WO2011071691A2 - Unité télescopique avec barrière soluble - Google Patents

Unité télescopique avec barrière soluble Download PDF

Info

Publication number
WO2011071691A2
WO2011071691A2 PCT/US2010/057763 US2010057763W WO2011071691A2 WO 2011071691 A2 WO2011071691 A2 WO 2011071691A2 US 2010057763 W US2010057763 W US 2010057763W WO 2011071691 A2 WO2011071691 A2 WO 2011071691A2
Authority
WO
WIPO (PCT)
Prior art keywords
powder
particle
telescopic member
nanomatrix
dispersed
Prior art date
Application number
PCT/US2010/057763
Other languages
English (en)
Other versions
WO2011071691A3 (fr
Inventor
Gaurav Agrawal
Zhiyue Xu
Bennett Richard
Yang Xu
Original Assignee
Baker Hughes Incorporated
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baker Hughes Incorporated filed Critical Baker Hughes Incorporated
Priority to CA2783113A priority Critical patent/CA2783113C/fr
Priority to AU2010328531A priority patent/AU2010328531B2/en
Priority to GB1209720.0A priority patent/GB2488282B/en
Publication of WO2011071691A2 publication Critical patent/WO2011071691A2/fr
Publication of WO2011071691A3 publication Critical patent/WO2011071691A3/fr
Priority to NO20120596A priority patent/NO341042B1/no

Abstract

L'invention concerne un élément télescopique qui comprend au moins un composant central et une barrière dans ledit composant; cette barrière présente une courbe de taux de dissolution à ajustement sélectif et des propriétés structurelles permettant la résistance à une pression élevée avant l'apparition de défaut structurel de la barrière par dissolution.
PCT/US2010/057763 2009-12-08 2010-11-23 Unité télescopique avec barrière soluble WO2011071691A2 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CA2783113A CA2783113C (fr) 2009-12-08 2010-11-23 Unite telescopique avec barriere soluble
AU2010328531A AU2010328531B2 (en) 2009-12-08 2010-11-23 Telescopic unit with dissolvable barrier
GB1209720.0A GB2488282B (en) 2009-12-08 2010-11-23 Telescopic unit with dissolvable barrier suitable for downhole use
NO20120596A NO341042B1 (no) 2009-12-08 2012-05-23 Teleskopisk element

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US12/633,683 2009-12-08
US12/633,683 US8297364B2 (en) 2009-12-08 2009-12-08 Telescopic unit with dissolvable barrier

Publications (2)

Publication Number Publication Date
WO2011071691A2 true WO2011071691A2 (fr) 2011-06-16
WO2011071691A3 WO2011071691A3 (fr) 2011-11-24

Family

ID=44080885

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2010/057763 WO2011071691A2 (fr) 2009-12-08 2010-11-23 Unité télescopique avec barrière soluble

Country Status (6)

Country Link
US (1) US8297364B2 (fr)
AU (1) AU2010328531B2 (fr)
CA (1) CA2783113C (fr)
GB (1) GB2488282B (fr)
NO (1) NO341042B1 (fr)
WO (1) WO2011071691A2 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10196880B2 (en) 2014-12-29 2019-02-05 Halliburton Energy Services, Inc. Multilateral junction with wellbore isolation
US10655433B2 (en) 2014-12-29 2020-05-19 Halliburton Energy Services, Inc. Multilateral junction with wellbore isolation using degradable isolation components

