WO2014112337A1 - Matériau diélectrique et élément électrochimique utilisant celui-ci - Google Patents

Matériau diélectrique et élément électrochimique utilisant celui-ci Download PDF

Info

Publication number
WO2014112337A1
WO2014112337A1 PCT/JP2014/000065 JP2014000065W WO2014112337A1 WO 2014112337 A1 WO2014112337 A1 WO 2014112337A1 JP 2014000065 W JP2014000065 W JP 2014000065W WO 2014112337 A1 WO2014112337 A1 WO 2014112337A1
Authority
WO
WIPO (PCT)
Prior art keywords
dielectric material
graphene oxide
graferrite
reduced graphene
electrode
Prior art date
Application number
PCT/JP2014/000065
Other languages
English (en)
Japanese (ja)
Inventor
松本　聡
愛 渋谷
和子 伊澤
エルセット カイ
Original Assignee
学校法人 芝浦工業大学
株式会社Ｍｉｃｃ Ｔｅｃ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 学校法人 芝浦工業大学, 株式会社Ｍｉｃｃ Ｔｅｃ filed Critical 学校法人 芝浦工業大学
Priority to JP2014557387A priority Critical patent/JPWO2014112337A1/ja
Publication of WO2014112337A1 publication Critical patent/WO2014112337A1/fr

Abstract

La présente invention concerne : un matériau diélectrique qui permet la fabrication d'un condensateur double couche électrique sans nécessiter une procédure de fabrication coûteuse et consommant du temps; et un matériau diélectrique qui est apte à fournir un condensateur double couche électrique ou analogue ayant une performance de stockage d'électricité égale ou supérieure à celle d'un condensateur double couche électrique classique ou analogue. Un matériau diélectrique selon la présente invention est caractérisé en ce qu'il contient un oxyde de graphène à réduction, un acide inorganique et/ou un ester d'acide carbonique.
PCT/JP2014/000065 2013-01-15 2014-01-09 Matériau diélectrique et élément électrochimique utilisant celui-ci WO2014112337A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2014557387A JPWO2014112337A1 (ja) 2013-01-15 2014-01-09 誘電材料及びこれを用いた電気化学素子

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013-004227 2013-01-15
JP2013004227 2013-01-15

Publications (1)

Publication Number Publication Date
WO2014112337A1 true WO2014112337A1 (fr) 2014-07-24

Family

ID=51209435

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/000065 WO2014112337A1 (fr) 2013-01-15 2014-01-09 Matériau diélectrique et élément électrochimique utilisant celui-ci

Country Status (2)

Country Link
JP (1) JPWO2014112337A1 (fr)
WO (1) WO2014112337A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106158410A (zh) * 2016-08-20 2016-11-23 海南师范大学 一种氧化锌/石墨烯超级电容器复合电极材料的制备方法
WO2019176933A1 (fr) 2018-03-14 2019-09-19 株式会社Ｎｂｃメッシュテック Élément de maillage, tamis et plaque d'impression d'écran
JP7399407B2 (ja) 2019-09-04 2023-12-18 時空化学株式会社 パウチ型スーパーキャパシタ、正極材料及び負極材料

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011044310A1 (fr) * 2009-10-07 2011-04-14 Miltec Corporation Liants pour électrode, durcissant sous un rayonnement actinique ou un faisceau d'électrons, et électrodes comprenant ceux-ci
WO2011078462A2 (fr) * 2009-12-22 2011-06-30 Suh Kwang Suck Dispersion de graphène et composé de polymère liquide ionique-graphène
JP2012250880A (ja) * 2011-06-03 2012-12-20 Semiconductor Energy Lab Co Ltd グラフェン、蓄電装置および電気機器

