WO2014097938A1 - Ciment et ciment mélangé - Google Patents

Ciment et ciment mélangé Download PDF

Info

Publication number
WO2014097938A1
WO2014097938A1 PCT/JP2013/083158 JP2013083158W WO2014097938A1 WO 2014097938 A1 WO2014097938 A1 WO 2014097938A1 JP 2013083158 W JP2013083158 W JP 2013083158W WO 2014097938 A1 WO2014097938 A1 WO 2014097938A1
Authority
WO
WIPO (PCT)
Prior art keywords
cement
mass
mixed
gypsum
waste
Prior art date
Application number
PCT/JP2013/083158
Other languages
English (en)
Japanese (ja)
Inventor
修 久保田
大亮 黒川
宙 平尾
秀幸 菅谷
Original Assignee
太平洋セメント株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2012275980A external-priority patent/JP6045328B2/ja
Priority claimed from JP2013135434A external-priority patent/JP6021753B2/ja
Application filed by 太平洋セメント株式会社 filed Critical 太平洋セメント株式会社
Publication of WO2014097938A1 publication Critical patent/WO2014097938A1/fr

Abstract

La présente invention concerne : un ciment qui permet l'augmentation de la quantité d'utilisation d'un matériau de déchet qui peut être utilisé en tant que matière première pour un matériau brûlé (scories) et qui possède les mêmes propriétés physiques que celles du ciment Portland à haute résistance initiale ; et un ciment mélangé contenant du ciment. Un ciment qui comprend un produit pulvérisé d'un matériau brûlé ayant un module hydraulique (H.M.) de 2,10 à 2,30, un module de silice (S.M.) de 1,80 à 2,48, un module de fer (I.M.) de 1,3 à 2,6, et une teneur en 3CaO.SiO2 de 70,0 % en masse ou moins à 100 % en masse du matériau brûlé calculée selon la formule de Bogue et du gypse, le rapport de teneur du gypse dans 100 % en masse du ciment est de 1,2 % en masse ou plus en termes de teneur en SO3, et la quantité de gypse hémihydraté par rapport à la quantité totale de gypse dihydraté, et de gypse hémihydraté dans le ciment est de 30 % en masse ou plus en termes de teneur en SO3 ; et un ciment mélangé, qui comprend le ciment, et un matériau de mélange de ciment, le matériau de mélange de ciment comprenant une poudre fine de laitier de haut fourneau et/ou de la cendre de charbon.
PCT/JP2013/083158 2012-12-18 2013-12-11 Ciment et ciment mélangé WO2014097938A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2012-275980 2012-12-18
JP2012275980A JP6045328B2 (ja) 2012-12-18 2012-12-18 セメントおよびその製造方法
JP2013-135434 2013-06-27
JP2013135434A JP6021753B2 (ja) 2013-06-27 2013-06-27 混合セメント

Publications (1)

Publication Number Publication Date
WO2014097938A1 true WO2014097938A1 (fr) 2014-06-26

Family

ID=50978273

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/083158 WO2014097938A1 (fr) 2012-12-18 2013-12-11 Ciment et ciment mélangé

Country Status (2)

Country Link
TW (1) TW201437177A (fr)
WO (1) WO2014097938A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104072015A (zh) * 2014-07-18 2014-10-01 锦州市好为尔保温材料有限公司 一种用于酚醛泡沫保温板的抹面砂浆
JP2016064940A (ja) * 2014-09-24 2016-04-28 株式会社トクヤマ セメントクリンカーの製造方法
CN113072312A (zh) * 2021-05-22 2021-07-06 江西南氏锂电新材料有限公司 一种锂渣制备水泥的方法
TWI753785B (zh) * 2021-02-24 2022-01-21 林文欽 膠結材料製造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002234757A (ja) * 2001-02-06 2002-08-23 Taiheiyo Cement Corp セメントクリンカ及びセメント組成物
JP2011132111A (ja) * 2009-11-30 2011-07-07 Taiheiyo Cement Corp 水硬性組成物
JP2011207699A (ja) * 2010-03-30 2011-10-20 Ube Industries Ltd セメント組成物及びその製造方法並びに砒素含有廃棄物の処理方法
JP2012224504A (ja) * 2011-04-19 2012-11-15 Tokuyama Corp セメントクリンカー

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002234757A (ja) * 2001-02-06 2002-08-23 Taiheiyo Cement Corp セメントクリンカ及びセメント組成物
JP2011132111A (ja) * 2009-11-30 2011-07-07 Taiheiyo Cement Corp 水硬性組成物
JP2011207699A (ja) * 2010-03-30 2011-10-20 Ube Industries Ltd セメント組成物及びその製造方法並びに砒素含有廃棄物の処理方法
JP2012224504A (ja) * 2011-04-19 2012-11-15 Tokuyama Corp セメントクリンカー

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
GIJUTSU SHOIN: "Concrete Soran", 10 June 1998, pages: 15 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104072015A (zh) * 2014-07-18 2014-10-01 锦州市好为尔保温材料有限公司 一种用于酚醛泡沫保温板的抹面砂浆
JP2016064940A (ja) * 2014-09-24 2016-04-28 株式会社トクヤマ セメントクリンカーの製造方法
TWI753785B (zh) * 2021-02-24 2022-01-21 林文欽 膠結材料製造方法
CN113072312A (zh) * 2021-05-22 2021-07-06 江西南氏锂电新材料有限公司 一种锂渣制备水泥的方法

Also Published As

Publication number Publication date
TW201437177A (zh) 2014-10-01

Similar Documents

Publication Publication Date Title
JP6021753B2 (ja) 混合セメント
JP7218083B2 (ja) セメント組成物の製造方法
JP4176660B2 (ja) 水硬性組成物
WO2014097938A1 (fr) Ciment et ciment mélangé
JP5441768B2 (ja) 水硬性組成物
JP5932478B2 (ja) セメント組成物およびその製造方法
JP2000281399A (ja) セメントクリンカ及びセメント組成物
JP6316576B2 (ja) セメント組成物
JP4842211B2 (ja) セメント添加材用焼成物、セメント添加材及びセメント組成物
JP2010168256A (ja) セメント添加材及びセメント組成物
JP7042643B2 (ja) セメント組成物
JP2000344555A (ja) セメントクリンカ及びセメント組成物
JP2013107780A (ja) セメントクリンカおよびセメント組成物
JP6045328B2 (ja) セメントおよびその製造方法
JP2010195601A (ja) セメント組成物
JP2008222475A (ja) 焼成物、セメント添加材及びセメント組成物
JP4154359B2 (ja) コンクリート
JP2013087036A (ja) 低水和熱セメントクリンカおよび低水和熱セメント組成物
JP2005272222A (ja) コンクリート
JP2014185042A (ja) セメント組成物
JP6472280B2 (ja) 固化材及びその製造方法
JP4116987B2 (ja) 水硬性組成物
JP5235057B2 (ja) 焼成物、セメント添加材及びセメント組成物
JP4852506B2 (ja) セメント添加材及びセメント組成物
JP5501705B2 (ja) セメント添加材及びセメント組成物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13866354

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13866354

Country of ref document: EP

Kind code of ref document: A1