WO2009104385A1 - チエタン化合物、これを含む重合性組成物、樹脂およびその製造方法ならびに使用 - Google Patents

チエタン化合物、これを含む重合性組成物、樹脂およびその製造方法ならびに使用 Download PDF

Info

Publication number
WO2009104385A1
WO2009104385A1 PCT/JP2009/000656 JP2009000656W WO2009104385A1 WO 2009104385 A1 WO2009104385 A1 WO 2009104385A1 JP 2009000656 W JP2009000656 W JP 2009000656W WO 2009104385 A1 WO2009104385 A1 WO 2009104385A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
bis
compound
general formula
polymerizable composition
Prior art date
Application number
PCT/JP2009/000656
Other languages
English (en)
French (fr)
Inventor
窪井浩徳
林秀俊
高後修
小林誠一
Original Assignee
三井化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三井化学株式会社 filed Critical 三井化学株式会社
Priority to US12/864,703 priority Critical patent/US8362280B2/en
Priority to CN200980103037.4A priority patent/CN101925592B/zh
Priority to KR1020107017488A priority patent/KR101281421B1/ko
Priority to JP2009554214A priority patent/JP5190471B2/ja
Priority to EP09712621.3A priority patent/EP2253626B1/en
Publication of WO2009104385A1 publication Critical patent/WO2009104385A1/ja

Abstract

　下記式（３０）で示される、チエタン化合物。 　式（３０）中、Ａは、ＯＨ基あるいは、ＳＨ基を示す。

Description

チエタン化合物、これを含む重合性組成物、樹脂およびその製造方法ならびに使用
　本発明は、チエタン化合物、これを含む重合性組成物、樹脂およびその製造方法ならびに使用に関する。
　近年、無機ガラスに代わる透明性材料として、透明性有機高分子材料が使用されている。こうした材料をたとえば光学用樹脂に用いる場合、一般に、たとえば透明性、熱的特性、機械的特性などの一般的に求められる特性を有しつつ、かつ高屈折率とすることが求められる。
　このような樹脂に関する技術として、特許文献１に記載のものがある。同文献には、金属含有チエタン化合物が記載されている。また、屈折率（ｎｄ）１．７を超える高屈折率の光学用樹脂が記載されている。
国際公開第２００５／０９５４９０号パンフレット 特開２００３－３２７５８３号公報
　上述した透明性材料において、屈折率を高める等の光学特性の向上に加えて、光学特性と機械強度等の他の樹脂物性とのバランスを向上させる点で、改善の余地があった。
　本発明は、新規なチエタン化合物を提供する。
　本発明は、以下の通りである。
［１］下記式（３０）で示される、チエタン化合物。
Figure JPOXMLDOC01-appb-C000001
　式（３０）中、Ａは、ＯＨ基あるいは、ＳＨ基を示す。
［２］［１］に記載のチエタン化合物を含む、重合性組成物。
［３］［２］に記載の重合性組成物において、イソシアネート化合物、前記式（３０）に示した化合物以外の活性水素化合物、エポキシ化合物、エピチオ化合物、前記式（３０）に示した化合物以外の非金属チエタン化合物および金属チエタン化合物からなる群から選択される一種以上をさらに含む、重合性組成物。
［４］［１］に記載のチエタン化合物と、下記一般式（２）に示される金属チエタン化合物とを含む、重合性組成物。
Figure JPOXMLDOC01-appb-C000002
（上記一般式（２）中、Ｍは金属原子である。Ｘ1およびＸ2は各々独立に硫黄原子または酸素原子である。Ｒ1は２価の有機基である。
　ｍは０または１以上の整数である。
　ｎはＭの価数であり、ｐは１以上ｎ以下の整数である。
　ｑは０または１以上ｎ－２以下の整数である。
　Ｙは１価または２価の基であり、Ｔは無機または有機基である。
　ｒは１または２である。
　ｒ＝１のとき、ｑ＝０であり、Ｙは１価の無機または有機基である。ｒ＝１かつｎ－ｐ－ｑが２以上の場合、複数のＹは、各々独立に１価の無機または有機基である。ｒ＝１かつｎ－ｐ－ｑが２以上の場合、複数のＹが互いに結合し、金属原子を含む環を形成していてもよい。
　ｒ＝２のとき、ｎ－ｐ－ｑ＝１または２であり、Ｙは２価の基である。ｒ＝２かつｎ－ｐ－ｑ＝２の場合、２つのＹが、２つの金属原子とともに環を形成していてもよい。ｒ＝２かつｑ＝２の場合、複数のＴは、各々独立に無機または有機基である。）
［５］［４］に記載の重合性組成物において、前記一般式（２）においてＭがＳｂまたはＳｎである化合物を含む、重合性組成物。
［６］［４］または［５］に記載の重合性組成物において、前記一般式（２）に示した化合物として、下記一般式（３）に示される化合物を含む、重合性組成物。
Figure JPOXMLDOC01-appb-C000003
［７］［４］乃至［６］いずれかに記載の重合性組成物において、前記一般式（２）においてｍ＝０である化合物を含む、重合性組成物。
［８］［４］乃至［７］いずれかに記載の重合性組成物において、前記一般式（２）においてＸ1が硫黄原子である化合物を含む、重合性組成物。
［９］［４］乃至［８］いずれかに記載の重合性組成物において、前記一般式（２）においてｎ＝ｐ＝３である化合物を含む、重合性組成物。
［１０］［４］乃至［９］いずれかに記載の重合性組成物において、前記一般式（２）に示した化合物として、下記式（４）に示される化合物を含む、重合性組成物。
Figure JPOXMLDOC01-appb-C000004
［１１］［４］または［５］に記載の重合性組成物において、前記一般式（２）においてｎ＝ｐ＝４である化合物を含む、重合性組成物。
［１２］［１１］に記載の重合性組成物において、前記一般式（２）に示した化合物として、下記式（５）に示される化合物を含む、重合性組成物。
Figure JPOXMLDOC01-appb-C000005
［１３］［２］乃至［１２］いずれかに記載の重合性組成物において、ブルーイング剤をさらに含む、重合成組成物。
［１４］［２］乃至［１３］いずれかに記載の重合性組成物を注型重合する工程を含む、樹脂の製造方法。
［１５］［２］乃至［１３］いずれかに記載の重合性組成物を重合して得られる樹脂。
［１６］［１５］に記載の樹脂からなる光学部品。
［１７］［２］乃至［１３］いずれかに記載の重合性組成物の光学部品としての使用。
［１８］［２］乃至［１３］いずれかに記載の重合性組成物を重合させた樹脂の光学部品としての使用。
　本発明によれば、新規なチエタン化合物が提供される。
　以下、本発明について、具体例を用いて説明するが、本発明は、これに限定されるものではない。また、本発明において、各成分または基について、例示されたものを単独で用いてもよいし、複数組み合わせて用いてもよい。
　本発明におけるチエタン化合物は、下記式（３０）に示される非金属チエタン化合物である。
Figure JPOXMLDOC01-appb-C000006
　式（３０）中、ＡはＯＨ基あるいは、ＳＨ基を示す。
　すなわち、式（３０）で示される非金属チエタン化合物は、下記の式（３１）で示される非金属チエタン化合物（１，３－ビス（チエタニルチオ）－２プロパノール）、あるいは、下記の式（３２）で示される非金属チエタン化合物（１，３－ビス（チエタニルチオ）－２メルカプトプロパン）である。
