WO2014162097A1 - Composition de mortier isolant - Google Patents
Composition de mortier isolant Download PDFInfo
- Publication number
- WO2014162097A1 WO2014162097A1 PCT/FR2014/050784 FR2014050784W WO2014162097A1 WO 2014162097 A1 WO2014162097 A1 WO 2014162097A1 FR 2014050784 W FR2014050784 W FR 2014050784W WO 2014162097 A1 WO2014162097 A1 WO 2014162097A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mortar
- weight
- total composition
- mortar according
- relative
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
- C04B28/04—Portland cements
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/04—Silica-rich materials; Silicates
- C04B14/14—Minerals of vulcanic origin
- C04B14/18—Perlite
- C04B14/185—Perlite expanded
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/04—Silica-rich materials; Silicates
- C04B14/20—Mica; Vermiculite
- C04B14/204—Mica; Vermiculite expanded
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/04—Silica-rich materials; Silicates
- C04B14/22—Glass ; Devitrified glass
- C04B14/24—Glass ; Devitrified glass porous, e.g. foamed glass
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/30—Oxides other than silica
- C04B14/301—Oxides other than silica porous or hollow
- C04B14/302—Aerogels
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B16/00—Use of organic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of organic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B16/04—Macromolecular compounds
- C04B16/08—Macromolecular compounds porous, e.g. expanded polystyrene beads or microballoons
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B18/04—Waste materials; Refuse
- C04B18/06—Combustion residues, e.g. purification products of smoke, fumes or exhaust gases
- C04B18/10—Burned or pyrolised refuse
- C04B18/105—Gaseous combustion products or dusts collected from waste incineration, e.g. sludge resulting from the purification of gaseous combustion products of waste incineration
- C04B18/106—Fly ash from waste incinerators
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B18/04—Waste materials; Refuse
- C04B18/14—Waste materials; Refuse from metallurgical processes
- C04B18/141—Slags
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B18/04—Waste materials; Refuse
- C04B18/14—Waste materials; Refuse from metallurgical processes
- C04B18/146—Silica fume
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B22/00—Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators, shrinkage compensating agents
- C04B22/02—Elements
- C04B22/04—Metals, e.g. aluminium used as blowing agent
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B22/00—Use of inorganic materials as active ingredients for mortars, concrete or artificial stone, e.g. accelerators, shrinkage compensating agents
- C04B22/06—Oxides, Hydroxides
- C04B22/068—Peroxides, e.g. hydrogen peroxide
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
- C04B28/06—Aluminous cements
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
- C04B28/10—Lime cements or magnesium oxide cements
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
- C04B28/10—Lime cements or magnesium oxide cements
- C04B28/12—Hydraulic lime
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
- C04B38/02—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof by adding chemical blowing agents
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
- C04B38/08—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof by adding porous substances
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/00034—Physico-chemical characteristics of the mixtures
- C04B2111/00146—Sprayable or pumpable mixtures
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
- C04B2111/00482—Coating or impregnation materials
- C04B2111/00517—Coating or impregnation materials for masonry
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/20—Resistance against chemical, physical or biological attack
- C04B2111/28—Fire resistance, i.e. materials resistant to accidental fires or high temperatures
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02W—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT
- Y02W30/00—Technologies for solid waste management
- Y02W30/50—Reuse, recycling or recovery technologies
- Y02W30/91—Use of waste materials as fillers for mortars or concrete
Definitions
- the present invention relates to a lightened insulating mortar and its use in the field of construction for coating and / or treating surfaces or walls of buildings, in particular facades, both for new constructions and for the renovation of existing constructions.
- Ble particularly relates to a mortar easily applicable to surfaces by means of usual applications, such as for example by pneumatic projection using a mortar pump.
- TE Outdoor thermal insulation
- ITE systems conventionally comprise an insulator on which one or more layers of facing plaster are applied. They are generally complex systems that are very thick.
- the insulating capacities of these systems are in particular a function of the choice of insulating material and its thickness. Sheets of expanded polystyrene with a thickness of between 20 and 500 mm are currently used. The greater the thickness of the plate, the better the insulation. However, too thick insulation results in a loss of floor space and also many additional costs. It is therefore necessary to find a compromise between a material with the best characteristics of soil and the most expensive weights.
- insulating plaster or mortar incorporates insulating materials such as expanded polystyrene beads or exfoliated vermiculite. They are usually applied in several layers. Even if they allow an improvement of the insulation of the surface on which they are applied, they do not make it possible to reach technical performances equivalent to those of the other techniques and system ITE, and do not make it possible to get rid of the plates insulation. Expanded polystyrene sheets used in conventional ITE systems have a thermal conductivity of about 37 mW / mK. In order for an insulating mortar to achieve similar thermal performance, it would be necessary for it to contain no heat.
