WO2016171530A1 - 세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판 - Google Patents

세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판 Download PDF

Info

Publication number
WO2016171530A1
WO2016171530A1 PCT/KR2016/004305 KR2016004305W WO2016171530A1 WO 2016171530 A1 WO2016171530 A1 WO 2016171530A1 KR 2016004305 W KR2016004305 W KR 2016004305W WO 2016171530 A1 WO2016171530 A1 WO 2016171530A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
ceramic substrate
brazing
seed layer
metal foil
Prior art date
Application number
PCT/KR2016/004305
Other languages
English (en)
French (fr)
Inventor
단성백
황진수
Original Assignee
주식회사 아모센스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 아모센스 filed Critical 주식회사 아모센스
Priority to US15/568,780 priority Critical patent/US10529646B2/en
Priority to CN201680032519.5A priority patent/CN107889559B/zh
Publication of WO2016171530A1 publication Critical patent/WO2016171530A1/ko

Abstract

본 발명은 세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판에 관한 것으로, 세라믹 기재 상에 시드층, 브레이징 필러층, 금속박을 적층하여 브레이징하여 상기 세라믹 기재에 상기 금속박을 브레이징 접합층을 통해 견고히 접합하는 것으로 금속박과 세라믹 기재의 접합력을 크게 향상시킨 것이다.

Description

세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판
본 발명은 세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판에 관한 것으로 보다 구체적으로는 브레이징 접합을 이용하여 금속박을 세라믹 기재 상에 견고하게 부착하는 세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판에 관한 것이다.
일반적으로 세라믹 기재의 일 예로, 세라믹 기재에 동박과 같은 금속박을 일체로 부착시킨 세라믹 DBC 기판이 많이 이용되고 있으며, 상기 세라믹 DBC 기판은 반도체 전력 모듈 등에서 사용되는 것으로서 리드를 기존의 방열소재 위에 배치하는 경우 보다 높은 방열 특성을 가질 뿐만 아니라, 방열판의 접착상태에 대한 검사 공정을 필요로 하지 않기 때문에 신뢰성이 향상되고 생산성과 일관성이 향상된 반도체 전력 모듈 등을 제공할 수 있다는 장점을 가진 기판이다.
상기 세라믹 DBC 기판은 전기 자동차의 증가와 함께 자동차의 전력 반도체 모듈로 사용 범위가 점차 확산되고 있다.
상기 세라믹 DBC 기판은 세라믹 기재와 구리 동박을 고온의 소성 공정을 통한 계면 결합으로 제조되고 있다.
일 예로, 세라믹 DBC 기판은 알루미나(Al2O3) 세라믹 기재와 CuO 산화막이 형성된 구리동박을 1000℃ ~ 1100℃로 소성하여 알루미나(Al2O3) 세라믹 기재와 CuO 산화막을 계면 결합하여 제조되고 있다.
다른 예로, 세라믹 DBC 기판은 AlN 세라믹 기재의 표면에 Al2O3층을 고온 산화로 형성한 후 AlN 세라믹 기재의 표면에 구리동박을 적층한 후 1000℃ ~ 1100℃로 소성하여 알루미나(Al2O3) 세라믹 기판과 CuO 산화막을 계면 결합하여 제조되고 있다.
종래의 세라믹 DBC 기판은 제조 시 세라믹 기재와 구리동박을 계면 결합하기 위해 고온의 소성 공정이 요구되고, 고온의 소성 공정 시 Cu 산화 방지를 위해 환원 분위기를 유지해야 한다.
즉, 종래 세라믹 DBC 기판을 제조하기 위해서는 소성 중 환원분위기 조성이 가능한 소성 장치를 준비해야 하므로 소성 장치를 준비하는 비용이 많이 소요되고 이로써 제조비용이 많이 소요되는 문제점이 있었다.
또한, 종래 세라믹 DBC 기판은, 1000℃ ~ 1100℃로 소성하여 세라믹 기재와 구리동박을 계면 결합하므로 소성을 위한 고온 가열에 따른 제조비용이 많이 소요되며, 제조 시간이 오래 소요되어 생산성이 낮은 문제점이 있었다.
또한, 종래 세라믹 DBC 기판은, 계면 결합을 위해 구리동박에 CuO 산화막을 형성하거나, AlN 세라믹 기재의 표면에 Al2O3층을 고온 산화로 형성한 후 소성 과정을 거치게 되므로 제조 과정이 복잡한 문제점이 있었다.
또한, 종래 세라믹 DBC 기판은, 구리동박과 세라믹 기재 간의 부착력 문제로 인해 사용 중 오작동이 발생되어 작동 신뢰성이 저하되는 문제점이 있고, 특히 전력 반도체 모듈로 사용 시 발열과 냉각 등에 의한 열충격 발생 시 구리동박과 세라믹 기재 간의 부착력 문제가 발생될 위험이 높은 것이다.
본 발명은 상기와 같은 점을 감안하여 안출한 것으로, 브레이징 접합 공정을 통해 금속박을 일체화시킴으로써 금속박의 접합 강도를 크게 향상시키는 세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판을 제공하는 데 그 목적이 있다.
또한, 본 발명은 상기와 같은 점을 감안하여 안출한 것으로, 본 발명은 브레이징용 페이스트를 인쇄하여 퍼짐성과 균일성을 고려한 브레이징 필러층을 간단하게 형성하여 브레이징접합할 수 있어 금속박의 접합 강도를 크게 향상시키고, 브레이징 접합층의 품질을 향상시키는 세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판을 제공하는 데 그 목적이 있다.
또한, 본 발명은 상기와 같은 점을 감안하여 안출한 것으로, 본 발명은 도금으로 브레이징 필러층을 형성하여 브레이징 접합층의 두께를 원하는 두께로 세밀하게 조절할 수 있는 세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판을 제공하는 데 그 목적이 있다.
상기 목적을 달성하기 위한 본 발명의 일 실시예에 의한 세라믹 기판 제조방법은, 세라믹 기재와 금속박을 준비하는 단계, 상기 세라믹 기재 상에 시드층을 형성하는 단계, 상기 시드층 상에 브레이징 필러층을 형성하는 단계 및 상기 브레이징 필러층 상에 금속박을 적층하고 브레이징하는 단계를 포함하는 것을 특징으로 한다.
본 발명에서 상기 세라믹 기재와 금속박을 준비하는 단계는 약품을 이용한 화학적 처리 또는 물리적 처리로 상기 세라믹 기재의 표면을 거칠게 하는 표면 개질 과정을 포함할 수 있다.
본 발명에서 금속박을 준비하는 단계는 절단하거나 타발되어 회로패턴 형상으로 형성된 금속박을 준비할 수 있다.
본 발명에서 상기 브레이징 필러층을 형성하는 단계는 브레이징 시트를 적층하거나 페이스트 형태의 브레이징 필러를 인쇄하여 브레이징 필러층을 형성할 수 있다.
본 발명에서 상기 브레이징 필러층을 형성하는 단계는 상기 브레이징 필러층을 형성하는 과정은, 도금으로 브레이징 필러 도금층을 형성할 수 있다.
본 발명에서 상기 브레이징 필러층을 형성하는 과정은, 도금으로 브레이징 필러 도금층을 0초과 10㎛ 이하의 두께를 가지도록 형성할 수 있다.