Figure JPOXMLDOC01-appb-C000007
Figure JPOXMLDOC01-appb-C000008
　上記一般式（３１）に示した化合物の製造方法に特に制限はないが、たとえば実施例の項で後述するように、３－メルカプトチエタンとエピクロロヒドリンとをアルカリ性の水溶液中で反応させて得ることができる。
　上記一般式（３１）に示した化合物は、分子構造中に２つのチエタニルチオ基を含むとともに水酸基を含む。このため、重合性組成物中に配合することにより、たとえば高屈折率、機械強度、耐熱性のバランスを向上させることが可能となる。
　上記一般式（３２）に示した化合物の製造方法に特に制限はないが、たとえば実施例の項で後述するように、３－メルカプトチエタンと、エピチオクロロヒドリンとをアルカリ性の溶液中で反応させることで得られる。
　上記一般式（３２）に示した化合物は、分子構造中に２つのチエタニルチオ基を含むとともにメルカプト基を含む。このため、重合性組成物中に配合することにより、たとえば高屈折率、機械強度、耐熱性のバランスを向上させることが可能となる。
　以下、上記一般式（３０）に示した化合物を含む重合性組成物を説明する。
　本発明における重合性組成物は、上記一般式（３０）に示した化合物を含んでいればよい。
　重合性組成物中の上記一般式（３０）に示した化合物の配合量に特に制限はない。たとえば光学樹脂組成物の機械的強度をさらに向上させる観点からは、重合性組成物全体中に１重量％以上としてもよい。
　本発明における重合性組成物は、上記式（３１）に示した化合物、上記式（３２）に示した化合物のうち、いずれか一方を含めばよいが、上記式（３１）に示した化合物、上記式（３２）に示した化合物の両方を含むものであってもよい。
　本発明における重合性組成物に含まれる他の成分として、たとえば、イソシアネート化合物、上記式（３０）に示した化合物以外の活性水素化合物、エポキシ化合物、エピチオ化合物、上記式（３０）に示した化合物以外の非金属チエタン化合物および金属チエタン化合物からなる群から選択される一種以上をさらに含んでもよい。
　以下、各成分について、具体例を挙げて説明する。
　なお、本発明における重合性組成物の成分が複数の官能基を有するときの官能基の優先順位は、以下の通りとする。
（ｉ）チオール基
（ｉｉ）イソシアネート基
（ｉｉｉ）エポキシ基
（ｉｖ）エピチオ（エピスルフィド）基
（ｖ）チエタニル基
　たとえば、以下において、チオール基とチエタニル基とを有する化合物については、チオール化合物の項で説明する。
　（活性水素化合物）
　本発明において用いられる活性水素化合物は、活性水素を有する化合物であって、上記式（３０）に示した化合物以外の化合物である。活性水素化合物は、具体的には、ポリオール化合物、（ポリ）チオール化合物およびヒドロキシチオール化合物より選ばれる。
　このうち、ポリオール化合物としては、たとえばエチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、ブチレングリコール、ネオペンチルグリコール、グリセリン、トリメチロールエタン、トリメチロールプロパン、ブタントリオール、 １，２－メチルグルコサイド、ペンタエリスリトール、ジペンタエリスリトール、トリペンタエリスリトール、ソルビトール、エリスリトール、スレイトール、リビトール、アラビニトール、キシリトール、アリトール、マニトール、ドルシトール、イディトール、グリコール、イノシトール、ヘキサントリオール、トリグリセロース、ジグリペロール、トリエチレングリコール、ポリエチレングリコール、トリス（２－ヒドロキシエチル）イソシアヌレート、シクロブタンジオール、シクロペンタンジオール、シクロヘキサンジオール、シクロヘプタンジオール、シクロオクタンジオール、シクロヘキサンジメタノール、ヒドロキシプロピルシクロヘキサノール、トリシクロ［５．２．１．０2,6］デカン－ジメタノール、ビシクロ［４，３，０］－ノナンジオール、ジシクロヘキサンジオール、トリシクロ［５，３，１，１］ドデカンジオール、ビシクロ［４，３，０］ノナンジメタノール、トリシクロ［５，３，１，１］ドデカン－ジエタノール、ヒドロキシプロピルトリシクロ［５，３，１，１］ドデカノール、スピロ［３，４］オクタンジオール、ブチルシクロヘキサンジオール、１，１'－ビシクロヘキシリデンジオール、シクロヘキサントリオール、マルチトール、ラクトース等の脂肪族ポリオール；
ジヒドロキシナフタレン、トリヒドロキシナフタレン、テトラヒドロキシナフタレン、ジヒドロキシベンゼン、ベンゼントリオール、ビフェニルテトラオール、ピロガロール、（ヒドロキシナフチル）ピロガロール、トリヒドロキシフェナントレン、ビスフェノールＡ、ビスフェノールＦ、キシリレングリコール、ジ（２－ヒドロキシエトキシ）ベンゼン、ビスフェノールＡ－ビス－（２－ヒドロキシエチルエーテル）、テトラブロムビスフェノールＡ、テトラブロムビスフェノールＡ－ビス－（２－ヒドロキシエチルエーテル）等の芳香族ポリオール；
ジブロモネオペンチルグリコール等のハロゲン化ポリオール；
エポキシ樹脂等の高分子ポリオールが挙げられる。
　また、ポリオール化合物として他に、シュウ酸、グルタミン酸、アジピン酸、酢酸、プロピオン酸、シクロヘキサンカルボン酸、β－オキソシクロヘキサンプロピオン酸、ダイマー酸、フタル酸、イソフタル酸、サリチル酸、３－ブロモプロピオン酸、２－ブロモグリコール、ジカルボキシシクロヘキサン、ピロメリット酸、ブタンテトラカルボン酸、ブロモフタル酸などの有機酸と上記ポリオールとの縮合反応生成物；
上記ポリオールとエチレンオキサイドやプロピレンオキサイドなどアルキレンオキサイドとの付加反応生成物；
アルキレンポリアミンとエチレンオキサイドや、プロピレンオキサイドなどアルキレンオキサイドとの付加反応生成物；さらには、
ビス－［４－（ヒドロキシエトキシ）フェニル］スルフィド、ビス－［４－（２－ヒドロキシプロポキシ）フェニル］スルフィド、ビス－［４－（ ２，３－ジヒドロキシプロポキシ）フェニル］スルフィド、ビス－［４－（４－ヒドロキシシクロヘキシロキシ）フェニル］スルフィド、ビス－［２－メチル－４－（ヒドロキシエトキシ）－６－ブチルフェニル］スルフィドおよびこれらの化合物に水酸基当たり平均３分子以下のエチレンオキシドおよび／またはプロピレンオキシドが付加された化合物；
ジ－（２－ヒドロキシエチル）スルフィド、１，２－ビス－（２－ヒドロキシエチルメルカプト）エタン、ビス（２－ヒドロキシエチル）ジスルフィド、１，４－ジチアン－２，５－ジオール、ビス（２，３－ジヒドロキシプロピル）スルフィド、テトラキス（４－ヒドロキシ－２－チアブチル）メタン、ビス（４－ヒドロキシフェニル）スルホン（商品名ビスフェノールＳ）、テトラブロモビスフェノールＳ、テトラメチルビスフェノールＳ、４，４'－チオビス（６－ｔｅｒｔ－ブチル－３－メチルフェノール）、１，３－ビス（２－ヒドロキシエチルチオエチル）－シクロヘキサンなどの硫黄原子を含有したポリオール等が挙げられる。
　チオール化合物として、具体的には、１価のチオール化合物としては、メチルメルカプタン、エチルメルカプタン、プロピルメルカプタン、ブチルメルカプタン、オクチルメルカプタン、ドデシルメルカプタン、ｔｅｒｔ－ドデシルメルカプタン、ヘキサデシルメルカプタン、オクタデシルメルカプタン、シクロヘキシルメルカプタン、ベンジルメルカプタン、エチルフェニルメルカプタン、２－メルカプトメチル－１，３－ジチオラン、２－メルカプトメチル－１，４－ジチアン、１－メルカプト－２，３－エピチオプロパン、１－メルカプトメチルチオ－２，３－エピチオプロパン、１－メルカプトエチルチオ－２，３－エピチオプロパン、３－メルカプトチエタン、２－メルカプトチエタン、３－メルカプトメチルチオチエタン、２－メルカプトメチルチオチエタン、３－メルカプトエチルチオチエタン、２－メルカプトエチルチオチエタン等の脂肪族メルカプタン化合物、チオフェノール、メルカプトトルエン等の芳香族メルカプタン化合物、ならびに２－メルカプトエタノール、３－メルカプト－１，２－プロパンジオール等のメルカプト基以外にヒドロキシ基を含有する化合物が挙げられる。
