WO2014025078A1 - 열경화가 가능한 공작용 고무찰흙 - Google Patents

열경화가 가능한 공작용 고무찰흙 Download PDF

Info

Publication number
WO2014025078A1
WO2014025078A1 PCT/KR2012/006348 KR2012006348W WO2014025078A1 WO 2014025078 A1 WO2014025078 A1 WO 2014025078A1 KR 2012006348 W KR2012006348 W KR 2012006348W WO 2014025078 A1 WO2014025078 A1 WO 2014025078A1
Authority
WO
WIPO (PCT)
Prior art keywords
rubber clay
rubber
clay
weight
platinum
Prior art date
Application number
PCT/KR2012/006348
Other languages
English (en)
French (fr)
Inventor
유정희
Original Assignee
대일소재(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 대일소재(주) filed Critical 대일소재(주)
Priority to PCT/KR2012/006348 priority Critical patent/WO2014025078A1/ko
Publication of WO2014025078A1 publication Critical patent/WO2014025078A1/ko

Abstract

본 발명은 열경화가 가능한 공작용 고무찰흙에 관한 것으로; 본 발명의 목적은 백금경화제를 첨가하여 열오븐기로 열을 가하면 만들어진 공작물이 경화되면서 탄성이 부여되어 장난감으로도 적합하도록 하는 것이다. 이를 위해 본 발명에 따른 공작용 고무찰흙에 의하면; 전체 고무찰흙 중량에 대하여 60 ~ 80%로 마련되며 실록산과 실리콘, 다이메틸, 메틸비닐, 비닐군-터미네이티드가 혼합되어 이루어진 젤상태의 실리콘베이스와; 전체 고무찰흙 중량에 대하여 15 ~ 35%로 마련되며 파우더 형태의 실리카계로 이루어져 경도를 조절하는 가소도 조절제와; 전체 고무찰흙 중량에 대하여 1 ~ 5%로 마련되며 폴리다이메틸실록산계로 이루어져 고화를 방지하기 위한 오일 형태의 고화방지제와; 전체 고무찰흙 중량에 대하여 0.1 ~ 1%로 마련되며 세균번식을 방지하기 위한 항균제와; 전체 고무찰흙 중량에 대하여 0.65 ~ 5%로 마련되는 백금경화제를; 혼합하여 이루어지는 것을 특징으로 한다.

Description

열경화가 가능한 공작용 고무찰흙
본 발명은 공작용 고무찰흙에 관한 것으로; 더욱 상세하게는 끈적임이 없어 손에 묻지 않고 수공예로 공작물을 만든 후에 장시간 방치하여도 굳지 않아 재사용이 가능한 것은 물론이며 공작물을 경화시켜 장난감으로도 활용할 수 있는 열경화가 가능한 공작용 고무찰흙에 관한 것이다.
일반적으로 공작용 고무찰흙(일명, 고무점토)은 어린이들이 손쉽게 공작놀이를 할 수 있도록 만들어진 것으로, 유성 고무찰흙 또는 수성 고무찰흙 등으로 제조 및 판매되고 있다.
유성 고무찰흙은 공작 조형물을 제작한 후 보관시 모형 그대로 형태를 유지할 수 있으나, 고무찰흙이 단단하여 어린이들이 이를 사용하여 공작 조형물을 제작하기가 어려운 문제점이 있다.
또한, 수성 고무찰흙은 반죽이 용이하여 어린이들이 놀이용도로 사용하기가 용이한 반면에, 수분 함량이 많아 제작시 끈적임 현상이 심하고 건조되었을 때 수축 및 뒤틀림 현상이 발생하여 장기간 보관이 어려운 문제점이 있다.
또한, 상기의 유성 고무찰흙 및 수성 고무찰흙은 공작물을 제작한 후 방치하면 쉽게 굳어 재사용이 불가능한 문제점이 있으며, 유성 고무찰흙이나 수성 고무찰흙으로 공작물을 제작한 후에 영구보관을 목적으로 오븐기를 이용하여 건조과정을 거치면 경화가 급속하게 진행되어 공작물에 균열이 발생하는 문제점이 있다.