본 발명에서 상기 브레이징 필러층은 제1Ag층, 상기 제1Ag층 상에 적층되는 Al층, Ni층, Sn층, In층 중 어느 하나, 상기 Cu층 상에 적층되는 제2Ag층을 포함하거나, Al층, Ni층, Sn층, In층 중 어느 하나의 제1층, 상기 제1층 상에 적층되는 Ag층, 상기 Ag층 상에 적층되는 Al층, Ni층, Sn층, In층 중 어느 하나의 제2층을 포함할 수 있다.
본 발명에서 상기 시드층을 형성하는 단계는, 상기 세라믹 기재 상에 세라믹 기재와의 결합력을 확보하는 제1시드층을 형성하는 과정 및 상기 제1시드층 상에 브레이징 필러층와의 결합력을 확보하는 제2시드층을 형성하는 과정을 포함할 수 있다.
본 발명에서 상기 시드층을 형성하는 단계는, 물리증착 방법으로 상기 시드층을 형성할 수 있다.
본 발명에서 상기 제1시드층은 Ti, Hf, Zr 중 어느 하나로 증착되고, 상기 제2시드층은 Cu, Ag Al, Ni, Sn, In 중 어느 하나의 재료로 증착될 수 있다.
본 발명에서 상기 시드층을 형성하는 단계에서 상기 시드층을 합금으로 단층형 합금시드층으로 형성할 수 있다.
본 발명에서 상기 시드층을 형성하는 단계는 TiCu, NiTi, TiCu, NiNb, CuMo, TiAg 중 어느 하나의 합금으로 상기 세라믹 기재 상에 단층형 합금시드층을 형성할 수 있다.
본 발명에서 상기 브레이징 필러층은, 복수의 구멍이 형성된 형태를 가질 수 있다.
본 발명의 일 실시예에 의한 세라믹 기판은, 세라믹 기재, 상기 세라믹 기재 상에 형성된 시드층, 상기 시드층 상에 형성된 브레이징 접합층 및 상기 브레이징 접합층에 의해 상기 시드층 상에 브레이징 접합된 금속박을 포함하는 것을 특징으로 한다.
본 발명에서 상기 세라믹 기재의 표면에는 미세 돌기부가 형성될 수 있다.
본 발명에서 상기 시드층은, 상기 세라믹 기재와의 결합력을 가지며 증착으로 형성된 제1시드층; 및 상기 브레이징층과의 결합력을 가지는 증착으로 형성된 제2시드층을 포함할 수 있다.
본 발명에서 상기 제1시드층은 Ti, Hf, Zr 중 어느 하나이고, 상기 제2시드층은 Cu, Ag Al, Ni, Sn, In 중 어느 하나일 수 있다.
본 발명에서 상기 시드층은 적어도 두개의 금속이 혼합된 합금으로 형성되는 단층형 합금시드층일 수 있다.
본 발명에서 상기 단층형 합금시드층은 TiCu, NiTi, TiCu, NiNb, CuMo, TiAg 중 어느 하나일 수 있다.
본 발명에서 상기 브레이징 접합층은 Ag와 Al, Ni, Sn, In 중 적어도 어느 하나를 혼합한 합금층일 수 있다.
본 발명에서 상기 브레이징층과 상기 시드층은 회로패턴의 형상과 대응되게 형성되되 상기 금속박 패턴의 측면으로 일부 돌출되게 형성될 수 있다.
본 발명은 기존에 소성공정에 의한 계면 결합 대신에 브레이징 접합을 통해 금속박과 세라믹 기재를 일체화시키는 구성으로 금속박과 세라믹 기재의 접합력을 크게 향상시키는 효과가 있다.
본 발명은 고온 또는 진공 소성 장치가 필요 없고, 고온 또는 진공의 소성공정을 거치지 않고 제조가 가능하므로 제조비용을 크게 절감할 수 있는 효과가 있다.
본 발명은 브레이징용 페이스트를 인쇄하여 퍼짐성과 균일성을 고려한 형상으로 브레이징 필러층을 간단하게 형성할 수 있어 브레이징 접합공정의 품질을 향상시키고, 브레이징 접합공정을 단순화하는 효과가 있다.
본 발명은 본 발명은 도금으로 브레이징 필러 도금층을 형성하여 브레이징 접합층의 두께를 원하는 두께로 세밀하게 조절할 수 있어 세라믹 기판을 설계된 두께로 정확하게 제조할 수 있어 세라믹 기판의 품질을 향상시키고, 생산시 불량률을 크게 절감하는 효과가 있다.
특히, 본 발명은 도금을 통해 브레이징 필러의 두께를 10㎛ 이하로 형성하여 세라믹 기판의 두께를 슬림하게 하고, 금속박과 세라믹 기재와의 간격을 최소화하여 방열 효과를 극대화하는 효과가 있다.
본 발명은 브레이징 접합 후 에칭과정을 단순화하여 전체 제조공정을 단순화하고, 생산성을 향상시키는 효과가 있다.
도 1은 본 발명에 따른 세라믹 기판 제조 방법의 일 실시예를 도시한 공정도
도 2는 본 발명에 따른 세라믹 기판 제조 방법의 일 실시예를 도시한 개략도
도 3은 본 발명에 따른 세라믹 기판 제조 방법에서 상기 금속박 에칭과정과 상기 브레이징 접합층 에칭과정의 일 실시예를 도시한 공정도
도 4는 본 발명에 따른 세라믹 기판 제조 방법에서 상기 금속박 에칭과정과 상기 브레이징 접합층 에칭과정의 일 실시예를 도시한 개략도.
도 5는 본 발명에 따른 세라믹 기판 제조 방법의 다른 실시예를 도시한 공정도
도 6은 본 발명에 따른 세라믹 기판 제조 방법의 다른 실시예를 도시한 개략도
도 7 및 도 8은 본 발명에 따른 세라믹 기판 제조 방법의 또 다른 실시예를 도시한 개략도
도 9는 본 발명에 따른 세라믹 기판 제조 방법의 또 다른 실시예를 도시한 개략도
도 10은 본 발명에 따른 세라믹 기판의 일 실시예를 도시한 단면도
도 11은 본 발명에 따른 세라믹 기판의 다른 실시예를 도시한 단면도
도 12 및 도 13은 본 발명에 따른 세라믹 기판의 또 다른 실시예를 도시한 단면도
도 14 및 도 15는 본 발명에 따른 세라믹 기판을 주사전자현미경으로 확대하여 찍은 사진
본 발명을 첨부된 도면을 참조하여 상세히 설명하면 다음과 같다. 여기서, 반복되는 설명, 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능, 및 구성에 대한 상세한 설명은 생략한다. 본 발명의 실시형태는 당 업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해서 제공되는 것이다. 따라서, 도면에서의 요소들의 형상 및 크기 등은 보다 명확한 설명을 위해 과장될 수 있다.
도 1 및 도 2를 참고하면, 본 발명의 일 실시예에 의한 세라믹 기판 제조방법은, 세라믹 기재(10)와 금속박(40)을 준비하는 단계(S100), 상기 세라믹 기재(10) 상에 시드층(20)을 형성하는 단계(S200), 상기 시드층(20) 상에 브레이징 필러층(31)을 형성하는 단계(S300), 상기 브레이징 필러층(31) 상에 금속박(40)을 적층하고 브레이징하는 단계(S400)를 포함한다.
상기 세라믹 기재(10)와 금속박(40)을 준비하는 단계(S100)는 상기 세라믹 기재(10)의 표면을 거칠게 하는 표면 개질 과정을 포함하여 시드층(20)과 세라믹 기재(10)간의 접합력을 더 견고하게 하는 것이 바람직하다.
상기 표면 개질 과정은 약품을 이용한 화학적 처리 또는 연마, 샌드 블라스트 등을 이용한 물리적 처리로 상기 세라믹 기재(10)의 표면을 거칠게 하여 미세돌기부를 형성하는 것을 일 예로 하며, 이외에도 상기 세라믹 기재(10)의 표면을 거칠게 하는 어떠한 예로도 변형실시될 수 있음을 밝혀둔다.
상기 시드층(20)을 형성하는 단계(S200)는, 상기 세라믹 기재(10) 상에 세라믹 기재(10)와의 결합력을 확보하는 제1시드층(21)을 형성하는 과정(S210); 및
상기 제1시드층(21) 상에 브레이징 필러층(31)과의 결합력을 확보하는 제2시드층(22)을 형성하는 과정(S220)을 포함하는 것이 바람직하다.
상기 시드층(20)을 형성하는 단계(S200)는, 물리 증착법으로 상기 시드층(20)을 형성하고, 상기 물리 증착법은 진공증착, 열증착(Evaporation), 이빔(ebeam)증착, 레이저(laser) 증착, 스퍼터링(Sputtering), 아크이온플레이팅(Arc Ion Plating) 중 어느 하나인 것을 일 예로 한다.
즉, 상기 제1시드층(21)을 형성하는 과정(S210)은, Ti, Hf, Zr 등과 같이 상기 세라믹 기재(10)와의 결합력이 우수한 재료를 타겟재료로 하여 상기 세라믹 기재(10) 상에 증착하여 제1시드층(21)을 형성하는 것이다.
상기 제1시드층(21)은 Ti, Hf, Zr 중 어느 하나로 증착되는 것이 바람직하며 상기 Ti, Hf, Zr은 활성 금속(Active Metal)으로 산소, 질소와 반응성 높아 산화물, 질화물로 되는 성질이 있다.
상기 세라믹 기재(10)는 산화질소를 포함하고 있어 Ti의 예를 들면 Ti를 증착시키면 TiO가 계면에 형성되면서 계면 결합력이 높은 화학 결합이 발생하는 것이다.
또한, 상기 제2시드층(22)을 형성하는 과정(S220)은, Cu 또는 Ag 등과 같이 Cu 계열 브레이징 필러층(31) 또는 Ag 계열 브레이징 필러층(31) 등의 브레이징 필러층(31)과 결합력이 우수한 재료를 타겟재료로 하여 상기 제1시드층(21) 상에 증착하는 것을 일 예로 한다.
상기 브레이징 필러층(31)은 Ag와 Cu가 혼합된 합금 브레이징 시트일 수도 있고, Ag층과 Cu층이 적층된 적층 구조의 브레이징 시트일 수도 있다.
상기 적층 구조의 브레이징 시트의 일 예로 제1Ag층, 상기 제1Ag층 상에 적층되는 Cu층, 상기 Cu층 상에 적층되는 제2Ag층을 포함할 수 있고, 상기 적층 구조의 브레이징 시트의 다른 예로 제1Cu층, 상기 제1Cu층 상에 적층되는 Ag층, 상기 Ag층 상에 적층되는 제2Cu층을 포함할 수 있다.
또한, 상기 브레이징 필러층(31)에서 상기 Cu층 대신 Al층, Ni층, Sn층, In층 중 어느 하나를 사용할 수 있다.
즉, 상기 브레이징 시트는 제1Ag층, 상기 제1Ag층 상에 적층되는Al층, Ni층, Sn층, In층 중 어느 하나, 상기 Cu층 상에 적층되는 제2Ag층을 포함할 수 있다. 또한, Al층, Ni층, Sn층, In층 중 어느 하나의 제1층, 상기 제1층 상에 적층되는 Ag층, 상기 Ag층 상에 적층되는 Al층, Ni층, Sn층, In층 중 어느 하나의 제2층을 포함할 수 있다.
이 경우 상기 제2시드층(22)을 형성하는 과정(S220)은, Al, Ni, Sn, In 중 어느 하나의 재료로 증착시켜 제2시드층(22)을 형성할 수도 있다.
이는 상기 브레이징 필러층(31)의 재료에 따라 결정될 수 있음을 밝혀둔다.
상기 브레이징 시트에 Al층, Ni층, Sn층, In층 중 어느 하나의 층을 사용함으로써 공정온도를 조정하고, 해당 공정온도에 따라 브레이징 필러층을 다양하게 설계하여 사용할 수 있음을 밝혀둔다.
상기 브레이징 필러층(31)을 형성하는 단계는 브레이징 시트를 상기 시드층(20) 상에 적층시키는 것일 수 있다.
더 상세하게 상기 브레이징 필러층(31)은 브레이징 시트를 복수의 조각으로 구분한 것일 수도 있고, 복수의 구멍이 형성된 브레이징 시트로 상기 시드층(20) 상에서 구멍을 제외한 부분만 덮도록 즉, 구멍에 의한 복수의 빈공간이 이격되게 형성되는 형태를 가지도록 형성되는 것을 일 예로 한다.
이는 상기 브레이징하는 단계(S400)에서 상기 브레이징 필러층(31)의 퍼짐성을 확보함과 동시에 상기 브레이징 필러층(31)이 용융되어 상기 시드층(20)과 상기 금속박(40) 사이에서 접합면의 전면에 균일하고 고르게 퍼질 수 있도록 한다.
또한, 상기 브레이징하는 단계(S400)에서 상기 브레이징 필러층(31)이 용융되면서 가압됨으로써 상기 세라믹 기재(10)와 상기 금속박(40)의 측면으로 유출되는 것을 방지한다.
상기 브레이징 시트의 구멍은 원형일 수도 있고, 사각 형상일 수도 있으며 상기 세라믹 기재(10)의 크기 및 형상, 상기 브레이징 시트의 종류, 설계된 브레이징 접합층(30)의 두께 등에 따라 다양하게 변형 실시될 수 있음을 밝혀둔다.
또한, 상기 브레이징 필러층(31)을 형성하는 단계는 상기 시드층(20) 상에 페이스트 형태의 브레이징용 페이스트를 인쇄하여 브레이징 필러층(31)을 형성할 수도 있다.
상기 브레이징 필러층(31)을 형성하는 단계는 Ag페이스트를 인쇄하여 제1Ag층을 형성하는 과정, 상기 제1Ag층 상에 Cu페이스트를 인쇄하여 Cu층을 형성하는 과정, 상기 Cu층 상에 Ag페이스트를 인쇄하여 제2Ag층을 형성하는 과정을 포함할 수 있다.
또는 상기 브레이징 필러층(31)을 형성하는 단계는 Cu페이스트를 인쇄하여 제1Cu층을 형성하는 과정, 상기 제1Cu층 상에 Ag페이스트를 인쇄하여 Ag층을 형성하는 과정, 상기 Cu층 상에 Cu페이스트를 인쇄하여 제2Cu층을 형성하는 과정을 포함할 수도 있다.
