WO2016199997A1 - 자외선 차단 기능이 부여된 화장료 조성물 및 이의 제조 방법 - Google Patents

자외선 차단 기능이 부여된 화장료 조성물 및 이의 제조 방법 Download PDF

Info

Publication number
WO2016199997A1
WO2016199997A1 PCT/KR2015/013715 KR2015013715W WO2016199997A1 WO 2016199997 A1 WO2016199997 A1 WO 2016199997A1 KR 2015013715 W KR2015013715 W KR 2015013715W WO 2016199997 A1 WO2016199997 A1 WO 2016199997A1
Authority
WO
WIPO (PCT)
Prior art keywords
graphene quantum
weight
cosmetic composition
quantum dot
sunscreen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2015/013715
Other languages
English (en)
French (fr)
Inventor
전석우
윤혜원
송성호
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Korea Advanced Institute of Science and Technology KAIST
Original Assignee
Korea Advanced Institute of Science and Technology KAIST
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Korea Advanced Institute of Science and Technology KAIST filed Critical Korea Advanced Institute of Science and Technology KAIST
Publication of WO2016199997A1 publication Critical patent/WO2016199997A1/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

그래핀 양자점(Graphene Quantum Dots: GQD)을 포함하며 자외선 차단 기능을 갖는 화장료 조성물이 제공된다. 그래핀 양자점 추가에 따라 피부 친화도가 향상되면서 자외선 흡수능이 강화될 수 있다.

Description

자외선 차단 기능이 부여된 화장료 조성물 및 이의 제조 방법
본 발명은 자외선 차단 기능이 부여된 화장료 조성물 및 이의 제조 방법에 관한 것이다. 보다 상세하게는, 본 발명은 자외선 흡수가 가능하며 자외선 차단 기능이 부여된 화장료 조성물 및 이의 제조 방법에 관한 것이다.
환경 오염에 따라 자외선 노출 우려도 증가하고 있으며, 자외선 차단제의 수요 역시 함께 증가하고 있다. 예를 들면, 지표면에 도달하는 자외선은 파장대에 따라 UVC(약 200 nm 내지 약 280 nm), UVB(약 280 내지 약 320 nm) 및 UVA(약 320 nm 내지 약 400 nm)으로 분류되며, 이 중 UVC는 오존층에서 대부분 흡수되므로, UVA 및 UVB 영역의 자외선을 효과적으로 동시에 차단하기 위한 자외선 차단제가 필요하다.
상기 자외선 차단제는 자외선 산란 기능을 갖는 이산화티탄과 같은 무기 계열 자외선 산란제, 및 화학적으로 자외선을 흡수하는 유기 화합물을 포함하는 유기 계열 자외선 흡수제를 포함할 수 있다.
예를 들면, 특허문헌 1은 이산화티탄을 포함한 자외선 차단제를 개시하고 있다.
<선행기술문헌>
<특허문헌>
1. 대한민국 공개특허공보 제2015-0035126호(2015.04.06)
본 발명의 일 과제는 우수한 화학적 특성을 가지며 인체 적용성이 우수한 자외선 차단 기능이 부여된 화장료 조성물을 제공하는 것이다.
본 발명의 일 과제는 우수한 화학적 특성을 가지며 인체 적용성이 우수한 자외선 차단 기능이 부여된 화장료 조성물을 제조 방법을 제공하는 것이다.
다만, 본 발명이 해결하고자 하는 과제는 상기 언급된 과제에 한정되는 것이 아니며, 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위에서 다양하게 확장될 수 있을 것이다.
상술한 본 발명의 일 과제를 달성하기 위한 본 발명의 예시적인 실시예들에 따른 화장료 조성물은 그래핀 양자점을 포함하며 자외선 차단 기능을 가질 수 있다.
예시적인 실시예들에 따르면, 상기 화장료 조성물은 상기 그래핀 양자점, 무기 자외선 산란제, 유기 자외선 흡수제 및 에멀젼을 포함할 수 있다.
예시적인 실시예들에 따르면, 상기 조성물은 총 중량 대비 약 0.5 중량% 내지 약 5 중량%의 상기 그래핀 양자점, 약 5 중량% 내지 약 10 중량%의 상기 무기 자외선 산란제, 약 3 내지 약 7.5 중량%의 상기 유기 자외선 흡수제, 및 약 78 중량% 내지 약 91 중량%의 상기 에멀젼을 포함할 수 있다.
예시적인 실시예들에 따르면, 상기 무기 자외선 산란제는 금홍석(rutile) 이산화티탄을 포함할 수 있다.
예시적인 실시예들에 따르면, 상기 유기 자외선 흡수제는 에틸헥실 메톡시신나메이트, 에틸헥실살리실레이트, 4-메틸벤질리덴캠퍼, 이소아밀 p-메톡시신나메이트, 옥토크릴렌, 페닐벤즈이미다졸설포닉산, 호모살레이트, 시녹세이트, 에틸헥실트리아존, 폴리실리콘-15, 티이에이-살리실레이트, 팝바(PABA), 에틸헥실디메틸파바 또는 글리세릴파바를 포함할 수 있다. 이들은 단독으로 혹은 2 이상이 조합되어 사용될 수 있다.
상술한 본 발명의 일 과제를 달성하기 위한 본 발명의 예시적인 실시예들에 따른 자외선 차단제의 제조 방법에 따르면 그래핀 양자점 분말을 준비한다. 상기 그래핀 양자점 분말 및 무기 자외선 산란제의 혼합물을 제조한다. 상기 혼합물을 열처리하여 복합 안료를 형성한다. 상기 복합 안료에 유기 자외선 흡수제 및 에멀젼을 혼합한다.
예시적인 실시예들에 따르면, 상기 그래핀 양자점 분말을 준비함에 있어서, 금속 이온이 그래파이트 층에 삽입된 그래파이트 층간 화합물로부터 금속 이온을 제거하여 그래핀 양자점 수분산체를 제조할 수 있다.
예시적인 실시예들에 따르면, 상기 그래핀 양자점 분말을 준비함에 있어서 상기 그래핀 양자점 수분산체를 약 100℃ 내지 약 130℃의 온도에서 건조시킬 수 있다.
예시적인 실시예들에 따르면, 상기 혼합물을 열처리하는 단계는 약 100℃ 내지 약 200℃의 온도에서 수행될 수 있다.
예시적인 실시예들에 따르면, 상기 무기 자외선 산란제 및 상기 유기 자외선 흡수제로서 각각 금홍석 이산화티탄 및 에틸헥실 메톡시신나메이트를 사용할 수 있다.
예시적인 실시예들에 따르면, 상기 자외선 차단제의 총 중량 대비 약 0.5 중량% 내지 약 5 중량%의 상기 그래핀 양자점 분말, 약 5 중량% 내지 약 10 중량%의 상기 무기 자외선 산란제, 약 3 내지 약 7.5 중량%의 상기 유기 자외선 흡수제, 및 약 78 중량% 내지 약 91 중량%의 상기 에멀젼이 조합될 수 있다.
상술한 바와 같이 본 발명의 예시적인 실시예들에 따르면, 자외선 흡수 기능을 갖는 그래핀 양자점을 화장료 조성물에 포함시킬 수 있다. 예를 들어, 그래핀 양자점이 이산화티탄과 같은 무기계열 자외선 산란제 및 유기 계열 자외선 흡수제와 함께 사용되는 경우, 상기 무기 물질에 의한 피부 발림성 저하, 백탁 현상 등을 현저히 개선하여 피부에의 친화성을 증가시킬 수 있다. 또한, 이산화티탄에 의한 광촉매 반응을 억제하고, 자외선 흡수 가능한 파장 영역 및 흡수 세기를 확장시킬 수 있다.
상기 그래핀 양자점은 저비용으로 표준화된 공정에 의해 생산될 수 있으므로, 화장료 조성물의 경제성 역시 향상될 수 있다.