본 발명은 이러한 문제점을 해결하기 위한 것으로; 본 발명의 목적은 백금경화제를 첨가하여 열오븐기로 건조하게 되면 만들어진 공작물이 경화되면서 탄성이 부여되어 장난감으로도 적합한 『열경화가 가능한 공작용 고무찰흙』을 제공하는 것이다.
본 발명의 다른 목적은 투명도가 우수한 실리콘베이스와 고화방지제를 사용하여 제조과정에서 끈적임이 없고, 공작물을 만든 후에도 굳지 않는『열경화가 가능한 공작용 고무찰흙』을 제공하는 것이다.
본 발명의 또 다른 목적은 항균제가 함유되어 세균 증식을 억제할 수 있는 『열경화가 가능한 공작용 고무찰흙』을 제공하는 것이다.
이러한 목적을 달성하기 위한 본 발명은; 공작용도로 사용할 수 있는 무기화합물로 이루어진 공작용 고무찰흙에 있어서;
상기 고무 찰흙이; 전체 고무찰흙 중량에 대하여 60~80%로 마련되며 실록산과 실리콘, 다이메틸, 메틸비닐, 비닐군-터미네이티드가 혼합되어 이루어진 젤상태의 실리콘베이스와; 전체 고무찰흙 중량에 대하여 15~35%로 마련되며 파우더 형태의 실리카계로 이루어져 경도를 조절하는 가소도 조절제와; 전체 고무찰흙 중량에 대하여 1~5%로 마련되며 폴리다이메틸실록산계로 이루어져 고화를 방지하기 위한 오일 형태의 고화방지제와; 전체 고무찰흙 중량에 대하여 0.1~1%로 마련되며 세균번식을 방지하기 위한 항균제와; 전체 고무찰흙 중량에 대하여 0.65~5%로 마련되는 백금경화제를; 혼합하여 이루어지는 것을 특징으로 한다.
또한, 본 발명은; 상기 백금경화제가 전체 고무찰흙 중량에 대하여 0.15~1.5%로 마련되는 백금촉매와; 전체 고무찰흙 중량에 대하여 0.5~3.5%로 마련되는 가교결합제로; 이루어지는 것을 특징으로 한다.
또한, 본 발명은 상기 백금촉매는 아래의 구조식을 갖는 것을 특징으로 한다.
Figure PCTKR2012006348-appb-I000001
상기와 같은 혼합물로 이루어진 본 발명에 따른 『열경화가 가능한 공작용 고무찰흙』에 의하면; 백금경화제가 첨가되어 열오븐기로 건조하는 과정에서 경화됨과 동시에 탄성이 부여되어 장난감으로도 적합한 공작물을 제공할 수 있는 탁월한 효과를 나타낸다.
또한, 본 발명에 따른 『열경화가 가능한 공작용 고무찰흙』의하면; 투명도가 우수한 실리콘베이스와 고화방지제를 사용하여 제조과정에서 끈적임이 없고, 공작물로 제조된 후에도 굳지 않는 탁월한 효과를 나타낸다.
또한, 본 발명에 따른 『열경화가 가능한 공작용 고무찰흙』의하면; 항균제가 함유되어 세균의 증식이 억제되는 탁월한 효과를 나타낸다.
도 1은 본 발명에 사용되는 백금촉매의 구조식을 나타낸 것이다.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.
본 발명에 따른 열경화가 가능한 공작용 고무찰흙은 실리콘 베이스, 가소도 조절제, 고화방지제, 항균제 및 백금경화제가 혼합되어 이루어지며, 전체 고무찰흙 중량에 대하여 실리콘 베이스 60 내지 80 중량부, 가소도 조절제 15 내지 35 중량부, 고화방지제 1 내지 5 중량부, 항균제 0.1 내지 1 중량부 및 백금경화제 0.65 내지 5 중량부로 이루어지는 것이 더욱 바람직하다.
상기 실리콘 베이스는 60 내지 80 중량부가 함유되며, 실록산과 실리콘(Siloxanes and silicones), 디메틸(Dimethly), 메틸비닐(methylvinyl) 및 비닐군-터미네이티드(vinyl group-terminated)로 이루어지는데, 상기의 성분으로 이루어진 실리콘 베이스는 공작용 고무찰흙의 형상을 유지해 주는 역할을 한다.