또한, 상기 브레이징용 페이스트에서 상기 Cu페이스트 대신 Al페이스트, Ni페이스트, Sn페이스트, In페이스트 중 어느 하나를 사용할 수 있다.
즉, 브레이징용 페이스트를 인쇄하여 적층 형성되는 상기 브레이징 필러층(31)은 제1Ag층, 상기 제1Ag층 상에 적층되는Al층, Ni층, Sn층, In층 중 어느 하나, 상기 Cu층 상에 적층되는 제2Ag층을 포함할 수 있다. 또한, 상기 브레이징 필러층(31)은 Al층, Ni층, Sn층, In층 중 어느 하나의 제1층, 상기 제1층 상에 적층되는 Ag층, 상기 Ag층 상에 적층되는 Al층, Ni층, Sn층, In층 중 어느 하나의 제2층을 포함할 수 있다. 이 경우 상기 제2시드층(22)을 형성하는 과정(S220)은, Al, Ni, Sn, In 중 어느 하나의 재료로 증착시켜 제2시드층(22)을 형성할 수도 있다.
이는 상기 브레이징용 페이스트의 재료에 따라 결정될 수 있음을 밝혀둔다.
상기 상기 브레이징 필러층(31)에 Al층, Ni층, Sn층, In층 중 어느 하나의 층을 사용함으로써 공정온도를 조정하고, 해당 공정온도에 따라 브레이징 필러층(31)을 다양하게 설계하여 사용할 수 있음을 밝혀둔다.
상기 브레이징용 페이스트는 브레이징용 금속분말과 솔벤트를 포함한 페이스트 형태로 형성된 것이며, 바인더 등을 더 포함할 수 있고 450℃ 이상의 온도에서 용융되는 금속분말 중 다양하게 변형실시 가능함을 밝혀둔다.
상기 브레이징 필러층(31)을 형성하는 단계는 상기 브레이징용 페이스트를 스크린 인쇄하여 상기 시드층(20)을 노출시키는 복수의 구멍이 형성이 되도록 상기 브레이징 필러층(31)을 형성하는 즉, 상기 브레이징 필러층(31)이 상기 시드층(20) 상에서 구멍을 제외한 부분만 덮도록 즉, 구멍에 의한 복수의 빈공간이 이격된 형태로 형성되는 것을 일 예로 한다.
이는 상기 브레이징하는 단계(S400)에서 상기 브레이징용 페이스트의 퍼짐성을 확보함과 동시에 상기 브레이징 필러층(31)이 용융되어 상기 시드층(20)과 상기 금속박(40) 사이에서 접합면의 전면에 균일하고 고르게 퍼질 수 있도록 한다.
또한, 상기 브레이징하는 단계(S400)에서 상기 브레이징 필러층(31)이 용융되면서 가압됨으로써 상기 세라믹 기재(10)와 상기 금속박(40)의 측면으로 유출되는 것을 방지한다.
즉, 상기 브레이징 필러층(31)을 형성하는 단계는 상기 시드층(20)을 노출시키는 복수의 구멍이 형성이 되는 브레이징 필러층을 브레이징용 페이스트를 인쇄하여 원하는 형태 즉, 최적의 퍼짐성과 균일성을 고려한 형태로 간단하게 형성할 수 있다.
또한, 상기 브레이징 필러층(31)을 형성하는 단계는, 상기 시드층(20) 상에 브레이징 필러층을 도금하여 형성할 수도 있다.
상기 브레이징 필러층(31)을 형성하는 단계는, Ag를 도금하여 제1Ag층을 형성하는 과정, 상기 제1Ag층 상에 Cu도금하여 Cu층을 형성하는 과정, 상기 Cu층 상에 Ag를 도금하여 제2Ag층을 형성하는 과정을 포함할 수 있다.
또는 상기 브레이징 필러층(31)을 형성하는 단계는 Cu 도금하여 제1Cu층을 형성하는 과정, 상기 제1Cu층 상에 Ag를 도금하여 Ag층을 형성하는 과정, 상기 Cu층 상에 Cu를 도금하여 제2Cu층을 형성하는 과정을 포함할 수도 있다.
또한, 상기 브레이징 필러층(31)을 형성하는 단계에서 상기 Cu대신 Al, Ni, Sn, In 중 어느 하나를 사용할 수 있다.
즉, 도금으로 형성되는 상기 브레이징 필러층(31)은 제1Ag층, 상기 제1Ag층 상에 적층되는Al층, Ni층, Sn층, In층 중 어느 하나, 상기 Cu층 상에 적층되는 제2Ag층을 포함할 수 있다. 또한, 상기 브레이징 필러층(31)은 Al층, Ni층, Sn층, In층 중 어느 하나의 제1층, 상기 제1층 상에 적층되는 Ag층, 상기 Ag층 상에 적층되는 Al층, Ni층, Sn층, In층 중 어느 하나의 제2층을 포함할 수 있다. 이 경우 상기 제2시드층(22)을 형성하는 과정(S220)은, Al, Ni, Sn, In 중 어느 하나의 재료로 증착시켜 제2시드층(22)을 형성할 수도 있다.
이는 상기 브레이징용 페이스트의 재료에 따라 결정될 수 있음을 밝혀둔다.
상기 브레이징 필러층(31)에 Al층, Ni층, Sn층, In층 중 어느 하나의 층을 사용함으로써 공정온도를 조정하고, 해당 공정온도에 따라 브레이징 필러층(31)을 다양하게 설계하여 사용할 수 있음을 밝혀둔다.
상기 브레이징 필러층(31)을 형성하는 단계는 도금을 통해 원하는 두께로 상기 브레이징 필러층(31)을 제조할 수 있다.
상기 브레이징 필러층(31)을 형성하는 단계는 도금으로 0초과 10㎛ 이하의 두께로 브레이징 필러층(31)을 형성할 수 있다.
즉, 상기 브레이징 필러층(31)을 형성하는 단계는 도금을 통해 브레이징 필러층(31)을 10㎛ 이하의 얇은 두께로 형성할 수 있고, 이는 브레이징 시트 또는 페이스트 형태의 브레이징 필러를 인쇄하여 형성되는 브레이징층에서 구현할 수 없는 두께이다.
상기 브레이징 필러층(31)은, 도금 공정으로 0초과 10㎛ 이하의 두께로 형성되어 추후 브레이징 공정 후 상기 금속박과 상기 세라믹 기재(10) 사이에 배치되는 브레이징층(30)의 두께를 최소화하여 세라믹 기판의 전체 두께를 슬림하게 하고, 상기 금속박으로 형성되는 회로패턴에서 발생되는 열을 상기 세라믹 기재로 원활하게 전달하여 방출될 수 있도록 한다.
상기 브레이징 필러층(31)을 형성하는 단계는 절연마스킹을 통해 상기 시드층(20)을 노출시키는 복수의 구멍을 가지는 상기 브레이징 필러층(31)을 형성하는 것이 바람직하다. 상기 브레이징 필러층(31)은 상기 시드층(20) 상에서 구멍을 제외한 부분만 덮도록 즉, 구멍에 의한 복수의 빈공간이 이격되게 형성되는 형태로 형성되는 것을 일 예로 한다.