　また、ポリチオール化合物としては、たとえば、メタンジチオール、１，２－エタンジチオール、１，１－プロパンジチオール、１，２－プロパンジチオール、１，３－プロパンジチオール、２，２－プロパンジチオール、１，６－ヘキサンジチオール、１，２，３－プロパントリチオール、１，１－シクロヘキサンジチオール、１，２－シクロヘキサンジチオール、２，２－ジメチルプロパン－１，３－ジチオール、３，４－ジメトキシブタン－１，２－ジチオール、２－メチルシクロヘキサン－２，３－ジチオール、ビシクロ［２，２，１］ペプタ－ｅｘｏ－ｃｉｓ－２，３－ジチオール、１，１－ビス（メルカプトメチル）シクロヘキサン、チオリンゴ酸ビス（２－メルカプトエチルエステル）、２，３－ジメルカプトコハク酸（２－メルカプトエチルエステル）、２，３－ジメルカプト－１－プロパノール（２－メルカプトアセテート）、２，３－ジメルカプト－１－プロパノール（３－メルカプトアセテート）、ジエチレングリコールビス（２－メルカプトアセテート）、ジエチレングリコールビス（３－メルカプトプロピオネート）、１，２－ジメルカプトプロピルメチルエーテル、２，３－ジメルカプトプロピルメチルエーテル、２，２－ビス（メルカプトメチル）－１，３－プロパンジチオール、ビス（２－メルカプトエチル）エーテル、エチレングリコールビス（２－メルカプトアセテート）、エチレングリコールビス（３－メルカプトプロピオネート）、トリメチロールプロパントリス（２－メルカプトアセテート）、トリメチロールプロパントリス（３－メルカプトプロピオネート）、ペンタエリスリトールテトラキス（２－メルカプトアセテート）、ペンタエリスリトールテトラキス（３－メルカプトプロピオネート）、１，２－ビス（２－メルカプトエチルチオ）－３－メルカプトプロパン）、５，７－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、４，７－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、４，８－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、１，１，３，３－テトラキス（メルカプトメチルチオ）プロパン、４，６－ビス（メルカプトメチルチオ）－１，３－ジチアン、２－（２，２－ビス（メルカプトメチルチオ）エチル）－１，３－ジチエタン等の脂肪族ポリチオール；
１，２－ジメルカプトベンゼン、１，３－ジメルカプトベンゼン、１，４－ジメルカプトベンゼン、１，２－ビス（メルカプトメチル）ベンゼン、１，３－ビス（メルカプトメチル）ベンゼン、１，４－ビス（メルカプトメチル）ベンゼン、１，２－ビス（メルカプトエチル）ベンゼン、１，３－ビス（メルカプトエチル）ベンゼン、１，４－ビス（メルカプトエチル）ベンゼン、１，２－ビス（メルカプトメチレンオキシ）ベンゼン、１，３－ビス（メルカプトメチレンオキシ）ベンゼン、１，４－ビス（メルカプトメチレンオキシ）ベンゼン、１，２－ビス（メルカプトエチレンオキシ）ベンゼン、１，３－ビス（メルカプトエチレンオキシ）ベンゼン、１，４－ビス（メルカプトエチレンオキシ）ベンゼン、１，２，３－トリメルカプトベンゼン、１，２，４－トリメルカプトベンゼン、１，３，５－トリメルカプトベンゼン、１，２，３－トリス（メルカプトメチル）ベンゼン、１，２，４－トリス（メルカプトメチル）ベンゼン、１，３，５－トリス（メルカプトメチル）ベンゼン、１，２，３－トリス（メルカプトエチル）ベンゼン、１，２，４－トリス（メルカプトエチル）ベンゼン、１，３，５－トリス（メルカプトエチル）ベンゼン、１，２，３－トリス（メルカプトメチレンオキシ）ベンゼン、１，２，４－トリス（メルカプトメチレンオキシ）ベンゼン、１，３，５－トリス（メルカプトメチレンオキシ）ベンゼン、１，２，３－トリス（メルカプトエチレンオキシ）ベンゼン、１，２，４－トリス（メルカプトエチレンオキシ）ベンゼン、１，３，５－トリス（メルカプトエチレンオキシ）ベンゼン、１，２，３，４－テトラメルカプトベンゼン、１，２，３，５－テトラメルカプトベンゼン、１，２，４，５－テトラメルカプトベンゼン、１，２，３，４－テトラキス（メルカプトメチル）ベンゼン、１，２，３，５－テトラキス（メルカプトメチル）ベンゼン、１，２，４，５－テトラキス（メルカプトメチル）ベンゼン、１，２，３，４－テトラキス（メルカプトエチル）ベンゼン、１，２，３，５－テトラキス（メルカプトエチル）ベンゼン、１，２，４，５－テトラキス（メルカプトエチル）ベンゼン、１，２，３，４－テトラキス（メルカプトエチル）ベンゼン、１，２，３，５－テトラキス（メルカプトメチレンオキシ）ベンゼン、１，２，４，５－テトラキス（メルカプトメチレンオキシ）ベンゼン、１，２，３，４－テトラキス（メルカプトエチレンオキシ）ベンゼン、１，２，３，５－テトラキス（メルカプトエチレンオキシ）ベンゼン、１，２，４，５－テトラキス（メルカプトエチレンオキシ）ベンゼン、２，２'－ジメルカプトビフェニル、４，４'－ジメルカプトビフェニル、４，４'－ジメルカプトビベンジル、２，５－トルエンジチオール、３，４－トルエンジチオール、１，４－ナフタレンジチオール、１，５－ナフタレンジチオール、２，６－ナフタレンジチオール、２，７－ナフタレンジチオール、２，４－ジメチルベンゼン－１，３－ジチオール、４，５－ジメチルベンゼン－１，３－ジチオール、９，１０－アントラセンジメタンチオール、１，３－ジ（ｐ－メトキシフェニル）プロパン－２，２－ジチオール、１，３－ジフェニルプロパン－２，２－ジチオール、フェニルメタン－１，１－ジチオール、２，４－ジ（ｐ－メルカプトフェニル）ペンタン等の芳香族ポリチオール；
２，５－ジクロロベンゼン－１，３－ジチオール、１，３－ジ（ｐ－クロロフェニル）プロパン－２，２－ジチオール、３，４，５－トリブロム－１，２－ジメルカプトベンゼン、２，３，４，６－テトラクロル－１，５－ビス（メルカプトメチル）ベンゼン等の塩素置換体、臭素置換体等のハロゲン置換芳香族ポリチオール；
２－メチルアミノ－４，６－ジチオール－ｓｙｍ－トリアジン、２－エチルアミノ－４，６－ジチオール－ｓｙｍ－トリアジン、２－アミノ－４，６－ジチオール－ｓｙｍ－トリアジン、２－モルホリノ－４，６－ジチオール－ｓｙｍ－トリアジン、２－シクロヘキシルアミノ－４，６－ジチオール－ｓｙｍ－トリアジン、２－メトキシ－４，６－ジチオール－ｓｙｍ－トリアジン、２－フェノキシ－４，６－ジチオール－ｓｙｍ－トリアジン、２－チオベンゼンオキシ－４，６－ジチオール－ｓｙｍ－トリアジン、２－チオブチルオキシ－４，６－ジチオール－ｓｙｍ－トリアジン等の複素環を含有したポリチオール；
１，２－ビス（メルカプトメチルチオ）ベンゼン、１，３－ビス（メルカプトメチルチオ）ベンゼン、１，４－ビス（メルカプトメチルチオ）ベンゼン、１，２－ビス（メルカプトエチルチオ）ベンゼン、１，３－ビス（メルカプトエチルチオ）ベンゼン、１，４－ビス（メルカプトエチルチオ）ベンゼン、１，２，３－トリス（メルカプトメチルチオ）ベンゼン、１，２，４－トリス（メルカプトメチルチオ）ベンゼン、１，３，５－トリス（メルカプトメチルチオ）ベンゼン、１，２，３－トリス（メルカプトエチルチオ）ベンゼン、１，２，４－トリス（メルカプトエチルチオ）ベンゼン、１，３，５－トリス（メルカプトエチルチオ）ベンゼン、１，２，３，４－テトラキス（メルカプトメチルチオ）ベンゼン、１，２，３，５－テトラキス（メルカプトメチルチオ）ベンゼン、１，２，４，５－テトラキス（メルカプトメチルチオ）ベンゼン、１，２，３，４－テトラキス（メルカプトエチルチオ）ベンゼン、１，２，３，５－テトラキス（メルカプトエチルチオ）ベンゼン、１，２，４，５－テトラキス（メルカプトエチルチオ）ベンゼン等及びこれらの核アルキル化物等のメルカプト基以外に硫黄原子を含有する芳香族ポリチオール；
