CN101549978A - 海泡石纤维改性玻化微珠保温砂浆 - Google Patents

海泡石纤维改性玻化微珠保温砂浆 Download PDF

Info

Publication number
CN101549978A
CN101549978A CNA2009100511468A CN200910051146A CN101549978A CN 101549978 A CN101549978 A CN 101549978A CN A2009100511468 A CNA2009100511468 A CN A2009100511468A CN 200910051146 A CN200910051146 A CN 200910051146A CN 101549978 A CN101549978 A CN 101549978A
Authority
CN
China
Prior art keywords
thermal insulation
insulation mortar
sepiolite
fiber modified
vitrification bead
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2009100511468A
Other languages
English (en)
Inventor
王培铭
张永明
岳兴国
张国防
朱永超
朱绘美
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongji University
Original Assignee
Tongji University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongji University filed Critical Tongji University
Priority to CNA2009100511468A priority Critical patent/CN101549978A/zh
Publication of CN101549978A publication Critical patent/CN101549978A/zh
Pending legal-status Critical Current

Abstract

本发明属于建筑材料领域，涉及玻化微珠、保温砂浆及其制备方法。一种海泡石纤维改性玻化微珠保温砂浆，各组分的质量分数如下：52.5R普通硅酸盐水泥：35％－55％、粉煤灰：5％－15％、重钙粉：1％－5％、玻化微珠：35％－55％、可再分散乳胶粉：0.5％－2％、纤维素醚：0.1％－0.3％、淀粉醚：0.025％－0.07％、引气剂：0.01％－0.02％、海泡石纤维：0.5％－2％，其中海泡石纤维的级配为：3－5mm30％～40％；5－10mm40％～50％；10－15mm20％～30％。本发明所述的海泡石纤维改性玻化微珠保温砂浆具有优良的施工性能、不空鼓开裂、与墙体粘结性能好、强度高、保温性能好、成本低等优势。

