WO2013128653A1 - シリコンインゴットの切断方法 - Google Patents

シリコンインゴットの切断方法 Download PDF

Info

Publication number
WO2013128653A1
WO2013128653A1 PCT/JP2012/058812 JP2012058812W WO2013128653A1 WO 2013128653 A1 WO2013128653 A1 WO 2013128653A1 JP 2012058812 W JP2012058812 W JP 2012058812W WO 2013128653 A1 WO2013128653 A1 WO 2013128653A1
Authority
WO
WIPO (PCT)
Prior art keywords
wire
silicon ingot
cutting
metal wire
hydrofluoric acid
Prior art date
Application number
PCT/JP2012/058812
Other languages
English (en)
French (fr)
Inventor
順二 村田
宙治 桐野
Original Assignee
株式会社クリスタル光学
株式会社ツールバンク
学校法人立命館
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社クリスタル光学, 株式会社ツールバンク, 学校法人立命館 filed Critical 株式会社クリスタル光学
Publication of WO2013128653A1 publication Critical patent/WO2013128653A1/ja

Abstract

【課題】 砥粒を用いることなく、簡易な処理でシリコンインゴット（２）の切断を効率的に行うことができるとともに、シリコンウェーハの表面のダメージを軽減し、且つ薄膜化を図ることができるシリコンインゴットの切断方法を提供する。【解決手段】 金属製ワイヤ（４）にエッチング液（６）を供給した状態で、前記金属製ワイヤ（４）をシリコンインゴット（２）に押し当てながら走行させることにより、前記シリコンインゴット（２）を切断する。

