WO2015167163A1 - 점착제 조성물 - Google Patents

점착제 조성물 Download PDF

Info

Publication number
WO2015167163A1
WO2015167163A1 PCT/KR2015/004004 KR2015004004W WO2015167163A1 WO 2015167163 A1 WO2015167163 A1 WO 2015167163A1 KR 2015004004 W KR2015004004 W KR 2015004004W WO 2015167163 A1 WO2015167163 A1 WO 2015167163A1
Authority
WO
WIPO (PCT)
Prior art keywords
sensitive adhesive
pressure
adhesive composition
agent
weight
Prior art date
Application number
PCT/KR2015/004004
Other languages
English (en)
French (fr)
Inventor
최한영
안명용
유민근
Original Assignee
동우 화인켐 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 동우 화인켐 주식회사 filed Critical 동우 화인켐 주식회사
Publication of WO2015167163A1 publication Critical patent/WO2015167163A1/ko

Abstract

발명은 대전방지성 및 내구성이 뛰어난 점착제 조성물에 관한 것이다. 본 발명의 점착제 조성물은 요오드화리튬을 대전방지제로 사용함으로써 향상된 대전방지기능을 갖는 것이 특징이며, 환원제를 포함으로써 투명성이 저하되지 않는 효과를 갖는다.

Description

점착제 조성물
본 발명은 대전방지성 및 내구성이 뛰어난 점착제 조성물에 관한 것이다.
액정표시장치는 액정을 포함하는 액정 셀, 편광판, 및 이들을 접합하기 위한 접착 또는 점착층으로 이루어진다. 상기 편광판은 일정한 방향으로 배열된 요오드계 화합물 또는 이색성 편광물질, 이들 편광소자를 보호하기 위한 트리아세틸셀룰로오스(triacetyl cellulose, TAC)계의 보호필름, 점착층, 이형필름 등의 다층으로 구성된다.
상기와 같은 액정표시장치 제조시 액정 셀에 편광판을 부착하기 위하여 접착층에서 이형필름을 박리할 때 발생하는 정전기는 액정표시장치 내부의 액정배향에 영향을 주어 불량을 유발하며, 상기 정전기 발생을 막기 위하여 편광판 외면에 대전방지층을 형성시키는 방법을 사용하였으나, 이는 정전기 발생의 원천적 방지는 되지 못하며 그 효과 또한 극히 낮다는 문제점이 있었다.
따라서, 근본적인 정전기 발생을 차단하기 위해서는 점착제의 대전방지기능이 필요하다.
점착제에 대전방지기능을 부여하기 위해서는 도전성 금속분말이나 탄소입자 등의 물질을 첨가하는 방법, 계면활성제와 같은 이온성 물질을 접착제에 첨가하는 방법 등이 있다. 그러나, 상기 도전성 금속분말이나 탄소입자를 첨가하는 경우 대전방지성을 나타내기 위하여는 다량의 도전성 금속분말이나 탄소입자가 사용되어야 하며, 이에 따라 투명성이 저하된다는 문제점이 있다. 또한, 계면활성제를 첨가하는 경우에는 습도의 영향을 받기 쉬우며, 점착제 표면으로의 이행에 따라 접착성이 저하되는 문제점이 있었다.
이에 점착제에 대전방지기능을 부여하기 위한 다양한 연구가 진행되었으나, 여전히 내구신뢰성 등 아크릴계 점착제의 물성을 변화시키지 않으면서 대전방지성능이 우수하고 투명성이 저하되지 않는 점착제를 제시하지 못하고 있다. 일례로, 대한민국 공개특허 10-2006-0127347호에서는 아크릴계 공중합체, 퍼플루오르알킬기를 함유하는 음이온과 알칼리금속 양이온으로 이루어지는 금속염 및 다관능성 가교제를 포함하는 점착제 조성물을 기재하고 있으나, 대전방지성을 만족시키기 위해 과량의 대전방지제를 사용해야 하는 문제점을 가지고 있다.
