CN102584146A - 一种改性玻化微珠保温砂浆 - Google Patents

一种改性玻化微珠保温砂浆 Download PDF

Info

Publication number
CN102584146A
CN102584146A CN2012100541728A CN201210054172A CN102584146A CN 102584146 A CN102584146 A CN 102584146A CN 2012100541728 A CN2012100541728 A CN 2012100541728A CN 201210054172 A CN201210054172 A CN 201210054172A CN 102584146 A CN102584146 A CN 102584146A
Authority
CN
China
Prior art keywords
vitrified micro
thermal
insulating
improved
thermal insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100541728A
Other languages
English (en)
Inventor
赵正齐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHAN QIXIN NEW BUILDING MATERIALS CO Ltd
Original Assignee
WUHAN QIXIN NEW BUILDING MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHAN QIXIN NEW BUILDING MATERIALS CO Ltd filed Critical WUHAN QIXIN NEW BUILDING MATERIALS CO Ltd
Priority to CN2012100541728A priority Critical patent/CN102584146A/zh
Publication of CN102584146A publication Critical patent/CN102584146A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种改性波化微珠保温砂浆，其组分及各组分质量百分比为：玻化微珠：35%-55%，胶凝材料：30%-40%，粉煤灰：10%-20%，纤维素醚：0.2%-0.4%，可再分散乳胶粉0.44%-0.55%，聚丙烯纤维：0.1%-0.2%，稠化增强剂：0.2%-1%，石膏：0.1%-0.2%，膨润土：0.1%-0.2%，重钙：0.1%-0.2%。所述的胶凝材料为42.5R的普通硅酸盐水泥。所述的玻化微珠堆积密度为100-130KG/m3。所述的纤维素醚选用20万粘度羟丙基甲基纤维素醚。本发明提高了保温胶粉的和易性，使得胶粉料的各项性能得到很大的发挥。不仅增大了包裹轻质保温材料的能力，提高抗垂流能力，而且大大改善了施工性，使浆料表面平整；本发明保水性能优异，可延长操作时间，方便了工作员施工。

Description

一种改性玻化微珠保温砂浆
技术领域
本发明涉及建筑材料领域，更具体的涉及一种改性玻化微珠保温砂浆。具有性能稳定，放射性低的优点。
背景技术
近些年来，随着国内建筑节能的蓬勃发展，建筑外墙保温技术在全国范围内全面展开。各种有机、无机保温系统得到了广泛应用，保温材料种类也是琳琅满目。
由于有机保温材料诸多性能上的弊端，如耐候性差、稳定性不良、不耐火等，目前无机保温材料，尤其是玻化微珠保温砂浆在市场的应用越来越广泛。但由于之前的保温厂商甚多，而且也未形成统一的规格和标准，造成目前市面上的保温材料良莠不齐、纷繁混杂。
本发明针对市场上玻化微珠保温砂浆的粘接性差、收缩大、空鼓开裂等一些性能上的弊端，通过TL-1稠化增强剂来改进玻化微珠保温砂浆，制出了综合性能高的玻化微珠保温砂浆。
发明内容
本发明的目的在于提出了一种改性玻化微珠保温砂浆。具有性能稳定，放射性低的优点。
为实现上述目的，采用如下技术方案：
一种改性波化微珠保温砂浆，其组分及各组分质量百分比为：
玻化微珠：            35％-55％
胶凝材料：            30％-40％
粉煤灰：              10％-20％
纤维素醚：            0.2％-0.4％
可再分散乳胶粉        0.44％-0.55％
聚丙烯纤维：          0.1％-0.2％
稠化增强剂：          0.2％-1％
石膏：                0.1％-0.2％
膨润土：              0.1％-0.2％
重钙：                0.1％-0.2％。
所述的胶凝材料为42.5R的普通硅酸盐水泥。
所述的玻化微珠堆积密度为100-130KG/m3。
所述的纤维素醚选用20万粘度羟丙基甲基纤维素醚。
稠化增强剂采用TL-1稠化增强剂，TL-1是由特种胶粉及多种有机、无机保水增稠材料和粉煤灰激发剂制成的专用于保温浆料的稠化剂，因其涵盖了多种成分，能够很好的与其他配方成分结合，发挥其最大功效。所制作出来的玻化微珠保温胶粉综合性能大幅提高，性价比优。
本发明各基本性能的检测结果如下表所示：
Figure BDA0000140494170000031
与现有技术相比，本发明具有如下优点和有益效果：针对目前市场上保温材料的普遍问题，如粘性小，强度差，伸缩性大，空鼓，开裂等现象，本发明提高了保温胶粉的获益性，使得胶粉原料的各项性能得到很大的发挥。不仅增大了包裹轻质保温材料的能力，提高抗垂流能力，而且大大改善了施工性，使浆料表面平整；本发明保水性能优异，可延长操作时间，方便了工作员施工。
由上表可以看出，经过TL-1改性后的玻化微珠保温砂浆各项指标都较稳定，特别是放射性低。
综上所述，TL-1改性玻化微珠保温砂浆各项性能指标优良、稳定，符合节能环保的要求，可大规模推广应用。
具体实施方式：
实施例1：
一种改性波化微珠保温砂浆，其组分及各组分质量百分比为：玻化微珠：40％，胶凝材料：38.4％，粉煤灰：20％，纤维素醚：0.24％，短纤维：0.1％，稠化增强剂：0.3％，可再分散乳胶粉：0.6％，石膏：0.12％，膨润土：0.12％，重钙：0.12％。
实施例2：
一种改性波化微珠保温砂浆，其组分及各组分质量百分比为：玻化微珠：45％，胶凝材料：33％，粉煤灰：20.4％，纤维素醚：0.27％，短纤维：0.09％，稠化增强剂：0.44％，可再分散乳胶粉：0.44％，石膏：0.12％，膨润土：0.12％，重钙：0.12％。
上述实例便于相关工作人员用作实际操作中的参考，施工人员可根据具体施工条件适当做些更改。本发明配比有相当的发挥灵活性，可广泛推广应用。

Claims (4)

1.一种改性波化微珠保温砂浆，其组分及各组分质量百分比为：
玻化微珠：             35%—55%
胶凝材料：             30%—40%
粉煤灰：               10%—20%
纤维素醚：             0.2%—0.4%
可再分散乳胶粉         0.44%—0.55%
聚丙烯纤维：           0.1%—0.2%
稠化增强剂：           0.2%—1%
石膏：                 0.1%—0.2%
膨润土：               0.1%—0.2%
重钙：                 0.1%—0.2%。
2.如权利要求1所述的一种改性波化微珠保温砂浆，其特征在于：所述的胶凝材料为42.5R的普通硅酸盐水泥。
3.如权利要求1所述的一种改性波化微珠保温砂浆，其特征在于：所述的玻化微珠堆积密度为100—130KG/m3。
4.如权利要求1所述的一种改性波化微珠保温砂浆，其特征在于：所述的纤维素醚选用20万粘度羟丙基甲基纤维素醚。
CN2012100541728A 2012-03-05 2012-03-05 一种改性玻化微珠保温砂浆 Pending CN102584146A (zh)