WO2014120991A1 - Fusion/frittage par laser de manière sélective en utilisant du flux en poudre - Google Patents

Fusion/frittage par laser de manière sélective en utilisant du flux en poudre Download PDF

Info

Publication number
WO2014120991A1
WO2014120991A1 PCT/US2014/013972 US2014013972W WO2014120991A1 WO 2014120991 A1 WO2014120991 A1 WO 2014120991A1 US 2014013972 W US2014013972 W US 2014013972W WO 2014120991 A1 WO2014120991 A1 WO 2014120991A1
Authority
WO
WIPO (PCT)
Prior art keywords
flux
powder
layer
alloy
particles
Prior art date
Application number
PCT/US2014/013972
Other languages
English (en)
Inventor
Gerald J. Bruck
Ahmed Kamel
Original Assignee
Siemens Energy, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US13/755,098 external-priority patent/US9283593B2/en
Application filed by Siemens Energy, Inc. filed Critical Siemens Energy, Inc.
Priority to EP14704988.6A priority Critical patent/EP2950950A1/fr
Priority to KR1020157023573A priority patent/KR20150113149A/ko
Priority to CN201480006187.4A priority patent/CN105263667A/zh
Priority to JP2015556145A priority patent/JP2016511697A/ja
Priority to RU2015131615A priority patent/RU2015131615A/ru
Publication of WO2014120991A1 publication Critical patent/WO2014120991A1/fr

Abstract

La présente invention concerne un procédé de fabrication d'additif (110), tel qu'une poudre (116) incluant un matériau de superalliage et du flux sont mélangés de manière sélective en couches avec un faisceau laser (124) afin de former un composant de superalliage (126). Le flux réalise une fonction de nettoyage afin de réagir avec des contaminants et de les faire flotter à la surface du bain pour former des scories. Le flux fournit en outre une fonction d'écran, éliminant de ce fait le besoin d'un gaz de couverture inerte. La poudre peut être un mélange de particules de flux et d'alliage, ou bien elle peut être formée de particules alliage/flux composites.
PCT/US2014/013972 2013-01-31 2014-01-31 Fusion/frittage par laser de manière sélective en utilisant du flux en poudre WO2014120991A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
EP14704988.6A EP2950950A1 (fr) 2013-01-31 2014-01-31 Fusion/frittage par laser de manière sélective en utilisant du flux en poudre
KR1020157023573A KR20150113149A (ko) 2013-01-31 2014-01-31 분말형 용제를 사용하는 선택적 레이저 용융 및 소결
CN201480006187.4A CN105263667A (zh) 2013-01-31 2014-01-31 使用粉末状焊剂的选择性激光熔化/烧结
JP2015556145A JP2016511697A (ja) 2013-01-31 2014-01-31 粉末状フラックスを用いた選択的レーザ溶融／焼結
RU2015131615A RU2015131615A (ru) 2013-01-31 2014-01-31 Способ селективного лазерного плавления/спекания с применением порошкообразного флюса

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US13/755,098 US9283593B2 (en) 2011-01-13 2013-01-31 Selective laser melting / sintering using powdered flux
US13/755,098 2013-01-31

Publications (1)

Publication Number Publication Date
WO2014120991A1 true WO2014120991A1 (fr) 2014-08-07

Family

ID=50114576

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2014/013972 WO2014120991A1 (fr) 2013-01-31 2014-01-31 Fusion/frittage par laser de manière sélective en utilisant du flux en poudre

Country Status (6)

Country Link
EP (1) EP2950950A1 (fr)
JP (1) JP2016511697A (fr)
KR (1) KR20150113149A (fr)
CN (1) CN105263667A (fr)
RU (1) RU2015131615A (fr)
WO (1) WO2014120991A1 (fr)

