WO2014092318A1 - 점착 테이프 - Google Patents

점착 테이프 Download PDF

Info

Publication number
WO2014092318A1
WO2014092318A1 PCT/KR2013/008943 KR2013008943W WO2014092318A1 WO 2014092318 A1 WO2014092318 A1 WO 2014092318A1 KR 2013008943 W KR2013008943 W KR 2013008943W WO 2014092318 A1 WO2014092318 A1 WO 2014092318A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive tape
adhesive
polyurethane foam
foam layer
layer
Prior art date
Application number
PCT/KR2013/008943
Other languages
English (en)
French (fr)
Inventor
이재황
김장순
장애정
김지혜
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to US14/650,368 priority Critical patent/US10246612B2/en
Priority to CN201380064335.3A priority patent/CN104837943B/zh
Publication of WO2014092318A1 publication Critical patent/WO2014092318A1/ko

Abstract

제1 점착층, 약 0.1g/cm3 내지 약 0.5g/cm3의 밀도를 갖는 폴리우레탄 발포층 및 제2 점착층을 순차적으로 포함하는 점착 테이프를 제공한다.

Description

점착 테이프
점착 테이프에 관한 것이다.
전기 산업 또는 전자 산업에서 부품을 접착하거나, 고정하는 것은 중요한 문제이고, 특히 2개 이상의 강성 소재 또는 부품을 서로 접합하는 것에는 많은 어려움이 있다.
강성 소재 또는 부품을 접착하는 것의 예로는, 디스플레이의 터치 패널의 유리 등의 강성 재료 상에 폴리카보네이트 테두리를 부착하는 경우를 들 수 있다.
이와 같이 강성 소재 또는 부품 간의 접착시 점착 테이프의 양면에 각 소재 또는 부품을 적층하여 점착 테이프를 매개로 접합할 수 있다.
본 발명의 일 구현예는 TV 테두리 접착시 사용되어 내구성을 향상시킬 수 있는 점착 테이프를 제공한다.
본 발명의 일 구현예에서, 제1 점착층, 약 0.1g/cm3 내지 약 0.5g/cm3의 밀도를 갖는 폴리우레탄 발포층 및 제2 점착층을 순차적으로 포함하는 점착 테이프를 제공한다.
상기 폴리우레탄 발포층은 압축 강도가 약 100gf/in2 내지 약 2000gf/in2일 수 있다.
상기 폴리우레탄 발포층은 인장 강도가 약 2kgf/in2 내지 약 20kgf/in2일 수 있다.
상기 점착 테이프는 약 80℃에서 전단 강도가 약 0.3kg/㎠ 내지 약 1.0kg/㎠ 인일 수 있다.
상기 폴리우레탄 발포층의 두께가 약 0.2mm 내지 약 5.0mm일 수 있다.
상기 점착층은 아크릴계 점착제, 고무계 점착제, 실리콘계 점착제 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있다.
상기 점착 테이프는 TV 테두리 부착 용도로 사용될 수 있다.
상기 점착 테이프는 폭이 약 1mm 내지 약 7mm일 수 있다.
상기 점착 테이프는 TV 테두리 접착시 사용되어 휨 현상 및 탈착을 방지하여 빛샘 현상을 억제하고 내구성을 향상시킨다.
이하, 본 발명의 구현 예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구항의 범주에 의해 정의될 뿐이다.
본 발명의 일 구현예에서, 제1 점착층, 약 0.1g/cm3 내지 약 0.5g/cm3의 밀도를 갖는 폴리우레탄 발포층 및 제2 점착층을 순차적으로 포함하는 점착 테이프를 제공한다.
상기 점착 테이프는 상기 범위의 밀도를 갖는 연성의 폴리우레탄 발포층을 포함하여 응력 완화 특성이 부여된다.
구체적으로, 상기 폴리우레탄 발포층은 압축 강도가 약 100gf/in2 내지 약 2,000gf/in2일 수 있고, 또한, 상기 폴리우레탄 발포층은 인장 강도가 약 2kgf/in2 내지 약 20kgf/in2일 수 있다.
상기 폴리우레탄 발포층은 50미크론 내지 200미크론의 평균 직경을 갖는 기공을 포함할 수 있다.
상기 점착 테이프는 전자 부품의 부착하기 위한 매개체로 적용되고, 전술하 바와 같이 응력 완화 특성을 갖기 때문에 베젤폭이 좁은 TV 테두리 부착용으로 유용하다.
접착 대상의 두 물질 간 고온에서의 팽창률이 다를 경우 휨 현상, 탈착 등의 문제가 발생할 수 있는데, 상기 점착 테이프는 전술한 바와 같이 응력 완화 특성이 우수하기 때문에 이러한 문제를 억제할 수 있다. 예를 들어, 폴리카보네이트 재료의 TV 테두리를 유리 패널에 접착하는 경우 유리 패널의 반대 방향으로 휘게 되고, 나아가 이로 인한 탈착이 발생할 수 있으며, 그 결과 빛샘 현상이 초래될 수 있다. 상기 점착 테이프를 TV 테두리 부착 용도로 적용하게 되면 휨 현상, 탈착 등을 억제하여 내구성을 향상시킬 수 있을 뿐만 아니라 빛샘 현상을 억제할 수 있는 잇점이 있다.