ビス（メルカプトメチル）スルフィド、ビス（メルカプトエチル）スルフィド、ビス（メルカプトプロピル）スルフィド、ビス（メルカプトメチルチオ）メタン、ビス（２－メルカプトエチルチオ）メタン、ビス（３－メルカプトプロピル）メタン、１，２－ビス（メルカプトメチルチオ）エタン、１，２－（２－メルカプトエチルチオ）エタン、１，２－（３－メルカプトプロピル）エタン、１，３－ビス（メルカプトメチルチオ）プロパン、１，３－ビス（２－メルカプトエチルチオ）プロパン、１，３－ビス（３－メルカプトプロピルチオ）プロパン、１，２，３－トリス（メルカプトメチルチオ）プロパン、１，２，３－トリス（２－メルカプトエチルチオ）プロパン、１，２，３－トリス（３－メルカプトプロピルチオ）プロパン、テトラキス（メルカプトメチルチオメチル）メタン、テトラキス（２－メルカプトエチルチオメチル）メタン、テトラキス（３－メルカプトプロピルチオメチル）メタン、ビス（２，３－ジメルカプトプロピル）スルフィド、２，５－ジメルカプト－１，４－ジチアン、ビス（メルカプトメチル）ジスルフィド、ビス（メルカプトエチル）ジスルフィド、ビス（メルカプトプロピル）ジスルフィド、１，５－ジメルカプト-３－チアペンタン等、及びこれらのチオグリコール酸及びメルカプトプロピオン酸のエステル；
ヒドロキシメチルスルフィドビス（２－メルカプトアセテート）、ヒドロキシメチルスルフィドビス（３－メルカプトプロピオネート）、ヒドロキシエチルスルフィドビス（２－メルカプトアセテート）、ヒドロキシエチルスルフィドビス（３－メルカプトプロピオネート）、ヒドロキシプロピルスルフィドビス（２－メルカプトアセテート）、ヒドロキシプロピルスルフィドビス（３－メルカプトプロピオネート）、ヒドロキシメチルジスルフィドビス（２－メルカプトアセテート）、ヒドロキシメチルジスルフィドビス（３－メルカプトプロピオネート）、ヒドロキシエチルジスルフィドビス（２－メルカプトアセテート）、ヒドロキシエチルジスルフィドビス（３－メルカプトプロピオネート）、ヒドロキシプロピルジスルフィドビス（２－メルカプトアセテート）、ヒドロキシプロピルジスルフィドビス（３－メルカプトプロピオネート）、２－メルカプトエチルエーテルビス（２－メルカプトアセテート）、２－メルカプトエチルエーテルビス（３－メルカプトプロピオネート）、１，４－ジチアン－２，５－ジオールビス（２－メルカプトアセテート）、１，４－ジチアン－２，５－ジオールビス（３－メルカプトプロピオネート）、チオグリコール酸ビス（２－メルカプトエチルエステル）、チオジプロピオン酸ビス（２－メルカプトエチルエステル）、４，４－チオジブチル酸ビス（２－メルカプトエチルエステル）、ジチオジグリコール酸ビス（２－メルカプトエチルエステル）、ジチオジプロピオン酸ビス（２－メルカプトエチルエステル）、４，４－ジチオジブチル酸ビス（２－メルカプトエチルエステル）、チオジグリコール酸ビス（２，３－ジメルカプトプロピルエステル）、チオジプロピオン酸ビス（２，３－ジメルカプトプロピルエステル）、ジチオグリコール酸ビス（２，３－ジメルカプトプロピルエステル）、ジチオジプロピオン酸（２，３－ジメルカプトプロピルエステル）等のメルカプト基以外に硫黄原子を含有する脂肪族ポリチオール；
３，４－チオフェンジチオール、２，５－ジメルカプト－１，３，４－チアジアゾール等のメルカプト基以外に硫黄原子を含有する複素環化合物等が挙げられる。
　また、ヒドロキシチオール化合物としては、たとえば、２－メルカプトエタノール、３－メルカプト－１，２－プロパンジオール、グルセリンジ（メルカプトアセテート）、１－ヒドロキシ－４－メルカプトシクロヘキサン、２，４－ジメルカプトフェノール、２－メルカプトハイドロキノン、４－メルカプトフェノール、３，４－ジメルカプト－２－プロパノール、１，３－ジメルカプト－２－プロパノール、２，３－ジメルカプト－１－プロパノール、１，２－ジメルカプト－１，３－ブタンジオール、ペンタエリスリトールトリス（３－メルカプトプロピオネート）、ペンタエリスリトールモノ（３－メルカプトプロピオネート）、ペンタエリスリトールビス（３－メルカプトプロピオネート）、ペンタエリスリトールトリス（チオグリコレート）、ペンタエリスリトールペンタキス（３－メルカプトプロピオネート）、ヒドロキシメチル－トリス（メルカプトエチルチオメチル）メタン、１－ヒドロキシエチルチオ－３－メルカプトエチルチオベンゼン、４－ヒドロキシ－４'－メルカプトジフェニルスルホン、２－（２－メルカプトエチルチオ）エタノール、ジヒドロキシエチルスルフィドモノ（３－メルカプトプロピオネート）、ジメルカプトエタンモノ（サルチレート）、ヒドロキシエチルチオメチル－トリス（メルカプトエチルチオ）メタン等が挙げられる。
　さらには、これらの活性水素化合物の塩素置換体、臭素置換体のハロゲン置換体を使用してもよい。これらはそれぞれ単独で用いることも２種類以上を混合して用いることもできる。
　（イソシアネート化合物）
　本発明において使用されるイソシアネート化合物は、分子内に１つ以上のイソシアネート基（ＮＣＯ基）を含有する化合物である。イソシアネート化合物を加えることにより機械物性等がさらに改良される場合がある。
　ここで用いられるイソシアネート化合物は、特に限定されないが、複数のイソシアナト基を有するポリイソシアネート化合物が好ましく、さらに好ましくはジイソシアネート化合物である。具体的にはヘキサメチレンジイソシアネート、ビス（イソシアナトメチル）シクロヘキサン、キシレンジイソシアネート、ジシクロヘキシルメタンジイソシアネート、トルエンジイソシアネート、２，５－ビス（イソシアナトメチル）ビシクロ－［２，２，１］－へプタン、２，６－ビス（イソシアナトメチル）ビシクロ－［２，２，１］－へプタン、イソホロンジイソシアネート等が好適な例として挙げられる。
　本発明のイソシアネート化合物の使用量としては、樹脂組成物中の成分および各成分の使用量により異なるが、得られる樹脂の屈折率を考慮すれば、本発明の重合性組成物全体に対して、２５重量％以下含有すると好ましい。２３重量％以下であればより好ましく、２０重量％以下であればさらに好ましい。得られる樹脂の色相および機械強度を考慮すれば、２．５重量％以上であることが好ましい。
　（エポキシ化合物およびエピチオ化合物）
　エポキシ化合物およびエピチオ化合物は、それぞれ、分子内に１つ以上のエポキシ基およびエピチオ基を含有する。また、好ましくはエポキシ基および／またはエピチオ基を合計２つ以上含有する化合物である。
（エポキシ化合物）
　このうち、エポキシ化合物として、具体的には、ビスフェノールＡ、ビスフェノールＦ等の多価フェノール化合物と、エピハロヒドリン化合物との縮合反応により得られるフェノール系エポキシ化合物（たとえば、ビスフェノールＡグリシジルエーテル、ビスフェノールＦグリシジルエーテル）；
水添ビスフェノールＡ、水添ビスフェノールＦ、シクロヘキサンジメタノール等の多価アルコール化合物と、エピハロヒドリン化合物との縮合により得られるアルコール系エポキシ化合物（たとえば、水添ビスフェノールＡグリシジルエーテル、水添ビスフェノールＦグリシジルエーテル）、およびエチレングリコールジグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、１，４－シクロヘキサンジメタノールジグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル等のその他のアルコール系エポキシ化合物；
３，４－エポキシシクロヘキシルメチル－３'，４'－エポキシシクロヘキサンカルボキシレートや１，２－ヘキサヒドロフタル酸ジグリシジルエステル等のグリシジルエステル系エポキシ化合物；および
一級および二級アミン化合物とエピハロヒドリン化合物との縮合により得られるアミン系エポキシ化合物（たとえば、イソシアヌル酸トリグリシジルエーテル）等が挙げられる。また、その他、４－ビニル－１－シクロヘキサンジエポキシドなどのビニルシクロヘキセンジエポキシド等の脂肪族多価エポキシ化合物等を挙げることができる。
