WO2018090121A1 - Revêtements pour augmenter l'éclat des couleurs et procédés pour leur application - Google Patents

Revêtements pour augmenter l'éclat des couleurs et procédés pour leur application Download PDF

Info

Publication number
WO2018090121A1
WO2018090121A1 PCT/CA2016/051325 CA2016051325W WO2018090121A1 WO 2018090121 A1 WO2018090121 A1 WO 2018090121A1 CA 2016051325 W CA2016051325 W CA 2016051325W WO 2018090121 A1 WO2018090121 A1 WO 2018090121A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
substrate
silica particles
binder solids
colour
Prior art date
Application number
PCT/CA2016/051325
Other languages
English (en)
Inventor
Barry R. Knowlton
Original Assignee
Knowlton Barry R
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Knowlton Barry R filed Critical Knowlton Barry R
Priority to PCT/CA2016/051325 priority Critical patent/WO2018090121A1/fr
Publication of WO2018090121A1 publication Critical patent/WO2018090121A1/fr

Abstract

L'invention concerne un revêtement destiné à être appliqué sur un substrat de couleur naturelle, qui permet d'augmenter l'éclat de couleur du colorant appliqué sur le substrat revêtu. Le revêtement comprend des particules de silice et au moins un solide de liant et peut en outre comprendre du siloxane. Le revêtement peut comprendre une monodispersion ou une polydispersion aqueuse de sol de particules de silice présentant éventuellement des grosseurs de particule d'environ 1 à environ 150 nm.
PCT/CA2016/051325 2016-11-15 2016-11-15 Revêtements pour augmenter l'éclat des couleurs et procédés pour leur application WO2018090121A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/CA2016/051325 WO2018090121A1 (fr) 2016-11-15 2016-11-15 Revêtements pour augmenter l'éclat des couleurs et procédés pour leur application

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CA2016/051325 WO2018090121A1 (fr) 2016-11-15 2016-11-15 Revêtements pour augmenter l'éclat des couleurs et procédés pour leur application

Publications (1)

Publication Number Publication Date
WO2018090121A1 true WO2018090121A1 (fr) 2018-05-24

Family

ID=62145975

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CA2016/051325 WO2018090121A1 (fr) 2016-11-15 2016-11-15 Revêtements pour augmenter l'éclat des couleurs et procédés pour leur application

Country Status (1)

Country Link
WO (1) WO2018090121A1 (fr)

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5463178A (en) * 1993-07-16 1995-10-31 Asahi Glass Company Ltd. Recording sheet and process for its production
US5985076A (en) * 1994-09-09 1999-11-16 Asahi Glass Company Ltd. Coated paper and methods for its preparation
US6420039B1 (en) * 1998-10-02 2002-07-16 Cabot Corporation Recording medium
CA2435432A1 (fr) * 2001-01-24 2002-08-01 Bayer Aktiengesellschaft Enveloppe protectrice ayant une structure de revetement a deux couches
CA2662496A1 (fr) * 2006-09-07 2008-03-13 Benjamin Moore & Co. Systeme de peinture a revetement de base couleur et revetement superieur couleur
CA2664479A1 (fr) * 2006-10-23 2008-10-23 Ppg Industries Ohio, Inc. Composition d'amorceur et articles incorporant l'amorceur
CA2733944A1 (fr) * 2008-09-22 2010-03-25 Benjamin Moore & Co. Finitions de fondation colorees a auto-amorcage
CA2925495A1 (fr) * 2013-09-26 2015-04-02 Ross Technology Corporation Revetements flexibles de polyurethane super-hydrophobes et/ou oleophobes
CA2912232A1 (fr) * 2015-09-03 2017-03-03 Barry R. Knowlton Revetements servant a augmenter la vivacite des couleurs et methodes d'application connexes

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5463178A (en) * 1993-07-16 1995-10-31 Asahi Glass Company Ltd. Recording sheet and process for its production
US5985076A (en) * 1994-09-09 1999-11-16 Asahi Glass Company Ltd. Coated paper and methods for its preparation
US6420039B1 (en) * 1998-10-02 2002-07-16 Cabot Corporation Recording medium
CA2435432A1 (fr) * 2001-01-24 2002-08-01 Bayer Aktiengesellschaft Enveloppe protectrice ayant une structure de revetement a deux couches
CA2662496A1 (fr) * 2006-09-07 2008-03-13 Benjamin Moore & Co. Systeme de peinture a revetement de base couleur et revetement superieur couleur
CA2664479A1 (fr) * 2006-10-23 2008-10-23 Ppg Industries Ohio, Inc. Composition d'amorceur et articles incorporant l'amorceur
CA2733944A1 (fr) * 2008-09-22 2010-03-25 Benjamin Moore & Co. Finitions de fondation colorees a auto-amorcage
CA2925495A1 (fr) * 2013-09-26 2015-04-02 Ross Technology Corporation Revetements flexibles de polyurethane super-hydrophobes et/ou oleophobes
CA2912232A1 (fr) * 2015-09-03 2017-03-03 Barry R. Knowlton Revetements servant a augmenter la vivacite des couleurs et methodes d'application connexes

Similar Documents

Publication Publication Date Title
CA2586207C (fr) Processus de production de papier couche
KR101206842B1 (ko) 잉크 젯 인쇄용 장식지
JP6034032B2 (ja) 塗工白板紙およびその製造方法
US20080075869A1 (en) Multi-functional paper for enhanced printing performance
CN101772422A (zh) 用于喷墨卷筒纸印刷机印刷的介质
CN106567277A (zh) 磷酸铝、多磷酸铝和偏磷酸铝颗粒在纸张涂层应用中的用途
EP0863255A1 (fr) Papier hydrofuge opaque et recyclable
US20080038553A1 (en) Paper Coated with a Surface Layer Comprising Offset-Printable Silica
US20060099408A1 (en) Pigment composition
US20020071019A1 (en) Recording material bearing an embedded image
US20170066934A1 (en) Coatings for increasing colour vibrancy and methods of applying same
US20050282026A1 (en) Porous coating compositions for printing applications
US20040126572A1 (en) Zirconium-containing metal oxide dispersions for recording media with improved ozone resistance
JP2008036998A (ja) インクジェット記録用紙
WO2018090121A1 (fr) Revêtements pour augmenter l'éclat des couleurs et procédés pour leur application
JP5746590B2 (ja) 塗工紙
CN111989435B (zh) 涂布白板纸
JP2010077552A (ja) 塗工ライナー及びそれを用いた段ボールシート
ITMI20091794A1 (it) Articolo cartaceo patinato stampabile e relativo procedimento di fabbricazione
JP2004353130A (ja) 塗工特殊板紙
JP7463623B2 (ja) 二酸化チタン不含のタバコチッピングインク
JP2002317396A (ja) 美粧ライナ
RU2004122104A (ru) Составы покрытий из карбоната кальция для придания высокого лоска и бумага и картон с покрытием, образованным из вышеуказанных составов
JPH02293499A (ja) ライナー塗工用組成物及び塗工ライナー
JPH11158796A (ja) コーテッド紙

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16921794

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16921794

Country of ref document: EP

Kind code of ref document: A1