WO2017114047A1 - 一种改进的防紫外线涂料及其制备方法 - Google Patents

一种改进的防紫外线涂料及其制备方法 Download PDF

Info

Publication number
WO2017114047A1
WO2017114047A1 PCT/CN2016/107289 CN2016107289W WO2017114047A1 WO 2017114047 A1 WO2017114047 A1 WO 2017114047A1 CN 2016107289 W CN2016107289 W CN 2016107289W WO 2017114047 A1 WO2017114047 A1 WO 2017114047A1
Authority
WO
WIPO (PCT)
Prior art keywords
parts
improved
benzyl dimethyl
diphenylphosphine oxide
sodium
Prior art date
Application number
PCT/CN2016/107289
Other languages
English (en)
French (fr)
Inventor
曲少春
Original Assignee
曲少春
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 曲少春 filed Critical 曲少春
Publication of WO2017114047A1 publication Critical patent/WO2017114047A1/zh

Abstract

防紫外线涂料，其由以下重量份数的原料制成：苄基二甲基酚聚氧乙烯醚1.5-4份，混合脂肪醇硫酸钠0.35-0.66份，α-氰基丙烯酸酯胶黏剂1.25-1.65份，2,4,6-三甲基苯甲酰基-二苯基氧化膦0.36-0.67份，着色剂0.22-0.66份，二磷酸钾4-6.5份，消泡剂1.23-3.25份，直链烷基苯磺酸钠1.55-2.68份。该防紫外线涂料的制备方法，包括将各原料处理和均匀混合步骤。

Description

一种改进的防紫外线涂料及其制备方法 技术领域
[0001] 本发明涉及一种涂料， 尤其是涉及一种改进的防紫外线涂料及其制备方法， 属 于涂料领域。
背景技术
[0002] 紫外线是太阳光中对人体危害较大的一种光波， 过渡照射紫外线吋紫外线的能 量可引发皮肤老化、 甚至容易导致皮肤癌， 也可导致各种窗户帘及地板、 塑料 和印刷品的褪色。 因此人们越来越关注防紫外线照射的危害， 特别是其会使皮 肤产生红斑、 黑斑、 使皮肤老化， 甚至引起皮肤癌， 人们希望传统的衣物具有 一定的紫外线屏蔽功能， 且不影响透气透湿性。
技术问题
[0003] 针对现有技术的不足， 本发明所要解决的技术问题是， 提供一种改进的防紫外 线涂料及其制备方法， 提高了涂料的防紫外线性能和稳定性， 具有一定的紫外 线屏蔽功能， 且不影响透气透湿性。
问题的解决方案
技术解决方案
[0004] 为解决上述技术问题， 本发明采取的技术方案是， 一种改进的防紫外线涂料， 其由以下重量份数的原料制成： 苄基二甲基酚聚氧乙烯醚 1.5-4份， 混合脂肪醇 硫酸钠 0.35-0.66份， ot-氰基丙烯酸酯胶黏剂 1.25-1.65份， 2,4,6-三甲基苯甲酰基- 二苯基氧化膦 0.36-0.67份， 着色剂 0.22-0.66份， 二磷酸钾 4-6.5份， 消泡剂 1.23-3. 25份， 直链烷基苯磺酸钠 1.55-2.68份。
[0005] 优化的， 上述改进的防紫外线涂料， 其由以下重量份数的原料制成： 苄基二甲 基酚聚氧乙烯醚 1.5份， 混合脂肪醇硫酸钠 0.35份， a-氰基丙烯酸酯胶黏剂 1.25份 ， 2,4,6-三甲基苯甲酰基-二苯基氧化膦 0.36份， 着色剂 0.22份， 二磷酸钾 4份， 消 泡剂 1.23份， 直链烷基苯磺酸钠 1.55份。
[0006] 优化的， 上述改进的防紫外线涂料， 其着色剂为分散染料。 [0007] 优化的， 上述改进的防紫外线涂料， 其消泡剂为聚醚改性有机硅。
[0008] 一种改进的防紫外线涂料的制备方法， 包括以下步骤： 1) 按照上述组分配比 ， 将苄基二甲基酚聚氧乙烯醚、 混合脂肪醇硫酸钠和 a-氰基丙烯酸酯胶黏剂倒入 容器中， 加入消泡剂， 接入热处理机， 保持蒸汽温度≥ 100°C， 10-15min热处理 后自然冷却至室温； 2) 然后将 2,4,6-三甲基苯甲酰基 -二苯基氧化膦和着色剂按 配方比例， 投入到容器中， 用硅藻土过滤机进行初滤， 其过滤压力至≤ 0.1兆帕 ， 透光率达 96%以上； 3) 在反应容器中加入二磷酸钾， 以 400-500r/min进行分 散搅拌 20-25min ; 4) 然后降低转速加入直链烷基苯磺酸钠， 以 300-400r/min进 行分散搅拌 15min ; 5) 用高压均质机在 8.8-9.6MPa压力下， 使悬浮粒子受压而 破碎， 使悬浮粒均匀地分散， 冷却后即为成品。
发明的有益效果
有益效果
[0009] 本发明有以下积极的效果： 本发明的涂料涂层量
11.5g/cm2, 透气量是 17.6kg/m2*s， 伸长率是 45%， 具有良好的紫外线屏蔽效果 ， 波长 40nm的紫外光透过率为 15%， 对波长 600nm
的可见光的透过率为 50% ; a-氰基丙烯酸酯胶黏剂具有高的折光性和高光活性， 可以用作防晒剂， 解决了很多实际的需要， 适用于各种织物， 具有一定的紫外 线屏蔽功能， 且不影响透气透湿性。
实施该发明的最佳实施例
本发明的最佳实施方式
[0010] 实施例 1本发明为一种改进的防紫外线涂料， 其由以下重量份数的原料制成： 苄基二甲基酚聚氧乙烯醚 1.5份， 混合脂肪醇硫酸钠 0.35份， a-氰基丙烯酸酯胶黏 齐 1J 1.25份， 2,4,6-三甲基苯甲酰基-二苯基氧化膦 0.36份， 着色剂即分散染料 0.22份 ， 二磷酸钾 4份， 消泡剂即聚醚改性有机硅 1.23份， 直链烷基苯磺酸钠 1.55份。 一种改进的防紫外线涂料的制备方法， 包括以下步骤： 1) 按照上述组分配比 ， 将苄基二甲基酚聚氧乙烯醚、 混合脂肪醇硫酸钠和 a-氰基丙烯酸酯胶黏剂倒入 容器中， 加入消泡剂， 接入热处理机， 保持蒸汽温度≥ 100°C， lOmin热处理后自 然冷却至室温； 2) 然后将 2,4,6-三甲基苯甲酰基-二苯基氧化膦和着色剂按配方 比例， 投入到容器中， 用硅藻土过滤机进行初滤， 其过滤压力至≤ 0.1兆帕， 透 光率达 96%以上； 3) 在反应容器中加入二磷酸钾， 以 400r/min
进行分散搅拌 20min ; 4) 然后降低转速加入直链烷基苯磺酸钠， 以 300r/min进 行分散搅拌 15min ; 5) 用高压均质机在 8.8MPa压力下， 使悬浮粒子受压而破碎
， 使悬浮粒均匀地分散， 冷却后即为成品。
本发明的实施方式
实施例 2本发明为一种改进的防紫外线涂料， 其由以下重量份数的原料制成： 苄基二甲基酚聚氧乙烯醚 4份， 混合脂肪醇硫酸钠 0.66份， a-氰基丙烯酸酯胶黏 剂 1.65份， 2,4,6-三甲基苯甲酰基-二苯基氧化膦 0.67份， 着色剂即分散染料 0.66份 ， 二磷酸钾 6.5份， 消泡剂即聚醚改性有机硅 3.25份， 直链烷基苯磺酸钠 2.68份。
[0013] 一种改进的防紫外线涂料的制备方法， 包括以下步骤： 1 ) 按照上述组分配比 ， 将苄基二甲基酚聚氧乙烯醚、 混合脂肪醇硫酸钠和 a-氰基丙烯酸酯胶黏剂倒入 容器中， 加入消泡剂， 接入热处理机， 保持蒸汽温度≥ 100°C， 12min热处理后自 然冷却至室温； 2) 然后将 2,4,6-三甲基苯甲酰基-二苯基氧化膦和着色剂按配方 比例， 投入到容器中， 用硅藻土过滤机进行初滤， 其过滤压力至≤ 0.1兆帕， 透 光率达 96%以上； 3) 在反应容器中加入二磷酸钾， 以 450r/min
进行分散搅拌 22min ; 4) 然后降低转速加入直链烷基苯磺酸钠， 以 350r/min进 行分散搅拌 15min ; 5) 用高压均质机在 8.9MPa压力下， 使悬浮粒子受压而破碎 ， 使悬浮粒均匀地分散， 冷却后即为成品。
[0014] 实施例 3本发明为一种改进的防紫外线涂料， 其由以下重量份数的原料制成： 苄基二甲基酚聚氧乙烯醚 2.7份， 混合脂肪醇硫酸钠 0.46份， a-氰基丙烯酸酯胶 黏剂 1.45份， 2,4,6-三甲基苯甲酰基-二苯基氧化膦 0.47份， 着色剂即分散染料 0.43 份， 二磷酸钾 5.6份， 消泡剂即聚醚改性有机硅 2.37份， 直链烷基苯磺酸钠 2.25份 一种改进的防紫外线涂料的制备方法， 包括以下步骤： 1 ) 按照上述组分配比 ， 将苄基二甲基酚聚氧乙烯醚、 混合脂肪醇硫酸钠和 a-氰基丙烯酸酯胶黏剂倒入 容器中， 加入消泡剂， 接入热处理机， 保持蒸汽温度≥ 100°C， 15min热处理后自 然冷却至室温 2) 然后将 2,4,6-三甲基苯甲酰基 -二苯基氧化膦和着色剂按配方比 例， 投入到容器中， 用硅藻土过滤机进行初滤， 其过滤压力至≤ 0.1兆帕， 透光 率达 96%以上； 3) 在反应容器中加入二磷酸钾， 以 500r/min
进行分散搅拌 25min ; 4) 然后降低转速加入直链烷基苯磺酸钠， 以 400r/min进 行分散搅拌 15min ; 5) 用高压均质机在 9.6MPa压力下， 使悬浮粒子受压而破碎 ， 使悬浮粒均匀地分散， 冷却后即为成品。
分别将实施例 1-3得到的防紫外线涂料涂覆在聚酯膜上， 以 3kW的紫外灯进行 光固化， 在 5-10秒钟内完全固化， 得到漆膜。 对上述漆膜进行性能测试， 性能 测试结果见表 1， 其中对漆膜进行耐黄变测试， 具体为： 将漆膜喷涂在白色底 板上， 漆膜紫外光固化后， 与没有漆膜的白色底板进行目测比较， 看是否有色 差。
[表 1]
Figure imgf000005_0001
工业实用性
从检测的数据可以看出， 本发明具有很好的附着力和柔韧性， 抗冲击性也很强 ， 具有很高的硬度和耐磨性。 本发明的涂料涂层量
11.5g/cm2, 透气量是 17.6kg/m2*s， 伸长率是 45%， 具有良好的紫外线屏蔽效果 ， 波长 40nm的紫外光透过率为 15%， 对波长 600nm 的可见光的透过率为 50% ; oc-氰基丙烯酸酯胶黏剂具有高的折光性和高光活性， 可以用作防晒剂， 解决了很多实际的需要， 适用于各种织物， 具有一定的紫外 线屏蔽功能， 且不影响透气透湿性。
以上实施例的说明只是用于帮助理解本发明的方法及其核心思想。 应当指出， 对于本技术领域的普通技术人员来说， 在不脱离本发明原理的前提下， 还可以 对本发明进行若干改进和修饰， 这些改进和修饰也落入本发明权利要求的保护 范围内。 对所公幵的实施例的上述说明， 使本领域专业技术人员能够实现或使 用本发明。 对这些实施例的多种修改对本领域的专业技术人员来说将是显而易 见的， 本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下， 在其它实施例中实现。 因此， 本发明将不会被限制于本文所示的这些实施例， 而是要符合与本文所公幵的原理和新颖特点相一致的最宽的范围。

Claims

权利要求书
一种改进的防紫外线涂料， 其特征在于： 由以下重量份数的原料制成
： 苄基二甲基酚聚氧乙烯醚 1.5-4份， 混合脂肪醇硫酸钠 0.35-0.66份 ， α-氰基丙烯酸酯胶黏剂 1.25-1.65份， 2,4,6-三甲基苯甲酰基-二苯基 氧化膦 0.36-0.67份， 着色齐 ij0.22-0.66份， 二磷酸钾 4-6.5份， 消泡剂 1.2 3-3.25份， 直链烷基苯磺酸钠 1.55-2.68份。
根据权利要求 1所述的改进的防紫外线涂料， 其特征在于： 由以下重 量份数的原料制成： 苄基二甲基酚聚氧乙烯醚 1.5份， 混合脂肪醇硫 酸钠 0.35份， ot-氰基丙烯酸酯胶黏剂 1.25份， 2,4,6-三甲基苯甲酰基- 二苯基氧化膦 0.36份， 着色剂 0.22份， 二磷酸钾 4份， 消泡剂 1.23份， 直链烷基苯磺酸钠 1.55份。
根据权利要求 1所述的改进的防紫外线涂料， 其特征在于： 所述着色 剂为分散染料。
根据权利要求 1所述的改进的防紫外线涂料， 其特征在于： 所述消泡 剂为聚醚改性有机硅。
根据权利要求 1-4任一项所述的改进的防紫外线涂料的制备方法， 包 括以下步骤： 1) 按照上述组分配比， 将苄基二甲基酚聚氧乙烯醚、 混合脂肪醇硫酸钠和 a-氰基丙烯酸酯胶黏剂倒入容器中， 加入消泡剂 ， 接入热处理机， 保持蒸汽温度≥ 100°C， 10-15min热处理后自然冷 却至室温； 2) 然后将 2,4,6-三甲基苯甲酰基-二苯基氧化膦和着色剂 按配方比例， 投入到容器中， 用硅藻土过滤机进行初滤， 其过滤压力 至≤0.1兆帕， 透光率达 96%以上； 3) 在反应容器中加入二磷酸钾， 以 400-500r/min进行分散搅拌 20-25min； 4) 然后降低转速加入直链 烷基苯磺酸钠， 以 300-400r/min进行分散搅拌 15min ; 5) 用高压均质 机在 8.8-9.6MPa压力下， 使悬浮粒子受压而破碎， 使悬浮粒均匀地分 散， 冷却后即为成品。
PCT/CN2016/107289 2015-12-30 2016-11-25 一种改进的防紫外线涂料及其制备方法 WO2017114047A1 (zh)