　スルフィド基含有エポキシ化合物とエーテル基含有エポキシ化合物の具体的化合物例としては、ビス（２，３－エポキシプロピル）スルフィド、ビス（２，３－エポキシプロピル）ジスルフィド、ビス（２，３－エポキシプロピルチオ）メタン、１，２－ビス（２，３－エポキシプロピルチオ）エタン、１，２－ビス（２，３－エポキシプロピルチオ）プロパン、１，３－ビス（２，３－エポキシプロピルチオ）プロパン、１，３－ビス（２，３－エポキシプロピルチオ）－２－メチルプロパン、１，４－ビス（２，３－エポキシプロピルチオ）ブタン、１，４－ビス（２，３－エポキシプロピルチオ）－２－メチルブタン、１，３－ビス（２，３－エポキシプロピルチオ）ブタン、１，５－ビス（２，３－エポキシプロピルチオ）ペンタン、１，５－ビス（２，３－エポキシプロピルチオ）－２－メチルペンタン、１，５－ビス（２，３－エポキシプロピルチオ）－３－チアペンタン、１，６－ビス（２，３－エポキシプロピルチオ）ヘキサン、１，６－ビス（２，３－エポキシプロピルチオ）－２－メチルヘキサン、３，８－ビス（２，３－エポキシプロピルチオ）－３，６－ジチアオクタン、１，２，３－トリス（２，３－エポキシプロピルチオ）プロパン、２，２－ビス（２，３－エポキシプロピルチオ）－１，３－ビス（２，３－エポキシプロピルチオメチル）プロパン、２，２－ビス（２，３－エポキシプロピルチオメチル）－１－（２，３－エポキシプロピルチオ）ブタン、１，５－ビス（２，３－エポキシプロピルチオ）－２－（２，３－エポキシプロピルチオメチル）－３－チアペンタン、１，５－ビス（２，３－エポキシプロピルチオ）－２，４－ビス（２，３－エポキシプロピルチオメチル）－３－チアペンタン、１－（２，３－エポキシプロピルチオ）－２，２－ビス（２，３－エポキシプロピルチオメチル）－４－チアヘキサン、１，５，６－トリス（２，３－エポキシプロピルチオ）－４－（２，３－エポキシプロピルチオメチル）－３－チアヘキサン、１，８－ビス（２，３－エポキシプロピルチオ）－４－（２，３－エポキシプロピルチオメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エポキシプロピルチオ）－４，５－ビス（２，３－エポキシプロピルチオメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エポキシプロピルチオ）－４，４－ビス（２，３－エポキシプロピルチオメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エポキシプロピルチオ）－２，５－ビス（２，３－エポキシプロピルチオメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エポキシプロピルチオ）－２，４，５－トリス（２，３－エポキシプロピルチオメチル）－３，６－ジチアオクタン、１，１，１－トリス［［２－（２，３－エポキシプロピルチオ）エチル］チオメチル］－２－（２，３－エポキシプロピルチオ）エタン、１，１，２，２－テトラキス［［２－（２，３－エポキシプロピルチオ）エチル］チオメチル］エタン、１，１１－ビス（２，３－エポキシプロピルチオ）－４，８－ビス（２，３－エポキシプロピルチオメチル）－３，６，９－トリチアウンデカン、１，１１－ビス（２，３－エポキシプロピルチオ）－４，７－ビス（２，３－エポキシプロピルチオメチル）－３，６，９－トリチアウンデカン、１，１１－ビス（２，３－エポキシプロピルチオ）－５，７－ビス（２，３－エポキシプロピルチオメチル）－３，６，９－トリチアウンデカン、１，５－ビス（グリシジルチオ）－３－チアペンタン等の鎖状脂肪族の２，３－エポキシプロピルチオ化合物；
１，３－ビス（２，３－エポキシプロピルチオ）シクロヘキサン、１，４－ビス（２，３－エポキシプロピルチオ）シクロヘキサン、１，３－ビス（２，３－エポキシプロピルチオメチル）シクロヘキサン、１，４－ビス（２，３－エポキシプロピルチオメチル）シクロヘキサン、２，５－ビス（２，３－エポキシプロピルチオメチル）－１，４－ジチアン、２，５－ビス［［２－（２，３－エポキシプロピルチオ）エチル］チオメチル］－１，４－ジチアン、２，５－ビス（２，３－エポキシプロピルチオメチル）－２，５－ジメチル－１，４－ジチアン、３－（２，３－エポキシプロピルチオ）チエタン等の環状脂肪族の２，３－エポキシプロピルチオ化合物；
１，２－ビス（２，３－エポキシプロピルチオ）ベンゼン、１，３－ビス（２，３－エポキシプロピルチオ）ベンゼン、１，４－ビス（２，３－エポキシプロピルチオ）ベンゼン、１，２－ビス（２，３－エポキシプロピルチオメチル）ベンゼン、１，３－ビス（２，３－エポキシプロピルチオメチル）ベンゼン、１，４－ビス（２，３－エポキシプロピルチオメチル）ベンゼン、ビス［４－（２，３－エポキシプロピルチオ）フェニル］メタン、２，２－ビス［４－（２，３－エポキシプロピルチオ）フェニル］プロパン、ビス［４－（２，３－エポキシプロピルチオ）フェニル］スルフィド、ビス［４－（２，３－エポキシプロピルチオ）フェニル］スルホン、４，４'－ビス（２，３－エポキシプロピルチオ）ビフェニル等の芳香族の２，３－エポキシプロピルチオ化合物；
エチレンオキシド、プロピレンオキシド、グリシドール、エピクロルヒドリン等の単官能エポキシ化合物；
ビス（２，３－エポキシプロピル）エーテル、ビス（２，３－エポキシプロピルオキシ）メタン、１，２－ビス（２，３－エポキシプロピルオキシ）エタン、１，２－ビス（２，３－エポキシプロピルオキシ）プロパン、１，３－ビス（２，３－エポキシプロピルオキシ）プロパン、１，３－ビス（２，３－エポキシプロピルオキシ）－２－メチルプロパン、１，４－ビス（２，３－エポキシプロピルオキシ）ブタン、１，４－ビス（２，３－エポキシプロピルオキシ）－２－メチルブタン、１，３－ビス（２，３－エポキシプロピルオキシ）ブタン、１，５－ビス（２，３－エポキシプロピルオキシ）ペンタン、１，５－ビス（２，３－エポキシプロピルオキシ）－２－メチルペンタン、１，５－ビス（２，３－エポキシプロピルオキシ）－３－チアペンタン、１，６－ビス（２，３－エポキシプロピルオキシ）ヘキサン、１，６－ビス（２，３－エポキシプロピルオキシ）－２－メチルヘキサン、３，８－ビス（２，３－エポキシプロピルオキシ）－３，６－ジチアオクタン、１，２，３－トリス（２，３－エポキシプロピルオキシ）プロパン、２，２－ビス（２，３－エポキシプロピルオキシ）－１，３－ビス（２，３－エポキシプロピルオキシメチル）プロパン、２，２－ビス（２，３－エポキシプロピルオキシメチル）－１－（２，３－エポキシプロピルオキシ）ブタン、１，５－ビス（２，３－エポキシプロピルオキシ）－２－（２，３－エポキシプロピルオキシメチル）－３－チアペンタン、１，５－ビス（２，３－エポキシプロピルオキシ）－２，４－ビス（２，３－エポキシプロピルオキシメチル）－３－チアペンタン、１－（２，３－エポキシプロピルオキシ）－２，２－ビス（２，３－エポキシプロピルオキシメチル）－４－チアヘキサン、１，５，６－トリス（２，３－エポキシプロピルオキシ）－４－（２，３－エポキシプロピルオキシメチル）－３－チアヘキサン、１，８－ビス（２，３－エポキシプロピルオキシ）－４－（２，３－エポキシプロピルオキシメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エポキシプロピルオキシ）－４，５－ビス（２，３－エポキシプロピルオキシメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エポキシプロピルオキシ）－４，４－ビス（２，３－エポキシプロピルオキシメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エポキシプロピルオキシ）－２，５－ビス（２，３－エポキシプロピルオキシメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エポキシプロピルオキシ）－２，４，５－トリス（２，３－エポキシプロピルオキシメチル）－３，６－ジチアオクタン、１，１，１－トリス［［２－（２，３－エポキシプロピルオキシ）エチル］チオメチル］－２－（２，３－エポキシプロピルオキシ）エタン、１，１，２，２－テトラキス［［２－（２，３－エポキシプロピルオキシ）エチル］チオメチル］エタン、１，１１－ビス（２，３－エポキシプロピルオキシ）－４，８－ビス（２，３－エポキシプロピルオキシメチル）－３，６，９－トリチアウンデカン、１，１１－ビス（２，３－エポキシプロピルオキシ）－４，７－ビス（２，３－エポキシプロピルオキシメチル）－３，６，９－トリチアウンデカン、１，１１－ビス（２，３－エポキシプロピルオキシ）－５，７－ビス（２，３－エポキシプロピルオキシメチル）－３，６，９－トリチアウンデカン等の鎖状脂肪族の２，３－エポキシプロピルオキシ化合物；