도 1은 예시적인 실시예들에 따른 화장료 조성물의 제조 방법을 설명하기 위한 순서도이다.
도 2는 건조된 분말상의 그래핀 양자점의 사진이다.
도 3은 실험예 1에 따른 조성물들을 사용하여 자외선 흡수능을 측정한 UV/VIS 그래프이다.
도 4는 실험예 2에 따른 조성물들을 사용하여 자외선 흡수능을 측정한 UV/VIS 그래프이다.
도 5는 실험예 3에 따른 스킨 토너를 사용하여 자외선 흡수능을 측정한 UV/VIS 그래프이다.
도 6은 예시적인 실시예들에 따른 화장료 조성물의 발색을 비교하기 위한 사진들이다.
도 7은 예시적인 실시예들에 따른 화장료 조성물의 피부 발림성을 나타내는 사진들이다.
도 8은 예시적인 실시예들에 따른 화장료 조성물의 피부 안정성을 나타내는 사진들이다.
이하, 첨부한 도면을 참조하여 본 발명의 실시예에 대해 상세히 설명한다. 본 발명은 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있는 바, 특정 실시예들을 예시하고 본문에 상세하게 설명하고자 한다. 그러나 이는 본 발명을 특정한 개시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 첨부된 도면에 있어서, 구조물들의 치수는 본 발명의 명확성을 기하기 위하여 실제보다 확대하여 도시한 것이다.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.
화장료 조성물
예시적인 실시예들에 따르면, 화장료 조성물은 그래핀 양자점(Graphene Quantum Dots: GQD)을 포함할 수 있다. 상기 그래핀 양자점이 포함됨에 따라 상기 화장료 조성물은 자외선 흡수 기능을 가지며 이에 따라, 자외선 차단 기능이 부여된 각종 화장품, 미용 제품으로 제공될 수 있다.
상기 그래핀 양자점은 최종적으로 건조된 분말 상으로 제조될 수 있다(도 2 참조). 일부 실시예들에 있어서, 상기 그래핀 양자점은 자외선 흡수 기능의 효율을 위해 예를 들면 약 20 nm이하의 직경을 갖는 것을 사용할 수 있다. 일 실시예에 있어서, 약 10 nm 내지 약 20 nm의 직경을 갖는 그래핀 양자점을 사용할 수 있다.
일부 예시적인 실시예들에 따르면, 상기 화장료 조성물은 자외선 차단제로 제공될 수 있다. 예시적인 실시예들에 따르면, 상기 자외선 차단제는 에멀젼, 무기 자외선 산란제, 유기 자외선 흡수제 및 상기 그래핀 양자점을 포함할 수 있다.
상기 에멀젼은 상기 자외선 차단제의 도포성, 피부 적용성을 부여하기 위한 베이스 제제일 수 있다. 상기 에멀젼은 다양한 유기 계열의 당해 기술 분야에서 공지된 물질을 포함할 수 있으며, 특별히 그 조성이 한정되는 것은 아니다.
예시적인 실시예들에 따르면, 상기 무기 자외선 산란제로서 이산화티탄(TiO2)을 사용할 수 있다. 일부 실시예들에 있어서, 상기 무기 자외선 산란제로서 예를 들면, 약 100 nm 이하의 직경을 갖는 금홍석(rutile) 이산화티탄 나노입자를 사용할 수 있다. 아나타제(anatase) 형태의 이산화티탄 나노입자를 사용하는 경우, 자외선에 의해 광촉매 반응이 활성화되어 라디칼과 같은 활성종이 다량 생성될 수 있으므로, 금홍석 형태의 이산화티탄 나노입자를 사용할 수 있다.
