CN103224363A - 一种柔性抗裂防护砂浆及其制备方法 - Google Patents
一种柔性抗裂防护砂浆及其制备方法 Download PDFInfo
- Publication number
- CN103224363A CN103224363A CN2013101283268A CN201310128326A CN103224363A CN 103224363 A CN103224363 A CN 103224363A CN 2013101283268 A CN2013101283268 A CN 2013101283268A CN 201310128326 A CN201310128326 A CN 201310128326A CN 103224363 A CN103224363 A CN 103224363A
- Authority
- CN
- China
- Prior art keywords
- cracking
- resistant protection
- break resistant
- flexible break
- protection mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种柔性抗裂防护砂浆,同时还涉及其制备方法,属于建筑材料技术领域。该柔性抗裂防护砂浆各组分重量份数为:普通硅酸盐水泥:30-50、石英砂:50-65、消石灰:5-10、抗裂纤维:3-6、可再分散乳胶粉:1.2-2.5、纤维素醚:0.2-0.5、塑性膨胀剂:0.05-0.2、憎水剂:0.3-0.6。本发明的柔性抗裂防护砂浆施工性能良好,抗折强度和抗压强度高、柔韧性好、粘结抗拉强度高、抗开裂性能良好,具有优异的防水憎水效果等特点,用于建筑墙体保温节能体系的抗裂防护,能够解决各种应力导致的干燥收缩开裂问题,在工地现场直接加水即可使用,性能良好、稳定;本发明还可用于各种新型建筑墙体材料的抹面抗裂防护施工过程,起到抗裂防护及防水作用。
Description
技术领域
本发明涉及一种砂浆,尤其是一种柔性抗裂防护砂浆,同时还涉及其制备方法,属于建筑材料技术领域。
背景技术
随着我国建筑能耗的快速上升,建筑节能已成为我国的基本国策。在诸多建筑节能技术中,应用安全高效耐久的建筑墙体保温体系是主要技术措施之一。在建筑墙体保温体系中,可以起到保护保温体系、防止外力破坏、防止水分渗透等作用的抗裂防护砂浆成为决定整个保温体系安全高效耐候的关键材料之一。
此外,我国正逐渐大力推广应用各种新型建筑墙体材料,但由于新型墙体材料多具有轻质、保温、吸水率大等特点,采用普通抹灰砂浆时易导致建筑墙体收缩开裂、渗漏渗水、空鼓等问题,因此严重制约了新型墙体材料的推广应用。
发明内容
本发明的目的在于:通过对柔性抗裂防护砂浆的组分、配比的选择、优化以及制备方法的研究,提出一种各项性能优良稳定、防水憎水和抗裂性能好的柔性抗裂防护砂浆,同时给出其制备方法,从而满足各种建筑墙体保温节能体系要求。
为了达到以上目的,本发明的柔性抗裂防护砂浆基本技术方案主要由如下重量份的组分组成:
硅酸盐水泥:30-50、石英砂:50-65、消石灰:5-10、抗裂纤维:3-6、可再分散乳胶粉:1.2-2.5、纤维素醚:0.2-0.5、塑性膨胀剂:0.05-0.2、憎水剂:0.3-0.6(总重量份100为宜)。
本发明进一步的完善包括:
所述石英砂由30-50目、40-70目、70-100目,按重量份3:4-6:1-3的比例配制而成。
所述抗裂纤维采用纤维长度≦3mm的木质素纤维,其作用是赋予柔性抗裂防护砂浆更好的抗裂性能和柔韧性能。
所述可再分散乳胶粉为乙烯-醋酸乙烯酯乳胶粉、乙烯-氯乙烯-月桂酸乙烯酯乳胶粉中的至少一种。
所述纤维素醚为黏度6000mPa.s-45000mPa.s的羟乙基甲基纤维素、羟丙基甲基纤维素中的至少一种。
所述塑性膨胀剂为粉末状改性有机酸盐基的塑性膨胀剂。
所述憎水剂为有机硅类憎水剂、渗透结晶材料中的至少一种。
本发明柔性抗裂防护砂浆的制备方法具体步骤为:按重量份称量各组分后,先将可再分散乳胶粉、纤维素醚、塑性膨胀剂、憎水剂搅拌混合均匀,然后将所得混合物与其余组分(普通硅酸盐水泥、消石灰、石英砂及木质素纤维等)搅拌混合均匀,即得所需产品。优选在先的搅拌速率为500-1000r/min,之后的搅拌速率为50-150r/min。
本发明的柔性抗裂防护砂浆成品为单组分的干混砂浆,施工时只需在施工现场将其与水按所需比例搅拌2-3min,即可使用。
本发明柔性抗裂防护砂浆的检测结果见表1。
表1柔性抗裂防护砂浆基本性能
由表1可以看出,本发明的柔性抗裂防护砂浆物理力学性能良好,完全达到甚至远远超过相关标准要求,具有良好的抗收缩开裂性能、防水性能以及柔韧性能,可以满足建筑墙体保温节能工程各种需求。
实践证明,本发明的柔性抗裂防护砂浆具有优异的施工性能,可施工时间长、施工便捷、粘结性能好、干燥收缩率低、柔韧性和防水性能俱佳、吸水率低,能抵抗各种应力导致的开裂问题,且应用范围广,不仅能用于建筑墙体保温节能工程,还能用于各种建筑墙体材料的抹面工程。
综上所述,本发明的柔性抗裂防护砂浆各性能指标优良,制备方法简便易行,产品品质易于控制,施工性能优异,柔性抗裂性能和防水憎水性能优良,适用于各种建筑保温节能体系的抗裂防护,以及各种新型墙体材料的抹面防护。
具体实施方式
下面通过实施例进一步说明本发明。
实施例一
本实施例的柔性抗裂防护砂浆重量份组分为:普通硅酸盐水泥:30.55、石英砂:58、消石灰:5、抗裂纤维:4.2、可再分散乳胶粉:1.5、纤维素醚:0.3、塑性膨胀剂:0.05、憎水剂:0.4。其中石英砂由30-50目、40-70目、70-100目按重量份2:4:1的比例配制而成;抗裂纤维采用纤维长度≦3mm的木质素纤维,其作用是赋予柔性抗裂防护砂浆更好的抗裂性能和柔韧性能;可再分散乳胶粉为乙烯-醋酸乙烯酯乳胶粉;纤维素醚为黏度6000mPa.s-45000mPa.s的羟乙基甲基纤维素;塑性膨胀剂为粉末状改性有机酸盐基的塑性膨胀剂;憎水剂为有机硅类憎水剂。
制备时,先按重量份称量各组分后,先将可再分散乳胶粉、纤维素醚、塑性膨胀剂、憎水剂搅拌混合均匀,搅拌速率为500-1000r/min然后将所得混合物与其余组分(普通硅酸盐水泥、消石灰、石英砂及木质素纤维等)搅拌混合均匀,搅拌速率为50-150r/min即得所需产品。
测试得到的性能均超过国家行业标准《无机轻集料砂浆保温系统技术规程》JGJ253-2011规定的技术指标要求以及表1的性能指标要求。
实施例二
本实施例的柔性抗裂防护砂浆重量份组分为:普通硅酸盐水泥:40、石英砂:48、消石灰:6、抗裂纤维:3.2、可再分散乳胶粉:2、纤维素醚:0.2、塑性膨胀剂:0.15、憎水剂:0.45。其中石英砂由30-50目、40-70目、70-100目按重量份3:6:3的比例配制而成;其中抗裂纤维采用纤维长度2mm左右的木质素纤维;可再分散乳胶粉为乙烯-氯乙烯-月桂酸乙烯酯乳胶粉;纤维素醚为黏度6000mPa.s-45000mPa.s的羟丙基甲基纤维素;塑性膨胀剂为粉末状改性有机酸盐基的塑性膨胀剂;憎水剂为渗透结晶材料。制备方法与实施例一基本相同,不另赘述。
测试得到的性能均显著超过国家行业标准《无机轻集料砂浆保温系统技术规程》JGJ253-2011规定的技术指标要求以及表1的性能指标要求。
由以上实施例可见,本发明可根据具体要求配制出柔韧性、抗裂性能以及防水憎水性能良好的柔性抗裂防护砂浆。各项性能指标均满足或超过相关标准和实际工程要求,作为一种柔性抗裂防护砂浆,不仅可广泛推广应用于各种建筑保温节能体系,起到柔性抗裂防护、防水憎水作用,而且还可以应用于各种建筑墙体材料的抹面工程,起到抗裂防护及防水作用。
总之,上述实施例的柔性抗裂防护砂浆施工性能良好、抗折强度和抗压强度高、柔韧性好、粘结抗拉强度高、抗开裂性能良好,具有优异的防水憎水效果等特点,用于建筑墙体保温节能体系的抗裂防护,能够解决各种应力导致的干燥收缩开裂问题,在工地现场直接加水即可使用,性能良好、稳定;还可用于各种新型建筑墙体材料的抹面抗裂防护施工过程,起到抗裂防护及防水作用。
Claims (8)
1.一种柔性抗裂防护砂浆,其特征在于主要由如下重量份的组分组成:
硅酸盐水泥:30-50
石英砂:50-65
消石灰:5-10
抗裂纤维:3-6
可再分散乳胶粉:1.2-2.5
纤维素醚:0.2-0.5
塑性膨胀剂:0.05-0.2
憎水剂:0.3-0.6。
2.根据权利要求1所述的柔性抗裂防护砂浆,其特征在于:所述石英砂由30-50目、40-70目、70-100目,按重量份3:4-6:1-3的比例配制而成。
3.根据权利要求1所述的柔性抗裂防护砂浆,其特征在于:所述抗裂纤维采用纤维长度≦3mm的木质素纤维。
4.根据权利要求1所述的柔性抗裂防护砂浆,其特征在于:所述可再分散乳胶粉为乙烯-醋酸乙烯酯乳胶粉、乙烯-氯乙烯-月桂酸乙烯酯乳胶粉中的至少一种。
5.根据权利要求1所述的柔性抗裂防护砂浆,其特征在于:所述纤维素醚为黏度6000mPa.s-45000mPa.s的羟乙基甲基纤维素、羟丙基甲基纤维素中的至少一种。
6.根据权利要求1所述的柔性抗裂防护砂浆,其特征在于:所述塑性膨胀剂为粉末状改性有机酸盐基的塑性膨胀剂。
7.根据权利要求1所述的柔性抗裂防护砂浆,其特征在于:所述憎水剂为有机硅类憎水剂、渗透结晶材料中的至少一种。
8.根据权利要求1至7任一所述柔性抗裂防护砂浆的制备方法,其特征在于:按重量份称量各组分后,先将可再分散乳胶粉、纤维素醚、塑性膨胀剂、憎水剂搅拌混合均匀,然后将所得混合物与其余组分搅拌混合均匀。