Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
  • B32B17/10614—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer comprising particles for purposes other than dyeing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/10165—Functional features of the laminated safety glass or glazing
  • B32B17/10431—Specific parts for the modulation of light incorporated into the laminated safety glass or glazing
  • B32B17/1044—Invariable transmission
  • B32B17/10458—Polarization selective transmission
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/10009—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets
  • B32B17/10036—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the number, the constitution or treatment of glass sheets comprising two outer glass sheets
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
  • B32B17/10761—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing vinyl acetal
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B17/00—Layered products essentially comprising sheet glass, or glass, slag, or like fibres
  • B32B17/06—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material
  • B32B17/10—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin
  • B32B17/10005—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing
  • B32B17/1055—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer
  • B32B17/10788—Layered products essentially comprising sheet glass, or glass, slag, or like fibres comprising glass as the main or only constituent of a layer, next to another layer of a specific material of synthetic resin laminated safety glass or glazing characterized by the resin layer, i.e. interlayer containing ethylene vinylacetate
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B7/00—Layered products characterised by the relation between layers; Layered products characterised by the relative orientation of features between layers, or by the relative values of a measurable parameter between layers, i.e. products comprising layers having different physical, chemical or physicochemical properties; Layered products characterised by the interconnection of layers
  • B32B7/04—Interconnection of layers
  • B32B7/12—Interconnection of layers using interposed adhesives or interposed materials with bonding properties
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
  • C03C17/006—Surface treatment of glass, not in the form of fibres or filaments, by coating with materials of composite character
  • C03C17/007—Surface treatment of glass, not in the form of fibres or filaments, by coating with materials of composite character containing a dispersed phase, e.g. particles, fibres or flakes, in a continuous phase
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C27/00—Joining pieces of glass to pieces of other inorganic material; Joining glass to glass other than by fusing
  • C03C27/06—Joining glass to glass by processes other than fusing
  • C03C27/10—Joining glass to glass by processes other than fusing with the aid of adhesive specially adapted for that purpose
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F21—LIGHTING
  • F21V—FUNCTIONAL FEATURES OR DETAILS OF LIGHTING DEVICES OR SYSTEMS THEREOF; STRUCTURAL COMBINATIONS OF LIGHTING DEVICES WITH OTHER ARTICLES, NOT OTHERWISE PROVIDED FOR
  • F21V3/00—Globes; Bowls; Cover glasses
  • F21V3/04—Globes; Bowls; Cover glasses characterised by materials, surface treatments or coatings
  • F21V3/10—Globes; Bowls; Cover glasses characterised by materials, surface treatments or coatings characterised by coatings
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F21—LIGHTING
  • F21V—FUNCTIONAL FEATURES OR DETAILS OF LIGHTING DEVICES OR SYSTEMS THEREOF; STRUCTURAL COMBINATIONS OF LIGHTING DEVICES WITH OTHER ARTICLES, NOT OTHERWISE PROVIDED FOR
  • F21V9/00—Elements for modifying spectral properties, polarisation or intensity of the light emitted, e.g. filters
  • F21V9/02—Elements for modifying spectral properties, polarisation or intensity of the light emitted, e.g. filters for simulating daylight
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B5/00—Optical elements other than lenses
  • G02B5/02—Diffusing elements; Afocal elements
  • G02B5/0205—Diffusing elements; Afocal elements characterised by the diffusing properties
  • G02B5/0236—Diffusing elements; Afocal elements characterised by the diffusing properties the diffusion taking place within the volume of the element
  • G02B5/0242—Diffusing elements; Afocal elements characterised by the diffusing properties the diffusion taking place within the volume of the element by means of dispersed particles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2250/00—Layers arrangement
  • B32B2250/03—3 layers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2250/00—Layers arrangement
  • B32B2250/40—Symmetrical or sandwich layers, e.g. ABA, ABCBA, ABCCBA
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2255/00—Coating on the layer surface
  • B32B2255/10—Coating on the layer surface on synthetic resin layer or on natural or synthetic rubber layer
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2255/00—Coating on the layer surface
  • B32B2255/26—Polymeric coating
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2255/00—Coating on the layer surface
  • B32B2255/28—Multiple coating on one surface
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2307/00—Properties of the layers or laminate
  • B32B2307/40—Properties of the layers or laminate having particular optical properties
  • B32B2307/406—Bright, glossy, shiny surface
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2307/00—Properties of the layers or laminate
  • B32B2307/40—Properties of the layers or laminate having particular optical properties
  • B32B2307/412—Transparent
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2307/00—Properties of the layers or laminate
  • B32B2307/40—Properties of the layers or laminate having particular optical properties
  • B32B2307/414—Translucent
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2307/00—Properties of the layers or laminate
  • B32B2307/40—Properties of the layers or laminate having particular optical properties
  • B32B2307/42—Polarizing, birefringent, filtering
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C2217/00—Coatings on glass
  • C03C2217/40—Coatings comprising at least one inhomogeneous layer
  • C03C2217/43—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase
  • C03C2217/44—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase characterized by the composition of the continuous phase
  • C03C2217/445—Organic continuous phases
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C2217/00—Coatings on glass
  • C03C2217/40—Coatings comprising at least one inhomogeneous layer
  • C03C2217/43—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase
  • C03C2217/46—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase characterized by the dispersed phase
  • C03C2217/47—Coatings comprising at least one inhomogeneous layer consisting of a dispersed phase in a continuous phase characterized by the dispersed phase consisting of a specific material
  • C03C2217/475—Inorganic materials
• • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
  • F21—LIGHTING
  • F21V—FUNCTIONAL FEATURES OR DETAILS OF LIGHTING DEVICES OR SYSTEMS THEREOF; STRUCTURAL COMBINATIONS OF LIGHTING DEVICES WITH OTHER ARTICLES, NOT OTHERWISE PROVIDED FOR
  • F21V7/00—Reflectors for light sources