상기 유기 자외선 흡수제로서 UVB 영역의 자외선을 흡수할 수 있는 유기 화합물을 사용할 수 있다. 예를 들면, 상기 유기 자외선 흡수제로서 에틸헥실 메톡시신나메이트(예를 들면, 2-Ethylhexyl 4-methoxycinnamate), 에틸헥실살리실레이트, 4-메틸벤질리덴캠퍼, 이소아밀 p-메톡시신나메이트, 옥토크릴렌, 페닐벤즈이미다졸설포닉산, 호모살레이트, 시녹세이트, 에틸헥실트리아존, 폴리실리콘-15, 티이에이-살리실레이트, 팝바(PABA), 에틸헥실디메틸파바, 글리세릴파바 등을 사용할 수 있다. 이들은 단독으로 또는 2 이상이 조합되어 사용될 수 있다.
일부 예시적인 실시예들에 있어서, 상기 유기 자외선 흡수제로서 에틸헥실 메톡시신나메이트를 사용할 수 있다.
예시적인 실시예들에 있어서, 상기 자외선 차단제는 총 중량 대비 약 0.5 중량% 내지 약 5 중량%의 상기 그래핀 양자점, 약 5 중량% 내지 약 10 중량%의 상기 무기 자외선 산란제, 약 3 내지 약 7.5 중량%의 상기 유기 자외선 흡수제, 및 잔량의 상기 에멀젼을 포함할 수 있다. 예를 들면, 상기 에멀젼은 상기 자외선 차단제의 총 중량 대비 약 78 중량% 내지 약 91 중량%의 함량으로 포함될 수 있다.
상술한 바와 같이, 예시적인 실시예들에 따르면, 상기 그래핀 양자점의 첨가에 의해 상기 자외선 차단제의 자외선 흡수능력(예를 들면, 흡수 파장 영역 및 흡수 세기)이 보다 강화될 수 있다.
추가적으로, 상기 자외선 차단제에 자외선 흡수 기능을 갖는 상기 그래핀 양자점이 포함되므로, 상기 무기 자외선 산란제 및 상기 유기 자외선 흡수제의 함량이 인체 적용을 위한 허용 한도보다 감소될 수 있다. 예를 들면, 피부 발림성이 약하고, 광촉매 반응을 유발할 수 있는 이산화티탄과 같은 상기 무기 자외선 산란제의 함량이 감소될 수 있다. 따라서, 피부 질환과 같은 부작용을 야기하지 않으면서 인체 친화도 및/또는 적합성이 향상된 자외선 차단제가 수득될 수 있다.
또한, 상기 그래핀 양자점의 갈색 계통의 고유한 색상이 백색의 이산화티탄과 혼합되어, 자연스러운 피부색 발현이 가능할 수 있다. 따라서, 추가적인 색소, 안료의 첨가 없이도 적용 가능한 자외선 차단제가 수득될 수 있다.
예시적인 실시예들에 따른 화장료 조성물은 상기 자외선 차단제에 제한되는 것은 아니다. 예를 들면, 상기 화장료 조성물은 상기 그래핀 양자점이 포함된 미백용 로션, 보습제, 스킨 등과 같은 다양한 화장료 제품으로 제조되어 자외선 흡수능이 부여된 기능성 조성물로 제공될 수 있다.
도 1은 예시적인 실시예들에 따른 화장료 조성물의 제조 방법을 설명하기 위한 순서도이다. 예를 들면, 도 1은 그래핀 양자점이 첨가된 자외선 차단제의 제조 방법을 설명하고 있다. 한편, 도 2는 건조된 분말상의 그래핀 양자점의 사진이다.
도 1 및 도 2를 참조하면, 단계 S10에서, 그래핀 양자점 분말을 준비할 수 있다.
일부 실시예들에 있어서, 상기 그래핀 양자점은 금속 이온이 그래파이트 층에 삽입된 그래파이트 층간 화합물로부터 금속 이온을 제거함으로써 제조될 수 있다. 상기 그래핀 양자점의 제조 방법은 예를 들면, 본 출원에 참조로서 병합되는 본 출원인의 공개특허공보 제2015-0044326호(공개일 2015.05.04, 출원번호 2013-0127275)를 참조할 수 있다. 예를 들면, 상기 그래핀 양자점은 약 20 nm 이하의 직경을 갖는 수분산체로서 제조될 수 있다.