이는 상기 브레이징하는 단계(S400)에서 상기 브레이징용 페이스트의 퍼짐성을 확보함과 동시에 상기 브레이징 필러층(31)이 용융되어 상기 시드층(20)과 상기 금속박(40) 사이에서 접합면의 전면에 균일하고 고르게 퍼질 수 있도록 한다.
또한, 상기 브레이징하는 단계(S400)에서 상기 브레이징 필러층(31)이 용융되면서 가압됨으로써 상기 세라믹 기재(10)와 상기 금속박(40)의 측면으로 유출되는 것을 방지한다.
상기 브레이징 필러층(31)의 구멍은 원형일 수도 있고, 사각 형상일 수도 있으며 상기 세라믹 기재(10)의 크기 및 형상, 상기 브레이징 필러층(31)의 종류, 설계된 브레이징 접합층(30)의 두께 등에 따라 다양하게 변형 실시될 수 있음을 밝혀둔다.
한편, 상기 브레이징하는 단계(S400)는, 상기 세라믹 기재(10) 상에 상기 브레이징 필러층(31)과 상기 금속박(40)이 적층된 상태에서 브레이징을 통해 접합시킨다. 즉, 상기 브레이징하는 단계(S400)는, 상기 금속박(40)과 상기 제2시드층(22)의 사이에 상기 브레이징 필러층(31)이 개재된 상태에서 상기 브레이징 필러층(31)을 용융시켜 형성되는 브레이징층(30)을 통해 상기 금속박(40)을 상기 제2시드층(22) 상에 접합시킨다.
상기 브레이징하는 단계(S400)는, 브레이징 로(1) 내에서 상기 금속박(40)과 상기 세라믹 기재(10) 사이에서 상기 브레이징 필러층(31)을 800℃ ~ 900℃가열하는 중에 가압하는 것을 일 예로 한다.
즉, 상기 브레이징 로(1) 내에는 상기 세라믹 기재(10)가 올려지는 하부 가압지그부(2), 상기 하부 가압지그부(2)의 상부에서 상기 금속박(40)과 이격되게 위치하는 상부 가압지그부(3)를 포함하고, 상기 하부 가압지그부(2)와 상기 상부 가압지그부(3) 중 적어도 어느 하나를 상, 하 이동시켜 상기 브레이징 필러층(31)을 가열 중에 상기 금속박(40)과 상기 세라믹 기재(10) 사이에서 가압하는 것을 일 예로 한다.
상기 브레이징 필러층(31)은 브레이징 로(1) 내에서 가열되어 용융되며 상기 하부 가압지그부(2)와 상기 상부 가압지그부(3)의 사이에서 가압되어 상기 제2시드층(22)과 상기 금속박(40) 사이에 고르고 균일하게 퍼져 상기 금속박(40)을 접합하는 브레이징층(30)으로 형성된다.
또한, 상기 브레이징하는 단계(S400)는, 상기 세라믹 기재(10)를 브레이징 로(1)에서 인출하여 냉각시키는 과정을 포함하고, 상기 냉각하는 과정을 통해 최종적으로 상기 금속박(40)이 상기 세라믹 기재(10)에 접합되는 것이다.
상기 브레이징하는 단계(S400)는 상기 금속박(40)의 측면으로 상기 브레이징 필러층(31)이 일부 돌출되게 형성하는 것이 바람직하다. 이는 상기 브레이징 필러의 접촉면적을 넓혀 상기 금속박(40)의 접합력을 더 강화시킬 수 있다.
상기 브레이징하는 단계(S400)는, 상기 브레이징 필러층(31) 상에 금속박(40)을 적층한 후 브레이징 로(1) 내에서 가열하여 상기 브레이징 필러층(31)을 용융시켜 형성되는 브레이징 접합층(30)을 통해 상기 금속박(40)을 상기 시드층(20)과 접합시키는 것이다.
상기 브레이징하는 단계(S400)는, 브레이징 로(1) 내에서 상기 금속박(40)과 상기 세라믹 기재(10) 사이에서 상기 브레이징 필러층(31)을 800℃ ~ 900℃가열하는 중에 가압하는 것을 일 예로 한다.
즉, 상기 브레이징 로(1) 내에는 상기 세라믹 기재(10)가 올려지는 하부 가압지그부(2), 상기 하부 가압지그부(2)의 상부에서 상기 금속박(40)과 이격되게 위치하는 상부 가압지그부(3)를 포함하고, 상기 하부 가압지그부(2)와 상기 상부 가압지그부(3) 중 적어도 어느 하나를 상, 하 이동시켜 상기 브레이징 필러층(31)을 가열 중에 상기 금속박(40)과 상기 세라믹 기재(10) 사이에서 가압하는 것을 일 예로 한다.
상기 브레이징 필러층(31)은 브레이징 로(1) 내에서 가열되어 용융되며 복수의 빈공간을 포함하므로 상기 하부 가압지그부(2)와 상기 상부 가압지그부(3)의 사이에서 가압될 때 상기 세라믹 기재(10)와 상기 금속박(40)의 외측둘레로 유출되지 않고 상기 시드층(20) 상의 전면과 상기 금속박(40)의 전면 사이에 고르고 균일하게 퍼지게 되어 상기 금속박(40)을 상기 제2시드층(22) 상에 견고하게 접합시킬 수 있다.
또한, 상기 브레이징하는 단계(S400)는, 상기 세라믹 기재(10)를 브레이징 로(1)에서 인출하여 냉각시키는 과정을 포함하고, 상기 냉각하는 과정을 통해 최종적으로 상기 금속박(40)이 상기 세라믹 기재(10)에 접합되는 것이다.
본 발명에 따른 세라믹 기판 제조방법의 일 실시예는 상기 금속박(40), 상기 브레이징 접합층(30), 상기 시드층(20)을 에칭하여 회로패턴(50)을 형성하는 에칭단계(S500)를 더 포함할 수 있다.
상기 에칭단계(S500)는 상기 금속박(40)과 상기 브레이징 접합층(30)을 한종류의 에칭액으로 한번에 에칭하는 금속박(40) 및 브레이징 접합층 에칭과정(S510), 상기 시드층(20)을 에칭하는 시드층 에칭과정(S520)을 포함할 수 있다.
상기 금속박(40) 및 브레이징 접합층 에칭과정(S510)은 한 종류의 에칭액으로 한번의 에칭공정으로 수행되며 상기 금속박(40)과 상기 브레이징 접합층(30)을 회로패턴(50)의 형상에 대응되게 에칭하되 상기 브레이징 접합층(30)을 상기 금속박(40)의 측면으로 돌출되게 에칭한다.
상기 브레이징 접합층(30)을 상기 금속박(40)의 측면으로 돌출되게 에칭하는 것은 금속박(40)의 접합강도를 더 향상시키기 위함임을 밝혀둔다.
상기 시드층 에칭과정(S520)은 에칭된 상기 브레이징 접합층(30)을 장벽으로 하여 시드층(20)을 에칭하는 것으로 제2시드층(22)을 에칭하는 과정(S521), 제1시드층(21)을 에칭하는 과정(S522)으로 구분될 수 있다.
