WO2016003462A1 - Liaison de non-tissés à des matériaux à base de fluor - Google Patents

Liaison de non-tissés à des matériaux à base de fluor Download PDF

Info

Publication number
WO2016003462A1
WO2016003462A1 PCT/US2014/045263 US2014045263W WO2016003462A1 WO 2016003462 A1 WO2016003462 A1 WO 2016003462A1 US 2014045263 W US2014045263 W US 2014045263W WO 2016003462 A1 WO2016003462 A1 WO 2016003462A1
Authority
WO
WIPO (PCT)
Prior art keywords
nonwoven
reinforcement
nonwoven fabric
fluoro
aqueous fluoropolymer
Prior art date
Application number
PCT/US2014/045263
Other languages
English (en)
Inventor
Arvind PURUSHOTHAMAN
Douglas McKee BENTON
Rui Ferreira
Ann Marie EDWARDS
Mark Mancilla
Original Assignee
Ahlstrom Corporation
Porous Power Technologies, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ahlstrom Corporation, Porous Power Technologies, Inc. filed Critical Ahlstrom Corporation
Priority to PCT/US2014/045263 priority Critical patent/WO2016003462A1/fr
Publication of WO2016003462A1 publication Critical patent/WO2016003462A1/fr

Abstract

La présente invention concerne un non-tissé et un procédé de fabrication d'un non-tissé qui comprend un voile non tissé et une émulsion aqueuse de fluoropolymère comprenant un composant fluoro et un composant de liaison non fluoro appliqué sur le voile non tissé pour fournir des sites de liaison sur la surface et/ou à l'intérieur du voile non tissé, lesquels sont compatibles pour fixer le non-tissé à un matériau à base de fluor. La résistance d'adhérence entre le non-tissé et le matériau à base de fluor est supérieure à environ 25 grammes. Le non-tissé possède une résistance à la traction dans le sens machine supérieure à environ 4 N/cm, et une porosité à l'air supérieure à environ 50 %. L'invention concerne également un séparateur de batterie qui comprend un non-tissé constitué d'un renfort non tissé composé du non-tissé stratifié sur une membrane polymère microporeuse à base de fluor comprenant du PVDF.
PCT/US2014/045263 2014-07-02 2014-07-02 Liaison de non-tissés à des matériaux à base de fluor WO2016003462A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/US2014/045263 WO2016003462A1 (fr) 2014-07-02 2014-07-02 Liaison de non-tissés à des matériaux à base de fluor

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2014/045263 WO2016003462A1 (fr) 2014-07-02 2014-07-02 Liaison de non-tissés à des matériaux à base de fluor

Publications (1)

Publication Number Publication Date
WO2016003462A1 true WO2016003462A1 (fr) 2016-01-07

Family

ID=55019804

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2014/045263 WO2016003462A1 (fr) 2014-07-02 2014-07-02 Liaison de non-tissés à des matériaux à base de fluor

Country Status (1)

Country Link
WO (1) WO2016003462A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018147866A1 (fr) * 2017-02-10 2018-08-16 Daramic, Llc Séparateurs améliorés comprenant un mat fibreux, accumulateurs au plomb-acide, procédés et systèmes associés à ceux-ci
CN109004149A (zh) * 2017-06-07 2018-12-14 银隆新能源股份有限公司 一种锂离子电池隔膜制作方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5478628A (en) * 1992-05-18 1995-12-26 Minnesota Mining And Manufacturing Company Non-woven fluorescent retrorefletive fabric
US20030003363A1 (en) * 1999-03-07 2003-01-02 Takahiro Daido Lithium secondary cell, separator, cell pack, and charging method
US20040121677A1 (en) * 2002-08-26 2004-06-24 Bernhard Jahn Textile fabric and yarn composed of synthetic fibers, preparation thereof and use thereof
US20050106326A1 (en) * 2002-01-21 2005-05-19 Audenaert Frans A. Method of treatment of a textile or non-woven substrate to render same water and oil repellent
US20050112970A1 (en) * 2003-11-25 2005-05-26 Kimberly-Clark Worldwide, Inc. Method of treating nonwoven fabrics with non-ionic fluoropolymers
US20060182950A1 (en) * 2002-12-19 2006-08-17 Tesa Ag Easy-to-tear wrapping tape
WO2013126490A1 (fr) * 2012-02-21 2013-08-29 Arkema Inc. Composition de fluorure de polyvinylidène aqueux