상기와 같이 대전방지제를 과량 사용하게 되면, 가격경쟁력이 저하되며, 과량의 대전방지제의 글라스방향으로의 이동에 의해 점착력이 저하되어 점착내구성 불량이 우려되고, 과량의 대전방지제의 편광자방향으로의 이동에 의하여 편광자의 폴리요오드 이온과의 반응에 의하여 광학내구성의 저하가 우려된다.
이에, 본 발명은 점착력을 유지하면서 대전방지성능이 우수하고 투명성이 저하되지 않는 점착제 조성물을 제공하는 것을 목적으로 한다.
상기 과제를 해결하고자, 본 발명은 아크릴계 공중합체, 대전방지제 및 환원제를 함유하며, 상기 대전방지제는 요오드화리튬(LiI)인 것인 점착제 조성물을 제공한다.
본 발명의 일 구현예는 상기 대전방지제가 조성물 총 중량에 대하여 0.1 내지 5 중량%로 포함되는 것일 수 있다.
다른 일 구현예는 상기 환원제는 설파이트류, 티오설페이트류 및 포스파이트류로 이루어진 군으로부터 선택되는 1종 이상인 것일 수 있다.
또 다른 일 구현예는 환원제가 대전방지제 100중량부에 대하여 10 내지 100중량부로 포함되는 것일 수 있다.
또 다른 일 구현예는 아크릴계 공중합체는 탄소수 1 내지 12의 알킬기를 갖는 (메타)아크릴레이트 단량체; 및 히드록시기를 갖는 단량체, 아미드기를 갖는 단량체 및 3차 아민기를 갖는 단량체로 이루어진 군으로부터 1종 이상 선택되는 가교성 단량체를 함유하는 것일 수 있다.
또 다른 일 구현예는 가교제를 추가로 함유하는 것일 수 있다.
또 다른 일 구현예는 실란 커플링제를 추가로 함유하는 것일 수 있다.
본 발명의 점착제 조성물은 요오드화리튬을 대전방지제로 사용함으로써 소량으로도 향상된 대전방지기능을 갖는 것이 특징이며, 환원제를 포함으로써 투명성이 저하되지 않는 효과를 갖는다.
아크릴계 공중합체, 대전방지제 및 환원제를 함유하며, 상기 대전방지제는 요오드화리튬(LiI)인 것인 점착제 조성물을 제공한다.
본 발명자들은 요오드화리튬(LiI)을 대전방지제로 포함함으로써 소량으로도 대전방지기능이 향상되는 것과, 환원제를 포함함으로써 변색이 방지되는 것을 확인함으로써 본 발명을 완성하였다.
이하, 각 성분에 대하여 구체적으로 설명한다.
아크릴계 공중합체
본 발명에서의 아크릴계 공중합체는 점착제 탄소수 1-12의 알킬기를 갖는 (메타) 아크릴레이트 단량체 및 가교성 단량체가 공중합된 아크릴계 공중합체인 것이 바람직하다.
상기 (메타)아크릴레이트는 아크릴레이트 및 메타크릴레이트 모두를 의미하며, 탄소수 1-12의 알킬기를 갖는 (메타)아크릴레이트 단량체로는 n-부틸(메타)아크릴레이트, 2-부틸(메타)아크릴레이트, t-부틸(메타)아크릴레이트, 2-에틸헥실(메타)아크릴레이트, 에틸(메타)아크릴레이트, 메틸(메타)아크릴레이트, 메틸에틸(메타)아크릴레이트, n-프로필(메타)아크릴레이트, 이소프로필(메타)아크릴레이트, 펜틸(메타)아크릴레이트, n-옥틸(메타)아크릴레이트, 이소옥틸(메타)아크릴레이트, 노닐(메타)아크릴레이트, 데실(메타)아크릴레이트, 라우릴(메타)아크릴레이트 등을 들 수 있으며, 이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다. 이 중에서 n-부틸아크릴레이트, 2-에틸헥실아크릴레이트 또는 이들의 혼합물이 바람직하다.
탄소수 1-12의 알킬기를 갖는 (메타)아크릴레이트 단량체는 아크릴계 공중합체의 제조에 사용되는 총 단량체 100중량부를 기준으로 80 내지 99중량부로 포함될 수 있고, 바람직하게 90 내지 95중량부인 것이 좋다. 함량이 80중량부 미만인 경우 점착력이 충분하지 못하고, 99중량부 초과인 경우 응집력이 저하될 수 있다.
가교성 단량체는 화학 결합에 의해 점착제 조성물의 응집력 또는 점착 강도를 보강하여 내구성과 절단성을 부여하기 위한 성분으로서, 예컨대 히드록시기를 갖는 단량체, 아미드기를 갖는 단량체, 3차 아민기를 갖는 단량체 등을 들 수 있으며, 이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다.
히드록시기를 갖는 단량체로는 2-히드록시에틸(메타)아크릴레이트, 2-히드록시프로필(메타)아크릴레이트, 2-드록시부틸(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 6-히드록시헥실(메타)아크릴레이트, 2-히드록시에틸렌글리콜(메타), 아크릴레이트, 2-히드록시프로필렌글리콜(메타)아크릴레이트, 알킬렌기의 탄소수가 2-4인 히드록시알킬렌글리콜(메타)아크릴레이트, 4-히드록시부틸비닐에테르, 5-히드록시펜틸비닐에테르, 6-히드록시헥실비닐에테르, 7-히드록시헵틸비닐에테르, 8-히드록시옥틸비닐에테르, 9-히드록시노닐비닐에테르, 10-히드록시데실비닐에테르 등을 들 수 있으며, 이들 중에서 4-히드록시부틸비닐에테르가 바람직하다.
아미드기를 갖는 단량체로는 (메타)아크릴아미드, N-이소프로필아크릴아미드, N-3차부틸아크릴아미드, 3-히드록시프로필(메타)아크릴아미드, 4-히드록시부틸(메타)아크릴아미드, 6-히드록시헥실(메타)아크릴아미드, 8-히드록시옥틸(메타)아크릴아미드, 2-히드록시에틸헥실(메타)아크릴아미드 등을 들 수 있으며, 이들중에서 (메타)아크릴아미드가 바람직하다.
3차 아민기를 갖는 단량체로는 N,N-(디메틸아미노)에틸(메타)아크릴레이트, N,N-(디에틸아미노)에틸(메타)아크릴레이트, N,N-(디메틸아미노)프로필(메타)아크릴레이트 등을 들 수 있다.
가교성 단량체는 아크릴계 공중합체의 제조에 사용되는 총 단량체 100중량부를 기준으로 0.05 내지 10중량부로 포함되는 것이 바람직하고, 보다 바람직하게는 0.1 내지 8중량부인 것이 좋다. 함량이 0.05중량부 미만인 경우 점착제의 응집력이 작아지게 되어 내구성이 저하될 수 있으며, 10중량부 초과인 경우 높은 겔분율에 의해 점착력이 떨어지고 내구성에 문제를 야기할 수 있다.
또한, 상기 단량체들 이외에 다른 중합성 단량체가 점착력을 저하시키지 않는 범위, 예컨대 총 단량체 함량을 기준으로 10중량부 이하로 더 포함될 수 있다.
공중합체의 제조방법은 특별히 한정되지 않으며, 당 분야에서 통상적으로 사용되는 괴상중합, 용액중합, 유화중합 또는 현탁중합 등의 방법을 이용하여 제조할 수 있으며, 용액중합이 바람직하다. 또한, 중합 시 통상 사용되는 용매, 중합개시제, 분자량 제어를 위한 연쇄이동제 등을 사용할 수 있다.
대전방지제
본 발명에서의 대전방지제는, 정전기를 방지하여 정전기적 인력에 의해 액정셀과 점착제 사이에 유입된 이물에 의해 유발되는 오염 또는 액정의 배향에 영향을 주어 유발되는 불량을 방지하는 기능을 하는 것으로, 요오드화리튬(LiI)을 사용하는 것이 특징이다. 상기 요오드화리튬은 수용성염을 제외한 이온염 중에서 양이온이 가장 작아 이온의 이동의 이동성이 좋으며, 또한 할로겐 산 중에서 가장 안정한 음이온인 요오드이온을 함유하여 이온의 해리도가 높아 결과적으로 대전방지성이 가장 우수하다.
