WO2018056551A1 - 인장강도가 개선된 친환경 자연분해 멀칭재 - Google Patents

인장강도가 개선된 친환경 자연분해 멀칭재 Download PDF

Info

Publication number
WO2018056551A1
WO2018056551A1 PCT/KR2017/006319 KR2017006319W WO2018056551A1 WO 2018056551 A1 WO2018056551 A1 WO 2018056551A1 KR 2017006319 W KR2017006319 W KR 2017006319W WO 2018056551 A1 WO2018056551 A1 WO 2018056551A1
Authority
WO
WIPO (PCT)
Prior art keywords
natural
mulching material
tensile strength
weight
eco
Prior art date
Application number
PCT/KR2017/006319
Other languages
English (en)
French (fr)
Inventor
황영준
Original Assignee
황영준
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 황영준 filed Critical 황영준
Publication of WO2018056551A1 publication Critical patent/WO2018056551A1/ko

Abstract

본 발명은 종래 비닐 필름 또는 생분해성 필름을 소재로 한 멀칭재의 약한 강도(인장력) 문제점을 해소한 친환경 자연분해 멀칭재에 관한 것으로서, (A) 젤라틴 : PVA : 황촉규추출물을 3~7 : 10~15 : 0.2~1.5의 중량비로 포함하는 천연접착제 1중량부; 및 (B) 천연솜 : 천연레이온, 천연마 또는 그들의 혼합물인 섬유원료 : 코코넛피 및 아몬드피 또는 사탕수수 중에서 선택되는 하나 또는 둘 이상으로부터 추출한 천연섬유질을 15~29 : 12~22 : 7~13의 중량비로 포함하는 섬유질부 12~16중량부;를 포함하는 인장강도가 개선된 친환경 자연분해 멀칭재인 것을 특징으로 한다. 이상과 같은 본 발명에 의하면, 종래 생분해성 멀칭재보다 우수한 인장력을 가지게 되어 생산원가가 낮으면서도 생산공정이나 사용현장에서 비닐 필름 멀칭재와 동일한 방식으로 취급할 수 있는 친환경 자연분해 멀칭재의 제공이 가능해진다.

Description

인장강도가 개선된 친환경 자연분해 멀칭재
본 발명은 친환경 자연분해 멀칭재에 관한 것으로서, 보다 상세하게는 종래 비닐 필름 또는 생분해성 필름을 소재로 한 멀칭재의 약한 강도(인장력) 문제점을 해소한 친환경 자연분해 멀칭재에 관한 것이다.
멀칭은 농작물을 재배할 때 경지토양의 표면을 덮어주는 것으로, 토양침식방지, 토양수분유지, 저온조절, 잡초억제, 토양오염방지 등의 목적으로 널리 활용되고 있다.
멀칭재로 초기에는 볏짚, 조릿짚, 목초 등과 같은 친환경 재료가 사용되었으나, 근래에는 가격이 저렴하고 설치작업이 간편한 합성수지(비닐) 필름이 주로 이용되고 있다. 그러나 이러한 비닐 필름 멀칭재는 설치가 간편하지만 생분해가 되지 않아 사용 후에 일일이 수거해야 하는데, 수거작업이 용이하지 않아 회수율이 낮고, 잔류하는 비닐에 의해 토양오염이 유발되는 문제가 있다.
이러한 비닐 필름 멀칭재에 의한 노동력 소요, 환경파괴 및 환경복구비용 등을 줄일 수 있는 두 가지 개념의 분해성 농업용 멀칭재가 알려져 있다.
