Classifications

• • D—TEXTILES; PAPER
  • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
  • D06P—DYEING OR PRINTING TEXTILES; DYEING LEATHER, FURS OR SOLID MACROMOLECULAR SUBSTANCES IN ANY FORM
  • D06P1/00—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed
  • D06P1/44—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed using insoluble pigments or auxiliary substances, e.g. binders
  • D06P1/64—General processes of dyeing or printing textiles, or general processes of dyeing leather, furs, or solid macromolecular substances in any form, classified according to the dyes, pigments, or auxiliary substances employed using insoluble pigments or auxiliary substances, e.g. binders using compositions containing low-molecular-weight organic compounds without sulfate or sulfonate groups
  • D06P1/651—Compounds without nitrogen
  • D06P1/65168—Sulfur-containing compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G75/00—Macromolecular compounds obtained by reactions forming a linkage containing sulfur with or without nitrogen, oxygen, or carbon in the main chain of the macromolecule
  • C08G75/02—Polythioethers
  • C08G75/06—Polythioethers from cyclic thioethers
  • C08G75/08—Polythioethers from cyclic thioethers from thiiranes
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J7/00—Chemical treatment or coating of shaped articles made of macromolecular substances
  • C08J7/04—Coating
  • C08J7/0427—Coating with only one layer of a composition containing a polymer binder
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J7/00—Chemical treatment or coating of shaped articles made of macromolecular substances
  • C08J7/04—Coating
  • C08J7/046—Forming abrasion-resistant coatings; Forming surface-hardening coatings
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B1/00—Optical elements characterised by the material of which they are made; Optical coatings for optical elements
  • G02B1/04—Optical elements characterised by the material of which they are made; Optical coatings for optical elements made of organic materials, e.g. plastics
  • G02B1/041—Lenses
  • G02B1/043—Contact lenses
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2481/00—Characterised by the use of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing sulfur with or without nitrogen, oxygen, or carbon only; Polysulfones; Derivatives of such polymers