상기 금속박 및 브레이징 접합층 에칭과정(S510)은 상기 금속박(40)을 회로패턴(50)의 형상과 대응되게 마스킹한 후 금속박용 에칭액을 이용하여 회로패턴(50)의 형상으로 정확하게 에칭하면서 상기 브레이징 접합층(30)을 동시에 에칭하는 것으로 도 3 및 도 4를 참고하여 더 상세하게 설명하면 하기와 같다.
상기 금속박 및 브레이징 접합층 에칭과정(S510)은 상기 금속박(40) 상에 포토레지스트층(1)을 적층하는 과정(S511), 상기 포토레지스트층(1) 상에 회로패턴(50)에 대응되는 패턴홀(2a)이 형성된 마스크(2)를 적층하고 노광하는 과정(S512), 마스크를 제거하고 노광되어 경화된 부분만 남기고 나머지 포토레지스트층(1)을 제거하는 과정(S513), 상기 금속박(40) 상에 잔류된 포토레지스트층(1a)을 장벽으로 하여 에칭하는 과정(S514), 상기 에칭하는 과정(S514) 후 금속박(40) 상에 잔류된 포토레지스트층(1a)을 제거하는 과정(S515)을 포함한다.
한편, 도 5는 본 발명에 따른 세라믹 기판 제조 방법의 다른 실시예를 도시한 공정도이고, 도 6은 본 발명에 따른 세라믹 기판 제조 방법의 다른 실시예를 도시한 개략도이다.
도 5 및 도 6을 참고하면 본 발명의 다른 실시예에 의한 세라믹 기판 제조방법은, 상기 시드층(20)을 형성하는 단계(S200)에서 상기 시드층(20)을 합금으로 단층형 합금시드층(23)으로 형성하는 것을 일 예로 하는 것이다.
더 상세하게 상기 시드층(20)을 형성하는 단계(S200)는 TiCu, NiTi, TiCu, NiNb, CuMo, TiAg 중 어느 하나의 합금으로 상기 세라믹 기재(10) 상에 단층형 합금시드층(23)을 형성하는 것을 일 예로 한다.
상기 TiCu, NiTi, TiCu, NiNb, CuMo, TiAg는 활성화 금속의 역할이 가능하며 하나의 에칭액으로 한번의 에칭공정으로 에칭될 수 있는 합금비로 제조된다.
상기 시드층(20)을 형성하는 단계(S200)는 단층형 합금시드층(23)을 형성하면서도 세라믹 기재(10)와의 접합력과 브레이징 접합층(30)과의 접합력을 동시에 만족시킬 수 있어 시드층을 형성하는 공정을 단순화한다.
또한, 상기 시드층 에칭과정(S520)에서 한번의 에칭과정으로 단층형 합금시드층(23)을 에칭시킬 수 있어 상기 에칭단계(S500)의 공정수를 크게 줄일 수 있는 것이다.
한편, 도 7 및 도 8을 참고하면 본 발명의 다른 실시예에 의한 세라믹 기판 제조방법은, 회로패턴 형상으로 가공한 금속박(40)을 준비하는 것을 일 예로 한다.
레이저, 커터로 절단하거나 타발하여 회로패턴 형상의 금속박(40)을 형성한다.
상기 금속박(40)은 지지시트(42)에 점착되며, 상기 금속박(40)을 준비하는 단계(S200)는, 상기 지지시트(42)를 하프커팅하는 범위로 상기 금속박(40)을 절단 또는 타발하여 상기 지지시트(42)는 완전히 절단되지 않고 형태를 유지하면서 상기 금속박(40)만 회로패턴 형상으로 절단 또는 타발된다.
상기 금속박(40)은 레이저, 커터로 절단되거나 타발되어 회로패턴 형상으로 형성된다.
상기 금속박(40)은 지지시트(42)에 점착되며, 상기 금속박(40)을 준비하는 단계(S200)는, 상기 지지시트(42)를 하프커팅하는 범위로 상기 금속박(40)을 절단 또는 타발하여 상기 지지시트(42)는 완전히 절단되지 않고 형태를 유지하면서 상기 금속박(40)만 회로패턴 형상으로 절단 또는 타발된다.
따라서, 상기 지지시트(42)에서 회로패턴인 금속박(40)을 제외한 나머지 부분은 용이하게 제거되며, 회로패턴인 금속박(40)만 상기 지지시트(42) 상에 남은 상태에서 상기 세라믹 기재(10) 상에 상기 금속박(40)을 정확한 위치로 용이하게 배치시킬 수 있는 것이다.
상기 브레이징 필러층(31)은 도 8을 참고하면 상기 금속박(40) 상에 형성될 수도 있음을 밝혀둔다.
상기 브레이징하는 단계(S300)는 상기 금속박(40)의 측면으로 상기 브레이징 필러층(31)이 일부 돌출되게 형성하는 것이 바람직하다. 이는 상기 브레이징 필러의 접촉면적을 넓혀 상기 금속박(40)의 접합력을 더 강화시킬 수 있다.
또한, 에칭하는 단계(S500)는 상기 금속박 및 브레이징 접합층 에칭과정(S510) 없이 상기 금속박(40)을 장벽으로 하여 상기 브레이징층(30) 및 상기 시드층(20)을 에칭하여 상기 회로패턴에 대응되는 부분을 제외한 부분을 상기 세라믹 기재(10) 상에서 제거할 수 있다.
또한, 상기 에칭하는 단계(S500)는, 상기 금속박(40)의 측면으로 돌출되는 상기 브레이징층을 장벽으로 하여 상기 시드층(20)을 에칭하여 제거하는 것이다.
상기 에칭하는 단계(S500)는, 상기 금속박(40)의 측면으로 돌출되는 상기 브레이징 접합층(30)을 장벽으로 하여 시드층(20)을 에칭하는 것으로 제2시드층(22)을 에칭하는 과정(S510), 제1시드층(21)을 에칭하는 과정(S520)으로 구분될 수 있고, 상기 브레이징층을 장벽으로 하여 상기 시드층(20)을 에칭하여 상기 금속박(40)의 측면으로 상기 브레이징층과 상기 시드층(20)이 일부 노출되게 한다.
한편, 도 9를 참고하면, 본 발명의 다른 실시예에 의한 세라믹 기판 제조방법은, 상기 세라믹 기재(10)의 양면에 각각 상기 금속박(40)을 적층하여 브레이징을 통해 각각 접합시킬 수 있다. 이 경우 상기 시드층(20)을 형성하는 단계(S200)에서 상기 세라믹 기재(10)의 양면에 시드층(20)을 각각 형성하고, 상기 브레이징 필러층(31)을 상기 세라믹 기재(10)의 양면에 형성된 시드층(20)에 각각 적층한다.
또한, 상기 브레이징하는 단계(S400)는, 상기 세라믹 기재(10)의 양면에서 상기 브레이징 필러층(31) 상에 각각 금속박(40)을 적층하고, 브레이징 로(1) 내의 상기 하부 가압지그부(2)와 상기 상부 가압지그부(3)의 사이에 상기 세라믹 기재(10)를 배치하고 가열 중에 상기 세라믹 기재(10)의 양면에서 상기 금속박(40)을 가압하는 것이다.