먼저, 합성수지 원료를 베이스로 하고 생분해성 고분자를 첨가하여 필름의 형태가 용이하게 해체되도록 하는 유형의 멀칭재이다. 미국특허 제5,407,979호에는 알카노일 중합체, 에틸렌 중합체와 생분해성 고분자인 전분으로 구성된 분해 가능한 열가소성 필름이 개시되어 있다. 대한민국 등록특허 제10-0545271호는 스테아린산, 젖당, 에틸아세테이트, 가루우유 등을 LDPE(저밀도 폴리에틸렌), LLDPE(선형 저밀도 폴리에틸렌), HDPE(고밀도 폴리에틸렌), PSP(폴리스틸렌페이퍼)와 PP(폴리프로필렌) 등의 플라스틱 수지를 혼합가공 후 압출하는 분해성 멀칭재에 관한 것이다. 그러나 이들은 베이스폴리머로서 플라스틱 수지를 이용함으로써 필름의 형태가 해체되어 마치 "생분해성"인 것처럼 보이지만, 플라스틱 수지 재질의 미세 필름이 토양에 잔류함으로써 여전히 토양오염의 문제를 가지고 있다.
또다른 유형의 생분해성 멀칭재로서, 생분해가 가능한 천연물질을 원료로 하는 것이 있다. 대한민국 공개특허 제10-2004-0021196호에는 롤 형태의 재생지에 생분해성 수지를 용융 분사시켜 강도를 보강한 멀칭 매트가, 대한민국 공개특허 제10-2010-0116974호에는 노일(noil)과 텐셀 또는 레이온으로 이루어진 섬유원료에 식물성아교, 동물성아교, 색소, 촉매제, 타피오카가 함유된 생분해성 멀칭재가, 대한민국 등록특허 제10-1347898호에는 천연솜과, 천연레이온이나 천연마 또는 그들의 혼합물인 섬유원료와, 코코넛피나 아몬드피나 사탕수수 또는 대나무에서 추출한 천연섬유질과, 식물성아교 또는 동물성아교인 천연접착제를 포함하는 친환경 자연분해 멀칭재가 각각 개시되어 있다. 그러나 이들은 완전한 생분해가 가능하지만 경제성이 있는 범위에서는 인장강도가 낮아 제조 및 현장 취급 시에 불편함이 있어 널리 활용되지 못하고 있다.
예를 들면, 상기 등록특허 제10-1347898호는, 본 특허출원의 발명자들이 개발한 것인데, 경제성이 유지될 정도의 두께(80~100 ㎛)로 제조하여 현장에서 매우 우수한 결과를 보여주었다. 그러나 이렇게 제조된 멀칭재의 인장강도가 6.4~7.2㎏/㎟임에도 불구하고 여전히 다소 약하여 필름성형과정(펠트성형과정)에서 필름이 부분적으로 찢어지고 뒤틀리는 현상이 나타나는 문제가 있다. 또한 상기 등록특허 제10-1347898호에 의한 멀칭재는 멀칭재의 분해와 해체 시기를 조절하기 용이하지 아니하여 국내에서 적절한 유지기간인 3~4개월 내에 분해가 잘 이루어지지 않았다. 3~4개월 내에 충분히 분해되지 않으면 가을 농사를 위한 밭갈이를 할 때 트렉터나 경운기 바퀴에 잔류하는 멀칭재가 감겨서 작업이 불가능하게 되는 문제가 발생한다.
본 발명은 상기 등록특허 제10-1347898호를 개선하여 인장강도 강화 및 멀칭재 분해시기의 조절을 용이하게 할 목적으로 한 연구와 개발 결과 이루어진 것이다.
본 발명은, 기능을 다 한 후에 자연스럽게 분해되어 퇴비화될 수 있어 회수를 위한 노동력이 필요 없고 환경파괴 및 환경복구가 요구되지 않는 생분해성 친환경 멀칭재로서, 현장에서 이용할 때 종래 비닐 필름 재질의 멀칭재와 유사한 정도의 인장강도를 갖고 분해속도가 개선된 친환경 자연분해 멀칭재를 제공하는 것을 목적으로 한다.