Families Citing this family (74)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9101978B2 (en) 2002-12-08 2015-08-11 Baker Hughes Incorporated Nanomatrix powder metal compact
US8327931B2 (en) 2009-12-08 2012-12-11 Baker Hughes Incorporated Multi-component disappearing tripping ball and method for making the same
US8403037B2 (en) 2009-12-08 2013-03-26 Baker Hughes Incorporated Dissolvable tool and method
US9079246B2 (en) 2009-12-08 2015-07-14 Baker Hughes Incorporated Method of making a nanomatrix powder metal compact
US8297364B2 (en) 2009-12-08 2012-10-30 Baker Hughes Incorporated Telescopic unit with dissolvable barrier
US9109429B2 (en) 2002-12-08 2015-08-18 Baker Hughes Incorporated Engineered powder compact composite material
US9682425B2 (en) 2009-12-08 2017-06-20 Baker Hughes Incorporated Coated metallic powder and method of making the same
US20110005759A1 (en) * 2009-07-10 2011-01-13 Baker Hughes Incorporated Fracturing system and method
US9127515B2 (en) 2010-10-27 2015-09-08 Baker Hughes Incorporated Nanomatrix carbon composite
US8425651B2 (en) 2010-07-30 2013-04-23 Baker Hughes Incorporated Nanomatrix metal composite
US9243475B2 (en) 2009-12-08 2016-01-26 Baker Hughes Incorporated Extruded powder metal compact
US8528633B2 (en) 2009-12-08 2013-09-10 Baker Hughes Incorporated Dissolvable tool and method
US9227243B2 (en) 2009-12-08 2016-01-05 Baker Hughes Incorporated Method of making a powder metal compact
US10240419B2 (en) 2009-12-08 2019-03-26 Baker Hughes, A Ge Company, Llc Downhole flow inhibition tool and method of unplugging a seat
US8573295B2 (en) 2010-11-16 2013-11-05 Baker Hughes Incorporated Plug and method of unplugging a seat
US8297349B2 (en) * 2010-01-26 2012-10-30 Baker Hughes Incorporated Openable port and method
US8424610B2 (en) 2010-03-05 2013-04-23 Baker Hughes Incorporated Flow control arrangement and method
US8776884B2 (en) 2010-08-09 2014-07-15 Baker Hughes Incorporated Formation treatment system and method
US9090955B2 (en) 2010-10-27 2015-07-28 Baker Hughes Incorporated Nanomatrix powder metal composite
US8789610B2 (en) 2011-04-08 2014-07-29 Baker Hughes Incorporated Methods of casing a wellbore with corrodable boring shoes
US9080098B2 (en) 2011-04-28 2015-07-14 Baker Hughes Incorporated Functionally gradient composite article
US8631876B2 (en) 2011-04-28 2014-01-21 Baker Hughes Incorporated Method of making and using a functionally gradient composite tool
US8844635B2 (en) 2011-05-26 2014-09-30 Baker Hughes Incorporated Corrodible triggering elements for use with subterranean borehole tools having expandable members and related methods
US9139928B2 (en) 2011-06-17 2015-09-22 Baker Hughes Incorporated Corrodible downhole article and method of removing the article from downhole environment
US9428988B2 (en) * 2011-06-17 2016-08-30 Magnum Oil Tools International, Ltd. Hydrocarbon well and technique for perforating casing toe
US9707739B2 (en) 2011-07-22 2017-07-18 Baker Hughes Incorporated Intermetallic metallic composite, method of manufacture thereof and articles comprising the same
US9643250B2 (en) * 2011-07-29 2017-05-09 Baker Hughes Incorporated Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle
US9833838B2 (en) 2011-07-29 2017-12-05 Baker Hughes, A Ge Company, Llc Method of controlling the corrosion rate of alloy particles, alloy particle with controlled corrosion rate, and articles comprising the particle
US9057242B2 (en) 2011-08-05 2015-06-16 Baker Hughes Incorporated Method of controlling corrosion rate in downhole article, and downhole article having controlled corrosion rate
US9033055B2 (en) 2011-08-17 2015-05-19 Baker Hughes Incorporated Selectively degradable passage restriction and method
US9856547B2 (en) 2011-08-30 2018-01-02 Bakers Hughes, A Ge Company, Llc Nanostructured powder metal compact
US9109269B2 (en) * 2011-08-30 2015-08-18 Baker Hughes Incorporated Magnesium alloy powder metal compact
US9090956B2 (en) 2011-08-30 2015-07-28 Baker Hughes Incorporated Aluminum alloy powder metal compact
US9643144B2 (en) 2011-09-02 2017-05-09 Baker Hughes Incorporated Method to generate and disperse nanostructures in a composite material
US9347119B2 (en) 2011-09-03 2016-05-24 Baker Hughes Incorporated Degradable high shock impedance material
WO2013033535A2 (fr) * 2011-09-03 2013-03-07 Baker Hughes Incorporated Matériau dégradable à haute impédance aux chocs
US9133695B2 (en) 2011-09-03 2015-09-15 Baker Hughes Incorporated Degradable shaped charge and perforating gun system
US9187990B2 (en) 2011-09-03 2015-11-17 Baker Hughes Incorporated Method of using a degradable shaped charge and perforating gun system
