WO2013127353A1 - Tube revêtu - Google Patents

Tube revêtu Download PDF

Info

Publication number
WO2013127353A1
WO2013127353A1 PCT/CN2013/072017 CN2013072017W WO2013127353A1 WO 2013127353 A1 WO2013127353 A1 WO 2013127353A1 CN 2013072017 W CN2013072017 W CN 2013072017W WO 2013127353 A1 WO2013127353 A1 WO 2013127353A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
coated tube
coated
tube according
tube
Prior art date
Application number
PCT/CN2013/072017
Other languages
English (en)
Inventor
Zhening Zhao
Shijun Li
Shumin Zhai
Qijun Sun
Yifang Chen
Lifeng Dong
Yongchang Zhao
Minghong Chen
Guobin Sun
Jinhe HUANG
Guocheng Li
Baiwen Cao
Original Assignee
Bundy Fluid Systems Co., Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from CN2012200681894U external-priority patent/CN202442061U/zh
Priority claimed from CN2012200686968U external-priority patent/CN202442063U/zh
Priority claimed from CN2012200681907U external-priority patent/CN202442062U/zh
Priority claimed from CN2012200685715U external-priority patent/CN202451990U/zh
Application filed by Bundy Fluid Systems Co., Ltd filed Critical Bundy Fluid Systems Co., Ltd
Publication of WO2013127353A1 publication Critical patent/WO2013127353A1/fr

Abstract

La présente invention concerne un tube revêtu, en particulier pour un système de canalisations de transport de fluide dans un véhicule, ledit tube revêtu comprenant : un tube de base (1) ; et un revêtement d'alliage zinc/aluminium (3), un revêtement primaire de nylon (5) et un revêtement de nylon (6) revêtus et agencés vers l'extérieur depuis l'intérieur sur ledit tube de base, l'invention étant caractérisée en ce qu'une couche de zinc de pré-placage (2) est ajoutée et disposée entre ledit tube de base et ledit revêtement d'alliage zinc/aluminium et en ce qu'un revêtement d'enduit étanche (4) est revêtu entre ledit revêtement d'alliage zinc/aluminium et ledit revêtement primaire de nylon.
PCT/CN2013/072017 2012-02-29 2013-02-28 Tube revêtu WO2013127353A1 (fr)

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
CN2012200681894U CN202442061U (zh) 2012-02-29 2012-02-29 涂层管
CN201220068696.8 2012-02-29
CN2012200686968U CN202442063U (zh) 2012-02-29 2012-02-29 涂层管
CN2012200681907U CN202442062U (zh) 2012-02-29 2012-02-29 涂层管
CN2012200685715U CN202451990U (zh) 2012-02-29 2012-02-29 涂层管
CN201220068189.4 2012-02-29
CN201220068571.5 2012-02-29
CN201220068190.7 2012-02-29

Publications (1)

Publication Number Publication Date
WO2013127353A1 true WO2013127353A1 (fr) 2013-09-06

Family

ID=49081647

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2013/072017 WO2013127353A1 (fr) 2012-02-29 2013-02-28 Tube revêtu

Country Status (1)

Country Link
WO (1) WO2013127353A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2840292A4 (fr) * 2012-04-17 2016-05-18 Xinxing Ductile Iron Pipes Co Revêtement anticorrosion pour canalisation à base de métal noire enterrée et procédé pour l'application de celui-ci par pulvérisation

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002294378A (ja) * 2001-04-03 2002-10-09 Mitsubishi Alum Co Ltd ヘッダータンクを製造するためのアルミニウム合金押出管
CN101875255A (zh) * 2009-04-30 2010-11-03 邦迪管路系统有限公司 多层耐腐蚀涂层及包含该涂层的部件
CN202442061U (zh) * 2012-02-29 2012-09-19 邦迪管路系统有限公司 涂层管
CN202442062U (zh) * 2012-02-29 2012-09-19 邦迪管路系统有限公司 涂层管
CN202442063U (zh) * 2012-02-29 2012-09-19 邦迪管路系统有限公司 涂层管
CN202451990U (zh) * 2012-02-29 2012-09-26 邦迪管路系统有限公司 涂层管

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002294378A (ja) * 2001-04-03 2002-10-09 Mitsubishi Alum Co Ltd ヘッダータンクを製造するためのアルミニウム合金押出管
CN101875255A (zh) * 2009-04-30 2010-11-03 邦迪管路系统有限公司 多层耐腐蚀涂层及包含该涂层的部件
CN202442061U (zh) * 2012-02-29 2012-09-19 邦迪管路系统有限公司 涂层管
CN202442062U (zh) * 2012-02-29 2012-09-19 邦迪管路系统有限公司 涂层管
CN202442063U (zh) * 2012-02-29 2012-09-19 邦迪管路系统有限公司 涂层管
CN202451990U (zh) * 2012-02-29 2012-09-26 邦迪管路系统有限公司 涂层管

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2840292A4 (fr) * 2012-04-17 2016-05-18 Xinxing Ductile Iron Pipes Co Revêtement anticorrosion pour canalisation à base de métal noire enterrée et procédé pour l'application de celui-ci par pulvérisation

Similar Documents

Publication Publication Date Title
RU2429084C2 (ru) Стальной плоский прокат и способ изготовления стального тонкого проката
JP3515183B2 (ja) 金属管における耐食性樹脂被覆構造
EP2581467B1 (fr) Tuyau de métal pour canalisations de véhicule et procédé de traitement de surface correspondant
JPH09509723A (ja) 自動車用の配管及びその製造方法
JPWO2007052683A1 (ja) 自動車配管用鋼管
CN101876015A (zh) 耐腐蚀合金材料、该材料构成的涂层及包含该涂层的部件
US20180179642A1 (en) Component, in Particular Structural Component, for a Motor Vehicle, as well as a Method for Producing a Component
JP6782621B2 (ja) 自動車用部材
CN202451990U (zh) 涂层管
JP5138957B2 (ja) 鋼材とアルミニウム材との異材接合体
US7300706B2 (en) High-carbon steel wire with nickel sub coating
US5849382A (en) Tubing for systems in automotive vehicles and a method of manufacturing the same
JP3164654U (ja) 高耐食性鉄製部品
CN202442062U (zh) 涂层管
WO2013127353A1 (fr) Tube revêtu
CN101875255A (zh) 多层耐腐蚀涂层及包含该涂层的部件
JP5134269B2 (ja) 鋼材とアルミニウム材との異材接合体とそのスポット溶接方法
JPS5815554B2 (ja) カチオン電着塗装用のメッキ鋼材
CN105624605A (zh) 锌脂防腐钢管杆及其涂层方法
CN202442061U (zh) 涂层管
CN202442063U (zh) 涂层管
JP6541992B2 (ja) 塗装かつ犠牲防食効果を利用した耐穴あき性に優れた自動車用部材および自動車用給油管
JPS5914940A (ja) 溶接作業性に優れた複合塗装鋼板
JP2668419B2 (ja) 耐熱耐食性重層被覆鋼管
JP2016125070A (ja) 保全性に優れた架空機材用の蓋

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13754056

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13754056

Country of ref document: EP

Kind code of ref document: A1