CN103664099A - 一种环保无机保温砂浆 - Google Patents

一种环保无机保温砂浆 Download PDF

Info

Publication number
CN103664099A
CN103664099A CN201310606499.6A CN201310606499A CN103664099A CN 103664099 A CN103664099 A CN 103664099A CN 201310606499 A CN201310606499 A CN 201310606499A CN 103664099 A CN103664099 A CN 103664099A
Authority
CN
China
Prior art keywords
parts
friendly inorganic
raw material
environment
thermal insulation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310606499.6A
Other languages
English (en)
Inventor
许正贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Tian Wangyuxu Articles For Use Co Ltd
Original Assignee
Bengbu Tian Wangyuxu Articles For Use Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Tian Wangyuxu Articles For Use Co Ltd filed Critical Bengbu Tian Wangyuxu Articles For Use Co Ltd
Priority to CN201310606499.6A priority Critical patent/CN103664099A/zh
Publication of CN103664099A publication Critical patent/CN103664099A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种环保无机保温砂浆，它是由下述重量份的原料组成的：普通硅酸盐水泥170-200、葡萄糖酸钙0.01-0.03、磷酸钾0.1-0.3、石油磺酸钡0.5-1、乙二醇1-2、聚氨酯流平增稠剂pu-80801-2、松香酸聚氧乙烯酯2-3、消石灰20-30、膨润土6-10、聚乙烯醇缩丁醛2-3、改性助剂4-6、水适量；本发明生产的保温砂浆具有很好的抗渗性能，吸水率低，具有很好的抗开裂性能，强度高，保温性好，环保无毒。

Description

一种环保无机保温砂浆
 
技术领域
    本发明主要涉及一种砂浆，尤其涉及一种环保无机保温砂浆。
背景技术
保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业搅拌混合而制成的一种预拌干粉砂浆。主要用于建筑外墙保温，具有施工方便、耐久性好等优点。
发明内容
本发明目的就是提供一种环保无机保温砂浆。
本发明是通过以下技术方案实现的：
一种环保无机保温砂浆，其特征在于它是由下述重量份的原料组成的：
普通硅酸盐水泥170-200、葡萄糖酸钙0.01-0.03、磷酸钾0.1-0.3、石油磺酸钡0.5-1、乙二醇1-2、聚氨酯流平增稠剂pu-8080 1-2、松香酸聚氧乙烯酯2-3、消石灰20-30、膨润土6-10、聚乙烯醇缩丁醛2-3、改性助剂4-6、水适量；
所述的改性助剂是由下述重量份的原料组成的：
红土40-65、骨粉2-4、蜂胶3-5、磷酸二氢铝3-4、可再分散乳胶粉20-30、聚乙烯吡咯烷酮2-3、硅烷偶联剂KH560 1-2、羟丙基甲基纤维素醚1-2、聚乙二醇400 2-3；
所述的改性助剂的制备方法包括以下步骤：
将上述红土在700-800℃下煅烧2-3小时，冷却至室温，加6-10%的氢氧化钠溶液研磨1-2小时，再加入10-15%的盐酸，调节PH为中性，在搅拌调节下依次加入蜂胶、磷酸二氢铝、可再分散乳胶粉、聚乙烯吡咯烷酮、聚乙二醇400，加入完毕后在60-80℃下保温搅拌10-16分钟，再加入剩余各原料，800-1000转/分搅拌分散3-5分钟，即得所述改性助剂。
一种环保无机保温砂浆的制备方法，包括以下步骤：
将上述普通硅酸盐水泥、消石灰、膨润土混合，加入混合料重量60-75%的水，搅拌均匀，加入聚乙烯醇缩丁醛、聚氨酯流平增稠剂pu-8080，300-400转/分搅拌分散4-6分钟，加入剩余各原料，充分搅拌混合均匀，即得所述环保无机保温砂浆。
本发明的优点是：
本发明生产的保温砂浆具有很好的抗渗性能，吸水率低，具有很好的抗开裂性能，强度高，保温性好，环保无毒。
具体实施方式
实施例1
一种环保无机保温砂浆，它是由下述重量份的原料组成的：
普通硅酸盐水泥200、葡萄糖酸钙0.03、磷酸钾0.3、石油磺酸钡0.5、乙二醇2、聚氨酯流平增稠剂pu-8080 2、松香酸聚氧乙烯酯3、消石灰30、膨润土10、聚乙烯醇缩丁醛2、改性助剂4、水适量；
所述的改性助剂是由下述重量份的原料组成的：
红土65、骨粉2、蜂胶3、磷酸二氢铝3、可再分散乳胶粉30、聚乙烯吡咯烷酮3、硅烷偶联剂KH560 2、羟丙基甲基纤维素醚1、聚乙二醇400 3；
所述的改性助剂的制备方法包括以下步骤：
将上述红土在800℃下煅烧3小时，冷却至室温，加10%的氢氧化钠溶液研磨2小时，再加入15%的盐酸，调节PH为中性，在搅拌调节下依次加入蜂胶、磷酸二氢铝、可再分散乳胶粉、聚乙烯吡咯烷酮、聚乙二醇400，加入完毕后在80℃下保温搅拌16分钟，再加入剩余各原料，1000转/分搅拌分散5分钟，即得所述改性助剂。
一种环保无机保温砂浆的制备方法，包括以下步骤：
将上述普通硅酸盐水泥、消石灰、膨润土混合，加入混合料重量75%的水，搅拌均匀，加入聚乙烯醇缩丁醛、聚氨酯流平增稠剂pu-8080，400转/分搅拌分散4分钟，加入剩余各原料，充分搅拌混合均匀，即得所述环保无机保温砂浆。
性能测试：
28d抗折强度：0.42MPa；
28d抗压强度：1.03 Mpa。

