WO2014143929A2 - Appareil de fabrication et de traitement de films pré-étirés comportant des bandes d'épaisseur augmentée - Google Patents

Appareil de fabrication et de traitement de films pré-étirés comportant des bandes d'épaisseur augmentée Download PDF

Info

Publication number
WO2014143929A2
WO2014143929A2 PCT/US2014/028115 US2014028115W WO2014143929A2 WO 2014143929 A2 WO2014143929 A2 WO 2014143929A2 US 2014028115 W US2014028115 W US 2014028115W WO 2014143929 A2 WO2014143929 A2 WO 2014143929A2
Authority
WO
WIPO (PCT)
Prior art keywords
film
die
producing
polymer
stretch
Prior art date
Application number
PCT/US2014/028115
Other languages
English (en)
Other versions
WO2014143929A3 (fr
Inventor
Hassan Helmy
Robert F. Moeller
John P. Christiano
Daniel F. Hould
Original Assignee
Davis-Standard, Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Davis-Standard, Llc filed Critical Davis-Standard, Llc
Priority claimed from US14/210,531 external-priority patent/US20140265006A1/en
Publication of WO2014143929A2 publication Critical patent/WO2014143929A2/fr
Publication of WO2014143929A3 publication Critical patent/WO2014143929A3/fr

Abstract

La présente invention concerne un dispositif de production de film pré-étiré comprenant une filière définissant une sortie de filière à travers laquelle un polymère fondu est extrudé. Le polymère est approprié à la production du film pré-étiré. Un dispositif de production de film est espacé de la filière. Une ou plusieurs alimentations en agent de refroidissement sont placées à proximité du dispositif de production de film afin de diriger un flux d'agent de refroidissement sur le polymère fondu disposé sur le dispositif de production de film.
PCT/US2014/028115 2013-03-15 2014-03-14 Appareil de fabrication et de traitement de films pré-étirés comportant des bandes d'épaisseur augmentée WO2014143929A2 (fr)

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US201361788776P 2013-03-15 2013-03-15
US61/788,776 2013-03-15
US201461932519P 2014-01-28 2014-01-28
US61/932,519 2014-01-28
US14/210,531 US20140265006A1 (en) 2013-03-15 2014-03-14 Apparatus for manufacturing and processing films
US14/210,531 2014-03-14

Publications (2)

Publication Number Publication Date
WO2014143929A2 true WO2014143929A2 (fr) 2014-09-18
WO2014143929A3 WO2014143929A3 (fr) 2015-02-26

Family

ID=51538286

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2014/028115 WO2014143929A2 (fr) 2013-03-15 2014-03-14 Appareil de fabrication et de traitement de films pré-étirés comportant des bandes d'épaisseur augmentée

Country Status (1)

Country Link
WO (1) WO2014143929A2 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016096648A1 (fr) * 2014-12-19 2016-06-23 Windmöller & Hölscher Kg Procédé et dispositif de mesure pour surveiller l'extensibilité lors de la fabrication d'un film étirable dans un procédé de feuille mince moulée

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5215629B1 (fr) * 1966-05-23 1977-05-02
GB1277519A (en) * 1970-08-21 1972-06-14 Mobil Oil Corp Method for the production of biaxially oriented polypropylene film
US4315963A (en) * 1979-09-14 1982-02-16 The Dow Chemical Co. Thermoplastic film with integral ribbed pattern and bag therefrom
JPS61209135A (ja) * 1985-03-13 1986-09-17 Shikoku Kako Kk 熱可塑性合成樹脂製筋入フイルムの製造方法
AU4899299A (en) * 1998-05-28 1999-12-13 Mauser-Werke Gmbh Method and device for producing plastic hollow bodies and plastic hollow bodies produced by means of same

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
None

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016096648A1 (fr) * 2014-12-19 2016-06-23 Windmöller & Hölscher Kg Procédé et dispositif de mesure pour surveiller l'extensibilité lors de la fabrication d'un film étirable dans un procédé de feuille mince moulée
US11090851B2 (en) 2014-12-19 2021-08-17 Windmöller & Hölscher Kg Method and measurement device for monitoring stretchability in the production of stretch films in a cast film method

Also Published As

Publication number Publication date
WO2014143929A3 (fr) 2015-02-26

Similar Documents

Publication Publication Date Title
US9162403B2 (en) Apparatus for manufacturing and processing pre-stretch films having strips of increased thickness
JP4623935B2 (ja) 実質的一軸配向を有する横断方向延伸フィルムを製造するための方法
US5558930A (en) Heat sealable, high moisture barrier film and method of making same
JP5130495B2 (ja) ポリプロピレン系積層フィルム及びそれを用いた包装体
US20140272305A1 (en) Apparatus for manufacturing and processing pre-stretch films having strips of increased thickness
US20140265059A1 (en) Apparatus for manufacturing and processing films having strips of increased thickness
JP2006103339A (ja) 幅出機内で同時に二軸延伸されたフィルム
JP4650019B2 (ja) ポリプロピレン系積層フィルム及びそれを用いた包装体
US11072103B2 (en) Extrusion system and method for blown film with integral profiles
CN102481753B (zh) 充气交叉层合体及其制造方法和设备
JP5009768B2 (ja) ポリプロピレン系積層フィルム及びそれを用いた包装体
WO2014143929A2 (fr) Appareil de fabrication et de traitement de films pré-étirés comportant des bandes d'épaisseur augmentée
EP1232846A1 (fr) Procédé de fabrication d'un film en résine, et méthode et dispositif de fabrication d'une feuille stratifiée
CA2181056A1 (fr) Ruban adhesif autocollant
JP2023001059A (ja) 多層積層合流装置
US20140021644A1 (en) Dies and Methods for Improving Physical Properties of Stretch Film
JP6338865B2 (ja) 延伸フィルムの製造方法
US20140265006A1 (en) Apparatus for manufacturing and processing films
WO2015108035A1 (fr) Procédé de fabrication d'un film étiré
JP2009018549A (ja) 熱可塑性樹脂フィルムの製造方法及び装置
US11135757B2 (en) Extrusion system and method for blown film
JP3070823B2 (ja) 熱可塑性樹脂フィルムの製造方法
JP2000141448A (ja) 発泡シート及びフィルム成形装置
JPS5929125A (ja) 熱可塑性樹脂フイルムの成形方法
JPH10113985A (ja) 熱可塑性フィルムの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14729103

Country of ref document: EP

Kind code of ref document: A2

122 Ep: pct application non-entry in european phase

Ref document number: 14729103

Country of ref document: EP

Kind code of ref document: A2