WO2017200169A1 - Particules creuses d'aluminosilicate et procédé pour leur fabrication - Google Patents

Particules creuses d'aluminosilicate et procédé pour leur fabrication Download PDF

Info

Publication number
WO2017200169A1
WO2017200169A1 PCT/KR2016/014721 KR2016014721W WO2017200169A1 WO 2017200169 A1 WO2017200169 A1 WO 2017200169A1 KR 2016014721 W KR2016014721 W KR 2016014721W WO 2017200169 A1 WO2017200169 A1 WO 2017200169A1
Authority
WO
WIPO (PCT)
Prior art keywords
shell
particles
hollow
core
aluminosilicate particles
Prior art date
Application number
PCT/KR2016/014721
Other languages
English (en)
Inventor
Moo-Hyun CHOI
Jun-Chan LEE
Eon-Sik KIM
Original Assignee
Advanced Nano Products Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Advanced Nano Products Co., Ltd. filed Critical Advanced Nano Products Co., Ltd.
Publication of WO2017200169A1 publication Critical patent/WO2017200169A1/fr

Abstract

L'invention concerne des particules creuses d'aluminosilicate et un procédé pour leur fabrication. Le procédé consiste à faire réagir un noyau de matrice, comprenant un polymère organique sous forme de micelle ou de micelle inverse, avec un composé de type silane et un précurseur d'aluminium pour synthétiser des particules de noyau-enveloppe présentant une enveloppe en aluminosilicate, qui sont ensuite amenées à réagir avec une solution aqueuse basique ou acide, ce qui forme de fins pores dans l'enveloppe et élimine simultanément le noyau, produisant ainsi des particules creuses d'aluminosilicate, et à effectuer une réaction hydrothermique de manière à augmenter la densité des particules creuses d'aluminosilicate. Ce procédé permet la formation d'une enveloppe uniforme même sans traitement supplémentaire de la surface du noyau par formation de charges négatives pendant la préparation d'un oxyde complexe par la réaction d'un précurseur d'aluminium et d'un précurseur de silice lors de la formation d'une enveloppe, ce qui permet d'obtenir des particules creuses dans lesquelles l'enveloppe n'est pas cassée pendant la réaction à haute densité mais est uniforme.
PCT/KR2016/014721 2016-05-18 2016-12-15 Particules creuses d'aluminosilicate et procédé pour leur fabrication WO2017200169A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020160060492A KR101659709B1 (ko) 2016-05-18 2016-05-18 중공형 알루미노실리케이트 입자 및 이의 제조방법
KR10-2016-0060492 2016-05-18

Publications (1)

Publication Number Publication Date
WO2017200169A1 true WO2017200169A1 (fr) 2017-11-23

Family

ID=57068244

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2016/014721 WO2017200169A1 (fr) 2016-05-18 2016-12-15 Particules creuses d'aluminosilicate et procédé pour leur fabrication

Country Status (3)

Country Link
KR (1) KR101659709B1 (fr)
TW (1) TWI634074B (fr)
WO (1) WO2017200169A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114534685A (zh) * 2022-02-22 2022-05-27 广东邦普循环科技有限公司 一种硅-铝-铁复合材料及其制备方法和应用

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101659709B1 (ko) * 2016-05-18 2016-09-26 주식회사 나노신소재 중공형 알루미노실리케이트 입자 및 이의 제조방법
KR102155270B1 (ko) * 2017-05-18 2020-09-11 주식회사 엘지화학 우수한 분산성을 갖는 알루미노실리케이트 입자의 제조 방법, 상기 알루미노실리케이트 입자를 포함한 고무 보강재 및 이를 포함한 타이어용 고무 조성물
KR20220132328A (ko) * 2021-03-23 2022-09-30 삼성에스디아이 주식회사 경화형 수지 조성물, 이로부터 제조되는 박막, 및 상기 박막을 포함하는 색 변환 패널 및 표시 장치
KR102610941B1 (ko) 2021-06-29 2023-12-07 주식회사 나노신소재 중공형 나노 입자 및 이의 제조방법, 이를 이용한 기능성 소재

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6319486B1 (en) * 1999-09-22 2001-11-20 Chinese Petroleum Corp. Control of morphology of mesoporous aluminosilicate or pure-silica molecular sieves by effect of alcohol
KR20100038170A (ko) * 2007-06-26 2010-04-13 덴끼 가가꾸 고교 가부시키가이샤 구상 유기 폴리머-실리콘 화합물 복합 입자, 중공 입자 및 그들의 제조 방법
US20100310539A1 (en) * 2008-02-11 2010-12-09 Alfronso Garcia-Bennett Method for manufacturing mesoporous materials, materials so produced and use of mesoporous materials
KR20140106959A (ko) * 2013-02-27 2014-09-04 주식회사 나노신소재 중공형 금속 산화물-실리케이트 나노입자 및 그 제조 방법
US20140287910A1 (en) * 2011-11-10 2014-09-25 China Petroleum & Chemical Corporation Hollow spherical zeolite im-5 and preparation method therefor
KR101659709B1 (ko) * 2016-05-18 2016-09-26 주식회사 나노신소재 중공형 알루미노실리케이트 입자 및 이의 제조방법

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3200623B2 (ja) * 1997-02-25 2001-08-20 経済産業省産業技術総合研究所長 中空球状ケイ酸塩クラスターの製造方法
JP5387331B2 (ja) 2008-10-31 2014-01-15 日立化成株式会社 中空状無機粒子の前駆体、中空状無機粒子及びこの製造方法、並びに中空状無機粒子を用いた光学部材及び光学部材体
JP5463099B2 (ja) 2009-08-21 2014-04-09 電気化学工業株式会社 中空シリカ粉末、その製造方法及び用途

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6319486B1 (en) * 1999-09-22 2001-11-20 Chinese Petroleum Corp. Control of morphology of mesoporous aluminosilicate or pure-silica molecular sieves by effect of alcohol
KR20100038170A (ko) * 2007-06-26 2010-04-13 덴끼 가가꾸 고교 가부시키가이샤 구상 유기 폴리머-실리콘 화합물 복합 입자, 중공 입자 및 그들의 제조 방법
US20100310539A1 (en) * 2008-02-11 2010-12-09 Alfronso Garcia-Bennett Method for manufacturing mesoporous materials, materials so produced and use of mesoporous materials
US20140287910A1 (en) * 2011-11-10 2014-09-25 China Petroleum & Chemical Corporation Hollow spherical zeolite im-5 and preparation method therefor
KR20140106959A (ko) * 2013-02-27 2014-09-04 주식회사 나노신소재 중공형 금속 산화물-실리케이트 나노입자 및 그 제조 방법
KR101659709B1 (ko) * 2016-05-18 2016-09-26 주식회사 나노신소재 중공형 알루미노실리케이트 입자 및 이의 제조방법

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114534685A (zh) * 2022-02-22 2022-05-27 广东邦普循环科技有限公司 一种硅-铝-铁复合材料及其制备方法和应用
WO2023160105A1 (fr) * 2022-02-22 2023-08-31 广东邦普循环科技有限公司 Matériau composite silicium-aluminium-fer, son procédé de préparation et son application
CN114534685B (zh) * 2022-02-22 2023-09-12 广东邦普循环科技有限公司 一种硅-铝-铁复合材料及其制备方法和应用
GB2621299A (en) * 2022-02-22 2024-02-07 Guangdong Brunp Recycling Technology Co Ltd Silicon-aluminum-iron composite material, and preparation method therefor and application thereof

Also Published As

Publication number Publication date
TWI634074B (zh) 2018-09-01
TW201741238A (zh) 2017-12-01
KR101659709B1 (ko) 2016-09-26

Similar Documents

Publication Publication Date Title
WO2017200169A1 (fr) Particules creuses d'aluminosilicate et procédé pour leur fabrication
WO2013009150A2 (fr) Film de dispersion à particules inorganiques présentant une bonne performance d'extraction de lumière
JP3280667B2 (ja) 透明導電性被膜形成用塗布液、その製造方法、導電性基材、その製造方法および透明導電性基材を備えた表示装置
WO2015137761A1 (fr) Procédé de préparation d'un matériau de revêtement conducteur en graphène à dissipation thermique faisant appel à un procédé sol-gel et à l'oxyde de graphène, et matériau de revêtement conducteur en graphène à dissipation thermique préparé par ledit procédé
WO2012008780A2 (fr) Composition de revêtement antiréfléchissant et antireflet, film antiréfléchissant et antireflet, et procédé de fabrication de celui-ci
WO2012157960A2 (fr) Substrat multicouche en plastique et son procédé de fabrication
WO2010068027A2 (fr) Composition d'isolant hybride organique-inorganique photosensible positif
US20010024685A1 (en) Method for forming a protective coating and substrates coated with the same
WO2011108787A1 (fr) Solution de revêtement bloquant la chaleur solaire et verre avec revêtement bloquant la chaleur solaire utilisant cette solution
WO2015152559A1 (fr) Composition à faible réfraction, procédé de préparation associé, et film conducteur transparent
WO2012165766A2 (fr) Composite creux à faible indice de réfraction, son procédé de fabrication et liquide de revêtement en contenant
WO2013089413A1 (fr) Composition de revêtement dur
WO2020080844A1 (fr) Film de protection contre la chaleur et procédé pour la fabrication de celui-ci
WO2018182111A1 (fr) Solution de type dispersion de nanotubes de carbone et son procédé de préparation
WO2016047988A1 (fr) Nitrure de bore modifié en surface, composition ayant des particules de celui-ci dispersées en son sein, et câble revêtu de la composition
WO2015167235A1 (fr) Film polyester et son procédé de fabrication
WO2022270704A1 (fr) Composition de revêtement antibactérien et procédé de fabrication d'un film optique comprenant des nanoparticules antibactériennes
WO2012173459A2 (fr) Composition ayant une réfraction élevée
WO2015199449A1 (fr) Composition de résine photosensible pour protection contre la lumière, et couche de protection contre la lumière formée à partir de cette composition
WO2015182878A9 (fr) Procédé de fabrication de particules de silice creuses, particules de silice creuses, et composition et feuille d'isolation thermique les comprenant
WO2023121162A1 (fr) Composition hybride organique/inorganique et film adhésif la comprenant
WO2023277355A1 (fr) Nanoparticules creuses, procédé pour la fabrication de celles-ci et matériau fonctionnel utilisant celles-ci
WO2021045453A1 (fr) Composition de résine durcissable, film durci formé à partir de celle-ci, et dispositif électronique ayant un film durci
WO2015084097A1 (fr) Film de résine et procédé de fabrication de film de résine
WO2018143623A1 (fr) Émulsion et procédé de préparation de cette émulsion

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2017513170

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16902536

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 16902536

Country of ref document: EP

Kind code of ref document: A1