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016073193A1 (fr) * 2014-11-04 2016-05-12 Dresser-Rand Company Système et procédé de fabrication additive de composants de turbomachine
WO2016126455A1 (fr) * 2015-02-06 2016-08-11 Dresser-Rand Company Procédés pour fabrication additive d'un piston d'un seul tenant
WO2016196223A1 (fr) * 2015-05-29 2016-12-08 Velo3D, Inc. Objets tridimensionnels formés par impression tridimensionnelle
US9573225B2 (en) 2014-06-20 2017-02-21 Velo3D, Inc. Apparatuses, systems and methods for three-dimensional printing
US9662840B1 (en) 2015-11-06 2017-05-30 Velo3D, Inc. Adept three-dimensional printing
US9919360B2 (en) 2016-02-18 2018-03-20 Velo3D, Inc. Accurate three-dimensional printing
US9962767B2 (en) 2015-12-10 2018-05-08 Velo3D, Inc. Apparatuses for three-dimensional printing
US20180126649A1 (en) 2016-11-07 2018-05-10 Velo3D, Inc. Gas flow in three-dimensional printing
US10144176B1 (en) 2018-01-15 2018-12-04 Velo3D, Inc. Three-dimensional printing systems and methods of their use
US10252336B2 (en) 2016-06-29 2019-04-09 Velo3D, Inc. Three-dimensional printing and three-dimensional printers
US10272525B1 (en) 2017-12-27 2019-04-30 Velo3D, Inc. Three-dimensional printing systems and methods of their use
US10315252B2 (en) 2017-03-02 2019-06-11 Velo3D, Inc. Three-dimensional printing of three-dimensional objects
US10449696B2 (en) 2017-03-28 2019-10-22 Velo3D, Inc. Material manipulation in three-dimensional printing
US10611092B2 (en) 2017-01-05 2020-04-07 Velo3D, Inc. Optics in three-dimensional printing
WO2021156081A1 (fr) * 2020-02-03 2021-08-12 Eos Gmbh Procédé de modération d'une réaction de particules métalliques
US11691343B2 (en) 2016-06-29 2023-07-04 Velo3D, Inc. Three-dimensional printing and three-dimensional printers
RU2805731C1 (ru) * 2023-05-03 2023-10-23 Федеральное государственное автономное образовательное учреждение высшего образования "Белгородский государственный национальный исследовательский университет" (НИУ "БелГУ") Способ изготовления цельного инструмента для сварки трением с перемешиванием с помощью аддитивных технологий

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7001061B2 (ja) * 2016-11-02 2022-01-19 コニカミノルタ株式会社 粉末焼結積層造形物の製造方法
RU2738121C1 (ru) * 2017-08-15 2020-12-08 Сименс Энерджи, Инк. ЛАЗЕРНОЕ ОСАЖДЕНИЕ МЕТАЛЛОВ ДЛЯ СУПЕРСПЛАВОВ С ВЫСОКИМ СОДЕРЖАНИЕМ γ'-ФАЗЫ С ЭФФЕКТОМ ОХЛАЖДЕНИЯ
US20190091802A1 (en) * 2017-09-25 2019-03-28 General Electric Company Method for forming article, method for forming turbine bucket, and turbine bucket
EP3539712B1 (fr) * 2017-12-20 2020-08-05 C.R.F. Società Consortile per Azioni Procédé pour l'application d'un renfort métallique à un composant de matériau métallique, en particulier dans la construction d'une carrosserie de véhicule automobile ou d'un sous-ensemble de celle-ci
CN109097724B (zh) * 2018-09-18 2019-09-10 华中农业大学 一种基于脉冲电弧的渗碳强化仿生结构的制备方法
KR102145002B1 (ko) * 2018-12-21 2020-08-14 부산대학교 산학협력단 미세 와이어 제조방법
US20200324372A1 (en) * 2019-04-12 2020-10-15 Hobart Brothers Llc Laser additive manufacturing and welding with hydrogen shield gas
JP7403418B2 (ja) 2020-09-03 2023-12-22 株式会社神戸製鋼所 スラグ除去手順生成装置
CN113369728B (zh) * 2021-05-20 2022-08-19 北京航空航天大学 钛合金大型复杂结构构件的制造方法
JP2022191920A (ja) * 2021-06-16 2022-12-28 株式会社神戸製鋼所 積層計画作成方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1992010343A1 (fr) * 1990-12-07 1992-06-25 Board Of Regents, The University Of Texas System Fabrication de pieces par formation composite de poudres precurseurs
EP0764487A1 (fr) * 1995-09-19 1997-03-26 Rockwell International Corporation Préparation d'ébauches métalliques sans moule
RU2217266C2 (ru) * 1999-12-30 2003-11-27 Физический институт им. П.Н. Лебедева РАН Способ изготовления объёмных изделий из биметаллических порошковых композиций
US20070037509A1 (en) * 2005-05-31 2007-02-15 Bernd Renz Method for the manufacture of a molding as well as a sensor unit for the application thereof
EP2055424B1 (fr) * 2007-10-30 2012-12-12 General Electric Company Formulation de brasage et son procédé de fabrication