상기 점착 테이프는 전술한 바와 같이 응력 완화 특성이 우수하기 때문에 TV 테두리 부착용으로 사용시 탈착을 방지하기 위해 요구되는 높은 수준의 고온 전단 강도를 필요로 하지 않게 된다. 구체적으로 상기 점착 테이프는 약 80℃에서 전단 강도가 약 0.3 kg/㎠ 이상 수준일 수 있고, 보다 구체적으로 약 0.4 kg/㎠ 내지 약 1.0 kg/㎠ 일 수 있다.
상기 폴리우레탄 발포층은 폴리우레탄 수지에 열팽창성 미립자를 포함시켜 이를 발포시켜 발포체를 제조하는 방법 등 공지된 방법에 따라 제조될 수 있다.
상기 폴리우레탄 발포층의 두께는 약 0.2mm 내지 약 5.0mm 일 수 있다. 상기 범위의 두께를 갖도록 상기 폴리우레탄 발포층을 포함하는 경우 소정의 응력 완화 특성 부여가 가능하고, 예를 들어 TV 테두리 부착용으로 사용하기에 적합할 수 있다.
상기 제1 점착층 및 상기 제2 점착층은 예를 들어 아크릴계 점착제, 고무계 점착제, 실리콘계 점착제 또는 이들의 조합을 적용하여 제조될 수 있고, 공지된 점착제가 제한 없이 사용될 수 있다.
구체적으로 상기 제1 점착층 및 상기 제2 점착층은 상기 범위의 고온 전단 강도를 가지도록 형성될 수 있다. 점착제의 경화의 정도를 조절함으로써 고온 전당 강도를 구현할 수 있다.
상기 점착 테이프는 전술한 바와 같이 응력 완화 특성이 우수하여 베젤폭이 좁은 TV 테두리 접착시 적용되어도 우수한 내구성을 구현하며, 빛샘 현상을 억제할 수 있다. 구체적으로 상기 점착 테이프는 베젤폭이 좁은 TV 테두리 용도로서 폭이 약 1mm 내지 약 7mm 일 수 있다.
이하 본 발명의 실시예 및 비교예를 기재한다. 그러한 하기한 실시예는 본 발명의 일 실시예일뿐 본 발명이 하기한 실시예에 한정되는 것은 아니다.
(실시예)
실시예 1
상기 아크릴계 점착제 조성물로 재1 점착층이 형성된 이형지 위에 폴리우레탄 발포층 형성용 조성물을 도포하고 경화시켜 두께 1.5㎜의 폴리우레탄 발포층을 연성으로 형성하였다. 상기 연성의 폴리우레탄 발포층의 밀도는 0.2 g/cm3이고, 압축 강도 (Texture analysis, stable micro systems)가 980 gf/in2 이고, 인장 강도 (Texture analysis, stable micro systems)가 9.1 kgf/in2이었다. 이어서, 상기 폴리우레탄 발포층 상부에 다시 아크릴계 점착제 조성물을 50㎛ 두께로 코팅한 후 건조하여 고형화시켜 제2 점착층을 형성한 후, 이형 처리된 PET를 적층하여 점착 테이프를 제조하였다.
실시예 2
실시예 1에서 사용한 접착제 아크릴계 조성물 대신 고무계 점착제 조성물을 이용하여 점착제를 형성 하였다. 상기 고무계 점착제 조성물은 SIS (styrene-isoprene-styrene)계 선형 블록 공중합체를 톨루엔 용제를 이용하여 고형분 20중량%의 시럽을 제조하였다. 여기에 점착 물성을 높이는 점착 증진제를 고무 100 중량부 대비 80중량부 첨가하여 한 시간 교반한 후, 상온에서 탈포시켰다. 실리콘 이형 PET에 코팅을 한 후, 80도 오븐에 1분, 110도 오븐에서 2분간 건조시켜 제1 점착층을 형성하였다.
이어서, 상기 실시예 1에서와 동일한 방법으로 폴리우레탄 발포층을 형성하고, 상기 고무계 점착제 조성물로 제2 점착층을 형성하여 점착 테이프를 제조하였다.
비교예 1
폴리우레탄 발포층의 밀도는 0.6 g/cm3 이고, 압축 강도가 2890 gf/in2 이고, 인장 강도가 28.28 kgf/in2 인 폴리우레탄 발포층을 경성으로 형성하여 제조한 점을 제외하고 상기 실시예 1에서와 동일한 방법으로 점착제 조성물을 제조하여 제1 점착층 및 제2 점착층을 형성하여 점착 테이프를 제조하였다.
비교예 2
폴리우레탄 발포층을 형성시킨 대신 폴리에틸렌 (PE) 발포층을 형성한 점을 제외하고는 실시예 1의 점착 테이프와 동일하게 제조하였다.
비교예 3
폴리우레탄 발포층 대신 폴리아크릴 발포층을 형성한 점을 제외하고 상기 실시예 2에서와 동일한 방법으로 고무계 점착제 조성물을 제조하여 제1 점착층 및 제2 점착층을 형성하여 점착 테이프를 제조하였다.
평가
실험예 1: 고온 전단 강도
실시예 1-2 및 비교예 1-3의 점착 테이프를 1cm×1cm 크기로 준비하여 각각의 양면을 유리 면 및 폴리카보네이트 면에 부착한 후 고온 챔버에 넣고 80℃에서 30분간 유지한 후 전단 강도를 측정하였다.
실험예 2: 빛샘 및 탈착 평가
폭 5mm의 폴리카보네이트 테두리를 실시예 1-2 및 비교예 1-3의 점착 테이프를 5mm로 재단하여 55인치 TV의 유리 패널에 상부에 부착하여 고정시켰다. 이어서, 상기 테두리가 부착된 TV를 60℃ 오븐에 넣고 240 시간 방치 후 빛샘 및 탈착이 발생하는지를 하기 기준에 따라 관찰하여 하기 표 1에 그 평가 결과를 기재하였다.
<빛샘 평가 기준>
○: 빛샘 현상 발생하지 않음
×: 빛샘 현상 발생함
<탈착 평가 기준>
○: 탈착이 발생하지 않음
×: 탈착이 발생함
표 1
구분 고온 전단 강도 (kg/㎠) 빛샘 평가 탈착 평가
실시예 1 0.54 ○ ○
실시예 2 0.56 ○ ○
비교예 1 0.34 ○ ×
비교예 2 1.20 × ○
비교예 3 1.76 × ○
상기 표 1에서 볼 수 있듯이, 실시예 1-2의 광학용 점착 필름은 빛샘 평가 및 탈착 평가 모두 우수하여 내구성이 우수함을 확인할 수 있었다.

