WO2018230700A1 - Dialcoxymagnésium ainsi que procédé de fabrication de celui-ci, composant de catalyseur solide pour polymérisation d'oléfines, et procédé de fabrication de polymère d'oléfine - Google Patents

Dialcoxymagnésium ainsi que procédé de fabrication de celui-ci, composant de catalyseur solide pour polymérisation d'oléfines, et procédé de fabrication de polymère d'oléfine Download PDF

Info

Publication number
WO2018230700A1
WO2018230700A1 PCT/JP2018/022885 JP2018022885W WO2018230700A1 WO 2018230700 A1 WO2018230700 A1 WO 2018230700A1 JP 2018022885 W JP2018022885 W JP 2018022885W WO 2018230700 A1 WO2018230700 A1 WO 2018230700A1
Authority
WO
WIPO (PCT)
Prior art keywords
dialkoxymagnesium
carbon atoms
group
producing
present
Prior art date
Application number
PCT/JP2018/022885
Other languages
English (en)
Japanese (ja)
Inventor
保坂　元基
速 小川
研太郎 小森
菅野　利彦
Original Assignee
東邦チタニウム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東邦チタニウム株式会社 filed Critical 東邦チタニウム株式会社
Publication of WO2018230700A1 publication Critical patent/WO2018230700A1/fr

Abstract

L'invention concerne un dialcoxymagnésium qui est caractéristique en ce que la rugosité moyenne arithmétique (Ra) de la surface de ses particules est inférieure ou égale à 0,5, et la hauteur maximale (Rz) de la surface de ses particules est inférieure ou égale à 2,0. Plus précisément, l'invention permet de fournir un dialcoxymagnésium à surface lisse.
PCT/JP2018/022885 2017-06-15 2018-06-15 Dialcoxymagnésium ainsi que procédé de fabrication de celui-ci, composant de catalyseur solide pour polymérisation d'oléfines, et procédé de fabrication de polymère d'oléfine WO2018230700A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2017-117561 2017-06-15
JP2017117561 2017-06-15
JP2018061900 2018-03-28
JP2018-061900 2018-03-28

Publications (1)

Publication Number Publication Date
WO2018230700A1 true WO2018230700A1 (fr) 2018-12-20

Family

ID=64660730

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/022885 WO2018230700A1 (fr) 2017-06-15 2018-06-15 Dialcoxymagnésium ainsi que procédé de fabrication de celui-ci, composant de catalyseur solide pour polymérisation d'oléfines, et procédé de fabrication de polymère d'oléfine

Country Status (2)

Country Link
TW (1) TW201906806A (fr)
WO (1) WO2018230700A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115763822A (zh) * 2023-01-06 2023-03-07 碳佳(北京)科技有限公司 一种硅碳负极复合材料、应用及锂电池
US11680115B2 (en) 2020-03-31 2023-06-20 Sumitomo Chemical Company, Limited Solid catalyst component for olefin polymerization
US11840595B2 (en) 2020-08-07 2023-12-12 Sumitomo Chemical Company, Limited Solid catalyst component for olefin polymerization

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003342214A (ja) * 2002-05-24 2003-12-03 Idemitsu Petrochem Co Ltd マグネシウム化合物、オレフィン重合用固体触媒成分、オレフィン重合用触媒及びポリオレフィンの製造方法
WO2005102973A1 (fr) * 2004-04-23 2005-11-03 Idemitsu Kosan Co., Ltd. Composé magnésium, catalyseur pour la polymérisation oléfinique et procédé de production d'un polymère oléfinique
JP2006274105A (ja) * 2005-03-30 2006-10-12 Toho Catalyst Co Ltd オレフィン類重合用固体触媒成分および触媒並びにこれを用いたオレフィン類重合体又は共重合体の製造方法
JP2013530273A (ja) * 2010-05-27 2013-07-25 サムスン トータル ペトロケミカルズ カンパニー リミテッド 球形担体の製造方法、オレフィン重合用固形触媒、該触媒を用いて得られたプロピレン重合体
WO2017170077A1 (fr) * 2016-03-28 2017-10-05 東邦チタニウム株式会社 Alcoxy magnésium, procédé de production d'alcoxy magnésium, composant de catalyseur solide pour la polymérisation d'oléfines, catalyseur pour la polymérisation d'oléfines, et procédé de production d'un polymère d'oléfine

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003342214A (ja) * 2002-05-24 2003-12-03 Idemitsu Petrochem Co Ltd マグネシウム化合物、オレフィン重合用固体触媒成分、オレフィン重合用触媒及びポリオレフィンの製造方法
WO2005102973A1 (fr) * 2004-04-23 2005-11-03 Idemitsu Kosan Co., Ltd. Composé magnésium, catalyseur pour la polymérisation oléfinique et procédé de production d'un polymère oléfinique
JP2006274105A (ja) * 2005-03-30 2006-10-12 Toho Catalyst Co Ltd オレフィン類重合用固体触媒成分および触媒並びにこれを用いたオレフィン類重合体又は共重合体の製造方法
JP2013530273A (ja) * 2010-05-27 2013-07-25 サムスン トータル ペトロケミカルズ カンパニー リミテッド 球形担体の製造方法、オレフィン重合用固形触媒、該触媒を用いて得られたプロピレン重合体
WO2017170077A1 (fr) * 2016-03-28 2017-10-05 東邦チタニウム株式会社 Alcoxy magnésium, procédé de production d'alcoxy magnésium, composant de catalyseur solide pour la polymérisation d'oléfines, catalyseur pour la polymérisation d'oléfines, et procédé de production d'un polymère d'oléfine

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11680115B2 (en) 2020-03-31 2023-06-20 Sumitomo Chemical Company, Limited Solid catalyst component for olefin polymerization
US12037441B2 (en) 2020-03-31 2024-07-16 Sumitomo Chemical Company, Limited Solid catalyst component for olefin polymerization
US11840595B2 (en) 2020-08-07 2023-12-12 Sumitomo Chemical Company, Limited Solid catalyst component for olefin polymerization
CN115763822A (zh) * 2023-01-06 2023-03-07 碳佳(北京)科技有限公司 一种硅碳负极复合材料、应用及锂电池
CN115763822B (zh) * 2023-01-06 2023-08-04 碳佳(北京)科技有限公司 一种硅碳负极复合材料、应用及锂电池

Also Published As

Publication number Publication date
TW201906806A (zh) 2019-02-16

Similar Documents

Publication Publication Date Title
JP6577964B2 (ja) オレフィン類重合触媒の製造方法およびオレフィン類重合体の製造方法
TWI735673B (zh) 烯烴類聚合用固體觸媒成分、烯烴類聚合用固體觸媒成分之製造方法、烯烴類聚合用觸媒、烯烴類聚合體之製造方法、丙烯系共聚合體之製造方法及丙烯系共聚合體
JP6782292B2 (ja) アルコキシマグネシウム、アルコキシマグネシウムの製造方法、オレフィン類重合用固体触媒成分、オレフィン類重合用触媒およびオレフィン類重合体の製造方法
JP6343561B2 (ja) オレフィン類重合用固体触媒成分の製造方法、オレフィン類重合用触媒の製造方法およびオレフィン類重合体の製造方法
JP6283653B2 (ja) プロピレン系ブロック共重合体の製造方法
JP5785809B2 (ja) オレフィン類重合用固体触媒成分、その製造方法、オレフィン類重合触媒およびオレフィン類重合体の製造方法
WO2018230700A1 (fr) Dialcoxymagnésium ainsi que procédé de fabrication de celui-ci, composant de catalyseur solide pour polymérisation d'oléfines, et procédé de fabrication de polymère d'oléfine
JP5771462B2 (ja) オレフィン類重合用固体触媒成分および触媒
JP7100511B2 (ja) ジアルコキシマグネシウムの製造方法、オレフィン類重合用固体触媒成分、オレフィン類重合用固体触媒及びオレフィン類重合体の製造方法
WO2017188180A1 (fr) Constituant catalytique solide pour la polymérisation d'oléfines, catalyseur pour la polymérisation d'oléfines et procédé de production d'un polymère oléfinique
JP5340916B2 (ja) オレフィン類重合用固体触媒成分、重合用触媒およびこれを用いたオレフィン類重合体の製造方法
JP6067299B2 (ja) オレフィン類重合用固体触媒成分、オレフィン類重合用触媒およびオレフィン類重合体の製造方法
JP5886000B2 (ja) アルコキシマグネシウムの製造方法、オレフィン類重合用固体触媒成分の製造方法、オレフィン類重合用触媒の製造方法並びにオレフィン類重合体の製造方法
JP6914095B2 (ja) ジアルコキシマグネシウムの製造方法、オレフィン類重合用触媒成分の製造方法、オレフィン類重合用触媒の製造方法、及びオレフィン類重合体の製造方法
JP7324584B2 (ja) ジアルコキシマグネシウムの製造方法、オレフィン類重合用固体触媒成分の製造方法、オレフィン類重合用触媒の製造方法及びオレフィン類重合体の製造方法
JP7199980B2 (ja) ジアルコキシマグネシウムの製造方法、オレフィン類重合用固体触媒成分の製造方法、オレフィン類重合用触媒の製造方法及びオレフィン類重合体の製造方法
JP5745980B2 (ja) オレフィン類重合用固体触媒成分、オレフィン類重合用触媒及びオレフィン類重合体の製造方法
JP2001329014A (ja) オレフィン類重合用固体触媒成分および触媒
JP2013067701A (ja) オレフィン類重合用固体触媒成分、オレフィン類重合用触媒及びオレフィン類重合体の製造方法
JP2013067700A (ja) オレフィン類重合用固体触媒成分、オレフィン類重合用触媒及びオレフィン類重合体の製造方法
JP2002105115A (ja) オレフィン類重合用固体触媒成分および触媒

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18818704

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18818704

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP