WO2013053879A1 - Pneumatique comportant une couche d'elements de renforcement circonferentiels - Google Patents
Pneumatique comportant une couche d'elements de renforcement circonferentiels Download PDFInfo
- Publication number
- WO2013053879A1 WO2013053879A1 PCT/EP2012/070239 EP2012070239W WO2013053879A1 WO 2013053879 A1 WO2013053879 A1 WO 2013053879A1 EP 2012070239 W EP2012070239 W EP 2012070239W WO 2013053879 A1 WO2013053879 A1 WO 2013053879A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- working crown
- reinforcing elements
- layers
- phr
- Prior art date
Abstract
Description
Claims