Description

シリコンインゴットの切断方法
　本発明は、シリコンインゴットの切断方法に関し、特にワイヤを用いて切断を行うシリコンインゴットの切断方法に関する。
　従来、シリコンインゴットからシリコンウェーハを切り出す場合における切断手段として、ワイヤソーを用いることが知られている（例えば、特許文献１参照）。このワイヤソーでは、複数のガイドローラ間に巻回されたワイヤ列を走行させ、そのワイヤ列に遊離砥粒が含有されたスラリーを供給しながら、シリコンインゴットをワイヤ列に押し当てることによって、遊離砥粒の機械的作用（研削作用）により、シリコンインゴットから同時に複数枚のシリコンウェーハを切り出すことができる。しかしながら、このようなワイヤソーでは、遊離砥粒が含有されたスラリーを用いるため、廃液処理等の取り扱いが容易でないという問題がある。
　そこで、近年は、遊離砥粒を含有させたスラリーを用いなくても直接シリコンインゴット等の切断が行えるように、ワイヤにダイヤモンド砥粒等を樹脂や電着法等で固着させた固定砥粒方式のダイヤモンドワイヤが用いられている（例えば、特許文献２参照）。
　また、直流電源装置によって電解液に浸漬された状態のシリコンインゴットを陽極に帯電させ、電極線を陰極に帯電させて、該電極線によりシリコンインゴットをスライス加工する電解作用を利用した加工装置が提案されている（例えば、特許文献３参照）。
特開２００６－２２４２６６号公報 特開２００７－２０３４１７号公報 特開２０１０－２７４３９９号公報
　しかしながら、特許文献１のように遊離砥粒を含有させたスラリーを用いるものや特許文献２のようにワイヤにダイヤモンド砥粒等を固着させた固定砥粒方式のダイヤモンドワイヤを用いるものでは、砥粒の機械的作用によりシリコンインゴットを切断しているため、切り出されたシリコンウェーハの表面にダメージが残る。また、近年、より薄膜のシリコンウェーハが求められているが、特許文献１及び特許文献２では、砥粒の機械的作用によりシリコンインゴットを切断するので、シリコンウェーハを薄膜化するのが難しいという問題がある。また、特許文献３では、電解液を用いて加工処理を行うので、電解作用をコントロールするための制御及び廃液処理等が容易ではないため、処理が複雑になる。
　本発明は、上記のような種々の課題に鑑みてなされたものであって、砥粒を用いることなく、簡易な処理でシリコンインゴットの切断を効率的に行うことができるとともに、シリコンウェーハの表面のダメージを軽減し、且つ薄膜化を図ることができるシリコンインゴットの切断方法を提供することを目的とする。
　本願発明による第１のシリコンインゴットの切断方法は、金属製ワイヤにエッチング液を供給した状態で、前記金属製ワイヤをシリコンインゴットに押し当てながら走行させることにより、前記シリコンインゴットを切断することを特徴としている。
　本発明による第２のシリコンインゴットの切断方法は、前記金属線ワイヤを通電して加熱させることを特徴としている。
　本発明による第３のシリコンインゴットの切断方法は、前記金属製ワイヤが、ニクロム線、ピアノ線表面にニッケルクロムメッキが施された線、あるいは表面がクロム合金で覆われた線で形成されていることを特徴としている。
　本発明による第４のシリコンインゴットの切断方法は、前記金属製ワイヤを１００ｍ／分以上で走行させることを特徴としている。
　本発明による第５のシリコンインゴットの切断方法は、前記エッチング液が、フッ硝酸を主成分とすることを特徴としている。
　本発明による第６のシリコンインゴットの切断方法では、前記フッ硝酸は、硝酸濃度が５ｗｔ％以上６０ｗｔ％以下、フッ酸濃度が０．５ｗｔ％以上５０ｗｔ％以下とすることを特徴としている。
　第１のシリコンインゴットの切断方法によれば、金属製ワイヤにエッチング液を供給しながら、この金属製ワイヤによってシリコンインゴットを擦過することで、砥粒を用いることなく、エッチング液の化学的作用とワイヤの機械的作用によりシリコンインゴットの切断を効率的に行い、加工速度を向上させることができる。また、砥粒を用いることなくシリコンインゴットの切断を行うことができるので、シリコンウェーハの表面のダメージを軽減することができるとともに、薄膜のシリコンウェーハを作製することができる。
　第２のシリコンインゴットの切断方法によれば、金属製ワイヤを通電して加熱させるので、電熱作用によってエッチングを促進し、加工速度をより向上させることができる。
　第３のシリコンインゴットの切断方法では、金属製ワイヤが、ニクロム線、ピアノ線表面にニッケルクロムメッキが施された線、あるいは表面がクロム合金で覆われた線で形成されることにより、効率的に電熱作用を得ることができるので、エッチングをより効率的に促進し、加工速度を向上させることができる。また、金属製ワイヤとしてニクロム線を用いることにより、加工処理に掛かるコストを軽減することができる。
　第４のシリコンインゴットの切断方法によれば、金属製ワイヤを１００ｍ／分以上でシリコンインゴットに押し当てながら走行させるので、より加工速度を向上させることができる。
　第５のシリコンインゴットの切断方法では、エッチング液としてフッ硝酸を主成分とするものを用いることにより、シリコンインゴットに対して、より効率的に化学的作用を与えることができるので、加工速度を向上させることができる。
　第６のシリコンインゴットの切断方法では、前記フッ硝酸を、硝酸濃度が５ｗｔ％以上６０ｗｔ％以下、フッ酸濃度が０．５ｗｔ％以上５０ｗｔ％以下とすることにより、カーフロスに影響するフッ酸濃度を抑えているので、シリコンインゴットの切断時のカーフロス（切断代）を軽減することができる。