또한 본 발명은 멀칭재의 분해시점이 용이하게 제어될 수 있는 친환경 자연분해 멀칭재를 제공하는 것을 목적으로 한다.
전술한 목적을 달성하기 위한 본 발명은 (A) 젤라틴 : PVA : 황촉규추출물을 3~7 : 10~15 : 0.2~1.5의 중량비로 포함하는 천연접착제 1중량부; 및 (B) 천연솜 : 천연레이온, 천연마 또는 그들의 혼합물인 섬유원료 : 코코넛피 및 아몬드피 또는 사탕수수 중에서 선택되는 하나 또는 둘 이상으로부터 추출한 천연섬유질을 15~29 : 12~22 : 7~13의 중량비로 포함하는 섬유질부 12~ 16중량부;를 포함하는, 인장강도가 개선된 친환경 자연분해 멀칭재인 것을 특징으로 한다.
본 발명에서 상기 천연접착제는, 미역 추출물, 우뭇가사리 추출물, 다시마 추출물, 식물전분, 펄프분말, 콜라겐 및 카제인 중 어느 하나 이상을 추가로 포함할 수 있다.
본 발명에 의한 멀칭재는, 천연접착제 1 중량부에 대해 색소 0.03~0.15 중량부를 추가로 포함하는 것이 좋다. 이때 색소로는 숯가루, 오징어먹물, 참숯액, 동물의 피 및 조개류의 분비물에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있다. 제조공정상 이들 색소는 상기 천연접착제와 혼합하는 방식으로 사전에 준비되는 것이 바람직하다.
또한 본 발명에 의한 멀칭재는, 천연접착제 1 중량부에 대해 첨가제 0.05~1 중량부를 추가로 포함할 수 있다. 첨가제로는 화산석, 제올라이트, 규산염, 수용성규산, 천연조개가루 및 운모에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있다. 제조공정상 이들 첨가제는 상기 천연접착제와 혼합하는 방식으로 사전에 준비되는 것이 바람직하다.
이상과 같은 본 발명에 의하면, 종래 생분해성 멀칭재보다 우수한 인장력을 가지게 되어 생산원가가 낮으면서도 생산공정이나 사용현장에서 비닐 필름 멀칭재와 동일한 방식으로 취급할 수 있는 친환경 자연분해 멀칭재의 제공이 가능해진다.
또한 본 발명의 멀칭재에 의하면, 모두 자연분해 가능한 천연의 원료로만 제조되므로 통기성이 우수하며, 토양미생물에 의하여 자연분해됨으로써 사용 후 수거할 필요가 없어 인력절감의 효과가 있다. 또한 태양광의 투과를 막아 잡초의 발아 및 생장을 억제하고, 분해과정에서 유용미생물의 먹이가 되며, 자연생태계 질서회복과 유용미생물의 생장으로 인한 좋은 발효퇴비 원료가 될 수 있는 효과가 있다.
도 1은 본 발명에 의한 친환경 자연분해 멀칭재의 제조공정의 예시적 흐름도.
도 2는 실시예에서 제조된 본 발명에 의한 친환경 자연분해 멀칭재의 적용사례를 보여주는 사진.
도 3~6은 각각 실시예에서 제조된 본 발명에 의한 친환경 자연분해 멀칭재의 적용 직후 및 20일, 60일, 90일 후의 상태를 보여주는 사진.
도 7은 각각 실시예에서 제조된 본 발명에 의한 친환경 자연분해 멀칭재의 적용 110일 전후의 상태를 보여주는 사진.
이하 첨부된 도면을 참조하여 본 발명을 보다 상세히 설명한다. 그러나 첨부된 도면은 본 발명의 기술적 사상의 내용과 범위를 쉽게 설명하기 위한 예시일 뿐, 이에 의해 본 발명의 기술적 범위가 한정되거나 변경되는 것은 아니다. 이러한 예시에 기초하여 본 발명의 기술적 사상의 범위 안에서 다양한 변형과 변경이 가능함은 당업자에게는 당연할 것이다.
전술하였듯이 본 발명은, 젤라틴, PVA 및 황촉규추출물을 포함하는 천연접착제와, 천연솜, 천연레이온, 천연마 또는 그들의 혼합물인 섬유원료, 코코넛피 및 아몬드피 또는 사탕수수 중에서 선택되는 하나 또는 둘 이상으로부터 추출한 천연섬유질을 포함하는 섬유질부를 포함하여 이루어진 인장강도가 개선된 친환경 자연분해 멀칭재에 관한 것이다.
본 발명자들이 다양한 원료 성분과 비율로 자연분해 멀칭재를 제작하고 테스트 한 결과, 인장강도가 충분하게 개선되면서도 필드에서 적절한 시점에 분해될 수 있도록 하기 위해서는 위에서 설명한 것과 같이 베이스가 되는 섬유질부의 성분과 그 첨가량을 제어하는 것보다, 천연접착제의 성분 및 첨가량이 매우 중요함을 확인하였다.
이에 본 발명들은 ① 멀칭재의 인장강도 개선 ② 멀칭재 분해 시점의 제어 ③ 경제적인 멀칭재의 제공 및 ④ 색소나 첨가제의 누출없는 안정적 유지라는 조건을 만족시키기 위해 다양한 천연접착제를 탐색한 바, 젤라틴과 PVA와 황촉규추출물을 주재료로 하는 천연접착제를 도출하였다.
본 발명에서 상기 천연접착제는 젤라틴 : PVA : 황촉규추출물을 3~7 : 10~15 : 0.2~1.5의 중량비로 포함한다.
젤라틴은 동물의 껍질, 힘줄, 연골 등을 구성하는 천연단백질인 콜라겐에서 추출하여 얻어지는 유도 단백질의 일종으로써, 소나 돼지껍데기 등을 알칼리 또는 산 처리 후 열탕에서 끓여서 추출한 것이다. 본 발명에서 사용되는 젤라틴은 직접적으로 섭취하는 식용이 아니므로 유독유해성분이 없는 정도로만 정제된 젤라틴을 사용하면 된다. 젤라틴을 상기 범위보다 적게 사용하면 최종 멀칭재의 인장강도가 개선되지 않으며, 그보다 많이 사용하면 멀칭재가 너무 뻣뻣해져서 사용상에 문제가 된다.
PVA(폴리비닐 알코올)는 필름 형성, 에멀전, 접착 특성이 뛰어난 것으로 알려진 생분해성이 있으면서 수용성인 중합체이다. 본 발명에서 PVA를 상기 범위보다 조금 사용하면 멀칭재 필름의 성형이 용이하지 아니하며, 그보다 많이 사용하면 필드에서 너무 빨리 분해되어 멀칭효과가 감소되었다.
젤라틴과 PVA의 혼합물에 대한 테스트 결과 PVA를 상기 첨가량 기준으로 12 중량비 이상 첨가하는 경우에는 젤라틴을 7 중량비까지 첨가하면 제작된 멀칭재의 전체적인 인장강도는 유지되지만 유연성이 감소되어 멀칭재를 다루면서 굽힐 때 미세하게 크렉이 발생하였다. 이에 다양한 대안을 모색한 바, 황촉규추출물을 소량 첨가함으로써 크렉 문제를 해결하였다.
황촉규는 무궁화과에 속한 일년생 초본으로서 그 뿌리는 점액질이 풍부하여 그 추출물은 예를 들면 한지 공업에서 점활제(粘滑劑)로 많이 이용되고 있다. 황촉규추출물을 상기 범위보다 적게 사용하면 크렉 발생을 막지 못하며, 그 범위보다 많이 사용해도 크렉 방지효과가 증가하지 않는다.
아래 실시예에서 간단히 언급되듯이, 본 발명에 의한 멀칭재 제조 시에 천연접착제는 물에 용해된 '접착액' 상태로 제조에 이용되었다가 건조단계에서 물이 제거된다. 이때 접착액의 유동성을 확보하고 접착액의 접착력과 내구성이 향상될 수 있도록 상기 천연접착제에 미역 추출물, 우뭇가사리 추출물, 다시마 추출물, 식물전분, 펄프분말, 콜라겐 및 카제인 중 어느 하나 이상을 추가하는 것이 바람직하다. 하기 일 실시예에서는 다시마 추출물을 사용하였다.
본 발명에서 상기 섬유질부는, 천연솜 : 천연레이온, 천연마 또는 그들의 혼합물인 섬유원료 : 코코넛피 및 아몬드피 또는 사탕수수 중에서 선택되는 하나 또는 둘 이상으로부터 추출한 천연섬유질을 15~29 : 12~22 : 7~13의 중량비로 포함한다.
상기 천연솜은 토양에 유기물을 공급하면서 토양의 습도를 조절하는 역할을 하는 것으로, 양모, 거위털, 명주솜, 목화솜 등을 사용할 수 있으나 이에 제한되는 것은 아니다. 그러나 바람직하게는 목화솜을 사용하는 것이 토양에 많은 유기물을 공급할 수 있으며, 토양의 습도를 적절하게 조절할 수 있어 좋다.
천연솜은 상기 범위로 포함되어야 최종 생산되는 천연멀칭재의 형상이 제대로 이루어질 수 있으며, 공극성이 향상되어 토양의 호흡성을 향상시킬 수 있어 바람직하다.
상기 섬유원료로는 천연레이온, 천연마 또는 그들의 혼합물을 사용할 수 있다. 천연레이온으로는 비스코스레이온, 구리 암모늄레이온, 리오셀 및 아세트산섬유 등을, 천연마는 저마(Ramie: 모시), 아마(Linen, Flax), 대마(Hemp, 삼베), 황마(Jute), 마니라마 및 사이살마 등에서 선택되는 하나 또는 둘 이상의 혼합물을 사용할 수 있을 것이다.
본 발명에서 섬유원료는 상기의 범위로 포함하였을 경우 자외선 차단기능이 향상되고, 인장강도가 향상될 수 있어 좋다.
본 발명에서 상기 천연섬유질은 코코넛피 및 아몬드피 또는 사탕수수 중에서 선택되는 하나 또는 둘 이상으로부터 추출한 것인데, 이를 상기와 같은 범위로 포함함으로써 멀칭재가 자연분해 되기 쉽고, 인장강도가 향상된다.
본 발명에 의한 멀칭재에서 상기 천연접착제와 섬유질부의 중량비는 1 : 12~16인 것이 혼합물의 점성이 향상되어 유동성이 확보되어 작업이 용이해지고, 점착력을 증대시켜 섬유질부 성분들의 인장력과 탄성 등의 기계적 성질을 향상시킬 수 있다. 섬유질부가 상기 범위보다 적으면 멀칭재 제작은 용이하나 멀칭재의 유연성이 적어져서 필드에 설치하는데 어려움이 있으며, 상기 범위보다 많으면 멀칭재의 결합력이 떨어져 작은 습도와 우기에 흩어지기 쉬운 문제가 발생한다.
상기 색소로 숯가루, 오징어먹물, 참숯액, 동물의 피 및 조개류의 분비물에서 선택되는 어느 하나 또는 둘 이상의 혼합물을 사용할 수 있는데, 이때 발현되는 색은 검정색으로 자외선 및 직사광선으로부터 작물을 보호해 줄 수 있는 효과가 있다.