- the present invention has sought to develop a lightweight insulating mortar usable for facade cladding to overcome the drawbacks mentioned above.
- the insulating mortar according to the present invention has the advantage of combining good thermal insulation properties, comparable to those of expanded polystyrene plates, and good mechanical strength properties, compatible with the applications envisaged. It also has a very good fire resistance, superior to the EPS only plates.
- the present invention provides an insulating mortar lightened and having a density of less than 300 kg / m 3 in the cured state comprising at least one inorganic binder selected from cement and lime, in an amount between 50 and 95% by weight relative to the total composition of the mortar, at least 1% by weight of a polymeric adjuvant relative to the total composition of the mortar, at least 0.2% by weight of a rheological admixture relative to the total composition of the mortar, optionally aggregates, said mortar comprising at least 70% by volume of leaching fillers having a thermal conduction of less than 55 mW / mK, relative to the composition of the mortar, chosen from expanded polystyrene, aerogels, hollow microspheres of glass, expanded glass beads, cenospheres, vermiculite and perlite and of which at least 10% by weight of the inorganic binder is substituted by a pozzolanic agent.
- Percentages of binder, polymeric or rheological adjuvant, leaching charges or other fillers and / or additives are given by weight or by volume relative to the total composition of the mortar. Only the percentage of pozzolanic agent is expressed relative to the amount of inorganic binder, since part of it is substituted by this agent.
- the mortar is lightened and has a density of less than 300 kg / m 3 in the cured state.
- the density measurement is performed after setting, hardening and drying the mortar.
- lightlyened mortar it is understood that it is a mortar of low density, and comprising a large amount of air. Relief can be obtained in different ways.
- composition lightening fillers whose bulk density, that is to say the mass of material contained in a given volume, comprising the volume of interstitial air is conventionally less than 300 kg / m 3
- another way to alleviate the mortar is used in the form of foam, or by introducing into the composition of a preformed foam, as described for example in patent application WO 2011/095718, or by introducing into its composition of a so-called "porogenic" agent, creating pores during its decomposition as for example described in application EP0485814.
- the different ways of lightening the mortar can be combined with each other.
- the mortar according to the present invention comprises at least 70% by volume of leaching fillers having a thermal conductivity of less than 55 mW / m.K., relative to the composition of the mortar.
- the said lightening fillers are chosen from expanded polystyrene, aerogels, hollow glass microspheres, expanded glass beads, cenospheres, vermiculite and perlite.
- the term of lightening loads it is understood that it is a component for lightening the mortar, without playing any role of binder.
- the mortar according to the present invention comprises
- the composition of the mortar has the advantage of being able to be applied manually and projected onto the surfaces to be coated with conventional projection machines. Ble presents a good maneuverability and makes it possible to obtain coatings having good mechanical resistance, in particular with cracks.
- the mortar is both lightened and insulating.
- the solution provided by the present invention is very easy to implement and can in particular be used for existing constructions, particularly in the field of renovation.
- This mortar composition thus makes it possible to have a low thermal conductivity, without causing a decrease in mechanical performance.
- the presence of pozzolanic agent in the important proportions described above makes it possible in particular to obtain this compromise.
- rheological adjuvant advantageously gives the mortar good handling and thixotropic consistency for use in vertical.
- polymeric adjuvant advantageously gives the mortar the desired mechanical strength, as well as good cohesion.
- This additive makes it possible in particular to improve the resistance to cracking.
- the binder making it possible to ensure the cohesion of the various constituents of the mortar and its hardening is a mixture comprising cement and / or lime, and a pozzolanic agent.
- a pozzolanic agent In order to obtain the desired properties from a thermal and mechanical point of view, it is essential that the amount of pozzolanic agent is sufficient.
- At least 10% of the inorganic binder selected from cement and lime is substituted by a pozzolanic agent.
- the total amount of binder present in the mortar composition is between 50 and 95% by weight of the mortar composition.
- the mortar may comprise a blowing agent for releasing air and thus increasing the porosity of the mortar during its shaping.
- the decomposition of the blowing agent is generally carried out when this agent comes into contact with a decomposition catalyst.
- the blowing agent may be based on peroxides, aluminum powder or any other component known for its decomposition capabilities.
- the presence of this pore-forming agent can be the means of lightening the mortar. It is also possible that the mortar comprises both lightening fillers and a blowing agent.
- the cement used in the mortar according to the present invention is chosen from Port I and cements, pozzolanic mixture cements possibly comprising fly ash, blast furnace slag, silica fume and / or natural pozzolans, calcined or synthetic materials, aluminous cements, sulphoaluminous cements, crushed industrial residues, belitic cements, alone or as a mixture.
- the presence of the pozzolanic agent is necessary regardless of the type of inorganic binder used in the mortar to achieve the desired performance. Even if the inorganic binder comprises a pozzolanic mixture cement, at least 10% of this binder is substituted by the pozzolanic agent.
- the pozzolanic agent is selected from metakaolin, blast furnace slags, fly ash, silica fumes.
- the pozzolanic agent is chosen from metakaolin and blast furnace slags. These agents have the advantage of being able to react with the free lime generated during the hydration reaction of the cement to form stable hydration products and thus to improve the mechanical properties.
- the minimum amount of pozzolanic agent to achieve the desired mechanical and thermal performance varies depending on the type of agent. According to one embodiment, at least 25% by weight of the inorganic binder is substituted with metakaolin. According to another embodiment, at least 15% by weight of the inorganic binder is substituted by blast furnace slags.
- the lime can be hydraulic or aerial.
- the binder consists of cement, lime and pozzolanic agent in the following proportions: it is a mixture of 20 to 70% by weight of cement, from 0 to 50% by weight of lime and 3 to 50% weight pozzolanic agent, relative to the total composition of the mortar. Even more preferably, the binder consists of a mixture of 30 to 60% by weight of cement, 20 to 40% by weight of lime and 5 to 25% by weight of pozzolanic agent, relative to the total composition of the mortar.
- the polymeric adjuvant is a redispersible polymer powder and / or a latex.
- redispersible polymer powder is understood to mean a polymer powder which, when mixed with an aqueous medium, splits into small particles, forming a stable dispersion in water.
- polymers used in the composition of such a powder mention may be made of vinyl and / or acrylic polymers.
- latex refers in particular to the latex polymers usually used in building materials.
- latex means an emulsion or aqueous dispersion of one or more natural or synthetic polymeric substances. For example, elastomeric latexes, thermoplastic latices and thermosetting latices may be mentioned.
- polyethylene polyisoprene, polystyrene, polyvinyl chloride, polybutadienes, alkali metal polyacrylates, polyacrylic acid, polymethylmethacrylate, polyvinyl acetate and polylaurate.
- the polymeric adjuvant is at least 2% by weight, preferably at least 7% by weight of the total composition of the mortar.
- the rheological adjuvant present in the mortar according to the present invention is chosen from cellulose ethers, starch ethers and their mixtures, such as ethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxyethyl methahyl cel I ulose,
- ⁇ hydroxypropylmethyl cellulose It preferably represents between 0.4% by weight and 1.5% by weight of the total composition of the mortar.
- the mortar may comprise aggregates, aggregates or sands, playing in particular on the rheology, the thickness, the hardness, the final appearance and the permeability of the mortar. They are generally formed of siliceous sand, limestone and / or if lic-limestone, generally having a particle size of between 100 ⁇ and 5 mm. The rate of such aggregates can represent between 0 and 10% by weight relative to the total composition of the mortar.
- the mortar may comprise inert fillers, also called fillers, limestone and / or siliceous being generally in the form of powder whose particle size is less than 120 ⁇ . The level of fillers in the mortar composition represents between 0 and 20% by weight relative to the total composition of the mortar.
- the mortar according to the invention may also comprise additives or adjuvants conferring particular properties. They are chosen from rheological agents such as plasticizers or superplasticizers, water-retaining agents, thickening agents, biocidal protective agents, dispersing agents, pigments, accelerators and / or retarders, hydrophobic agents, and other agents to improve the setting, hardening and / or stability of the mortar or concrete after application, to adjust the color, the workability, the implementation or the impermeability.
- rheological agents such as plasticizers or superplasticizers, water-retaining agents, thickening agents, biocidal protective agents, dispersing agents, pigments, accelerators and / or retarders, hydrophobic agents, and other agents to improve the setting, hardening and / or stability of the mortar or concrete after application, to adjust the color, the workability, the implementation or the impermeability.
- the total content of additives typically varies between 0.1 and 5% by weight.
- the mortar according to the present invention is in the form of a dry mixture, preferably in a ready-to-mix form. Once the mixing with the mixing water is carried out, the mortar thus becomes applicable to the surface to be coated. The application can be done manually or by projection.
- the mortar according to the present invention has the advantage of being projectable on the surface.
- the present invention also relates to a coating or wall coating obtained by applying the tempered mortar described above.
- the coating is deposited on all or part of a support such as a wall or building facade in the form of one or more layers.
- the total thickness of the coating can vary between 1 and 12 cm.
- the coating has a compressive strength of at least
- the coating has a compressive strength of at least 0.4 MPa and a thermal conductivity less than or equal to
- the support on which the tempered mortar is applied can be made of different materials, such as concrete, brick, plate, cement, polystyrene board, wood, fiber cement, rock wool or glass wool, blocks, blocks, etc.
- the application can be carried out directly on the support or after application of an adhesion primer if necessary.
- the coating according to the present invention can be integrated into any external thermal insulation process and meets the safety standards in this field. It has the advantage of being a continuous coating, which avoids thermal bridges. It notably has a durability and an aging compatible with its use as a facade mortar, presenting no degradation or cracks at the end of the aging cycles described by the EOTA guide used for external thermal insulation processes with mortar and / or at the end of the artificial aging tests according to NF T 30-049, NF P 84-402 and / or EN1015-21 standards.
- Two mortar formulations according to the present invention are made by mixing the various constituents given in Table 1 in a Hobart type mixer.
- Composition 1 comprises a mineral binder consisting of a mixture of cement, metakaolin (pozzolanic agent) and aerial lime.
- Composition 2 comprises a mineral binder consisting of a mixture of cement, slag (pozzolanic agent) and hydraulic lime.
- Composition A1 Composition A2
- the mortars are prepared by mixing the various constituents with water.
- the fresh dough is poured into appropriate molds and then matured for 28 days (at a temperature of 22 ° C and 55% relative humidity) before undergoing final drying in an oven at 70 ° C for several days until stability of the mass of the sample (corresponding to the elimination of free water).
- the thermal conductivity is then determined on 25x25x4 cm samples, using a TCA 300DT conductivity meter from Taurus Instruments GmbH, in accordance with EN NF 12664.
- Mortar formulations not in accordance with the invention were prepared in the same manner as in Example 1, and are described in Table 3 below.
- Composition C2 55 0.5 250
- Composition C3 54 0.36 236
- Table 4 Composition C1 serves as a reference.
- the amount of expanded polystyrene beads increases in the formulation of the mortar, it is found that the thermal conductivity is improved since it decreases, to the detriment of the mechanical strength which falls below 0.3 MPa.
- Composition C6 is a formulation comprising a large quantity of expanded polystyrene beads and also polymeric additives: the thermal conductivity is improved but the mechanical strength does not exceed 0.3 MPa.
- the amount of metakaolin represents 7% by weight of the total composition: even if the thermal conductivity is improved with respect to the composition C5, the mechanical strength remains around 0.3 MPa.
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201480019697.5A CN105050981A (zh) | 2013-04-04 | 2014-04-02 | 保温砂浆组合物 |
SG11201508191VA SG11201508191VA (en) | 2013-04-04 | 2014-04-02 | Insulating mortar composition |
BR112015024596-0A BR112015024596B1 (pt) | 2013-04-04 | 2014-04-02 | Argamassa isolante reduzida no peso e revestimento isolante |
EP14722256.6A EP2981512A1 (fr) | 2013-04-04 | 2014-04-02 | Composition de mortier isolant |
MYPI2015703488A MY189772A (en) | 2013-04-04 | 2014-04-02 | Insulating mortar composition |
RU2015147154A RU2662741C2 (ru) | 2013-04-04 | 2014-04-02 | Состав изоляционного строительного раствора |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FR1353034 | 2013-04-04 | ||
FR1353034A FR3004177B1 (fr) | 2013-04-04 | 2013-04-04 | Composition de mortier isolant |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2014162097A1 true WO2014162097A1 (fr) | 2014-10-09 |
Family
ID=48699086
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/FR2014/050784 WO2014162097A1 (fr) | 2013-04-04 | 2014-04-02 | Composition de mortier isolant |
Country Status (9)
Country | Link |
---|---|
EP (1) | EP2981512A1 (es) |
CN (1) | CN105050981A (es) |
AR (1) | AR095692A1 (es) |
BR (1) | BR112015024596B1 (es) |
FR (1) | FR3004177B1 (es) |