US9010428B2 (en) 2011-09-06 2015-04-21 Baker Hughes Incorporated Swelling acceleration using inductively heated and embedded particles in a subterranean tool
US8893792B2 (en) 2011-09-30 2014-11-25 Baker Hughes Incorporated Enhancing swelling rate for subterranean packers and screens
CA2755848C (fr) * 2011-10-19 2016-08-16 Ten K Energy Service Ltd. Insertion pour un appareil de forage de fond de puits
US9284812B2 (en) 2011-11-21 2016-03-15 Baker Hughes Incorporated System for increasing swelling efficiency
US9309733B2 (en) 2012-01-25 2016-04-12 Baker Hughes Incorporated Tubular anchoring system and method
US9284803B2 (en) 2012-01-25 2016-03-15 Baker Hughes Incorporated One-way flowable anchoring system and method of treating and producing a well
US9010416B2 (en) 2012-01-25 2015-04-21 Baker Hughes Incorporated Tubular anchoring system and a seat for use in the same
US9016388B2 (en) 2012-02-03 2015-04-28 Baker Hughes Incorporated Wiper plug elements and methods of stimulating a wellbore environment
US9068428B2 (en) 2012-02-13 2015-06-30 Baker Hughes Incorporated Selectively corrodible downhole article and method of use
US8950504B2 (en) 2012-05-08 2015-02-10 Baker Hughes Incorporated Disintegrable tubular anchoring system and method of using the same
US9605508B2 (en) 2012-05-08 2017-03-28 Baker Hughes Incorporated Disintegrable and conformable metallic seal, and method of making the same
US9016363B2 (en) 2012-05-08 2015-04-28 Baker Hughes Incorporated Disintegrable metal cone, process of making, and use of the same
US20150218886A1 (en) 2012-08-13 2015-08-06 Matthew A. Dawson Penetrating A Subterranean Formation
US9033046B2 (en) * 2012-10-10 2015-05-19 Baker Hughes Incorporated Multi-zone fracturing and sand control completion system and method thereof
US9085968B2 (en) 2012-12-06 2015-07-21 Baker Hughes Incorporated Expandable tubular and method of making same
US8967279B2 (en) 2013-01-04 2015-03-03 Baker Hughes Incorporated Reinforced shear components and methods of using same
US9528343B2 (en) 2013-01-17 2016-12-27 Parker-Hannifin Corporation Degradable ball sealer
US9027637B2 (en) * 2013-04-10 2015-05-12 Halliburton Energy Services, Inc. Flow control screen assembly having an adjustable inflow control device
US9677349B2 (en) 2013-06-20 2017-06-13 Baker Hughes Incorporated Downhole entry guide having disappearing profile and methods of using same
US9816339B2 (en) 2013-09-03 2017-11-14 Baker Hughes, A Ge Company, Llc Plug reception assembly and method of reducing restriction in a borehole
US10865465B2 (en) 2017-07-27 2020-12-15 Terves, Llc Degradable metal matrix composite
US11167343B2 (en) 2014-02-21 2021-11-09 Terves, Llc Galvanically-active in situ formed particles for controlled rate dissolving tools
CA2936851A1 (fr) 2014-02-21 2015-08-27 Terves, Inc. Systeme metallique de desintegration a activation par fluide
US9910026B2 (en) 2015-01-21 2018-03-06 Baker Hughes, A Ge Company, Llc High temperature tracers for downhole detection of produced water
US10378303B2 (en) 2015-03-05 2019-08-13 Baker Hughes, A Ge Company, Llc Downhole tool and method of forming the same
US9879492B2 (en) 2015-04-22 2018-01-30 Baker Hughes, A Ge Company, Llc Disintegrating expand in place barrier assembly
US9885229B2 (en) 2015-04-22 2018-02-06 Baker Hughes, A Ge Company, Llc Disappearing expandable cladding
BR112017024312B1 (pt) 2015-05-12 2022-10-25 Shell Internationale Research Maatschappij B.V Método compreendendo fornecer composições induzivelmente degradáveis que compreendem poliacetal para uso em formações subterrâneas
US10221637B2 (en) 2015-08-11 2019-03-05 Baker Hughes, A Ge Company, Llc Methods of manufacturing dissolvable tools via liquid-solid state molding
US10016810B2 (en) 2015-12-14 2018-07-10 Baker Hughes, A Ge Company, Llc Methods of manufacturing degradable tools using a galvanic carrier and tools manufactured thereof
CA2915601A1 (fr) 2015-12-21 2017-06-21 Vanguard Completions Ltd. Bouchons de descente de fond de trou, vannes de fond de trou, outils de fracturation et methodes d'utilisation associees
US10677008B2 (en) * 2017-03-01 2020-06-09 Baker Hughes, A Ge Company, Llc Downhole tools and methods of controllably disintegrating the tools
US11313178B2 (en) * 2020-04-24 2022-04-26 Saudi Arabian Oil Company Concealed nozzle drill bit
CN111872385B (zh) * 2020-06-30 2022-06-03 中国石油天然气集团有限公司 一种双金属复合油井管螺纹接头的局部增材制造方法
US20220333458A1 (en) * 2021-04-15 2022-10-20 Canadian Casing Accessories Inc. Modified casing buoyancy system and methods of use
US11795789B1 (en) * 2022-08-15 2023-10-24 Saudi Arabian Oil Company Cased perforation tools