Description

海泡石纤维改性玻化微珠保温砂浆
技术领域
本发明属于建筑材料领域，涉及玻化微珠、保温砂浆及其制备方法。
背景技术
我国的外墙保温系统主要采用有机保温材料。这类保温材料虽然具有良好的保温隔热性能，但耐候性差、体积稳定性不良、不耐火、易老化。相比于有机保温材料，无机保温砂浆具有诸多优点。无机保温砂浆，尤其是玻化微珠保温砂浆，它是将玻化微珠骨料预拌在无机胶凝材料和有机添加剂中，形成的单组分保温砂浆，具有成本低、强度高、保温、隔热、防火、耐候等优点，可与面层抗裂砂浆、界面处理砂浆及辅助材料一起形成保温隔热、防火抗裂、防水防渗的保温体系。
由于玻化微珠保温砂浆具有以上诸多优点，已在多层及高层钢混结构建筑、加气混凝土砌块墙体及各种砖混结构建筑内、外墙抹灰保温工程中得到了广泛的应用。然而，为防止玻化微珠保温砂浆收缩开裂，一般会在保温砂浆中加入聚丙烯纤维或木质纤维等抗裂纤维。但聚丙烯纤维表面光滑，表面能低，掺入水泥基材料时，存在纤维分散性能差以及纤维-基体间粘结性能差的问题。木质纤维虽较易在玻化微珠保温砂浆体系中混合均匀，但存在缓凝的缺点。
发明内容
本发明针对目前玻化微珠保温砂浆材料存在的施工性能不稳定、收缩大、空鼓开裂的问题，通过海泡石纤维改性玻化微珠保温砂浆、优化配合比，制得了综合性能优良、成本较低的玻化微珠保温砂浆。
本发明采用如下技术方案来实现上述目的：一种高性能海泡石改性玻化微珠保温砂浆，其组分及配比(质量百分比)为：
胶凝材料：              35％-55％
粉煤灰：                5％-15％
消石灰：                1％-5％
玻化微珠：              35％-55％
海泡石纤维：            0.5％-2％
可再分散乳胶粉：        0.5％-2％
纤维素醚：              0.1％-0.3％
淀粉醚：                0.025％-0.07％
引气剂：                0.01％-0.02％
进一步：所述的胶凝材料为52.5R普通硅酸盐水泥。
所述的玻化微珠堆积密度为100-120Kg/m3。
所述的海泡石纤维为不同长度级配：3-5mm 30％～40％；；5-10mm 40％～50％；；10-15mm20％～30％。
选用的羟乙基甲基纤维素醚粘度介于100000Pa.s-150000Pa.s。
所述的纤维素醚与淀粉醚的质量比为4∶1～3∶1。
按所述各比例称量各组分，先将水泥与海泡石纤维混合均匀，然后依次加入各种添加剂及玻化微珠，混合均匀后即得到所述的海泡石纤维改性玻化微珠保温砂浆。
施工时将保温砂浆干粉料与水按1∶1～1∶1.1比例搅拌2到3分钟，稠度控制在65-85mm，静置3到5分钟即可使用。
本发明将不同长度级配的海泡石纤维掺入玻化微珠保温砂浆中替代聚丙烯纤维和木质纤维作为抗裂纤维。
由于海泡石纤维本身是一种无机材料，它与水泥有很好的亲和性，很容易与玻化微珠保温砂浆混合均匀，使玻化微珠保温砂浆的质量易于控制；海泡石纤维使成型的浆料有很高的防开裂性能：海泡石纤维同时具有极佳的保水性和可操作性，加入海泡石纤维的玻化微珠保温砂浆具有较好的施工性；另外海泡石纤维本身就是一种性能很好的保温材料，它具有很小的导热系数，可进一步提高玻化微珠保温砂浆的保温性能。
本发明海泡石纤维改性玻化微珠保温砂浆的检测结果如下：
表一海泡石纤维改性玻化微珠保温砂浆基本性能
Figure A20091005114600041
由上表可以看出，本发明所述的海泡石纤维改性玻化微珠保温砂浆导热系数可调节范围广，最小可达到0.060W/m·k，抗压及粘结拉伸强度高、线性收缩率小，各项指标均符合工程要求。
本海泡石纤维改性玻化微珠保温砂浆同时具有优异的施工性能。在指定稠度(65-85mm)的情况下，本玻化微珠保温砂浆可供用时间长，施工手感好，一次性涂抹2cm以上不流挂。
综上所述，本保温砂浆各性能指标优良、施工性能优异、品质易于控制，便于大规模推广应用。
具体实施方式
实施例1：一种海泡石纤维改性玻化微珠保温砂浆，其组分及配比(质量百分比)为：
水泥：40.1％，粉煤灰：10.9％，消石灰：3％，玻化微珠：43.5％，海泡石纤维：0.6％，可再分散乳胶粉：1.5％，甲基纤维素醚：0.29％，淀粉醚：0.07％，引气剂：0.01％。
表二实施例-1海泡石纤维改性玻化微珠保温砂浆性能指标
  项目     技术指标
  湿表观密度(kg/m3)     ≤530
  干表观密度(kg/m3)     ≤300
  导热系数(W/m·k)     ≤0.065
  抗压强度(MPa)     ≥0.40
  线性收缩率(％)     ≤0.2
  拉伸粘结强度(MPa)     ≥0.1
  软化系数     ≥0.70
实施例2：一种海泡石纤维改性玻化微珠保温砂浆，其组分及配比(质量百分比)为：
水泥：41.8％，粉煤灰：7.5％，消石灰：2.5％，玻化微珠：46.3％，海泡石纤维：0.5％，可再分散乳胶粉：1.1％，甲基纤维素醚：0.21％，淀粉醚：0.05％，引气剂：0.01％。
表三实施例-2海泡石纤维改性玻化微珠保温砂浆性能指标
  项目     技术指标
  湿表观密度(kg/m3)     ≤550
  干表观密度(kg/m3)     ≤320
  导热系数(W/m·k)     ≤0.070
  抗压强度(MPa)     ≥0.8
  线性收缩率(％)     ≤0.2
  拉伸粘结强度(MPa)     ≥0.15
  软化系数     ≥0.70
实施例3：一种海泡石纤维改性玻化微珠保温砂浆，其组分及配比(质量百分比)为：
水泥：53.1％，粉煤灰：5％，消石灰：3％，玻化微珠：36.9％，海泡石纤维：0.5％，可再分散乳胶粉：1.2％，甲基纤维素醚：0.25％，淀粉醚：0.07％，引气剂：0.01％。
表四实施例-3海泡石纤维改性玻化微珠保温砂浆性能指标
  项目     技术指标
  湿表观密度(kg/m3)     ≤620
  干表观密度(kg/m3)     ≤420
  导热系数(W/m·k)     ≤0.080
  抗压强度(MPa)     ≥1.0
  线性收缩率(％)     ≤0.2
  拉伸粘结强度(MPa)     ≥0.3
  软化系数     ≥0.70
由以上实施例可见，海泡石纤维改性玻化微珠保温砂浆可以制备具有不同导热系数的保温砂浆。各指标均满足工程要求，可以作为高性能墙体保温材料推广使用。
上述的对实施例的描述是为便于该技术领域的普通技术人员能理解和应用本发明。熟悉本领域技术的人员显然可以容易地对这些实施例做出各种修改，并把在此说明的一般原理应用到其他实施例中而不必经过创造性的劳动。因此，本发明不限于这里的实施例，本领域技术人员根据本发明的揭示，对于本发明做出的改进和修改都应该在本发明的保护范围之内。