Definitions

• the present disclosure relates generally to lighting systems, in particular to lighting systems for optically providing a widened perception/impression of the ambient space and in particular for imitating natural sunlight illumination. Moreover, the present disclosure relates generally to panel structures such as glass structures with chromatic features.
• WO 2014/076656 Al disclose lighting systems that use a light source producing visible light, and a panel containing nanoparticles used in transmission, i.e. the light source and the illuminated area are positioned on opposing sides of the panel.
• PCT/EP2014/059802 filed on 13 May 2015 and to be published on 19 November 2015 or PCT/EP2015/000407 filed on 23 February 2015 disclose lighting systems that use a light source producing visible light, and a chromatic mirror structure containing nanoparticles used in reflection.
• the panel receives the light from the light source and acts in transmission as a so-called Rayleigh diffuser, namely it diffuses light rays similarly to the earth atmosphere in clear-sky conditions.
• the concept uses directional light with lower correlated color temperature (CCT), which corresponds to sunlight and generates shadows in presence of lit objects, and diffuse light with larger CCT, which corresponds to the light of the blue sky and, in principal, can generate shadows with a blue tinge.
• CCT correlated color temperature
• coatings can provide properties such as anti- scratch, anti-fog, flame retardant, anti-reflection, optical features and the like.
• dispersing absorbing pigments in a resin gives the possibility to make chromatic coatings by modifying the spectrum of impinging light on the coating by absorption.
• Another way to chromatically modifying the spectrum of impinging light is to use nano-sized particles able to diffuse light by Rayleigh-like scattering.
• the present disclosure is directed, at least in part, to improving or overcoming one or more aspects of prior systems.
• Fig. 1 is a schematic illustration of a stratified panel structure
• FIGs. 2A and 2B are schematic illustration of exemplarily lighting systems using a Rayleigh-like acting panel in transmission and reflection configurations
• Figs. 3A to 4C are schematic illustrations of panel structures with one or two nanoparticle-based Rayleigh-like diffusing coatings provided as interlayers;
• Figs. 5 is an overview of three support materials for exemplary panel structures
• Figs. 6 is an overview of an exemplary coatings to be applied on selective surfaces of the support materials
• Figs. 7A to 7F is an overview of exemplary panel structure configurations using an adhesive polymeric layer as an interlay er
• Fig. 8 is an overview of modifications of an adhesive polymeric layer to perform itself Rayleigh- like scattering.
• Figs. 9 A to 9E is an overview of further exemplary panel structure configurations using the modified adhesive polymeric layer as an interlay er;
• Fig. 10 is a schematic illustration of a further stratified panel structure.
• the disclosure is based in part on the realization that compact configurations of the herein disclosed Rayleigh- like scattering feature will allow downsizing of lighting systems using the Rayleigh-like scattering feature for sun-sky-imitation effects.
• generating the sun-sky- imitation possible comprises two cover panels 102, 104. At least one of the two cover panels 102, 104 is configured to provide for the required transmission, i.e. is a transparent panel such as a glass sheet.
• An adhesive transparent polymeric layer 106 is sandwiched between two inner faces 102A, 104B of the two cover panels 102, 104. At least one nanoparticle-based Rayleigh-like diffusing coating 108 is applied to one of the inner face 102A, 104B of at least one of the two cover panels 102, 104.
• nanoparticle-based Rayleigh-like diffusing coating may be applied to a face of adhesive transparent polymeric layer 106 that prior formation of stratified panel structure 100 is a self-supporting structure and, thus, can act, for example, as a support material for a coating.
• Nanoparticle-based Rayleigh-like diffusing coating 108 therefore, forms an interlayer between one of the cover panels 102, 104 and adhesive transparent polymeric layer 106.
• a four-layer system with the Rayleigh-like diffusing coating/paint is disclosed where the coating/paint is protected inside the stratified e.g. glass structure.
• the layers between cover panels 102, 104 are herein referred to as an adhesive interlayer 110.
• exemplary sun-sky- imitation lighting system are disclosed.
• a lighting system in transmission mode with respect to chromatic stratified panel structure 100 is disclosed
• a lighting system in reflection mode with respect to chromatic stratified panel structure 100 is disclosed.
• a lighting system 1 is illustrated schematically in a cut view of a room 30.
• lighting system 1 comprises a first light source 2, configured to emit light in an emission solid angle to form a light beam 3 propagating along a main light beam direction 4.
• first light source 2 emits light in the visible region of the light spectrum, for example, with wavelengths between 400 nm and 700 nm.
• first light source 2 emits light (visible electromagnetic radiation) with a spectral width preferably larger than 100 nm, more preferably higher than 170 nm. The spectral width may be defined as the standard deviation of the first light source's wavelength spectrum.
• Bottom unit 12 comprises a diffused light generator based on chromatic stratified panel structure 100 disclosed herein and operates as a Rayleigh- like diffuser, which substantially does not absorb light in the visible range and which diffuses more efficiently the short- wavelength in respect to the long-wavelength components of the impinging light, e.g.
• a panel which substantially does not absorb light in the visible range and which diffuses light at the wavelength 450 nm (blue) at least 1.2 times, for example at least 1.4 times, such as at least 1.6 times more efficiently than light in the wavelength range around 650 nm (red), wherein a diffusion efficiency is given by the ratio between the diffused light radiant power with respect the impinging light radiant power.
• Optical properties and microscopic characteristic of Rayleigh like diffusers are also described in detail in the patent application EP 2 304 478 Almentioned above. A further insight on the microscopic features is also provided in what follows.
• Chromatic stratified panel structure 100 will separate an incident light beam 3 of light source 2 in four components, particularly in:
• a transmitted (directed non-diffuse) component (light beam 3A), formed by light rays that pass through and do not experience significant deviations, e.g. is formed by light rays experiencing a deviation smaller than 0.1 °; a luminous flux of the transmitted component is a significant fraction of the overall luminous flux incident on diffused light generator 20;
• a forward diffuse component formed by scattered light propagating into lightwell 40/room 30 (with the exception of that light beam direction and of directions differing from that light beam direction by an angle smaller than 0.1 °); a luminous flux of the forward diffuse component corresponds to a blue skylight fraction generated from the overall luminous flux incident on chromatic stratified panel structure 100;
• a backward diffuse component formed by scattered light propagating into box 16;
• a luminous flux of the backward diffuse component is, in general, in the range of but preferably less than the blue skylight fraction;
• a reflected component formed by reflected light and propagating along a direction at a mirror angle into box 16
• a luminous flux of the reflected component depends, for example, on the incident angle of the light beam onto chromatic stratified panel structure 100.
• optical properties of chromatic stratified panel structure 100 are such that
• the blue skylight fraction is within the range from 5 % to 50 %, such within the range from 7 % to 40 %, or even in the range from 10 % to 30 %, or within the range from 15 % to 20 %;
• the average CCT of the forward diffuse component is significantly higher than the average correlated color temperature CCT of the transmitted component, for example it may be higher by a factor of 1.2, or 1.3, or 1.5 or more;
• chromatic stratified panel structure 100 does not absorb significantly incident light, namely the sum of the four components is at least equal to 80 %, or 90 %, or even 95 %, or 97 % or more;
• chromatic stratified panel structure 100 scatters mostly forward, namely more than 1.1, or 1.3, or eve 1.5, or 2 two times more than is back scattered;
• chromatic stratified panel structure 100 may have low reflection, namely less than a portion of 9 %, or 6 %, or even less than 3 %, or 2 % of the impinging light is reflected.
• FIG. 2B aspects of an optical setup as well as the perceptive aspects of illuminations systems as generally described herein are described for a reflective lighting system 1.
• Lighting system 1 comprises again light source 2, configured to emit light in an emission solid angle to form a light beam 3 (in Fig. 1 delimited by dashed lines 13) propagating along a main light beam direction 4 (also referred to as main beam axis).
• light source 2 can be, for example, a cool white light source.
• Exemplary embodiments of light sources may comprise LED based light emitters or discharge lamp based light emitters or hydrargyrum medium-arc iodide lamp based light emitters or halogen lamp based light emitters and respective optical systems downstream of the respective light emitter.
• the optical systems downstream of the respective light emitter may include an optical system such as folding optics (see also Fig. 2A)
• Illumination system 1 further includes a reflector unit 6 that couples the light originating from light source 2 to a region to be lit up.
• reflector unit 6 comprises a reflective structure 8 providing a reflective surface 8A and chromatic stratified panel structure 100.
• Reflective surface 8 A is generally any type of optical acting interface that reflects light having passed through adhesive interlay er 110.
• reflective surface 8A may be a surface of an aluminum layer or an interface between components, such as a reflective coating. Due to reflective surface 8A, light of light beam 3 being incident on reflective surface 8A is redirected to pass again through chromatic stratified panel structure 100, thereafter forming an illuminating light beam 3 A (in Fig. 2B delimited by dash-dash- dotted lines 7A). In Fig.
• Illuminating light beam 3 A is, thus, directed in the to be illuminated region and comprises directed light (herein also referred to as directed (light) component of the lighting system).
• Chromatic stratified panel structure 100 is generally configured for emitting diffuse light (later also referred to as diffuse (light) component of the illumination system) at a first color, e.g. in case of a sky imitation a bluish sky color, extends in front of reflective surface 8A, and comprises a visible front area section 100A that an observer can see when looking at reflector unit 6.
• a frame-like area 14A of a frame structure 14 extends next to and surrounding visible front area section 100 A.
• the first color and the second color may be separated in the CIE
• the illuminating light beam CCT of the second color may be close to the Planckian locus (e.g. in the range from 800 K to 6 500 K).
• the second color may correspond to u'v' points with a maximum distance from the Planckian locus of e.g. 0.06.
• a distance from the Planckian locus is, for example in the range from 800 K to 6500 K, given by Au'v' ⁇ 0.060.
• the color and/or CCT of light beam 3 and illuminating light beam 3 A may be essentially identical or may differ.
• the CCT difference may be, for example, at least 300 K or even 1 000 K or more.
• an observer may have an optical perception as schematically indicated in Fig. 2B within range 7.
• the optical perception essentially depends on reflector unit 6 and the light coming therefrom as illustrated by dash-dotted lines 7B being specific for the respective observer position.
• lighting system 1 is configured such that light of significant intensity incident within range 7 of sun-observer locations originates from chromatic stratified panel structure 100.
• the light of significant intensity comprises light of light beam 3 A (originating from light source 2 and being light of light beam 3 redirected by reflector unit 6), and diffuse light originating from visible front area section 10A.
• the optical perception will - for the embodiment of Fig. 1 - comprise a, for example dark colored, frame-like area 18 around visible front area section 100A.
• Nanoparticle-based Rayleigh-like diffusing material used in the chromatic stratified panel comprises a solid matrix of a first material (e.g. resins having excellent optical transparency), wherein nanoparticles of a second material (organic or inorganic nanoparticles such as ZnO, Ti02, Si02, A1203 and similar) are dispersed.
• a first material e.g. resins having excellent optical transparency
• nanoparticles of a second material organic or inorganic nanoparticles such as ZnO, Ti02, Si02, A1203 and similar
• the refractive indexes of the two materials are different, and this mismatch on the refractive index on the nano-scale is responsible of the Rayleigh-like scattering phenomenon.
• the absorption of the first and the second material in the visible wavelength range can be considered negligible.
• the chromatic stratified panel 100 may be uniform, in the sense that, given any point of the chromatic stratified panel, the physical characteristics of the panel in that point does not depend on the position of that point.
• the nanoparticles may be monodisperse or polydisperse, they may be spherically shaped or shaped otherwise.
• the effective diameter d of the nanoparticles falls within the range [5 nm-350 nm], such as [10 nm-250 nm], or even [40 nm-180 nm], or [60 nm-150 nm], where the effective diameter d is the diameter of the equivalent spherical particle, namely the effective diameter spherical particle having similar scattering properties as the aforementioned nanoparticles.
• Diameter, refractive index mismatch and areal density (number per square meter) of the nanoparticles are the parameters that define the cross section of the scattering phenomenon in the chromatic panel.
• the amount of the impinging light scattered from the chromatic panel increases by increasing one of the parameters mentioned above.
• the regular transmittance property ⁇ ( ⁇ ) of the material at a certain wavelength as defined in the Standard Terminology of Appearance, ASTM international, E 284 - 09a, the transmittance is in general the ratio of the transmitted flux to the incident flux in the given conditions.
• the regular transmittance ⁇ ( ⁇ ) is the transmittance under the undiffused angle, i.e. the angle of incidence.
• the regular transmittance is intended for non-polarized incident light with an incident angle corresponding to the main light beam propagation.
• the regular transmittance for the blue T[450 nm] may be in general within the range [0.05-0.9]. In particular in some embodiments aiming at a pure clear sky the range would be [0.3-0.9], such as [0.35-0.85] or even [0.4-0.8]; in the embodiments aiming at a Nordic sky the range would be [0.05-0.3], such as [0.1-0.3] or even [0.15-0.3]. Since the transmittance
• the regular transmittance for the blue T[450 nm] of a chromatic stratified panel before the mirroring of the outer surface may be in general within the range [0.2-0.95]. In particular in some embodiments aiming at a pure clear sky the range would be [0.55-0.95], such as [0.6-0.92] or even [0.62-0.9]; in the
• the range would be [0.2-0.55], such as [0.3-0.55] or even [0.4-0.55].
• the transmittance of a pure clear sky is higher than the one of a Nordic sky. For example, considering the same light source impinging on two chromatic stratified panels, one in the pure clear sky configuration and one in Nordic configuration, the chromatic properties in the sun-sky effect will be different.
• diffusing coating with the structural features disclosed herein may allow addressing one or more aspects of the prior art as will be exemplarily described below for various exemplary embodiments.
• the chromatic effect is further based on nanoparticles having a refractive index that is different than the refractive index of the embedding matrix.
• the nanoparticles have a real refractive index n p sufficiently different from that of the matrix ⁇ 3 ⁇ 4 (also referred to as host material) in order to allow light scattering to take place.
• the ratio m between the particle and host medium refractive indexes (with m ⁇ — ) n h may be in the range 0.5 ⁇ m ⁇ 2.5 such as in the range 0.7 ⁇ m ⁇ 2.1 or 0.7 ⁇ m ⁇ 1.9 .
• the chromatic effect is further based on the number of nanoparticles per unit area seen by the impinging light propagating in the given direction as well as the volume-
• the distribution of nanoparticles in the diffusing layer may lose its randomness, and the particle positions may become correlated.
• the light scattered by the particle distribution experiences a modulation which depends not only on the single-particle characteristics but also on the so called structure factor.
• the effect of high filling fractions is that of severely depleting the scattering efficiency.