이후, 물에 분산된 상기 그래핀 양자점을 예를 들면, 약 100℃ 내지 약 130℃의 온도에서 건조시켜 도 2에 도시된 바와 같은 그래핀 양자점 분말을 수득할 수 있다.
그러나, 상기 그래핀 양자점은 상기 그래파이트 층간 화합물 외에 다양한 탄소 전구체들로부터 수득될 수도 있다.
다시 도 1을 참조하면, 단계 S20에서, 상기 그래핀 양자점 분말 및 무기 자외선 산란제의 혼합물을 제조할 수 있다.
상술한 바와 같이, 상기 무기 자외선 산란제로서 금홍석 이산화티탄을 사용할 수 있다. 예를 들면, 상기 그래핀 양자점 분말 및 금홍석 이산화티탄을 유발 및 막자사발을 이용하여 고르게 혼합/교반하여 상기 혼합물을 제조할 수 있다.
단계 S30에서, 상기 혼합물을 열처리하여 복합 안료를 형성할 수 있다.
예시적인 실시예들에 따르면, 약 100℃ 내지 약 200℃의 온도에서 상기 혼합물을 수분 내지 수백분 동안 가열하여 상기 그래핀 양자점 분말 및 금홍석 이산화티탄이 고르게 분포되어 실질적으로 균일상으로 형성된 복합 안료가 제조될 수 있다. 상기 열처리에 의해 상기 복합 안료들에 포함된 상기 그래핀 양자점 분말 및 금홍석 이산화티탄의 결정 구조가 안정화될 수 있다. 일부 실시예들에 있어서, 상기 열처리는 약 150℃ 내지 약 200℃의 온도에서 수행될 수 있다.
이후, 단계 S40에서, 상기 복합 안료에 유기 자외선 흡수제 및 에멀젼을 혼합하여 예시적인 실시예들에 따른 화장료 조성물이 제조될 수 있다.
상술한 바와 같이, 상기 유기 자외선 흡수제로서 에틸헥실 메톡시신나메이트와 같은 UVB 영역 자외선 흡수 기능을 갖는 유기 화합물을 사용할 수 있다.
일부 실시예들에 따르면, 제조된 상기 화장료 조성물은 총 중량 대비 약 0.5 증량% 내지 약 5 중량%의 상기 그래핀 양자점, 약 5 중량% 내지 약 10 중량%의 상기 무기 자외선 산란제, 약 3 내지 약 7.5 중량%의 상기 유기 자외선 흡수제, 및 약 78 중량% 내지 약 91 중량%의 상기 에멀젼을 포함할 수 있다.
이하에서는, 구체적인 실험예를 참조로 예시적인 실시예들에 따른 화장료 조성물의 특성에 대해 보다 상세히 설명한다.
실험예 1: 그래핀 양자점 추가에 따른 자외선 흡수능 평가
도 1을 참조로 설명한 제조 방법에 따라, 하기의 표 1에 따른 조성을 갖는 조성물들을 제조하였다. 구체적으로, 무기 자외선 산란제로서 금홍석 이산화티탄(rutile TiO2)을 사용하였고, 유기 자외선 흡수제로서 2-에틸헥실 4-메톡시신나메이트(OMC)를 사용하였다. 그래핀 양자점은 GQD로 표시된다
Figure PCTKR2015013715-appb-T000001
도 3은 실험예 1에 따른 조성물들(표 1의 조성물들)을 사용하여 자외선 흡수능을 측정한 UV/VIS 그래프이다.
표 1 및 도 3을 참조하면, OMC를 포함한 조성물 2의 경우 약 320 nm 내지 약 340 nm 영역의 UV를 흡수하며, 조성물 6과 같이 그래핀 양자점이 추가됨에 따라 흡수의 세기가 보다 강해짐을 알 수 있다. 따라서, 상기 그래핀 양자점이 자외선 흡수 강화제로서 작용함을 알 수 있다.
한편, OMC 및 TiO2가 함께 포함된 조성물 5의 경우 보다 넓은 파장 범위에서 UV 흡수능이 나타났으며, 조성물 8과 같이 그래핀 양자점이 추가됨에 따라 흡수 파장 영역 및 흡수의 세기가 보다 강화됨을 알 수 있다.