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5829520A (en) * 1995-02-14 1998-11-03 Baker Hughes Incorporated Method and apparatus for testing, completion and/or maintaining wellbores using a sensor device
US20050194143A1 (en) * 2004-03-05 2005-09-08 Baker Hughes Incorporated One trip perforating, cementing, and sand management apparatus and method
US7401648B2 (en) * 2004-06-14 2008-07-22 Baker Hughes Incorporated One trip well apparatus with sand control
US20080296024A1 (en) * 2007-05-29 2008-12-04 Baker Hughes Incorporated Procedures and Compositions for Reservoir Protection

Family Cites Families (195)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2238895A (en) * 1939-04-12 1941-04-22 Acme Fishing Tool Company Cleansing attachment for rotary well drills
US2261292A (en) 1939-07-25 1941-11-04 Standard Oil Dev Co Method for completing oil wells
US3106959A (en) 1960-04-15 1963-10-15 Gulf Research Development Co Method of fracturing a subsurface formation
US3326291A (en) 1964-11-12 1967-06-20 Zandmer Solis Myron Duct-forming devices
US3637446A (en) 1966-01-24 1972-01-25 Uniroyal Inc Manufacture of radial-filament spheres
US3390724A (en) * 1966-02-01 1968-07-02 Zanal Corp Of Alberta Ltd Duct forming device with a filter
US3645331A (en) 1970-08-03 1972-02-29 Exxon Production Research Co Method for sealing nozzles in a drill bit
DK125207B (da) 1970-08-21 1973-01-15 Atomenergikommissionen Fremgangsmåde til fremstilling af dispersionsforstærkede zirconiumprodukter.
US3894850A (en) 1973-10-19 1975-07-15 Jury Matveevich Kovalchuk Superhard composition material based on cubic boron nitride and a method for preparing same
US4039717A (en) * 1973-11-16 1977-08-02 Shell Oil Company Method for reducing the adherence of crude oil to sucker rods
US4010583A (en) 1974-05-28 1977-03-08 Engelhard Minerals & Chemicals Corporation Fixed-super-abrasive tool and method of manufacture thereof
US4157732A (en) 1977-10-25 1979-06-12 Ppg Industries, Inc. Method and apparatus for well completion
US4248307A (en) * 1979-05-07 1981-02-03 Baker International Corporation Latch assembly and method
US4373584A (en) * 1979-05-07 1983-02-15 Baker International Corporation Single trip tubing hanger assembly
US4374543A (en) * 1980-08-19 1983-02-22 Tri-State Oil Tool Industries, Inc. Apparatus for well treating
US4372384A (en) * 1980-09-19 1983-02-08 Geo Vann, Inc. Well completion method and apparatus
US4384616A (en) * 1980-11-28 1983-05-24 Mobil Oil Corporation Method of placing pipe into deviated boreholes
US4716964A (en) 1981-08-10 1988-01-05 Exxon Production Research Company Use of degradable ball sealers to seal casing perforations in well treatment fluid diversion
US4422508A (en) * 1981-08-27 1983-12-27 Fiberflex Products, Inc. Methods for pulling sucker rod strings
US4399871A (en) * 1981-12-16 1983-08-23 Otis Engineering Corporation Chemical injection valve with openable bypass
US4452311A (en) * 1982-09-24 1984-06-05 Otis Engineering Corporation Equalizing means for well tools
US4681133A (en) * 1982-11-05 1987-07-21 Hydril Company Rotatable ball valve apparatus and method
US4534414A (en) * 1982-11-10 1985-08-13 Camco, Incorporated Hydraulic control fluid communication nipple
US4499049A (en) 1983-02-23 1985-02-12 Metal Alloys, Inc. Method of consolidating a metallic or ceramic body
US4499048A (en) 1983-02-23 1985-02-12 Metal Alloys, Inc. Method of consolidating a metallic body
US4498543A (en) * 1983-04-25 1985-02-12 Union Oil Company Of California Method for placing a liner in a pressurized well
US4539175A (en) 1983-09-26 1985-09-03 Metal Alloys Inc. Method of object consolidation employing graphite particulate
FR2556406B1 (fr) * 1983-12-08 1986-10-10 Flopetrol Procede pour actionner un outil dans un puits a une profondeur determinee et outil permettant la mise en oeuvre du procede
US4708202A (en) * 1984-05-17 1987-11-24 The Western Company Of North America Drillable well-fluid flow control tool
US4709761A (en) * 1984-06-29 1987-12-01 Otis Engineering Corporation Well conduit joint sealing system
US4674572A (en) * 1984-10-04 1987-06-23 Union Oil Company Of California Corrosion and erosion-resistant wellhousing
US4664962A (en) 1985-04-08 1987-05-12 Additive Technology Corporation Printed circuit laminate, printed circuit board produced therefrom, and printed circuit process therefor
US4678037A (en) * 1985-12-06 1987-07-07 Amoco Corporation Method and apparatus for completing a plurality of zones in a wellbore
US4738599A (en) * 1986-01-25 1988-04-19 Shilling James R Well pump
US4673549A (en) 1986-03-06 1987-06-16 Gunes Ecer Method for preparing fully dense, near-net-shaped objects by powder metallurgy
US4693863A (en) 1986-04-09 1987-09-15 Carpenter Technology Corporation Process and apparatus to simultaneously consolidate and reduce metal powders
NZ218154A (en) * 1986-04-26 1989-01-06 Takenaka Komuten Co Container of borehole crevice plugging agentopened by falling pilot weight
NZ218143A (en) * 1986-06-10 1989-03-29 Takenaka Komuten Co Annular paper capsule with lugged frangible plate for conveying plugging agent to borehole drilling fluid sink
US4708208A (en) * 1986-06-23 1987-11-24 Baker Oil Tools, Inc. Method and apparatus for setting, unsetting, and retrieving a packer from a subterranean well
US4869325A (en) * 1986-06-23 1989-09-26 Baker Hughes Incorporated Method and apparatus for setting, unsetting, and retrieving a packer or bridge plug from a subterranean well
US4805699A (en) * 1986-06-23 1989-02-21 Baker Hughes Incorporated Method and apparatus for setting, unsetting, and retrieving a packer or bridge plug from a subterranean well
US4688641A (en) * 1986-07-25 1987-08-25 Camco, Incorporated Well packer with releasable head and method of releasing
US5222867A (en) * 1986-08-29 1993-06-29 Walker Sr Frank J Method and system for controlling a mechanical pump to monitor and optimize both reservoir and equipment performance
US5063775A (en) * 1987-08-19 1991-11-12 Walker Sr Frank J Method and system for controlling a mechanical pump to monitor and optimize both reservoir and equipment performance
US4714116A (en) * 1986-09-11 1987-12-22 Brunner Travis J Downhole safety valve operable by differential pressure
US4817725A (en) * 1986-11-26 1989-04-04 C. "Jerry" Wattigny, A Part Interest Oil field cable abrading system
US4741973A (en) 1986-12-15 1988-05-03 United Technologies Corporation Silicon carbide abrasive particles having multilayered coating
US4768588A (en) * 1986-12-16 1988-09-06 Kupsa Charles M Connector assembly for a milling tool
US4952902A (en) 1987-03-17 1990-08-28 Tdk Corporation Thermistor materials and elements
USH635H (en) * 1987-04-03 1989-06-06 Injection mandrel
US4784226A (en) * 1987-05-22 1988-11-15 Arrow Oil Tools, Inc. Drillable bridge plug
US5006044A (en) * 1987-08-19 1991-04-09 Walker Sr Frank J Method and system for controlling a mechanical pump to monitor and optimize both reservoir and equipment performance
US4853056A (en) 1988-01-20 1989-08-01 Hoffman Allan C Method of making tennis ball with a single core and cover bonding cure
US5084088A (en) 1988-02-22 1992-01-28 University Of Kentucky Research Foundation High temperature alloys synthesis by electro-discharge compaction
US4975412A (en) 1988-02-22 1990-12-04 University Of Kentucky Research Foundation Method of processing superconducting materials and its products
US4929415A (en) 1988-03-01 1990-05-29 Kenji Okazaki Method of sintering powder
US4869324A (en) * 1988-03-21 1989-09-26 Baker Hughes Incorporated Inflatable packers and methods of utilization
US4889187A (en) * 1988-04-25 1989-12-26 Jamie Bryant Terrell Multi-run chemical cutter and method
US4932474A (en) * 1988-07-14 1990-06-12 Marathon Oil Company Staged screen assembly for gravel packing
US4834184A (en) * 1988-09-22 1989-05-30 Halliburton Company Drillable, testing, treat, squeeze packer
US4909320A (en) * 1988-10-14 1990-03-20 Drilex Systems, Inc. Detonation assembly for explosive wellhead severing system
US4850432A (en) * 1988-10-17 1989-07-25 Texaco Inc. Manual port closing tool for well cementing
US5049165B1 (en) * 1989-01-30 1995-09-26 Ultimate Abrasive Syst Inc Composite material
US4890675A (en) * 1989-03-08 1990-01-02 Dew Edward G Horizontal drilling through casing window
US4977958A (en) * 1989-07-26 1990-12-18 Miller Stanley J Downhole pump filter
US5117915A (en) * 1989-08-31 1992-06-02 Union Oil Company Of California Well casing flotation device and method
MY106026A (en) * 1989-08-31 1995-02-28 Union Oil Company Of California Well casing flotation device and method
US4986361A (en) * 1989-08-31 1991-01-22 Union Oil Company Of California Well casing flotation device and method
US4981177A (en) * 1989-10-17 1991-01-01 Baker Hughes Incorporated Method and apparatus for establishing communication with a downhole portion of a control fluid pipe
US4944351A (en) * 1989-10-26 1990-07-31 Baker Hughes Incorporated Downhole safety valve for subterranean well and method
US4949788A (en) * 1989-11-08 1990-08-21 Halliburton Company Well completions using casing valves
US5095988A (en) * 1989-11-15 1992-03-17 Bode Robert E Plug injection method and apparatus
GB2240798A (en) * 1990-02-12 1991-08-14 Shell Int Research Method and apparatus for perforating a well liner and for fracturing a surrounding formation
US5178216A (en) * 1990-04-25 1993-01-12 Halliburton Company Wedge lock ring
US5271468A (en) * 1990-04-26 1993-12-21 Halliburton Company Downhole tool apparatus with non-metallic components and methods of drilling thereof
US5074361A (en) * 1990-05-24 1991-12-24 Halliburton Company Retrieving tool and method
US5010955A (en) * 1990-05-29 1991-04-30 Smith International, Inc. Casing mill and method
US5048611A (en) * 1990-06-04 1991-09-17 Lindsey Completion Systems, Inc. Pressure operated circulation valve
US5090480A (en) * 1990-06-28 1992-02-25 Slimdril International, Inc. Underreamer with simultaneously expandable cutter blades and method
US5036921A (en) * 1990-06-28 1991-08-06 Slimdril International, Inc. Underreamer with sequentially expandable cutter blades
US5188182A (en) * 1990-07-13 1993-02-23 Otis Engineering Corporation System containing expendible isolation valve with frangible sealing member, seat arrangement and method for use
US5188183A (en) * 1991-05-03 1993-02-23 Baker Hughes Incorporated Method and apparatus for controlling the flow of well bore fluids
US5161614A (en) * 1991-05-31 1992-11-10 Marguip, Inc. Apparatus and method for accessing the casing of a burning oil well
US5292478A (en) 1991-06-24 1994-03-08 Ametek, Specialty Metal Products Division Copper-molybdenum composite strip
US5228518A (en) * 1991-09-16 1993-07-20 Conoco Inc. Downhole activated process and apparatus for centralizing pipe in a wellbore
US5234055A (en) * 1991-10-10 1993-08-10 Atlantic Richfield Company Wellbore pressure differential control for gravel pack screen
US5252365A (en) 1992-01-28 1993-10-12 White Engineering Corporation Method for stabilization and lubrication of elastomers
US5226483A (en) * 1992-03-04 1993-07-13 Otis Engineering Corporation Safety valve landing nipple and method
US5293940A (en) * 1992-03-26 1994-03-15 Schlumberger Technology Corporation Automatic tubing release
US5253714A (en) * 1992-08-17 1993-10-19 Baker Hughes Incorporated Well service tool
US5282509A (en) * 1992-08-20 1994-02-01 Conoco Inc. Method for cleaning cement plug from wellbore liner
US5310000A (en) * 1992-09-28 1994-05-10 Halliburton Company Foil wrapped base pipe for sand control
US5380473A (en) 1992-10-23 1995-01-10 Fuisz Technologies Ltd. Process for making shearform matrix
US5309874A (en) 1993-01-08 1994-05-10 Ford Motor Company Powertrain component with adherent amorphous or nanocrystalline ceramic coating system