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011044310A1 (fr) * 2009-10-07 2011-04-14 Miltec Corporation Liants pour électrode, durcissant sous un rayonnement actinique ou un faisceau d'électrons, et électrodes comprenant ceux-ci
WO2011078462A2 (fr) * 2009-12-22 2011-06-30 Suh Kwang Suck Dispersion de graphène et composé de polymère liquide ionique-graphène
JP2012250880A (ja) * 2011-06-03 2012-12-20 Semiconductor Energy Lab Co Ltd グラフェン、蓄電装置および電気機器

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106158410A (zh) * 2016-08-20 2016-11-23 海南师范大学 一种氧化锌/石墨烯超级电容器复合电极材料的制备方法
CN106158410B (zh) * 2016-08-20 2018-07-03 海南师范大学 一种氧化锌/石墨烯超级电容器复合电极材料的制备方法
WO2019176933A1 (fr) 2018-03-14 2019-09-19 株式会社Ｎｂｃメッシュテック Élément de maillage, tamis et plaque d'impression d'écran
JP7399407B2 (ja) 2019-09-04 2023-12-18 時空化学株式会社 パウチ型スーパーキャパシタ、正極材料及び負極材料

Also Published As

Publication number Publication date
JPWO2014112337A1 (ja) 2017-01-19

Similar Documents

Publication Publication Date Title
US10741335B2 (en) Partially surface-mediated lithium ion-exchanging cells and method for operating same
JP5322435B2 (ja) 蓄電デバイス用負極活物質
US10566668B2 (en) Sodium ion-based internal hybrid electrochemical energy storage cell
US9349542B2 (en) Stacks of internally connected surface-mediated cells and methods of operating same
Naoi et al. Second generation ‘nanohybrid supercapacitor’: Evolution of capacitive energy storage devices
US8889298B2 (en) Surface-mediated lithium ion-exchanging energy storage device
TWI429131B (zh) Storage element
US11545310B2 (en) High capacitance composites
US20130171502A1 (en) Hybrid electrode and surface-mediated cell-based super-hybrid energy storage device containing same
KR102235565B1 (ko) 2차원 Ni-유기구조체/rGO 복합체 및 이를 포함하는 이차전지 또는 슈퍼 커패시터용 전극
WO2019070568A2 (fr) Cellule hybride interne de stockage d'énergie électrochimique à base d'ions lithium ou sodium
JP2013054958A (ja) 非水電解質二次電池用負極材、リチウムイオン二次電池及び電気化学キャパシタ
ES2734883T3 (es) Dispositivos de almacenamiento y recolección de energía de alto rendimiento que contienen nanotubos exfoliados que han adjuntado partículas a nanoescala
JP2009205918A (ja) 蓄電デバイス
Aristote et al. General overview of sodium, potassium, and zinc-ion capacitors
Zeng et al. Nano-Sn doped carbon-coated rutile TiO 2 spheres as a high capacity anode for Li-ion battery
KR20130028423A (ko) 그래핀/금속산화물 나노 복합체를 이용한 슈퍼커패시터용 전극
WO2014112337A1 (fr) Matériau diélectrique et élément électrochimique utilisant celui-ci
WO2020080520A1 (fr) Condensateur, et électrode de condensateur
Parangi et al. Titanium dioxide as energy storage material: A review on recent advancement
KR20110000099A (ko) 수퍼커패시터 및 이의 제조방법
JP2006310412A (ja) リチウムイオンキャパシタ
KR101940405B1 (ko) 음극 활물질 및 그 음극 활물질을 포함하는 리튬이온 2차 전지 및 리튬이온 커패시터
Prabakaran et al. Innovative PANI/g-C3N4@ rGO nanocomposite electrode for improved energy storage and conversion applications
KR101627438B1 (ko) 결정성 탄소 구조체, 이의 제조방법, 및 이를 함유하는 에너지 저장소자

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14741058

Country of ref document: EP

Kind code of ref document: A1

DPE2 Request for preliminary examination filed before expiration of 19th month from priority date (pct application filed from 20040101)
ENP Entry into the national phase

Ref document number: 2014557387

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14741058

Country of ref document: EP

Kind code of ref document: A1