Definitions

• the present invention pertains to a method for dyeing substrates to obtain tinted substrates or articles, for example tinted optical or ophthalmic lenses.
• the invention particularly concerns articles obtained from substrates prepared by curing a polymerizable composition comprising at least one monomer containing at least one episulfide group and optionally at least one thiol group.
• the polymerization of said monomer leads to a polymer comprising at least one thioether group.
• Substrate prepared by curing a polymerizable composition comprising at least one monomer containing at least one episulfide group is herein after called "substrate of high refractive index comprising a thioether group”.
• Tinting / colouring an ophthalmic lens is an increasing need.
• substrates of high refractive index comprising a thioether group are difficult to tint with conventional processes such as conventional bath direct tinting.
• Water bath dyeing is not suitable because of its limited dye absorption amount, even during prolonged time.
• the present invention discloses a method that addresses the issues discussed above.
• the invention provides a solution for tinting substrates of high refractive index comprising a thioether group in a short time and achieving a higher tinting intensity with good uniformity.
• a dye solution comprising at least one dye, or dye precursor, and at least one carrier in at least one solvent, the carrier being chosen from the compounds represented by the following formulae (1 ) and (2):
• Ri, R 2 , R3 and R 4 are each selected from the group consisting of the following radicals: alkyl having from 1 to 10 carbon atom, H, -CH 2 SH, -CH 2 SCH 2 CH 2 SH,
• Ri, R 2 , R3 and R 4 are not H or an alkyl simultaneously, or that if any three of Ri, R 2 , R3 and R 4 are H or an alkyl, the other radical consists of one of the following radicals:
• the immersion step can be carried out once, or can be repeated several times, in order to manufacture a tinted substrate of higher intensity.
• This step can be carried out by the use of a dyeing apparatus, in which the substrate is moved in the dye solution according to scheduled sequences.
• the substrate can be immersed totally, or partially. If the substrate is immersed partially, generally only the immersed part of the substrate is tinted.
• the substrate can be a commercially available product, or it can be manufactured just before the tinting.
• the substrate has generally the shape of an article.
• the method according to the invention is rapid, reproducible and easy to carry out. Moreover the tinting of the part of the substrate which is immersed is substantially uniform.
• this method allows the production of the whole range of coloration, from the lightest colour to the darkest colour.
• Substrate in the sense of the present invention, should be understood to mean an uncoated substrate.
• the substrate may in particular be an optically transparent material having the shape of an optical article.
• the substrate has a refractive index of at least 1 .67, preferably from 1 .67 to 1 .79 and more preferably from 1 .71 to 1 .79.
• the monomer containing at least one episulfide group and optionally at least one thiol group according to the invention contains episulfide group(s), or episulfide group(s) and thiol group(s).
• the monomer does not comprise any other functional group than episulfide group(s) (and optionally thiol group(s)).
• the episulfide group has the structure of formula (3): R 6 R 7
• R 5 represents a hydrocarbon group having 1 to 10 carbon atoms
• R6, R7 and Rs each represents a hydrogen atom or a hydrocarbon group having 1 to 10 carbon atoms
• X represents S or O with the proviso that, in the molecule, the average number of S represented by X is about 50% of the total number of S and O in the three-member ring
• X is S.
• the episulfide group has the structure of formula (4):
• R 9 , R10, Rn , R12, R13 and Ri 4 each represents a hydrogen atom or a hydrocarbon group having 1 to 10 carbon atoms
• X represents S or O with the proviso that, in the molecule, the average number of S represented by X is about 50% of the total number of S and O in the three-member ring
• m represents an integer from 0 to 6
• n represents an integer from 0 to 4,
• X is S.
• the polymerizable composition further comprises one or more polythiols of formula R'(SH) n ', in which n' is an integer from 2 to 6 and R' is an organic group of valency equal to n'.
• the carrier is chosen from the group comprising straight-chain dimercaptan compounds such as bis(2- mercaptoethyl) sulfide, 1 ,2-[bis(2-mercaptoethylthio)]ethane; branched aliphatic polymercaptan compounds such as 2-mercaptomethyl-1 ,3-dimercaptopropane, 2-mercaptomethyl-1 ,4-dimercaptobutane, 2-(2-mercaptoethylthio)1 ,3- dimercaptopropane, 1 ,2-bis[(2-mercaptoethylthio)]-3-mercaptopropane, 1 ,1 ,1 - tris(mercaptomethyl)propane and tetrakismercaptomethylmethane ; 4- mercaptomethyl-3,6-dithia-1 ,8-octanedithiol and 2-mercaptoethyl sulphide, preferably said carrier
• the solvent is water or an organic solvent, and more preferably the solvent is water.
• the dye solution can contain a dye chosen from the group of azo type dyes, quinophtalones type dyes, and anthraquinone type dyes.
• the dye solutions which are suitable are commercially available disperse dye solutions, to be combined with at least one carrier according to the invention.
• the dyes sold as BPI® Molecular Catalytic Tints by Brain Power International are available in more than 180 colours.
• the dye solution contains 0.05% to 5%, preferably 0.05% to 1 %, and more preferably 0.08 to 0.5% by weight of the carrier.
• the amount of the dye is not critical but is ordinarily 0.5 to 30 g/ Liter in terms of concentration in the dye solution.
• the dye solution can comprise any other additive known to the one skilled in the art.
• the dye solution can contain an emulsifier, preferably chosen from the group of amine salts or alkali salts of carboxylic, sulfamic or phosphoric acids, acid salts of amines, ethoxylated or propoxylated alkyl or aryl phenolic compounds.