US5392860A (en) * 1993-03-15 1995-02-28 Baker Hughes Incorporated Heat activated safety fuse
US5394941A (en) * 1993-06-21 1995-03-07 Halliburton Company Fracture oriented completion tool system
US5536485A (en) 1993-08-12 1996-07-16 Agency Of Industrial Science & Technology Diamond sinter, high-pressure phase boron nitride sinter, and processes for producing those sinters
US5407011A (en) * 1993-10-07 1995-04-18 Wada Ventures Downhole mill and method for milling
US5398754A (en) * 1994-01-25 1995-03-21 Baker Hughes Incorporated Retrievable whipstock anchor assembly
US5411082A (en) * 1994-01-26 1995-05-02 Baker Hughes Incorporated Scoophead running tool
US5425424A (en) 1994-02-28 1995-06-20 Baker Hughes Incorporated Casing valve
US5456327A (en) 1994-03-08 1995-10-10 Smith International, Inc. O-ring seal for rock bit bearings
DE4407593C1 (de) 1994-03-08 1995-10-26 Plansee Metallwerk Verfahren zur Herstellung von Pulverpreßlingen hoher Dichte
US5479986A (en) 1994-05-02 1996-01-02 Halliburton Company Temporary plug system
US6403210B1 (en) 1995-03-07 2002-06-11 Nederlandse Organisatie Voor Toegepast-Natuurwetenschappelijk Onderzoek Tno Method for manufacturing a composite material
CA2215402A1 (fr) 1995-03-14 1996-09-19 Takafumi Atarashi Poudre a pellicule multicouche sur sa surface et son procede de preparation
DE69513203T2 (de) 1995-10-31 2000-07-20 Ecole Polytech Batterie-anordnung von fotovoltaischen zellen und herstellungsverfahren
US5772735A (en) 1995-11-02 1998-06-30 University Of New Mexico Supported inorganic membranes
US5698081A (en) 1995-12-07 1997-12-16 Materials Innovation, Inc. Coating particles in a centrifugal bed
EP0828922B1 (fr) 1996-03-22 2001-06-27 Smith International, Inc. Boule d'actionnement
US5905000A (en) * 1996-09-03 1999-05-18 Nanomaterials Research Corporation Nanostructured ion conducting solid electrolytes
DE19716524C1 (de) 1997-04-19 1998-08-20 Daimler Benz Aerospace Ag Verfahren zur Herstellung eines Körpers mit einem Hohlraum
US6612826B1 (en) 1997-10-15 2003-09-02 Iap Research, Inc. System for consolidating powders
US6189618B1 (en) 1998-04-20 2001-02-20 Weatherford/Lamb, Inc. Wellbore wash nozzle system
DE19844397A1 (de) 1998-09-28 2000-03-30 Hilti Ag Abrasive Schneidkörper enthaltend Diamantpartikel und Verfahren zur Herstellung der Schneidkörper
JP2000185725A (ja) 1998-12-21 2000-07-04 Sachiko Ando 筒状包装体
US6561269B1 (en) 1999-04-30 2003-05-13 The Regents Of The University Of California Canister, sealing method and composition for sealing a borehole
US6613383B1 (en) 1999-06-21 2003-09-02 Regents Of The University Of Colorado Atomic layer controlled deposition on particle surfaces
US6341747B1 (en) 1999-10-28 2002-01-29 United Technologies Corporation Nanocomposite layered airfoil
US6713177B2 (en) 2000-06-21 2004-03-30 Regents Of The University Of Colorado Insulating and functionalizing fine metal-containing particles with conformal ultra-thin films
US6472068B1 (en) 2000-10-26 2002-10-29 Sandia Corporation Glass rupture disk
US6491097B1 (en) 2000-12-14 2002-12-10 Halliburton Energy Services, Inc. Abrasive slurry delivery apparatus and methods of using same
US6491083B2 (en) 2001-02-06 2002-12-10 Anadigics, Inc. Wafer demount receptacle for separation of thinned wafer from mounting carrier
JP3607655B2 (ja) 2001-09-26 2005-01-05 株式会社東芝 マウント材、半導体装置及び半導体装置の製造方法
US7017677B2 (en) 2002-07-24 2006-03-28 Smith International, Inc. Coarse carbide substrate cutting elements and method of forming the same
US20040005483A1 (en) 2002-03-08 2004-01-08 Chhiu-Tsu Lin Perovskite manganites for use in coatings
US6939388B2 (en) 2002-07-23 2005-09-06 General Electric Company Method for making materials having artificially dispersed nano-size phases and articles made therewith
US6943207B2 (en) 2002-09-13 2005-09-13 H.B. Fuller Licensing & Financing Inc. Smoke suppressant hot melt adhesive composition
US6887297B2 (en) 2002-11-08 2005-05-03 Wayne State University Copper nanocrystals and methods of producing same
US8403037B2 (en) 2009-12-08 2013-03-26 Baker Hughes Incorporated Dissolvable tool and method
US8297364B2 (en) 2009-12-08 2012-10-30 Baker Hughes Incorporated Telescopic unit with dissolvable barrier
US9101978B2 (en) 2002-12-08 2015-08-11 Baker Hughes Incorporated Nanomatrix powder metal compact
US9109429B2 (en) 2002-12-08 2015-08-18 Baker Hughes Incorporated Engineered powder compact composite material
US9682425B2 (en) 2009-12-08 2017-06-20 Baker Hughes Incorporated Coated metallic powder and method of making the same
US9079246B2 (en) 2009-12-08 2015-07-14 Baker Hughes Incorporated Method of making a nanomatrix powder metal compact
JP2004225084A (ja) 2003-01-21 2004-08-12 Nissin Kogyo Co Ltd 自動車用ナックル
JP2004225765A (ja) 2003-01-21 2004-08-12 Nissin Kogyo Co Ltd 車両用ディスクブレーキのディスクロータ
US7416029B2 (en) 2003-04-01 2008-08-26 Specialised Petroleum Services Group Limited Downhole tool
JP4599294B2 (ja) 2003-04-14 2010-12-15 積水化学工業株式会社 合わせガラスの剥離方法
DE10318801A1 (de) 2003-04-17 2004-11-04 Aesculap Ag & Co. Kg Flächiges Implantat und seine Verwendung in der Chirurgie
US20040231845A1 (en) 2003-05-15 2004-11-25 Cooke Claude E. Applications of degradable polymers in wells
CA2530471A1 (fr) 2003-06-23 2005-02-17 William Marsh Rice University Elastomeres renforces par des nanotubes de carbone
JP4222157B2 (ja) 2003-08-28 2009-02-12 大同特殊鋼株式会社 剛性および強度が向上したチタン合金
JP4593473B2 (ja) 2003-10-29 2010-12-08 住友精密工業株式会社 カーボンナノチューブ分散複合材料の製造方法
US20050102255A1 (en) 2003-11-06 2005-05-12 Bultman David C. Computer-implemented system and method for handling stored data
US20050109502A1 (en) 2003-11-20 2005-05-26 Jeremy Buc Slay Downhole seal element formed from a nanocomposite material
US7013998B2 (en) 2003-11-20 2006-03-21 Halliburton Energy Services, Inc. Drill bit having an improved seal and lubrication method using same
US20050161212A1 (en) 2004-01-23 2005-07-28 Schlumberger Technology Corporation System and Method for Utilizing Nano-Scale Filler in Downhole Applications