따라서, TiO2의 첨가에 따라 흡수되는 파장의 범위가 보다 확대될 수 있으며, 그래핀 양자점이 첨가되면서 흡수의 세기가 강화됨을 예측할 수 있다.
실험예 2: 그래핀 양자점 함량에 따른 자외선 흡수능 평가
도 1 및 실험예 1을 참조로 설명한 제조 방법에 따라, 하기의 표 2에 따른 조성을 갖는 조성물들을 제조하였다.
Figure PCTKR2015013715-appb-T000002
도 4는 실험예 2에 따른 조성물들(표 2의 조성물들)을 사용하여 자외선 흡수능을 측정한 UV/VIS 그래프이다.
표 2 및 도 4를 참조하면, 조성물 2에서 그래핀 양자점이 추가됨에 따라(조성물 3) 전체적으로 UV 흡수 세기가 증가하였으며, 특히 약 340 nm 이상의 범위에서 이러한 경향이 확인되었다. 또한, 그래핀 양자점이 더욱 증가됨에 따라(조성물 4) UV 흡수 세기가 추가적으로 증가되었다.
실험예 3: 그래핀 양자점이 첨가된 스킨 토너의 자외선 흡수능 평가
상업적으로 시판되는 스킨 토너 제품에 그래핀 양자점을 아래의 표 3에 따라 첨가하여 자외선 흡수 특성을 평가하였다.
Figure PCTKR2015013715-appb-T000003
도 5는 실험예 3에 따른 스킨 토너를 사용하여 자외선 흡수능을 측정한 UV/VIS 그래프이다.
표 3 및 도 5를 참조하면, 일반 스킨 토너는 약 300 nm 이상의 파장 범위에서는 실질적으로 흡수능을 보이지 않으나, 그래핀 양자점의 양이 증가함에 따라 약 300 nm 이상의 파장의 UV 영역에서 흡수 세기가 증가함을 알 수 있다.
따라서, 자외선 차단제 뿐만 아니라 일반 화장료 제품에도 자외선 차단 기능을 부여하기 위해 그래핀 양자점을 첨가할 수 있음을 확인할 수 있다.
도 6은 예시적인 실시예들에 따른 화장료 조성물의 발색을 비교하기 위한 사진들이다. 구체적으로 도 6은 실험예 2의 조성물 2, 조성물 3 및 조성물 4(표 2 참조)의 발색을 나타내는 사진들이다.
도 6을 참조하면, 에멀젼, OMC 및 이산화티탄만을 포함하는 조성물 2의 경우 백색을 나타내나, 그래핀 양자점이 추가되면서 피부색에 가까운 색상으로 변화함을 확인할 수 있다.
도 7은 예시적인 실시예들에 따른 화장료 조성물의 피부 발림성을 나타내는 사진들이다. 구체적으로, 도 7은 실험예 1의 조성물 8(표 1 참조)을 피부에 도포하는 과정을 나타내는 사진들이다.
도 7을 참조하면, 그래핀 양자점을 포함하는 예시적인 실시예들에 따른 자외선 차단제는 백탁 현상, 들뜸 현상 없이 실질적으로 피부색과 동일한 색상으로 도포됨을 확인할 수 있다.
도 8은 예시적인 실시예들에 따른 화장료 조성물의 피부 안정성을 나타내는 사진들이다. 구체적으로, 도 8은 실험예 2의 조성물 4(표 2 참조)을 피부에 적용시킨 후 24시간 이후에 촬영된 사진을 포함하고 있다.
도 8을 참조하면, 그래핀 양자점을 포함하는 예시적인 실시예들에 따른 자외선 차단제를 적용 후, 장시간이 지난 경우에도 두드러기, 피부 변색 등과 같은 부작용이 관찰되지 않았다.
전술한 예시적인 실시예들에 따른 화장료 조성물은 그래핀 양자점을 포함하며, 향상된 피부 친화도, 적용성을 가지며 자외선 차단 기능성을 보유할 수 있다. 상기 화장료 조성물은 자외선 차단제 뿐만 아니라 자외선 차단성이 부가된 스킨, 로션 등 다양한 화장료 제품으로 제공될 수 있다.
이상에서는 본 발명의 실시예들을 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.

Claims (11)

  1. 그래핀 양자점(Graphene Quantum Dots: GQD)을 포함하며 자외선 차단 기능을 갖는 화장료 조성물.
  2. 제1항에 있어서, 상기 조성물은 상기 그래핀 양자점, 무기 자외선 산란제, 유기 자외선 흡수제 및 에멀젼을 포함하는 화장료 조성물.
  3. 제2항에 있어서, 상기 조성물은 총 중량 대비 0.5 중량% 내지 5 중량%의 상기 그래핀 양자점, 5 중량% 내지 10 중량%의 상기 무기 자외선 산란제, 3 내지 7.5 중량%의 상기 유기 자외선 흡수제, 및 78 중량% 내지 91 중량%의 상기 에멀젼을 포함하는 화장료 조성물.
  4. 제2항에 있어서, 상기 무기 자외선 산란제는 금홍석(rutile) 이산화티탄을 포함하는 화장료 조성물.
  5. 제2항에 있어서, 상기 유기 자외선 흡수제는 에틸헥실 메톡시신나메이트, 에틸헥실살리실레이트, 4-메틸벤질리덴캠퍼, 이소아밀 p-메톡시신나메이트, 옥토크릴렌, 페닐벤즈이미다졸설포닉산, 호모살레이트, 시녹세이트, 에틸헥실트리아존, 폴리실리콘-15, 티이에이-살리실레이트, 팝바(PABA), 에틸헥실디메틸파바 및 글리세릴파바로 구성된 그룹에서 선택된 적어도 하나를 포함하는 화장료 조성물.
  6. 그래핀 양자점 분말을 준비하는 단계;
    상기 그래핀 양자점 분말 및 무기 자외선 산란제의 혼합물을 제조하는 단계;
    상기 혼합물을 열처리하여 복합 안료를 형성하는 단계; 및
    상기 복합 안료에 유기 자외선 흡수제 및 에멀젼을 혼합하는 단계를 포함하는 자외선 차단제의 제조 방법
  7. 제6항에 있어서, 상기 그래핀 양자점 분말을 준비하는 단계는 금속 이온이 그래파이트 층에 삽입된 그래파이트 층간 화합물로부터 금속 이온을 제거하여 그래핀 양자점 수분산체를 제조하는 단계를 포함하는 자외선 차단제의 제조 방법.
  8. 제7항에 있어서, 상기 그래핀 양자점 분말을 준비하는 단계는 상기 그래핀 양자점 수분산체를 100℃ 내지 130℃의 온도에서 건조시키는 단계를 더 포함하는 자외선 차단제의 제조 방법.
  9. 제6항에 있어서, 상기 혼합물을 열처리하는 단계는 100℃ 내지 200℃의 온도에서 수행되는 자외선 차단제의 제조 방법.
  10. 제6항에 있어서, 상기 무기 자외선 산란제 및 상기 유기 자외선 흡수제로서 각각 금홍석 이산화티탄 및 에틸헥실 메톡시신나메이트를 사용하는 자외선 차단제의 제조 방법.
  11. 제6항에 있어서, 상기 자외선 차단제의 총 중량 대비 0.5 중량% 내지 5 중량%의 상기 그래핀 양자점 분말, 5 중량% 내지 10 중량%의 상기 무기 자외선 산란제, 3 내지 7.5 중량%의 상기 유기 자외선 흡수제, 및 78 중량% 내지 91 중량%의 상기 에멀젼이 조합되는 자외선 차단제의 제조 방법.
PCT/KR2015/013715 2015-06-12 2015-12-15 자외선 차단 기능이 부여된 화장료 조성물 및 이의 제조 방법 Ceased WO2016199997A1 (ko)