WO2018012390A1 - 位相差フィルム、楕円偏光板及びそれを用いた表示装置 - Google Patents

位相差フィルム、楕円偏光板及びそれを用いた表示装置 Download PDF

Info

Publication number
WO2018012390A1
WO2018012390A1 PCT/JP2017/024776 JP2017024776W WO2018012390A1 WO 2018012390 A1 WO2018012390 A1 WO 2018012390A1 JP 2017024776 W JP2017024776 W JP 2017024776W WO 2018012390 A1 WO2018012390 A1 WO 2018012390A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
oco
coo
formula
carbon atoms
Prior art date
Application number
PCT/JP2017/024776
Other languages
English (en)
French (fr)
Inventor
浩一 延藤
一輝 初阪
美花 高崎
Original Assignee
Dic株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dic株式会社 filed Critical Dic株式会社
Priority to JP2018527556A priority Critical patent/JPWO2018012390A1/ja
Priority to US16/317,909 priority patent/US20210284766A1/en
Priority to KR1020197001365A priority patent/KR20190018705A/ko
Publication of WO2018012390A1 publication Critical patent/WO2018012390A1/ja

Abstract

［課題］　本発明が解決しようとする課題は、フィルム１枚で反射防止機能に優れる位相差フィルムを提供すると共に、高温状態にさらされた後でもその機能を維持し続ける位相差フィルムを提供することであり、更にこれらの位相差位相差フィルムを用いた楕円偏光板、表示装置を提供することにある。 ［解決手段］　本発明は、位相差層を有する位相差フィルムであって、該光学フィルムが（式１－１）を満たし、 Ｒｅ（４５０）／Ｒｅ（５５０）＜１　（式１－１） （該位相差層を形成する材料が少なくとも１種類以上の一般式（１）～（７）からなる群から選ばれる重合性液晶性化合物を含有する重合性組成物であり、該位相差層がハイブリッド構造をとることを特徴とする位相差フィルムを提供する。

Description

位相差フィルム、楕円偏光板及びそれを用いた表示装置
　従来、１枚の位相差板からなる１／４波長板は、１／４波長の位相差を与える波長が特定の波長に限られるため、ディスプレイ等の表面反射を抑制するための反射防止フィルタとして用いた場合、１／４波長の位相差を与える特定の波長付近以外の波長では十分な反射防止性能を得られず、ディスプレイ等が青、紫、赤等に着色して見える視認性の悪さが問題であった。
　この問題に対して、複数の位相差板をそれらの光軸が交差するように積層してなる位相差板が提案されている（特許文献１～３）。例えば、特許文献２によれば、波長４５０ｎｍにおける位相差Ｒｅ（４５０）と波長５５０ｎｍにおける位相差Ｒｅ（５５０）の比Ｒｅ（４５０）／Ｒｅ（５５０）で表される位相差比を用いて位相差板の波長特性を定義した場合、一方の位相差板の位相差比が１．１６であり、もう一方の位相差板の位相差比が１．０２５である２枚の位相差板を積層した位相差板において、良好な反射防止性能が得られたことが報告されている。また、特許文献３によれば、両方の位相差板の位相差比が１．００５である２枚の位相差板を積層した位相差板において、良好な反射防止性能が得られたことが報告されている。
　しかし、特許文献１～３の位相差板はいずれも、１／４波長の位相差を与える波長域の広さが不十分であり、また該位相差板に偏光板を積層して円偏光板を作成した場合、優れた反射防止性能を与える波長域の広さも不十分であることから、位相差板又は円偏光板を含むディスプレイ等の視認性の改善は不十分であった。具体的には、ディスプレイ等を斜めから観察した場合は防止しきれない僅かな反射光が必ず発生するが、その僅かな反射光が無彩色ではなく青、紫、赤等に着して見えてしまう問題があった。この着色は、観察者の周辺環境、特に、蛍光灯や太陽がディスプレイ等に青、紫、赤等に着色して映り込んでしまうことを意味し、ディスプレイ等の視認性の観点から極めて深刻な問題である。
　さらに、特許文献１～３のいずれも、膜厚が数十μｍである延伸フィルムを積層するため、積層した位相差板の厚さは１５０～２００μｍとなり、常に薄型化を要求されるディスプレイ等においては位相差板の厚さが厚過ぎるという問題があった。
　加えて、特許文献１～３のいずれも、遅相軸が延伸方向に固定されてしまう延伸フィルムを用いているため、位相差板の遅相軸と偏光板の透過軸が交差するように位相差板と偏光板を積層する工程において、生産効率の悪い枚葉方式を採用しなければならないという問題もあった。
　一方、特許文献４には広帯域の位相差板として有用である、逆波長分散特性を有する化合物を用いた位相差板が示されている。しかし、これだけでは斜めに入射する光に対しては補償しきれず、視野角特性が悪くなるという問題があった。
　なお、スマートフォン等に用いられるディスプレイの場合、高い信頼性が求められることが多く、高温放置後の光学特性の変化がほとんど無いことが求められている。
特開平１０－６８８１６号公報 特開平１０－９０５２１号公報 特開平１１－５２１３１号公報 特開２００２－２６７８３８号公報
　本発明が解決しようとする課題は、フィルム１枚で反射防止機能に優れる位相差フィルムを提供すると共に、高温状態にさらされた後でもその機能を維持し続ける位相差フィルムを提供することであり、更にこれらの位相差位相差フィルムを用いた楕円偏光板、表示装置を提供することにある。
　本発明は、上記課題を解決するために、鋭意研究を重ねた結果、本発明を提供するに至った。
　即ち本発明は、位相差層を有する位相差フィルムであって、該光学フィルムが（式１－１）を満たし、
Ｒｅ（４５０）／Ｒｅ（５５０）＜１　（式１－１）
（式中、Ｒｅ（４５０）は波長４５０ｎｍにおける面内の位相差を表し、Ｒｅ（５５０）は波長５５０ｎｍにおける面内の位相差を表す。）
該位相差層を形成する材料が少なくとも１種類以上の一般式（１）～（７）からなる群から選ばれる重合性液晶性化合物を含有する重合性組成物であり、該位相差層がハイブリッド構造をとることを特徴とする位相差フィルムを提供する。
　また併せて、当該位相差位相差フィルムを用いた楕円偏光板、表示素子、有機発光表示素子を提供することにある。
　本発明の位相差フィルムは反射防止機能に適した光学特性を有するため、各種表示装置の表面反射を抑えることができ、特に有機ＥＬディスプレイに用いると、優れた視認性を得ることができる。また、高温状態にさらされたとしてもその特性・機能を維持することができるため、屋外用途等の表示素子に最適である。
　以下に本発明による位相差フィルムの最良の形態について説明する。
　本発明の位相差フィルムは、逆波長分散特性を示す位相差フィルムであり（式１－１）を満たす。
　Ｒｅ（４５０ｎｍ）／Ｒｅ（５５０ｎｍ）＜１．０　（式１－１）
　（式中、Ｒｅ（４５０ｎｍ）は、本発明の位相差フィルムの４５０ｎｍの波長における面内位相差を表し、Ｒｅ（５５０ｎｍ）は、５５０ｎｍの波長における面内位相差を表す。）
より好ましくは、下記（式１－２）を満たすものであり、更により好ましくは下記（式１－３）を満たすものである。
　０．７＜Ｒｅ（４５０ｎｍ）／Ｒｅ（５５０ｎｍ）＜０．９　（式１－２）
　０．８＜Ｒｅ（４５０ｎｍ）／Ｒｅ（５５０ｎｍ）＜０．８７　（式１－３）
図１は、本発明のハイブリッド構造の配向状態、及びチルト角を示す概念図である。 図２も、本発明のハイブリッド構造の配向状態、及びチルト角を示す概念図であり、図１とは基板界面と空気界面とが逆になった構造である。 図３は、重合性液晶組成物中の液晶分子がツイスト角を有する場合、及びそのツイスト角を示す概念図であり、基板面内でねじれた構造を有する配向状態を示す。（液晶性化合物）　本位相差フィルムに使用される重合性組成物は、重合性液晶化合物を含有し、該重合性液晶化合物は一般式（１）～（７）からなる群から選ばれる。なお、本発明において、「液晶性化合物」とは、メソゲン性骨格を有する化合物を示すことを意図するものであり、化合物単独では、液晶性を示さなくてもよい。また、重合性とは紫外線等の光照射、あるいは加熱によって重合処理を行うことでポリマー化（フィルム化）することができることを意味する。また、一般式（１）～（７）の化合物は配向した場合、逆波長分散特性を示す化合物である。
Figure JPOXMLDOC01-appb-C000006
（式中、Ｐ１１～Ｐ７４は重合性基を表し、
Ｓ１１～Ｓ７２はスペーサー基を又は単結合を表すが、Ｓ１１～Ｓ７２が複数存在する場合それらは各々同一であっても異なっていても良く、
Ｘ１１～Ｘ７２は－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｘ１１～Ｘ７２が複数存在する場合それらは各々同一であっても異なっていても良く（ただし、各Ｐ－（Ｓ－Ｘ）－結合には－Ｏ－Ｏ－を含まない。）、
ＭＧ１１～ＭＧ７１は各々独立して式（ａ）を表し、
Figure JPOXMLDOC01-appb-C000007
（式中、
Ａ１１、Ａ１２は各々独立して１，４－フェニレン基、１，４－シクロヘキシレン基、ピリジン－２，５－ジイル基、ピリミジン－２，５－ジイル基、ナフタレン－２，６－ジイル基、ナフタレン－１，４－ジイル基、テトラヒドロナフタレン－２，６－ジイル基、デカヒドロナフタレン－２，６－ジイル基又は１，３－ジオキサン－２，５－ジイル基を表すが、これらの基は無置換又は１つ以上のＬ１によって置換されても良いが、Ａ１１及び／又はＡ１２が複数現れる場合は各々同一であっても異なっていても良く、
Ｚ１１及びＺ１２は各々独立して－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＣＨ２－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－、－Ｎ＝ＣＨ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｚ１１及び／又はＺ１２が複数現れる場合は各々同一であっても異なっていても良く、
Ｍは下記の式（Ｍ－１）から式（Ｍ－１１）
Figure JPOXMLDOC01-appb-C000008
から選ばれる基を表すが、これらの基は無置換又は１つ以上のＬ１によって置換されても良く、
Ｇは下記の式（Ｇ－１）から式（Ｇ－６）
Figure JPOXMLDOC01-appb-C000009
（式中、Ｒ３は水素原子、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、
Ｗ８１は少なくとも１つの芳香族基を有する、炭素原子数５から３０の基を表すが、当該基は無置換又は１つ以上のＬ１によって置換されても良く、
Ｗ８２は水素原子、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子及び／又は－ＯＨに置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－によって置換されても良く、若しくは、Ｗ８２はＷ８１と同様の意味を表しても良く、また、Ｗ８１及びＷ８２は互いに連結し同一の環構造を形成しても良く、若しくはＷ８２はＰ８－（Ｓ８－Ｘ８）ｊ－で表される基を表しても良く、Ｐ８は重合性基を表し、Ｓ８はスペーサー基又は単結合を表すが、Ｓ８が複数存在する場合それらは同一であっても異なっていても良く、Ｘ８は－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｘ８が複数存在する場合それらは同一であっても異なっていても良く（ただし、Ｐ８－（Ｓ８－Ｘ８）ｊ－には－Ｏ－Ｏ－結合を含まない。）、ｊは０から１０の整数を表し、
Ｗ８３及びＷ８４はそれぞれ独立してハロゲン原子、シアノ基、ヒドロキシ基、ニトロ基、カルボキシル基、カルバモイルオキシ基、アミノ基、スルファモイル基、少なくとも１つの芳香族基を有する炭素原子数５から３０の基、炭素原子数１から２０のアルキル基、炭素原子数３から２０のシクロアルキル基、炭素原子数２から２０のアルケニル基、炭素原子数３から２０のシクロアルケニル基、炭素原子数１から２０のアルコキシ基、炭素原子数２から２０のアシルオキシ基、炭素原子数２から２０の又は、アルキルカルボニルオキシ基を表すが、前記アルキル基、シクロアルキル基、アルケニル基、シクロアルケニル基、アルコキシ基、アシルオキシ基、アルキルカルボニルオキシ基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、但し、上記Ｍが式（Ｍ－１）～式（Ｍ－１０）から選択される場合Ｇは式（Ｇ－１）～式（Ｇ－５）から選択され、Ｍが式（Ｍ－１１）である場合Ｇは式（Ｇ－６）を表し、
Ｌ１はフッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、ニトロ基、イソシアノ基、アミノ基、ヒドロキシル基、メルカプト基、メチルアミノ基、ジメチルアミノ基、ジエチルアミノ基、ジイソプロピルアミノ基、トリメチルシリル基、ジメチルシリル基、チオイソシアノ基、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－から選択される基によって置換されても良いが、化合物内にＬ１が複数存在する場合それらは同一であっても異なっていても良く、
ｊ１１は１から５の整数、ｊ１２は１～５の整数を表すが、ｊ１１＋ｊ１２は２から５の整数を表す。）、Ｒ１１及びＲ３１は水素原子、フッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、シアノ基、ニトロ基、イソシアノ基、チオイソシアノ基、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、ｍ１１は０～８の整数を表し、ｍ２～ｍ７、ｎ２～ｎ７、ｌ４～ｌ６、ｋ６は各々独立して０から５の整数を表す。）
　一般式（１）から一般式（７）において、重合性基Ｐ１１～Ｐ７４は下記の式（Ｐ－１）から式（Ｐ－２０）
Figure JPOXMLDOC01-appb-C000010
から選ばれる基を表すことが好ましく、これらの重合性基はラジカル重合、ラジカル付加重合、カチオン重合及びアニオン重合により重合する。特に重合方法として紫外線重合を行う場合には、式（Ｐ－１）、式（Ｐ－２）、式（Ｐ－３）、式（Ｐ－４）、式（Ｐ－５）、式（Ｐ－７）、式（Ｐ－１１）、式（Ｐ－１３）、式（Ｐ－１５）又は式（Ｐ－１８）が好ましく、式（Ｐ－１）、式（Ｐ－２）、式（Ｐ－７）、式（Ｐ－１１）又は式（Ｐ－１３）がより好ましく、式（Ｐ－１）、式（Ｐ－２）又は式（Ｐ－３）がさらに好ましく、式（Ｐ－１）又は式（Ｐ－２）が特に好ましい。
　一般式（１）から一般式（７）において、Ｓ１１～Ｓ７２はスペーサー基又は単結合を表すが、Ｓ１１～Ｓ７２が複数存在する場合、それらは同一であっても異なっていても良い。また、スペーサー基としては、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－、－ＣＯＯ－、－ＯＣＯ－、－ＯＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＨ＝ＣＨ－、－Ｃ≡Ｃ－又は下記の式（Ｓ－１）
Figure JPOXMLDOC01-appb-C000011
に置き換えられても良い炭素原子数１から２０のアルキレン基を表すことが好ましい。Ｓは原料の入手容易さ及び合成の容易さの観点から複数存在する場合は各々同一であっても異なっていても良く、各々独立して、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－、－ＣＯＯ－、－ＯＣＯ－に置き換えられても良い炭素原子数１から１０のアルキレン基又は単結合を表すことがより好ましく、各々独立して炭素原子数１から１０のアルキレン基又は単結合を表すことがさらに好ましく、複数存在する場合は各々同一であっても異なっていても良く各々独立して炭素原子数１から８のアルキレン基を表すことが特に好ましい。
　一般式（１）から一般式（７）において、Ｘ１１～Ｘ７２は－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｘ１１～Ｘ７２が複数存在する場合それらは同一であっても異なっていても良い（ただし、Ｐ－（Ｓ－Ｘ）－結合には－Ｏ－Ｏ－を含まない。）。また、原料の入手容易さ及び合成の容易さの観点から、複数存在する場合は各々同一であっても異なっていても良く、各々独立して－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－又は単結合を表すことが好ましく、各々独立して－Ｏ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－又は単結合を表すことがより好ましく、複数存在する場合は各々同一であっても異なっていても良く、各々独立して－Ｏ－、－ＣＯＯ－、－ＯＣＯ－又は単結合を表すことが特に好ましい。