Claims (8)

  1. 제1 점착층, 0.1g/cm3 내지 0.5g/cm3의 밀도를 갖는 폴리우레탄 발포층 및 제2 점착층을 순차적으로 포함하는 점착 테이프.
  2. 제1항에 있어서,
    상기 폴리우레탄 발포층은 압축 강도가 100gf/in2 내지 2000gf/in2인
    점착 테이프.
  3. 제1항에 있어서,
    상기 폴리우레탄 발포층은 인장 강도가 2kgf/in2 내지 20kgf/in2인
    점착 테이프.
  4. 제1항에 있어서,
    상기 점착 테이프는 80℃에서 전단 강도가 0.3kg/㎠ 내지 1.0kg/㎠인
    점착 테이프.
  5. 제1항에 있어서,
    상기 폴리우레탄 발포층의 두께가 0.2mm 내지 5.0mm인
    점착 테이프.
  6. 제5항에 있어서,
    상기 점착층은 아크릴계 점착제, 고무계 점착제, 실리콘계 점착제 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함하는
    점착 테이프.
  7. 제1항에 있어서,
    TV 테두리 부착 용도로 사용되는
    점착 테이프.
  8. 제1항에 있어서,
    폭이 1mm 내지 7mm인
    점착 테이프.
PCT/KR2013/008943 2012-12-11 2013-10-07 점착 테이프 WO2014092318A1 (ko)