Claims (8)

1.一种玻化微珠保温砂浆，其特征在于：其组分及配比(质量百分比)为：
胶凝材料：      35％-55％
粉煤灰：        5％-15％
消石灰：        1％-5％
玻化微珠：      35％-55％
海泡石纤维：    0.5％-2％
可再分散乳胶粉：0.5％-2％
纤维素醚：      0.1％-0.3％
淀粉醚：        0.025％-0.07％
引气剂：        0.01％-0.02％
2.根据权利要求1所述的玻化微珠保温砂浆，其特征在于：所述的胶凝材料为52.5R普通硅酸盐水泥。
3.根据权利要求1所述的玻化微珠保温砂浆，其特征在于：所述的玻化微珠堆积密度为100-120Kg/m3。
4.根据权利要求1所述的玻化微珠保温砂浆，其特征在于：所述的海泡石纤维为不同长度级配：3-5mm 30％～40％；；5-10mm 40％～50％；；10-15mm 20％～30％。
5.根据权利要求1所述的玻化微珠保温砂浆，其特征在于：选用的羟乙基甲基纤维素醚粘度介于100000Pa.s-150000Pa.s。
6.根据权利要求1所述的海泡石纤维改性玻化微珠保温砂浆，其特征在于：所述的纤维素醚与淀粉醚的质量比为4∶1～3∶1。
7.权利要求1所述的海泡石纤维改性玻化微珠保温砂浆的制备方法，其特征在于：按所述各比例称量各组分，先将水泥与海泡石纤维混合均匀，然后依次加入各种添加剂及玻化微珠，混合均匀后即得到所述的海泡石纤维改性玻化微珠保温砂浆。
8.权利要求1所述的海泡石纤维改性玻化微珠保温砂浆的使用方法，其特征在于：施工时将保温砂浆干粉料与水按1∶1～1∶1.1比例搅拌2到3分钟，稠度控制在65-85mm，静置3到5分钟即可使用。
CNA2009100511468A 2009-05-13 2009-05-13 海泡石纤维改性玻化微珠保温砂浆 Pending CN101549978A (zh)