Claims (2)

1.一种环保无机保温砂浆，其特征在于它是由下述重量份的原料组成的：
普通硅酸盐水泥170-200、葡萄糖酸钙0.01-0.03、磷酸钾0.1-0.3、石油磺酸钡0.5-1、乙二醇1-2、聚氨酯流平增稠剂pu-8080 1-2、松香酸聚氧乙烯酯2-3、消石灰20-30、膨润土6-10、聚乙烯醇缩丁醛2-3、改性助剂4-6、水适量；
所述的改性助剂是由下述重量份的原料组成的：
红土40-65、骨粉2-4、蜂胶3-5、磷酸二氢铝3-4、可再分散乳胶粉20-30、聚乙烯吡咯烷酮2-3、硅烷偶联剂KH560 1-2、羟丙基甲基纤维素醚1-2、聚乙二醇400 2-3；
所述的改性助剂的制备方法包括以下步骤：
将上述红土在700-800℃下煅烧2-3小时，冷却至室温，加6-10%的氢氧化钠溶液研磨1-2小时，再加入10-15%的盐酸，调节PH为中性，在搅拌调节下依次加入蜂胶、磷酸二氢铝、可再分散乳胶粉、聚乙烯吡咯烷酮、聚乙二醇400，加入完毕后在60-80℃下保温搅拌10-16分钟，再加入剩余各原料，800-1000转/分搅拌分散3-5分钟，即得所述改性助剂。
2.一种如权利要求1所述的环保无机保温砂浆的制备方法，其特征在于包括以下步骤：
将上述普通硅酸盐水泥、消石灰、膨润土混合，加入混合料重量60-75%的水，搅拌均匀，加入聚乙烯醇缩丁醛、聚氨酯流平增稠剂pu-8080，300-400转/分搅拌分散4-6分钟，加入剩余各原料，充分搅拌混合均匀，即得所述环保无机保温砂浆。
CN201310606499.6A 2013-11-26 2013-11-26 一种环保无机保温砂浆 Pending CN103664099A (zh)