WO2009136854A1 - Procédé d'amélioration des propriétés magnétiques d'un composant composite magnétique doux compacté et traité à chaud - Google Patents

Procédé d'amélioration des propriétés magnétiques d'un composant composite magnétique doux compacté et traité à chaud Download PDF

Info

Publication number
WO2009136854A1
WO2009136854A1 PCT/SE2009/050492 SE2009050492W WO2009136854A1 WO 2009136854 A1 WO2009136854 A1 WO 2009136854A1 SE 2009050492 W SE2009050492 W SE 2009050492W WO 2009136854 A1 WO2009136854 A1 WO 2009136854A1
Authority
WO
WIPO (PCT)
Prior art keywords
soft magnetic
compacted
heat
stress
component
Prior art date
Application number
PCT/SE2009/050492
Other languages
English (en)
Inventor
Björn SKÅRMAN
Zhou Ye
Original Assignee
Höganäs Ab (Publ)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Höganäs Ab (Publ) filed Critical Höganäs Ab (Publ)
Publication of WO2009136854A1 publication Critical patent/WO2009136854A1/fr

Abstract

L'invention concerne un procédé de production d'un composant magnétique doux compacté et traité à chaud. Le procédé consiste à fournir un composant magnétique doux compacté et traité à chaud produit au moins à partir de particules de poudre de fer isolées électriquement pourvues d'une résistivité électrique, et à soumettre le composant magnétique doux compacté et traité à chaud à une contrainte pendant un laps de temps suffisamment long pour augmenter la résistivité électrique du composant magnétique doux compacté et traité à chaud.
PCT/SE2009/050492 2008-05-09 2009-05-06 Procédé d'amélioration des propriétés magnétiques d'un composant composite magnétique doux compacté et traité à chaud WO2009136854A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
DKPA200800666 2008-05-09
DKPA200800666 2008-05-09
US7167908P 2008-05-12 2008-05-12
US61/071,679 2008-05-12

Publications (1)

Publication Number Publication Date
WO2009136854A1 true WO2009136854A1 (fr) 2009-11-12

Family

ID=40042552

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/SE2009/050492 WO2009136854A1 (fr) 2008-05-09 2009-05-06 Procédé d'amélioration des propriétés magnétiques d'un composant composite magnétique doux compacté et traité à chaud

Country Status (2)

Country Link
TW (1) TW201007782A (fr)
WO (1) WO2009136854A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011140417A1 (fr) * 2010-05-07 2011-11-10 Hoeganaes Corporation Perfectionnements apportés à des procédés de compactage

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2509081A1 (fr) * 2011-04-07 2012-10-10 Höganäs AB Nouvelle composition et procédé

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2064773A (en) * 1933-06-01 1936-12-15 Ferrocart Corp Of America Method for making magnetic cores
WO1997030810A1 (fr) * 1996-02-23 1997-08-28 Höganäs Ab Poudre de fer enrobee de phosphate et son procede de fabrication

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2064773A (en) * 1933-06-01 1936-12-15 Ferrocart Corp Of America Method for making magnetic cores
WO1997030810A1 (fr) * 1996-02-23 1997-08-28 Höganäs Ab Poudre de fer enrobee de phosphate et son procede de fabrication

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
DATABASE COMPENDEX [online] ENGINEERING INFORMATION, INC., NEW YORK, NY, US; March 2006 (2006-03-01), NAKAYAMA R ET AL: "Magnetic properties of lower core loss soft magnetic composites made from heat resistance MgO insulation coated iron powders", XP002507415, Database accession no. E2006259945853 *
FUNTAI OYOBI FUMMATSU YAKIN/JOURNAL OF THE JAPAN SOCIETY OF POWDER AND POWDER METALLURGY MARCH 2006 FUNTAI FUNAMTSU YAKIN KYOKAI/JAPAN SOC. OF POWDER METALLURGY JP, vol. 53, no. 3, March 2006 (2006-03-01), pages 285 - 289 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011140417A1 (fr) * 2010-05-07 2011-11-10 Hoeganaes Corporation Perfectionnements apportés à des procédés de compactage
CN102917819A (zh) * 2010-05-07 2013-02-06 赫格纳斯公司 改进的压实方法
US8574489B2 (en) 2010-05-07 2013-11-05 Hoeganaes Corporation Compaction methods
CN102917819B (zh) * 2010-05-07 2015-04-01 赫格纳斯公司 改进的压实方法

Also Published As

Publication number Publication date
TW201007782A (en) 2010-02-16

Similar Documents

Publication Publication Date Title
Sunday et al. Magnetic and microstructural properties of Fe3O4-coated Fe powder soft magnetic composites
EP2147445A2 (fr) Poudre de materiau magnetique doux
JP2006225766A (ja) 磁性鉄粉末の熱処理
KR101926100B1 (ko) 연자성 분말
KR20120075425A (ko) 압분 자심용 철계 연자성 분말 및 그의 제조방법 및 압분 자심
KR101188135B1 (ko) Ａｃ 애플리케이션용 고성능 자기 복합재 및 그 제조 공정
KR101639960B1 (ko) 압분자심용 철분 및 압분자심의 제조 방법
JP5138227B2 (ja) 粉末組成物、軟磁性構成部材及び軟磁性複合体構成部材の製造方法
CN1326648C (zh) 制备高密度软磁产品的方法
De Wulf et al. Magnetic properties and loss separation in iron powder soft magnetic composite materials
WO2009136854A1 (fr) Procédé d'amélioration des propriétés magnétiques d'un composant composite magnétique doux compacté et traité à chaud
JP6853824B2 (ja) 鉄基粉末組成物
JP2005079511A (ja) 軟磁性材料およびその製造方法
Lemieux et al. Optimizing soft magnetic composites for power frequency applications and power-trains
WO2002058865A1 (fr) Alliages pulverulents a base de fer magnetique doux comprimes et traites thermiquement
Grande et al. New lines of investigation on the effects of processing conditions on soft magnetic composite materials behaviour for electromagnetic applications
Lefebvre et al. Consolidation of a lubricated ferromagnetic powder mix for AC soft magnetic applications
KR101269687B1 (ko) 연자성 분말 제조방법
EP1556871B1 (fr) Traitement thermique de composants magnetiques doux
Sato et al. Influence of Heat Treatment Temperature on Core Loss of Iron Soft Magnetic Composite Cores, for Low Frequency Applications
Hojo et al. PM Functional Materials-Magnetic Materials: Influence of Particle and Crystal Grain Size on Core Loss of Iron Soft Magnetic Composite Cores
Borba et al. Analysis of Electrical Resistivity of Iron-Resign Composite Materials from Powder Metallurgy
WO2005035171A1 (fr) Procede de production d'un composant de composite magnetique doux possedant une resistivite elevee
Maeda et al. Improvement of super low core-loss soft magnetic materials
KR20070112521A (ko) 연자성 분말 제조방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09742936

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09742936

Country of ref document: EP

Kind code of ref document: A1