加工装置を用いた本発明に係るシリコンインゴットの切断方法の一例について説明するための概略説明図である。 フッ硝酸に対する加工速度・カーフロスの関係を示すグラフであって、（ａ）は加工速度・カーフロスの硝酸濃度依存性を示すものであり、（ｂ）は加工速度・カーフロスのフッ酸濃度依存性を示すものである。 本発明に係るシリコンインゴットの切断方法を用いた場合のシリコンインゴットの切断状態について説明するための概略断面図である。 ワイヤ走行速度と加工速度との関係を示すグラフである。 電熱作用と加工速度との関係を示すグラフである。 本発明にシリコンインゴットの切断方法を用いた場合のシリコンインゴットの切断状態を示す図であって、（ａ）は切断溝を示すものであり、（ｂ）は切断溝の一部を拡大した形状を示すものである。
　以下、本発明に係るシリコンインゴットの切断方法について、図面を参照しつつ説明する。本発明に係るシリコンインゴットの切断方法は、例えば図１に示すような加工装置１を用いてシリコンインゴット２を切断するものであって、一方のリール３ａから金属製ワイヤ（以下、ワイヤという）４が繰り出され、該ワイヤ４にエッチング供給部５からエッチング液６が供給された状態で、ワイヤ４をガイドローラ７ａ、７ｂによってシリコンインゴット２に押し当てながら走行させることによりシリコンインゴットをウェハ状に切断する。その後、シリコンインゴット２を通過したワイヤ４は、ガイドローラ７ｂを介して他方のリール３ｂによって巻き取られる。また、加工装置１は、シリコンインゴット２を固定する支持台８と、ガイドローラ７ａ、７ｂを介してワイヤ４を通電させる電源９と、ワイヤ４へと供給されたエッチング液６を回収する回収タンク１０とを備えている。
　シリコンインゴット２は、例えば不図示のカーボンベッド等を介して支持台８に下面が固定されている。支持台８は、不図示の駆動モータ等によって上下方向に昇降可能に設けられており、シリコンインゴット２を固定させた状態で支持台８を上昇させることで、走行するワイヤ４にシリコンインゴット２が押し当てられる。
　リール３ａ、３ｂは、それぞれ不図示の駆動モータ等によってワイヤ４を繰り出し又は巻き取りするためのものである。図１では、矢印方向にワイヤ４が走行するように、リール３ｂがワイヤ４を巻き取るための巻き取りリールとして機能し、リール３ａはワイヤを繰り出すための繰り出しリールとして機能する場合の例を示しているが、ワイヤ４がリール３ｂに所定距離分以上巻き取られた後は、駆動モータによって逆方向にリール３ａ、３ｂを回転させることにより、矢印と逆方向にワイヤ４を走行させてシリコンインゴット２を切断することができる。
　ワイヤ４は、シリコンインゴット２に押し当てられながら走行することによって、シリコンインゴット２を擦過して機械的作用により切断するためのものである。このワイヤ４としては、ニクロム線により形成されたものを用いることが好ましい。ニクロム線は、エッチング液６としてフッ硝酸等を用いた場合にも溶解しないとともに、比較的安価に入手することができるので、コストを軽減することができる。また、ニクロム線は、電熱線として用いられるものであり、優れた電熱作用を有しているので、電源９によって通電させることにより容易に加熱させることができる。また、ニクロム線と同様に電熱線として従来から用いられているカンタル線等をワイヤ４として用いても良い。また、その他、ワイヤ４としては、白金（Ｐｔ）やチタン（Ｔｉ）等により形成されたものやピアノ線等の鋼線の表面にニクロムクロムメッキが施された線、あるいは表面がクロム合金で覆われた線等を用いることができるが、必ずしもこれらに限定されるものではなく、エッチング液６に対して耐性のある膜をコーティングした線やエッチング液６に対して耐性がある金属製の線であれば良い。
　ワイヤ４の直径としては、０．０１～０．５ｍｍ程度のものを用いることが好ましい。ニクロム線の場合には、例えば、最も細いものとして０．０２５ｍｍのものを用いることができる。これにより、カーフロスを軽減するとともに、表面にダメージの少ないシリコンウェーハを作製することができる。
　エッチング液供給部５は、走行するワイヤ４に対してエッチング液６を供給するためのものであり、走行するワイヤ４がシリコンインゴット２を切断する切断位置の上方に配置されている。このエッチング液供給部５は、詳しくは図示しないが、走行するワイヤ４へ満遍なくエッチング液６を供給するための噴出口が複数形成されており、エッチング液６が貯蔵されているエッチング液貯蔵タンクからポンプやホース等を介して所定流量のエッチング液６を噴出口から切断位置のワイヤ４に対して供給する。また、シリコンインゴット２の下方へと落ちたエッチング液６は、支持台８の下方に設けられた回収タンク１０に溜められ回収される。
　エッチング液供給部５からワイヤ４に供給されるエッチング液６としては、例えば、シリコンウェーハ製造工程のエッチング工程等で用いられるシリコン（Ｓｉ）の等方性エッチングが可能なフッ硝酸を所定量の酢酸（例えば、フッ酸：硝酸：酢酸＝１：３：８の割合）で希釈したエッチング液６を用いる。また、フッ硝酸を希釈するために添加する弱酸として、酢酸の他にリン酸やホウ酸等を用いても良い。このように、フッ硝酸にこれらの弱酸を添加することにより、エッチング面の粗さを改善することができる。図２は、フッ硝酸の硝酸（ＨＮＯ３）濃度及びフッ酸（ＨＦ）濃度が、シリコンインゴット２を切断する際の加工速度とカーフロスに及ぼす影響を示すものであり、それぞれワイヤ４を１００ｍ／ｍｉｎで走行させた場合の加工速度とカーフロスを縦軸に示している。図２（ａ）は、フッ酸濃度を４ｗｔ％とし、硝酸濃度を変更させた場合の加工速度とカーフロスを示しており、図２（ｂ）は、硝酸濃度を２０ｗｔ％とし、フッ酸濃度を変更させた場合の加工速度とカーフロスを示している。図２（ａ）に示すように、硝酸濃度を上げていった場合には、加工速度は向上するが、カーフロスはほとんど変化しない。つまり、フッ硝酸の硝酸濃度は、カーフロスにあまり影響していない。一方、図２（ｂ）に示すように、フッ酸濃度を上げていった場合には、加工速度が向上するとともに、カーフロスも増えてしまう。従って、本発明のシリコンインゴット２の切断方法では、フッ酸濃度を０．