WO2017182618A1 - Schlickergussverfahren zur herstellung von formkörpern - Google Patents

Schlickergussverfahren zur herstellung von formkörpern Download PDF

Info

Publication number
WO2017182618A1
WO2017182618A1 PCT/EP2017/059495 EP2017059495W WO2017182618A1 WO 2017182618 A1 WO2017182618 A1 WO 2017182618A1 EP 2017059495 W EP2017059495 W EP 2017059495W WO 2017182618 A1 WO2017182618 A1 WO 2017182618A1
Authority
WO
WIPO (PCT)
Prior art keywords
slurry
mold
dispersion
shaped body
slip casting
Prior art date
Application number
PCT/EP2017/059495
Other languages
English (en)
French (fr)
Inventor
Hermann Kaiser
Original Assignee
Ceramtec Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ceramtec Gmbh filed Critical Ceramtec Gmbh
Publication of WO2017182618A1 publication Critical patent/WO2017182618A1/de

Abstract

Gegenstand der Erfindung ist ein Schlicker umfassend Aluminitrid sowie ein Schlickergussverfahren zur Herstellung von Formkörpern aus Aluminiumnitridwerkstoffen.

Description

Schlickergussverfahren zur Herstellung von Formkörpern
Gegenstand der vorliegenden Erfindung ist ein Schlicker umfassend Aluminiumnitrid sowie ein Schlickergussverfahren zur Herstellung von Formkörpern aus Aluminiumnitridwerkstoffen und anderen in Pulverform mit Wasser unverträglichen Materialien. Grundsätzlich ist dieses Verfahren für alle Pulver geeignet.
Aluminiumnitrid (AIN) ist eine Keramik mit sehr hoher thermischer Leitfähigkeit bei sehr guten elektrischen Isolationseigenschaften. Daher wird Aluminumnitrid bisher überwiegend zur Abführung der Wärme in elektronischen Anwendungen eingesetzt. Es handelt sich überwiegend um Teile mit 2-dimensonaler Funktion, z. B. dünne Platten, die häufig auch metallisiert sind.
Mit dem Schlickergussverfahren werden seit über 100 Jahren Teile aus Keramik, insbesondere Porzellan hergestellt. Das Verfahren eignet sich besonders zur Herstellung von komplexen Formen und von Hohlkörpern. Dabei wird die wässrige Dispersion des gewünschten Werkstoffs (der Schlicker) in eine Form aus einem porösem Werkstoff, bevorzugt Gips gegossen und durch Wasserentzug verfestigt. Hat sich eine definierte Schicht („Scherben") an der Formoberfläche gebildet, wird der Schlicker ausgegossen. So werden auf der Innenseite sehr glatte Flächen erreicht. Hat sich der Scherben nach einiger Zeit weiter verfestigt, wird das gegossene Teil entnommen. Ebenso ist es möglich, Vollgußteile herzustellen, wenn der Schlicker in der Form bleibt, bis er sich vollständig verfestigt hat. Die verwendete Form kann ein- oder mehrteilig sein.
Das Problem bei der Verwendung von Aluminiumnitridwerkstoffen ist, dass Aluminiumnitrid in Pulverform mit Wasser unter Bildung von Ammoniak und Aluminiumhydroxid reagiert, wodurch die Herstellung von Aluminiumnitrid- Formkörpern mittels des klassischen Schlickergussverfahrens schwierig bis unmöglich ist. Die Aufgabe der vorliegenden Erfindung war deshalb die Bereitstellung eines Schlickers, mit dem Aluminiumnitrid und andere mit Wasser unverträgliche Materialien wie z. B. Erdalkalioxide (BeO, MgO, CaO, SrO, BaO) oder Metalle (Mg, AI, Si, Fe usw.) im Schlickergussverfahren verarbeitet werden kann, ebenso wie ein Schlickergussverfahren zur Herstellung von Formkörpern aus AI u m i n i u m n itrid Werkstoffen .
Diese Aufgabe konnte dadurch gelöst werden, dass statt Wasser ein wasserfreies, organisches Lösungsmittel oder Lösungsmittelgemisch, bevorzugt ein- oder mehrwertige Alkohole für die Aufbereitung der Dispersion (Schlicker) verwendet wird.
Um eine ausreichende Festigkeit des Formkörpers („Grünling") zu erreichen, ist die Zugabe eines geeigneten Binders zum Schlicker empfehlenswert. Die Art des Binders ist abhängig vom Lösungsmittel (Löslichkeit). Besonders geeignet sind Polymere mit ausreichender Kettenlänge. Diese Polymere verbleiben im Scherben und verstopfen / verkleben nicht die Poren der Form. Die Bindergehalte liegen üblicherweise bei 0,5 - 5%, abhängig von der Art und der für eine mögliche weitere Bearbeitung erforderlichen Festigkeit. Es sollte ein möglichst hoher Feststoffgehalt der Dispersion angestrebt werden, der üblicherweise zwischen 50 und 85% liegen kann. Entsprechend den jeweiligen Anforderungen des aus dem Schlicker mittels Schlickergussverfahrens hergestellten Formkörpers können dem Aluminiumnitrid- Schlicker organische Additive wie Dispergierhilfsmittel, Stellmittel usw. und anorganische Additive wie Sinterhilfmittel zugegeben werden. Die Art und Menge der Additive richtet sich nach dem eingesetzten Pulver, dem Lösemittel, der Verarbeitung des Schlickers, dem Sinterverfahren und den gewünschten Werkstoffeigenschaften . Das erfindungsgemäße Schlickergussverfahren zur Herstellung eines Aluminiumnitrid-Formkörpers umfasst die Schritte (a) Bereitstellung des Schlickers; (b) Gießen des Schlickers in eine Form, die bevorzugt aus porösem Werkstoff besteht; (c) Verfestigen des Schlickers in der Form; (d) Ausgießen des restlichen Schlickers, wenn die gewünschte Wandstärke des Formkörpers erreicht ist; (e) weiteres Verfestigen der Schicht, (f) Entnehmen des verfestigten Formkörpers aus der Form. Die so hergestellten Formkörper können ein- oder mehrteilig sein. Das Schlickergussverfahren wird üblicherweise bei Raumtemperatur durchgeführt, kann bei besonderen Anforderungen auch in klimatisierten Räumen, bei definierten Temperaturen stattfinden. Die Wandstärke richtet sich nach den Bauteilanforderungen und liegt normalerweise zwischen 2 und 20 mm.
Die Bereitstellung des Schlickers umfasst das Vermischen der Komponenten Aluminiumnitrid, organisches wasserfreies Lösemittel, Binder und optional weiteren Additiven. Das Vermischen kann mit den für diesem Zweck üblichen Geräten wie Rührer, Mühlen usw. erfolgen. Eine weitere Vermahlung zur Reduktion der Korngröße ist z. B. mit einer Rührwerkskugelmühle möglich. Eine Vakuumentgasung des Schlickers vor der Verarbeitung ist entsprechend den Anforderungen an die Bauteileigenschaften möglich.
Danach wird der so hergestellte Schlicker in eine Form aus einem porösem Werkstoff, bevorzugt Gips oder porösem Kunststoff gegossen. Die poröse Form entzieht dem Schlicker Lösemittel, was zur Bildung einer festen Schicht („Scherben") an der Formoberfläche führt.
Ist die gewünschte Wandstärke, z. B. 4 mm nach einer definierten Zeit, z.B. 15 Minuten erreicht, wird der restliche flüssige Schlicker ausgegossen. Nachdem sich die Schicht („Scherben") weiter verfestigt hat, kann das Teil aus der Form entnommen werden. Der Formkörper kann anschließend noch weiter bearbeitet werden, z.B. bohren, fräsen, sägen. Die Form kann getrocknet und wiederverwendet werden.
Durch das erfindungsgemäße Verfahren ist es möglich, komplexe Bauteile, z. B. Hohlkörper, Körper mit komplizierter Kontur und Freiformflächen, Muster und strukturierter Oberfläche, Radien und Übergängen, aus Aluminiumnitrid-Werkstoffen wirtschaftlich herzstellen.

Claims

Patentansprüche
1 . Dispersion (Schlicker) zur Verwendung im Schlickergussverfahren, dadurch gekennzeichnet, dass die Dispersion Aluminiumnitrid und ein organisches Lösemittel umfasst.
2. Dispersion nach Anspruch 1 , dadurch gekennzeichnet, dass die Dispersion zusätzlich einen Binder enthält.
3. Dispersion nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die Dispersion zusätzlich organische und / oder anorganische Additive umfasst.
4. Schlickergussverfahren zur Herstellung eines Formkörpers, dadurch gekennzeichnet, dass das Verfahren die Schritte (a) Bereitstellung des Schlickers nach einem der Ansprüche 1 bis 3; (b) Gießen des Schlickers in eine Form; (c) Verfestigen des Schlickers in der Form; (d) Ausgießen des restlichen Schlickers, wenn die gewünschte Wandstärke des Formkörpers erreicht ist; (e) weiteres Verfestigen der Schicht, und (f) Entnehmen des verfestigten Formkörpers aus der Form.
5. Verfahren nach Anspruch 4, dadurch gekennzeichnet, dass die Form in Schritt (b) aus einem porösen Werkstoff besteht.
6. Formkörper, hergestellt nach dem Verfahren nach Anspruch 4 oder 5.
7. Formkörper nach Anspruch 6, dadurch gekennzeichnet, dass der Formkörper ein- oder mehrteilig ist.
8. Formkörper nach Anpspruch 6 oder 7, dadurch gekennzeichnet, dass der Formkörper ein komplexes Bauteil ist.
PCT/EP2017/059495 2016-04-22 2017-04-21 Schlickergussverfahren zur herstellung von formkörpern WO2017182618A1 (de)