본 발명에서 첨가제로 화산석, 제올라이트, 규산염, 수용성규산, 천연조개가루 또는 운모 등에서 선택되는 어느 하나 또는 둘 이상의 혼합물을 포함할 수 있으며, 흡수력이 좋은 화산선 분말 또는 제올라이트 분말을 사용하면 오염물질을 흡착시킬 수 있어 지력을 향상시킬 수 있다. 또한 규산염을 첨가하게 되면 항균력이 향상되어 작물에 유해한 병원균을 억제하는 역할을 할 수 있다.
본 발명에 따른 친환경 자연분해 멀칭재는 멀칭재의 자연분해를 통한 잔여물질의 잔존을 없애 인력절감의 효과를 얻을 수 있고, 태양광의 투과를 막아 잡초의 발아 및 생장을 억제하고, 자연생태계 질서회복과 유용미생물의 생장으로 인한 좋은 발효퇴비 원료가 될 수 있는 효과가 있다.
[실시예]
(1) 천연접착제와 섬유질부의 준비
사전 테스트 결과 섬유질부의 성분비가 멀칭재의 인장강도 및 내구성(생분해 시점)에 미치는 영향은 천연접착제의 성분비에 비해 상대적으로 적은 것으로 파악되었다. 이에 섬유질부의 성분 및 비율은 천연솜 22, 섬유원료 17, 천연섬유질 10 중량부로 확정하였다. 천연접착제는, 아래 표와 같은 성분 및 비율(kg, 건조물 기준)을 물 1톤에 완전 혼합하여 용액화(이를 '접착액'이라 함)하였다. 천연접착제(물은 추후 건조에 의해 제거되므로 고려하지 않음) 1중량부에 섬유질부 14중량부가 혼합되도록 하였다.
사전 테스트에서 전술한 바와 같이 젤라틴 3~7 중량부 범위이지만 5 중량부가 최적인 것으로 확인되었기에 젤라틴 함량을 고정하였다.
황촉규추출물은 다음과 같은 방식으로 준비하였다. : 건조/세절된 황촉규 뿌리와 물을 1:3(중량비)로 혼합하고 실온에서 가끔 저어주면서 2일간 추출하고, 여과하여 황촉규 추출액을 얻었고, 추출액을 농축하거나 완전 건조하여 사용하였다. 완전 건조된 황촉규추출물의 수율은 대략 15% 정도였다. 황촉규추출물은 추출액이나 농축된 추출액이나 건조물을 사용할 수 있는데, 첨가량은 건조물 기준으로 계산하였다.
다시마 추출물은 다음과 같은 방식으로 준비하였다. : 건조/세절된 다시마와 물을 1:3(중량비)로 혼합하고 20분간 가열하고 여과하였다. 건조/세절된 다시마 1kg에서 추출한 다시마 추출물을 천연접착제 1톤에 첨가하는 비율이 되도록 하였다.
Figure PCTKR2017006319-appb-I000001
(2) 물성 측정용 멀칭재의 제조
상기 섬유질부 42g을 1m×1m 사각형 프레임 내에 고르게 펼쳐 펠트가 되도록 한 다음 상기 천연접착제(건조기준) 3g에 해당하는 접착액 약 130ml를 고르게 스프레이 하였다. 이를 편편한 판으로 살짝 눌러준 다음 충분히 건조시켰다. 이어서 90~100℃ 아이롱으로 양면을 고르게 정리하였다. 이는 [섬유펠트 형성 → 접착액 스프레이 → 롤링하여 표면정리 → 건조 → 열롤러 통과(아이러닝)]로 이루어지는 실제 멀칭재의 연속생산 공정의 단계와 동일하게 멀칭재를 수작업으로 제조하는 것이다.
(3) 제조된 멀칭재의 인장강도 측정
이렇게 제조된 멀칭재의 인장강도를 측정하여 아래 표에 나타내었다. 단위는 ㎏/mm2이다.
인장시험기를 사용하여 온도 23±2℃, 상대습도 50±2%인 상태에서 인장속도 10mm/분으로 측정을 행하였다.
