WO2011155164A1 - Condensateur - Google Patents
Condensateur Download PDFInfo
- Publication number
- WO2011155164A1 WO2011155164A1 PCT/JP2011/003133 JP2011003133W WO2011155164A1 WO 2011155164 A1 WO2011155164 A1 WO 2011155164A1 JP 2011003133 W JP2011003133 W JP 2011003133W WO 2011155164 A1 WO2011155164 A1 WO 2011155164A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- active material
- material layer
- positive electrode
- compound
- capacitor
- Prior art date
Abstract
La présente invention concerne un condensateur présentant une nouvelle configuration dans laquelle, en plus d'une double couche électrique formée au niveau de l'interface entre une électrode polarisable et un électrolyte, de l'énergie électrique est stockée en utilisant le transfert de charge entre l'électrode polarisable et un composé métallique. Le condensateur comprend : un collecteur d'électrode positive ; une couche de matériau actif d'électrode positive contenant un matériau de carbone ; un acide polylactique et un composé V3+ ; un séparateur ; un matériau de carbone ; une couche de matériau actif d'électrode négative contenant un acide polylactique et un composé V4+ ; un collecteur d'électrode négative ; et un électrolyte qui s'infiltre dans la couche de matériau actif d'électrode positive, le séparateur, et la couche de matériau actif d'électrode négative.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JPPCT/JP2010/003874 | 2010-06-10 | ||
PCT/JP2010/003874 WO2011155000A1 (fr) | 2010-06-10 | 2010-06-10 | Condensateur |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2011155164A1 true WO2011155164A1 (fr) | 2011-12-15 |
Family
ID=45097634
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2010/003874 WO2011155000A1 (fr) | 2010-06-10 | 2010-06-10 | Condensateur |
PCT/JP2011/003133 WO2011155164A1 (fr) | 2010-06-10 | 2011-06-02 | Condensateur |
Family Applications Before (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2010/003874 WO2011155000A1 (fr) | 2010-06-10 | 2010-06-10 | Condensateur |
Country Status (1)
Country | Link |
---|---|
WO (2) | WO2011155000A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2013076762A1 (fr) * | 2011-11-22 | 2013-05-30 | イノベーションエネルギー株式会社 | Condensateur |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN110892574A (zh) * | 2017-07-04 | 2020-03-17 | 优化公司 | 二次电池和二次电池的制造方法 |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2005032633A (ja) * | 2003-07-08 | 2005-02-03 | Tdk Corp | 電極及び電気化学素子 |
JP2005166459A (ja) * | 2003-12-03 | 2005-06-23 | Yuasa Corp | 電気化学デバイス、電気化学デバイス用電極、電気化学デバイス用電極材料及びその製造方法 |
JP2009519565A (ja) * | 2005-12-14 | 2009-05-14 | アヴェスター リミティッド パートナーシップ | 電気化学バッテリー及びその製造方法 |
JP2010034300A (ja) * | 2008-07-29 | 2010-02-12 | Jfe Chemical Corp | 電気二重層キャパシタの分極性電極用炭素材料、その製造方法および電気二重層キャパシタ |
-
2010
- 2010-06-10 WO PCT/JP2010/003874 patent/WO2011155000A1/fr active Application Filing
-
2011
- 2011-06-02 WO PCT/JP2011/003133 patent/WO2011155164A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2005032633A (ja) * | 2003-07-08 | 2005-02-03 | Tdk Corp | 電極及び電気化学素子 |
JP2005166459A (ja) * | 2003-12-03 | 2005-06-23 | Yuasa Corp | 電気化学デバイス、電気化学デバイス用電極、電気化学デバイス用電極材料及びその製造方法 |
JP2009519565A (ja) * | 2005-12-14 | 2009-05-14 | アヴェスター リミティッド パートナーシップ | 電気化学バッテリー及びその製造方法 |
JP2010034300A (ja) * | 2008-07-29 | 2010-02-12 | Jfe Chemical Corp | 電気二重層キャパシタの分極性電極用炭素材料、その製造方法および電気二重層キャパシタ |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2013076762A1 (fr) * | 2011-11-22 | 2013-05-30 | イノベーションエネルギー株式会社 | Condensateur |
Also Published As
Publication number | Publication date |
---|---|
WO2011155000A1 (fr) | 2011-12-15 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US10644324B2 (en) | Electrode material and energy storage apparatus | |
US7623339B2 (en) | Electrochemical device | |
KR101138502B1 (ko) | 리튬 이온 커패시터의 제조 방법 | |
JP5730321B2 (ja) | リチウムイオンキャパシタ | |
JP2007280803A (ja) | ハイブリッド型積層電極、それを用いたハイブリッド二次電源 | |
WO2006112068A1 (fr) | Condensateur à ion lithium | |
JP5096851B2 (ja) | 蓄電デバイスの製造方法 | |
JP2008097991A (ja) | 蓄電デバイス | |
JP5308646B2 (ja) | リチウムイオンキャパシタ | |
WO2013002119A1 (fr) | Dispositif de stockage, et procédé de fabrication de celui-ci | |
WO2012127991A1 (fr) | Dispositif de stockage de puissance | |
JP2019145628A (ja) | 活物質粒子およびそれを用いた蓄電デバイス | |
JP2011159642A (ja) | 電気化学デバイス | |
WO2011155164A1 (fr) | Condensateur | |
WO2013076762A1 (fr) | Condensateur | |
JP6188463B2 (ja) | 電気化学デバイス及び電気化学デバイスの製造方法 | |
JP2010245086A (ja) | リチウムイオンキャパシタの製造方法 | |
JP2008244378A (ja) | 蓄電デバイス | |
JP2006086148A (ja) | 電気二重層キャパシタおよびその製造方法 | |
JP2010003773A (ja) | 電気二重層キャパシタ | |
JP4826649B2 (ja) | 電気二重層キャパシタ | |
TW201322289A (zh) | 電容器 | |
WO2005076296A1 (fr) | Dispositif electrochimique et corps d’electrode | |
WO2013001962A1 (fr) | Composition de couche d'adhésif isolant, élément pour dispositif de stockage électrique, dispositif de stockage électrique et procédés de fabrication de ceux-ci | |
KR101409178B1 (ko) | 슈퍼커패시터 전극용 조성물 및 이를 이용한 슈퍼커패시터 전극의 제조방법 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 11792123 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 11792123 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: JP |