상기 세라믹 기재(10)의 양면에 상기 금속박(40)을 적층하여 접합시키기 위한 상기 시드층(20)을 형성하는 단계(S200), 상기 브레이징 필러층(31)을 적층하는 단계(S300), 상기 브레이징하는 단계(S400)는, 상기 세라믹 기재(10)의 양면에 각각 시드층(20), 브레이징 필러층(31), 상기 금속박(40)을 배치하는 것 이외의 실시 예는 상기한 실시 예와 중복되어 기재를 생략함을 밝혀둔다.
한편, 도 10을 참고하면 본 발명의 일 실시예에 의한 세라믹 기판은, 세라믹 기재(10)를 포함한다.
상기 세라믹 기재(10)는, 알루미나(Al2O3) 세라믹 기판, AlN 세라믹 기판, SiN 세라믹 기판, Si3N4 세라믹 기판 중 어느 하나인 것을 일 예로 하고, 이외에도 반도체 전력 모듈 등에 사용 가능한 세라믹 소재로 변형 실시 가능함을 밝혀둔다.
상기 세라믹 기재(10)의 표면에는 화학약품 또는 물리적 연마로 미세 돌기부가 형성되는 것이 바람직하다. 상기 미세 돌기부는 브레이징 접합층(30)과의 접합력을 강화시킨다.
상기 세라믹 기재(10) 상에는 시드층(20)이 구비되고, 상기 시드층(20) 상에는 브레이징 접합층(30)을 통해 금속박(40)이 접합된다. 상기 브레이징 접합층(30)은 브레이징 필러층(31)이 용융된 후 경화되어 형성되는 것으로 상기 금속박(40)을 상기 세라믹 기재(10)에 접합시키는 역할을 한다.
또한, 상기 시드층(20)은 브레이징 접합층(30)을 통해 금속박(40)을 견고히 접합시키는 역할을 한다.
상기 시드층(20)은, 상기 세라믹 기재(10)와의 결합력이 높은 재료로 형성된 제1시드층(21), 상기 브레이징 접합층(30)과의 결합력이 우수한 재료로 형성되는 제2시드층(22)을 포함한다.
즉, 상기 제1시드층(21)은 상기 세라믹 기재(10)와의 결합력이 우수한 Ti, Hf, Zr 중 어느 하나로 형성되어 상기 세라믹 기재(10)와의 결합력을 확보하는 증착층이고, 상기 제2시드층(22)은 상기 브레이징 접합층(30)과의 결합력이 우수한 Cu 또는 Ag로 형성된 증착층인 것을 일 예로 한다.
상기 브레이징 접합층(30)은, Ag와 Cu가 혼합된 것을 일 예로 하고, 중량%로 Ag 65 ~ 75%, Cu 35 ~ 25%를 포함한 것을 일 예로 한다. 이는 환원분위기 또는 진공의 브레이징 로(1) 내에서 브레이징 온도 제어가 용이한 브레이징 필러층(31) 조성으로 브레이징 로(1) 내의 가열 온도를 860℃ 내외로 제어하여 효율적인 브레이징 공정이 이루어질 수 있도록 한다.
또한, 상기 브레이징 접합층(30)은 Ag와 Al, Ni, Sn, In 중 적어도 어느 하나를 혼합한 합금층인 것을 일 예로 한다.
상기 브레이징 접합층(30)은 상기 제2시드층(22)과 견고히 접합되어 상기 세라믹 기재(10)에 상기 금속박(40)을 최종적으로 견고하게 접합시키는 것이다.
상기 금속박(40)은, 알루미늄박 또는 동박인 것을 일 예로 한다.
상기 금속박(40)은 회로패턴(50)의 형상으로 에칭되어 회로패턴(50)을 형성하고, 상기 회로패턴(50)을 형성하기 위한 에칭단계(S500)를 통해 회로패턴(50) 형상 이외의 상기 금속박(40), 상기 브레이징 접합층(30) 및 상기 시드층(20)은 상기 세라믹 기재(10) 상에서 제거되는 것이다.
도 11를 참고하면 상기 시드층(20)은 적어도 두개의 금속이 혼합된 합금으로 형성되는 단층형 합금시드층(23)인 것이 바람직하다.
상기 단층형 합금시드층(23)은 TiCu, NiTi, TiCu, NiNb, CuMo, TiAg 중 어느 하나인 것이 바람직하다.
상기 TiCu, NiTi, TiCu, NiNb, CuMo, TiAg는 활성화 금속의 역할이 가능하며 하나의 에칭액으로 한번의 에칭공정으로 에칭될 수 있는 합금비로 제조된다.
상기 시드층(20)은 단층형 합금시드층(23)으로 형성됨으로써 제조공정을 단순화하고, 제조원가를 크게 절감하며 생산성을 향상시키는 효과가 있다.
한편, 상기 시드층(20), 상기 브레이징 접합층(30), 상기 금속박(40)은 회로패턴(50)을 형성하는 것을 일 예로 한다.
즉, 상기 세라믹 기재(10) 상에는 회로패턴(50)이 구비되며 상기 회로패턴(50)은 상기 세라믹 기재(10) 상에 형성된 시드층(20), 상기 시드층(20) 상에 형성된 브레이징 접합층(30) 및 상기 브레이징 접합층(30)에 의해 상기 시드층(20)에 접합되고, 회로패턴(50)의 형상으로 형성된 금속박(40)을 포함한다.
또한, 상기 브레이징 접합층(30)과 상기 시드층(20)은 상기 금속박(40)의 측면으로 일부 돌출되게 형성되는 것이 바람직하다.
상기 브레이징 접합층(30)과 상기 시드층(20)은 상기 금속박(40)의 측면으로 일부 돌출되어 상기 금속박(40)의 접합력을 더 증대시킨다.
도 12 및 도 13을 참고하면, 본 발명의 다른 실시 예에 따른 세라믹 기판은, 상기 세라믹 기재(10)의 양면에 회로패턴(50) 형상의 금속박(40)이 상기 브레이징 접합층(30)을 통해 접합될 수 있다.
이 경우 상기 세라믹 기재(10)의 양면에 상기 미세 돌기부가 형성되고, 상기 시드층(20)이 각각 형성되는 것이다.
한편, 도 14는 본 발명에 따른 세라믹 기판을 주사전자현미경으로 확대하여 찍은 사진이고, 도 15 도 14의 세라믹 기판을 주사전자현미경으로 더 확대하여 찍은 사진이다.
도 14 및 도 15의 세라믹 기판은 상기 세라믹 기재(10)의 상에 Ti 시드층과 Cu 시드층을 형성한 후 Ag 72wt%와 Cu 28wt%를 포함한 브레이징 시트를 이용하여 상기 브레이징하는 단계(S400)를 통해 두께 300㎛의 동박을 접합한 예이다.
도 14 및 도 15의 세라믹 기판을 열충격을 가하지 않은 상온에서 접합강도 시험을 200회 반복한 결과 최소 5.41kgf/cm, 최대 7.41kgf/cm이고, 평균 6.34kgf/cm의 결과가 도출되었다. -40℃의 열충격과 125℃의 열충격을 200회 반복한 결과 평균 6.28kgf/cm로 확인되어 상온과의 접합강도와 별차이가 없음을 확인하였다.