MY (1) | MY189772A (es) |
RU (1) | RU2662741C2 (es) |
SG (1) | SG11201508191VA (es) |
WO (1) | WO2014162097A1 (es) |
Cited By (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN105298012A (zh) * | 2015-10-16 | 2016-02-03 | 江苏长达环保节能科技有限公司 | 防火免拆锚固现浇砼复合模制保温板 |
CN106082882A (zh) * | 2016-06-29 | 2016-11-09 | 北京住总商品混凝土中心 | 一种高强度保温混凝土及其制备方法 |
WO2017032412A1 (en) * | 2015-08-26 | 2017-03-02 | Siraso Ab | Lightweight concrete and manufacturing method |
EP3162777A1 (de) * | 2015-10-29 | 2017-05-03 | STO SE & Co. KGaA | Ausblühreduzierte bindemittelzusammensetzung mit günstiger co2 bilanz |
WO2017071722A1 (en) * | 2015-10-29 | 2017-05-04 | Knauf Gips Kg | Mineral sealing mortar |
WO2017077246A1 (fr) * | 2015-11-03 | 2017-05-11 | Parexgroup Sa | Composition de construction seche projetable en voie humide a l'aide d'une pompe a vis et comprenant un liant et une charge biosourcee - preparation et applications d'une telle composition |
CN106752431A (zh) * | 2016-12-07 | 2017-05-31 | 长江大学 | 一种薄涂型水性保温隔热涂料及其制备方法 |
US20170152182A1 (en) * | 2014-06-20 | 2017-06-01 | Ceves-Vergeer Bv | Dry mortar mixture with grains of expanded glass |
RU2637542C1 (ru) * | 2016-10-24 | 2017-12-05 | федеральное государственное бюджетное образовательное учреждение высшего образования "Белгородский государственный технологический университет им. В.Г. Шухова" | Теплоизоляционный раствор пониженной плотности |
FR3055133A1 (fr) * | 2016-08-19 | 2018-02-23 | Akta Sas | Composition de liant pour un beton de faible densite, tel qu'un beton de chanvre, et beton correspondant |
RU2646281C1 (ru) * | 2017-02-21 | 2018-03-02 | Федеральное государственное автономное образовательное учреждение высшего образования "Дальневосточный федеральный университет" (ДВФУ) | Вяжущее |
US20180148376A1 (en) * | 2015-05-31 | 2018-05-31 | Besim Pty Ltd | Thermally insulating material |
RU2674484C1 (ru) * | 2018-01-22 | 2018-12-11 | федеральное государственное автономное образовательное учреждение высшего образования "Южно-Уральский государственный университет (национальный исследовательский университет") | Сырьевая смесь для жаростойкого теплоизоляционного торкрет-бетона |
WO2021008765A1 (de) * | 2019-07-12 | 2021-01-21 | Franken Maxit Mauermörtel GmbH & Co. | Trockenputzmischung für eine spritzbare dämmung |
BE1028231B1 (nl) * | 2020-10-21 | 2021-11-23 | Aerobel Bv | Samenstelling van een isolatiemateriaal en een vast isolatiemateriaal op zich |
EP3907204A4 (en) * | 2019-01-02 | 2022-03-02 | Shanghai Shengkui Products Co., Ltd | RAW MATERIAL COMPOSITION FOR THERMAL INSULATION PANELS, THERMAL INSULATION PANELS AND PROCESS FOR THE MANUFACTURE OF THERMAL INSULATION PANELS |
WO2022175442A1 (de) * | 2021-02-19 | 2022-08-25 | Glasmit Ip Gmbh I. G. | Wärmedämmender putz |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
AU2017269603B2 (en) * | 2016-05-24 | 2020-07-02 | 2581776 Ontario Inc. | Lightweight concrete formulations |
CN106747589A (zh) * | 2017-01-26 | 2017-05-31 | 北京万源恒泰科技有限公司 | 一种蜂窝保温砂浆及其生产线的混料装置 |
CN108585705A (zh) * | 2018-07-27 | 2018-09-28 | 芜湖市棠华建材科技有限公司 | 一种改性玻璃微珠保温砂浆及其制备方法 |
CN108947569B (zh) * | 2018-08-30 | 2021-10-01 | 盛世瑶兰(深圳)科技有限公司 | 一种高强度空心隔热建筑材料及其应用 |
CN110330288A (zh) * | 2019-06-12 | 2019-10-15 | 江苏洋河新城新材料有限责任公司 | 一种地面保温砂浆及其制备方法 |
AU2022305107A1 (en) * | 2021-06-30 | 2023-12-07 | Sika Technology Ag | Cement slurry composition |
CN114956716B (zh) * | 2022-04-15 | 2023-03-17 | 武昌理工学院 | 轻质复合建筑外墙保温材料及其制备方法 |
Citations (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0485814A1 (de) | 1990-11-06 | 1992-05-20 | Wachter KG.Hindelang Baustoffwerk Bautechnik | Werktrockenmörtel für erhöhten Porengehalt |
WO1995026323A1 (fr) * | 1994-03-29 | 1995-10-05 | Thierry Lefebvre | Materiau composite allege et insonorisant a matrice minerale hydraulique et procede d'elaboration d'un tel materiau |
CN101033124A (zh) * | 2007-02-09 | 2007-09-12 | 上海大学 | 利用固体废弃物制备保温砂浆的方法 |
DE102006019056A1 (de) * | 2006-04-25 | 2007-10-31 | Schwenk Putztechnik Gmbh & Co. Kg | Verwendung einer Mörtelmischung als Ansetzmörtel |
FR2942473A1 (fr) * | 2009-02-26 | 2010-08-27 | Saint Gobain Weber France | Mortier isolant pulverulent, mortier isolant en couche |
CN101921091A (zh) * | 2010-06-29 | 2010-12-22 | 上海大学 | 利用废弃聚氨酯泡沫塑料制备干粉保温材料的方法 |
CN102010166A (zh) * | 2010-11-18 | 2011-04-13 | 重庆思贝肯节能技术开发有限公司 | 一种微膨胀无机保温砂浆制备方法 |
CN102093020A (zh) * | 2010-12-03 | 2011-06-15 | 吉林省志惠防腐保温工程有限公司 | 聚氨酯专用轻质防火防水保温浆料 |
FR2955790A1 (fr) * | 2010-02-03 | 2011-08-05 | Saint Gobain Weber | Procede de projection d'un materiau mousse et revetement obtenu a partir d'un tel procede |
EP2404885A2 (de) * | 2010-07-06 | 2012-01-11 | Quick-Mix Gruppe Gmbh & Co. Kg | Neue Baustoffmischungen |
EP2476659A1 (en) * | 2010-07-08 | 2012-07-18 | Shenzhen Grandland Decoration Group Co., Ltd. | Light-weight and energy-saving plastering mortar and construction method thereof |
CN101575191B (zh) * | 2008-05-08 | 2012-09-05 | 四川蜂巢科技有限公司 | 一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺 |
Family Cites Families (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2134666C1 (ru) * | 1997-05-15 | 1999-08-20 | Открытое акционерное общество Московского института материаловедения и эффективных технологий (ОАО "Московский ИМЭТ") | Изоляционно-декоративная штукатурная смесь |
RU2002113323A (ru) * | 2002-05-21 | 2004-02-27 | ОАО Всероссийский федеральный технологический институт "ВНИИЖЕЛЕЗОБЕТОН" | Сырьевая смесь для получения штукатурного покрытия |
RU2307809C1 (ru) * | 2006-02-01 | 2007-10-10 | Общество с ограниченной ответственностью "Органикс-Кварц" | Сухая строительная смесь (варианты) |
EA017880B1 (ru) * | 2009-10-27 | 2013-03-29 | Компания "Матанат А" | Сухая декоративно-отделочная смесь |
-
2013
- 2013-04-04 FR FR1353034A patent/FR3004177B1/fr active Active
-
2014
- 2014-03-20 AR ARP140101304A patent/AR095692A1/es active IP Right Grant
- 2014-04-02 BR BR112015024596-0A patent/BR112015024596B1/pt active IP Right Grant
- 2014-04-02 MY MYPI2015703488A patent/MY189772A/en unknown
- 2014-04-02 EP EP14722256.6A patent/EP2981512A1/fr active Pending
- 2014-04-02 RU RU2015147154A patent/RU2662741C2/ru active
- 2014-04-02 CN CN201480019697.5A patent/CN105050981A/zh active Pending
- 2014-04-02 SG SG11201508191VA patent/SG11201508191VA/en unknown
- 2014-04-02 WO PCT/FR2014/050784 patent/WO2014162097A1/fr active Application Filing
Patent Citations (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0485814A1 (de) | 1990-11-06 | 1992-05-20 | Wachter KG.Hindelang Baustoffwerk Bautechnik | Werktrockenmörtel für erhöhten Porengehalt |
WO1995026323A1 (fr) * | 1994-03-29 | 1995-10-05 | Thierry Lefebvre | Materiau composite allege et insonorisant a matrice minerale hydraulique et procede d'elaboration d'un tel materiau |
DE102006019056A1 (de) * | 2006-04-25 | 2007-10-31 | Schwenk Putztechnik Gmbh & Co. Kg | Verwendung einer Mörtelmischung als Ansetzmörtel |
CN101033124A (zh) * | 2007-02-09 | 2007-09-12 | 上海大学 | 利用固体废弃物制备保温砂浆的方法 |
CN101575191B (zh) * | 2008-05-08 | 2012-09-05 | 四川蜂巢科技有限公司 | 一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺 |
FR2942473A1 (fr) * | 2009-02-26 | 2010-08-27 | Saint Gobain Weber France | Mortier isolant pulverulent, mortier isolant en couche |
WO2011095718A1 (fr) | 2010-02-03 | 2011-08-11 | Saint-Gobain Weber | Procede de projection d'un materiau mousse et revetement obtenu a partir d'un tel procede |
FR2955790A1 (fr) * | 2010-02-03 | 2011-08-05 | Saint Gobain Weber | Procede de projection d'un materiau mousse et revetement obtenu a partir d'un tel procede |
CN101921091A (zh) * | 2010-06-29 | 2010-12-22 | 上海大学 | 利用废弃聚氨酯泡沫塑料制备干粉保温材料的方法 |
EP2404885A2 (de) * | 2010-07-06 | 2012-01-11 | Quick-Mix Gruppe Gmbh & Co. Kg | Neue Baustoffmischungen |
EP2476659A1 (en) * | 2010-07-08 | 2012-07-18 | Shenzhen Grandland Decoration Group Co., Ltd. | Light-weight and energy-saving plastering mortar and construction method thereof |
CN102010166A (zh) * | 2010-11-18 | 2011-04-13 | 重庆思贝肯节能技术开发有限公司 | 一种微膨胀无机保温砂浆制备方法 |
CN102093020A (zh) * | 2010-12-03 | 2011-06-15 | 吉林省志惠防腐保温工程有限公司 | 聚氨酯专用轻质防火防水保温浆料 |
Cited By (25)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10662115B2 (en) | 2014-06-20 | 2020-05-26 | Ceves-Vergeer Bv | Dry mortar mixture with grains of expanded glass |
US10364186B2 (en) * | 2014-06-20 | 2019-07-30 | Ceves-Vergeer Bv | Dry mortar mixture with grains of expanded glass |
US20170152182A1 (en) * | 2014-06-20 | 2017-06-01 | Ceves-Vergeer Bv | Dry mortar mixture with grains of expanded glass |
US20180148376A1 (en) * | 2015-05-31 | 2018-05-31 | Besim Pty Ltd | Thermally insulating material |
WO2017032412A1 (en) * | 2015-08-26 | 2017-03-02 | Siraso Ab | Lightweight concrete and manufacturing method |
JP2018528920A (ja) * | 2015-08-26 | 2018-10-04 | シラソ エービー | 軽量コンクリートおよび製造方法 |
CN105298012A (zh) * | 2015-10-16 | 2016-02-03 | 江苏长达环保节能科技有限公司 | 防火免拆锚固现浇砼复合模制保温板 |
EP3162777A1 (de) * | 2015-10-29 | 2017-05-03 | STO SE & Co. KGaA | Ausblühreduzierte bindemittelzusammensetzung mit günstiger co2 bilanz |
WO2017071722A1 (en) * | 2015-10-29 | 2017-05-04 | Knauf Gips Kg | Mineral sealing mortar |
EP3640224A1 (de) * | 2015-10-29 | 2020-04-22 | STO SE & Co. KGaA | Ausblühreduzierte bindemittelzusammensetzung mit günstiger co2 bilanz |
GB2557859A (en) * | 2015-11-03 | 2018-06-27 | Parexgroup Sa | Dry construction composition wet-sprayable by means of a screw pump and containing a binder and a biosourced filler, and preparation and uses of such |
WO2017077246A1 (fr) * | 2015-11-03 | 2017-05-11 | Parexgroup Sa | Composition de construction seche projetable en voie humide a l'aide d'une pompe a vis et comprenant un liant et une charge biosourcee - preparation et applications d'une telle composition |
ES2676912R1 (es) * | 2015-11-03 | 2018-09-21 | Parexgroup Sa | Composición de construcción seca proyectable en vía húmeda con la ayuda de una bomba a tornillo y que comprende un ligante y una carga de origen biológico - preparación y aplicación de dicha composición |
US11845696B2 (en) | 2015-11-03 | 2023-12-19 | Parexgroup Sa | Dry construction composition wet-sprayable by means of a screw pump and containing a binder and a biosourced filler, and preparation and uses of such a composition |
CN106082882A (zh) * | 2016-06-29 | 2016-11-09 | 北京住总商品混凝土中心 | 一种高强度保温混凝土及其制备方法 |
FR3055133A1 (fr) * | 2016-08-19 | 2018-02-23 | Akta Sas | Composition de liant pour un beton de faible densite, tel qu'un beton de chanvre, et beton correspondant |
RU2637542C1 (ru) * | 2016-10-24 | 2017-12-05 | федеральное государственное бюджетное образовательное учреждение высшего образования "Белгородский государственный технологический университет им. В.Г. Шухова" | Теплоизоляционный раствор пониженной плотности |
CN106752431A (zh) * | 2016-12-07 | 2017-05-31 | 长江大学 | 一种薄涂型水性保温隔热涂料及其制备方法 |
RU2646281C1 (ru) * | 2017-02-21 | 2018-03-02 | Федеральное государственное автономное образовательное учреждение высшего образования "Дальневосточный федеральный университет" (ДВФУ) | Вяжущее |
RU2674484C1 (ru) * | 2018-01-22 | 2018-12-11 | федеральное государственное автономное образовательное учреждение высшего образования "Южно-Уральский государственный университет (национальный исследовательский университет") | Сырьевая смесь для жаростойкого теплоизоляционного торкрет-бетона |
EP3907204A4 (en) * | 2019-01-02 | 2022-03-02 | Shanghai Shengkui Products Co., Ltd | RAW MATERIAL COMPOSITION FOR THERMAL INSULATION PANELS, THERMAL INSULATION PANELS AND PROCESS FOR THE MANUFACTURE OF THERMAL INSULATION PANELS |
WO2021008765A1 (de) * | 2019-07-12 | 2021-01-21 | Franken Maxit Mauermörtel GmbH & Co. | Trockenputzmischung für eine spritzbare dämmung |
BE1028231B1 (nl) * | 2020-10-21 | 2021-11-23 | Aerobel Bv | Samenstelling van een isolatiemateriaal en een vast isolatiemateriaal op zich |
WO2022084898A1 (en) * | 2020-10-21 | 2022-04-28 | Aerobel Bv | Composition of an insulation material and a solid insulation material in itself |
WO2022175442A1 (de) * | 2021-02-19 | 2022-08-25 | Glasmit Ip Gmbh I. G. | Wärmedämmender putz |
Also Published As
Publication number | Publication date |
---|---|
RU2015147154A3 (es) | 2018-03-01 |
CN105050981A (zh) | 2015-11-11 |
FR3004177B1 (fr) | 2015-11-20 |
MY189772A (en) | 2022-03-04 |
RU2015147154A (ru) | 2017-05-15 |
SG11201508191VA (en) | 2015-11-27 |
BR112015024596A2 (pt) | 2017-07-18 |
EP2981512A1 (fr) | 2016-02-10 |
FR3004177A1 (fr) | 2014-10-10 |
BR112015024596B1 (pt) | 2021-09-08 |
RU2662741C2 (ru) | 2018-07-30 |
AR095692A1 (es) | 2015-11-04 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2014162097A1 (fr) | Composition de mortier isolant | |
EP2401239B1 (fr) | Mortier isolant pulverulent, mortier isolant en couche | |
EP2822911B1 (fr) | Composition seche a base de liant mineral et destinee a la preparation d'une formulation humide durcissable pour le batiment | |
EP3442929A1 (fr) | Composition de mortier fortement allege et isolant thermique | |
JP5026250B2 (ja) | 軽量モルタル | |
WO2013131584A1 (fr) | Utilisation d'au moins un polymere superabsorbant -psa- (b), dans une composition seche a base de liant mineral et destinee a la preparation d'une formulation humide durcissable pour le batiment | |
EP2523928A1 (fr) | Adjuvant moussant pour la preparation de mousses minerales d'enduits, de mortiers et betons, mousses ainsi obtenues et produits durcis issus de ces mousses | |
EP3778524A1 (fr) | Enduit isolant a base de xerogel de silice | |
MX2013013835A (es) | Compuestos de eter de celulosa para desempeño de temperatura caliente mejorado en morteros de sistemas de acabado de aislamiento externo (eifs). | |
FR2973024A1 (fr) | Composition cimentaire seche pour la preparation d'une formulation humide d'enduit, de mortier ou de beton sans efflorescence | |
JP4947716B2 (ja) | 建築用セメントモルタル | |
JP2009096657A (ja) | 左官用セメントモルタル | |
EP3325424A1 (fr) | Procede de preparation d'un béton ou mortier allegé contenant de la glycerine | |
EP0760806A1 (fr) | Materiau composite allege et insonorisant a matrice minerale hydraulique et procede d'elaboration d'un tel materiau | |
EP2531462B1 (fr) | Procede de projection d'un materiau mousse et revetement obtenu a partir d'un tel procede | |
CN108285308A (zh) | 一种保温砂浆、保温层结构及保温外墙体结构 | |
JP2009137787A (ja) | 低温用軽量モルタル | |
JP2002293601A (ja) | 軽量モルタル材の製造方法 | |
CN110642584A (zh) | 一种轻质隔音高弹性胶泥及其制备方法 | |
JP2013119498A (ja) | ポリマーセメントモルタル及び補修用モルタル | |
RU2708138C1 (ru) | Смесь для изготовления цементсодержащего строительного материала | |
JP2017114735A (ja) | 仕上用モルタル | |
RU2168479C2 (ru) | Состав раствора для герметизации стыков | |
CN113121164A (zh) | 一种防水抗裂抹面砂浆及其加工方法 | |
CN116102287A (zh) | 一种建筑用粘结材料及其制备方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 201480019697.5 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 14722256 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: P1319/2015 Country of ref document: AE Ref document number: 2014722256 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: IDP00201506187 Country of ref document: ID |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 2015147154 Country of ref document: RU Kind code of ref document: A |
|
REG | Reference to national code |
Ref country code: BR Ref legal event code: B01A Ref document number: 112015024596 Country of ref document: BR |
|
ENP | Entry into the national phase |
Ref document number: 112015024596 Country of ref document: BR Kind code of ref document: A2 Effective date: 20150924 |