WO2017164357A1 - アルキル変性カルボキシル基含有共重合体 - Google Patents

アルキル変性カルボキシル基含有共重合体 Download PDF

Info

Publication number
WO2017164357A1
WO2017164357A1 PCT/JP2017/011952 JP2017011952W WO2017164357A1 WO 2017164357 A1 WO2017164357 A1 WO 2017164357A1 JP 2017011952 W JP2017011952 W JP 2017011952W WO 2017164357 A1 WO2017164357 A1 WO 2017164357A1
Authority
WO
WIPO (PCT)
Prior art keywords
alkyl
mass
carboxyl group
modified carboxyl
containing copolymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2017/011952
Other languages
English (en)
French (fr)
Inventor
梨絵 中島
亮輔 村上
慎郷 井澤
慧 西口
美有 池田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Seika Chemicals Co Ltd
Original Assignee
Sumitomo Seika Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Seika Chemicals Co Ltd filed Critical Sumitomo Seika Chemicals Co Ltd
Publication of WO2017164357A1 publication Critical patent/WO2017164357A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

水溶成分と油溶成分とのエマルジョンを安定化し得るアルキル変性カルボキシル基含有共重合体を提供する。 （メタ）アクリル酸（ａ）１００質量部と、アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（ｂ）１．０～５．０質量部と、エチレン性不飽和基を２個以上有する化合物（ｃ）０．４５質量部以上とを含む単量体の共重合体であり、　前記共重合体の１質量％中和粘稠液の粘度が、２５℃において、２０，０００ｍＰａ・ｓ～４０，０００ｍＰａ・ｓであり、　前記１質量％中和粘稠液１００質量部に対して１．０質量部の塩化ナトリウムを添加したときの粘度が、２５℃において、４，０００ｍＰａ・ｓ～７，５００ｍＰａ・ｓである、　アルキル変性カルボキシル基含有共重合体。

Description

アルキル変性カルボキシル基含有共重合体
　本発明は、アルキル変性カルボキシル基含有共重合体、当該共重合体を含むエマルジョン安定化剤、及び当該共重合体を含むエマルジョンに関する。
　従来、例えば、化粧品用の増粘剤、パップ剤用の保湿剤、乳化剤、および懸濁安定剤には、（メタ）アクリル酸と（メタ）アクリル酸アルキルエステルを単量体とした種々の共重合体が用いられている。このような共重合体としては、例えば、特定量のオレフィン系不飽和カルボン酸単量体と、特定量の（メタ）アクリル酸アルキルエステル（アルキル基の炭素数が１０～３０）との反応生成物（例えば、特許文献１を参照）が知られている。
特開昭５１－６１９０号公報
　このような共重合体は、化粧品等では水溶成分と油溶成分とのＯ／Ｗエマルジョンを安定化させるための安定化剤としても使用されている。しかしながら、従来の共重合体を安定化剤とした化粧品等においては、時間が経過したときにＯ／Ｗエマルジョンが水溶成分と油溶成分とに分離するなどの問題がある。このため、時間が経過したときにＯ／Ｗエマルジョンが水溶成分と油溶成分とに分離しにくいというエマルジョンの安定性をさらに向上させることが求められる。
　本発明の目的は、エマルジョンの安定性を向上できるアルキル変性カルボキシル基含有共重合体、当該共重合体を含むエマルジョン安定化剤、及び共重合体を含むエマルジョンを提供することである。
　本発明者らは、上記課題を解決するために鋭意検討した。その結果、（メタ）アクリル酸（ａ）１００質量部と、アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（ｂ）１．０～５．０質量部と、エチレン性不飽和基を２個以上有する化合物（ｃ）０．４５質量部以上とを含む単量体の共重合体であって、当該共重合体の１質量％中和粘稠液の粘度が２０，０００ｍＰａ・ｓ～４０，０００ｍＰａ・ｓの範囲内にあり、かつ、当該１質量％中和粘稠液１００質量部に対して１．０質量部の塩化ナトリウムを添加したときの粘度が、４，０００ｍＰａ・ｓ～７，５００ｍＰａ・ｓの範囲内であるアルキル変性カルボキシル基含有共重合体は、エマルジョン（特に、Ｏ／Ｗ型エマルジョン）の安定性を向上できることを見出した。
　すなわち、本発明は、下記の構成を備える発明を提供する。
項１．　（メタ）アクリル酸（ａ）１００質量部と、アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（ｂ）１．０～５．０質量部と、エチレン性不飽和基を２個以上有する化合物（ｃ）０．４５質量部以上とを含む単量体の共重合体であり、
　前記共重合体の１質量％中和粘稠液の粘度が、２５℃において、２０，０００ｍＰａ・ｓ～４０，０００ｍＰａ・ｓであり、
　前記１質量％中和粘稠液１００質量部に対して１．０質量部の塩化ナトリウムを添加したときの粘度が、２５℃において、４，０００ｍＰａ・ｓ～７，５００ｍＰａ・ｓである、
　アルキル変性カルボキシル基含有共重合体。
項２．　前記エチレン性不飽和基を２個以上有する化合物（ｃ）が、ペンタエリスリトールポリアリルエーテル、ジエチレングリコールジアリルエーテル、ポリエチレングリコールジアリルエーテル、及びポリアリルサッカロースからなる群より選ばれた少なくとも１種である、項１に記載のアルキル変性カルボキシル基含有共重合体。
項３．　前記アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（ｂ）が、（メタ）アクリル酸ステアリルを含む、項１または２に記載のアルキル変性カルボキシル基含有共重合体。
項４．　項１～３のいずれかに記載のアルキル変性カルボキシル基含有共重合体を含む、エマルジョン安定化剤。
項５．　項１～３のいずれかに記載のアルキル変性カルボキシル基含有共重合体を含む、エマルジョン。
　本発明は、エマルジョンの安定性を向上できるアルキル変性カルボキシル基含有共重合体、当該共重合体を含むエマルジョン安定化剤、及び当該共重合体を含むエマルジョンを提供できる。
　本発明のアルキル変性カルボキシル基含有共重合体は、（メタ）アクリル酸（ａ）１００質量部と、アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（ｂ）１．０～５．０質量部と、エチレン性不飽和基を２個以上有する化合物（ｃ）０．４５質量部以上とを含む単量体の共重合体であり、さらに、当該共重合体の１質量％中和粘稠液の粘度が、２５℃において、２０，０００ｍＰａ・ｓ～４０，０００ｍＰａ・ｓであり、かつ、当該１質量％中和粘稠液１００質量部に対して１．０質量部の塩化ナトリウムを添加したときの粘度が、２５℃において、４，０００ｍＰａ・ｓ～７，５００ｍＰａ・ｓであることを特徴とする。以下、本発明のアルキル変性カルボキシル基含有共重合体、当該共重合体を含むエマルジョン安定化剤、及び当該共重合体を含むエマルジョンについて、詳述する。
　なお、本発明において、「アクリル酸及びメタクリル酸」を総称して「（メタ）アクリル酸」という。また、本発明において、「中和粘稠液」とは、アルキル変性カルボキシル基含有共重合体の水分散液のｐＨが６．５～７．５となるように、アルキル変性カルボキシル基含有共重合体の水分散液に水酸化ナトリウムの水溶液を混合して得られた粘性液体を意味する。また、本発明において、「１質量％中和粘稠液」とは、アルキル変性カルボキシル基含有共重合体の割合が１質量％である中和粘稠液を意味する。
　本発明のアルキル変性カルボキシル基含有共重合体は、（メタ）アクリル酸（以下、成分（ａ）ということがある）と、アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（以下、成分（ｂ）ということがある）と、エチレン性不飽和基を２個以上有する化合物（以下、成分（ｃ）ということがある）との共重合体である。すなわち、本発明のアルキル変性カルボキシル基含有共重合体は、少なくとも、成分（ａ）、（ｂ）、及び（ｃ）を共重合した重合体である。
　本発明において、（メタ）アクリル酸（成分（ａ））としては、アクリル酸及びメタクリル酸の少なくとも一方を使用することができる。
　アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（成分（ｂ））は、（メタ）アクリル酸と、アルキル基の炭素数が１８～２４である高級アルコールとを反応させて得られるエステルである。成分（ｂ）の具体例としては、（メタ）アクリル酸ステアリル、（メタ）アクリル酸エイコサニル、（メタ）アクリル酸ベヘニル、（メタ）アクリル酸テトラコサニルなどがある。これらの成分（ｂ）の中でも、水溶成分と油溶成分とのエマルジョンのより高い安定性を得る観点から、メタクリル酸ステアリル、メタクリル酸エイコサニル、メタクリル酸ベヘニル及びメタクリル酸テトラコサニル等が好適に用いられる。
　本発明のアルキル変性カルボキシル基含有共重合体において、単量体を構成している成分（ｂ）は、１種類を用いてもよいし、２種類以上を用いてもよい。成分（ｂ）を２種類以上用いて共重合するときは、例えば、日本油脂株式会社製の商品名ブレンマーＶＭＡ－７０（メタクリル酸ステアリルが１０質量部～２０質量部、メタクリル酸エイコサニルが１０質量部～２０質量部、メタクリル酸ベヘニルが５９質量部～８０質量部及びメタクリル酸テトラコサニルが１質量部以下の混合物）を用いることができる。
　本発明のアルキル変性カルボキシル基含有共重合体における成分（ｂ）の割合は、（メタ）アクリル酸（成分（ａ））１００質量部に対して、１質量部～５質量部である。エマルジョンの安定性をより高める観点からは、成分（ｂ）の割合は、成分（ａ）１００質量部に対して、１質量部～３質量部が好ましい。なお、成分（ｂ）の割合が、成分（ａ）１００質量部に対して１質量部未満であるときには、アルキル変性カルボキシル基含有共重合体がエマルジョンを安定化させる効果が不十分になる可能性がある。一方、成分（ｂ）の割合が、成分（ａ）１００質量部に対して５質量部を超えるときには、アルキル変性カルボキシル基含有共重合体を水に分散させた際（例えば、水溶成分と油溶成分のエマルジョンの安定化剤として、当該共重合体を水に分散させた際）にアルキル変性カルボキシル基含有共重合体が塊状化する可能性がある。
　エチレン性不飽和基を２個以上有する化合物（成分（ｃ））は、重合性を有するエチレン性不飽和基を２個以上有する化合物である。成分（ｃ）の好ましい具体例としては、ペンタエリスリトールジアリルエーテル、ペンタエリスリトールトリアリルエーテル、ペンタエリスリトールテトラアリルエーテル等のペンタエリスリトールポリアリルエーテルや、ジエチレングリコールジアリルエーテル、ポリエチレングリコールジアリルエーテル、ポリアリルサッカロース等がある。成分（ｃ）は、１種類を用いてもよいし、２種類以上を用いてもよい。アルキル変性カルボキシル基含有共重合体の中和粘稠液の粘度を所定の範囲により容易に調整できるという理由から、これらの中でも、成分（ｃ）は、ペンタエリスリトールポリアリルエーテル、ジエチレングリコールジアリルエーテル、ポリエチレングリコールジアリルエーテル、及びポリアリルサッカロースからなる群より選ばれた少なくとも１種を含んでいることが好ましい。
　本発明のアルキル変性カルボキシル基含有共重合体における成分（ｃ）の割合は、（メタ）アクリル酸（成分（ａ））１００質量部に対して、０．４５質量部以上である。エマルジョンの安定性をより高める観点からは、成分（ｃ）の割合は、０．４７質量部以上が好ましい。成分（ｃ）の割合が、０．４５質量部未満である場合、アルキル変性カルボキシル基含有共重合体がエマルジョンを経時的に安定化させる効果が不十分になる可能性がある。また、エマルジョンの安定性をより高める観点からは、成分（ｃ）の割合は、（メタ）アクリル酸（成分（ａ））１００質量部に対して、１０質量部以下が好ましく、３質量部以下がより好ましい。成分（ｃ）の割合が１０質量部以下であることにより、得られるアルキル変性カルボキシル基含有共重合体を水に分散させる際（例えば、水溶成分と油溶成分のエマルジョンの安定化剤として、当該共重合体を水に分散させた際）にアルキル変性カルボキシル基含有共重合体が塊状化することを抑制することができる。
　本発明のアルキル変性カルボキシル基含有共重合体は、成分（ａ）、（ｂ）、及び（ｃ）に加えて、成分（ａ）、（ｂ）、及び（ｃ）以外の単量体（成分（ａ）、（ｂ）、及び（ｃ）の少なくとも１種と共重合可能な他の単量体）を共重合させてもよい。
　本発明のアルキル変性カルボキシル基含有共重合体の１質量％中和粘稠液の粘度（以下、「１％粘度」ということがある）は、２５℃において、２０，０００ｍＰａ・ｓ～４０，０００ｍＰａ・ｓの範囲内にある。水溶成分と油溶成分とのエマルジョンの安定性をより高める観点からは、当該１％粘度は、２５，０００ｍＰａ・ｓ～３５，０００ｍＰａ・ｓの範囲内にあることが好ましい。なお、１％粘度が２０，０００ｍＰａ・ｓ未満のときは、アルキル変性カルボキシル基含有共重合体を使用したエマルジョンが分離するまでの時間が短くなる。一方、前記１％粘度が４０，０００ｍＰａ・ｓを超えるときは、エマルジョンが分離するまでの時間が短くなる。なお、当該「１％粘度」は、実施例の［評価方法］に記載の方法で測定した値を意味する。
　さらに、本発明のアルキル変性カルボキシル基含有共重合体においては、当該１質量％中和粘稠液１００質量部に対して１．０質量部の塩化ナトリウムを添加したときの粘度（以下「耐塩粘度」ということがある）が、２５℃において、４，０００ｍＰａ・ｓ～７，５００ｍＰａ・ｓの範囲内にある。エマルジョンの安定性をより高める観点からは、当該耐塩粘度は、４，５００ｍＰａ・ｓ～７，０００ｍＰａ・ｓの範囲内にあることが好ましい。耐塩粘度が４，０００ｍＰａ・ｓ未満、または７，５００ｍＰａ・ｓを超えるときは、エマルジョンが分離しやすくなる。なお、当該「耐塩粘度」は、実施例の［評価方法］に記載の方法で測定した値を意味する。
　本発明のアルキル変性カルボキシル基含有共重合体の１％粘度は、例えば、エチレン性不飽和基を２個以上有する化合物（成分（ｃ））の割合の増減によって制御することができる。具体的には、共重合体を構成している成分（ｃ）の割合を増やすことでアルキル変性カルボキシル基含有共重合体の１％粘度を高めることができる。また、成分（ｃ）の割合を少なくすることでアルキル変性カルボキシル基含有共重合体の１％粘度を低くできる。
　本発明のアルキル変性カルボキシル基含有共重合体の耐塩粘度は、例えば、重合に使用する全ての単量体の溶媒に対する濃度、反応温度によって制御することができる。具体的には、重合に使用する全ての単量体の溶媒に対する濃度を高くすることや、重合温度を低くすることでアルキル変性カルボキシル基含有共重合体の耐塩粘度を高めることができる。また、該濃度を低くすることや、重合温度を高くすることでアルキル変性カルボキシル基含有共重合体の耐塩粘度を低くすることができる。
　本発明のアルキル変性カルボキシル基含有共重合体の製造方法としては、特に制限されず、少なくとも前述の成分（ａ）、（ｂ）、及び（ｃ）を含む原料並びに重合開始剤を溶媒に添加した溶液を、不活性ガス素雰囲気下で攪拌しながら加熱して重合する方法等がある。
　不活性ガス雰囲気とするための不活性ガスとしては、特に制限されないが、窒素ガス、アルゴンガスなどがある。
　また、溶媒は、少なくとも成分（ａ）、（ｂ）、及び（ｃ）は溶解するが、生成するアルキル変性カルボキシル基含有共重合体は溶解せず、かつ、共重合反応を阻害しなければ、特に限定されない。溶媒の具体例としては、ノルマルペンタン、ノルマルヘキサン、ノルマルヘプタン、ノルマルオクタン、イソオクタン、シクロペンタン、メチルシクロペンタン、シクロヘキサン、メチルシクロヘキサン、ベンゼン、トルエン、キシレン、クロロベンゼン、エチレンジクロライド、酢酸エチル、酢酸イソプロピル、エチルメチルケトン、イソブチルメチルケトンなどがある。溶媒は、１種類で使用してもよいし、２種類以上を組み合わせて使用してもよい。これらの溶媒の中でも、品質が安定しており、入手が容易である観点から、ノルマルヘキサン、ノルマルヘプタン、シクロヘキサン、エチレンジクロライド、酢酸エチルなどが好適に用いられる。
　溶媒の使用量は、アルキル変性カルボキシル基含有共重合体の耐塩粘度を上記の範囲に調整する観点や、撹拌操作性を向上させる観点、経済性の観点等から、成分（ａ）１００質量部に対して、３００質量部～５，０００質量部とすることが好ましい。
　重合開始剤としては、例えば、ラジカル重合開始剤が好ましい。重合開始剤の具体例としては、α、α’－アゾイソブチロニトリル、２，２’－アゾビス－２，４－ジメチルバレロニトリル、ジメチル－２，２’－アゾビスイソブチレート、過酸化ベンゾイル、ラウロイルパーオキサイド、クメンハイドロパーオキサイド、第三級ブチルハイドロパーオキサイドなどがある。重合開始剤は、１種類で使用してもよいし、２種類以上を組み合わせて使用してもよい。
　重合開始剤の使用量としては、反応速度を適度に保つ観点から成分（ａ）１００質量部に対して、好ましくは０．０１質量部～０．４５質量部、より好ましくは０．０１質量部～０．３５質量部である。
　重合温度としては、重合速度を適度に保つ観点から好ましくは５０℃～９０℃程度、より好ましくは５５℃～８５℃程度である。
　重合時間は、重合温度などによって異なるが、通常、０．５時間～１０時間程度である。
　重合後のスラリー液を、乾燥時間を短くし共重合体の塊状化を抑制する観点から例えば８０℃～１３０℃に加熱して溶媒を除去することにより、本発明のアルキル変性カルボキシル基含有共重合体を得ることができる。
　本発明のアルキル変性カルボキシル基含有共重合体を使用することにより、安定性の高いエマルジョン（特に、Ｏ／Ｗ型エマルジョン）を得ることができる。したがって、本発明のアルキル変性カルボキシル基含有共重合体を必須成分として含むエマルジョン安定化剤は、エマルジョン（特に、Ｏ／Ｗ型エマルジョン）の安定化剤として有用である。
　本発明のエマルジョン安定化剤は、前述の本発明のアルキル変性カルボキシル基含有共重合体を含むことを特徴としている。本発明のエマルジョン安定化剤は、本発明のアルキル変性カルボキシル基含有共重合体のみより形成されていてもよい。
　また、本発明のエマルジョンは、本発明のアルキル変性カルボキシル基含有共重合体を含むことを特徴としている。すなわち、本発明のエマルジョンは、エマルジョン安定化剤として、本発明のアルキル変性カルボキシル基含有共重合体を含んでいる。
　本発明のエマルジョン中における、本発明のアルキル変性カルボキシル基含有共重合体の含有量は、エマルジョンの安定性を高める観点からは、好ましくは０．１質量％以上、より好ましくは０．２質量％～１質量％である。
　本発明のエマルジョンは、水溶成分と油溶成分とのエマルジョンであり、特にＯ／Ｗ型エマルジョンであることが好ましい。水溶成分としては、水に溶ける成分であればよい。例えば、低級アルコール、多価アルコール、水溶性高分子、水溶性界面活性剤、保湿剤、薬用成分、ｐＨ調整剤、酸化防止剤、色材などの化粧品に配合される公知の成分を水に添加することができる。また、油溶成分としては、水と分離してエマルジョンを形成できる成分であればよい。例えば、炭化水素、エステル、高級脂肪酸、などの化粧品に配合される公知の成分を油溶成分に用いることができる。本発明のエマルジョンは、美容成分などを配合した化粧品とすることもできる。
　以下に実施例及び比較例を示して本発明を詳細に説明する。但し本発明は実施例に限定されるものではない。
（実施例１）
　攪拌機、温度計、窒素吹込み管及び冷却管を備えた容量５００ｍＬの四つ口フラスコに、アクリル酸４５ｇ、ブレンマーＶＭＡ７０（日油株式会社製：メタクリル酸ステアリルが１０～２０質量部、メタクリル酸エイコサニルが１０～２０質量部、メタクリル酸ベヘニルが５９～８０質量部及びメタクリル酸テトラコサニルが１質量部以下の混合物）０．９９ｇ、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）０．２０３ｇ、ノルマルヘプタン１６３．２ｇ、酢酸エチル５４ｇ及び２，２’－アゾビスメチルイソブチレート０．０２５ｇを仕込んだ。その後、フラスコの内容物を撹拌しながら、フラスコ内の酸素を除去するために、溶液中に窒素ガスを吹き込んだ。その後、攪拌と窒素ガスの吹き込みを続けた状態でオイルバスの設定温度を７５～７９℃に設定し、フラスコの内容物を４時間加熱した。その後、オイルバスの設定温度を１１０℃に設定して加熱し、フラスコ内からノルマルヘプタンと酢酸エチルを除去した。その後フラスコの内容物を減圧乾燥機（Ｙａｍａｔｈｏ社製、バキュームドライオーブンＤＰ３３）に移し、オーブンの設定温度を１１５℃に設定して、設定圧力を１０ｍｍＨｇに設定して８時間乾燥し、白色粉末状のアルキル変性カルボキシル基含有共重合体４４ｇを得た。
（実施例２）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２２５ｇに変更したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４４ｇを得た。
（実施例３）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２４８ｇに変更したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４３ｇを得た。
（実施例４）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２７０ｇに変更したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４３ｇを得た。
（実施例５）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２２５ｇ、ブレンマーＶＭＡ７０の使用量を０．４５ｇに変更したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４４ｇを得た。
（実施例６）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２２５ｇ、ブレンマーＶＭＡ７０の使用量を２．２５ｇに変更したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４５ｇを得た。
（実施例７）
　攪拌機、温度計、窒素吹込み管、添加装置及び冷却管を備えた容量５００ｍＬの５つ口フラスコを用意した。フラスコにブレンマーＶＭＡ７０（日油株式会社製：メタクリル酸ステアリルが１０～２０質量部、メタクリル酸エイコサニルが１０～２０質量部、メタクリル酸ベヘニルが５９～８０質量部及びメタクリル酸テトラコサニルが１質量部以下の混合物）１．１ｇ、ノルマルヘプタン１０４ｇ、酢酸エチル３５ｇ及び２，２’－アゾビスメチルイソブチレート０．０３０ｇを仕込み、また、添加装置にアクリル酸５０ｇとペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）０．２２５ｇ、ノルマルヘプタン４０ｇ、および酢酸エチル１４ｇを仕込んだ。その後、フラスコの内容物を攪拌しながら、フラスコ内の酸素を除去する為に、溶液中に窒素ガスを吹き込んだ。その後、攪拌と窒素ガスの吹き込みを続けた状態で、フラスコを加熱し、フラスコの内容物の温度が６０℃に到達したときから、添加装置に仕込んだ混合物を１１０分かけてフラスコの内容物に滴下した。滴下を開始した後にフラスコ内の内容物の温度が７０～７３℃になるようにオイルバスを設定した。添加装置に仕込んだ混合物の滴下が終了した後、フラスコの内容物の温度が７０～７３℃になるようにオイルバスを設定した状態で１時間フラスコの内容物を攪拌した。その後、オイルバスの設定温度を１１０℃に設定してフラスコを加熱し、フラスコ内からノルマルヘプタンと酢酸エチルを除去した。その後フラスコの内容物を減圧乾燥機（Ｙａｍａｔｈｏ社製、バキュームドライオーブンＤＰ３３）に移し、オーブンの設定温度を１１５℃に設定し、設定圧力を１０ｍｍＨｇに設定して８時間乾燥して、白色粉末状のアルキル変性カルボキシル基含有共重合体４９ｇを得た。
（実施例８）
　実施例７において、添加装置に仕込んだペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２６３ｇに変更したこと以外は、実施例７と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４７ｇを得た。
（実施例９）
　実施例７において、添加装置に仕込んだペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２５ｇ、１．１ｇのブレンマーＶＭＡ７０の代わりに１．５ｇのステアリルメタクリレートを使用したこと以外は、実施例７と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４９ｇを得た。
（比較例１）
　実施例７において、反応容器に仕込んだノルマルヘプタンの使用量を８２ｇ、酢酸エチルの使用量を２７ｇ、添加装置に仕込んだペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２５ｇに変更したこと以外は、実施例７と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４７ｇを得た。
（比較例２）
　実施例７において、滴下を開始した後はフラスコ内の内容物の温度が７６～７９℃となるようオイルバスの設定を変更し、添加装置に仕込んだ混合物の滴下が終了した後はフラスコ内の内容物の温度が７６～７９℃となるようオイルバスの設定を変更したこと以外は実施例７と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４６ｇを得た。
（比較例３）
　実施例７において、反応容器に仕込んだノルマルヘプタンの使用量を８２ｇ、酢酸エチルの使用量を２７ｇに変更し、滴下を開始した後はフラスコ内の内容物の温度が６７～７０℃となるようオイルバスの設定を変更し、添加装置に仕込んだ混合物の滴下が終了した後はフラスコ内の内容物の温度が６７～７０℃となるようオイルバスの設定を変更し攪拌時間を２時間半に変更したこと以外は実施例７と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４７ｇを得た。
（比較例４）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２７ｇに変更し、滴下を開始した後は内容物の温度が７９～８４℃になるようにオイルバスを設定し、添加装置に仕込んだ混合物の滴下が終了した後はフラスコの内容物の温度が７９～８４℃になるようにオイルバスを設定して１時間フラスコの内容物を攪拌したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４２ｇを得た。
（比較例５）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．１８ｇに変更したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４３ｇを得た。
（比較例６）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２２５ｇ、ブレンマーＶＭＡ７０の使用量を０．２２５ｇに変更したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４２ｇを得た。
（比較例７）
　実施例１において、ペンタエリスリトールポリアリルエーテル（ペンタエリスリトールトリアリルエーテルとペンタエリスリトールテトラアリルエーテルの混合物）の使用量を０．２２５ｇ、ブレンマーＶＭＡ７０の使用量を２．４７５ｇに変更したこと以外は、実施例１と同様にして、白色粉末状のアルキル変性カルボキシル基含有共重合体４２ｇを得た。
［評価方法］
　実施例、比較例により得られたアルキル変性カルボキシル基含有共重合体を以下の方法により測定、評価した。
（１質量％中和粘稠液粘度）
　容量５００ｍＬのビーカーにイオン交換水２９７．０ｇを入れ、４枚羽根パドル（翼径５０ｍｍ）を備えた攪拌機を用いて３００ｒｐｍの回転速度で撹拌しながらアルキル変性カルボキシル基含有共重合体３．０ｇを投入した。アルキル変性カルボキシル基含有共重合体の凝集物（ママコ）が消えて均一に分散したことを目視により確認し、得られた１質量％分散液に水酸化ナトリウム水溶液を加えて、ｐＨ＝７に調整し、これを評価用中和粘稠液とした。Ｂ型回転粘度計を用い、ローターＮｏ．６、毎分２０回転、および、温度２５℃の条件下で、６０秒間ローターが回転した後の得られた評価用中和粘稠液の粘度を測定し、これを「１質量％中和粘稠液粘度」とした。
（１％ＮａＣｌ耐塩粘度）
　容量３００ｍＬのビーカーに１質量％中和粘稠液粘度評価で得られた評価用中和粘稠液１５０ｇを入れ、塩化ナトリウム１．５ｇを添加し、４枚羽根パドル（翼径５０ｍｍ）を備えた攪拌機を用いて攪拌を３０分間行い、電解質添加溶液とした。Ｂ型回転粘度計を用い、ローターＮｏ．５、毎分２０回転、および、温度２５℃の条件下で、６０秒間ローターが回転した後の得られた電解質添加溶液の粘度を測定し、これを「１％ＮａＣｌ耐塩粘度」とした。
（エマルジョンの安定性の評価）
　容量２００ｍＬビーカーにイオン交換水１０２．１２ｇを入れ、攪拌機（プライミクス株式会社製、型番：Ｔ．Ｋ．ロボミクス、翼直径３０ｍｍのディスパー翼）を用いて５，０００ｒｐｍで攪拌しながら、アルキル変性カルボキシル基含有共重合体０．７５ｇを投入した後、３０分間攪拌し未中和分散液を得た。その後、攪拌機の攪拌翼をホモミキサー（プライミクス株式会社製、型番：Ｔ．Ｋ．ロボミクス、ホモミキサー）に変更した。その後未中和分散液をホモミキサー１３，０００ｒｐｍで攪拌しながら、流動パラフィン４５ｇをビーカーに投入し、５分間攪拌した。その後５０質量％トリエタノールアミン水溶液２．１３ｇをビーカーに投入し、ホモミキサー１３，０００ｒｐｍで５分間攪拌し、エマルジョン安定性評価用のＯ／Ｗ型エマルジョンを得た。得られたエマルジョンを容器に密封し温度４０℃、湿度７５％ＲＨの恒温恒湿機内に静置し、Ｏ／Ｗ型エマルジョンの水溶成分と油溶成分の分離の有無を１日ごとに目視で確認した。９０日以上分離しなければ、エマルジョンの安定性が良好と判断した。Ｏ／Ｗ型エマルジョンが分離するまでの日数を表１、２に示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002

Claims (5)

  1. 　（メタ）アクリル酸（ａ）１００質量部と、アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（ｂ）１．０～５．０質量部と、エチレン性不飽和基を２個以上有する化合物（ｃ）０．４５質量部以上とを含む単量体の共重合体であり、
    　前記共重合体の１質量％中和粘稠液の粘度が、２５℃において、２０，０００ｍＰａ・ｓ～４０，０００ｍＰａ・ｓであり、
    　前記１質量％中和粘稠液１００質量部に対して１．０質量部の塩化ナトリウムを添加したときの粘度が、２５℃において、４，０００ｍＰａ・ｓ～７，５００ｍＰａ・ｓである、
    　アルキル変性カルボキシル基含有共重合体。
  2. 　前記エチレン性不飽和基を２個以上有する化合物（ｃ）が、ペンタエリスリトールポリアリルエーテル、ジエチレングリコールジアリルエーテル、ポリエチレングリコールジアリルエーテル、及びポリアリルサッカロースからなる群より選ばれた少なくとも１種である、請求項１に記載のアルキル変性カルボキシル基含有共重合体。
  3. 　前記アルキル基の炭素数が１８～２４である（メタ）アクリル酸アルキルエステル（ｂ）が、（メタ）アクリル酸ステアリルを含む、請求項１または２に記載のアルキル変性カルボキシル基含有共重合体。
  4. 　請求項１～３のいずれかに記載のアルキル変性カルボキシル基含有共重合体を含む、エマルジョン安定化剤。
  5. 　請求項１～３のいずれかに記載のアルキル変性カルボキシル基含有共重合体を含む、エマルジョン。
PCT/JP2017/011952 2016-03-25 2017-03-24 アルキル変性カルボキシル基含有共重合体 Ceased WO2017164357A1 (ja)