• high filling fractions impact also the dependence of scattering efficiency on wavelength, and on angle as well.
• d [meter] is the average particle size defined as the average particle diameter in the case of spherical particles, and as the average diameter of volume-to-area equivalent spherical particles in the case of non-spherical particles, as defined in [T.C. GRENFELL, AND S.G. WARREN, "Representation of a non-spherical ice particle by a collection of independent spheres for scattering and absorption of radiation". Journal of Geophysical Research 104, D24, 31,697-31,709. (1999)].
• the effective particle diameter is given in meters or, where specified in nm.
• N ⁇ X ⁇ — m + 2 [ me t e rs ⁇ 2 ], (Z) given
• N ⁇ ⁇ [meters -2 ], (D given in [meters] ) and N ⁇
• N, [meters -2 ] such as N ⁇ N [meters -2 ] D 6 m 2 -1 and N ⁇ [meters -2 ], more specifically
• N N > N, [meters -2 ], (D given in [meters] ) and N ⁇
• a light beam passing through a diffusive coating will generate scattered light and transmitted light.
• the coating features can modify both the spectral properties and the intensity distribution of the transmitted light.
• the morphology of the coating i.e. flatness, smoothness or orange peel
• a phase variation which implies a modulation of the intensity distribution of the transmitted light.
• the inventors realized that, when considering a rough (non-planar on a small scale) surface, the phase variation for a light beam increases by increasing the index mismatch between the two media separated by the rough surface. If a coating is exposed to the air, then the mismatch is the one between the coating and the refractive index of air. The inventors realized that a reduction of the refractive index mismatch will decrease the phase variation, and thus it will increase the uniformity in transmission (double transmission in the case of reflective configurations).
• the inventors suggest herein inter alia a configuration for a flat transparent support coated with a diffusive paint in which any modifications and distortions of a light beam passing through the coating is reduced due to refractive index adaptation.
• a glass sheet 202 is
• nano-loaded diffusive paint 208 (herein also referred to as coating when its dry form is considered).
• a transparent adhesive polymeric layer 206 (such as a PVB, EVA or similar) is sandwiched between this coated glass 202 and another glass sheet 204 wherein coating 208 is in contact with adhesive layer 206. Through a lamination process, adhesive layer 206 joins the two glass sheets 202, 204.
• the refractive index mismatch between coating 208 and adhesive layer 206 is much lower than the one that would be present between coating 208 and the air and further considering that the flatness of an outer surface of the glass sheets 202, 204 can be achieved much higher than the one achievable with a coating, the intensity profile of a light beam 3 passing through this stratified glass panel structure remains almost unmodified.
• a transparent adhesive polymeric layer 206 (such as a PVB, EVA or similar) is coated with nano-loaded diffusive paint 208.
• Transparent adhesive polymeric layer 206 is then sandwiched between two glass sheets 202, 204.
• adhesive layer 206 joins the two glass sheets 202, 204.
• light beam 3 passing through this stratified glass panel structure remains almost unmodified in terms of intensity distribution.
• the result for both process can be, for example, a safety dichroic glass sheet with the structure as shown in Fig. 1.
• the diffusing layer may be protected against atmospheric agents like UV light, dust, humidity and so on, which could change the chromatic and optical properties of the diffusing layers.
• the panel may be strong enough in order to fulfill architectural requirements such as fire resistance, shock resistance, scratch resistance and the like.
• That assembly is then introduced, for example, in a plastic bag and a low vacuum is applied to the system in order to remove any air in the bag.
• the vacuum- packed bag can then be introduced in an oven and the temperature be raised to 85 °C (with a raising rate of, for example, 3.5°C/min).
• the assemble is maintained at that temperature for about 10 min.
• the temperature is further raised to about 125°C (raising rate 3.5°C/min) and maintained at that temperature for about 30 min.
• the assembly is than cooled to room temperature in, e.g. about 20 min and the stratified glass panel structure is removed from the plastic bag.
• FIGs. 4A to 4C starting points of a lamination process is illustrated for a chromatic stratified panel structure with two nano-loaded diffusive coatings 306.
• the layers of nano-loaded diffusive coatings 306 are separated by a transparent adhesive polymeric layer 308.
• the starting point of the lamination process can be based on two glass sheets 302, 304 each coated with a nano-loaded diffusive paint 306 at their inner surfaces (Fig. 4A).
• both sides of transparent adhesive polymeric layer 308 may be coated (Fig. 4C) or one side of one of the glass sheets 302, 304 and transparent adhesive polymeric layer 308 may be coated (Fig. 4B).
• the panel structure generally comprises three main free stranding (self- supporting) components suitable for coating purposes (herein also referred to as support layer) so that at four internal surfaces need to be joined. This allows up to four internal surfaces being coated with nano-loaded diffusive paint 306, wherein all layers together provide the desired Rayleigh-like scattering effect. In configurations having multiple surfaces coated, the randomness in layer thickness of the various coatings may reduce the overall variations in thickness of the combined layers such that the uniformity with respect to the Rayleigh-like scattering process over the panel structure can be increased.