US7044230B2 (en) 2004-01-27 2006-05-16 Halliburton Energy Services, Inc. Method for removing a tool from a well
US7353879B2 (en) 2004-03-18 2008-04-08 Halliburton Energy Services, Inc. Biodegradable downhole tools
US7093664B2 (en) 2004-03-18 2006-08-22 Halliburton Energy Services, Inc. One-time use composite tool formed of fibers and a biodegradable resin
US7168494B2 (en) 2004-03-18 2007-01-30 Halliburton Energy Services, Inc. Dissolvable downhole tools
US7250188B2 (en) 2004-03-31 2007-07-31 Her Majesty The Queen In Right Of Canada, As Represented By The Minister Of National Defense Of Her Majesty's Canadian Government Depositing metal particles on carbon nanotubes
US8211247B2 (en) 2006-02-09 2012-07-03 Schlumberger Technology Corporation Degradable compositions, apparatus comprising same, and method of use
JP4476701B2 (ja) 2004-06-02 2010-06-09 日本碍子株式会社 電極内蔵焼結体の製造方法
US7141207B2 (en) 2004-08-30 2006-11-28 General Motors Corporation Aluminum/magnesium 3D-Printing rapid prototyping
JP2006078614A (ja) 2004-09-08 2006-03-23 Ricoh Co Ltd 電子写真感光体中間層用塗工液、それを用いた電子写真感光体、画像形成装置及び画像形成装置用プロセスカートリッジ
US8309230B2 (en) 2004-11-12 2012-11-13 Inmat, Inc. Multilayer nanocomposite barrier structures
JP5255842B2 (ja) 2004-12-03 2013-08-07 エクソンモービル・ケミカル・パテンツ・インク ナノ複合組成物を製造するための修飾層状フィラーおよびその使用法
US7322417B2 (en) 2004-12-14 2008-01-29 Schlumberger Technology Corporation Technique and apparatus for completing multiple zones
US7350582B2 (en) 2004-12-21 2008-04-01 Weatherford/Lamb, Inc. Wellbore tool with disintegratable components and method of controlling flow
US20060260031A1 (en) 2005-05-20 2006-11-23 Conrad Joseph M Iii Potty training device
US20070131912A1 (en) 2005-07-08 2007-06-14 Simone Davide L Electrically conductive adhesives
US7509993B1 (en) 2005-08-13 2009-03-31 Wisconsin Alumni Research Foundation Semi-solid forming of metal-matrix nanocomposites
US8567494B2 (en) 2005-08-31 2013-10-29 Schlumberger Technology Corporation Well operating elements comprising a soluble component and methods of use
JP4721828B2 (ja) 2005-08-31 2011-07-13 東京応化工業株式会社 サポートプレートの剥離方法
JP5148820B2 (ja) 2005-09-07 2013-02-20 株式会社イーアンドエフ チタン合金複合材料およびその製造方法
US20080020923A1 (en) 2005-09-13 2008-01-24 Debe Mark K Multilayered nanostructured films
US7363970B2 (en) 2005-10-25 2008-04-29 Schlumberger Technology Corporation Expandable packer
US8231947B2 (en) 2005-11-16 2012-07-31 Schlumberger Technology Corporation Oilfield elements having controlled solubility and methods of use
US7604049B2 (en) 2005-12-16 2009-10-20 Schlumberger Technology Corporation Polymeric composites, oilfield elements comprising same, and methods of using same in oilfield applications
US7647964B2 (en) 2005-12-19 2010-01-19 Fairmount Minerals, Ltd. Degradable ball sealers and methods for use in well treatment
US7579087B2 (en) 2006-01-10 2009-08-25 United Technologies Corporation Thermal barrier coating compositions, processes for applying same and articles coated with same
US8770261B2 (en) 2006-02-09 2014-07-08 Schlumberger Technology Corporation Methods of manufacturing degradable alloys and products made from degradable alloys
US8220554B2 (en) * 2006-02-09 2012-07-17 Schlumberger Technology Corporation Degradable whipstock apparatus and method of use
US7325617B2 (en) 2006-03-24 2008-02-05 Baker Hughes Incorporated Frac system without intervention
WO2007118048A2 (fr) 2006-04-03 2007-10-18 William Marsh Rice University Traitement de composites a nanotube de carbone a paroi unique avec matrice metallique fabriques par un procede de chauffage par induction
US8021721B2 (en) 2006-05-01 2011-09-20 Smith International, Inc. Composite coating with nanoparticles for improved wear and lubricity in down hole tools
US7441596B2 (en) 2006-06-23 2008-10-28 Baker Hughes Incorporated Swelling element packer and installation method
US8281860B2 (en) 2006-08-25 2012-10-09 Schlumberger Technology Corporation Method and system for treating a subterranean formation
US7559357B2 (en) 2006-10-25 2009-07-14 Baker Hughes Incorporated Frac-pack casing saver
EP2082619B1 (fr) 2006-11-06 2022-10-12 Agency for Science, Technology And Research Empilement de barrières d'encapsulation de nanoparticules
US20080149351A1 (en) 2006-12-20 2008-06-26 Schlumberger Technology Corporation Temporary containments for swellable and inflatable packer elements
US7875313B2 (en) 2007-04-05 2011-01-25 E. I. Du Pont De Nemours And Company Method to form a pattern of functional material on a substrate using a mask material
US20080314588A1 (en) 2007-06-20 2008-12-25 Schlumberger Technology Corporation System and method for controlling erosion of components during well treatment
US20090038858A1 (en) 2007-08-06 2009-02-12 Smith International, Inc. Use of nanosized particulates and fibers in elastomer seals for improved performance metrics for roller cone bits
US7503392B2 (en) 2007-08-13 2009-03-17 Baker Hughes Incorporated Deformable ball seat
US7644772B2 (en) 2007-08-13 2010-01-12 Baker Hughes Incorporated Ball seat having segmented arcuate ball support member
US7637323B2 (en) 2007-08-13 2009-12-29 Baker Hughes Incorporated Ball seat having fluid activated ball support
CN101816224A (zh) 2007-10-02 2010-08-25 派克汉尼芬公司 用于电磁干扰(emi)垫片的纳米涂料
US8371369B2 (en) 2007-12-04 2013-02-12 Baker Hughes Incorporated Crossover sub with erosion resistant inserts
US20090152009A1 (en) 2007-12-18 2009-06-18 Halliburton Energy Services, Inc., A Delaware Corporation Nano particle reinforced polymer element for stator and rotor assembly
US8413727B2 (en) 2009-05-20 2013-04-09 Bakers Hughes Incorporated Dissolvable downhole tool, method of making and using
US8528633B2 (en) 2009-12-08 2013-09-10 Baker Hughes Incorporated Dissolvable tool and method
US20110135805A1 (en) 2009-12-08 2011-06-09 Doucet Jim R High diglyceride structuring composition and products and methods using the same