　一般式（１）から一般式（７）において、Ａ１１及びＡ１２は各々独立して１，４－フェニレン基、１，４－シクロヘキシレン基、ピリジン－２，５－ジイル基、ピリミジン－２，５－ジイル基、ナフタレン－２，６－ジイル基、ナフタレン－１，４－ジイル基、テトラヒドロナフタレン－２，６－ジイル基、デカヒドロナフタレン－２，６－ジイル基又は１，３－ジオキサン－２，５－ジイル基を表すが、これらの基は無置換であるか又は１つ以上のＬによって置換されても良いが、Ａ１１及び／又はＡ１２が複数現れる場合は各々同一であっても異なっていても良い。Ａ１１及びＡ１２は原料の入手容易さ及び合成の容易さの観点から各々独立して無置換又は１つ以上のＬ１によって置換されても良い１，４－フェニレン基、１，４－シクロへキシレン基又はナフタレン－２，６－ジイルを表すことが好ましく、各々独立して下記の式（Ａ－１）から式（Ａ－１１）
Figure JPOXMLDOC01-appb-C000012
から選ばれる基を表すことがより好ましく、各々独立して式（Ａ－１）から式（Ａ－８）から選ばれる基を表すことがさらに好ましく、各々独立して式（Ａ－１）から式（Ａ－４）から選ばれる基を表すことが特に好ましい。
　一般式（１）から一般式（７）において、Ｚ１１及びＺ１２は各々独立して－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＣＨ２－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＯＣＯ－ＮＨ－、－ＮＨ－ＣＯＯ－、－ＮＨ－ＣＯ－ＮＨ－、－ＮＨ－Ｏ－、－Ｏ－ＮＨ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－、－Ｎ＝ＣＨ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｚ１１及び／又はＺ１２が複数現れる場合は各々同一であっても異なっていても良い。Ｚ１１及びＺ１２は化合物の液晶性、原料の入手容易さ及び合成の容易さの観点から、各々独立して単結合、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＨ２ＣＨ２－、－ＣＦ２ＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すことが好ましく、各々独立して－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＣＨ２－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｃ≡Ｃ－又は単結合を表すことがより好ましく、各々独立して－ＣＨ２ＣＨ２－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－又は単結合を表すことがさらに好ましく、各々独立して－ＣＨ２ＣＨ２－、－ＣＯＯ－、－ＯＣＯ－又は単結合を表すことが特に好ましい。
　一般式（１）から一般式（７）において、Ｍは下記の式（Ｍ－１）から式（Ｍ－１１）
Figure JPOXMLDOC01-appb-C000013
から選ばれる基を表すが、これらの基は無置換又は１つ以上のＬ１によって置換されても良い。Ｍは原料の入手容易さ及び合成の容易さの観点から各々独立して無置換であるか又は１つ以上のＬ１によって置換されても良い式（Ｍ－１）又は式（Ｍ－２）若しくは無置換の式（Ｍ－３）から式（Ｍ－６）から選ばれる基を表すことが好ましく、無置換又は１つ以上のＬ１によって置換されても良い式（Ｍ－１）又は式（Ｍ－２）から選ばれる基を表すことがより好ましく、無置換の式（Ｍ－１）又は式（Ｍ－２）から選ばれる基を表すことが特に好ましい。
　一般式（１）から一般式（７）において、Ｒ１１及びＲ３１は水素原子、フッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、シアノ基、ニトロ基、イソシアノ基、チオイソシアノ基、又は、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良い炭素原子数１から２０の直鎖状又は分岐状アルキル基を表すが、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良い。Ｒ１は液晶性及び合成の容易さの観点から水素原子、フッ素原子、塩素原子、シアノ基、若しくは、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－、－ＣＯＯ－、－ＯＣＯ－、－Ｏ－ＣＯ－Ｏ－によって置換されても良い炭素原子数１から１２の直鎖又は分岐アルキル基を表すことが好ましく、水素原子、フッ素原子、塩素原子、シアノ基、若しくは、炭素原子数１から１２の直鎖アルキル基又は直鎖アルコキシ基を表すことがより好ましく、炭素原子数１から１２の直鎖アルキル基又は直鎖アルコキシ基を表すことが特に好ましい。
　一般式（１）から一般式（７）において、Ｇは式（Ｇ－１）から式（Ｇ－６）から選ばれる基を表す。
Figure JPOXMLDOC01-appb-C000014
　式中、Ｒ３は水素原子、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、
Ｗ８１は少なくとも１つの芳香族基を有する、炭素原子数５から３０の基を表すが、当該基は無置換であるか又は１つ以上のＬ１によって置換されても良く、
Ｗ８２は、水素原子、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－によって置換されても良く、若しくは、Ｗ８２はＷ８１と同様の意味を表しても良く、また、Ｗ８１及びＷ８２は一緒になって環構造を形成しても良い。
　Ｗ８１に含まれる芳香族基は芳香族炭化水素基又は芳香族複素基であっても良く、両方を含んでいても良い。これらの芳香族基は単結合又は連結基（－ＯＣＯ－、－ＣＯＯ－、－ＣＯ－、－Ｏ－）を介して結合していても良く、縮合環を形成しても良い。また、Ｗ８１は芳香族基に加えて芳香族基以外の非環式構造及び／又は環式構造を含んでいても良い。Ｗ８１に含まれる芳香族基は原料の入手容易さ及び合成の容易さの観点から、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１）から式（Ｗ－１９）
Figure JPOXMLDOC01-appb-C000015
（式中、これらの基は任意の位置に結合手を有していて良く、これらの基から選ばれる２つ以上の芳香族基を単結合で連結した基を形成しても良く、Ｑ１は－Ｏ－、－Ｓ－、－ＮＲ４－（式中、Ｒ４は水素原子又は炭素原子数１から８のアルキル基を表す。）又は－ＣＯ－を表す。これらの芳香族基中の－ＣＨ＝は各々独立して－Ｎ＝に置き換えられても良く、－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＮＲ４－（式中、Ｒ４は水素原子又は炭素原子数１から８のアルキル基を表す。）又は－ＣＯ－に置き換えられても良いが、－Ｏ－Ｏ－結合を含まない。式（Ｗ－１）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１－１）から式（Ｗ－１－８）
Figure JPOXMLDOC01-appb-C000016
（式中、これらの基は任意の位置に結合手を有していて良い。）から選ばれる基を表すことが好ましく、式（Ｗ－７）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－７－１）から式（Ｗ－７－７）
Figure JPOXMLDOC01-appb-C000017
（式中、これらの基は任意の位置に結合手を有していて良い。）から選ばれる基を表すことが好ましく、式（Ｗ－１０）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１０－１）から式（Ｗ－１０－８）
Figure JPOXMLDOC01-appb-C000018
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表す。）から選ばれる基を表すことが好ましく、式（Ｗ－１１）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１１－１）から式（Ｗ－１１－１３）
Figure JPOXMLDOC01-appb-C000019
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表す。）から選ばれる基を表すことが好ましく、式（Ｗ－１２）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１２－１）から式（Ｗ－１２－１９）
Figure JPOXMLDOC01-appb-C000020
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表すが、Ｒ６が複数存在する場合それぞれ同一であっても、異なっていてもよい。）から選ばれる基を表すことが好ましく、式（Ｗ－１３）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１３－１）から式（Ｗ－１３－１０）
Figure JPOXMLDOC01-appb-C000021
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表すが、Ｒ６が複数存在する場合それぞれ同一であっても、異なっていてもよい。）から選ばれる基を表すことが好ましく、式（Ｗ－１４）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１４－１）から式（Ｗ－１４－４）
Figure JPOXMLDOC01-appb-C000022
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表す。）から選ばれる基を表すことが好ましく、式（Ｗ－１５）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１５－１）から式（Ｗ－１５－１８）
Figure JPOXMLDOC01-appb-C000023
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表す。）から選ばれる基を表すことが好ましく、式（Ｗ－１６）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１６－１）から式（Ｗ－１６－４）
Figure JPOXMLDOC01-appb-C000024
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表す。）から選ばれる基を表すことが好ましく、式（Ｗ－１７）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１７－１）から式（Ｗ－１７－６）
Figure JPOXMLDOC01-appb-C000025
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表す。）から選ばれる基を表すことが好ましく、式（Ｗ－１８）で表される基としては、無置換又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１８－１）から式（Ｗ－１８－６）
Figure JPOXMLDOC01-appb-C000026
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表すが、Ｒ６が複数存在する場合それぞれ同一であっても、異なっていてもよい。）から選ばれる基を表すことが好ましく、式（Ｗ－１９）で表される基としては、無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－１９－１）から式（Ｗ－１９－９）
Figure JPOXMLDOC01-appb-C000027
（式中、これらの基は任意の位置に結合手を有していて良く、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表すが、Ｒ６が複数存在する場合それぞれ同一であっても、異なっていてもよい。）から選ばれる基を表すことが好ましい。Ｗ８１に含まれる芳香族基は、無置換であるか又は１つ以上のＬ１によって置換されても良い式（Ｗ－１－１）、式（Ｗ－７－１）、式（Ｗ－７－２）、式（Ｗ－７－７）、式（Ｗ－８）、式（Ｗ－１０－６）、式（Ｗ－１０－７）、式（Ｗ－１０－８）、式（Ｗ－１１－８）、式（Ｗ－１１－９）、式（Ｗ－１１－１０）、式（Ｗ－１１－１１）、式（Ｗ－１１－１２）又は式（Ｗ－１１－１３）から選ばれる基を表すことがより好ましく、無置換であるか又は１つ以上のＬ１によって置換されても良い式（Ｗ－１－１）、式（Ｗ－７－１）、式（Ｗ－７－２）、式（Ｗ－７－７）、式（Ｗ－１０－６）、式（Ｗ－１０－７）又は式（Ｗ－１０－８）から選ばれる基を表すことが特に好ましい。さらに、Ｗ８１は下記の式（Ｗ－ａ－１）から式（Ｗ－ａ－６）
Figure JPOXMLDOC01-appb-C000028
（式中、ｒは０から５の整数を表し、ｓは０から４の整数を表し、ｔは０から３の整数を表す。）から選ばれる基を表すことが特に好ましい。
　原料の入手容易さ及び合成の容易さの観点から、Ｗ８２は水素原子、又は、基中の任意の水素原子がフッ素原子及び／又は－ＯＨに置換されても良く、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－によって置換されても良い炭素原子数１から２０の直鎖状又は分岐状アルキル基、若しくは、Ｐ８－（Ｓ８－Ｘ８）ｊ－で表される基を表すことがより好ましく、Ｗ８２は水素原子、又は、基中の任意の水素原子がフッ素原子に置換されても良く、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－によって置換されても良い炭素原子数１から２０の直鎖状又は分岐状アルキル基、若しくは、Ｐ８－（Ｓ８－Ｘ８）ｊ－で表される基を表すことがさらに好ましく、Ｗ８２は水素原子、又は、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－によって置換されても良い炭素原子数１から１２の直鎖状アルキル基、若しくは、Ｐ８－（Ｓ８－Ｘ８）ｊ－で表される基を表すことがさらにより好ましく、Ｗ８２は水素原子、又は、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－によって置換されている炭素原子数１から１２の直鎖状アルキル基、若しくは、Ｐ８－（Ｓ８－Ｘ８）ｊ－で表される基を表すことがさらにより好ましい。
　また、Ｗ８２が少なくとも１つの芳香族基を有する炭素原子数２から３０の基を表す場合、Ｗ８２は上記の式（Ｗ－１）から式（Ｗ－１８）から選ばれる基を表すことが好ましい。その場合、より好ましい構造としては上記と同様である。
　また、Ｗ８２がＰ８－（Ｓ８－Ｘ８）ｊ－で表される基を表す場合、Ｐ８、Ｓ８、Ｘ８、で表される基の好ましい構造は、それぞれ、上記Ｐ１１～Ｐ７４、上記Ｓ１１～Ｓ７２、上記Ｘ１１～Ｘ７２で表される基の好ましい構造と同様である。さらに、ｊは、０～３の整数が好ましく、０又は１がより好ましい。
　また、Ｗ８２の末端基はＯＨ基でも良い。
　また、Ｗ８１及びＷ８２が一緒になって環構造を形成する場合、－ＮＷ８１Ｗ８２で表される環状基は無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－ｂ－１）から式（Ｗ－ｂ－４２）
Figure JPOXMLDOC01-appb-C000029
Figure JPOXMLDOC01-appb-C000030
（式中、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表す。）から選ばれる基を表すことが好ましく、原料の入手容易さ及び合成の容易さの観点から、無置換又は１つ以上のＬ１によって置換されても良い式（Ｗ－ｂ－２０）、式（Ｗ－ｂ－２１）、式（Ｗ－ｂ－２２）、式（Ｗ－ｂ－２３）、式（Ｗ－ｂ－２４）、式（Ｗ－ｂ－２５）又は式（Ｗ－ｂ－３３）から選ばれる基を表すことが特に好ましい。
　また、＝ＣＷ８１Ｗ８２で表される環状基は無置換であるか又は１つ以上のＬ１によって置換されても良い下記の式（Ｗ－ｃ－１）から式（Ｗ－ｃ－８１）
Figure JPOXMLDOC01-appb-C000031
Figure JPOXMLDOC01-appb-C000032
Figure JPOXMLDOC01-appb-C000033
（式中、Ｒ６は水素原子又は炭素原子数１から８のアルキル基を表すが、Ｒ６が複数存在する場合それぞれ同一であっても、異なっていてもよい。）から選ばれる基を表すことが好ましく、原料の入手容易さ及び合成の容易さの観点から、無置換又は１つ以上のＬによって置換されても良い式（Ｗ－ｃ－１１）、式（Ｗ－ｃ－１２）、式（Ｗ－ｃ－１３）、式（Ｗ－ｃ－１４）、式（Ｗ－ｃ－５３）、式（Ｗ－ｃ－５４）、式（Ｗ－ｃ－５５）、式（Ｗ－ｃ－５６）、式（Ｗ－ｃ－５７）又は式（Ｗ－ｃ－７８）から選ばれる基を表すことが特に好ましい。
　Ｗ８１及びＷ８２に含まれるπ電子の総数は、波長分散特性、保存安定性、液晶性及び合成の容易さの観点から４から２４であることが好ましい。Ｗ８３、Ｗ８４はそれぞれ独立してハロゲン原子、シアノ基、ヒドロキシ基、ニトロ基、カルボキシル基、カルバモイルオキシ基、アミノ基、スルファモイル基、少なくとも１つの芳香族基を有する炭素原子数５から３０の基、炭素原子数１から２０のアルキル基、炭素原子数３から２０のシクロアルキル基、炭素原子数２から２０のアルケニル基、炭素原子数３から２０のシクロアルケニル基、炭素原子数１から２０のアルコキシ基、炭素原子数２から２０のアシルオキシ基、炭素原子数２から２０の又は、アルキルカルボニルオキシ基を表すが、前記アルキル基、シクロアルキル基、アルケニル基、シクロアルケニル基、アルコキシ基、アシルオキシ基、アルキルカルボニルオキシ基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、Ｗ８３はシアノ基、ニトロ基、カルボキシル基、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換された、炭素原子数１から２０のアルキル基、アルケニル基、アシルオキシ基、アルキルカルボニルオキシ基から選択される基がより好ましく、シアノ基、カルボキシル基、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換された、炭素原子数１から２０のアルキル基、アルケニル基、アシルオキシ基、アルキルカルボニルオキシ基で選択される基が特に好ましく、Ｗ８４はシアノ基、ニトロ基、カルボキシル基、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換された、炭素原子数１から２０のアルキル基、アルケニル基、アシルオキシ基、アルキルカルボニルオキシ基から選択される基がより好ましく、シアノ基、カルボキシル基、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換された、炭素原子数１から２０のアルキル基、アルケニル基、アシルオキシ基、アルキルカルボニルオキシ基で選択される基で選択される基が特に好ましい。
　Ｌ１はフッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、ニトロ基、イソシアノ基、アミノ基、ヒドロキシル基、メルカプト基、メチルアミノ基、ジメチルアミノ基、ジエチルアミノ基、ジイソプロピルアミノ基、トリメチルシリル基、ジメチルシリル基、チオイソシアノ基、又は、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－によって置換されても良い炭素原子数１から２０の直鎖状又は分岐状アルキル基を表すが、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良い。液晶性、合成の容易さの観点から、Ｌ１はフッ素原子、塩素原子、ペンタフルオロスルフラニル基、ニトロ基、メチルアミノ基、ジメチルアミノ基、ジエチルアミノ基、ジイソプロピルアミノ基、又は、任意の水素原子はフッ素原子に置換されても良く、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－から選択される基によって置換されても良い炭素原子数１から２０の直鎖状又は分岐状アルキル基を表すことが好ましく、フッ素原子、塩素原子、又は、任意の水素原子はフッ素原子に置換されても良く、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－ＣＯＯ－又は－ＯＣＯ－から選択される基によって置換されても良い炭素原子数１から１２の直鎖状又は分岐状アルキル基を表すことがより好ましく、フッ素原子、塩素原子、又は、任意の水素原子はフッ素原子に置換されても良い炭素原子数１から１２の直鎖状又は分岐状アルキル基若しくはアルコキシ基を表すことがさらに好ましく、フッ素原子、塩素原子、又は、炭素原子数１から８の直鎖アルキル基若しくは直鎖アルコキシ基を表すことが特に好ましい。
　一般式（１）から一般式（７）において、ＭＧ１１からＭＧ７１に結合する各々の置換基は、上記一般式（ａ）のＡ１１及び／又はＡ１２に結合する。
　一般式（１）において、ｍ１１は０から８の整数を表すが、液晶性、原料の入手容易さ及び合成の容易さの観点から０から４の整数を表すことが好ましく、０から２の整数を表すことがより好ましく、０又は１を表すことがさらに好ましく、１を表すことが特に好ましい。
　一般式（２）から一般式（７）において、ｍ２～ｍ７、ｎ２～ｎ７、ｌ４～ｌ６、ｋ６は各々独立して０から５の整数を表すが、液晶性、原料の入手容易さ及び合成の容易さの観点から０から４の整数を表すことが好ましく、０から２の整数を表すことがより好ましく、０又は１を表すことがさらに好ましく、１を表すことが特に好ましい。
　一般式（ａ）において、ｊ１１及びｊ１２は各々独立して１から５の整数を表すが、ｊ１１＋ｊ１２は２から５の整数を表す。液晶性、合成の容易さ及び保存安定性の観点から、ｊ１１及びｊ１２は各々独立して１から４の整数を表すことが好ましく、１から３の整数を表すことがより好ましく、１又は２を表すことが特に好ましい。ｊ１１＋ｊ１２は２から４の整数を表すことが好ましい。
　一般式（１）で表される化合物として具体的には、下記の式（１－ａ－１）から式（１－ａ－９３）で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000034
Figure JPOXMLDOC01-appb-C000035
Figure JPOXMLDOC01-appb-C000036
Figure JPOXMLDOC01-appb-C000037
Figure JPOXMLDOC01-appb-C000038
Figure JPOXMLDOC01-appb-C000039
Figure JPOXMLDOC01-appb-C000040
Figure JPOXMLDOC01-appb-C000041
Figure JPOXMLDOC01-appb-C000042
Figure JPOXMLDOC01-appb-C000043
Figure JPOXMLDOC01-appb-C000044
Figure JPOXMLDOC01-appb-C000045
Figure JPOXMLDOC01-appb-C000046
Figure JPOXMLDOC01-appb-C000047
Figure JPOXMLDOC01-appb-C000048
Figure JPOXMLDOC01-appb-C000049
Figure JPOXMLDOC01-appb-C000050
Figure JPOXMLDOC01-appb-C000051
Figure JPOXMLDOC01-appb-C000052
Figure JPOXMLDOC01-appb-C000053
　これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
一般式（２）で表される化合物として具体的には、下記の式（２－ａ－１）から式（２－ａ－６８）で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000054
Figure JPOXMLDOC01-appb-C000055
Figure JPOXMLDOC01-appb-C000056
Figure JPOXMLDOC01-appb-C000057
Figure JPOXMLDOC01-appb-C000058
Figure JPOXMLDOC01-appb-C000059
Figure JPOXMLDOC01-appb-C000060
Figure JPOXMLDOC01-appb-C000061
Figure JPOXMLDOC01-appb-C000062
Figure JPOXMLDOC01-appb-C000063
Figure JPOXMLDOC01-appb-C000064
Figure JPOXMLDOC01-appb-C000065
Figure JPOXMLDOC01-appb-C000066
Figure JPOXMLDOC01-appb-C000067
Figure JPOXMLDOC01-appb-C000068
Figure JPOXMLDOC01-appb-C000069
（式中、ｎは１～１０の整数を表す。）これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
　なお、本発明の位相差層を有する位相差フィルムを得るためには、該位相差層を形成する材料として、上記一般式（２－ａ）で表される重合性液晶化合物を含有することが好ましい。特に、該位相差層を形成する材料中に含まれる重合性液晶性化合物の合計量のうち、５～１００質量％含有することが好ましく、１０～１００質量％含有することがより好ましく、１５～１００質量％含有することが特に好ましい。
　一般式（３）で表される化合物として具体的には、下記の式（３－ａ－１）から式（３－ａ－１７）で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000070
Figure JPOXMLDOC01-appb-C000071
Figure JPOXMLDOC01-appb-C000072
Figure JPOXMLDOC01-appb-C000073
　これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
　一般式（４）で表される化合物として具体的には、下記の式（４－ａ－１）から式（４－ａ－２６）で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000074
Figure JPOXMLDOC01-appb-C000075
Figure JPOXMLDOC01-appb-C000076
Figure JPOXMLDOC01-appb-C000077
Figure JPOXMLDOC01-appb-C000078
Figure JPOXMLDOC01-appb-C000079
Figure JPOXMLDOC01-appb-C000080
（式中、ｍ及びｎはそれぞれ独立して１～１０の整数を表す。）これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
　一般式（５）で表される化合物として具体的には、下記の式（５－ａ－１）から式（５－ａ－２９）で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000081
Figure JPOXMLDOC01-appb-C000082
Figure JPOXMLDOC01-appb-C000083
Figure JPOXMLDOC01-appb-C000084
Figure JPOXMLDOC01-appb-C000085
Figure JPOXMLDOC01-appb-C000086
Figure JPOXMLDOC01-appb-C000087
Figure JPOXMLDOC01-appb-C000088
Figure JPOXMLDOC01-appb-C000089
（式中、ｎは炭素原子数１～１０を示す。）これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
　一般式（６）で表される化合物として具体的には、下記の式（６－ａ－１）から式（６－ａ－２５）で表される化合物が好ましい
Figure JPOXMLDOC01-appb-C000090
Figure JPOXMLDOC01-appb-C000091
Figure JPOXMLDOC01-appb-C000092
Figure JPOXMLDOC01-appb-C000093
Figure JPOXMLDOC01-appb-C000094
Figure JPOXMLDOC01-appb-C000095
（式中、ｋ、ｌ、ｍ及びｎはそれぞれ独立して炭素原子数１～１０を表す。）
　これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
　一般式（７）で表される化合物として具体的には、下記の式（７－ａ－１）から式（７－ａ－２６）で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000096
Figure JPOXMLDOC01-appb-C000097
Figure JPOXMLDOC01-appb-C000098
Figure JPOXMLDOC01-appb-C000099
Figure JPOXMLDOC01-appb-C000100
Figure JPOXMLDOC01-appb-C000101
Figure JPOXMLDOC01-appb-C000102
　これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
　上記１つ以上の重合性基を有する液晶性化合物の合計含有量は、重合性組成物に用いる液晶性化合物の総量に対し、６０～１００質量％含有することが好ましく、６５～９８質量％含有することがより好ましく、７０～９５質量％含有することが特に好ましい。
　また、一般式（１）～（７）に示された、逆波長分散特性を示す化合物は「Ｔの字」の構造を持つ化合物であるが、他にも逆波長分散性を示す化合物は「十字」構造や、「Ｈの字」構造などが考えられているが、「Ｈの字」構造の化合物は本質的に耐熱性が劣り、「十字」構造の化合物で重合性官能基が２つのものは、化合物構造が持つ立体障害から架橋密度の高い重合物を得ることが難しく、耐熱性は劣ってしまう。
　耐熱性の観点からは、一般式（１）～（７）に示された化合物の中でも、重合性官能基の数が２つ以上の化合物を含有する組成物が好ましく、重合性官能基の数が３つ以上の化合物を含有するほうがより好ましい。一方液晶性の観点からは、一般式（１）又は（２）の化合物を含有する組成物が好ましい。耐熱性と液晶性両方の観点からは、一般式（２）の化合物で、Ｗ８２がＰ８－（Ｓ８－Ｘ８）ｊ－で表される基（Ｐ８、Ｓ８、Ｘ８、およびｊは前述と同じ意味を表す）を有する化合物がより好ましい。
　具体的には、上記式（２－ａ－４８）、（２－ａ－４９）、（２－ａ－５２）、（２－ａ－５６）、（２－ａ－６０）、（２－ａ－６８）で表される化合物が好ましい。
（その他の液晶性化合物）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、一般式（１）から一般式（７）の液晶性化合物以外にも、重合性基を１つ以上有する液晶性化合物を含有することができる。そのような液晶化合物として、一般式（１－ｂ）から一般式（７－ｂ）の液晶化合物が挙げられる。しかし、添加量が多すぎると、（数式１－１）の値が１をこえてしまうため、添加する場合は、重合性組成物に用いる重合性化合物の合計量に対して３０質量％以下とすることが好ましく、２０質量％以下がさらに好ましく、１０質量％以下が特に好ましい。
Figure JPOXMLDOC01-appb-C000103
（式中、Ｐ１１～Ｐ７４は重合性基を表し、Ｓ１１～Ｓ７２はスペーサー基を又は単結合を表すが、Ｓ１１～Ｓ７２が複数存在する場合それらは各々同一であっても異なっていても良く、Ｘ１１～Ｘ７２は－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｘ１１～Ｘ７２が複数存在する場合それらは各々同一であっても異なっていても良く（ただし、各Ｐ－（Ｓ－Ｘ）－結合には－Ｏ－Ｏ－を含まない。）、ＭＧ１１～ＭＧ７１は各々独立して式（ｂ）を表し、
Figure JPOXMLDOC01-appb-C000104
（式中、Ａ８３、Ａ８４は各々独立して１，４－フェニレン基、１，４－シクロヘキシレン基、ピリジン－２，５－ジイル基、ピリミジン－２，５－ジイル基、ナフタレン－２，６－ジイル基、ナフタレン－１，４－ジイル基、テトラヒドロナフタレン－２，６－ジイル基、デカヒドロナフタレン－２，６－ジイル基又は１，３－ジオキサン－２，５－ジイル基を表すが、これらの基は無置換又は１つ以上のＬ２によって置換されても良いが、Ａ８３及び／又はＡ８４が複数現れる場合は各々同一であっても異なっていても良く、
Ｚ８３及びＺ８４は各々独立して－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＣＨ２－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－、－Ｎ＝ＣＨ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｚ８３及び／又はＺ８４が複数現れる場合は各々同一であっても異なっていても良く、
Ｍ８１は１，４－フェニレン基、１，４－シクロヘキシレン基、１，４－シクロヘキセニル基、テトラヒドロピラン－２，５－ジイル基、１，３－ジオキサン－２，５－ジイル基、テトラヒドロチオピラン－２，５－ジイル基、１，４－ビシクロ（２，２，２）オクチレン基、デカヒドロナフタレン－２，６－ジイル基、ピリジン－２，５－ジイル基、ピリミジン－２，５－ジイル基、ピラジン－２，５－ジイル基、チオフェン－２，５－ジイル基－、１，２，３，４－テトラヒドロナフタレン－２，６－ジイル基、ナフチレン－１，４－ジイル基、ナフチレン－１，５－ジイル基、ナフチレン－１，６－ジイル基、ナフチレン－２，６－ジイル基、フェナントレン－２，７－ジイル基、９，１０－ジヒドロフェナントレン－２，７－ジイル基、１，２，３，４，４ａ，９，１０ａ－オクタヒドロフェナントレン－２，７－ジイル基、ベンゾ［１，２－ｂ：４，５－ｂ‘］ジチオフェン－２，６－ジイル基、ベンゾ［１，２－ｂ：４，５－ｂ‘］ジセレノフェン－２，６－ジイル基、［１］ベンゾチエノ［３，２－ｂ］チオフェン－２，７－ジイル基、［１］ベンゾセレノフェノ［３，２－ｂ］セレノフェン－２，７－ジイル基、又はフルオレン－２，７－ジイル基から選ばれる基を表すが、これらの基は無置換又は１つ以上のＬ２によって置換されても良く、
Ｌ２はフッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、ニトロ基、イソシアノ基、アミノ基、ヒドロキシル基、メルカプト基、メチルアミノ基、ジメチルアミノ基、ジエチルアミノ基、ジイソプロピルアミノ基、トリメチルシリル基、ジメチルシリル基、チオイソシアノ基、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－から選択される基によって置換されても良いが、化合物内にＬ２が複数存在する場合それらは同一であっても異なっていても良く、ｍは０から８の整数を表し、ｊ８３及びｊ８４は各々独立して０から５の整数を表すが、ｊ８３＋ｊ８４は１から５の整数を表す。）、Ｒ１１及びＲ３１は水素原子、フッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、シアノ基、ニトロ基、イソシアノ基、チオイソシアノ基、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、ｍ１１は０～８の整数を表し、ｍ２～ｍ７、ｎ２～ｎ７、ｌ４～ｌ６、ｋ６は各々独立して０から５の整数を表す。但し、一般式（１）から一般式（７）を除く。）
一般式（１－ｂ）で表される化合物として具体的には、下記の式（１－ｂ－１）から式（１－ｂ－３９）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000105
Figure JPOXMLDOC01-appb-C000106
Figure JPOXMLDOC01-appb-C000107
Figure JPOXMLDOC01-appb-C000108
Figure JPOXMLDOC01-appb-C000109
（式中、ｍ１１、ｎ１１はそれぞれ独立して１～１０の整数を表し、Ｒ１１１及びＲ１１２は、それぞれ独立して水素原子、炭素原子数１～１０のアルキル基、又は、フッ素原子を表し、Ｒ１１３は水素原子、フッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、シアノ基、ニトロ基、イソシアノ基、チオイソシアノ基、又は、１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－が各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良い炭素原子数１から２０の直鎖状又は分岐状アルキル基を表すが、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良い。）これらの液晶化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
一般式（２－ｂ）で表される化合物として具体的には、下記の式（２－ｂ－１）から式（２－ｂ－３４）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000110
Figure JPOXMLDOC01-appb-C000111
Figure JPOXMLDOC01-appb-C000112
Figure JPOXMLDOC01-appb-C000113
Figure JPOXMLDOC01-appb-C000114
Figure JPOXMLDOC01-appb-C000115
（式中、ｍ及びｎはそれぞれ独立して１～１８の整数を表し、Ｒは水素原子、ハロゲン原子、炭素数１～６のアルキル基、炭素数１～６のアルコキシ基、シアノ基を示す。これらの基が炭素数１～６のアルキル基、あるいは炭素数１～６のアルコキシ基の場合、全部が未置換であるか、あるいは１つまたは２つ以上のハロゲン原子により置換されていてもよい。）これらの液晶化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
一般式（３－ｂ）で表される化合物として具体的には、下記の式（３－ｂ－１）から式（３－ｂ－１６）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000116
Figure JPOXMLDOC01-appb-C000117
Figure JPOXMLDOC01-appb-C000118
　これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
一般式（４－ｂ）で表される化合物として具体的には、下記の式（４－ｂ－１）から式（４－ｂ－２９）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000119
Figure JPOXMLDOC01-appb-C000120
Figure JPOXMLDOC01-appb-C000121
Figure JPOXMLDOC01-appb-C000122
Figure JPOXMLDOC01-appb-C000123
Figure JPOXMLDOC01-appb-C000124
（式中、ｍ及びｎはそれぞれ独立して１～１０の整数を表す。Ｒは水素原子、ハロゲン原子、炭素数１～６のアルキル基、炭素数１～６のアルコキシ基、シアノ基を示す。これらの基が炭素数１～６のアルキル基、あるいは炭素数１～６のアルコキシ基の場合、全部が未置換であるか、あるいは１つまたは２つ以上のハロゲン原子により置換されていてもよい。）これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
一般式（５－ｂ）で表される化合物として具体的には、下記の式（５－ｂ－１）から式（５－ｂ－２６）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000125
Figure JPOXMLDOC01-appb-C000126
Figure JPOXMLDOC01-appb-C000127
Figure JPOXMLDOC01-appb-C000128
Figure JPOXMLDOC01-appb-C000129
（式中、ｎはそれぞれ独立して１～１０の整数を表す。Ｒは水素原子、ハロゲン原子、炭素数１～６のアルキル基、炭素数１～６のアルコキシ基、シアノ基を示す。これらの基が炭素数１～６のアルキル基、あるいは炭素数１～６のアルコキシ基の場合、全部が未置換であるか、あるいは１つまたは２つ以上のハロゲン原子により置換されていてもよい。）これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
一般式（６－ｂ）で表される化合物として具体的には、下記の式（６－ｂ－１）から式（６－ｂ－２３）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000130
Figure JPOXMLDOC01-appb-C000131
Figure JPOXMLDOC01-appb-C000132
Figure JPOXMLDOC01-appb-C000133
Figure JPOXMLDOC01-appb-C000134
（式中、ｋ、ｌ、ｍ及びｎはそれぞれ独立して１～１０の整数を表す。Ｒは水素原子、ハロゲン原子、炭素数１～６のアルキル基、炭素数１～６のアルコキシ基、シアノ基を示す。これらの基が炭素数１～６のアルキル基、あるいは炭素数１～６のアルコキシ基の場合、全部が未置換であるか、あるいは１つまたは２つ以上のハロゲン原子により置換されていてもよい。）
　これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
　一般式（７－ｂ）で表される化合物として具体的には、下記の式（７－ｂ－１）から式（７－ｂ－２５）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000135
Figure JPOXMLDOC01-appb-C000136
Figure JPOXMLDOC01-appb-C000137
Figure JPOXMLDOC01-appb-C000138
（式中、Ｒは水素原子、ハロゲン原子、炭素数１～６のアルキル基、炭素数１～６のアルコキシ基、シアノ基を示す。これらの基が炭素数１～６のアルキル基、あるいは炭素数１～６のアルコキシ基の場合、全部が未置換であるか、あるいは１つまたは２つ以上のハロゲン原子により置換されていてもよい。）これらの液晶性化合物は、単独で使用することもできるし、２種類以上混合して使用することもできる。
　上記一般式（１）～（７）、および一般式（１－ｂ）～（７－ｂ）の中で、一般式（１）、又は一般式（１－ｂ）の化合物を含有すると、ハイブリッド構造が安定するため好ましい。これらの化合物は両末端の極性が異なる特徴を持つ。本発明に用いられる重合性組成物を基材上に塗布した場合、空気界面側には疎水基が出現しやすい傾向があるため、これらの化合物を添加し、後述のレベリング剤や配向制御剤等の種類、及びその添加量を適宜選択することによって、空気界面での重合性液晶の配向の角度を安定化することができる。
（キラル化合物）
　本発明の位相差フィルムを作製するために用いられる重合性組成物には、キラルネマチック相を得ることを目的としてキラル化合物を含有してもよい。前記キラル化合物は、それ自体が液晶性を示す必要はなく、また、重合性基を有していても、有していなくてもよい。また、キラル化合物の螺旋の向きは、重合体の使用用途によって適宜選択することができる。
　重合性基を有しているキラル化合物としては、特に限定はなく、公知慣用のものが使用できるが、らせんねじれ力（ＨＴＰ）の大きなキラル化合物が好ましい。また、重合性基は、ビニル基、ビニルオキシ基、アリル基、アリルオキシ基、アクリロイルオキシ基、メタクリロイルオキシ基、グリシジル基、オキセタニル基が好ましく、アクリロイルオキシ基、グリシジル基、オキセタニル基が特に好ましい。
　キラル化合物の配合量は、化合物の螺旋誘起力によって適宜調整することが必要であるが、重合性基を有する液晶性化合物及びキラル化合物の総量に対して、０．１～５．０質量％含有することが好ましく、０．２～３．０質量％含有することがより好ましく、０．５～２．０質量％含有することが特に好ましい。
　キラル化合物の具体例として、下記一般式（１０－１）～式（１０－４）で表される化合物を挙げることができるが、下記の一般式に限定されるわけではない。
Figure JPOXMLDOC01-appb-C000139
　上記式中、Ｓｐ５ａ、Ｓｐ５ｂはそれぞれ独立して、炭素原子数０～１８のアルキレン基を表し、該アルキレン基は１つ以上のハロゲン原子、ＣＮ基、又は重合性官能基を有する炭素原子数１～８のアルキル基により置換されていても良く、この基中に存在する１つのＣＨ2基又は隣接していない２つ以上のＣＨ2基はそれぞれ相互に独立して、酸素原子が相互に直接結合しない形で、－Ｏ－、－Ｓ－、－ＮＨ－、－Ｎ（ＣＨ３）－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＯＣＯＯ－、－ＳＣＯ－、－ＣＯＳ－又は－Ｃ≡Ｃ－により置き換えられていても良く、
Ａ１、Ａ２、Ａ３、Ａ４、Ａ５及びＡ６はそれぞれ独立して、１，４－フェニレン基、１，４－シクロヘキシレン基、１，４－シクロヘキセニル基、テトラヒドロピラン－２，５－ジイル基、１，３－ジオキサン－２，５－ジイル基、テトラヒドロチオピラン－２，５－ジイル基、１，４－ビシクロ（２，２，２）オクチレン基、デカヒドロナフタレン－２，６－ジイル基、ピリジン－２，５－ジイル基、ピリミジン－２，５－ジイル基、ピラジン－２，５－ジイル基、チオフェン－２，５－ジイル基－、１，２，３，４－テトラヒドロナフタレン－２，６－ジイル基、２，６－ナフチレン基、フェナントレン－２，７－ジイル基、９，１０－ジヒドロフェナントレン－２，７－ジイル基、１，２，３，４，４ａ，９，１０ａ－オクタヒドロフェナントレン－２，７－ジイル基、１，４－ナフチレン基、ベンゾ［１，２－ｂ：４，５－ｂ‘］ジチオフェン－２，６－ジイル基、ベンゾ［１，２－ｂ：４，５－ｂ‘］ジセレノフェン－２，６－ジイル基、［１］ベンゾチエノ［３，２－ｂ］チオフェン－２，７－ジイル基、［１］ベンゾセレノフェノ［３，２－ｂ］セレノフェン－２，７－ジイル基、又はフルオレン－２，７－ジイル基を表し、n、ｌ及びｋはそれぞれ独立して、０又は１を表し、０≦ｎ＋ｌ＋ｋ≦３となり、
ｍ５は０又は１を表し、
Ｚ０、Ｚ１、Ｚ２、Ｚ３、Ｚ４、Ｚ５及びＺ６はそれぞれ独立して、－ＣＯＯ－、－ＯＣＯ－、－ＣＨ2 ＣＨ2－、－ＯＣＨ2－、－ＣＨ2Ｏ－、－ＣＨ＝ＣＨ－、－Ｃ≡Ｃ－、－ＣＨ＝ＣＨＣＯＯ－、－ＯＣＯＣＨ＝ＣＨ－、－ＣＨ2ＣＨ2ＣＯＯ－、－ＣＨ2ＣＨ2ＯＣＯ－、－ＣＯＯＣＨ2ＣＨ2－、－ＯＣＯＣＨ2ＣＨ2－、－ＣＯＮＨ－、－ＮＨＣＯ－、炭素数２～１０のハロゲン原子を有してもよいアルキル基又は単結合を表し、
Ｒ５ａ及びＲ５ｂは、水素原子、ハロゲン原子、シアノ基又は炭素原子数１～１８のアルキル基を表すが、該アルキル基は１つ以上のハロゲン原子又はＣＮにより置換されていても良く、この基中に存在する１つのＣＨ2基又は隣接していない２つ以上のＣＨ2基はそれぞれ相互に独立して、酸素原子が相互に直接結合しない形で、－Ｏ－、－Ｓ－、－ＮＨ－、－Ｎ（ＣＨ３）－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＯＣＯＯ－、－ＳＣＯ－、－ＣＯＳ－又は－Ｃ≡Ｃ－により置き換えられていても良く、あるいはＲ５ａ及びＲ５ｂは一般式（１０－ａ）
Figure JPOXMLDOC01-appb-C000140
（式中、Ｐ５ａは重合性官能基を表し、Ｓｐ５ａはＳｐ１と同じ意味を表す。）
　Ｐ５ａは、下記の式（Ｐ－１）から式（Ｐ－２０）で表される重合性基から選ばれる置換基を表す。
Figure JPOXMLDOC01-appb-C000141
　上記キラル化合物のさらなる具体的例としては、下記一般式（１０－５）～式（１０－３５）で表される化合物を挙げることができる。
Figure JPOXMLDOC01-appb-C000142
Figure JPOXMLDOC01-appb-C000143
Figure JPOXMLDOC01-appb-C000144
Figure JPOXMLDOC01-appb-C000145
Figure JPOXMLDOC01-appb-C000146
Figure JPOXMLDOC01-appb-C000147
Figure JPOXMLDOC01-appb-C000148
　上記式中、ｍ、ｎはそれぞれ独立して１～１０の整数を表し、Ｒは水素原子、炭素原子数１～１０のアルキル基、又は、フッ素原子を表すが、Ｒが複数存在する場合は、それぞれ同一であっても、異なっていても良い。
　重合性基を有していないキラル化合物としては、具体的には、例えば、キラル基としてコレステリル基を有するペラルゴン酸コレステロール、ステアリン酸コレステロール、キラル基として２－メチルブチル基を有するビーディーエイチ社製の「ＣＢ－１５」、「Ｃ－１５」、メルク社製の「Ｓ－１０１１」、「Ｓ－１０８２」、チッソ社製の「ＣＭ－１９」、「ＣＭ－２０」、「ＣＭ」、キラル基として１－メチルヘプチル基を有するメルク社製の「Ｓ－８１１」、チッソ社製の「ＣＭ－２１」、「ＣＭ－２２」などが挙げられる。
　キラル化合物を添加する場合は、重合性組成物の重合体の用途によるが、得られる重合体の厚み（ｄ）を重合体中での螺旋ピッチ（Ｐ）で除した値（ｄ／Ｐ）が０．１～１００の範囲となる量を添加することが好ましく、０．１～２０の範囲となる量がさらに好ましい。
（重合開始剤）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、必要に応じて開始剤を含有することができる。重合性組成物で用いられる重合開始剤は、本発明に用いられる重合性組成物を重合させるために用いる。重合を光照射によって行う場合に使用する光重合開始剤としては、特に限定はないが、重合性組成物における重合性化合物の配向状態を阻害しない程度で公知慣用のものが使用できる。
　例えば１－ヒドロキシシクロヘキシルフェニルケトン「イルガキュア１８４」、１－（４－イソプロピルフェニル）－２－ヒドロキシ－２－メチルプロパン－１－オン「ダロキュア１１１６」、２－メチル－１－［（メチルチオ）フェニル］－２－モリホリノプロパン－１「イルガキュア９０７」、２，２－ジメトキシ－１，２－ジフェニルエタン－１－オン「イルガキュア６５１」、２－ベンジル－２－ジメチルアミノ－１－（４－モルフォリノフェニル）－ブタノン「イルガキュア３６９」）、２－ジメチルアミノ－２－（４－メチルベンジル）－１－（４－モルフォリノ－フェニル）ブタン－１－オン「イルガキュア３７９」、２，２－ジメトキシ－１，２－ジフェニルエタン－１－オン、ビス（２，４，６－トリメチルベンゾイル）－ジフェニルフォスフィンオキサイド「ルシリンＴＰＯ」、２，４，６－トリメチルベンゾイル－フェニル－フォスフィンオキサイド「イルガキュア８１９」、１，２－オクタンジオン，１－［４－（フェニルチオ）－，２－（Ｏ－ベンゾイルオキシム）］，エタノン「イルガキュアＯＸＥ０１」）、１－［９－エチル－６－（２－メチルベンゾイル）－９Ｈ－カルバゾール－３－イル］－，１－（Ｏ－アセチルオキシム）「イルガキュアＯＸＥ０２」（以上、ＢＡＳＦ株式会社製。２，４－ジエチルチオキサントン（日本化薬社製「カヤキュアＤＥＴＸ」）とｐ－ジメチルアミノ安息香酸エチル（日本化薬社製「カヤキュアＥＰＡ」）との混合物、イソプロピルチオキサントン（ワ－ドプレキンソップ社製「カンタキュア－ＩＴＸ」）とｐ－ジメチルアミノ安息香酸エチルとの混合物、「エサキュア　ＯＮＥ」、「エサキュアＫＩＰ１５０」、「エサキュアＫＩＰ１６０」、「エサキュア１００１Ｍ」、「エサキュアＡ１９８」、「エサキュアＫＩＰ　ＩＴ」、「エサキュアＫＴＯ４６」、「エサキュアＴＺＴ」（ｌａｍｂｅｒｔｉ株式会社製）、
ＬＡＭＢＳＯＮ社の「スピードキュアＢＭＳ」、「スピードキュアＰＢＺ」、「ベンゾフェノン」等が挙げられる。さらに、光カチオン開始剤としては、光酸発生剤を用いることができる。光酸発生剤としてはジアゾジスルホン系化合物、トリフェニルスルホニウム系化合物、フェニルスルホン系化合物、スルフォニルピリジン系化合物、トリアジン系化合物及びジフェニルヨードニウム化合物などが挙げられる。
　光重合開始剤の含有率は、重合性組成物に含まれる重合性化合物の総量に対し、０．１～１０質量％が好ましく、１～６質量％が特に好ましい。これらは、単独で使用することもできるし、２種類以上混合して使用することもできる。
　また、熱重合の際に使用する熱重合開始剤としては公知慣用のものが使用でき、例えば、メチルアセトアセテイトパーオキサイド、キュメンハイドロパーオキサイド、ベンゾイルパーオキサイド、ビス（４－ｔ－ブチルシクロヘキシル）パ－オキシジカーボネイト、ｔ－ブチルパーオキシベンゾエイト、メチルエチルケトンパーオキサイド、１，１－ビス（ｔ－ヘキシルパ－オキシ）３，３，５－トリメチルシクロヘキサン、ｐ－ペンタハイドロパーオキサイド、ｔ－ブチルハイドロパーオキサイド、ジクミルパーオキサイド、イソブチルパーオキサイド、ジ（３－メチル－３－メトキシブチル）パーオキシジカーボネイト、１，１－ビス（ｔ－ブチルパーオキシ）シクロヘキサン等の有機過酸化物、２，２’－アゾビスイソブチロニトリル、２，２’－アゾビス（２，４－ジメチルバレロニトリル）等のアゾニトリル化合物、２，２’－アゾビス（２－メチル－Ｎ－フェニルプロピオン－アミヂン）ジハイドロクロライド等のアゾアミヂン化合物、２，２’アゾビス｛２－メチル－Ｎ－［１，１－ビス（ヒドロキシメチル）－２－ヒドロキシエチル］プロピオンアミド｝等のアゾアミド化合物、２，２’アゾビス（２，４，４－トリメチルペンタン）等のアルキルアゾ化合物等を使用することができる。熱重合開始剤の含有利量は０．１～１０質量が好ましく、１～６質量％が特に好ましい。これらは、単独で使用することもできるし、２種類以上混合して使用することもできる。
（重合抑制剤）
本発明の位相差フィルムを作製するための重合性組成物には、重合抑制剤を含有することができる。重合性組成物は、当該重合抑制剤を用いることにより、重合性組成物として高温で保存された場合に、不必要な重合が抑制され、保存安定性を確保することができる。また、位相差フィルムとした場合に、塗膜に耐熱性を付与できるため、耐久性を十分確保することができる。
　前記重合抑制剤は、フェノール系重合抑制剤であることが好ましい。
前記フェノール系重合抑制剤としては、ハイドロキノン、メトキシフェノール、メチルハイドロキノン、ターシャリーブチルハイドロキノン、ターシャリーブチルカテコールのいずれかが好ましい。
　重合抑制剤の含有率は、重合性組成物に含まれる重合性化合物の総量に対し、０．０１～１質量％が好ましく、０．０１～０．５質量％が特に好ましい。これらは、単独で使用することもできるし、２種類以上混合して使用することもできる。
　重合性組成物中に前記重合抑制剤を溶解する際には、重合性化合物を有機溶剤に加熱攪拌により溶解する段階で同時に溶解することが好ましい。また、重合性化合物を有機溶剤に加熱攪拌により溶解させたのち、重合性組成物中にさらに添加し溶解させてもよい。
（添加剤）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、各々の目的に応じて汎用の添加剤を使用することもできる。例えば、酸化防止剤、紫外線吸収剤、レベリング剤、配向制御剤、連鎖移動剤、赤外線吸収剤、チキソ剤、帯電防止剤、色素、フィラー、キラル化合物、重合性基を有する非液晶性化合物、その他液晶化合物、配向材料等の添加剤を液晶の配向性を著しく低下させない程度添加することができる。
（酸化防止剤）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、必要に応じて酸化防止剤等を含有することができる。そのような化合物として、ヒドロキノン誘導体、ニトロソアミン系重合禁止剤、ヒンダードフェノール系酸化防止剤等が挙げられ、より具体的には、tert-ブチルハイドロキノン、和光純薬工業社の「Ｑ－１３００」、「Ｑ－１３０１」、ペンタエリスリトールテトラキス[３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート「ＩＲＧＡＮＯＸ１０１０」、チオジエチレンビス[３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート「ＩＲＧＡＮＯＸ１０３５」、オクタデシル－３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート「ＩＲＧＡＮＯＸ１０７６」、「ＩＲＧＡＮＯＸ１１３５」、「ＩＲＧＡＮＯＸ１３３０」、４，６－ビス（オクチルチオメチル）－ｏ－クレゾール「ＩＲＧＡＮＯＸ１５２０Ｌ」、「ＩＲＧＡＮＯＸ１７２６」、「ＩＲＧＡＮＯＸ２４５」、「ＩＲＧＡＮＯＸ２５９」、「ＩＲＧＡＮＯＸ３１１４」、「ＩＲＧＡＮＯＸ３７９０」、「ＩＲＧＡＮＯＸ５０５７」、「ＩＲＧＡＮＯＸ５６５」（以上、ＢＡＳＦ株式会社製）、株式会社ＡＤＥＫＡ製のアデカスタブＡＯ－２０、ＡＯ－３０、ＡＯ－４０、ＡＯ－５０、ＡＯ－６０、ＡＯ－８０、住友化学株式会社のスミライザーＢＨＴ、スミライザーＢＢＭ－Ｓ、およびスミライザーＧＡ－８０等々があげられる。
　酸化防止剤の添加量は、重合性組成物に含まれる重合性化合物の総量に対して０．０１～２．０質量％であることが好ましく、０．０５～１．０質量％であることがより好ましい。
（紫外線吸収剤）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、必要に応じて紫外線吸収剤や光安定剤を含有することができる。用いる紫外線吸収剤や光安定剤は特に限定はないが、位相差フィルムの耐光性を向上させるものが好ましい。
　前記紫外線吸収剤としては、例えば、２－（２－ヒドロキシ－５－ｔ－ブチルフェニル）－２Ｈ－ベンゾトリアゾール「チヌビン　ＰＳ」、「チヌビン　９９－２」、「チヌビン　１０９」、「ＴＩＮＵＶＩＮ　２１３」、「ＴＩＮＵＶＩＮ　２３４」、「ＴＩＮＵＶＩＮ　３２６」、「ＴＩＮＵＶＩＮ　３２８」、「ＴＩＮＵＶＩＮ　３２９」、「ＴＩＮＵＶＩＮ　３８４－２」、「ＴＩＮＵＶＩＮ　５７１」、２－（２Ｈ－ベンゾトリアゾール－２－イル）－４，６－ビス（１－メチル－１－フェニルエチル）フェノール「ＴＩＮＵＶＩＮ　９００」、２－（２Ｈ－ベンゾトリアゾール－２－イル）－６－（１－メチル－１－フェニルエチル）－４－（１，１，３，３－テトラメチルブチル）フェノール「ＴＩＮＵＶＩＮ　９２８」、「ＴＩＮＵＶＩＮ　１１３０」、「ＴＩＮＵＶＩＮ　４００」、「ＴＩＮＵＶＩＮ　４０５」、２，４－ビス[２－ヒドロキシ－４－ブトキシフェニル]－６－（２，４－ジブトキシフェニル）－１，３，５－トリアジン「ＴＩＮＵＶＩＮ　４６０」、「チヌビン　４７９」、「ＴＩＮＵＶＩＮ　５２３６」（以上、ＢＡＳＦ株式会社製）、「アデカスタブＬＡ－３２」、「アデカスタブＬＡ－３４」、「アデカスタブＬＡ－３６」、「アデカスタブＬＡ－３１」、「アデカスタブ１４１３」、「アデカスタブＬＡ－５１」（以上、株式会社ＡＤＥＫＡ製）等が挙げられる。
　光安定剤としては例えば、「ＴＩＮＵＶＩＮ　１１１ＦＤＬ」、「ＴＩＮＵＶＩＮ　１２３」、「ＴＩＮＵＶＩＮ　１４４」、「ＴＩＮＵＶＩＮ　１５２」、「ＴＩＮＵＶＩＮ　２９２」、「ＴＩＮＵＶＩＮ　６２２」、「ＴＩＮＵＶＩＮ　７７０」、「ＴＩＮＵＶＩＮ　７６５」、「ＴＩＮＵＶＩＮ　７８０」、「ＴＩＮＵＶＩＮ　９０５」、「ＴＩＮＵＶＩＮ　５１００」、「ＴＩＮＵＶＩＮ　５０５０」、「ＴＩＮＵＶＩＮ　５０６０」、「ＴＩＮＵＶＩＮ　５１５１」、「ＣＨＩＭＡＳＳＯＲＢ　１１９ＦＬ」、「ＣＨＩＭＡＳＳＯＲＢ　９４４ＦＬ」、「ＣＨＩＭＡＳＳＯＲＢ　９４４ＬＤ」（以上、ＢＡＳＦ株式会社製）、「アデカスタブＬＡ－５２」、「アデカスタブＬＡ－５７」、「アデカスタブＬＡ－６２」、「アデカスタブＬＡ－６７」、「アデカスタブＬＡ－６３Ｐ」、「アデカスタブＬＡ－６８ＬＤ」、「アデカスタブＬＡ－７７」、「アデカスタブＬＡ－８２」、「アデカスタブＬＡ－８７」（以上、株式会社ＡＤＥＫＡ製）等が挙げられる。
（レベリング剤）
　本発明の位相差フィルムを作製するための重合性組成物には、必要に応じてレベリング剤を含有することができる。用いるレベリング剤は特に限定はないが、位相差フィルムの薄膜を形成する場合に膜厚むらを低減させるためものが好ましい。　前記レベリング剤としては、アルキルカルボン酸塩、アルキルリン酸塩、アルキルスルホン酸塩、フルオロアルキルカルボン酸塩、フルオロアルキルリン酸塩、フルオロアルキルスルホン酸塩、ポリオキシエチレン誘導体、フルオロアルキルエチレンオキシド誘導体、ポリエチレングリコール誘導体、アルキルアンモニウム塩、フルオロアルキルアンモニウム塩類等が挙げられる。
　具体的には、「メガファックＦ－１１４」、「メガファックＦ－２５１」、「メガファックＦ－２８１」、「メガファックＦ－４１０」、「メガファックＦ－４３０」、「メガファックＦ－４４４」、「メガファックＦ－４７２ＳＦ」、「メガファックＦ－４７７」、「メガファックＦ－５１０」、「メガファックＦ－５１１」、「メガファックＦ－５５２」、「メガファックＦ－５５３」、「メガファックＦ－５５４」、「メガファックＦ－５５５」、「メガファックＦ－５５６」、「メガファックＦ－５５７」、「メガファックＦ－５５８」、「メガファックＦ－５５９」、「メガファックＦ－５６０」、「メガファックＦ－５６１」、「メガファックＦ－５６２」、「メガファックＦ－５６３」、「メガファックＦ－５６５」、「メガファックＦ－５６７」、「メガファックＦ－５６８」、「メガファックＦ－５６９」、「メガファックＦ－５７０」、「メガファックＦ－５７１」、「メガファックＲ－４０」、「メガファックＲ－４１」、「メガファックＲ－４３」、「メガファックＲ－９４」、「メガファックＲＳ－７２－Ｋ」、「メガファックＲＳ－７５」、「メガファックＲＳ－７６－Ｅ」、「メガファックＲＳ－７６－ＮＳ」、「メガファックＲＳ－９０」、「メガファックＥＸＰ．ＴＦ－１３６７」、「メガファックＥＸＰ．ＴＦ１４３７」、「メガファックＥＸＰ．ＴＦ１５３７」、「メガファックＥＸＰ．ＴＦ－２０６６」（以上、ＤＩＣ株式会社製）、
「フタージェント１００」、「フタージェント１００Ｃ」、「フタージェント１１０」、「フタージェント１５０」、「フタージェント１５０ＣＨ」、「フタージェント１００Ａ-Ｋ」、「フタージェント３００」、「フタージェント３１０」、「フタージェント３２０」、「フタージェント４００ＳＷ」、「フタージェント２５１」、「フタージェント２１５Ｍ」、「フタージェント２１２Ｍ」、「フタージェント２１５Ｍ」、「フタージェント２５０」、「フタージェント２２２Ｆ」、「フタージェント２１２Ｄ」、「ＦＴＸ－２１８」、「フタージェント２０９Ｆ」、「フタージェント２４５Ｆ」、「フタージェント２０８Ｇ」、「フタージェント２４０Ｇ」、「フタージェント２１２Ｐ」、「フタージェント２２０Ｐ」、「フタージェント２２８Ｐ」、「ＤＦＸ－１８」、「フタージェント６０１ＡＤ」、「フタージェント６０２Ａ」、「フタージェント６５０Ａ」、「フタージェント７５０ＦＭ」、「ＦＴＸ-７３０ＦＭ」、「フタージェント７３０ＦＬ」、「フタージェント７１０ＦＳ」、「フタージェント７１０ＦＭ」、「フタージェント７１０ＦＬ」、「フタージェント７５０ＬＬ」、「ＦＴＸ-７３０ＬＳ」、「フタージェント７３０ＬＭ」、（以上、株式会社ネオス製）、
「ＢＹＫ－３００」、「ＢＹＫ－３０２」、「ＢＹＫ－３０６」、「ＢＹＫ－３０７」、「ＢＹＫ－３１０」、「ＢＹＫ－３１５」、「ＢＹＫ－３２０」、「ＢＹＫ－３２２」、「ＢＹＫ－３２３」、「ＢＹＫ－３２５」、「ＢＹＫ－３３０」、「ＢＹＫ－３３１」、「ＢＹＫ－３３３」、「ＢＹＫ－３３７」、「ＢＹＫ－３４０」、「ＢＹＫ－３４４」、「ＢＹＫ－３７０」、「ＢＹＫ－３７５」、「ＢＹＫ－３７７」、「ＢＹＫ－３５０」、「ＢＹＫ－３５２」、「ＢＹＫ－３５４」、「ＢＹＫ－３５５」、「ＢＹＫ－３５６」、「ＢＹＫ－３５８Ｎ」、「ＢＹＫ－３６１Ｎ」、「ＢＹＫ－３５７」、「ＢＹＫ－３９０」、「ＢＹＫ－３９２」、「ＢＹＫ－ＵＶ３５００」、「ＢＹＫ－ＵＶ３５１０」、「ＢＹＫ－ＵＶ３５７０」、「ＢＹＫ－Ｓｉｌｃｌｅａｎ３７００」（以上、ＢＹＫ株式会社製）、
「ＴＥＧＯ Ｒａｄ２１００」、「ＴＥＧＯ Ｒａｄ２０１１」、「ＴＥＧＯ Ｒａｄ２２００Ｎ」、「ＴＥＧＯ Ｒａｄ２２５０」、「ＴＥＧＯ Ｒａｄ２３００」、「ＴＥＧＯ Ｒａｄ２５００」、「ＴＥＧＯ Ｒａｄ２６００」、「ＴＥＧＯ Ｒａｄ２６５０」、「ＴＥＧＯ Ｒａｄ２７００」、「ＴＥＧＯ　Ｆｌｏｗ３００」、「ＴＥＧＯ　Ｆｌｏｗ３７０」、「ＴＥＧＯ　Ｆｌｏｗ４２５」、「ＴＥＧＯ　Ｆｌｏｗ　ＡＴＦ２」、「ＴＥＧＯ　Ｆｌｏｗ　ＺＦＳ４６０」、「ＴＥＧＯ　Ｇｌｉｄｅ１００」、「ＴＥＧＯ　Ｇｌｉｄｅ１１０」、「ＴＥＧＯ　Ｇｌｉｄｅ１３０」、「ＴＥＧＯ　Ｇｌｉｄｅ４１０」、「ＴＥＧＯ　Ｇｌｉｄｅ４１１」、「ＴＥＧＯ　Ｇｌｉｄｅ４１５」、「ＴＥＧＯ　Ｇｌｉｄｅ４３２」、「ＴＥＧＯ　Ｇｌｉｄｅ４４０」、「ＴＥＧＯ　Ｇｌｉｄｅ４５０」、「ＴＥＧＯ　Ｇｌｉｄｅ４８２」、「ＴＥＧＯ　Ｇｌｉｄｅ　Ａ１１５」、「ＴＥＧＯ　Ｇｌｉｄｅ　Ｂ１４８４」、「ＴＥＧＯ　Ｇｌｉｄｅ　ＺＧ４００」、「ＴＥＧＯ　Ｔｗｉｎ４０００」、「ＴＥＧＯ　Ｔｗｉｎ４１００」、「ＴＥＧＯ　Ｔｗｉｎ４２００」、「ＴＥＧＯ　Ｗｅｔ２４０」、「ＴＥＧＯ　Ｗｅｔ２５０」、「ＴＥＧＯ　Ｗｅｔ２６０」、「ＴＥＧＯ　Ｗｅｔ２６５」、「ＴＥＧＯ　Ｗｅｔ２７０」、「ＴＥＧＯ　Ｗｅｔ２８０」、「ＴＥＧＯ　Ｗｅｔ５００」、「ＴＥＧＯ　Ｗｅｔ５０５」、「ＴＥＧＯ　Ｗｅｔ５１０」、「ＴＥＧＯ　Ｗｅｔ５２０」、「ＴＥＧＯ　Ｗｅｔ　ＫＬ２４５」、（以上、エボニック・インダストリーズ株式会社製）、「ＦＣ－４４３０」、「ＦＣ－４４３２」（以上、スリーエムジャパン株式会社製）、「ユニダインＮＳ」（以上、ダイキン工業株式会社製）、「サーフロンＳ－２４１」、「サーフロンＳ－２４２」、「サーフロンＳ－２４３」、「サーフロンＳ－４２０」、「サーフロンＳ－６１１」、「サーフロンＳ－６５１」、「サーフロンＳ－３８６」（以上、ＡＧＣセイミケミカル株式会社製）、「ＤＩＳＰＡＲＬＯＮ　ＯＸ－８８０ＥＦ」、「ＤＩＳＰＡＲＬＯＮ　ＯＸ－８８１」、「ＤＩＳＰＡＲＬＯＮ　ＯＸ－８８３」、「ＤＩＳＰＡＲＬＯＮ　ＯＸ－７７ＥＦ」、「ＤＩＳＰＡＲＬＯＮ　ＯＸ－７１０」、「ＤＩＳＰＡＲＬＯＮ　１９２２」、「ＤＩＳＰＡＲＬＯＮ　１９２７」、「ＤＩＳＰＡＲＬＯＮ　１９５８」、「ＤＩＳＰＡＲＬＯＮ　Ｐ－４１０ＥＦ」、「ＤＩＳＰＡＲＬＯＮ　Ｐ－４２０」、「ＤＩＳＰＡＲＬＯＮ　Ｐ－４２５」、「ＤＩＳＰＡＲＬＯＮ　ＰＤ－７」、「ＤＩＳＰＡＲＬＯＮ　１９７０」、「ＤＩＳＰＡＲＬＯＮ　２３０」、「ＤＩＳＰＡＲＬＯＮ　ＬＦ－１９８０」、「ＤＩＳＰＡＲＬＯＮ　ＬＦ－１９８２」、「ＤＩＳＰＡＲＬＯＮ　ＬＦ－１９８３」、「ＤＩＳＰＡＲＬＯＮ　ＬＦ－１０８４」、「ＤＩＳＰＡＲＬＯＮ　ＬＦ－１９８５」、「ＤＩＳＰＡＲＬＯＮ　ＬＨＰ－９０」、「ＤＩＳＰＡＲＬＯＮ　ＬＨＰ－９１」、「ＤＩＳＰＡＲＬＯＮ　ＬＨＰ－９５」、「ＤＩＳＰＡＲＬＯＮ　ＬＨＰ－９６」、「ＤＩＳＰＡＲＬＯＮ　ＯＸ－７１５」、「ＤＩＳＰＡＲＬＯＮ　１９３０Ｎ」、「ＤＩＳＰＡＲＬＯＮ　１９３１」、「ＤＩＳＰＡＲＬＯＮ　１９３３」、「ＤＩＳＰＡＲＬＯＮ　１９３４」、「ＤＩＳＰＡＲＬＯＮ　１７１１ＥＦ」、「ＤＩＳＰＡＲＬＯＮ　１７５１Ｎ」、「ＤＩＳＰＡＲＬＯＮ　１７６１」、「ＤＩＳＰＡＲＬＯＮ　ＬＳ－００９」、「ＤＩＳＰＡＲＬＯＮ　ＬＳ－００１」、「ＤＩＳＰＡＲＬＯＮ　ＬＳ－０５０」（以上、楠本化成株式会社製）、「ＰＦ－１５１Ｎ」、「ＰＦ－６３６」、「ＰＦ－６３２０」、「ＰＦ－６５６」、「ＰＦ－６５２０」、「ＰＦ－６５２－ＮＦ」、「ＰＦ－３３２０」（以上、ＯＭＮＯＶＡ ＳＯＬＵＴＩＯＮＳ社製）、「ポリフローＮｏ．７」、「ポリフローＮｏ．５０Ｅ」、「ポリフローＮｏ．５０ＥＨＦ」、「ポリフローＮｏ．５４Ｎ」、「ポリフローＮｏ．７５」、「ポリフローＮｏ．７７」、「ポリフローＮｏ．８５」、「ポリフローＮｏ．８５ＨＦ」、「ポリフローＮｏ．９０」、「ポリフローＮｏ．９０Ｄ－５０」、「ポリフローＮｏ．９５」、「ポリフローＮｏ．９９Ｃ」、「ポリフローＫＬ－４００Ｋ」、「ポリフローＫＬ－４００ＨＦ」、「ポリフローＫＬ－４０１」、「ポリフローＫＬ－４０２」、「ポリフローＫＬ－４０３」、「ポリフローＫＬ－４０４」、「ポリフローＫＬ－１００」、「ポリフローＬＥ－６０４」、「ポリフローＫＬ－７００」、「フローレンＡＣ－３００」、「フローレンＡＣ－３０３」、「フローレンＡＣ－３２４」、「フローレンＡＣ－３２６Ｆ」、「フローレンＡＣ－５３０」、「フローレンＡＣ－９０３」、「フローレンＡＣ－９０３ＨＦ」、「フローレンＡＣ－１１６０」、「フローレンＡＣ－１１９０」、「フローレンＡＣ－２０００」、「フローレンＡＣ－２３００Ｃ」、「フローレンＡＯ－８２」、「フローレンＡＯ－９８」、「フローレンＡＯ－１０８」（以上、共栄社化学株式会社製）、「Ｌ－７００１」、「Ｌ－７００２」、「８０３２ＡＤＤＩＴＩＶＥ」、「５７ＡＤＤＴＩＶＥ」、「Ｌ－７０６４」、「ＦＺ－２１１０」、「ＦＺ－２１０５」、「６７ＡＤＤＴＩＶＥ」、「８６１６ＡＤＤＴＩＶＥ」（以上、東レ・ダウシリコーン株式会社製）等の例を挙げることができる。
　レベリング剤の添加量は、重合性組成物に用いる、重合性化合物の合計量に対し、０．０１～２質量％であることが好ましく、０．０５～０．５質量％であることがより好ましい。
　また、上記レベリング剤の種類、添加量を適宜選択することで、重合性組成物を位相差フィルムとした場合、空気界面のチルト角を制御することもできる。
（配向制御剤）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、重合性化合物の配向状態を制御するために、配向制御剤を含有することができる。用いる配向制御剤としては、液晶性化合物が、基材に対して実質的に水平配向、実質的に垂直配向、実質的にハイブリッド配向するものが挙げられる。また、キラル化合物を添加した場合には実質的に平面配向するものが挙げられる。前述したように、界面活性剤によって、水平配向、平面配向が誘起される場合もあるが、各々の配向状態が誘起されるものであれば、特に限定はなく、公知慣用のものを使用することができる。
　そのような配向制御剤としては、例えば、位相差フィルムとした場合の空気界面のチルト角を効果的に減じる効果を持つ、下記一般式（８）で表される繰り返し単位を有する重量平均分子量が１００以上１００００００以下である化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000149
　（式中、Ｒ１１、Ｒ１２、Ｒ１３及びＲ１４はそれぞれ独立的に水素原子、ハロゲン原子又は炭素原子数１～２０の炭化水素基を表し、該炭化水素基中の水素原子は１つ以上のハロゲン原子で置換されていても良い。）
　また、フルオロアルキル基で変性された棒状液晶性化合物、円盤状液晶性化合物、分岐構造を有してもよい長鎖脂肪族アルキル基を含有した重合性化合物、等も挙げられる。
　位相差フィルムとした場合の空気界面のチルト角を効果的に増加させる効果を持つものとしては、硝酸セルロース、酢酸セルロース、プロピオン酸セルロース、酪酸セルロース、複素芳香族環塩変性された棒状液晶性化合物、シアノ基、シアノアルキル基で変性された棒状液晶性化合物、等が挙げられる。
（連鎖移動剤）
　本発明に用いる重合性組成物は、重合体や位相差フィルムと基材との密着性をより向上させるため、連鎖移動剤を含有することができる。連鎖移動剤としては、芳香族炭化水素類、クロロホルム、四塩化炭素、四臭化炭素、ブロモトリクロロメタン等のハロゲン化炭化水素類、
　オクチルメルカプタン、ｎ―ブチルメルカプタン、ｎ―ペンチルメルカプタン、ｎ－ヘキサデシルメルカプタン、ｎ－テトラデシルメル、ｎ―ドデシルメルカプタン、ｔ－テトラデシルメルカプタン、ｔ―ドデシルメルカプタン等のメルカプタン化合物、ヘキサンジチオール、デカンジチオール、１，４－ブタンジオールビスチオプロピオネート、１，４－ブタンジオールビスチオグリコレート、エチレングリコールビスチオグリコレート、エチレングリコールビスチオプロピオネート、トリメチロールプロパントリスチオグリコレート、トリメチロールプロパントリスチオプロピオネート、トリメチロールプロパントリス（３－メルカプトブチレート）、ペンタエリスリトールテトラキスチオグリコレート、ペンタエリスリトールテトラキスチオプロピオネート、トリメルカプトプロピオン酸トリス（２－ヒドロキシエチル）イソシアヌレート、１，４－ジメチルメルカプトベンゼン、２、４、６－トリメルカプト－ｓ－トリアジン、２－（Ｎ，Ｎ－ジブチルアミノ）－４，６－ジメルカプト－ｓ－トリアジン等のチオール化合物、ジメチルキサントゲンジスルフィド、ジエチルキサントゲンジスルフィド、ジイソプロピルキサントゲンジスルフィド、テトラメチルチウラムジスルフィド、テトラエチルチウラムジスルフィド、テトラブチルチウラムジスルフィド等のスルフィド化合物、Ｎ，Ｎ－ジメチルアニリン、Ｎ，Ｎ－ジビニルアニリン、ペンタフェニルエタン、α－メチルスチレンダイマー、アクロレイン、アリルアルコール、ターピノーレン、α－テルピネン、γ－テルビネン、ジペンテン、等が挙げられるが、２，４－ジフェニル－４－メチル－１－ペンテン、チオール化合物がより好ましい。
　具体的には下記一般式（９－１）～（９－１２）で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000150
Figure JPOXMLDOC01-appb-C000151
　式中、Ｒ９５は炭素原子数２～１８のアルキル基を表し、該アルキル基は直鎖であっても分岐鎖であっても良く、該アルキル基中の１つ以上のメチレン基は酸素原子、及び硫黄原子が相互に直接結合しないものとして、酸素原子、硫黄原子、－ＣＯ－、－ＯＣＯ－、－ＣＯＯ－、又は－ＣＨ＝ＣＨ－で置換されていてもよく、Ｒ９６は炭素原子数２～１８のアルキレン基を表し、該アルキレン基中の１つ以上のメチレン基は酸素原子、及び硫黄原子が相互に直接結合しないものとして、酸素原子、硫黄原子、－ＣＯ－、－ＯＣＯ－、－ＣＯＯ－、又は－ＣＨ＝ＣＨ－で置換されていてもよい。
　連鎖移動剤は、重合性化合物を有機溶剤に混合し加熱攪拌して重合性溶液を調製する工程において添加することが好ましいが、その後の、重合性溶液に重合開始剤を混合する工程において添加してもよいし、両方の工程において添加してもよい。
　連鎖移動剤の添加量は、重合性組成物に含まれる重合性化合物の総量に対して、０．５～１０質量％であることが好ましく、１．０～５．０質量％であることがより好ましい。
　更に物性調整のため、重合性でない液晶化合物等も必要に応じて添加することも可能である。液晶性のない重合性化合物は、重合性化合物を有機溶剤に混合し加熱攪拌して重合性溶液を調製する工程において添加することが好ましいが、重合性でない液晶化合物等は、その後の、重合性溶液に重合開始剤を混合する工程において添加してもよいし、両方の工程において添加してもよい。これらの化合物の添加量は重合性組成物に対して、２０質量％以下が好ましく、１０質量％以下がより好ましく、５質量％以下が更により好ましい。
（赤外線吸収剤）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、必要に応じて赤外線吸収剤を含有することができる。用いる赤外線吸収剤は、特に限定はなく、配向性を乱さない範囲で公知慣用のものを含有することができる。
　前記赤外線吸収剤としては、シアニン化合物、フタロシアニン化合物、ナフトキノン化合物、ジチオール化合物、ジインモニウム化合物、アゾ化合物、アルミニウム塩等が挙げられる。
　具体的には、ジインモニウム塩タイプの「ＮＩＲ－ＩＭ１」、アルミニウム塩タイプの「ＮＩＲ－ＡＭ１」（以上、ナガセケムテック株式会社製）、「カレンズＩＲ－Ｔ」、「カレンズＩＲ－１３Ｆ」（以上、昭和電工株式会社製）、「ＹＫＲ－２２００」、「ＹＫＲ－２１００」（以上、山本化成株式会社製）、「ＩＲＡ９０８」、「ＩＲＡ９３１」、「ＩＲＡ９５５」、「ＩＲＡ１０３４」（以上、ＩＮＤＥＣＯ株式会社）等が挙げられる。
（帯電防止剤）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、必要に応じて帯電防止剤を含有することができる。用いる帯電防止剤は、特に限定はなく、配向性を乱さない範囲で公知慣用のものを含有することができる。
　そのような帯電防止剤としては、スルホン酸塩基またはリン酸塩基を分子内に少なくとも１種類以上有する高分子化合物、４級アンモニウム塩を有する化合物、重合性基を有する界面活性剤等が挙げられる。
　中でも重合性基を有する界面活性剤が好ましく、例えば、重合性基を有する界面活性剤の内、アニオン系のものとして、「アントックスＳＡＤ」、「アントックスＭＳ－２Ｎ」（以上、日本乳化剤株式会社製）、「アクアロンＫＨ－０５」、「アクアロンＫＨ－１０」、「アクアロンＫＨ－２０」、「アクアロンＫＨ－０５３０」、「アクアロンＫＨ－１０２５」（以上、第一工業製薬株式会社製）、「アデカリアソープＳＲ－１０Ｎ」、「アデカリアソープＳＲ－２０Ｎ」（以上株式会社ＡＤＥＫＡ製）、「ラテムルＰＤ－１０４」（花王株式会社製）、等のアルキルエーテル系、「ラテムルＳ－１２０」、「ラテムルＳ－１２０Ａ」、「ラテムルＳ－１８０Ｐ」、「ラテムルＳ－１８０Ａ」（以上、花王株式会社製）、「エレミノールＪＳ－２」（三洋化成株式会社製）、等のスルフォコハク酸エステル系、「アクアロンＨ－２８５５Ａ」、「アクアロンＨ－３８５５Ｂ」、「アクアロンＨ－３８５５Ｃ」、「アクアロンＨ－３８５６」、「アクアロンＨＳ－０５」、「アクアロンＨＳ－１０」、「アクアロンＨＳ－２０」、「アクアロンＨＳ－３０」、「アクアロンＨＳ－１０２５」、「アクアロンＢＣ－０５」、「アクアロンＢＣ－１０」、「アクアロンＢＣ－２０」、「アクアロンＢＣ－１０２５」、「アクアロンＢＣ－２０２０」（以上、第一工業製薬株式会社製）、「アデカリアソープＳＤＸ－２２２」、「アデカリアソープＳＤＸ－２２３」、「アデカリアソープＳＤＸ－２３２」、「アデカリアソープＳＤＸ－２３３」、「アデカリアソープＳＤＸ－２５９」、「アデカリアソープＳＥ－１０Ｎ」、「アデカリアソープＳＥ－２０Ｎ」（以上、株式会社ＡＤＥＫＡ製）、等のアルキルフェニルエーテルあるいはアルキルフェニルエステル系、「アントックスＭＳ－６０」、「アントックスＭＳ－２Ｎ」（以上、日本乳化剤株式会社製）、「エレミノールＲＳ－３０」（三洋化成株式会社製）、等の（メタ）アクリレート硫酸エステル系、「Ｈ－３３３０Ｐ」（第一工業製薬株式会社製）、「アデカリアソープＰＰ－７０」（株式会社ＡＤＥＫＡ製）、等のリン酸エステル系が挙げられる。
　一方、重合性基を有する界面活性剤の内、ノニオン系のものとして、例えば、「アントックスＬＭＡ－２０」、「アントックスＬＭＡ－２７」、「アントックスＥＭＨ－２０」、「アントックスＬＭＨ-２０、「アントックスＳＭＨ－２０」（以上、日本乳化剤株式会社製）、「アデカリアソープＥＲ－１０」、「アデカリアソープＥＲ－２０」、「アデカリアソープＥＲ－３０」、「アデカリアソープＥＲ－４０」（以上、株式会社ＡＤＥＫＡ製）、「ラテムルＰＤ－４２０」、「ラテムルＰＤ－４３０」、「ラテムルＰＤ－４５０」（以上、花王株式会社製）、等のアルキルエーテル系、「アクアロンＲＮ－１０」、「アクアロンＲＮ－２０」、「アクアロンＲＮ－３０」、「アクアロンＲＮ－５０」、「アクアロンＲＮ－２０２５」（以上、第一工業製薬株式会社製）、「アデカリアソープＮＥ－１０」、「アデカリアソープＮＥ－２０」、「アデカリアソープＮＥ－３０」、「アデカリアソープＮＥ－４０」（以上、株式会社ＡＤＥＫＡ製）、等のアルキルフェニルエーテル系もしくはアルキルフェニルエステル系、「ＲＭＡ－５６４」、「ＲＭＡ－５６８」、「ＲＭＡ－１１１４」（以上、日本乳化剤株式会社製）等の（メタ）アクリレート硫酸エステル系が挙げられる。
　その他の帯電防止剤としては、例えば、ポリエチレングリコール（メタ）アクリレート、メトキシポリエチレングリコール（メタ）アクリレート、エトキシポリエチレングリコール（メタ）アクリレート、プロポキシポリエチレングリコール（メタ）アクリレート、ｎ－ブトキシポリエチレングリコール（メタ）アクリレート、ｎ－ペンタキシポリエチレングリコール（メタ）アクリレート、フェノキシポリエチレングリコール（メタ）アクリレート、ポリプロピレングリコール（メタ）アクリレート、メトキシポリプロピレングリコール（メタ）アクリレート、エトキシポリプロピレングリコール（メタ）アクリレート、プロポキシポリプロピレングリコール（メタ）アクリレート、ｎ－ブトキシポリプロピレングリコール（メタ）アクリレート、ｎ－ペンタキシポリプロピレングリコール（メタ）アクリレート、フェノキシポリプロピレングリコール（メタ）アクリレート、ポリテトラメチレングリコール（メタ）アクリレート、メトキシポリテトラメチレングリコール（メタ）アクリレート、フェノキシテトラエチレングリコール（メタ）アクリレート、ヘキサエチレングリコール（メタ）アクリレート、メトキシヘキサエチレングリコール（メタ）アクリレート等が挙げられる。
　前記帯電防止剤は、１種類のみで使用することも２種類以上組み合わせて使用することもできる。　前記帯電防止剤の添加量は、重合性組成物に含まれる重合性化合物の総量に対して、０．００１～１０重量％が好ましく、０．０１～５重量％がより好ましい。
（色素）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、必要に応じて色素を含有することができる。用いる色素は、特に限定はなく、配向性を乱さない範囲で公知慣用のものを含有することができる。
　前記色素としては、例えば、２色性色素、蛍光色素等が挙げられる。そのような色素としては、例えば、ポリアゾ色素、アントラキノン色素、シアニン色素、フタロシアニン色素、ペリレン色素、ペリノン色素、スクアリリウム色素等が挙げられるが、添加する観点から、前記色素は液晶性を示す色素が好ましい。
　例えば、米国特許第２，４００，８７７号公報、DreyerJ. F., Phys. and Colloid Chem., 1948, 52, 808., "The Fixing of MolecularOrientation"、Dreyer J. F., Journal de Physique, 1969, 4, 114., "LightPolarization from Films of Lyotropic Nematic Liquid Crystals"、及び、J.Lydon, "Chromonics" in "Handbook of Liquid Crystals Vol.2B: Low MolecularWeight Liquid Crystals II", D. Demus,J. Goodby, G. W. Gray, H. W. Spiessm,V. Vill ed, Willey-VCH, P.981-1007(1998) 、Dichroic Dyes for Liquid Crystal Display A．V．lvashchenko
CRC Press、1994年、および「機能性色素市場の新展開」、第一章、１頁、1994年、ＣＭＣ株式会社発光、等に記載の色素を使用することができる。
　２色性色素としては、例えば、以下の式（ｄ－１）～式（ｄ－８）
Figure JPOXMLDOC01-appb-C000152
Figure JPOXMLDOC01-appb-C000153
が挙げられる。前記２色性色素等の色素の添加量は、重合性組成物に含まれる重合性化合物の総量の総量に対して、０．００１～１０重量％が好ましく、０．０１～５重量％がより好ましい。
（フィラー）
　本発明の位相差フィルムを作製するために用いる重合性組成物には、必要に応じてフィラーを含有することができる。用いるフィラーは、特に限定はなく、得られた重合物の熱伝導性が低下しない範囲で公知慣用のものを含有することができる。
　前記フィラーとしては、例えば、アルミナ、チタンホワイト、水酸化アルミニウム、タルク、クレイ、マイカ、チタン酸バリウム、酸化亜鉛、ガラス繊維等の無機質充填材、銀粉、銅粉などの金属粉末や窒化アルミニウム、窒化ホウ素、窒化ケイ素、窒化ガリウム、炭化ケイ素、マグネシア（酸化アルミニウム）、アルミナ（酸化アルミニウム）、結晶性シリカ（酸化ケイ素）、溶融シリカ（酸化ケイ素）等などの熱伝導性フィラー、銀ナノ粒子等が挙げられる。
（重合性基を有する非液晶性化合物）
　本発明の位相差フィルムを作製するために用いられる重合性組成物には、重合性基を有するが液晶化合物ではない化合物を添加することもできる。このような化合物としては、通常、この技術分野で重合性モノマーあるいは重合性オリゴマーとして認識されるものであれば特に制限なく使用することができる。添加する場合は、重合性組成物に用いる重合性化合物の合計量に対して、１５質量％以下であることが好ましく、１０質量％以下が更に好ましい。
　具体的には、メチル（メタ）アクリレート、エチル（メタ）アクリレート、２－ヒドロキシエチルアクリレート、プロピル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、２－ヒドロキシブチル（メタ）アクリレート、オクチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ドデシル（メタ）アクリレート、ステアリル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、ジシクロペンタニルオキシルエチル（メタ）アクリレート、イソボルニルオキシルエチル（メタ）アクリレート、イソボルニル（メタ）アクリレート、アダマンチル（メタ）アクリレート、ジメチルアダマンチル（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレート、ジシクロペンテニル（メタ）アクリレート、メトキシエチル（メタ）アクリレート、エチルカルビトール（メタ）アクリレート、テトラヒドロフルフリル（メタ）アクリレート、ベンジル（メタ）アクリレート、フェノキシエチル（メタ）アクリレート、２－フェノキシジエチレングリコール（メタ）アクリレート、２－ヒドロキシ－３－フェノキシエチル（メタ）アクリレート、（２－メチル－２－エチル－１，３－ジオキソラン－４－イル）メチル（メタ）アクリレート、（３－エチルオキセタン－３－イル）メチル（メタ）アクリレート、ｏ－フェニルフェノールエトキシ（メタ）アクリレート、ジメチルアミノ（メタ）アクリレート、ジエチルアミノ（メタ）アクリレート、２，２，３，３，３－ペンタフルオロプロピル（メタ）アクリレート、２，２，３，４，４，４－ヘキサフルオロブチル（メタ）アクリレート、２，２，３，３，４，４，４－ヘプタフルオロブチル（メタ）アクリレート、２－（パーフルオロブチル）エチル（メタ）アクリレート、２－（パーフルオロヘキシル）エチル（メタ）アクリレート、１Ｈ，１Ｈ，３Ｈ－テトラフルオロプロピル（メタ）アクリレート、１Ｈ，１Ｈ，５Ｈ－オクタフルオロペンチル（メタ）アクリレート、１Ｈ，１Ｈ，７Ｈ－ドデカフルオロヘプチル（メタ）アクリレート、１Ｈ－１－（トリフルオロメチル）トリフルオロエチル（メタ）アクリレート、１Ｈ，１Ｈ，３Ｈ－ヘキサフルオロブチル（メタ）アクリレート、１，２，２，２－テトラフルオロ－１－（トリフルオロメチル）エチル（メタ）アクリレート、１Ｈ，１Ｈ－ペンタデカフルオロオクチル（メタ）アクリレート、１Ｈ，１Ｈ，２Ｈ，２Ｈ－トリデカフルオロオクチル（メタ）アクリレート、２－（メタ）アクリロイルオキシエチルフタル酸、２－（メタ）アクリロイルオキシエチルヘキサヒドロフタル酸、グリシジル（メタ）アクリレート、２－（メタ）アクリロイルオキシエチルりん酸、アクリロイルモルホリン、ジメチルアクリルアミド、ジメチルアミノプロピルアクリルアミド、イロプロピルアクリルアミド、ジエチルアクリルアミド、ヒドロキシエチルアクリルアミド、Ｎ－アクリロイルオキシエチルヘキサヒドロフタルイミド等のモノ（メタ）アクリレート、１，４－ブタンジオールジ（メタ）アクリレート、１，６－ヘキサンジオールジ（メタ）アクリレート、１，９－ノナンジオールジ（メタ）アクリレート、ネオペンチルジオールジ（メタ）アクリレート、トリプロピレングリコールジ（メタ）アクリレート、エチレングリコールジ（メタ）アクリレート、ジエチレングリコールジ（メタ）アクリレート、トリエチレングリコールジ（メタ）アクリレート、エチレンオキサイド変性ビスフェノールＡジ（メタ）アクリレート、トリシクロデカンジメタノールジ（メタ）アクリレート、９，９－ビス[４－（２－アクリロイルオキシエトキシ）フェニル]フルオレン、グリセリンジ（メタ）アクリレート、２－ヒドロキシ－３－アクロイルオキシプロピルメタクリレート、１，６－ヘキサンジオールジグリシジルエーテルのアクリル酸付加物、１，４－ブタンジオールジグリシジルエーテルのアクリル酸付加物、等のジアクリレート、トリメチロールプロパントリ（メタ）アクリレート、エトキシ化イソシアヌル酸トリアクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ε－カプロラクトン変性トリス－（２－アクリロイルオキシエチル）イソシアヌレート、等のトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ジトリメチロールプロパンテトラ（メタ）アクリレート、等のテトラ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、オリゴマー型の（メタ）アクリレート、各種ウレタンアクリレート、各種マクロモノマー、エチレングリコールジグリシジルエーテル、ジエチレングリコールジグリシジルエーテル、プロピレングリコールジグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、１，６－ヘキサンジオールジグリシジルエーテル、グリセリンジグリシジルエーテル、ビスフェノールＡジグリシジルエーテル、等のエポキシ化合物、マレイミド等が挙げられる。これらは単独で使用することもできるし、２種類以上混合して使用することもできる。
（配向材料）
　本発明の位相差フィルムを作製するために用いられる重合性組成物には、その配向性を向上させるために配向性が向上する配向材料を含有することができる。用いる配向材料は、重合性組成物に用いられる、重合性基を有する液晶性化合物を溶解させることができる溶剤に可溶であれば、公知慣用のものでよいが、添加することにより配向性を著しく劣化させない範囲で添加することができる。具体的には、重合性液晶組成物に含まれる重合性液晶性化合物の総量に対して０．０５～３０重量％が好ましく、０．５～１５重量％がさらに好ましく、１～１０重量％が特に好ましい。
　配向材料は具体的には、ポリイミド、ポリアミド、ＢＣＢ（ペンゾシクロブテンポリマー）、ポリビニルアルコール、ポリカーボネート、ポリスチレン、ポリフェニレンエーテル、ポリアリレート、ポリエチレンテレフタレート、ポリエーテルサルフォン、エポキシ樹脂、エポキシアクリレート樹脂、アクリル樹脂、クマリン化合物、カルコン化合物、シンナメート化合物、フルギド化合物、アントラキノン化合物、アゾ化合物、アリールエテン化合物等、光異性化、もしくは、光二量化する化合物が挙げられるが、紫外線照射、可視光照射により配向する材料（光配向材料）が好ましい。
　光配向材料としては、例えば、環状シクロアルカンを有するポリイミド、全芳香族ポリアリレート、特開５－２３２４７３号公報に示されているようなポリビニルシンナメート、パラメトキシ桂皮酸のポリビニルエステル、特開平６－２８７４５３、特開平６－２８９３７４号公報に示されているようなシンナメート誘導体、特開２００２－２６５５４１号公報に示されているようなマレイミド誘導体等が挙げられる。具体的には、以下の式（１２－１）～式（１２－７）で表される化合物が好ましい。
Figure JPOXMLDOC01-appb-C000154
　（式中、Ｒは水素原子、ハロゲン原子、炭素原子数１～３のアルキル基、アルコキシ基、ニトロ基、Ｒ‘は水素原子、炭素原子数１～１０のアルキル基を示すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、末端のＣＨ３は、ＣＦ３、ＣＣｌ３、シアノ基、ニトロ基、イソシアノ基、チオイソシアノ基に置換されても良い。ｎは４～１０００００を示し、ｍは１～１０の整数を示す。）
（位相差フィルム及び位相差フィルムの製造方法）
（位相差フィルム）
　本発明の位相差フィルムを作製するために用いられる重合性組成物を、基材、あるいは、配向機能を有する基材上に塗布し、重合性液晶組成物中の液晶分子を、ネマチック相やスメクチック相を保持した状態で均一に配向させ、重合させることによって、本発明の位相差フィルムを得ることができる。
　本発明の位相差フィルムはハイブリッド配向を有する。ハイブリッド配向とは［図１］、［図２］に示すように、基板界面でのチルト角と、空気界面でのチルト角が大きく異なる配向状態を有するものである。基板界面でのチルト角は０～４５°が好ましく、０～２０°がより好ましく、０～１０°が更により好ましく、０～５°が更により好ましく、０～３°が最も好ましい。空気界面でのチルト角は４５～９０°が好ましく５０～８０°がより好ましく、５５～７５°が更により好ましい。また、上記チルト角は［図２］のように基板界面と空気界面とが逆になってもよい。
　また、重合性液晶組成物中の液晶分子が基板面内でねじれた構造を保持した状態で配向することも好ましい。ねじれた構造とは［図３］に示すような配向状態を示す。基板界面での配向方向と、空気界面での配向方向とがなす角度はツイスト角と称される。ツイスト角は１０～８０°が好ましく、２５～８０°がより好ましく、３０～７０°が更により好ましく、４５～６５°が最も好ましい。
（基材）
　本発明の位相差フィルムに用いられる基材は、液晶表示素子、有機発光表示素子、その他表示素子、光学部品、着色剤、マーキング、印刷物や光学フィルムに通常使用する基材であって、重合性組成物溶液の塗布後の乾燥時における加熱に耐えうる耐熱性を有する材料であれば、特に制限はない。そのような基材としては、ガラス基材、金属基材、セラミックス基材、プラスチック基材や紙等の有機材料が挙げられる。特に基材が有機材料の場合、セルロース誘導体、ポリオレフィン、ポリエステル、ポリオレフィン、ポリカーボネート、ポリアクリレート、ポリアリレート、ポリエーテルサルホン、ポリイミド、ポリフェニレンスルフィド、ポリフェニレンエーテル、ナイロン又はポリスチレン等が挙げられる。中でもポリエステル、ポリスチレン、ポリオレフィン、セルロース誘導体、ポリアリレート、ポリカーボネート等のプラスチック基材が好ましい。基材の形状としては、平板の他、曲面を有するものであっても良い。これらの基材は、必要に応じて、電極層、反射防止機能、反射機能を有していてもよい。
　本発明の位相差フィルムを作製するために用いられる重合性組成物の塗布性や重合体との接着性向上のために、これらの基材の表面処理を行っても良い。表面処理として、オゾン処理、プラズマ処理、コロナ処理、シランカップリング処理などが挙げられる。また、光の透過率や反射率を調節するために、基材表面に有機薄膜、無機酸化物薄膜や金属薄膜等を蒸着など方法によって設ける、あるいは、光学的な付加価値をつけるために、基材がピックアップレンズ、ロッドレンズ、光ディスク、位相差フィルム、光拡散フィルム、カラーフィルター、等であっても良い。中でも付加価値がより高くなるピックアップレンズ、位相差フィルム、光拡散フィルム、カラーフィルターは好ましい。
（配向処理）
　また、上記基材には、本発明の位相差フィルムを作製するために用いられる重合性組成物を塗布乾燥した際に重合性組成物が配向するように、通常配向処理が施されている、あるいは配向膜が設けられていても良い。配向処理としては、延伸処理、ラビング処理、偏光紫外可視光照射処理、イオンビーム処理、基材へのＳｉＯ２の斜方蒸着処理、等が挙げられる。配向膜を用いる場合、配向膜は公知慣用のものが用いられる。そのような配向膜としては、ポリイミド、ポリシロキサン、ポリアミド、ポリビニルアルコール、ポリカーボネート、ポリスチレン、ポリフェニレンエーテル、ポリアリレート、ポリエチレンテレフタレート、ポリエーテルサルホン、エポキシ樹脂、エポキシアクリレート樹脂、アクリル樹脂、アゾ化合物、クマリン化合物、カルコン化合物、シンナメート化合物、フルギド化合物、アントラキノン化合物、アゾ化合物、アリールエテン化合物等の化合物、もしくは、前記化合物の重合体や共重合体が挙げられる。ラビングにより配向処理する化合物は、配向処理、もしくは配向処理の後に加熱工程を入れることで材料の結晶化が促進されるものが好ましい。ラビング以外の配向処理を行う化合物の中では光配向材料を用いることが好ましい。
　一般に、配向機能を有する基板に液晶組成物を接触させた場合、液晶分子は基板付近で基板を配向処理した方向に沿って配向する。液晶分子が基板と水平に配向するか、傾斜あるいは垂直して配向するかは、基板への配向処理方法によりコントロールすることができる。例えば、ポリイミド等をラビング処理した場合は、ラビング方向に基板界面側はわずかにチルトした配向状態となる。また、光配向膜の中でも、斜め方向から偏光紫外線を照射することにより基板界面側にチルト角を形成させることができる材料もある。一般的に光配向膜を垂直方向から偏光紫外線露光をしたものは基板界面側のチルト角が約０°となることが多い。その他、ＳｉＯ２の斜方蒸着により基板界面側にチルト角を着ける方法もある。一方、空気界面側のチルト角は前述の界面活性剤や配向制御剤の種類や添加量により調整することができる
　一方、ツイスト角を形成させるためには、重合性組成物に前述のキラル化合物を添加する手法が一般的である、ツイスト角は添加するキラル化合物の添加量により調整することができる。
（塗布）
　本発明の位相差フィルムを得るための塗布法としては、アプリケーター法、バーコーティング法、スピンコーティング法、ロールコーティング法、ダイレクトグラビアコーティング法、リバースグラビアコーティング法、フレキソコーティング法、インクジェット法、ダイコーティング法、キャップコーティング法、ディップコーティング法、スリットコーティング法、スプレーコーティング法等、公知慣用の方法を行うことができる。重合性組成物を塗布後、乾燥させる。
　塗布後、重合性組成物中の液晶分子をスメクチック相、あるいはネマチック相を保持した状態で均一に配向させることが好ましい。その方法の１つとして熱処理法が挙げられる。具体的には、本重合性組成物を基板上に塗布後、該液晶組成物のＮ（ネマチック相）－Ｉ（等方性液体相）転移温度（以下、Ｎ－Ｉ転移温度と略す）以上に加熱して、該液晶組成物を等方相液体状態にする。そこから、必要に応じ徐冷してネマチック相を発現させる。このとき、一旦液晶相を呈する温度に保ち、液晶相ドメインを充分に成長させてモノドメインとすることが望ましい。あるいは、重合性組成物を基板上に塗布後、重合性組成物のネマチック相が発現する温度範囲内で温度を一定時間保つような加熱処理を施しても良い。
　加熱温度が高過ぎると重合性液晶化合物が好ましくない重合反応を起こして劣化するおそれがある。また、冷却しすぎると、重合性組成物が相分離を起こし、結晶の析出、スメクチック相のような高次液晶相を発現し、配向処理が不可能になることがある。
　このような熱処理をすることで、単に塗布するだけの塗工方法と比べて、配向欠陥の少ない均質な位相差フィルムを作製することができる。
　また、このようにして均質な配向処理を行った後、液晶相が相分離を起こさない最低の温度、即ち過冷却状態となるまで冷却し、該温度において液晶相を配向させた状態で重合すると、より配向秩序が高く、透明性に優れる位相差フィルムを得ることができる。
（重合工程）
　乾燥した重合性組成物の重合処理は、一様に配向した状態で一般に可視紫外線等の光照射、あるいは加熱によって行われる。重合を光照射で行う場合は、具体的には４２０ｎｍ以下の可視紫外光を照射することが好ましく、２５０～３７０ｎｍの波長の紫外光を照射することが最も好ましい。但し、４２０ｎｍ以下の可視紫外光により重合性組成物が分解などを引き起こす場合は、４２０ｎｍ以上の可視紫外光で重合処理を行ったほうが好ましい場合もある。
（重合方法）
　本発明の位相差フィルムを作製するために用いられるの重合性組成物を重合させる方法としては、活性エネルギー線を照射する方法や熱重合法等が挙げられるが、加熱を必要とせず、室温で反応が進行することから活性エネルギー線を照射する方法が好ましく、中でも、操作が簡便なことから、紫外線等の光を照射する方法が好ましい。照射時の温度は、重合性組成物が液晶相を保持できる温度とし、重合性組成物の熱重合の誘起を避けるため、可能な限り３０℃以下とすることが好ましい。尚、重合性液晶組成物は、通常、昇温過程において、Ｃ（固相）－Ｎ（ネマチック）転移温度（以下、Ｃ－Ｎ転移温度と略す。）から、Ｎ－Ｉ転移温度範囲内で液晶相を示す。一方、降温過程においては、熱力学的に非平衡状態を取るため、Ｃ－Ｎ転移温度以下でも凝固せず液晶状態を保つ場合がある。この状態を過冷却状態という。本発明においては、過冷却状態にある液晶組成物も液晶相を保持している状態に含めるものとする。具体的には３９０ｎｍ以下の紫外光を照射することが好ましく、２５０～３７０ｎｍの波長の光を照射することが最も好ましい。但し、３９０ｎｍ以下の紫外光により重合性組成物が分解などを引き起こす場合は、３９０ｎｍ以上の紫外光で重合処理を行ったほうが好ましい場合もある。この光は、拡散光で、かつ偏光していない光であることが好ましい。紫外線照射強度は、０．０５ｋＷ／ｍ２～１０ｋＷ／ｍ２の範囲が好ましい。特に、０．２ｋＷ／ｍ２～２ｋＷ／ｍ２の範囲が好ましい。紫外線強度が０．０５ｋＷ／ｍ２未満の場合、重合を完了させるのに多大な時間がかかる。一方、２ｋＷ／ｍ２を超える強度では、重合性組成物中の液晶分子が光分解する傾向にあることや、重合熱が多く発生して重合中の温度が上昇し、重合性液晶のオーダーパラメーターが変化して、重合後のフィルムのリタデーションに狂いが生じる可能性がある。
　マスクを使用して特定の部分のみを紫外線照射で重合させた後、該未重合部分の配向状態を、電場、磁場又は温度等をかけて変化させ、その後該未重合部分を重合させると、異なる配向方向をもった複数の領域を有する位相差フィルムを得ることもできる。
　また、マスクを使用して特定の部分のみを紫外線照射で重合させる際に、予め未重合状態の重合性液晶組成物に電場、磁場又は温度等をかけて配向を規制し、その状態を保ったままマスク上から光を照射して重合させることによっても、異なる配向方向をもった複数の領域を有する位相差フィルムを得ることができる。
　本発明に用いられる重合性液晶組成物を重合させて得られる位相差フィルムは、基板から剥離して単体で位相差フィルムとして使用することも、基板から剥離せずにそのまま位相差フィルムとして使用することもできる。特に、他の部材を汚染し難いので、被積層基板として使用したり、他の基板に貼り合わせて使用したりするときに有用である。
（楕円偏光板）
　本発明の位相差フィルムを直線偏光板と張り合わせることで、本発明の楕円偏光板を作製することができる。直線偏光板としては通常、偏光子の片側または両側に保護フィルムを有するものが使用される。偏光子は、特に制限されず、各種のものを使用でき、例えば、ポリビニルアルコール系フィルム、部分ホルマール化ポリビニルアルコール系フィルム、エチレン・酢酸ビニル共重合体系部分ケン化フィルム等の親水性高分子フィルムに、ヨウ素や二色性染料等の二色性物質を吸着させて一軸延伸したもの、ポリビニルアルコールの脱水処理物やポリ塩化ビニルの脱塩酸処理物等のポリエン系配向フィルム等が挙げられる。これらのなかでもポリビニルアルコール系フィルムを延伸して二色性材料（沃素、染料）を吸着・配向したものが好適に用いられる。また、ワイヤーグリッド型偏光板等を用いてもよい。
　本発明の位相差フィルムと偏光板とを張り合わせるとき、ツイスト角が約０°の場合は偏光板の吸収軸と位相差板の遅相軸との角度が４０～５０°であることが好ましく、４３～４７°であることがより好ましく、４５°であることが最も好ましい。またツイスト角がある場合は、偏光板の吸収軸と偏光板に近い面の遅相軸との角度が６０～１００°であることが好ましく、７０～９０°であることがより好ましく、８０～９０°であることが更により好ましい。また偏光板の吸収軸と偏光板から遠い面での遅相軸との角度が０～６０°であることが好ましく、１０～５０°であることがより好ましく、２０～４０°であることが更により好ましい。
　上記楕円偏光板は上述のように、本発明の位相差フィルムを直線偏光板と張り合わせること以外にも、偏光板上に本発明に用いる重合性組成物を直接塗布して、偏光板上に位相差フィルム層を直接形成することもできる。
（液晶表示素子）
　本発明の位相差フィルムは液晶表示素子に用いることもできる。液晶表示素子は、少なくとも二つの基材に液晶媒体層、ＴＦＴ駆動回路、ブラックマトリックス層、カラーフィルター層、スペーサー、液晶媒体層に相応の電極回路が最低限狭持されており、通常、光学補償層、偏光板層、タッチパネル層は二つの基材の外側に配置されるが、場合によっては、光学補償層、オーバーコート層、偏光板層、タッチパネル用の電極層が二つの基材内に狭持されてもよい。
　液晶表示素子の配向モードとしては、ＴＮモード、ＶＡモード、ＩＰＳモード、ＦＦＳモード、ＯＣＢモード等があるが、光学補償フィルムや光学補償層で用いられる場合には、配向モードに相応する位相差を有するフィルムを作成することができる。パターン化された位相差フィルムで使用することもできる。
（有機発光表示素子）
　本発明の位相差フィルム、及び楕円偏光板は、本発明の有機発光表示素子に使用することができる。使用形態としては、有機発光表示素子の反射防止フィルムとして使用することができる。
　以下に本発明を実施例、及び、比較例によって説明するが、もとより本発明はこれらに限定されるものではない。なお、特に断りのない限り、「部」及び「％」は質量基準である。
（重合性組成物（１））
　式（２－ａ－４０）で表される化合物１００部をシクロペンタノン(ＣＰＮ)２５０部に加えた後、６０℃に加温、撹拌して溶解させ、溶解が確認された後、室温に戻し、イルガキュアＯＸＥ０１（ＯＸＥ０１:ＢＡＳＦ社製）５部、ｐ－メトキシフェノール（ＭＥＨＱ）０．１部、及び、メガファックＦ－５５６（Ｆ－５５６:ＤＩＣ株式会社製）０．２部を加えてさらに撹拌を行い、溶液を得た。溶液は透明で均一であった。得られた溶液を０．２０μｍのメンブランフィルターでろ過し、実施例用の重合性組成物（１）を得た。
（重合性組成物（２）～（３６））
　下記表に示す各化合物をそれぞれ下記表に示す割合に変更した以外は重合性組成物（１）の調整と同一条件で、実施例用の重合性組成物（２）～（３４）及び比較例用の重合性組成物（３５）～（３６）を得た。
　下記表１～５に、本発明用の重合性組成物（１）～（３４）、比較例用の重合性組成物（３５）～（３６）の具体的な組成を示す。
Figure JPOXMLDOC01-appb-T000155
Figure JPOXMLDOC01-appb-T000156
Figure JPOXMLDOC01-appb-T000157
Figure JPOXMLDOC01-appb-T000158
Figure JPOXMLDOC01-appb-T000159
Figure JPOXMLDOC01-appb-C000160
Figure JPOXMLDOC01-appb-C000161
Figure JPOXMLDOC01-appb-C000162
Figure JPOXMLDOC01-appb-C000163
Figure JPOXMLDOC01-appb-C000164
Figure JPOXMLDOC01-appb-C000165
Figure JPOXMLDOC01-appb-C000166
Figure JPOXMLDOC01-appb-C000167
Figure JPOXMLDOC01-appb-C000168
Figure JPOXMLDOC01-appb-C000169
Figure JPOXMLDOC01-appb-C000170
Figure JPOXMLDOC01-appb-C000171
　上記化合物のＲｅ（４５０ｎｍ）／Ｒｅ（５５０ｎｍ）は、それぞれ以下のとおりである。式（１－ａ―９０）：０．７６、式（１－ａ―９２）：０．８３、式（１－ａ―９３）：０．８５、式（２－ａ－４０：０．８３、式（２－ａ－４２）：０．８３、式（２－ａ－４６）：０．８４、式（２－ａ－４７）：０．８０、式（２－ａ－４８）：０．８２、式（２－ａ－４９）：０．８１、式（２－ａ－５０）：０．７９、式（２－ａ－５１）：０．７８、式（２－ａ－５２）：０．８２、式（２－ａ－５３）：０．７５、式（２－ａ－５４）：０．７７、式（２－ａ－５５）：０．７２、式（２－ａ－５６）：０．８３、式（２－ａ－５７）：０．７２、式（２－ａ－５９）：０．８３、式（２－ａ－６０）：０．８４、式（２－ａ－６２）：０．８３、式（２－ａ－６３）：０．８２、式（２－ａ－６６）：０．７７、式（２－ａ－６８）である。
（重合性組成物（１）～（３６）を用いた位相差フィルムの評価）
　上記重合性組成物（１）～（３６）の各組成物を以下の条件で位相差フィルム（１）～（３４）（実施例１～３４）、位相差フィルム（３５）（比較例１）、位相差フィルム（３６）（比較例２）を作製した。
　ポリエチレンナフタレートフィルム基材（帝人社製ＰＥＮ）に３％のポリビニルアルコール溶液（溶媒は純水とエタノールの重量比１：１の混合液）をスピンコートし、１２０℃で５分乾燥後、レーヨン布でラビング処理をした。このＰＶＡ膜上に重合性組成物（１）～（３６）をそれぞれスピンコーターで、５５０ｎｍでの位相差が１３８±５ｎｍとなるように調節しながら塗布した後、８０℃で３分間乾燥し、更に６０℃で５分放置した。得られた重合性組成物の塗布物に、ＵＶＢのエネルギーが１Ｊ／ｃｍ２のエネルギーを持つ紫外線を照射した。得られた位相差フィルムを基板から剥離し位相差フィルムの薄膜を得た。
　各位相差フィルムの（式１－１）：Ｒｅ（４５０ｎｍ）／Ｒｅ（５５０ｎｍ）の値、ＰＥＮ基材側であった液晶のチルト角と空気界面側の液晶のチルト角、及びツイスト角を表６に示す。なお、（式１－１）の値は、位相差測定装置ＲＥＴ－１００（大塚電子社製）を用いて測定し、チルト角については、チルト角測定器（ＡｘｏＳｃａｎ、ＡＸＯＭＲＥＴＲＩＣＳ社製）にて測定し、フィッティングによって数値を算出した。ツイスト角については、あらかじめ重合性液晶組成物とキラル剤とのＰＣ値（Ｐ：ピッチ長、Ｃ：添加濃度）の関係を測定しておき、キラル化合物の添加量から計算値で求めた。
　この位相差フィルム薄膜と市販の偏光板を、位相差フィルムの基板側であった面が偏光板と接し、且つ基板側であった面の遅相軸の方向と偏光板の吸収軸の角度（張り合わせ角度）が表６、表７の数値になるように張り合わせて楕円偏光板を作製した。
Figure JPOXMLDOC01-appb-T000172
Figure JPOXMLDOC01-appb-T000173
　この位相差フィルム薄膜と市販の偏光板を、基板側であった面の遅相軸の方向と偏光板の吸収軸の角度、及び空気界面側であった面の遅相軸と偏光板の吸収軸の角度が表８、表９に示す数値になるように、位相差フィルムの基板側であった面と偏光板とを張り合わせて、楕円偏光板を作製した。
Figure JPOXMLDOC01-appb-T000174
Figure JPOXMLDOC01-appb-T000175
（実施例１～３４、比較例１～２）
　上記の方法で作製された楕円偏光板を用いて、以下の評価基準に基づき視認性の評価を行った。
（視認性評価）
（色目）
　色目については、有機ＥＬパネル搭載のＳＡＭＳＵＮＧ社製ＧＡＬＡＸＹ ＳＩＩにおいて、用いられている円偏光板の変わりに、上記の楕円偏光板を張り合わせて、正面又は斜め４５°からの黒色の色味づきを下記基準で評価した。
Ａ：反射光の色づきがほとんど視認されない。（許容）
Ｂ：反射光の色づきがごくわずかに視認されるが実用上問題ない。（許容）
Ｃ：反射光の色づきが少し視認されるが実用上問題ない。（許容）
Ｄ：反射光の色づきが視認される、用途によっては許容できる。（許容）
Ｅ：反射光の色づきが強く視認され、許容できない。

また、使用した楕円偏光板を８０℃の恒温層に５００時間放置した後の色目の評価も同様の基準で行った。
結果を表１０、表１１に示す。
Figure JPOXMLDOC01-appb-T000176
Figure JPOXMLDOC01-appb-T000177
　上記の結果より、比較例の構成に比べて実施例の構成は、高温放置後の色目が優れていることが分かる。

Claims (10)

  1. 位相差層を有する位相差フィルムであって、該光学フィルムが（式１－１）を満たし、
    Ｒｅ（４５０）／Ｒｅ（５５０）＜１　（式１－１）
    （式中、Ｒｅ（４５０）は波長４５０ｎｍにおける面内の位相差を表し、Ｒｅ（５５０）は波長５５０ｎｍにおける面内の位相差を表す。）
    該位相差層を形成する材料が少なくとも１種類以上の下記一般式（１）～（７）からなる群から選ばれる重合性液晶性化合物を含有する重合性組成物であり、
    該位相差層がハイブリッド構造をとることを特徴とする位相差フィルム。
    Figure JPOXMLDOC01-appb-C000001
     （式中、Ｐ１１～Ｐ７４は重合性基を表し、
    Ｓ１１～Ｓ７２はスペーサー基を又は単結合を表すが、Ｓ１１～Ｓ７２が複数存在する場合それらは各々同一であっても異なっていても良く、
    Ｘ１１～Ｘ７２は－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｘ１１～Ｘ７２が複数存在する場合それらは各々同一であっても異なっていても良く（ただし、各Ｐ－（Ｓ－Ｘ）－結合には－Ｏ－Ｏ－を含まない。）、
    ＭＧ１１～ＭＧ７１は各々独立して式（ａ）を表し、
    Figure JPOXMLDOC01-appb-C000002
     （式中、
    Ａ１１、Ａ１２は各々独立して１，４－フェニレン基、１，４－シクロヘキシレン基、ピリジン－２，５－ジイル基、ピリミジン－２，５－ジイル基、ナフタレン－２，６－ジイル基、ナフタレン－１，４－ジイル基、テトラヒドロナフタレン－２，６－ジイル基、デカヒドロナフタレン－２，６－ジイル基又は１，３－ジオキサン－２，５－ジイル基を表すが、これらの基は無置換又は１つ以上のＬ１によって置換されても良いが、Ａ１１及び／又はＡ１２が複数現れる場合は各々同一であっても異なっていても良く、
    Ｚ１１及びＺ１２は各々独立して－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＨ２ＣＨ２－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－、－Ｎ＝ＣＨ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｚ１１及び／又はＺ１２が複数現れる場合は各々同一であっても異なっていても良く、
    Ｍは下記の式（Ｍ－１）から式（Ｍ－１１）
    Figure JPOXMLDOC01-appb-C000003
     から選ばれる基を表すが、これらの基は無置換又は１つ以上のＬ１によって置換されても良く、
    Ｇは下記の式（Ｇ－１）から式（Ｇ－６）
    Figure JPOXMLDOC01-appb-C000004
     （式中、Ｒ３は水素原子、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、
    Ｗ８１は少なくとも１つの芳香族基を有する、炭素原子数５から３０の基を表すが、当該基は無置換又は１つ以上のＬ１によって置換されても良く、
    Ｗ８２は水素原子、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子及び／又は－ＯＨに置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－によって置換されても良く、若しくは、Ｗ８２はＷ８１と同様の意味を表しても良く、また、Ｗ８１及びＷ８２は互いに連結し同一の環構造を形成しても良く、若しくはＷ８２はＰ８－（Ｓ８－Ｘ８）ｊ－で表される基を表しても良く、Ｐ８は重合性基を表し、Ｓ８はスペーサー基又は単結合を表すが、Ｓ８が複数存在する場合それらは同一であっても異なっていても良く、Ｘ８は－Ｏ－、－Ｓ－、－ＯＣＨ２－、－ＣＨ２Ｏ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＳＣＨ２－、－ＣＨ２Ｓ－、－ＣＦ２Ｏ－、－ＯＣＦ２－、－ＣＦ２Ｓ－、－ＳＣＦ２－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＯＯ－ＣＨ２ＣＨ２－、－ＯＣＯ－ＣＨ２ＣＨ２－、－ＣＨ２ＣＨ２－ＣＯＯ－、－ＣＨ２ＣＨ２－ＯＣＯ－、－ＣＯＯ－ＣＨ２－、－ＯＣＯ－ＣＨ２－、－ＣＨ２－ＣＯＯ－、－ＣＨ２－ＯＣＯ－、－ＣＨ＝ＣＨ－、－Ｎ＝Ｎ－、－ＣＨ＝Ｎ－Ｎ＝ＣＨ－、－ＣＦ＝ＣＦ－、－Ｃ≡Ｃ－又は単結合を表すが、Ｘ８が複数存在する場合それらは同一であっても異なっていても良く（ただし、Ｐ８－（Ｓ８－Ｘ８）ｊ－には－Ｏ－Ｏ－結合を含まない。）、ｊは０から１０の整数を表し、
    Ｗ８３及びＷ８４はそれぞれ独立してハロゲン原子、シアノ基、ヒドロキシ基、ニトロ基、カルボキシル基、カルバモイルオキシ基、アミノ基、スルファモイル基、少なくとも１つの芳香族基を有する炭素原子数５から３０の基、炭素原子数１から２０のアルキル基、炭素原子数３から２０のシクロアルキル基、炭素原子数２から２０のアルケニル基、炭素原子数３から２０のシクロアルケニル基、炭素原子数１から２０のアルコキシ基、炭素原子数２から２０のアシルオキシ基、炭素原子数２から２０の又は、アルキルカルボニルオキシ基を表すが、前記アルキル基、シクロアルキル基、アルケニル基、シクロアルケニル基、アルコキシ基、アシルオキシ基、アルキルカルボニルオキシ基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、但し、上記Ｍが式（Ｍ－１）～式（Ｍ－１０）から選択される場合Ｇは式（Ｇ－１）～式（Ｇ－５）から選択され、Ｍが式（Ｍ－１１）である場合Ｇは式（Ｇ－６）を表し、
    Ｌ１はフッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、ニトロ基、イソシアノ基、アミノ基、ヒドロキシル基、メルカプト基、メチルアミノ基、ジメチルアミノ基、ジエチルアミノ基、ジイソプロピルアミノ基、トリメチルシリル基、ジメチルシリル基、チオイソシアノ基、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－、－ＣＨ＝ＣＨ－ＣＯＯ－、－ＣＨ＝ＣＨ－ＯＣＯ－、－ＣＯＯ－ＣＨ＝ＣＨ－、－ＯＣＯ－ＣＨ＝ＣＨ－、－ＣＨ＝ＣＨ－、－ＣＦ＝ＣＦ－又は－Ｃ≡Ｃ－から選択される基によって置換されても良いが、化合物内にＬ１が複数存在する場合それらは同一であっても異なっていても良く、
    ｊ１１は１から５の整数、ｊ１２は１～５の整数を表すが、ｊ１１＋ｊ１２は２から５の整数を表す。）、Ｒ１１及びＲ３１は水素原子、フッ素原子、塩素原子、臭素原子、ヨウ素原子、ペンタフルオロスルフラニル基、シアノ基、ニトロ基、イソシアノ基、チオイソシアノ基、又は、炭素原子数１から２０のアルキル基を表すが、当該アルキル基は直鎖状であっても分岐状であっても良く、当該アルキル基中の任意の水素原子はフッ素原子に置換されても良く、当該アルキル基中の１個の－ＣＨ２－又は隣接していない２個以上の－ＣＨ２－は各々独立して－Ｏ－、－Ｓ－、－ＣＯ－、－ＣＯＯ－、－ＯＣＯ－、－ＣＯ－Ｓ－、－Ｓ－ＣＯ－、－Ｏ－ＣＯ－Ｏ－、－ＣＯ－ＮＨ－、－ＮＨ－ＣＯ－又は－Ｃ≡Ｃ－によって置換されても良く、ｍ１１は０～８の整数を表し、ｍ２～ｍ７、ｎ２～ｎ７、ｌ４～ｌ６、ｋ６は各々独立して０から５の整数を表す。）
  2. 　前記重合性基Ｐ１１～Ｐ７４が一般式（Ｐ－１）から（Ｐ－２０）のいずれかで表される、請求項１に記載の位相差フィルム。
    Figure JPOXMLDOC01-appb-C000005
  3. 　前記重合性組成物中にキラル化合物を含有する、請求項１又は請求項２に記載の位相差フィルム。
  4. 　前記キラル化合物が重合性キラル化合物である、請求項３に記載の位相差フィルム。
  5. 　前記位相差フィルムの液晶組成物の一方の面方向のチルト角が０～２０°であり、もう一方の面方向のチルト角が４５～９０°である請求項１～４のいずれか一項に記載の位相差フィルム。
  6. 　前記位相差フィルムのツイスト角が２５～８０°である、請求項１～５のいずれか一項に記載の位相差フィルム。
  7. 請求項１～６のいずれか一項に記載の位相差フィルムと偏光板を張り合わせた楕円偏光板。
  8. 請求項１～６のいずれか一項に記載の位相差フィルムを配置した表示素子。
  9. 請求項７に記載の楕円偏光板を配置した表示素子。
  10. 請求項７に記載の楕円偏光板を配置した有機発光表示素子。
PCT/JP2017/024776 2016-07-15 2017-07-06 位相差フィルム、楕円偏光板及びそれを用いた表示装置 WO2018012390A1 (ja)