• glass sheets may be used such as normal float glass, tempered, Anti Reflective (AR) coated glass, surface etched glass and similar.
• AR Anti Reflective
• one of the two external glass surfaces of the stratified panel structure may be provided with a reflective coating (i.e. aluminum coating).
• etching solution comprising hydrofluoric acid as an active component.
• Different parameters can affect the final results of etching process for example the composition of the etching liquid, the reaction time and temperature, the application method of the etching liquid, the surface quality of the glass and the glass composition .
• a similar process involving the use of etching cream based on fluoride compounds has been developed in order to minimize problems of toxicity and safety related with the handling of Hydrofluoric Acid.
• the glass is formed inside a structured mold, when removing the glass, it will have the shape and roughness of the mold. This is one of the cheapest methods in the glass industry.
• the terms "paint”, “coating” and “film” refer, in contrast to the term “adhesive polymeric layer", to a layer that is/needs to be applied on a support structure. In contrast, the “adhesive polymeric layer” is considered an independent structural unit.
• a paint may be a clear material that is applied in liquid form on a surface and after a time produces a dry adherent film. Paint is essentially composed of a binder, particles, and a solvent.
• Binder refers to the non- volatile portion of the vehicle of a coating material that binds the particles together and the film as a whole to the support substrate. Binders can include synthetic or natural resins and can further be classified according to the mechanisms for drying or curing.
• Particles refers to a material, usually with nano or micrometric size that is practically insoluble in the medium and commonly used because of its optical, protective or decorative properties. Particles are broadly classified as either organic or inorganic.
• a solvent refers to a liquid, single or blended, which is volatile under normal drying conditions and in which the binder is soluble.
• Additional components of a paint may be thinners (a volatile liquid, able to facilitate application), catalysts, thickeners, stabilizers, flatteners, emulsifiers, adhesion promoters, UV stabilizers etc.
• thinners a volatile liquid, able to facilitate application
• catalysts a volatile liquid, able to facilitate application
• thickeners a volatile liquid, able to facilitate application
• stabilizers a volatile liquid, able to facilitate application
• flatteners emulsifiers
• adhesion promoters esion promoters
• UV stabilizers etc.
• a primer can be used before application.
• the herein disclosed paints/coatings/films can be made by using as a binder an organic polymer commonly used in industry such as polystyrene, polyurethane, acrylics, alkyd polymer, polyester, siloxane-containing polymer, epoxy-containing polymer etc or a combination of them.
• organic polymer commonly used in industry
• a diluting agent can be added, including water or organic (i.e. alcohol, ethers, ketone, esters, aliphatic and aromatic hydrocarbons or others) acting as solvent.
• solvent commonly employed in the coating industries include, for example, xylene, hexane, acetone, diethyleneglycol, and isopropyl alcohol.
• the nature of binder and the relative amount of components added in the resulting paint mixture will depend on several parameters such as the glass surface properties, the application method, and the interaction of the coating with the adhesive layer during the lamination process.
• the material for the nanoparticles or their core may be made with one or more materials that essentially do not absorb light in the visible range having an organic or inorganic nature.
• the inventors are referring to polymers (optionally crosslinked) while in the second case preferably to metal oxides (e.g. Ti02, Si02, ZnO, Zr02, Fe203, A1203, Sb2Sn05, Bi203, Ce02 or a combination thereof) with a single phase structure or a core/shell structure.
• the external surface of the nanoparticle core is preferably functionalized with a specific organic coating in order to guarantee an optimal compatibility and dispersion in the paint matrix.
• a poor compatibility of nanoparticles with the paint matrix may lead to the formation of large aggregate/agglomerates and inhomogeneous distribution that will strongly affect the scattering properties of the diffusing coating and consequently of the resulting embodiment.
• the particle sizes may be selected to obtain the required chromatic properties.
• diameter size may be between about 5 nm to 250 nm such as between 20 nm and 150 nm.
• Functionalized nanoparticles may be introduced directly in the binder/solvent mixture or in the paint with the desired final composition.
• the dispersion process may use low/high shear mixing equipment such as magnetic stirrer and/or static mixers.
• the coating can be applied on the glass or directly on the adhesive polymeric layer by commonly used processes such as dip coating, spray coating, inkjet coating, electrodeposition, serigraphy and similar.
• suitable materials mainly include that one typically employed in the stratification industry such as transparent thermoplastic materials (TPU or PVB, EVA) or transparent thermoset material (EVA). At present EVA and PVB covered almost 100% of the production of the stratified glass.
• EVA PolyEthylene-vinyl acetate, is the copolymer of ethylene and vinyl acetate. The weight percent vinyl acetate usually varies from 10% to 40%, with the remainder being ethylene. Different mechanical/adhesive and chemical properties varying depending on the ratio between ethylene and vinyl acetate employed during the synthetic process. The main advantages of EVA are related to its excellent transparency, good adhesion and compatibility, resistance to humidity and long term reliability.