• the optional emulsifier may be used in an amount of 0 to 15 pbw, preferably 0.5 to 5 pbw, more preferably 3 to 4 pbw.
• Emulsifiers which may be used include ionic, non-ionic, or mixtures thereof.
• Typical ionic emulsifiers are anionic, including amine salts or alkali salts of carboxylic, sulfamic or phosphoric acids, for example sodium lauryl sulfate, ammonium lauryl sulfate, lignosulfonic acid salts, ethylene diamine tetra acetic acid (EDTA), sodium salts and acid salts of amines such as laurylamine, hydrochloride or poly(oxy-1 ,2-ethanediyl), alpha-sulfo-omega-hydroxy ether with phenol 1 -(methylphenyl)ethyl derivative ammonium salts ; or amphoteric, that is compounds bearing both anionic and cationic groups, for example lauryl sulfobetaine ; dihydroxy ethylalkyl betaine ; amido betaine based on coconut acids ;
• Typical non-ionic emulsifiers include ethoxylated or propoxylated alkyl or aryl phenolic compounds such as octylphenoxypolyethyleneoxyethanol or poly(oxy-1 ,2-ethanediyl), alpha-phenyl- omega-hydroxy, styrenated.
• the preferred emulsifier is a mixture of C M - Cis and Ci6 - Cis ethoxylated unsaturated fatty acids and poly(oxy-1 ,2-ethanediyl), alpha-sulfo-omega-hydroxy ether with phenol l -(methylphenyl) ethyl derivative ammonium salts and poly(oxy-1 ,2-ethanediyl), alpha-phenyl-omega-hydroxy, styrenated.
• the method of the invention provides tinted substrates in a short time and achieves a higher tinting intensity with good uniformity.
• the method of the invention enables tinting substrates to be provided of different luminous transmittance depending mainly on different tinting times and dye solutions of different dye concentration.
• the length of the immersion is within the range of from 3 to 100 minutes, preferably from 10 to 90 minutes, and more preferably from 30 to 96 minutes.
• the method can further comprise the heating of the dye solution at a temperature of from 90 to 100°C, preferably from 90 to 96°C, and more preferably from 93 to 96°C, during the immersion.
• the invention also concerns an article, preferably an ophthalmic lens, comprising a tinted substrate which is obtained by the method described above.
• the article is preferably such that the luminous transmittance of the article is lower than 20%, preferably lower than
• Said article is advantageously coated with coatings conventionally used in the ophthalmic optics field, such as anti abrasion coatings, scratch resistant coatings or anti-reflection coatings.
• coatings conventionally used in the ophthalmic optics field such as anti abrasion coatings, scratch resistant coatings or anti-reflection coatings.
• the invention thus also concerns said article further comprising at least partially a coating.
• the substrate is a commercially available compound provided by the company Mitsubishi Gas Chemical and sold as having a refractive index no of 1 .74.
• This substrate has a density d of 1 .45, and was obtained from the chemical curing of 2-mercaptoethyl sulfide
• Each water bath solution comprises the carrier and a dye solution (which is a commercially available disperse dye formulation sold as BPI dye solution #46300) diluted in water.
• a dye solution which is a commercially available disperse dye formulation sold as BPI dye solution #46300
• the two tinted substrates so obtained are two ophthalmic lenses according to the invention.
• the results of the measurements on said ophthalmic lenses are given in the Table below, in which Tv is the luminous transmittance and Hz is the haze.
• the haze value of the final ophthalmic lenses was measured by light transmission using the Haze-Guard Plus haze meter from BYK-Gardner (a color difference meter) according to the method of ASTM D1003-00, which is incorporated herein in its entirety by reference. All references to "haze" values in this application are by this standard.
• the instrument was first calibrated according to the manufacturer's instructions. Next, the sample was placed on the transmission light beam of the pre-calibrated meter and the haze value was recorded from three different specimen locations and averaged.
• Luminous transmittance also called “relative light transmission factor in the visible spectrum”
• Tv Luminous transmittance
• Each water bath solution comprises the carrier 4-mercaptomethyl-3,6-dithia-1 ,8- octanedithiol, under 0.1 % by volume concentration, and a dye solution (which is a commercially available disperse dye formulation sold as BPI lens dye solution #46300) diluted in water.
• the temperature during the immersion was equal to 94°C.
• the transmission of the so obtained ophthalmic lens may reach class 3 after 60 minutes immersion in the bath under 94°C.
• the haze level does not exhibit significant change before and after tinting.
• This example shows the possibility of varying the luminous transmittance of the ophthalmic lenses by adjusting tinting time.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Physics & Mathematics (AREA)
• General Physics & Mathematics (AREA)
• Optics & Photonics (AREA)
• Engineering & Computer Science (AREA)
• Textile Engineering (AREA)
• Coloring (AREA)
• Eyeglasses (AREA)
• Application Of Or Painting With Fluid Materials (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)

Priority Applications (3)

Applications Claiming Priority (2)

Publications (2)

Family

ID=42731995

Family Applications (1)

Country Status (7)

Families Citing this family (5)

Citations (1)

Family Cites Families (1)

• 2009
  • 2009-11-10 EP EP09306083A patent/EP2319981B1/en active Active
  • 2009-11-10 AT AT09306083T patent/ATE547556T1/de active
  • 2009-11-10 PT PT09306083T patent/PT2319981E/pt unknown
• 2010
  • 2010-10-14 WO PCT/IB2010/054662 patent/WO2011058460A1/en not_active Ceased
  • 2010-10-14 IN IN4933DEN2012 patent/IN2012DN04933A/en unknown
  • 2010-10-14 CN CN201080050582.4A patent/CN102639784B/zh active Active
  • 2010-10-14 US US13/508,757 patent/US20120238660A1/en not_active Abandoned

Patent Citations (1)

Also Published As

Similar Documents

Legal Events