１，３－ビス（２，３－エポキシプロピルオキシ）シクロヘキサン、１，４－ビス（２，３－エポキシプロピルオキシ）シクロヘキサン、１，３－ビス（２，３－エポキシプロピルオキシメチル）シクロヘキサン、１，４－ビス（２，３－エポキシプロピルオキシメチル）シクロヘキサン、２，５－ビス（２，３－エポキシプロピルオキシメチル）－１，４－ジチアン、２，５－ビス［［２－（２，３－エポキシプロピルオキシ）エチル］チオメチル］－１，４－ジチアン、２，５－ビス（２，３－エポキシプロピルオキシメチル）－２，５－ジメチル－１，４－ジチアン等の環状脂肪族の２，３－エポキシプロピルオキシ化合物；および、
１，２－ビス（２，３－エポキシプロピルオキシ）ベンゼン、１，３－ビス（２，３－エポキシプロピルオキシ）ベンゼン、１，４－ビス（２，３－エポキシプロピルオキシ）ベンゼン、１，２－ビス（２，３－エポキシプロピルオキシメチル）ベンゼン、１，３－ビス（２，３－エポキシプロピルオキシメチル）ベンゼン、１，４－ビス（２，３－エポキシプロピルオキシメチル）ベンゼン、ビス［４－（２，３－エポキシプロピルオキシ）フェニル］メタン、２，２－ビス［４－（２，３－エポキシプロピルオキシ）フェニル］プロパン、ビス［４－（２，３－エポキシプロピルオキシ）フェニル］スルフィド、ビス［４－（２，３－エポキシプロピルオキシ）フェニル］スルホン、４，４'－ビス（２，３－エポキシプロピルオキシ）ビフェニル等の芳香族の２，３－エポキシプロピルオキシ化合物等を挙げることができるが、例示化合物のみに限定されるものではない。
　これら例示したエポキシ化合物のうち、好ましくは、ビス（２，３－エポキシプロピル）ジスルフィド、４－ビニル－１－シクロヘキサンジエポキシド、ビスフェノールＡグリシジルエーテル、ビスフェノールＦグリシジルエーテル等のフェノール系エポキシ化合物；
水添ビスフェノールＡグリシジルエーテル、水添ビスフェノールＦグリシジルエーテル、エチレングリコールジグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、１，４－シクロヘキサンジメタノールジグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル等のアルコール系エポキシ化合物；
３，４－エポキシシクロヘキシルメチル－３'，４'－エポキシシクロヘキサンカルボキシレートや１，２－ヘキサヒドロフタル酸ジグリシジルエステル等のグリシジルエステル系エポキシ化合物；
イソシアヌル酸トリグリシジルエーテル等のアミン系エポキシ化合物等が挙げられる。また、その他、ビニルシクロヘキセンジエポキシド等の脂肪族多価エポキシ化合物等が挙げられる。
　エポキシ化合物は、より好ましくは、ビス（２，３－エポキシプロピル）ジスルフィド、１，４－シクロヘキサンジメタノールジグリシジルエーテル、ビスフェノールＡグリシジルエーテル、ビスフェノールＦグリシジルエーテル、エチレングリコールジグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、イソシアヌル酸トリグリシジルエーテルである。さらに好ましくは、１，４－シクロヘキサンジメタノールジグリシジルエーテルおよびビスフェノールＦグリシジルエーテルである。
　（エピチオ化合物）
　エピチオ化合物として、具体的には、ビス（１，２－エピチオエチル）スルフィド、ビス（１，２－エピチオエチル）ジスルフィド、ビス（エピチオエチルチオ）メタン、ビス（エピチオエチルチオ）ベンゼン、ビス［４－（エピチオエチルチオ）フェニル］スルフィド、ビス［４－（エピチオエチルチオ）フェニル］メタン等のエピチオエチルチオ化合物；
ビス（２，３－エピチオプロピル）スルフィド、ビス（２，３－エピチオプロピル）ジスルフィド、ビス（２，３－エピチオプロピルチオ）メタン、１，２－ビス（２，３－エピチオプロピルチオ）エタン、１，２－ビス（２，３－エピチオプロピルチオ）プロパン、１，３－ビス（２，３－エピチオプロピルチオ）プロパン、１，３－ビス（２，３－エピチオプロピルチオ）－２－メチルプロパン、１，４－ビス（２，３－エピチオプロピルチオ）ブタン、１，４－ビス（２，３－エピチオプロピルチオ）－２－メチルブタン、１，３－ビス（２，３－エピチオプロピルチオ）ブタン、１，５－ビス（２，３－エピチオプロピルチオ）ペンタン、１，５－ビス（２，３－エピチオプロピルチオ）－２－メチルペンタン、１，５－ビス（２，３－エピチオプロピルチオ）－３－チアペンタン、１，６－ビス（２，３－エピチオプロピルチオ）ヘキサン、１，６－ビス（２，３－エピチオプロピルチオ）－２－メチルヘキサン、３，８－ビス（２，３－エピチオプロピルチオ）－３，６－ジチアオクタン、１，２，３－トリス（２，３－エピチオプロピルチオ）プロパン、２，２－ビス（２，３－エピチオプロピルチオ）－１，３－ビス（２，３－エピチオプロピルチオメチル）プロパン、２，２－ビス（２，３－エピチオプロピルチオメチル）－１－（２，３－エピチオプロピルチオ）ブタン、１，５－ビス（２，３－エピチオプロピルチオ）－２－（２，３－エピチオプロピルチオメチル）－３－チアペンタン、１，５－ビス（２，３－エピチオプロピルチオ）－２，４－ビス（２，３－エピチオプロピルチオメチル）－３－チアペンタン、１－（２，３－エピチオプロピルチオ）－２，２－ビス（２，３－エピチオプロピルチオメチル）－４－チアヘキサン、１，５，６－トリス（２，３－エピチオプロピルチオ）－４－（２，３－エピチオプロピルチオメチル）－３－チアヘキサン、１，８－ビス（２，３－エピチオプロピルチオ）－４－（２，３－エピチオプロピルチオメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エピチオプロピルチオ）－４，５－ビス（２，３－エピチオプロピルチオメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エピチオプロピルチオ）－４，４－ビス（２，３－エピチオプロピルチオメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エピチオプロピルチオ）－２，５－ビス（２，３－エピチオプロピルチオメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エピチオプロピルチオ）－２，４，５－トリス（２，３－エピチオプロピルチオメチル）－３，６－ジチアオクタン、１，１，１－トリス［［２－（２，３－エピチオプロピルチオ）エチル］チオメチル］－２－（２，３－エピチオプロピルチオ）エタン、１，１，２，２－テトラキス［［２－（２，３－エピチオプロピルチオ）エチル］チオメチル］エタン、１，１１－ビス（２，３－エピチオプロピルチオ）－４，８－ビス（２，３－エピチオプロピルチオメチル）－３，６，９－トリチアウンデカン、１，１１－ビス（２，３－エピチオプロピルチオ）－４，７－ビス（２，３－エピチオプロピルチオメチル）－３，６，９－トリチアウンデカン、１，１１－ビス（２，３－エピチオプロピルチオ）－５，７－ビス（２，３－エピチオプロピルチオメチル）－３，６，９－トリチアウンデカン等の鎖状脂肪族の２，３－エピチオプロピルチオ化合物；
１，３－ビス（２，３－エピチオプロピルチオ）シクロヘキサン、１，４－ビス（２，３－エピチオプロピルチオ）シクロヘキサン、１，３－ビス（２，３－エピチオプロピルチオメチル）シクロヘキサン、１，４－ビス（２，３－エピチオプロピルチオメチル）シクロヘキサン、２，５－ビス（２，３－エピチオプロピルチオメチル）－１，４－ジチアン、２，５－ビス［［２－（２，３－エピチオプロピルチオ）エチル］チオメチル］－１，４－ジチアン、２，５－ビス（２，３－エピチオプロピルチオメチル）－２，５－ジメチル－１，４－ジチアン等の環状脂肪族の２，３－エピチオプロピルチオ化合物；