본 발명에 따른 세라믹 기판의 접합강도는 기존 세라믹 기재(10)의 접합강도는 상온뿐만 아니라 -40℃의 열충격과 125℃의 열충격을 가했을 경우에도 세라믹 기판의 접합 강도 기준인 4kgf/cm보다 크게 높은 것을 확인하였다.
본 발명은 기존에 소성공정에 의한 계면 결합 대신에 브레이징을 통해 금속박(40)과 세라믹 기재(10)를 일체화시키는 구성으로 금속박(40)과 세라믹 기재(10)의 접합력을 크게 향상시킨다.
본 발명은 고온 또는 진공 소성 장치가 필요 없고, 고온 또는 진공의 소성공정을 거치지 않고 제조가 가능하므로 제조비용을 크게 절감할 수 있다.
이와 같은 본 발명의 기본적인 기술적 사상의 범주 내에서, 당업계의 통상의 지식을 가진 자에게 있어서는 다른 많은 변형이 가능함은 물론이고, 본 발명의 권리범위는 첨부한 특허청구 범위에 기초하여 해석되어야 할 것이다.

Claims (21)

  1. 세라믹 기재와 금속박을 준비하는 단계;
    상기 세라믹 기재 상에 시드층을 형성하는 단계;
    상기 시드층 상에 브레이징 필러층을 적층하는 단계; 및
    상기 브레이징 필러층 상에 금속박을 적층하고 브레이징하는 단계를 포함하는 것을 특징으로 하는 세라믹 기판 제조방법.
  2. 제1항에 있어서,
    상기 세라믹 기재와 금속박을 준비하는 단계는 약품을 이용한 화학적 처리 또는 물리적 처리로 상기 세라믹 기재의 표면을 거칠게 하는 표면 개질 과정을 포함하는 것을 특징으로 하는 세라믹 기판 제조방법.
  3. 제1항에 있어서,
    금속박을 준비하는 단계는 절단하거나 타발되어 회로패턴 형상으로 형성된 금속박을 준비하는 것을 특징으로 하ㄴ는 세라믹 기판 제조방법.
  4. 제1항에 있어서,
    상기 브레이징 필러층을 형성하는 단계는 브레이징 시트를 적층하거나 페이스트 형태의 브레이징 필러를 인쇄하여 브레이징 필러층을 형성하는 것을 특징으로 하는 세라믹 기판 제조방법.
  5. 제1항에 있어서,
    상기 브레이징 필러층을 형성하는 단계는 도금으로 브레이징 필러 도금층을 형성하는 것을 특징으로 하는 세라믹 기판 제조방법.
  6. 제5항에 있어서,
    상기 브레이징 필러층을 형성하는 단계는, 도금으로 브레이징 필러 도금층을 0초과 10㎛ 이하의 두께를 가지도록 형성하는 것을 특징으로 하는 세라믹 기판 제조방법.
  7. 제1항에 있어서,
    상기 브레이징 필러층은 제1Ag층, 상기 제1Ag층 상에 적층되는 Al층, Ni층, Sn층, In층 중 어느 하나, 상기 Cu층 상에 적층되는 제2Ag층을 포함하거나, Al층, Ni층, Sn층, In층 중 어느 하나의 제1층, 상기 제1층 상에 적층되는 Ag층, 상기 Ag층 상에 적층되는 Al층, Ni층, Sn층, In층 중 어느 하나의 제2층을 포함하는 것을 특징으로 하는 세라믹 기판 제조방법.
  8. 제1항에 있어서,
    상기 시드층을 형성하는 단계는,
    상기 세라믹 기재 상에 세라믹 기재와의 결합력을 확보하는 제1시드층을 형성하는 과정; 및
    상기 제1시드층 상에 브레이징 필러층와의 결합력을 확보하는 제2시드층을 형성하는 과정을 포함하는 것을 특징으로 하는 세라믹 기판 제조방법.
  9. 제1항에 있어서,
    상기 시드층을 형성하는 단계는, 물리증착 방법으로 상기 시드층을 형성하는 것을 특징으로 하는 세라믹 기판 제조방법.
  10. 제8항에 있어서,
    상기 제1시드층은 Ti, Hf, Zr 중 어느 하나로 증착되고,
    상기 제2시드층은 Cu, Ag Al, Ni, Sn, In 중 어느 하나의 재료로 증착되는 것을 특징으로 하는 세라믹 기판 제조방법.
  11. 제1항에 있어서,
    상기 시드층을 형성하는 단계에서 상기 시드층을 합금으로 단층형 합금시드층으로 형성하는 것을 특징으로 하는 세라믹 기판 제조방법.
  12. 제1항에 있어서,
    상기 시드층을 형성하는 단계는 TiCu, NiTi, TiCu, NiNb, CuMo, TiAg 중 어느 하나의 합금으로 상기 세라믹 기재 상에 단층형 합금시드층을 형성하는 것을 특징으로 하는 세라믹 기판 제조방법.
  13. 제1항에 있어서,
    상기 브레이징 필러층은, 복수의 구멍을 가지는 형상으로 형성되는 것을 특징으로 하는 세라믹 기판 제조방법.
  14. 세라믹 기재;
    상기 세라믹 기재 상에 형성된 시드층;
    상기 시드층 상에 형성된 브레이징 접합층; 및
    상기 브레이징 접합층에 의해 상기 시드층 상에 브레이징 접합된 금속박을 포함하는 것을 특징으로 하는 세라믹 기판.
  15. 제14항에 있어서,
    상기 세라믹 기재의 표면에는 미세 돌기부가 형성되는 것을 특징으로 하는 세라믹 기판.
  16. 제14항에 있어서,
    상기 시드층은,
    상기 세라믹 기재와의 결합력을 가지며 증착으로 형성된 제1시드층; 및
    상기 브레이징층과의 결합력을 가지는 증착으로 형성된 제2시드층을 포함하는 것을 특징으로 하는 세라믹 기판.
  17. 제16항에 있어서,
    상기 제1시드층은 Ti, Hf, Zr 중 어느 하나이고,
    상기 제2시드층은 Cu, Ag Al, Ni, Sn, In 중 어느 하나인 것을 특징으로 하는 세라믹 기판.
  18. 제14항에 있어서,
    상기 시드층은 적어도 두개의 금속이 혼합된 합금으로 형성되는 단층형 합금시드층인 것을 특징으로 하는 세라믹 기판.
  19. 제18항에 있어서,
    상기 단층형 합금시드층은 TiCu, NiTi, TiCu, NiNb, CuMo, TiAg 중 어느 하나인 것을 특징으로 하는 세라믹 기판.
  20. 제14항에 있어서,
    상기 브레이징 접합층은 Ag와 Al, Ni, Sn, In 중 적어도 어느 하나를 혼합한 합금층인 것을 특징으로 하는 세라믹 기판.
  21. 제14항에 있어서,
    상기 브레이징층과 상기 시드층은 회로패턴의 형상과 대응되게 형성되되 상기 금속박 패턴의 측면으로 일부 돌출되게 형성되는 것을 특징으로 하는 세라믹 기판.
PCT/KR2016/004305 2015-04-24 2016-04-25 세라믹 기판 제조 방법 및 이 제조방법으로 제조된 세라믹 기판 WO2016171530A1 (ko)