• PVB Poly(Vinyl Butyral) is prepared from polyvinyl alcohol by reaction with butyraldehyde. Elasticity, mechanical strength, toughness, high light transmission and the adhesion to glass are the most significant PVB properties.
• F represents a glass panel (or generally a light transmitting panel), F represents a
• microstructured surface glass i.e. a support material with one side being provided with a microstructure
• A represents an adhesive polymer layer
• microstructured surface glass in G i° and F i° “ j" refers to the outer side, "o", and "i" to inner side, "i”.
• the syntax is based on coating types shown in Fig. 6 that include a nanoparticle-based Rayleigh-like diffusing coating (a), a microparticle-based diffusing coating (b), a coating combining nanoparticle-based Rayleigh-like diffusing and
• microparticle-based diffusing (c), an antireflective coating (d), and a mirror (reflective e.g. in the visible) coating (e).
• microparticle-based diffusing coating (b) is obtained with the same
• the desired particles size range is comprised between 1 ⁇ to 20 ⁇ .
• Materials composing the particles can have organic or inorganic nature, in the first case we refer mainly to polymers while in the second case to metal oxide or similar preferably not absorbing in the visible.
• additional functionalization can also be included on the microparticle's surface in order to increase the compatibility between the particles and the transparent paint.
• Microparticles may be present in an amount of about 1 to about 40% (w/w) with respect to the binder.
• the resulting coating after paint dry may have a thickness of about 2 ⁇ to about 100 ⁇ . These particles are beyond of the Rayleigh scattering regime because of their size. Both the chromatic and the distribution intensity of the light scattered by these microparticles are different to the one scattered by the nanosized particles. The spectrum and the intensity of the scattered light is strongly dependent to the scattering angle. In general, considering a sample of microparticles not perfectly monodispersed, the scattered light will be mostly forward scattered without any dependence on the wavelength. By increasing the microparticles size, the scattering angle (the cone angle defined by the intensity profile of the forward scattering) becomes narrower. The microparticle diffusive layer provokes a blurry effect on the panel.
• the coating (c) combines the nanoparticle-based Rayleigh-like diffusing features and the microparticle-based diffusing features.
• the antireflective coating (d) is a physico-chemical surface treatment that allows increasing the regular transmittance of a material. This treatment has to be optimized on a defined wavelength range (visible range for the present application) and strongly depends on the optical properties of the materials facing the antireflective coating.
• An antireflective coating optimized for the interface glass-air in the visible spectrum makes the panels shown in Fig. 2 more efficient in terms of transmittance and decrease the intensity of the reflected scene.
• the mirror coating (e) can be applied on the outer surface of the stratified panels in order to obtain high quality surface chromatic stratified mirror.
• a typical way to produce mirror is to deposit metals such as aluminum or silver on a glass surface. The reflection efficiency depends on the deposited material and the quality of the reflected image depends on the flatness/roughness of the glass.
• r can be (a), (b), or (c).
• i can be (a), (b), or (c), while "o” can be (b), (d) or (e).
• Figs. 7A to 7F illustrate exemplary sandwich structures.
• Figs. 7A and 7B correspond to Figs. 3A and 3B, respectively.
• Fig. 7C illustrates a sandwich structure having a microstructure on one outer surface.
• a microstructure surface has the effect of blurring the perceived scene behind the microstructure surface. This property may be desired because those objects seen through (unwanted structures beyond) and virtual images on the panel (refiected images coming from objects of the scene) will be perceived blurry. Accordingly, the variation of the luminance - typical in an observed surface - may originally have sharp edges but can be smoothed by the microstructure surface based, thereby enhancing the depth perception.
• Fig. 7D illustrates a structure similar to Fig. 4B, wherein one nanoparticle- based Rayleigh-like diffusing coating is replaced with a microparticle-based diffusing coating such that forward scattering and a respective blurring effect is introduced.
• Fig. 7E illustrates a sandwich structure having a microstructure on one outer side and an antireflective coating on the inner side.
• the antireflective coating allows, for example, increasing the transmittance of the panel, thereby making the lighting system more efficient.
• Fig. 7F illustrates a sandwich structure having a mirror coating on one outer side. This configuration can be used in the reflection mode as the lighting system described in connection with Fig. 2B.
• the embodiments are modified in that the diffusing property of the diffusing layer is transferred from a separate coating, being applied e.g. on the interface surfaces including on the side wall of a stand alone adhesive polymeric layer, to being directly inside in the polymeric adhesive layer.
• those new embodiments comprises a stratified-glass panel structure composed of two float glass sheets 104 and 106 sandwiching, and affixed to each other, by way of an adhesive transparent polymeric layer (e.g. an EVA, PVB layer or similar) that is loaded with nanoparticles.
• an adhesive transparent polymeric layer e.g. an EVA, PVB layer or similar
• the adhesive polymeric layer can - in addition to nanoparticles - be loaded with (larger) microparticles together.