１，２－ビス（２，３－エピチオプロピルチオ）ベンゼン、１，３－ビス（２，３－エピチオプロピルチオ）ベンゼン、１，４－ビス（２，３－エピチオプロピルチオ）ベンゼン、１，２－ビス（２，３－エピチオプロピルチオメチル）ベンゼン、１，３－ビス（２，３－エピチオプロピルチオメチル）ベンゼン、１，４－ビス（２，３－エピチオプロピルチオメチル）ベンゼン、ビス［４－（２，３－エピチオプロピルチオ）フェニル］メタン、２，２－ビス［４－（２，３－エピチオプロピルチオ）フェニル］プロパン、ビス［４－（２，３－エピチオプロピルチオ）フェニル］スルフィド、ビス［４－（２，３－エピチオプロピルチオ）フェニル］スルホン、４，４'－ビス（２，３－エピチオプロピルチオ）ビフェニル等の芳香族の２，３－エピチオプロピルチオ化合物；
エチレンスルフィド、プロピレンスルフィド、メルカプトプロピレンスルフィド、メルカプトブテンスルフィド、エピチオクロルヒドリン等のエピチオ基を１つ有する化合物；
ビス（２，３－エピチオプロピル）エーテル、ビス（２，３－エピチオプロピルオキシ）メタン、１，２－ビス（２，３－エピチオプロピルオキシ）エタン、１，２－ビス（２，３－エピチオプロピルオキシ）プロパン、１，３－ビス（２，３－エピチオプロピルオキシ）プロパン、１，３－ビス（２，３－エピチオプロピルオキシ）－２－メチルプロパン、１，４－ビス（２，３－エピチオプロピルオキシ）ブタン、１，４－ビス（２，３－エピチオプロピルオキシ）－２－メチルブタン、１，３－ビス（２，３－エピチオプロピルオキシ）ブタン、１，５－ビス（２，３－エピチオプロピルオキシ）ペンタン、１，５－ビス（２，３－エピチオプロピルオキシ）－２－メチルペンタン、１，５－ビス（２，３－エピチオプロピルオキシ）－３－チアペンタン、１，６－ビス（２，３－エピチオプロピルオキシ）ヘキサン、１，６－ビス（２，３－エピチオプロピルオキシ）－２－メチルヘキサン、３，８－ビス（２，３－エピチオプロピルオキシ）－３，６－ジチアオクタン、１，２，３－トリス（２，３－エピチオプロピルオキシ）プロパン、２，２－ビス（２，３－エピチオプロピルオキシ）－１，３－ビス（２，３－エピチオプロピルオキシメチル）プロパン、２，２－ビス（２，３－エピチオプロピルオキシメチル）－１－（２，３－エピチオプロピルオキシ）ブタン、１，５－ビス（２，３－エピチオプロピルオキシ）－２－（２，３－エピチオプロピルオキシメチル）－３－チアペンタン、１，５－ビス（２，３－エピチオプロピルオキシ）－２，４－ビス（２，３－エピチオプロピルオキシメチル）－３－チアペンタン、１－（２，３－エピチオプロピルオキシ）－２，２－ビス（２，３－エピチオプロピルオキシメチル）－４－チアヘキサン、１，５，６－トリス（２，３－エピチオプロピルオキシ）－４－（２，３－エピチオプロピルオキシメチル）－３－チアヘキサン、１，８－ビス（２，３－エピチオプロピルオキシ）－４－（２，３－エピチオプロピルオキシメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エピチオプロピルオキシ）－４，５－ビス（２，３－エピチオプロピルオキシメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エピチオプロピルオキシ）－４，４－ビス（２，３－エピチオプロピルオキシメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エピチオプロピルオキシ）－２，５－ビス（２，３－エピチオプロピルオキシメチル）－３，６－ジチアオクタン、１，８－ビス（２，３－エピチオプロピルオキシ）－２，４，５－トリス（２，３－エピチオプロピルオキシメチル）－３，６－ジチアオクタン、１，１，１－トリス［［２－（２，３－エピチオプロピルオキシ）エチル］チオメチル］－２－（２，３－エピチオプロピルオキシ）エタン、１，１，２，２－テトラキス［［２－（２，３－エピチオプロピルオキシ）エチル］チオメチル］エタン、１，１１－ビス（２，３－エピチオプロピルオキシ）－４，８－ビス（２，３－エピチオプロピルオキシメチル）－３，６，９－トリチアウンデカン、１，１１－ビス（２，３－エピチオプロピルオキシ）－４，７－ビス（２，３－エピチオプロピルオキシメチル）－３，６，９－トリチアウンデカン、１，１１－ビス（２，３－エピチオプロピルオキシ）－５，７－ビス（２，３－エピチオプロピルオキシメチル）－３，６，９－トリチアウンデカン等の鎖状脂肪族の２，３－エピチオプロピルオキシ化合物；
１，３－ビス（２，３－エピチオプロピルオキシ）シクロヘキサン、１，４－ビス（２，３－エピチオプロピルオキシ）シクロヘキサン、１，３－ビス（２，３－エピチオプロピルオキシメチル）シクロヘキサン、１，４－ビス（２，３－エピチオプロピルオキシメチル）シクロヘキサン、２，５－ビス（２，３－エピチオプロピルオキシメチル）－１，４－ジチアン、２，５－ビス［［２－（２，３－エピチオプロピルオキシ）エチル］チオメチル］－１，４－ジチアン、２，５－ビス（２，３－エピチオプロピルオキシメチル）－２，５－ジメチル－１，４－ジチアン等の環状脂肪族の２，３－エピチオプロピルオキシ化合物；および、
１，２－ビス（２，３－エピチオプロピルオキシ）ベンゼン、１，３－ビス（２，３－エピチオプロピルオキシ）ベンゼン、１，４－ビス（２，３－エピチオプロピルオキシ）ベンゼン、１，２－ビス（２，３－エピチオプロピルオキシメチル）ベンゼン、１，３－ビス（２，３－エピチオプロピルオキシメチル）ベンゼン、１，４－ビス（２，３－エピチオプロピルオキシメチル）ベンゼン、ビス［４－（２，３－エピチオプロピルオキシ）フェニル］メタン、２，２－ビス［４－（２，３－エピチオプロピルオキシ）フェニル］プロパン、ビス［４－（２，３－エピチオプロピルオキシ）フェニル］スルフィド、ビス［４－（２，３－エピチオプロピルオキシ）フェニル］スルホン、４，４'－ビス（２，３－エピチオプロピルオキシ）ビフェニル等の芳香族の２，３－エピチオプロピルオキシ化合物等を挙げることができるが、例示化合物のみに限定されるものではない。
　これら例示化合物のうち好ましい化合物としては、ビス（１，２－エピチオエチル）スルフィド、ビス（１，２－エピチオエチル）ジスルフィド、ビス（２，３－エピチオプロピル）スルフィド、ビス（２，３－エピチオプロピルチオ）メタンおよびビス（２，３－エピチオプロピル）ジスルフィドであり、より好ましい化合物としてはビス（１，２－エピチオエチル）スルフィド、ビス（１，２－エピチオエチル）ジスルフィド、ビス（２，３－エピチオプロピル）スルフィドおよびビス（２，３－エピチオプロピル）ジスルフィドである。また、より一層好ましい化合物は、ビス（２，３－エピチオプロピル）スルフィドおよびビス（２，３－エピチオプロピル）ジスルフィドである。
　エポキシ化合物および／またはエピチオ化合物の使用量としては、樹脂組成物中の成分の構造や使用量により異なるが、得られる樹脂の屈折率を考慮すれば、本発明の重合性組成物全体に対して、２５重量％以下含有すると好ましい。２３重量％以下であればより好ましく、２０重量％以下であればさらに好ましい。得られる樹脂の色相および機械強度を考慮すれば、２．５重量％以上であると好ましい。
　エポキシ化合物および／またはエピチオ化合物は、いずれか一方、もしくは両方を併用して使用することができ、その量比は特に限定されるものではない。また、エポキシ化合物同士であって異なるエポキシ化合物、または、エピチオ化合物同士であって異なるエピチオ化合物を複数併用することも可能である。ただし、高屈折率の樹脂を得るためには、エピチオ化合物の使用が好ましい。
　（非金属チエタン化合物）
　本発明において用いられる非金属チエタン化合物は、分子構造中に１つ以上のチエタン基を含むとともに金属原子を含まない化合物であって、上記式（３０）に示した化合物以外の化合物である。好ましくはチエタニル基を合計２つ以上含有する化合物である。
　上記式（３０）に示した化合物以外の非金属チエタン化合物として、具体的には、ビスチエタニルスルフィド、ビス（チエタニルチオ）メタン、３－（（（チエタニルチオ）メチルチオ）メチルチオ）チエタン等のスルフィド系チエタン化合物；
ビスチエタニルジスルフィド、ビスチエタニルトリスルフィド、ビスチエタニルテトラスルフィド、ビスチエタニルペンタスルフィド等のポリスルフィド系チエタン化合物等が挙げられる。