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4086463A (en) * 1972-11-13 1978-04-25 Tsukishima Kikai Co., Ltd. Flux-cored wire
JPS5419383B2 (fr) * 1972-11-13 1979-07-14
JPH0673556A (ja) * 1992-05-13 1994-03-15 Ishikawajima Harima Heavy Ind Co Ltd 炭素鋼等のレーザクラッド法
US6129795A (en) * 1997-08-04 2000-10-10 Integran Technologies Inc. Metallurgical method for processing nickel- and iron-based superalloys
WO2001034371A2 (fr) * 1999-11-05 2001-05-17 Z Corporation Systemes de produit et procedes pour impression tridimensionnelle
JP2001305271A (ja) * 2000-04-24 2001-10-31 Toshiba Corp 原子力発電プラント用炉内機器の補修方法
US7326892B1 (en) * 2006-09-21 2008-02-05 General Electric Company Process of microwave brazing with powder materials
WO2008098614A1 (fr) * 2007-02-13 2008-08-21 Siemens Aktiengesellschaft Réparation par soudage de défauts en position intérieure
FR2939340B1 (fr) * 2008-12-09 2010-12-31 Air Liquide Flux et fil pour le soudage a l'arc submerge des aciers crmov.
DE102009049518A1 (de) * 2009-10-15 2011-04-21 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Verfahren und Vorrichtung zum Schweißen von Werkstücken aus hochwarmfesten Superlegierungen
EP2322313A1 (fr) * 2009-11-13 2011-05-18 Siemens Aktiengesellschaft Procédé de soudure de pièces usinées en superalliages résistant aux températures avec un débit particulier du matériau d'apport de soudage

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1992010343A1 (fr) * 1990-12-07 1992-06-25 Board Of Regents, The University Of Texas System Fabrication de pieces par formation composite de poudres precurseurs
EP0764487A1 (fr) * 1995-09-19 1997-03-26 Rockwell International Corporation Préparation d'ébauches métalliques sans moule
RU2217266C2 (ru) * 1999-12-30 2003-11-27 Физический институт им. П.Н. Лебедева РАН Способ изготовления объёмных изделий из биметаллических порошковых композиций
US20070037509A1 (en) * 2005-05-31 2007-02-15 Bernd Renz Method for the manufacture of a molding as well as a sensor unit for the application thereof
EP2055424B1 (fr) * 2007-10-30 2012-12-12 General Electric Company Formulation de brasage et son procédé de fabrication

Cited By (42)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9821411B2 (en) 2014-06-20 2017-11-21 Velo3D, Inc. Apparatuses, systems and methods for three-dimensional printing
US10195693B2 (en) 2014-06-20 2019-02-05 Vel03D, Inc. Apparatuses, systems and methods for three-dimensional printing
US10493564B2 (en) 2014-06-20 2019-12-03 Velo3D, Inc. Apparatuses, systems and methods for three-dimensional printing
US9573225B2 (en) 2014-06-20 2017-02-21 Velo3D, Inc. Apparatuses, systems and methods for three-dimensional printing
US9573193B2 (en) 2014-06-20 2017-02-21 Velo3D, Inc. Apparatuses, systems and methods for three-dimensional printing
US9586290B2 (en) 2014-06-20 2017-03-07 Velo3D, Inc. Systems for three-dimensional printing
US10507549B2 (en) 2014-06-20 2019-12-17 Velo3D, Inc. Apparatuses, systems and methods for three-dimensional printing
US10464171B2 (en) 2014-11-04 2019-11-05 Dresser-Rand Company Method for additive manufacturing of turbomachine components
WO2016073193A1 (fr) * 2014-11-04 2016-05-12 Dresser-Rand Company Système et procédé de fabrication additive de composants de turbomachine
WO2016126455A1 (fr) * 2015-02-06 2016-08-11 Dresser-Rand Company Procédés pour fabrication additive d'un piston d'un seul tenant
WO2016196223A1 (fr) * 2015-05-29 2016-12-08 Velo3D, Inc. Objets tridimensionnels formés par impression tridimensionnelle
US9676145B2 (en) 2015-11-06 2017-06-13 Velo3D, Inc. Adept three-dimensional printing
US9662840B1 (en) 2015-11-06 2017-05-30 Velo3D, Inc. Adept three-dimensional printing
US10357957B2 (en) 2015-11-06 2019-07-23 Velo3D, Inc. Adept three-dimensional printing
US10065270B2 (en) 2015-11-06 2018-09-04 Velo3D, Inc. Three-dimensional printing in real time
US10688722B2 (en) 2015-12-10 2020-06-23 Velo3D, Inc. Skillful three-dimensional printing
US10183330B2 (en) 2015-12-10 2019-01-22 Vel03D, Inc. Skillful three-dimensional printing
US10071422B2 (en) 2015-12-10 2018-09-11 Velo3D, Inc. Skillful three-dimensional printing
US10207454B2 (en) 2015-12-10 2019-02-19 Velo3D, Inc. Systems for three-dimensional printing
US9962767B2 (en) 2015-12-10 2018-05-08 Velo3D, Inc. Apparatuses for three-dimensional printing
US10286603B2 (en) 2015-12-10 2019-05-14 Velo3D, Inc. Skillful three-dimensional printing
US10252335B2 (en) 2016-02-18 2019-04-09 Vel03D, Inc. Accurate three-dimensional printing
US9931697B2 (en) 2016-02-18 2018-04-03 Velo3D, Inc. Accurate three-dimensional printing
US9919360B2 (en) 2016-02-18 2018-03-20 Velo3D, Inc. Accurate three-dimensional printing
US10434573B2 (en) 2016-02-18 2019-10-08 Velo3D, Inc. Accurate three-dimensional printing
US10252336B2 (en) 2016-06-29 2019-04-09 Velo3D, Inc. Three-dimensional printing and three-dimensional printers
US10259044B2 (en) 2016-06-29 2019-04-16 Velo3D, Inc. Three-dimensional printing and three-dimensional printers
US11691343B2 (en) 2016-06-29 2023-07-04 Velo3D, Inc. Three-dimensional printing and three-dimensional printers
US10286452B2 (en) 2016-06-29 2019-05-14 Velo3D, Inc. Three-dimensional printing and three-dimensional printers
US20180126649A1 (en) 2016-11-07 2018-05-10 Velo3D, Inc. Gas flow in three-dimensional printing
US10661341B2 (en) 2016-11-07 2020-05-26 Velo3D, Inc. Gas flow in three-dimensional printing
US10611092B2 (en) 2017-01-05 2020-04-07 Velo3D, Inc. Optics in three-dimensional printing
US10888925B2 (en) 2017-03-02 2021-01-12 Velo3D, Inc. Three-dimensional printing of three-dimensional objects
US10442003B2 (en) 2017-03-02 2019-10-15 Velo3D, Inc. Three-dimensional printing of three-dimensional objects
US10369629B2 (en) 2017-03-02 2019-08-06 Veo3D, Inc. Three-dimensional printing of three-dimensional objects
US10315252B2 (en) 2017-03-02 2019-06-11 Velo3D, Inc. Three-dimensional printing of three-dimensional objects
US10357829B2 (en) 2017-03-02 2019-07-23 Velo3D, Inc. Three-dimensional printing of three-dimensional objects
US10449696B2 (en) 2017-03-28 2019-10-22 Velo3D, Inc. Material manipulation in three-dimensional printing
US10272525B1 (en) 2017-12-27 2019-04-30 Velo3D, Inc. Three-dimensional printing systems and methods of their use
US10144176B1 (en) 2018-01-15 2018-12-04 Velo3D, Inc. Three-dimensional printing systems and methods of their use
WO2021156081A1 (fr) * 2020-02-03 2021-08-12 Eos Gmbh Procédé de modération d'une réaction de particules métalliques
RU2805731C1 (ru) * 2023-05-03 2023-10-23 Федеральное государственное автономное образовательное учреждение высшего образования "Белгородский государственный национальный исследовательский университет" (НИУ "БелГУ") Способ изготовления цельного инструмента для сварки трением с перемешиванием с помощью аддитивных технологий

Also Published As

Publication number Publication date
EP2950950A1 (fr) 2015-12-09
CN105263667A (zh) 2016-01-20
KR20150113149A (ko) 2015-10-07
RU2015131615A (ru) 2017-03-07
JP2016511697A (ja) 2016-04-21

Similar Documents

Publication Publication Date Title
US9283593B2 (en) Selective laser melting / sintering using powdered flux
EP2950972B1 (fr) Réparation locale d'un composant de superalliage
US9352413B2 (en) Deposition of superalloys using powdered flux and metal
US9315903B2 (en) Laser microcladding using powdered flux and metal
US9352419B2 (en) Laser re-melt repair of superalloys using flux
EP2950959B1 (fr) Placage d'alliages au moyen de matériau d'alimentation à coeur de fondant en poudre et métal
EP2950966B1 (fr) Dépôt de super alliages par flux et métal pulverulentes
US20130316183A1 (en) Localized repair of superalloy component
WO2014120991A1 (fr) Fusion/frittage par laser de manière sélective en utilisant du flux en poudre
WO2014121060A1 (fr) Réparation localisée d'un composant de superalliage
US20150125335A1 (en) Additive manufacturing using a fluidized bed of powdered metal and powdered flux
US9272363B2 (en) Hybrid laser plus submerged arc or electroslag cladding of superalloys
EP2950973A1 (fr) Procédé de réparation par re-fusion par laser des superalliages à l'aide d'un flux
WO2014120729A1 (fr) Microrevêtement au laser à l'aide d'un métal et d'un flux en poudre

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201480006187.4

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14704988

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2014704988

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2015556145

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20157023573

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2015131615

Country of ref document: RU

Kind code of ref document: A