CN101575191B - 一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺 - Google Patents

一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺 Download PDF

Info

Publication number
CN101575191B
CN101575191B CN200810044375A CN200810044375A CN101575191B CN 101575191 B CN101575191 B CN 101575191B CN 200810044375 A CN200810044375 A CN 200810044375A CN 200810044375 A CN200810044375 A CN 200810044375A CN 101575191 B CN101575191 B CN 101575191B
Authority
CN
China
Prior art keywords
percent
expanded
construction wall
component
vitrified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200810044375A
Other languages
English (en)
Other versions
CN101575191A (zh
Inventor
夏广
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan honeycomb building material Co., Ltd.
Original Assignee
SICHUAN BEEHIVE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SICHUAN BEEHIVE TECHNOLOGY Co Ltd filed Critical SICHUAN BEEHIVE TECHNOLOGY Co Ltd
Priority to CN200810044375A priority Critical patent/CN101575191B/zh
Publication of CN101575191A publication Critical patent/CN101575191A/zh
Application granted granted Critical
Publication of CN101575191B publication Critical patent/CN101575191B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺。本发明中的膨胀玻化微珠保温材料包括的组份及各组份的质量百分比如下：水泥30—60％，聚丙烯酰胺0.1—0.3％，乳胶粉1—4％，粉煤灰10—40％，氢氧化钙8—12％，木质纤维5—10％，早强剂0.2—0.5％，聚丙烯纤维2—4％，纤维素醚3—6％，膨胀玻化微珠30—60％，引气剂0.1—0.3％，膨润土1—2％，其中各组分之和为100％。本发明充分利用膨胀玻化微珠与墙体相容性好且导热系数低这一特点，具有生产工艺简单、效率高的优点；具有优良的防火性能；可广泛应用于建筑墙体保温隔热，无污染且节能环保。

Description

一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺
技术领域
本发明涉及一种墙体保温材料，尤其涉及一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺，属于墙体保温材料的生产领域。
背景技术
近年来，环保和节能作为各生产领域的主导思想已被广泛接纳，各领域的环保、节能型产品也相继出现，国家也大力鼓励企业生产环保、节能型产品。现有的建筑墙体的保温材料一般为聚苯乙烯颗粒、膨胀聚苯板、挤塑聚苯板或其它砌块，施工时将这些保温材料贴或抹在主墙体上，成为墙体保温层，其优点是材料自身的保温隔热效果好，保温层的厚度能很好控制。但这种方式随着对建筑要求的提高和新材料的出现，弊端也不断显漏出来：一是在施工时，操作配料的人为因素多，使材料的一致性差，质量得不到保证；二是受温度、气候的影响大，粘结牢固性差；三是防火性能差。
发明内容
本发明的目的是为了解决上述问题而提供一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺，这种保温材料与墙体的粘结性好，成型后受气候、温度的影响较小，具有优良的防火性能，而且节能、环保。
本发明是通过以下技术方案来实现上述目的的：
本发明中的膨胀玻化微珠保温材料包括的组份及各组份的质量百分比如下：
Figure GSB00000687639500011
Figure GSB00000687639500021
作为本发明中膨胀玻化微珠保温材料的最佳技术方案，其包括的组份及各组份的质量百分比如下：
作为本发明中膨胀玻化微珠保温材料的各组份的具体要求，所述水泥为32.5R复合硅酸盐水泥；所述乳胶粉是可再分散乳胶粉；所述氢氧化钙中CaO的含量为50——90％；所述木质纤维的直径为40——100mm；所述早强剂是甲酸钙；所述膨润土为400目型号；所述引气剂是十二醇硫酸钠；所述聚丙烯纤维为6——8μm；所述纤维素醚是甲基羟丙基纤维素；所述膨胀玻化微珠的闭孔率≥80％。
本发明中膨胀玻化微珠保温材料的生产工艺是：先将称好量的水泥、聚丙烯酰胺、乳胶粉、粉煤灰、氢氧化钙、木质纤维、早强剂、聚丙烯纤维、纤维素醚、引气剂、膨润土放入搅拌机搅拌均匀，再将称好量的膨胀玻化微珠放入搅拌机搅拌均匀；将上述搅拌均匀的混合物包装后成为干拌型保温材料。在使用时，只需将干拌型材料加水搅拌均匀即可，非常方便。
本发明的有益效果在于：
本发明充分利用膨胀玻化微珠与墙体相容性好且导热系数低这一特点，具有生产工艺简单、效率高的优点；与墙体的粘结效果好，成型后受气候、温度的影响很小；具有优良的防火性能；可广泛应用于建筑墙体保温隔热，隔热保温效果好且无污染、节能环保。
具体实施方式
下面结合实施例对本发明作进一步具体描述：
实施例1：选用以下组份及各组份的质量百分比的原材料加工保温材料：
Figure GSB00000687639500031
Figure GSB00000687639500041
在生产过程中，先将称好量的水泥、聚丙烯酰胺、乳胶粉、粉煤灰、氢氧化钙、木质纤维、早强剂、聚丙烯纤维、纤维素醚、引气剂、膨润土放入搅拌机搅拌均匀，再将称好量的膨胀玻化微珠放入搅拌机搅拌均匀；将上述搅拌均匀的混合物包装后成为干拌型保温材料。在使用时，只需将干拌型材料加水搅拌均匀即可，非常方便。
实施例2：选用以下组份及各组份的质量百分比的原材料加工保温材料：
Figure GSB00000687639500042
生产方法与实施例1相同，此略。
实施例3：选用以下组份及各组份的质量百分比的原材料加工保温材料：
Figure GSB00000687639500051
生产方法与实施例1相同，此略。

Claims (4)

1.一种用于建筑墙体的膨胀玻化微珠保温材料，其特征在于：其包括的组份及各组份的质量百分比如下：
Figure FSB00000687639400011
2.根据权利要求1所述的用于建筑墙体的膨胀玻化微珠保温材料，其特征在于：其包括的组份及各组份的质量百分比如下：
Figure FSB00000687639400012
Figure FSB00000687639400021
3.根据权利要求1或2所述的用于建筑墙体的膨胀玻化微珠保温材料，其特征在于：所述水泥为32.5R复合硅酸盐水泥；所述乳胶粉是可再分散乳胶粉；所述氢氧化钙中CaO的含量为50——90％；所述木质纤维的直径为40——100mm；所述早强剂是甲酸钙；所述膨润土为400目型号；所述引气剂是十二醇硫酸钠；所述聚丙烯纤维为6——8μm；所述纤维素醚是甲基羟丙基纤维素；所述膨胀玻化微珠的闭孔率≥80％。
4.一种如权利要求1所述的用于建筑墙体的膨胀玻化微珠保温材料的生产工艺，其特征在于：先将称好量的水泥、聚丙烯酰胺、乳胶粉、粉煤灰、氢氧化钙、木质纤维、早强剂、聚丙烯纤维、纤维素醚、引气剂、膨润土放入搅拌机搅拌均匀，再将称好量的膨胀玻化微珠放入搅拌机搅拌均匀；将上述搅拌均匀的混合物包装后成为干拌型保温材料。
CN200810044375A 2008-05-08 2008-05-08 一种用于建筑墙体的膨胀玻化微珠保温材料及生产工艺 Expired - Fee Related CN101575191B (zh)