이때, 상기 실리콘 베이스는 화학물질서비스요약번호(CAS No) 68083-18-1의 실록산과 실리콘(Siloxanes and silicones), 디메틸(Dimethly), 메틸비닐(methylvinyl) 및 비닐군-터미네이티드(vinyl group-terminated)를 채택하였다.
이러한 실리콘 베이스는 전체 공작용 고무찰흙 중량에 대해 60 내지 80 중량부로 함유되어야 성형을 용이하게 할 수 있고 형태를 유지할 수 있는데, 80 중량부를 초과하여 함유되면 공작물의 성형성은 향상되나 공작물을 만든 후에 방치하면 형상이 쉽게 변형된다.
상기 가소도 조절제는 전체 고무찰흙 중량에 대하여 15 내지 35 중량부가 함유되며, 파우더 형태의 실리카계로 이루어지는데, 공작용 고무 찰흙에 함유되어 공작용 고무 찰흙의 가소도(경도)를 결정하는 역할을 한다.
이때, 상기 가소도 조절제는 실리카의 입자가 5 내지 50,000 밀리마이크론(Millimicron)의 파우더 형태이며, 화학물질서비스요약번호(CAS No) 7631-86-9의 이산화실리콘(Silicone Dioxide)을 사용하는 것이 바람직하다.
또한, 상기 실리카는 입자가 5 내지 20 밀리마이크론(Millimicron)인 건식실리카 및 입자가 20 내지 2,000 밀리마이크론(Millimicron)인 습식실리카, 입자가 2,000 내지 50,000 밀리마이크론(Millimicron)인 규조토로 이루어진 그룹으로부터 선택된 하나 이상으로 이루어질 수도 있다.
상기 건식실리카(Fumed Silica)는 투명도가 아주 우수하여 여러 가지 색상을 맑게 표현할 수 있는 장점이 있으며, 습식실리카(Precipitated Silica)는 투명도가 매우 우수하지는 않지만 색상을 맑게 표현할 수 있다.
또한, 상기 규조토(Diatomaceous Earth)는 자체 색상이 연한 회색 또는 베이지 색상을 띠기 때문에 맑은 색상을 내기에는 부적합하나, 어두운 색상을 표현하기에는 적합하다.
상기 고화방지제는 전체 고무찰흙 중량에 대하여 1 내지 5 중량부가 함유되며, 폴리디메틸실록산계로 이루어지며, 상기 공작용 고무찰흙에 함유되어 공작용 고무찰흙의 고화를 방지하는 역할을 한다.
또한, 상기 고화방지제는 투명한 오일(oil)의 형태이며, 화학물질서비스요약번호(CAS No) 63148-62-9의 폴리디메틸실록산(Polydimethylsiloxane)를 사용하는 것이 바람직하다.
상기의 성분으로 이루어진 고화방지제는 시간이 지남에 따라 공작용 고무찰흙이 경화되어 고화되는 것을 지연시키면서 공작용 고무찰흙을 유연하게 하는 윤활제의 역할을 한다.
또한, 폴리디메틸실록산으로 이루어진 고화방지제는 여성용 화장품 등에 폭넓게 사용되며, 공작용 고무찰흙의 고화를 방지할 뿐만 아니라, 공작용 고무찰흙 의 표면에 윤기와 밝기를 밝게 하는 역할을 한다.
상기 항균제는 전체 고무찰흙 중량에 대하여 0.1 내지 1 중량부가 함유되며, 상기 공작용 고무찰흙에서 세균이 증식하는 것을 방지하는 역할을 하는데, 상기 공작용 고무찰흙에 항균성을 부여할 수 있는 것이면 액상형이나 파우더 형 등 어떠한 것이든 사용 가능하며, 이러한 항균제를 함유한 공작용 고무찰흙은 제조가 완료된 후에 세균의 증식이 억제되어 공작용 고무찰흙을 장난감으로 가지고 노는 사용자가 세균으로부터 감염되는 것을 차단하는 역할을 한다.
상기 백금경화제는 전체 고무찰흙 중량에 대하여 0.65 내지 5 중량부가 함유되며, 공작용 고무찰흙으로 만들어진 공작물을 오븐기로 건조하는 과정에서 공작물이 경화됨과 동시에 탄성을 갖도록 하는 역할을 하며, 탄성이 부여된 공작물을 건조과정이 완료된 후에 장난감으로도 적합한 특성을 갖는다.
상기 백금경화제의 함량이 0.65 중량부 미만으로 함유되면 공작용 고무찰흙이 잘 굳지 않아 공작물이 제조된 후에도 외력에 의해 변형이 발생할 수 있기 때문에 장기관 보관이 어렵고, 백금경화제의 함량이 5 중량부를 초과하게 되면 경화시간이 지나치게 짧아 공작물을 제조하는 과정에서 굳어지게 된다.
이러한 백금경화제는 전체 고무찰흙 중량에 대하여 0.15 내지 1.5 중량부의 백금촉매와 전체 고무찰흙 중량에 대하여 0.5 내지 3.5 중량부의 가교결합제(架橋結合; cross-link)로 이루어지는데, 백금촉매는 아래 도 1과 같은 구조로 이루어지는 것을 사용하는 것이 바람직하며, 비닐그룹이 말단에 치환된 오가노비닐폴리실록산과, 실리콘 원소에 수소원소가 직접 결합되어 있는 오가노하이드로겐폴리실록산을 경화시키게 된다.
본 발명에서 백금경화제를 이루는 백금촉매는 Siloxanesandsilicones, di-Me, Mevinyl, vinylgroup-terminated에 Platinate(2-), hexachloro-,(OC-6-11)-dihydrogenreaction productswith2, 4, 6, 8-terraethenyl-2, 4 , 6 ,8-tetramethylcyclotetrasiloxane 등이 혼합되어 이루어진 것이다. 그리고 본 발명에서 백금경화제를 이루는 가교결합제는 Siloxanesandsilicones,di-Me,Mevinyl,vinylgroup-terminated와, Siloxanes and silicones,di-Me,mMe hydrogen와, Dichlorodimethylsilane reaction products with silica와, 1,3,5-Triazine-2,4,6(1H,3H,5H)trione,1,3,5-tri-2-propenyl-와, 1-Ethynylcyclohexanol 등이 혼합되어 이루어진 것이다.
또한, 본 발명에 따른 공작용 고무 찰흙은 색상안료나 축광제를 더 포함하여 이루어질 수도 있다.
상기 색상안료는 유기화합물이 주성분이며, 전체 고무찰흙 중량에 1 내지 3 중량부가 함유되어 투명도가 우수한 실리콘 베이스 조성물에 칼라(색상)를 부여하는 역할을 한다.
상기의 공작용 고무 찰흙은 실리콘 베이스, 가소도 조절제, 고화방지제, 항균제 및 백금경화제만을 혼합하여 공작용 고무찰흙을 제조하면 맑은 투명색이며, 여기에 레드, 그린 및 블루 등의 색을 띠는 색상안료를 혼합하면 다양한 칼라를 갖는 공작용 고무 찰흙을 제조할 수 있다.
상기 축광제는 전체 고무찰흙 중량에 대하여 1 내지 10 중량부가 함유되며, 입자가 3 내지 10,000 밀리마이크론인 알루미늄계 축광제를 혼합하면, 스스로 빛 에너지를 축적하였다가 어두울 때 빛을 발산하는 야광 공작물을 제작할 수 있다.
본 발명의 실시예에서는 축광제로 알루미늄 계열을 채택하였으나, 이외에도 다양한 종류의 축광제를 선택하여 적용할 수 있음은 물론이다.
이하에서는, 상기와 같은 조성물을 이용한 본 발명에 따른 열경화가 가능한 공작용 고무찰흙의 제조공정 방법 및 물성을 실시예를 들어 설명한다.
<실시예 1>
실리콘 베이스 68 중량부, 가소도 조절제 27 중량부, 고화방지제 3 중량부, 항균제 1 중량부 및 백금경화제 1 중량부를 혼합하고 반죽하여 공작용 고무찰흙을 제조하였다.
<비교예 1>
실리콘 베이스 82 중량부, 가소도 조절제 13 중량부, 고화방지제 3 중량부, 항균제 1 중량부 및 백금경화제 1 중량부를 혼합하고 반죽하여 공작용 고무찰흙을 제조하였다.
<비교예 2>
실리콘 베이스 38 중량부, 가소도 조절제 57 중량부, 고화방지제 3 중량부, 항균제 1 중량부 및 백금경화제 1 중량부를 혼합하고 반죽하여 공작용 고무 찰흙을 제조하였다.
상기의 실시예 1 및 비교예 1 내지 2를 통해 제조된 공작용 고무찰흙의 가소도 경시변화(단위:1/100㎜)를 측정하여 아래 표 1에 나타내었다.
(단, 시험기준으로 사용되는 가소도계는 2개의 평행선반 사이에 시료를 넣고 정해진 하중을 가하여 시간과 두께변화를 다이얼표시기(Dial Indicator)로 읽어 가소도를 구하는 것으로;
① 규격 : ASTMD-926
② 형식 : 윌리암스식(Williams Type)
③ 표준사양 : 가압하중:5Kg, 가압면적:직경 60mm,
다이얼게이지: Stroke 15mm 이상, 본체 중량: 약 10kg
④시료 준비 : 시료 두께 10mm, 원통직경 16mm
⑤시험방법 : a. 다이얼표시기를 영점에 맞춘다.
b. 시험기 환경온도가 안정될 때까지 기다린다.
c. 두 평행선반 사이에 빠르게 시료를 넣는다.
d. 측정하고자 하는 시간이 지난 후에 게이지를 읽는다.
표 1
구분 1일 2일 3일 4일 5일 비고
실시예 1 206 182 189 196 195 오랜시간이 지나도 공작후 제품형태가 유지됨
비교예 1 209 191 191 198 190 가소도가 너무 낮아 공작후 작품이 일그러짐
비교예 2 실험불가 제품이 만들어지지 않음
위에 [표 1]에 나타낸 것처럼 실시예 1을 통해 제조된 공작용 고무찰흙은 상온에서 오랜시간 방치하여도 전혀 굳지 않았으며, 가소도가 적정하여 제품으로 공작물을 성형하여도 제품 모형이 잘 일그러지지 않아 공작물의 성형을 용이하여 장기간 보관이 가능하였다.
그러나 비교예 1을 통해 제조된 공작용 고무 찰흙은 상온에서 오랜 시간 방치되도 전혀 굳지 않았으며, 가소도가 너무 낮아 공작물을 성형해도 공작물의 모형이 일그러지며, 비교예 2를 통해 제조된 공작용 고무찰흙은 제품이 만들어지지 않고 부서지기 때문에 공작물의 제조가 불가능하였다.
상기 실시예 1을 통해 제조된 공작용 고무찰흙과 타사제품의 가소도 경시변화(단위:1/100㎜)를 측정하여 아래 표 2에 나타내었다.
표 2
구분 1일 2일 3일 4일 5일 비고
실시예 1 206 182 189 196 195 오랜시간이 지나도 굳지 않음
A사 제품 214 269 446 746 568 1일 경과후 표면이 굳어공작물이 부서짐
B사 제품 267 430 473 554 427 1일 경과후 표면이 굳어 공작물이 부서짐
C사 제품 707 716 692 694 702 처음부터 가소도가 너무 높음
위에 [표 2]에서 알 수 있듯이, 본 발명에 따른 공작용 고무찰흙의 경우 측정에 약간의 오차는 있겠지만, 오랜 시간 상온에 방치하여도 가소도의 큰 변화가 없어 언제든지 공작이 가능한데, 반면, A사 제품의 경우는 시간이 지날수록 가소도가 향상되어 1일 이상 경과하면 표면에 균열이 발생하여 공작이 불가능하며, B사 제품의 경우는 시간이 경과함에 따라 가소도가 증가하여, 1일 이상이 경과하면 표면이 스펀지처럼 굳어 공작이 불가능하고, C사 제품의 경우는 처음부터 가소도가 높아 유아나 어린이가 공작물을 만들기에는 매우 부적합하였다.
<실시예 2>
실리콘 베이스 68 중량부, 가소도 조절제 27 중량부, 고화방지제 3 중량부, 항균제 1 중량부 및 백금경화제(도 1에 나타낸 백금촉매 0.5 중량부 및 가교결합제 2 중량부)를 반죽하고, 열오븐기를 이용하여 200℃의 온도에서 10분 동안 공작용 고무찰흙을 가열하였다.
<비교예 3>
실시예 2와 동일하게 진행하되, 도 1에 나타낸 백금촉매 0.1 중량부 및 1-에틸시클로헥사놀 0.5 중량부로 이루어진 백금경화제를 혼합하여 제조된 공작용 고무 찰흙을 가열하였다.
<비교예 4>
실시예 2와 동일하게 진행하되, 도 1에 나타낸 백금촉매 1.7 중량부 및 가교결합제 4 중량부로 이루어진 백금경화제를 혼합하여 제조된 공작용 고무 찰흙을 가열하였다.
상기의 실시예 2 및 비교예 3 내지 4를 통해 가열된 고무찰흙의 상태를 확인하여 아래 표 3에 나타내었다.
표 3
구분 백금경화제 함량(%) 온도(℃) 가열시간(분) 공작용 찰흙상태
실시예 2 백금촉매 0.1 200 10 실리콘 찰흙이 굳지않음
1-에틸시클로헥사놀 0.4
실시예 3 백금촉매 0.5 원하는 모양을 유지하며 굳어짐
1-에틸시클로헥사놀 2.0
실시예 4 백금촉매 1.7 작업성이 좋지 않아 작업도중 굳어버림
1-에틸시클로헥사놀 4.0
위에 [표 3]에 나타낸 것처럼 본 발명의 실시예 2에 사용된 백금경화제는 백금촉매와 가교결합제가 적절한 함량으로 혼합되어, 제조가 완료된 공작물을 오븐기에 넣고 가열하게 되면 공작용 고무찰흙이 잘 경화되도록 하고, 공작용 고무찰흙에 탄성을 부여하여 장난감으로 사용가능하며, 영구적으로 보존이 가능한 공작용 고무찰흙을 제공하는 역할을 한다.
본 발명은 실리콘을 주재료로 하여 끈적임이 없으며 공작물을 만든 후 장시간 방치하여도 딱딱하게 굳지 않아 재사용이 가능한 공작용 고무찰흙 분야에 광범위하게 이용될 수 있다.

Claims (3)

  1. 공작용도로 사용할 수 있는 무기화합물로 이루어진 공작용 고무찰흙에 있어서;
    상기 고무 찰흙은;
    전체 고무찰흙 중량에 대하여 60 ~ 80%로 마련되며 실록산과 실리콘, 다이메틸, 메틸비닐, 비닐군-터미네이티드가 혼합되어 이루어진 젤상태의 실리콘베이스와;
    전체 고무찰흙 중량에 대하여 15 ~ 35%로 마련되며 파우더 형태의 실리카계로 이루어져 경도를 조절하는 가소도 조절제와;
    전체 고무찰흙 중량에 대하여 1 ~ 5%로 마련되며 폴리다이메틸실록산계로 이루어져 고화를 방지하기 위한 오일 형태의 고화방지제와;
    전체 고무찰흙 중량에 대하여 0.1 ~ 1%로 마련되며 세균번식을 방지하기 위한 항균제와;
    전체 고무찰흙 중량에 대하여 0.65 ~ 5%로 마련되는 백금경화제를; 혼합하여 이루어지는 것을 특징으로 하는 열경화가 가능한 공작용 고무찰흙.
  2. 제 1항에 있어서,
    상기 백금경화제는;
    전체 고무찰흙 중량에 대하여 0.15 ~ 1.5%로 마련되는 백금촉매와;
    전체 고무찰흙 중량에 대하여 0.5 ~ 3.5%로 마련되는 가교결합제로; 이루어지는 것을 특징으로 하는 열경화가 가능한 공작용 고무찰흙.
  3. 제 2항에 있어서,
    상기 백금촉매는 아래의 구조식을 갖는 것을 특징으로 하는 열경화가 가능한 공작용 고무찰흙.
    Figure PCTKR2012006348-appb-I000002
PCT/KR2012/006348 2012-08-09 2012-08-09 열경화가 가능한 공작용 고무찰흙 WO2014025078A1 (ko)