WO2014008322A1 - Blindage thermique souple avec mousse au silicone pour dispositifs de sécurité gonflables - Google Patents

Blindage thermique souple avec mousse au silicone pour dispositifs de sécurité gonflables Download PDF

Info

Publication number
WO2014008322A1
WO2014008322A1 PCT/US2013/049184 US2013049184W WO2014008322A1 WO 2014008322 A1 WO2014008322 A1 WO 2014008322A1 US 2013049184 W US2013049184 W US 2013049184W WO 2014008322 A1 WO2014008322 A1 WO 2014008322A1
Authority
WO
WIPO (PCT)
Prior art keywords
fabric
layer
composite sheet
barrier layer
fabric layer
Prior art date
Application number
PCT/US2013/049184
Other languages
English (en)
Inventor
William Blackwood
Lawrence Joseph Rapson
Original Assignee
Dow Corning Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Corning Corporation filed Critical Dow Corning Corporation
Publication of WO2014008322A1 publication Critical patent/WO2014008322A1/fr

Abstract

L'invention porte sur un dispositif de sécurité de véhicule gonflable (1), lequel dispositif comprend un gonfleur (10), un compartiment de fluide et un blindage thermique. Le gonfleur (10) est apte à délivrer un fluide de gonflage (15) utilisé pour gonfler le compartiment de fluide. Le blindage thermique, qui est disposé à l'intérieur du compartiment de fluide, comprend une couche de tissu et une couche de barrière thermique disposée au voisinage du film. La couche de barrière comprend au moins une couche de mousse au silicone cellulaire. Le blindage thermique a une valeur de résistance thermique de six secondes ou plus à 725°C, testée dans un test de résistivité thermique à tige chaude.
PCT/US2013/049184 2012-07-06 2013-07-03 Blindage thermique souple avec mousse au silicone pour dispositifs de sécurité gonflables WO2014008322A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201261668702P 2012-07-06 2012-07-06
US61/668,702 2012-07-06

Publications (1)

Publication Number Publication Date
WO2014008322A1 true WO2014008322A1 (fr) 2014-01-09

Family

ID=48914409

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2013/049184 WO2014008322A1 (fr) 2012-07-06 2013-07-03 Blindage thermique souple avec mousse au silicone pour dispositifs de sécurité gonflables

Country Status (1)

Country Link
WO (1) WO2014008322A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9312416B2 (en) 2012-11-12 2016-04-12 Dow Corning Corporation Method of forming an electronic article
DE102017106498A1 (de) * 2017-03-27 2018-09-27 Trw Automotive Gmbh Gassack für ein Sicherheitssystem in Fahrzeugen
US10392743B2 (en) 2012-11-12 2019-08-27 Dow Silicones Corporation Flexible heat shield with silicone elastomer and a topcoat for inflatable safety devices
WO2020139805A1 (fr) 2018-12-28 2020-07-02 Dow Brasil Sudeste Industrial Ltda. Article composite pour appareil isolant, appareil comprenant un article composite, et procédé associé
US11465582B2 (en) 2018-03-13 2022-10-11 Toyobo Co., Ltd. Base fabric for coated airbag, manufacturing method therefor, and coating composition used for said manufacturing method

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4433069A (en) 1983-01-03 1984-02-21 Dow Corning Corporation Method for preparing flame resistant polysiloxane foams and foams prepared thereby
GB2225291A (en) * 1988-07-13 1990-05-30 Gen Engineering Crash restraint bags for vehicles
WO1990015713A1 (fr) * 1989-06-16 1990-12-27 W.L. Gore & Associates, Inc. Sacs d'air en stratifies et leurs procedes de fabrication
US5574073A (en) 1996-01-17 1996-11-12 Dow Corning Corporation Curable silicone compositions which are foams or elastomers
EP0763621A2 (fr) * 1995-09-18 1997-03-19 Toray Industries, Inc. Tissu de base pour airbags, son procédé de fabrication et airbag le comprenant
US5670556A (en) 1996-12-16 1997-09-23 Dow Corning Corporation Foamable siloxane compositions and silicone foams prepared therefrom
US5708043A (en) 1996-12-17 1998-01-13 Dow Corning Corporation Foamable siloxane compositions and silicone foams prepared therefrom
US5733946A (en) 1996-12-17 1998-03-31 Dow Corning Corporation Foamable siloxane compositions and silicone foams prepared therefrom
US6084002A (en) 1999-02-02 2000-07-04 Dow Corning Corporation Flame retardant silicone foams
WO2001034435A1 (fr) * 1999-11-10 2001-05-17 Milliken & Company Revetements pour airbags offrant une resistance thermique amelioree
EP1591325A1 (fr) * 2004-04-30 2005-11-02 Highland Industries, Inc. Tissue de sac gonflable revêtu
WO2011082134A1 (fr) 2009-12-30 2011-07-07 Dow Corning Corporation Composition d'enduction à base de silicone pour des coussins de sécurité gonflables
WO2011137121A1 (fr) 2010-04-30 2011-11-03 Dow Corning Toray Co., Ltd. Composition de caoutchouc de silicone liquide durcissable et étoffe tissée revêtue du produit durci obtenu à partir de cette composition

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4433069A (en) 1983-01-03 1984-02-21 Dow Corning Corporation Method for preparing flame resistant polysiloxane foams and foams prepared thereby
GB2225291A (en) * 1988-07-13 1990-05-30 Gen Engineering Crash restraint bags for vehicles
WO1990015713A1 (fr) * 1989-06-16 1990-12-27 W.L. Gore & Associates, Inc. Sacs d'air en stratifies et leurs procedes de fabrication
EP0763621A2 (fr) * 1995-09-18 1997-03-19 Toray Industries, Inc. Tissu de base pour airbags, son procédé de fabrication et airbag le comprenant
US5574073A (en) 1996-01-17 1996-11-12 Dow Corning Corporation Curable silicone compositions which are foams or elastomers
US5670556A (en) 1996-12-16 1997-09-23 Dow Corning Corporation Foamable siloxane compositions and silicone foams prepared therefrom
US5708043A (en) 1996-12-17 1998-01-13 Dow Corning Corporation Foamable siloxane compositions and silicone foams prepared therefrom
US5733946A (en) 1996-12-17 1998-03-31 Dow Corning Corporation Foamable siloxane compositions and silicone foams prepared therefrom
US6084002A (en) 1999-02-02 2000-07-04 Dow Corning Corporation Flame retardant silicone foams
WO2001034435A1 (fr) * 1999-11-10 2001-05-17 Milliken & Company Revetements pour airbags offrant une resistance thermique amelioree
EP1591325A1 (fr) * 2004-04-30 2005-11-02 Highland Industries, Inc. Tissue de sac gonflable revêtu
WO2011082134A1 (fr) 2009-12-30 2011-07-07 Dow Corning Corporation Composition d'enduction à base de silicone pour des coussins de sécurité gonflables
WO2011137121A1 (fr) 2010-04-30 2011-11-03 Dow Corning Toray Co., Ltd. Composition de caoutchouc de silicone liquide durcissable et étoffe tissée revêtue du produit durci obtenu à partir de cette composition

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9312416B2 (en) 2012-11-12 2016-04-12 Dow Corning Corporation Method of forming an electronic article
US10392743B2 (en) 2012-11-12 2019-08-27 Dow Silicones Corporation Flexible heat shield with silicone elastomer and a topcoat for inflatable safety devices
DE102017106498A1 (de) * 2017-03-27 2018-09-27 Trw Automotive Gmbh Gassack für ein Sicherheitssystem in Fahrzeugen
US11465582B2 (en) 2018-03-13 2022-10-11 Toyobo Co., Ltd. Base fabric for coated airbag, manufacturing method therefor, and coating composition used for said manufacturing method
WO2020139805A1 (fr) 2018-12-28 2020-07-02 Dow Brasil Sudeste Industrial Ltda. Article composite pour appareil isolant, appareil comprenant un article composite, et procédé associé
US12098851B2 (en) 2018-12-28 2024-09-24 Dow Brasil Sudeste Industrial Ltda. Composite article for insulating appliance, appliance comprising composite article, and related method

Similar Documents

Publication Publication Date Title
CA2888358C (fr) Ecran thermique souple avec elastomere de silicone et un revetement de surface pour dispositifs de securite gonflables
CN1104521C (zh) 具有涂层的纺织织物
EP2382271B2 (fr) Compositions de revêtement et tissus recouverts avec ces compositions
EP1332254B1 (fr) Compositions de revetement et toiles textiles revetues de celles-ci
EP1505132B1 (fr) Cossin gonflable avec des compositions de mélanges de polymère pour revêtement
WO2014008322A1 (fr) Blindage thermique souple avec mousse au silicone pour dispositifs de sécurité gonflables
KR101414895B1 (ko) 액상 실리콘 고무 코팅제 조성물, 커튼 에어백 및 그의제조 방법
JP3999987B2 (ja) エアバッグコーティング用シリコーン組成物
JP2018104560A (ja) コーティング用シリコーンゴム組成物
WO2018082876A1 (fr) Composition de caoutchouc de silicone pour revêtement de coussin de sécurité gonflable
JP5142071B2 (ja) 液状シリコーンゴムコーティング剤組成物、カーテンエアーバッグ及びその製造方法
JP5170433B2 (ja) エアーバッグ用液状シリコーンゴムコーティング剤組成物、エアーバッグ及びその製造方法
JP6518590B2 (ja) 膨張可能な安全装置のためのシリコーンエラストマー及びトップコートを有する可撓性熱シールド
US11332855B2 (en) Heat resistant reinforcing cloth for airbag
JP2004149992A (ja) エアバック用基布
JP5179932B2 (ja) エアバッグ
KR20240107180A (ko) 에어백용 실리콘 코팅
WO2024119508A1 (fr) Revêtements de silicone
EP4172007A1 (fr) Dispositifs de sécurité gonflables
JP5162266B2 (ja) エアバッグ

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13744862

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13744862

Country of ref document: EP

Kind code of ref document: A1