이에 따라, 상기 요오드화리튬은 소량을 사용하더라도 대전방지기능을 현저히 향상시키며, 이로 인하여 저가화가 가능하고 대전방지제 소량사용에 의한 블리드 아웃(bleed-out) 현상이 적어 내구성 개선이 가능한 것이 특징이다.
상기 대전방지제는 점착제 조성물 총 중량에 대하여 0.1 내지 5중량%로 포함되는 것이 바람직하다. 상기 기준으로 대전방지제가 0.1중량% 미만이면 대전방지성이 부족하며, 5중량%를 초과하면 블리드 아웃에 의한 점착력 저하를 유발할 우려가 있다.
환원제
본 발명에서 변색이란 요오드음이온이 점착제 내에 존재하는 산화제(산소)와 반응하여 요오드 분자가 형성되고, 형성된 요오드 분자와 요오드음이온이 반응하여, 요오드원자의 3량체, 5량체 등을 형성하여, 이들의 광흡수로 인하여 색을 나타내는 현상을 말한다.
본 발명에서의 환원제는 변색방지 기능을 하는 것으로, 보다 구체적으로는 산화제(산소)를 제거하거나 생성된 요오드 분자를 환원시킴으로써 변색방지 기능을 하는 것을 말한다. 상기 환원제는 S계, P계 환원제를 사용하는 것이 바람직하며, 산소나 요오드 분자는 약산화제이기 때문에 약한 환원제(예를 들어, 페놀, 알데히드)에 의해서 환원이 안되고, 강한 한원제는 이소시아네이트의 분해 문제로 사용할 수 없기 때문에 설파이트류, 티오설페이트류, 포스파이트류를 사용하는 것이 가장 바람직하다.
구체적으로는, 환원제로 다이알킬 설파이트, 설파이트 금속염, 히드로설파이트 금속염, 티오설페이트 금속염, 디아킬포스파이트, 트리알킬포스파이트 또는 포스파이트 금속염이 사용될 수 있다.
상기 환원제는 대전방지제 100중량부에 대하여 10 내지 100중량부로 포함되는 것이 바람직하다. 상기 기준으로 환원제가 10 중량부 미만인 경우 변색 억제효과가 부족할 수 있으며, 100중량부를 초과하는 경우 환원제 자체의 블리드아웃에 의한 내구성 저하가 우려될 수 있다.
가교제
가교제는 공중합체를 적절히 가교함으로써 점착제의 응집력을 강화하기 위한 성분으로서, 그 종류는 특별히 한정되지 않는다. 예컨대, 이소시아네이트계 화합물, 에폭시계 화합물 등을 들 수 있으며, 이들은 단독 또는 2종 이상 혼합하여 사용할 수 있다.
이소시아네이트계 화합물로는 톨릴렌디이소시아네이트, 자일렌디이소시아네이트, 2,4-디페닐메탄디이소시아네트, 4,4-디페닐메탄디이소시아네트, 헥사메틸렌디이소시아네이트, 이소포론디이소시아네이트, 테트라메틸자일렌디이소시아네이트, 나프탈렌디이소시아네이트 등의 디이소시아네이트화합물; 트리메틸올프로판 등의 다가 알콜계 화합물 1몰에 디이소시아네이트 화합물 3몰을 반응시킨 부가체, 디이소시아네이트 화합물 3몰을 자기 축합시킨 이소시아누레이트체, 디이소시아네이트 화합물 3몰 중 2몰로부터 얻어지는 디이소시아네이트 우레아에 나머지 1몰의 디이소시아네이트가 축합된 뷰렛체, 트리페닐메탄트리이소시아네이트, 메틸렌비스트리이소시아네이트 등의 3개의 관능기를 함유하는 다관능 이소시아네이트 화합물 등을 들 수 있다.
에폭시계 화합물로는 에틸렌글리콜디글리시딜에테르, 디에틸렌글리콜디글리시딜에테르, 폴리에틸렌글리콜디글리시딜에테르, 프로필렌글리콜디글리시딜에테르, 트리프로필렌글리콜디글리시딜에테르, 폴리프로필렌글리콜디글리시딜에테르, 네오펜틸글리콜디글리시딜에테르, 1,6-헥산디올디글리시딜에테르, 폴리테트라메틸렌글리콜디글리시딜에테르, 글리세롤디글리시딜에테르, 글리세롤트리글리시딜에테르, 디글리세롤폴리글리시딜에테르, 폴리글리세롤폴리글리시딜에테르, 레졸신디글리시딜에테르, 2,2-디브로모네오펜틸글리콜디글리시딜에테르, 트리메틸올프로판트리글리시딜에테르, 펜타에리트리톨폴리글리시딜에테르, 소르비톨폴리글리시딜에테르, 아디핀산디글리시딜에스테르, 프탈산디글리시딜에스테르, 트리스(글리시딜)이소시아누레이트, 트리스(글리시독시에틸)이소시아누레이트, 1,3-비스(N,N-글리시딜아미노메틸)시클로헥산, N,N,N',N'-테트라글리시딜-m-자일릴렌디아민 등을 들 수 있다.
또한, 이소시아네이트계 화합물, 에폭시계 화합물과 함께 멜라민계 화합물을 단독 또는 2종 이상 혼합하여 추가로 사용할 수 있다. 멜리민계 화합물로는 헥사메틸올멜라민, 헥사메톡시메틸멜라민, 헥사부톡시메틸멜라민 등을 들 수 있다.
가교제는 고형분 함량을 기준으로 아크릴계 공중합체 100중량부에 대하여 0.1 내지 15중량부로 포함되는 것이 바람직하고, 보다 바람직하게는 0.1 내지 5중량부 인 것이 좋다. 함량이 0.1중량부 미만인 경우 부족한 가교도로 인해 응집력이 작아지게 되어 기재면과 들뜨는 현상과 같은 내구성 저하가 유발되고 절단성을 해칠 수 있으며, 15중량부 초과인 경우 과다 가교반응에 의해 잔류응력 완화에 문제가 발생할 수 있다.
실란커플링제
점착제 조성물은 실란커플링제를 더 포함할 수 있다.
실란커플링제는 점착제와 기재와의 밀착력을 향상시키기 위해서 첨가되며, 아미노기, 에폭시기, 아세토아세틸기, 폴리알킬렌글리콜기, 아크릴기, 알킬기 등의 관능기를 함유하는 알콕시실란을 사용하며, 고형분 함량을 기준으로 아크릴계 공중합체 100중량부에 대하여 0.1 내지 2.0중량부로 포함되는 것이 바람직하고, 보다 바람직하게는 0.1 내지 0.5중량부 인 것이 좋다. 함량이 0.1중량부 미만인 경우 기재밀착력이 부족하여, 내습열조건에서 박리가 일어나기 쉬위며, 2중량부 이상인경우에는 내열조건에서 박리가 일어날 우려가 있다.
상기와 같은 성분 이외에, 점착제 조성물은 용도에 따라 요구되는 점착력, 응집력, 점성, 탄성률, 유리전이온도, 대전방지성 등을 조절하기 위하여, 점착성 부여 수지, 산화방지제, 레벨링제, 표면윤활제, 염료, 안료,소포제, 충전제, 광안정제, 대전방지제 등의 첨가제를 더 포함할 수 있다.
본 발명의 편광판은 점착제 조성물로 이루어진 점착제층이 적층된 것을 특징으로 한다.
점착제층의 두께는 그 점착력에 따라 조절될 수 있으며, 통상 3 내지 100㎛인 것이 바람직하며, 보다 바람직하게는 10 내지 100㎛인 것이 좋다. 이러한 편광판은 통상의 액정표시장치에 모두 적용 가능하며, 구체적으로 점착제층이 적층된 편광판을 액정셀의 적어도 한 면에 접합한 액정패널을 포함하는 액정표시장치를 구성할 수 있다.
이하, 본 발명을 실시예, 비교예 및 실험예를 이용하여 더욱 상세하게 설명한다. 그러나 하기 실시예, 비교예 및 실험예는 본 발명을 예시하기 위한 것으로서, 본 발명은 하기 실시예, 비교예 및 실험예에 의해 한정되지 않고 다양하게 수정 및 변경될 수 있다.
제조예 1. 아크릴계 공중합체 제조
질소가스가 환류되고 온도조절이 용이하도록 냉각장치를 설치한 1 L의 반응기에 n-부틸아크릴레이트(BA) 90중량부, 메틸아크릴레이트(MA) 7중량부, 2-히드록시에틸아크릴레이트 2중량부, 아크릴산 1중량부로 이루어진 단량체 혼합물을 투입한 후, 용제로 아세톤 100중량부를 투입하였다. 그 다음 산소를 제거하기 위하여 질소가스를 1시간 동안 퍼징한 후, 62℃로 유지하였다. 상기 혼합물을 균일하게 한 후, 반응개시제로 아조비스이소부티로니트릴(AIBN) 0.07중량부를 투입하고, 6시간 동안 반응시켜 중량평균분자량이 약 100만인 아크릴계 공중합체를 제조하였다.
실시예 1 내지 10 및 비교예 1 내지 5
(1) 점착제 조성물
하기 표 1에 기재된 성분 및 함량으로 점착제 조성물을 제조하였다. 함량의 단위는 중량부이며, 대전방지제는 고형분 함량을 나타낸 것이다.
표 1
구분 아크릴계 공중합체 가교제 실란 커플링제 대전방지제 환원제
실시예1 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(0.5) A(0.1)
실시예2 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(0.5) B(0.1)
실시예3 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(0.5) C(0.1)
실시예4 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(0.2) A(0.05)
실시예5 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(1) A(0.5)
실시예6 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(2) A(0.5)
실시예7 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(3) A(1)
실시예8 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(0.5) A(0.5)
실시예9 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(1) A(1.5)
실시예10 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(1) A(0.2)
비교예 1 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(0.5) -
비교예 2 제조예 1(100) Cor-L(1) KBM-403(0.5) LiI(0.5) D(0.1)
비교예 3 제조예 1(100) Cor-L(1) KBM-403(0.5) E(0.5) -
비교예 4 제조예 1(100) Cor-L(1) KBM-403(0.5) F(0.5) -
비교예 5 제조예 1(100) Cor-L(1) KBM-403(0.5) G(0.5) -
A: 다이프로필설파이트 (TCI사)
B: 소듐티오설페이트 (TCI사) 10% 아세트산 용액
C: 디아이소프로필 포스파이트(TCI사)
D: 소듐설페이트 (TCI사) 10% 아세트산 용액
E:
Figure PCTKR2015004004-appb-I000001
F:
Figure PCTKR2015004004-appb-I000002
G: NaPF6
(2) 점착시트
제조된 점착제 조성물을 실리콘 이형제가 코팅된 필름 상에 건조 후 두께가 25㎛가 되도록 도포하고 100℃에서 1분 동안 건조하여 점착제층을 형성하였다. 그 위에 다른 한 층의 이형필름을 라미네이션하여 점착시트를 제조하였다.
(3) 점착제 부착 편광판
제조된 점착시트의 이형필름을 박리한 후 두께 185㎛의 요오드계 편광판에 점착제층을 점착 가공하여 적층하여 점착제 부착 편광판을 제조하였다.
실험예
(1) 내열성 평가
상기의 제조된 점착제 부착편광판의 이형필름을 제거하고, 코닝글라스에 접합하고, 오토클레이브 처리한뒤, 60℃에서 300시간 방치 후 기포와 박리현상을 관찰하였고, 그 결과를 하기 표 2에 나타내었다.