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5478628A (en) * 1992-05-18 1995-12-26 Minnesota Mining And Manufacturing Company Non-woven fluorescent retrorefletive fabric
US20030003363A1 (en) * 1999-03-07 2003-01-02 Takahiro Daido Lithium secondary cell, separator, cell pack, and charging method
US20050106326A1 (en) * 2002-01-21 2005-05-19 Audenaert Frans A. Method of treatment of a textile or non-woven substrate to render same water and oil repellent
US20040121677A1 (en) * 2002-08-26 2004-06-24 Bernhard Jahn Textile fabric and yarn composed of synthetic fibers, preparation thereof and use thereof
US20060182950A1 (en) * 2002-12-19 2006-08-17 Tesa Ag Easy-to-tear wrapping tape
US20050112970A1 (en) * 2003-11-25 2005-05-26 Kimberly-Clark Worldwide, Inc. Method of treating nonwoven fabrics with non-ionic fluoropolymers
WO2013126490A1 (fr) * 2012-02-21 2013-08-29 Arkema Inc. Composition de fluorure de polyvinylidène aqueux

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018147866A1 (fr) * 2017-02-10 2018-08-16 Daramic, Llc Séparateurs améliorés comprenant un mat fibreux, accumulateurs au plomb-acide, procédés et systèmes associés à ceux-ci
CN109004149A (zh) * 2017-06-07 2018-12-14 银隆新能源股份有限公司 一种锂离子电池隔膜制作方法
CN109004149B (zh) * 2017-06-07 2021-08-10 银隆新能源股份有限公司 一种锂离子电池隔膜制作方法

Similar Documents

Publication Publication Date Title
CN108352483B (zh) 改进的膜、压延微孔膜、电池隔板和相关方法
JP5495210B2 (ja) 複合多孔質膜、複合多孔質膜の製造方法並びにそれを用いた電池用セパレーター
JP5203949B2 (ja) 改善されたナノファイバーセパレータを含む電気化学二重層キャパシタ
JP5065737B2 (ja) 改良された強度及び安定性を示す多層分離膜
KR101777076B1 (ko) 높은 용융 온도 미세다공성 리튬-이온 2차 전지 세퍼레이터 및 제조방법 및 용도
CN111615761B (zh) 电化学装置用隔膜及其制造方法
TWI529999B (zh) 超高熔融溫度微孔高溫電池分離器及相關方法
JP2021122019A (ja) 改良されたバッテリーセパレータおよび関連する方法
CN106574071B (zh) 微孔片材产品及其制备和使用方法
JP5412009B1 (ja) 電池用セパレータ及びその製造方法
KR101044167B1 (ko) 에너지 디바이스용 세퍼레이터, 및 그것을 포함하는 에너지디바이스
WO2012100064A1 (fr) Séparateur pour pile au lithium présentant une fonction d'arrêt
EP2064379A2 (fr) Nanotoiles perfectionnées
JP2007311332A5 (fr)
CN111344054B (zh) 浸渍用基膜、改进的被浸渍的产品及相关方法
US20240141198A1 (en) Separator coating for li-ion batteries based on pvdf acrylate latex
JPH11207888A (ja) 複合多孔質体
KR20210129132A (ko) 비수계 이차전지용 세퍼레이터 및 비수계 이차전지
WO2016003462A1 (fr) Liaison de non-tissés à des matériaux à base de fluor
JP7191536B2 (ja) 電気化学素子用セパレータ
JP7324173B2 (ja) 非水系二次電池用セパレータ及び非水系二次電池
JP4796123B2 (ja) 複合膜のための連続被覆方法
JP7493548B2 (ja) 電気化学素子用セパレータ及びこの製造方法
Veitl Development of a laminable, cellulose-based Separator for Lithium-Ion Batteries

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14896648

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase