Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L71/00—Compositions of polyethers obtained by reactions forming an ether link in the main chain; Compositions of derivatives of such polymers
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D127/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Coating compositions based on derivatives of such polymers
  • C09D127/02—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Coating compositions based on derivatives of such polymers not modified by chemical after-treatment
  • C09D127/12—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Coating compositions based on derivatives of such polymers not modified by chemical after-treatment containing fluorine atoms
  • C09D127/20—Homopolymers or copolymers of hexafluoropropene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
  • C08G65/002—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from unsaturated compounds
  • C08G65/005—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from unsaturated compounds containing halogens
  • C08G65/007—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from unsaturated compounds containing halogens containing fluorine
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L27/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers
  • C08L27/02—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L27/12—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment containing fluorine atoms
  • C08L27/18—Homopolymers or copolymers or tetrafluoroethene
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D127/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Coating compositions based on derivatives of such polymers
  • C09D127/02—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Coating compositions based on derivatives of such polymers not modified by chemical after-treatment
  • C09D127/12—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Coating compositions based on derivatives of such polymers not modified by chemical after-treatment containing fluorine atoms
  • C09D127/18—Homopolymers or copolymers of tetrafluoroethene
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
  • H01B13/00—Apparatus or processes specially adapted for manufacturing conductors or cables
  • H01B13/06—Insulating conductors or cables
  • H01B13/18—Applying discontinuous insulation, e.g. discs, beads
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
  • H01B13/00—Apparatus or processes specially adapted for manufacturing conductors or cables
  • H01B13/30—Drying; Impregnating
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01B—CABLES; CONDUCTORS; INSULATORS; SELECTION OF MATERIALS FOR THEIR CONDUCTIVE, INSULATING OR DIELECTRIC PROPERTIES
  • H01B3/00—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties
  • H01B3/18—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances
  • H01B3/30—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes
  • H01B3/44—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes vinyl resins; acrylic resins
  • H01B3/443—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes vinyl resins; acrylic resins from vinylhalogenides or other halogenoethylenic compounds
  • H01B3/445—Insulators or insulating bodies characterised by the insulating materials; Selection of materials for their insulating or dielectric properties mainly consisting of organic substances plastics; resins; waxes vinyl resins; acrylic resins from vinylhalogenides or other halogenoethylenic compounds from vinylfluorides or other fluoroethylenic compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G2650/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
  • C08G2650/28—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule characterised by the polymer type
  • C08G2650/46—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule characterised by the polymer type containing halogen
  • C08G2650/48—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule characterised by the polymer type containing halogen containing fluorine, e.g. perfluropolyethers

Definitions

• the present invention relates to compositions for repairing damaged sheathing of fluoropolymer sheathed electrical signal-carrying cables.
• wires and/or cables may be damaged during harness production or installation phases.
• the present invention provides for a liquid composition for repairing the insulating fluoropolymer sheath of electrical signal-carrying cables, the liquid composition comprising at least one amorphous fluoropolymer, at least one amorphous perfluoroalkylether and at least one fluorinated solvent.
• the present invention also provides for the use of said
• the present invention also provides for an electrical signal-carrying cable comprising the liquid composition according to the above.
• the present invention further provides for a process for repairing an electrically insulating sheath of an electrical signal-carrying cable, comprising the steps of, in this order, depositing a liquid composition according to the above on at least a damaged area of the electrically insulating sheath to form at least one layer of liquid composition and evaporating the fluorinated solvent to solidify the liquid composition, as well as the electrical signal-carrying cable obtainable by said process.
• the present invention further provides for a process for repairing an electrically insulating sheath of an electrical signal-carrying cable, comprising the steps of, in this order, depositing a liquid composition according to the above on at least a damaged area of the electrically insulating sheath to form at least one layer of liquid composition thereon, depositing at least one layer of unsintered polytetrafluoroethylene (PTFE) on at least the damaged area of the electrically insulating sheath, and evaporating the fluorinated solvent to solidify the liquid composition, as well as the electrical signal-carrying cable obtainable by said process.
• PTFE polytetrafluoroethylene
• the present invention alternatively provides for a process for repairing an electrically insulating sheath of an electrical signal-carrying cable, comprising the steps of, in this order, depositing a liquid
• composition according the above on at least a damaged area of the electrically insulating sheath to form at least one layer of liquid
• composition thereon, depositing at least one layer of unsintered polytetrafluoroethylene (PTFE) on at least the damaged area of the electrically insulating sheath, and evaporating the fluorinated solvent to solidify the liquid composition, as well as the electrical signal-carrying cable obtainable by said process.
• PTFE polytetrafluoroethylene
• the present invention additionally provides for a pre-impregnated unsintered polytetrafluoroethylene (PTFE) tape or film for repairing the insulating sheath of electrical signal-carrying cables comprising unsintered polytetrafluoroethylene (PTFE) and a liquid composition according to the above.
• PTFE pre-impregnated unsintered polytetrafluoroethylene
• the present invention additionally provides for a process for repairing an electrically insulating sheath of an electrical signal-carrying cable, comprising the steps of, in this order, depositing a pre-impregnated unsintered polytetrafluoroethylene (PTFE) tape or film according to the above, on at least a damaged area of the electrically insulating sheath, and evaporating the fluorinated solvent to solidify the liquid composition.
• PTFE polytetrafluoroethylene
• hydrofluorocarbons refers to both hydrofluorocarbons and
• the present invention provides for a liquid composition for repairing the insulating sheath of electrical signal-carrying cables comprising at least one amorphous fluoropolymer, at least one amorphous
• perfluoroalkylether and at least one fluorinated solvent.
• the liquid composition for repairing the insulating sheath of electrical signal-carrying cables according to the present invention can comprise of from 1 to 30 weight percent, preferably of from 5 to 18 weight percent, of amorphous fluoropolymer, based on the total weight of the composition.
• the liquid composition for repairing the insulating sheath of electrical signal-carrying cables according to the present invention can comprise of from 1 to 45 weight percent, preferably of from 5 to 27 weight percent of amorphous perfluoroalkylether, based on the total weight of the composition.
• the liquid composition for repairing the insulating sheath of electrical signal-carrying cables according to the present invention can comprise of from 25 to 98 weight percent, preferably of from 55 to 90 weight percent of fluorinated solvent, based on the total weight of the composition.
• the liquid composition for repairing the insulating sheath of electrical signal-carrying cables according to the present invention comprises amorphous fluoropolymer and amorphous perfluoroalkylether in a weight ratio of from 3/2 to 2/3.
• the amorphous fluoropolymer may be chosen among amorphous copolymers of tetrafluoroethylene, amorphous fluoropolymers of perfluorodienes, and mixtures thereof.
• Suitable amorphous copolymers of tetrafluoroethylene may be chosen among amorphous copolymers of tetrafluoroethylene comprising perfluorinated derivatives of dioxole such as for example 2,2,- bis(trifluoromethyl)-4,5-difluoro-1 ,3,dioxole or 2,2,4-trifluoro-5- (trifluoromethoxy)-l ,3-dioxole.
• the amorphous copolymers of tetrafluoroethylene comprising perfluorinated derivatives of dioxole may have a number average molecular weight M n of from 200 000 to 1 000 000 g/mol, more preferably of form 200 000 to 450 000 g/mol, most preferably of from 200 000 to 300 000 g/mol.
• Suitable copolymers of tetrafluoroethylene comprising 2,2,- bis(trifluoromethyl)-4,5-difluoro-1 ,3,dioxole may be chosen among amorphous copolymers of tetrafluoroethylene comprising at least 10 mole percent or from 10 to 95 mole percent, more preferably at least 55 mole percent or from than 55 to 95 mole percent of 2,2,-bis(trifluoromethyl)-4,5- difluoro-1 ,3,dioxole.
• Suitable copolymers of tetrafluoroethylene comprising 2,2,-bis(trifluoromethyl)-4,5-difluoro-1 ,3,dioxole are further described in European Patent 0073087, and are commercially obtainable from E. I. du Pont de Nemours and Company (Wilmington, USA) under the trademark TEFLON® AF.
• Suitable copolymers of tetrafluoroethylene comprising 2,2,4- trifluoro-5-(trifluoromethoxy)-1 ,3-dioxole may be chosen among
• amorphous copolymers of tetrafluoroethylene comprising at least 10 mole percent or from 10 to 95 mole percent, more preferably at least 55 mole percent or from 55 to 95 mole percent of 2,2,4-trifluoro-5- (trifluoromethoxy)-l ,3-dioxole.
• copolymers of tetrafluoroethylene comprising 2,2,- bis(trifluoromethyl)-4,5-difluoro-1 ,3,dioxole or 2,2,4-trifluoro-5-
• (trifluoromethoxy)-1 ,3-dioxole may further comprise at least one other ethylenically unsaturated monomer.
• Suitable amorphous fluoropolymers of perfluorodienes may be chosen among amorphous fluoropolymers obtainable by
• linear perfluorodienes and their derivatives such as for example linear perfluorodienes having a general structure of
• the perfluoroalkylether may be chosen among amorphous perfluoroalkylethers, or perfluoroalkyl oils.
• Suitable amorphous perfluoroalkylethers may be chosen among amorphous perfluoroalkylethers having a number average molecular weight of at least 500, or of from 500 to 12000, more preferably of at least 4000, or of from 4000 to 12000.
• Suitable amorphous perfluoroalkylethers may be chosen among amorphous perfluoroalkylethers comprising repeat units derivable from perfluoroalkene oxides, more preferably repeat units derivable from C2 or C3 perfluoroalkene oxides.
• suitable amorphous perfluoroalkylethers comprising repeat units derivable from perfluoroalkene oxides, more preferably repeat units derivable from C2 or C3 perfluoroalkene oxides.
• perfluoroalkylethers may be chosen among perfluoroalkylethers
• the amorphous perfluoroalkylethers comprise repeat units of the formula -CF(CF 3 )CF 2 O-.
• a preferred amorphous perfluoroalkylether may have the general structure of: CF 3 (CF 2 ) 2 O[CF(CF 3 )CF 2 O] m -R, where m is of from 2 to 100 and R can be either -CF 2 CF 3 or -CF(CF 3 ) 2 .
• Suitable amorphous perfluoroalkylethers may be obtained, for example, by anionic polymerization of hexafluoropropylene epoxide as described by Moore in United States Patent 3332826, the disclosure of which is incorporated herein by reference, and are commercially obtainable from E. I. du Pont de Nemours and Company (USA) under the trademark Krytox® GPL.
• the fluorinated solvent may be chosen among fluorinated solvents having a boiling point of from 45°C to 220°C, preferably of from 45°C to 160°C or of from 45°C to 105°C, at atmospheric pressure.
• the fluorinated solvent may be chosen among linear, branched, cyclic or heterocyclic (hydro )fluorocarbons, such as for example hydrofluoroalkanes or perfluoroalkanes having the general structure of: C n F(2n+2-m)H m , where n can be an integer of from 5 to 12 and more preferably of from 5 to 9, and where m can be of from 0 to 3 and preferably is 0.
• the fluorinated solvent may be chosen among
• the fluorinated solvent may be chosen among
• (perfluoroalkyl)perfluorotetrahydrofuranes preferably among those having a perfluoroalkyi moiety having from one 1 to 10 carbon atoms, such as for example 2,2,3,3,4,4,5-heptafluoro-5-(1 ,1 ,2,2,3,3,4,4,4- nonafluorobutyl)tetrahydrofuran; or among tri(perfluoroalkyl)amines, preferably among those having a perfluoroalkyi moiety having from 1 to 10 carbon atoms, such as for example tri(perfluoropentyl)amine or tri(perfluorobutyl)amine; or among N-(perfluoroalkyl)morpholines, preferably the ones having a perfluoroalkyi moiety having from 1 to 10 carbon atoms, such as for example N-(perfluoromethyl)morpholine.
• Suitable fluorinated solvents may be obtained, for example, by the reduction of polyfluoroolefin starting materials, as described by Krespan in United States Patent 6506950, the disclosure of which is incorporated herein by reference, and are commercially obtainable from E. I. du Pont de Nemours and Company (USA) under the trademark Vertrel®.
• the liquid composition for repairing the insulating sheath of electrical signal-carrying cables according to the present invention may be obtainable by dissolving an amount of amorphous fluoropolymer in the fluorinated solvent, optionally under agitation and/or heating, and subsequently dissolving the perfluoroalkylether in the fluorinated solvent solution of amorphous polymer to form the liquid composition according to the present invention.
• the liquid composition for repairing the insulating sheath of electrical signal-carrying cables according to the present invention may further comprise from 1 to 30 weight percent of at least one non-fibrillating polytetrafluoroethylene (PTFE), the weight percentages being based one the total weight of the composition.
• PTFE non-fibrillating polytetrafluoroethylene
• the non-fibrillating polytetrafluoroethylene (PTFE) is preferably present in the form of a particulate material having an average particle size of from 1 to 50 ⁇ , more preferably of from 1 to 25 ⁇ when measured according to standard ASTM D4464.
• PTFE polytetrafluoroethylene
• PTFE Micro Powder Such non-fibrillating polytetrafluoroethylene
• Non-fibrillating polytetrafluoroethylene (PTFE) grades are commercially obtainable from E. I. du Pont de Nemours and Company (USA) under the trademark Zonyl®.
• liquid composition for repairing the insulating sheath of electrical signal-carrying cables according to the present invention may be further useful in the manufacture of novel electrical signal-carrying cables comprising an electrical insulation sheath comprising the liquid
• the present invention further provides for a process for repairing an electrically insulating sheath of an electrical signal-carrying cable, comprising the steps of, in this order: a. depositing a liquid composition comprising at least one amorphous fluoropolymer, at least one amorphous perfluoroalkylether and at least one fluorinated solvent, on at least a damaged area of the electrically insulating sheath to form at least one layer of liquid
• the liquid composition may be deposited to the at least a damaged area of an electrically insulating sheath of an electrical signal-carrying cable by coating, spraying, or any suitable method for delivering a liquid to a surface, such as for example with a brush, spatula, an aerosol dispensing pressurized container, atomizer or vaporizer.
• the fluorinated solvent of the liquid composition may be evaporated by any suitable means to solidify the liquid composition, such as for example drying with or without heating, or exposing the liquid composition to vacuum or radiation such as IR, UV or microwave radiation.
• the thus formed coating restores the electrical insulation of the electrical signal-carrying cable.
• the present invention further provides for a process for repairing an electrically insulating sheath of an electrical signal-carrying cable, comprising the steps of, in this order, depositing a liquid composition according to the above description, on at least a damaged area of the electrically insulating sheath to form at least one layer of liquid composition thereon, then depositing at least one layer of unsintered polytetrafluoroethylene (PTFE) on at least the damaged area of the electrically insulating sheath, and evaporating the fluorinated solvent to solidify the liquid composition.
• PTFE polytetrafluoroethylene
• the present invention further provides for a process for repairing an electrically insulating sheath of an electrical signal-carrying cable, comprising the steps of, in this order, depositing a liquid composition according to the above description on at least one layer of unsintered polytetrafluoroethylene (PTFE) to form an at least one layer of coated, unsintered polytetrafluoroethylene (PTFE), then depositing the at least one of layer of coated, unsintered
• PTFE polytetrafluoroethylene
• the at least one layer of unsintered polytetrafluoroethylene (PTFE) can be deposited by winding, preferably in a helical manner, the at least one layer of unsintered polytetrafluoroethylene (PTFE) around the damaged area of the electrical signal-carrying cable.
• a knot may be formed in the at least one layer of unsintered
• PTFE polytetrafluoroethylene
• the at least one layer of unsintered polytetrafluoroethylene (PTFE) suitable in the above preferred processes may be in the form of a film, tape or preformed coil of unsintered polytetrafluoroethylene (PTFE).
• the at least one layer of unsintered polytetrafluoroethylene (PTFE) suitable in the above preferred processes may have a thickness of from a 0.025 to 1 mm, preferably of from 0.025 to 0.51 mm or from 0.1 to 0.5 mm.
• Polytetrafluoroethylenes that may be used for obtaining the at least one layer of unsintered polytetrafluoroethylene (PTFE) are
• polytetrafluoroethylenes having a propensity to fibrillate and form a fibrous matrix preferably among those defined under ASTM D 4895.
• Polytetrafluoroethylenes (PTFE) that may be used for obtaining the at least one layer of unsintered polytetrafluoroethylene (PTFE) may be chosen among polytetrafluoroethylenes (PTFE) having a standard specific gravity of from 2.14 to 2.185, more preferably from 2.15 to 2.175, when measured according to ISO 12086-2.
• Polytetrafluoroethylenes that may be used for obtaining the at least one layer of unsintered polytetrafluoroethylene (PTFE) are obtainable under the designation of "PTFE fine powders", i.e. particulate polytetrafluoroethylene (PTFE) having an average diameter of from 100 to 1000 ⁇ , when measured according to ISO 12086-2.
• PTFE fine powders i.e. particulate polytetrafluoroethylene (PTFE) having an average diameter of from 100 to 1000 ⁇ , when measured according to ISO 12086-2.
• the present invention provides for a pre- impregnated unsintered polytetrafluoroethylene (PTFE) tape or film for repairing the insulating sheath of electrical signal-carrying cables, comprising unsintered polytetrafluoroethylene (PTFE) and the liquid composition as described above.
• PTFE polytetrafluoroethylene
• the pre-impregnated unsintered polytetrafluoroethylene (PTFE) tape or film may be obtained either by applying the liquid composition as described above onto a previously obtained unsintered
• PTFE polytetrafluoroethylene
• PTFE polytetrafluoroethylene
• liquid composition as described above into a tape or film.
• the liquid composition is absorbed into the unsintered polytetrafluoroethylene (PTFE) tape or film because of its relatively high porosity.
• polytetrafluoroethylene (PTFE) tape or film is obtained by applying the liquid composition as described above onto a previously obtained unsintered polytetrafluoroethylene (PTFE) tape or film, the application of liquid composition may be achieved by suitable methods such as for example dipping, roll coating, brushing, spraying, and such methods known in the art.
• polytetrafluoroethylene (PTFE) tape or film is obtained by extruding a mixture of unsintered polytetrafluoroethylene (PTFE) and liquid
• the resulting extrudate is processed into a film or tape of the desired thickness by methods known in the art.
• a non-limiting, exemplary method of extrusion is lubricated paste extrusion.
• polytetrafluoroethylene (PTFE) tape or film for repairing the insulating sheath of electrical signal-carrying cable may be immediately deposited on a damaged area of the electrically insulating sheath of an electrical signal- carrying cable after obtaining it, or may be stored in an air-tight container which prevents the fluorinated solvent to evaporate until needed.
• PTFE polytetrafluoroethylene
• the pre-impregnated unsintered polytetrafluoroethylene (PTFE) tape or film for repairing the insulating sheath of electrical signal-carrying cable may comprise of from 10 to 60 weight percent, preferably of from 40 to 60 weight percent, of unsintered polytetrafluoroethylene (PTFE), and of from 40 to 90 weight percent, preferably of from 40 to 60 weight percent of liquid composition as described above, the weight percentages being based on the total weight of the pre-impregnated unsintered unsintered
• PTFE polytetrafluoroethylene
• the present invention further provides for a process for repairing an electrically insulating sheath of an electrical signal-carrying cable, comprising the steps of, in this order:
• PTFE polytetrafluoroethylene
• hexafluoropropylene-based perfluoropolyether oil was prepared by dissolving the corresponding quantities of perfluoropolyether oil in tri(perfluorobutyl)amine.
• tri(perfluorobutyl)amine containing 18 weight percent of the amorphous copolymer was prepared by dissolving the corresponding quantities of amorphous copolymer in tri(perfluorobutyl)amine.
• hexafluoropropylene-based perfluoropolyether oil and 9 weight percent of amorphous copolymer of tetrafluoroethylene and 2,2,-bis(trifluoromethyl)- 4,5-difluoro-1 ,3,dioxole in 82 weight percent tri(perfluorobutyl)amine.
• liquid composition was then deposited on one side of an unsintered polytetrafluoroethylene (PTFE) tape having a width of 32 mm, a thickness of 0.07 mm and a length of 200 mm, with a metal spatula, such as to cover the entire surface of the one side of the tape.
• PTFE polytetrafluoroethylene
• FEP fluorinated ethylene propylene
• the damaged area of the electric cable was then coated with the above-obtained liquid composition by brushing the damaged area, and the area within 40 mm of the damaged area, and then immediately winding the unsintered polytetrafluoroethylene (PTFE) tape around in a spiral, with the coated side of the tape facing the electric cable.
• PTFE polytetrafluoroethylene
• the sample electric cable was then placed in an oven at 50°C for 24 hours to evaporate the tri(perfluorobutyl)amine of the liquid
• the 5 samples were tested to determine the break down voltage of the repaired cable section using a Hypotronic #1417 tester, by submerging the repaired cable section in the 3 weight percent saline solution and applying an increasing voltage trough the cable.
• the voltage was increased from 0V up to 5kV at a voltage increase rate of 500V/min.
• the voltage was maintained for 2 minutes at 5kV. No failure occurred for any of the 5 samples.
• a first sample of the 5 samples was removed from the oven after 36 hours and the repaired cable section submerged in the 3 weight percent saline solution of sodium chloride for 7 hours.
• the sample was then tested to determine the break down voltage of the repaired cable section.
• the voltage was increased from 0V up to 7kV at a voltage increase rate of 500V/min.
• the voltage was maintained for 2 minutes at 7kV. No failure occurred.
• the four remaining samples in the oven were removed from the oven after 168 hours and the repaired cable section submerged in the 3 weight percent saline solution of sodium chloride for 12 hours.
• the samples were then tested to determine the break down voltage of the repaired cable section.
• the voltage was increased from OV up to 7kV at a voltage increase rate of 500V/min.
• the voltage was maintained for 2 minutes at 7kV. No failure occurred in any of the four samples.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Engineering & Computer Science (AREA)
• Manufacturing & Machinery (AREA)
• Wood Science & Technology (AREA)
• Life Sciences & Earth Sciences (AREA)
• Materials Engineering (AREA)
• Physics & Mathematics (AREA)
• Spectroscopy & Molecular Physics (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Paints Or Removers (AREA)
• Organic Insulating Materials (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (2)

Family

ID=48771747

Family Applications (1)

Country Status (5)

Families Citing this family (4)

Family Cites Families (13)

• 2013
  • 2013-06-26 US US14/410,262 patent/US20150368495A1/en not_active Abandoned
  • 2013-06-26 CN CN201380033518.9A patent/CN104641425A/zh active Pending
  • 2013-06-26 EP EP13735154.0A patent/EP2864989A2/en not_active Withdrawn
  • 2013-06-26 WO PCT/US2013/047739 patent/WO2014004594A2/en not_active Ceased
  • 2013-06-26 JP JP2015520416A patent/JP2015528837A/ja not_active Withdrawn

Also Published As