Figure PCTKR2017006319-appb-I000002
실시예에 의해 제조된 멀칭재들은 인장강도가 6.8~7.7로서 제조공정과 현장(밭)에 적용할 때 문제가 없을 정도의 충분한 인장력을 가짐을 알 수 있다.
(4) 제조된 멀칭재의 분해성 측정
실시예2에 의해 제조된 멀칭재를 실제 밭에 적용하고, 분해 특성을 확인하였다(도 2~7).
5월초에 충청남도 공주시의 밭과 논에 멀칭재를 도포하고 통상의 방법으로 고추모종, 콩 및 벼를 이식한 후 시간 경과에 따른 멀칭재의 상태를 관찰하였다. 도 3~6은 각각 실시예에서 제조된 본 발명에 의한 친환경 자연분해 멀칭재의 적용 직후(도 3) 및 20일, 60일, 90일 후의 상태를 보여주는 사진이며, 도 7은 110일 전후의 상태를 보여주는 사진이다.
멀칭재의 분해정도는 본 발명자의 시각과 촉각에 의해 결정하여 아래 표에 나타내었다.
Figure PCTKR2017006319-appb-I000003
표와 사진에서 볼 수 있듯이, 본 발명에 의한 멀칭재를 밭에 적용한 후 90일 정도가 경과되면 90% 정도 분해가 완료되었으며, 100~120일 이후에는 밭이나 논에 거뭇거뭇한 부분적인 흔적만이 남아 있었다(도 7 참조).
따라서 본 발명에 의하면 원하는 시간 내에 멀칭재가 충분히 분해되는 것을 확인하였다.

Claims (6)

  1. (A) 젤라틴 : PVA : 황촉규추출물을 3~7 : 10~15 : 0.2~1.5의 중량비로 포함하는 천연접착제 1중량부; 및
    (B) 천연솜 : 천연레이온, 천연마 또는 그들의 혼합물인 섬유원료 : 코코넛피 및 아몬드피 또는 사탕수수 중에서 선택되는 하나 또는 둘 이상으로부터 추출한 천연섬유질을 15~29 : 12~22 : 7~13의 중량비로 포함하는 섬유질부 12~16중량부;
    를 포함하는 것을 특징으로 하는 인장강도가 개선된 친환경 자연분해 멀칭재.
  2. 제 1 항에 있어서,
    상기 천연접착제는,
    미역 추출물, 우뭇가사리 추출물, 다시마 추출물, 식물전분, 펄프분말, 콜라겐 및 카제인 중 어느 하나 이상을 추가로 포함하는 것을 특징으로 하는 인장강도가 개선된 친환경 자연분해 멀칭재.
  3. 제 1 항 또는 제 2 항에 있어서,
    천연접착제 1 중량부에 대해 색소 0.03~0.15 중량부를 추가로 포함하는 것을 특징으로 하는 인장강도가 개선된 친환경 자연분해 멀칭재.
  4. 제 3 항에 있어서,
    상기 색소는 숯가루, 오징어먹물, 참숯액, 동물의 피 및 조개류의 분비물에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 것을 특징으로 하는 인장강도가 개선된 친환경 자연분해 멀칭재.
  5. 제 1 항 또는 제 2 항에 있어서,
    천연접착제 1 중량부에 대해 첨가제 0.05~1 중량부를 추가로 포함하는 것을 특징으로 하는 인장강도가 개선된 친환경 자연분해 멀칭재.
  6. 제 5 항에 있어서,
    상기 첨가제는 화산석, 제올라이트, 규산염, 수용성규산, 천연조개가루 및 운모에서 선택되는 하나 또는 둘 이상의 혼합물인 것을 특징으로 하는 인장강도가 개선된 친환경 자연분해 멀칭재.
PCT/KR2017/006319 2016-09-20 2017-06-16 인장강도가 개선된 친환경 자연분해 멀칭재 WO2018056551A1 (ko)