WO2018229146A1 - Stratifié d'emballage et récipient d'emballage produit à partir du stratifié - Google Patents
Stratifié d'emballage et récipient d'emballage produit à partir du stratifié Download PDFInfo
- Publication number
- WO2018229146A1 WO2018229146A1 PCT/EP2018/065694 EP2018065694W WO2018229146A1 WO 2018229146 A1 WO2018229146 A1 WO 2018229146A1 EP 2018065694 W EP2018065694 W EP 2018065694W WO 2018229146 A1 WO2018229146 A1 WO 2018229146A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- packaging
- packaging laminate
- laminate
- bulk
- Prior art date
Abstract
L'invention concerne un stratifié d'emballage comprenant une couche en vrac, une couche thermoscellable thermoplastique transparente la plus à l'extérieur dirigée vers l'extérieur d'un emballage formé à partir du stratifié d'emballage, et une couche thermoplastique thermoscellable la plus à l'intérieur dirigée vers l'intérieur d'un emballage pour avoir un contact direct avec le produit rempli. L'invention concerne également un récipient d'emballage produit à partir du stratifié d'emballage, et destiné en particulier à l'emballage de produits alimentaires liquides et de boissons.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201720685412.2 | 2017-06-13 | ||
CN201720685412.2U CN208006409U (zh) | 2017-06-13 | 2017-06-13 | 一种包装层压板以及由该包装层压板制成的包装容器 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2018229146A1 true WO2018229146A1 (fr) | 2018-12-20 |
Family
ID=62816490
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2018/065694 WO2018229146A1 (fr) | 2017-06-13 | 2018-06-13 | Stratifié d'emballage et récipient d'emballage produit à partir du stratifié |
Country Status (2)
Country | Link |
---|---|
CN (1) | CN208006409U (fr) |
WO (1) | WO2018229146A1 (fr) |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20040229004A1 (en) * | 2003-05-15 | 2004-11-18 | Hazen Paper Company | Inkjet receptive and laser printable coating for holographic and metallic media |
JP2006160321A (ja) * | 2004-12-08 | 2006-06-22 | Toppan Printing Co Ltd | 美粧性紙カップ容器 |
EP3169518A1 (fr) * | 2014-07-14 | 2017-05-24 | Tetra Laval Holdings & Finance SA | Procede de fabrication d'un materiau d'emballage stratifie, et materiau d'emballage stratifie |
-
2017
- 2017-06-13 CN CN201720685412.2U patent/CN208006409U/zh not_active Ceased
-
2018
- 2018-06-13 WO PCT/EP2018/065694 patent/WO2018229146A1/fr active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20040229004A1 (en) * | 2003-05-15 | 2004-11-18 | Hazen Paper Company | Inkjet receptive and laser printable coating for holographic and metallic media |
JP2006160321A (ja) * | 2004-12-08 | 2006-06-22 | Toppan Printing Co Ltd | 美粧性紙カップ容器 |
EP3169518A1 (fr) * | 2014-07-14 | 2017-05-24 | Tetra Laval Holdings & Finance SA | Procede de fabrication d'un materiau d'emballage stratifie, et materiau d'emballage stratifie |
Also Published As
Publication number | Publication date |
---|---|
CN208006409U (zh) | 2018-10-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP6867384B2 (ja) | ラミネートバリアフィルム及び包装用の縁部カバーストリップ | |
JP7001592B2 (ja) | ラミネート包装材料及び該包装材料から製造された包装容器 | |
JP6893926B2 (ja) | ラミネート包装材料、それから製造された包装容器、およびラミネート材料を製造するための方法 | |
ES2858353T3 (es) | Método de fabricación de un material de envasado estratificado, el material de envasado obtenido por el método y recipientes de envasado fabricados a partir del mismo | |
CN110678329B (zh) | 层压包装材料、由其制造的包装容器及制造层压材料的方法 | |
JP6893923B2 (ja) | ラミネート包装材料、それから製造された包装容器、およびラミネート材料を製造するための方法 | |
FI117748B (fi) | Pakkauksen kansi, sen valmistusmenetelmä sekä kannella suljettu pakkaus | |
TR201809602T4 (tr) | Lamine edilmiş ambalajlama materyali ve lamine edilmiş bir ambalajlama materyalinin üretim yöntemi. | |
JP6965243B2 (ja) | バリアフィルムを備えるラミネート包装材料及び該ラミネート包装材料から製造された包装容器 | |
EP3089919B1 (fr) | Matériau d'emballage et contenant d'emballage pourvu d'un dispositif d'ouverture fabriqué à partir de celui-ci | |
JP2013504450A (ja) | 熱機械安定性且つ熱シール性の遮断コート薄膜、該薄膜を備える包装積層体、該包装積層体から形成された包装容器、並びに該薄膜の作製方法 | |
DK3140115T3 (en) | PACKAGING MATERIAL LAMINATE STRUCTURE | |
JP2005528236A (ja) | 光、気体および液体を通さないヒートシール可能なパッケージ用複合材料 | |
ES2908728T3 (es) | Material de envasado laminado que comprende una película de barrera | |
WO2018229146A1 (fr) | Stratifié d'emballage et récipient d'emballage produit à partir du stratifié | |
JP7325338B2 (ja) | ラミネートされた材料を製造するための方法 | |
ES2890099T3 (es) | Material de envasado laminado que comprende una película de barrera y recipientes de envasado fabricados a partir del mismo | |
EP4253047A1 (fr) | Matériau d'emballage stratifié et récipient d'emballage fabriqué à partir de celui-ci | |
AU2023245512A1 (en) | A laminated packaging material and packaging container manufactured therefrom | |
EP3368302B1 (fr) | Matériau d'emballage stratifié comprenant un film barrière et contenants d'emballage ainsi fabriques | |
JP2004224343A (ja) | ストリップテープ及び包装容器 | |
WO2016038254A1 (fr) | Stratifié d'emballage, emballage et procédé de production de stratifié d'emballage | |
JP2005022740A (ja) | 包装材料 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 18737158 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 18737158 Country of ref document: EP Kind code of ref document: A1 |