• the modified adhesive transparent polymeric layer is herein referred to as nanoloaded adhesive polymeric layer.
• a nanoloaded adhesive polymeric layer may be obtained by different processes available in the industry. One possible process may comprise melting of a solid thermoplastic resin in an extruder followed by addition of the desired amount of nanoparticles. After blending the two component, the mixture is extruded in sheet form with the desired thickness. The method may further comprises pre-mixing the solid thermoplastic resin and the nanoparticles prior to melting the solid thermoplastic resin.
• a second type of process may comprise a direct dissolution and mixing of the nanoparticles with monomers (the simplest unit, or the repeating unit, of a polymer) prior of the polymerization process. This process can lead to a higher degree of dispersion of the nanoparticles even though it has some drawback for the scale up in an industrial plant.
• the adhesive polymeric layer may be based on suitable materials including those that are typically employed in the stratification industry such as transparent thermoplastic materials (TPU or PVB, EVA) or transparent thermoset material (EVA).
• suitable materials including those that are typically employed in the stratification industry such as transparent thermoplastic materials (TPU or PVB, EVA) or transparent thermoset material (EVA).
• Nanoparticles and microparticles features are the same as previously stated for the nanoparticle coating.
• the adhesive layer and consequently in the final stratified structure, it may be convenient to modify the surface structure of the nanoparticles itself with a specific agent (molecule, polymer etc.) able to guarantee a good compatibility between the particles and the polymeric layer.
• a specific agent molecule, polymer etc.
• microparticles may be added during the mixing process together with the nanoparticles.
• the inner sandwiched material i.e. the "adhesive polymeric layer” used for incorporating the nanoparticle for the Rayleigh-like diffusing, is referred to in the syntax introduced above as NA.
• the inner sandwiched material "adhesive polymeric layer” may be used for incorporating microparticles for diffusing light - additionally to the nanoparticles for the Rayleigh-like diffusing.
• that layer is referred to as NA '.
• Respective support structures are schematically indicated in Fig. 8 similar to Fig. 5, which also illustrates the glass panels G and F. [1 12] It is noted that in the case of most simple sandwich structures, none of the support structures has an "inner” coating, i.e. N I 1S only NA same for NA and G°i is only G°.
• the outer surfaces defined for the materials can be coated, for example, with an antireflective coating (d), and a mirror (reflective e.g. in the visible) coating (e).
• FIG. 9A to 9E illustrate exemplary sandwich structures.
• Figs. 9A and 9B correspond to simple three-layer structures without and with a microstructured outer surface, respectively.
• FIG. 9C The embodiment of Fig. 9C combines Rayleigh-like scattering features with forward scattering features.
• FIG. 9D uses microstructure at the inner side of one of the glass panels for diffusing, thereby also strengthening the adhesion between NA and that glass panel.
• an outer side is coated with an antireflecting coating to e.g. suppress any back scattering from the background.
• FIG. 10 schematically shows a resulting chromatic stratified panel structure
• Chromatic stratified panel 400 comprises two cover panels 102, 104, at least one of which being a transparent panel and/or having a microstructure surface at one side.
• Chromatic stratified panel 400 comprises further as an interlayer 1 10, an adhesive transparent polymeric layer 406 (left side of the embodiment illustrated in Fig. 10) as described above or a modified adhesive polymeric layer 406' incorporating microparticles for diffusing light in additionally to the nanoparticles for the Rayleigh-like diffusing (right side of the embodiment illustrated in Fig. 10) as also described above.
• the adhesive polymeric layers 406 , 406' are sandwiched between the two inner faces of the two cover panels 102, 104. Moreover, they may be essentially transparent in the visible.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Physics & Mathematics (AREA)
• General Engineering & Computer Science (AREA)
• Dispersion Chemistry (AREA)
• Geochemistry & Mineralogy (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Life Sciences & Earth Sciences (AREA)
• Materials Engineering (AREA)
• Organic Chemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Spectroscopy & Molecular Physics (AREA)
• General Physics & Mathematics (AREA)
• Optics & Photonics (AREA)
• Composite Materials (AREA)
• Ceramic Engineering (AREA)
• Optical Elements Other Than Lenses (AREA)
• Non-Portable Lighting Devices Or Systems Thereof (AREA)
• Laminated Bodies (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Related Child Applications (1)

Publications (1)

Family

ID=57544383

Family Applications (1)

Country Status (6)

Cited By (4)

Families Citing this family (12)

Citations (7)

Family Cites Families (20)

• 2016
  • 2016-11-15 KR KR1020187017285A patent/KR20180084937A/ko not_active Withdrawn
  • 2016-11-15 JP JP2018526091A patent/JP6487605B2/ja not_active Expired - Fee Related
  • 2016-11-15 WO PCT/EP2016/077770 patent/WO2017085079A1/en active Application Filing
  • 2016-11-15 CN CN201680079390.3A patent/CN109153232B/zh active Active
  • 2016-11-15 EP EP20150861.1A patent/EP3702151A1/en not_active Withdrawn
  • 2016-11-15 EP EP16810258.0A patent/EP3377317B1/en active Active
  • 2016-11-15 US US15/777,003 patent/US10723103B2/en active Active
• 2019
  • 2019-02-21 JP JP2019029088A patent/JP2019096622A/ja active Pending

Patent Citations (9)

Also Published As

Similar Documents

Legal Events