zh) 2017-09-06 2017-09-06 一种氧化钨-云母光致变色珠光颜料及其分散液的制备方法
CN201710795004.7 2017-09-06

Publications (1)

Publication Number Publication Date
WO2019047387A1 true WO2019047387A1 (fr) 2019-03-14

Family

ID=61099914

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2017/113060 WO2019047387A1 (fr) 2017-09-06 2017-11-27 Pigment nacré photochromique à base d'oxyde de tungstène-mica et procédé de préparation d'un liquide de dispersion de celui-ci

Country Status (2)

Country Link
CN (1) CN107629782B (fr)
WO (1) WO2019047387A1 (fr)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113980668A (zh) * 2021-11-10 2022-01-28 天津大学 一种铜-云母-氧化钨的光致变色复合纳米材料及方法
CN113861959A (zh) * 2021-11-10 2021-12-31 天津大学 一种银-铜-氧化钨的光致变色复合纳米材料及制备方法
CN114958036B (zh) * 2022-06-30 2023-12-01 丰田自动车株式会社 一种珠光颜料及其制备方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1461332A (zh) * 2000-10-14 2003-12-10 Sky化学株式会社 合成云母涂覆金属氧化物制备珍珠状颜料的方法
CN1519278A (zh) * 2002-11-21 2004-08-11 Ĭ��ר���ɷ����޹�˾ 具有高亮度和高色度的闪光颜料
WO2016168455A1 (fr) * 2015-04-15 2016-10-20 Sun Chemical Corporation Préparation de pigments à effet
CN106833030A (zh) * 2017-01-13 2017-06-13 爱乐彩（天津）新材料科技有限公司 一种超大粒径人工合成基材珠光颜料的制备方法

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103013186A (zh) * 2012-12-21 2013-04-03 福建师范大学 一种复合着色型珠光颜料及其制备
CN103333528A (zh) * 2013-06-26 2013-10-02 福建师范大学 一种具有荧光效果的珠光颜料的制备方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1461332A (zh) * 2000-10-14 2003-12-10 Sky化学株式会社 合成云母涂覆金属氧化物制备珍珠状颜料的方法
CN1519278A (zh) * 2002-11-21 2004-08-11 Ĭ��ר���ɷ����޹�˾ 具有高亮度和高色度的闪光颜料
WO2016168455A1 (fr) * 2015-04-15 2016-10-20 Sun Chemical Corporation Préparation de pigments à effet
CN106833030A (zh) * 2017-01-13 2017-06-13 爱乐彩（天津）新材料科技有限公司 一种超大粒径人工合成基材珠光颜料的制备方法

Also Published As

Publication number Publication date
CN107629782B (zh) 2020-09-11
CN107629782A (zh) 2018-01-26

Similar Documents

Publication Publication Date Title
JP4304343B2 (ja) 酸化亜鉛微粒子及びその集合体と分散溶液の製造方法
CN106750466B (zh) 可逆热致变色薄膜及其制备方法
WO2019047387A1 (fr) Pigment nacré photochromique à base d'oxyde de tungstène-mica et procédé de préparation d'un liquide de dispersion de celui-ci
CN109422244B (zh) 可阻断紫外线的光致变色纳米材料及其制备方法和用途
CN105233874B (zh) 一步法制备卟啉功能化纳米硫化锌的工艺
CN111718450B (zh) 一种有机-无机电极化粒子及其制备方法和应用
CN106892460A (zh) 一种钨青铜纳米片的制备方法
CN106746724A (zh) 一种氧化钼电致变色纳米薄膜及其制备方法
CN108659831A (zh) 一种一锅法制备固体室温磷光碳点的方法
CN110487772B (zh) 一种三维SnO2/Ag NPs拉曼增强基底及其制备方法与应用
CN109095445B (zh) 一种镂空纳米带的制备方法、镂空纳米带及应用
CN113548809B (zh) 一种NiOx电致变色多孔材料及其制备方法
CN109835945B (zh) 氧缺陷二氧化锡气敏材料的制备方法及其产品和应用
CN111944512B (zh) 一种超小无机纳米异质结光致变色材料、采用该材料制备的可擦重写介质及其制备方法
CN110862681B (zh) 一种三元复合气敏材料及其制备方法
JP5385190B2 (ja) 着色二酸化チタン粉末の製造方法
CN106966430A (zh) 一种金属钒酸盐纳米材料的制备方法
CN106190096B (zh) 一种力敏型TiO2/BOx微米晶压力变色薄膜的制备方法
CN105776323B (zh) 一种制备具有可见光响应的二氧化锡量子点的方法
CN110255923B (zh) 一种TiO2纳米颗粒吸附苝酰亚胺衍生物薄膜及其作为电致变色材料的应用
CN108033482B (zh) 一种制备氧化铟空心纳米球的方法及产品
CN107601516B (zh) 一种碳包覆硼掺杂二氧化硅纳米材料及其制备方法
CN107039186B (zh) Ag2Se量子点-染料共敏化太阳能电池的制备方法
CN106830086B (zh) 一种氧化钨纳米棒及其制备方法
Maswanganye et al. Strain induced by temperature evolution of mesoporous ZnO nanopowders and its effect on structural, optical and electrical impedance properties

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17924468

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17924468

Country of ref document: EP

Kind code of ref document: A1