５ｗｔ％以上５０ｗｔ％以下に抑え、硝酸濃度を５ｗｔ％以上６０ｗｔ％以下としたフッ硝酸を用いることが好ましく、より好ましくはフッ酸濃度を０．５ｗｔ％以上８ｗｔ％以下、硝酸濃度を４０ｗｔ％以上６０ｗｔ％以下のフッ硝酸を用いる。これにより、このフッ硝酸の化学的作用とワイヤ４の機械的作用によりシリコンインゴット２の切断を効率的に行うことができるので、加工速度を向上させることができるとともに、カーフロスを軽減させることができる。尚、エッチング液６は、必ずしもフッ硝酸に限定されるものではなく、例えば、過酸化水素水、リン酸、硫酸、過マンガン酸カリウム、過硫酸カリウム、オゾン水等の酸化剤とフッ酸、フッ化アンモニウム、フッ化水素アンモニウム等の酸化膜を溶解する薬液の混合液、あるいは水酸化カリウム、４メチル水酸化アンモニウム（ＴＭＡＨ）等の塩基性薬液等の従来公知のエッチング液６を用いても良い。
　ガイドローラ７ａ、７ｂは、ワイヤ４をシリコンインゴット２に押し当てた状態で走行するように案内するためのものである。このガイドローラ７ａ、７ｂの外周面には、例えば、その円周方向に沿って複数のワイヤ溝（不図示）が形成されている。ワイヤ溝は、所定ピッチで形成されており、このワイヤ溝に複数のワイヤ４がそれぞれ巻き付けられて所定ピッチのワイヤ列が形成され、このワイヤ列をシリコンインゴット２に押し当てながら走行させることにより、図３に示すように、シリコンインゴット２を複数同時に切断することができる。
　また、ワイヤ４にエッチング液６を供給しながら、シリコンインゴット２を切断する際の加工速度は、図４に示すように、ガイドローラ７ａ、７ｂ間を走行するワイヤ４の走行速度に依存するため、ワイヤ４を１００ｍ／ｍｉｎ以上で走行させることが好ましい。図４は、エッチング液６として、フッ酸濃度：４ｗｔ％、硝酸濃度：６０ｗｔ％のフッ硝酸を用いたシリコンインゴット２の切断時におけるワイヤ４の走行速度と加工速度との関係を示すものである。この図４に示すように、シリコンインゴット２を切断する際の加工速度は、ワイヤ４の走行速度に依存しており、ワイヤ４の走行速度が速くなるのに伴って、加工速度も上昇する。そのため、本発明のシリコンインゴット２の切断方法では、ワイヤ４を１００ｍ／ｍｉｎ以上、より好ましくは２００ｍ／ｍｉｎ以上で走行させることにより、エッチングを機械的に促進し、加工速度を向上させることができる。
　電源９は、導電性のガイドローラ７ａ、７ｂを介してワイヤ４を通電により加熱させるためのものである。この電源９によって所定の電圧が、ガイドローラ７ａ、７ｂ間に加えられることにより、ガイドローラ７ａ、７ｂ間を走行するワイヤに電流が流れる。これにより、ジュール熱が発生し、ワイヤ４が所定温度に加熱される。また、ワイヤ４としてニクロム線を用いた場合には、電熱作用に優れているので、効率的に加熱させることができる。
　図５は、電源９によって１０Ｖの電圧を加えることにより、ニクロム線形で形成された線径が１６０μｍのワイヤ４に０．５５Ａの電流を流して加熱させた状態でシリコンインゴット２を切断した際の加工速度とワイヤ４を通電していない状態の加工速度とを示している。ここでは、エッチング液６として、フッ酸濃度：４ｗｔ％、硝酸濃度：６０ｗｔ％のフッ硝酸を用いて、ワイヤ４の走行速度を１０ｍ／ｍｉｎとしてシリコンインゴット２の切断を行った結果を示している。図５に示すように、ワイヤ４を通電させて加熱させた場合には、ワイヤ４を通電させなかった場合に比べて、電熱作用によってエッチングが熱的に促進され、加工速度が５倍以上向上している。尚、ワイヤ４を加熱するための機構は、これに限定されるものではなく、例えば、加熱ヒータ等によりワイヤ４を加熱するようにしても良い。
　尚、図１では、切断位置の上方からエッチング液供給部５によってワイヤ４へエッチング液６を供給しているが、ワイヤ４の走行方向の上流側であるガイドローラ７ａ側にエッチング液供給部５を配置し、ワイヤ４に対してエッチング液６を供給するようにしても良い。また、エッチャント浴等に予めエッチング液６を溜めておき、その中にシリコンインゴット２を浸漬させて、ワイヤ４をこのエッチャント浴内を走行させることにより、ワイヤ４にエッチング液６が供給された状態でシリコンインゴット２を擦過するようにしても良い。
　次に、本発明のシリコンインゴット２の切断方法を用いた場合のシリコンインゴット２の切断状態について説明する。図６は、太陽電池用の１５０ｍｍ角の四角柱状のシリコンインゴット２を下記の表１に示す加工条件にてスライス加工した際の切断状態を示すものである。表１に示すように、線径が１６０μｍのニクロム線から形成されるワイヤ４を用いてシリコンインゴットの切断を行った場合には、図６（ａ）に示すように、切断溝のカーフロスＷは１７５μｍであり、ワイヤ４によってシリコンインゴット２が機械的に擦過された方向に直交する横方向にはほとんど広がることなく、シリコンインゴットを切断することができている。また図６（ｂ）は、図６（ａ）の切断溝の円で囲む箇所の一部を拡大したものであり、図６（ｂ）に示すように、切断面形状は従来の砥粒による研削作用により切断した場合に比べてダメージが少なく、滑らかに切断することができている。従って、このような本発明のシリコンインゴットの切断方法を用いることにより、薄膜のシリコンウェーハを作製することができる。また、ワイヤ４として、線径がより小さいものを用いることによって、カーフロスを更に軽減することができる。また、ワイヤ４の走行速度を上げるとともに、ワイヤ４を通電させて加熱することにより、エッチングを機械的及び熱的に促進することで、加工速度を向上させることができる。
Figure JPOXMLDOC01-appb-T000001
　尚、本発明の実施の形態は上述の形態に限るものではなく、本発明の思想の範囲を逸脱しない範囲で適宜変更することができる。
２　　　　シリコンインゴット
４　　　　ワイヤ
６　　　　エッチング液

Claims (6)

  1. 　金属製ワイヤにエッチング液を供給した状態で、前記金属製ワイヤをシリコンインゴットに押し当てながら走行させることにより、前記シリコンインゴットを切断することを特徴とするシリコンインゴットの切断方法。
  2. 　前記金属線ワイヤを通電して加熱させることを特徴とする請求項１に記載のシリコンインゴットの切断方法。
  3. 　前記金属製ワイヤは、ニクロム線、ピアノ線表面にニッケルクロムメッキが施された線、あるいは表面がクロム合金で覆われた線で形成されていることを特徴とする請求項１又は２に記載のシリコンインゴットの切断方法。
  4. 　前記金属製ワイヤを１００ｍ／分以上で走行させることを特徴とする請求項１乃至３のいずれかに記載のシリコンインゴットの切断方法。
  5. 　前記エッチング液は、フッ硝酸を主成分とすることを特徴とする請求項１乃至４のいずれかに記載のシリコンインゴットの切断方法。
  6. 　前記フッ硝酸は、硝酸濃度が５ｗｔ％以上６０ｗｔ％以下、フッ酸濃度が０．５ｗｔ％以上５０ｗｔ％以下とすることを特徴とする請求項１乃至５のいずれかに記載のシリコンインゴットの切断方法。
PCT/JP2012/058812 2012-03-02 2012-04-02 シリコンインゴットの切断方法 WO2013128653A1 (ja)