<평가기준>
X: 기포 또는 박리가 전면에서 육안으로 확인됨
△: 기포 또는 박리가 육안으로 3개이상 10개 이하 확인됨
○: 기포 또는 박리가 육안으로 2개 이하 확인됨
◎: 기포 또는 박리가 육안으로 확인 안됨
(2) 대전방지성(표면비저항)
제조된 점착제 부착 편광판을 표면저항 측정기(MCP-HT450, Mitsubishi chemical사)를 이용하여 점착제층의 3지점을 각각 10회씩 측정하고, 그 평균값으로 나타내었다.
이후에 점착제 부착 편광판을 60℃에서 24시간 방치한 후에 상기와 동일한 방법으로 측정하였고, 그 결과를 하기 표 2에 나타내었다.
(3) 변색방지성
상기 내열성 평가 샘 V의 변색 유무를 육안으로 확인하였고, 그 결과를 하기 표 2에 나타내었다.
<평가기준>
X: 변색이 육안으로 확인됨
○: 변색이 육안으로 미확인됨
표 2
구분 내열성 표면비저항 (Ω/□) 변색방지성
실시예1 ◎ 3X1010 ○
실시예2 ◎ 3X1010 ○
실시예3 ◎ 3X1010 ○
실시예4 ◎ 7X1010 ○
실시예5 ◎ 1X1010 ○
실시예6 ◎ 5X109 ○
실시예7 ○ 1X109 ○
실시예8 ○ 1X1010 ○
실시예9 △ 3X1010 ○
실시예10 ◎ 1X1010 ○
비교예1 ◎ 3X1010 X
비교예2 ◎ 3X1010 X
비교예3 ○ 4X1011 ○
비교예4 ◎ 2X1011 ○
비교예5 X 3X1011 ○
상기 표 2에 나타난 바와 같이, 실시예 1 내지 10의 점착제 조성물은 비교예 1 내지 5에 비해 내열성, 대전방지성 및 변색방지성이 동시에 우수하다는 것을 확인할 수 있었다.
본 발명의 점착제 조성물은 요오드화리튬을 대전방지제로 사용함으로써 소량으로도 향상된 대전방지기능을 갖는 것이 특징이며, 환원제를 포함으로써 투명성이 저하되지 않는 효과를 갖는다.

Claims (7)

  1. 아크릴계 공중합체, 대전방지제 및 환원제를 함유하며,
    상기 대전방지제는 요오드화리튬(LiI)인 것인 점착제 조성물.
  2. 청구항 1에 있어서, 상기 대전방지제는 조성물 총 중량에 대하여 0.1 내지 5 중량%로 포함되는 것을 특징으로 하는 점착제 조성물.
  3. 청구항 1에 있어서, 상기 환원제는 설파이트류, 티오설페이트류 및 포스파이트류로 이루어진 군으로부터 선택되는 1종 이상인 것을 특징으로 하는 점착제 조성물.
  4. 청구항 1에 있어서, 상기 환원제는 대전방지제 100중량부에 대하여 10 내지 100중량부로 포함되는 것을 특징으로 하는 점착제 조성물.
  5. 청구항 1에 있어서, 상기 아크릴계 공중합체는
    탄소수 1 내지 12의 알킬기를 갖는 (메타)아크릴레이트 단량체; 및
    히드록시기를 갖는 단량체, 아미드기를 갖는 단량체 및 3차 아민기를 갖는 단량체로 이루어진 군으로부터 1종 이상 선택되는 가교성 단량체를 함유하는 것을 특징으로 하는 점착제 조성물.
  6. 청구항 1에 있어서, 상기 점착제 조성물은 가교제를 추가로 함유하는 것을 특징으로 하는 점착제 조성물.
  7. 청구항 1에 있어서, 상기 점착제 조성물은 실란 커플링제를 추가로 함유하는 것을 특징으로 하는 점착제 조성물.
PCT/KR2015/004004 2014-04-30 2015-04-22 점착제 조성물 WO2015167163A1 (ko)