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5829520A (en) * 1995-02-14 1998-11-03 Baker Hughes Incorporated Method and apparatus for testing, completion and/or maintaining wellbores using a sensor device
US20050194143A1 (en) * 2004-03-05 2005-09-08 Baker Hughes Incorporated One trip perforating, cementing, and sand management apparatus and method
US7401648B2 (en) * 2004-06-14 2008-07-22 Baker Hughes Incorporated One trip well apparatus with sand control
US20080296024A1 (en) * 2007-05-29 2008-12-04 Baker Hughes Incorporated Procedures and Compositions for Reservoir Protection

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10196880B2 (en) 2014-12-29 2019-02-05 Halliburton Energy Services, Inc. Multilateral junction with wellbore isolation
US10655433B2 (en) 2014-12-29 2020-05-19 Halliburton Energy Services, Inc. Multilateral junction with wellbore isolation using degradable isolation components
US11313205B2 (en) 2014-12-29 2022-04-26 Halliburton Energy Services, Inc. Multilateral junction with wellbore isolation
US11506025B2 (en) 2014-12-29 2022-11-22 Halliburton Energy Services, Inc. Multilateral junction with wellbore isolation using degradable isolation components

Also Published As

Publication number Publication date
CA2783113A1 (fr) 2011-06-16
GB2488282A (en) 2012-08-22
NO341042B1 (no) 2017-08-14
US8297364B2 (en) 2012-10-30
AU2010328531B2 (en) 2014-08-21
US20110132612A1 (en) 2011-06-09
GB201209720D0 (en) 2012-07-18
WO2011071691A3 (fr) 2011-11-24
AU2010328531A1 (en) 2012-06-07
CA2783113C (fr) 2015-01-20
GB2488282B (en) 2015-10-14
NO20120596A1 (no) 2012-08-28

Similar Documents

Publication Publication Date Title
CA2783113C (fr) Unite telescopique avec barriere soluble
US10669797B2 (en) Tool configured to dissolve in a selected subsurface environment
AU2016203091B2 (en) Plug and method of unplugging a seat
US9022107B2 (en) Dissolvable tool
AU2012259072B2 (en) Formation treatment system and method
US8714268B2 (en) Method of making and using multi-component disappearing tripping ball
US8403037B2 (en) Dissolvable tool and method
EP2737156A2 (fr) Comprimé extrudé de métal en poudre
EP2509734A2 (fr) Procédé de fabrication d'un ensemble compact nanomatriciel de poudre métallique
WO2011071910A2 (fr) Matériau composite compact de poudre manufacturé
EP2509731A2 (fr) Compact métallique en poudre à nanomatrice
WO2013019410A2 (fr) Procédé permettant de préparer un comprimé métallique en poudre

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10836417

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2010328531

Country of ref document: AU

ENP Entry into the national phase

Ref document number: 1209720

Country of ref document: GB

Kind code of ref document: A

Free format text: PCT FILING DATE = 20101123

WWE Wipo information: entry into national phase

Ref document number: 1209720.0

Country of ref document: GB

ENP Entry into the national phase

Ref document number: 2783113

Country of ref document: CA

ENP Entry into the national phase

Ref document number: 2010328531

Country of ref document: AU

Date of ref document: 20101123

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10836417

Country of ref document: EP

Kind code of ref document: A2