WO2018074402A1 - Feuille conductrice étirable, câble étirable, tissu avec câble étirable, et procédé de rétablissement de conduction - Google Patents

Feuille conductrice étirable, câble étirable, tissu avec câble étirable, et procédé de rétablissement de conduction Download PDF

Info

Publication number
WO2018074402A1
WO2018074402A1 PCT/JP2017/037321 JP2017037321W WO2018074402A1 WO 2018074402 A1 WO2018074402 A1 WO 2018074402A1 JP 2017037321 W JP2017037321 W JP 2017037321W WO 2018074402 A1 WO2018074402 A1 WO 2018074402A1
Authority
WO
WIPO (PCT)
Prior art keywords
stretchable
wiring
conductivity
recovery rate
sheet
Prior art date
Application number
PCT/JP2017/037321
Other languages
English (en)
Japanese (ja)
Inventor
弘倫 米倉
義哲 権
達彦 入江
万紀 木南
石丸　園子
Original Assignee
東洋紡株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東洋紡株式会社 filed Critical 東洋紡株式会社
Priority to JP2018546314A priority Critical patent/JP7063271B2/ja
Publication of WO2018074402A1 publication Critical patent/WO2018074402A1/fr

Abstract

L'invention fournit un matériau conducteur étirable qui est destiné à former un câble étirable dans un appareil électronique de type vestimentaire, et qui permet du point de vue de son utilisateur un allongement de la durée de vie du produit en ce qui concerne la détérioration de câbles électriques. Selon l'invention, une électrode ou câble électrique est formé sur un vêtement en mettant en œuvre une feuille conductrice étirable dans un câble. Laquelle feuille conductrice étirable est configurée par une charge conductrice et une résine de liant, et est caractéristique en ce que son irrégularité d'épaisseur est inférieure ou égale à 10%, et son coefficient de rétablissement d'extension après une extension de 20% à 25°C, est supérieur ou égal à 92%. De préférence, la feuille conductrice étirable est également caractéristique en ce que Ｍｗ／Ｍｎ est supérieur ou égal à 4 lorsque la masse moléculaire moyenne en nombre de ladite résine de liant est représentée par Mn et sa masse moléculaire moyenne en poids est représentée par Mw. Cette électrode ou ce câble présente une conductivité qui peut être rétablie à un niveau d'utilisation par chauffage à une température supérieure ou égale à 60°C, y compris lorsque la conductivité est abaissée par extension répétée, lavage, ou similaire.
PCT/JP2017/037321 2016-10-18 2017-10-16 Feuille conductrice étirable, câble étirable, tissu avec câble étirable, et procédé de rétablissement de conduction WO2018074402A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2018546314A JP7063271B2 (ja) 2016-10-18 2017-10-16 伸縮性導体シート、伸縮性配線、伸縮性配線付き布帛、および導電性回復方法

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2016-204204 2016-10-18
JP2016204204 2016-10-18
JP2016-217097 2016-11-07
JP2016217097 2016-11-07

Publications (1)

Publication Number Publication Date
WO2018074402A1 true WO2018074402A1 (fr) 2018-04-26

Family

ID=62018660

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/037321 WO2018074402A1 (fr) 2016-10-18 2017-10-16 Feuille conductrice étirable, câble étirable, tissu avec câble étirable, et procédé de rétablissement de conduction

Country Status (3)

Country Link
JP (1) JP7063271B2 (fr)
TW (1) TW201825013A (fr)
WO (1) WO2018074402A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20220045041A (ko) * 2019-09-21 2022-04-12 엘지전자 주식회사 변환에 기반한 영상 코딩 방법 및 그 장치
JP2022083344A (ja) * 2020-11-24 2022-06-03 東和株式会社 ウェアラブルデバイス用電極パッド
CH718480A1 (de) * 2021-03-29 2022-09-30 Vorn Mehrlagiges Kleidungsstück als Teil eines Personenüberwachungsystems.
WO2023188455A1 (fr) * 2022-03-31 2023-10-05 Tdk株式会社 Matériau de câblage étirable et dispositif étirable
JP7452722B2 (ja) 2019-05-17 2024-03-19 コニカミノルタ株式会社 検査装置及び画像生成方法

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7444361B2 (ja) * 2018-11-06 2024-03-06 積水ポリマテック株式会社 伸縮配線部材
JP7256729B2 (ja) * 2018-12-26 2023-04-12 信越化学工業株式会社 伸縮性配線膜の形成方法
TWI805064B (zh) * 2021-11-08 2023-06-11 財團法人工業技術研究院 軟性混合電子基板及包含其的電子織物

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010153364A (ja) * 2008-11-18 2010-07-08 Tokai Rubber Ind Ltd 導電膜、およびそれを備えたトランスデューサ、フレキシブル配線板
JP2012054192A (ja) * 2010-09-03 2012-03-15 Bayer Material Science Ag 伸縮性配線を有する導電部材
WO2016114278A1 (fr) * 2015-01-14 2016-07-21 東洋紡株式会社 Film conducteur
WO2016114279A1 (fr) * 2015-01-14 2016-07-21 東洋紡株式会社 Pâte d'argent électroconductrice
WO2016114298A1 (fr) * 2015-01-14 2016-07-21 東洋紡株式会社 Électrode extensible, feuille de câblage, et interface pour mesure d'informations biologiques
JP2016141713A (ja) * 2015-01-30 2016-08-08 タツタ電線株式会社 導電性組成物およびそれを備えた導電性シート
JP2017073364A (ja) * 2015-10-09 2017-04-13 プラスコート株式会社 導電性ペーストおよび導電膜
WO2017122639A1 (fr) * 2016-01-13 2017-07-20 東洋紡株式会社 Composition de conducteur élastique, pâte permettant de former un conducteur élastique, vêtement comportant des fils réalisés à partir de la composition de conducteur élastique et son procédé de production

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6303367B2 (ja) 2013-09-30 2018-04-04 東洋紡株式会社 導電性ペースト、導電性膜及びタッチパネル
JP6406359B2 (ja) 2015-01-14 2018-10-17 東洋紡株式会社 導電性布帛

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010153364A (ja) * 2008-11-18 2010-07-08 Tokai Rubber Ind Ltd 導電膜、およびそれを備えたトランスデューサ、フレキシブル配線板
JP2012054192A (ja) * 2010-09-03 2012-03-15 Bayer Material Science Ag 伸縮性配線を有する導電部材
WO2016114278A1 (fr) * 2015-01-14 2016-07-21 東洋紡株式会社 Film conducteur
WO2016114279A1 (fr) * 2015-01-14 2016-07-21 東洋紡株式会社 Pâte d'argent électroconductrice
WO2016114298A1 (fr) * 2015-01-14 2016-07-21 東洋紡株式会社 Électrode extensible, feuille de câblage, et interface pour mesure d'informations biologiques
JP2016141713A (ja) * 2015-01-30 2016-08-08 タツタ電線株式会社 導電性組成物およびそれを備えた導電性シート
JP2017073364A (ja) * 2015-10-09 2017-04-13 プラスコート株式会社 導電性ペーストおよび導電膜
WO2017122639A1 (fr) * 2016-01-13 2017-07-20 東洋紡株式会社 Composition de conducteur élastique, pâte permettant de former un conducteur élastique, vêtement comportant des fils réalisés à partir de la composition de conducteur élastique et son procédé de production

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7452722B2 (ja) 2019-05-17 2024-03-19 コニカミノルタ株式会社 検査装置及び画像生成方法
KR20220045041A (ko) * 2019-09-21 2022-04-12 엘지전자 주식회사 변환에 기반한 영상 코딩 방법 및 그 장치
KR102467334B1 (ko) 2019-09-21 2022-11-16 엘지전자 주식회사 변환에 기반한 영상 코딩 방법 및 그 장치
US11805257B2 (en) 2019-09-21 2023-10-31 Lg Electronics Inc. Image coding method based on transform, and device therefor
JP2022083344A (ja) * 2020-11-24 2022-06-03 東和株式会社 ウェアラブルデバイス用電極パッド
CH718480A1 (de) * 2021-03-29 2022-09-30 Vorn Mehrlagiges Kleidungsstück als Teil eines Personenüberwachungsystems.
WO2023188455A1 (fr) * 2022-03-31 2023-10-05 Tdk株式会社 Matériau de câblage étirable et dispositif étirable

Also Published As

Publication number Publication date
TW201825013A (zh) 2018-07-16
JPWO2018074402A1 (ja) 2019-12-12
JP7063271B2 (ja) 2022-05-09

Similar Documents

Publication Publication Date Title
WO2018074402A1 (fr) Feuille conductrice étirable, câble étirable, tissu avec câble étirable, et procédé de rétablissement de conduction
US11357104B2 (en) Garment-type electronic device and method for producing same
JP6766869B2 (ja) ウェアラブル・スマート・デバイス
CN108701505B (zh) 伸缩性导体片、具有粘接性的伸缩性导体片、布帛上的伸缩性导体构成的配线的形成方法
KR102562579B1 (ko) 신축성 도체 조성물, 신축성 도체 형성용 페이스트, 신축성 도체 조성물로 이루어지는 배선을 갖는 의복 및 그의 제조 방법
JP6551422B2 (ja) 伸縮性電極および配線シート、生体情報計測用インターフェス
JP6973372B2 (ja) 伸縮性導体シート及び伸縮性導体シート形成用ペースト
JP2017168438A (ja) 伸縮性導体形成用ペースト、伸縮性導体シートおよび生体情報計測用プローブ
JP6926500B2 (ja) 衣服型電子機器
JP2017144239A (ja) 衣服型電子機器
JP6996214B2 (ja) 着用型生体情報計測装置および生体情報計測方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17862784

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2018546314

Country of ref document: JP

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 17862784

Country of ref document: EP

Kind code of ref document: A1