　非金属チエタン化合物の使用量としては、使用する化合物の構造や使用量により異なるが、得られる樹脂の屈折率を考慮すれば、本発明の重合性組成物全体に対して、上記式（３０）に示した化合物以外の化合物と合計でたとえば２５重量％以下含有する構成とすることができ、２３重量％以下であれば好ましく、２０重量％以下であればより好ましい。一方、得られる樹脂の色相および機械強度を考慮すれば、非金属チエタン化合物の使用量を、上記式（３０）に示した化合物以外の化合物と合計でたとえば２．５重量％以上とする。
　（金属チエタン化合物）
　本発明において重合性組成物に用いられる金属チエタン化合物は、分子内にチエタン基および特定の金属原子を含有する化合物である。金属チエタン化合物として、具体的には、下記一般式（２）に示す化合物が挙げられ、さらに具体的には後述する下記一般式（６）に示す化合物が挙げられる。以下、下記一般式（２）に示す化合物を例に説明する。この重合性組成物は、たとえば光学部品の材料として用いられる。
Figure JPOXMLDOC01-appb-C000009
（上記一般式（２）中、Ｍは金属原子である。Ｘ1およびＸ2は各々独立に硫黄原子または酸素原子である。Ｒ1は２価の有機基である。
　ｍは０または１以上の整数である。
　ｎはＭの価数であり、ｐは１以上ｎ以下の整数である。
　ｑは０または１以上ｎ－２以下の整数である。
　Ｙは１価または２価の基であり、Ｔは無機または有機基である。
　ｒは１または２である。
　ｒ＝１のとき、ｑ＝０であり、Ｙは１価の無機または有機基である。ｒ＝１かつｎ－ｐ－ｑが２以上の場合、複数のＹは、各々独立に１価の無機または有機基である。ｒ＝１かつｎ－ｐ－ｑが２以上の場合、複数のＹが互いに結合し、金属原子を含む環を形成していてもよい。
　ｒ＝２のとき、ｎ－ｐ－ｑ＝１または２であり、Ｙは２価の基である。ｒ＝２かつｎ－ｐ－ｑ＝２の場合、２つのＹが、２つの金属原子とともに環を形成していてもよい。ｒ＝２かつｑ＝２の場合、複数のＴは、各々独立に無機または有機基である。）
　本発明における重合性組成物は、上記一般式（２）に示した金属チエタン化合物として、一種類の化合物を含んでいてもよいし、異なる複数の化合物を含んでいてもよい。
　たとえば、金属チエタン化合物として、上記一般式（２）においてＭがＳｂ（アンチモン）またはＳｎ（スズ）である化合物を含んでもよい。
　また、一般式（２）に示した金属チエタン化合物として、ｍ＝０であることが好ましく、また、Ｘ1が硫黄原子であることが好ましい。さらに、一般式（２）に示した金属チエタン化合物はｎ＝ｐ＝３あるいは、ｎ＝ｐ＝４であることが好ましい。
　また、金属チエタン化合物として、金属原子Ｍが異なる複数の化合物を含んでいてもよい。このとき、重合性組成物は、たとえば本発明における金属チエタン化合物として上記一般式（２）においてＭがＳｂの化合物（たとえば、下記一般式（４）に示す化合物）およびＭがＳｎである化合物（たとえば、下記一般式（５）に示す化合物）を含んでもよい。
　また、本発明の重合性組成物は、金属原子Ｍが異なる複数の化合物と、分子構造中に金属原子を含まないチエタン化合物（非金属チエタン化合物）を含んでもよい。
　以下、上記一般式（２）において金属原子ＭがＳｂ原子である場合を主に例に挙げながら、さらに詳しく説明する。
　ＭがＳｂ原子のとき、上記一般式（２）に示した金属チエタン化合物は、分子内にチエタン基およびＳｂ原子を含有する化合物であり、下記一般式（６）で表される。
　本発明の重合性組成物は、上記一般式（６）に示した金属チエタン化合物として、一種類の化合物を含んでいてもよいし、異なる複数の化合物を含んでいてもよい。
Figure JPOXMLDOC01-appb-C000010
（上記一般式（６）中、Ｘ1およびＸ2は各々独立に硫黄原子または酸素原子である。Ｒ1は２価の有機基である。
　ｍは０または１以上の整数である。
　ｎは３または５である。ｎ＝３のとき、ｐは１以上３以下の整数である。ｎ＝５のとき、ｐは１以上５以下の整数である。
　ｑは０または１以上ｎ－２以下の整数である。
　Ｙは１価または２価の基であり、Ｔは無機または有機基である。
　ｒは１または２である。
　ｒ＝１のとき、ｑ＝０であり、Ｙは１価の無機または有機基である。ｒ＝１かつｎ－ｐ－ｑが２以上の場合、複数のＹは、各々独立に１価の無機または有機基である。ｒ＝１かつｎ－ｐ－ｑが２以上の場合、複数のＹが互いに結合し、Ｓｂ原子を含む環を形成していてもよい。
　ｒ＝２のとき、ｎ－ｐ－ｑ＝１または２であり、Ｙは２価の基である。ｒ＝２かつｎ－ｐ－ｑ＝２の場合、２つのＹが、２つのＳｂ原子とともに環を形成していてもよい。ｒ＝２かつｑ＝２の場合、複数のＴは、各々独立に無機または有機基である。）
　以下、上記一般式（６）について具体的に説明する。
　まず、上記一般式（６）中、ｒ＝１の場合について説明する。ｒ＝１のとき、ｑ＝０であり、本発明の金属チエタン化合物は下記一般式（３）に示される化合物となる。
Figure JPOXMLDOC01-appb-C000011
（上記一般式（３）中、Ｘ1およびＸ2は各々独立に硫黄原子または酸素原子である。Ｒ1は２価の有機基である。
　ｍは０または１以上の整数である。ｎは３または５である。ｎ＝３のとき、ｐは１以上３以下の整数であり、ｎ＝５のとき、ｐは１以上５以下の整数である。
　Ｙは１価の無機または有機基である。ｎ－ｐが２以上の場合、複数のＹは、各々独立に１価の無機または有機基である。ｎ－ｐが２以上の場合、複数のＹが互いに結合し、Ｓｂ原子を含む環を形成していてもよい。）
　以下、上記一般式（３）について具体的に説明する。
　まず、上記一般式（３）において、Ｘ1およびＸ2は、各々独立に硫黄原子または酸素原子を表す。本発明の所望の効果である高屈折率であることを鑑みると、Ｘ1およびＸ2として、硫黄原子はより好ましい。
　上記一般式（３）において、Ｒ1は２価の有機基を表す。
　かかる二価の有機基としては、鎖状または環状脂肪族基、芳香族基および芳香族－脂肪族基が挙げられ、好ましくは、炭素数１以上２０以下の鎖状脂肪族基、炭素数３以上２０以下の環状脂肪族基、炭素数５以上２０以下の芳香族基、炭素数６以上２０以下の芳香族－脂肪族基である。
　Ｒ1は、より具体的には、かかる二価の有機基が鎖状または環状脂肪族基、芳香族基または芳香族－脂肪族基であって、好ましくは、
メチレン基、エチレン基、１，２－ジクロロエチレン基、トリメチレン基、テトラメチレン基、ペンタメチレン基、シクロペンチレン基、ヘキサメチレン基、シクロヘキシレン基、ヘプタメチレン基、オクタメチレン基、ノナメチレン基、デカメチレン基、ウンデカメチレン基、ドデカメチレン基、トリデカメチレン基、テトラデカメチレン基、ペンタデカメチレン基等の炭素数１以上２０以下の置換または無置換の鎖状または環状脂肪族基；
フェニレン基、クロロフェニレン基、ナフチレン基、インデニレン基、アントラセニレン基、フルオレニレン基等の置換または無置換の炭素数５以上２０以下の芳香族基；または
－Ｃ6Ｈ4－ＣＨ2－基、－ＣＨ2－Ｃ6Ｈ4－ＣＨ2－基、－ＣＨ2－Ｃ6Ｈ3（Ｃｌ）－ＣＨ2－基、－Ｃ10Ｈ6－ＣＨ2－基、－ＣＨ2－Ｃ10Ｈ6－ＣＨ2－基、－ＣＨ2ＣＨ2－Ｃ6Ｈ4－ＣＨ2ＣＨ2－基等の置換または無置換の炭素数６以上２０以下の芳香族－脂肪族基である。
　Ｒ1は、より好ましくはメチレン基、エチレン基、１，２－ジクロロエチレン基、トリメチレン基、シクロペンチレン基、シクロヘキシレン基等の炭素数１以上６以下の置換または無置換の鎖状または環状脂肪族基；
フェニレン基、クロロフェニレン基、ナフチレン基、インデニレン基、アントラセニレン基、フルオレニレン基等の置換または無置換の炭素数５以上１５以下の芳香族基；または
－Ｃ6Ｈ4－ＣＨ2－基、－ＣＨ2－Ｃ6Ｈ4－ＣＨ2－基、－ＣＨ2－Ｃ6Ｈ3（Ｃｌ）－ＣＨ2－基、－Ｃ10Ｈ6－ＣＨ2－基、－ＣＨ2－Ｃ10Ｈ6－ＣＨ2－基、－ＣＨ2ＣＨ2－Ｃ6Ｈ4－ＣＨ2ＣＨ2－基等の置換または無置換の炭素数６以上１５以下の芳香族－脂肪族基である。
　かかる二価の有機基は、基中に炭素原子、水素原子以外のヘテロ原子を含有していてもよい。かかるヘテロ原子としては、酸素原子または硫黄原子が挙げられるが、本発明の所望の効果を考慮すると、硫黄原子であることが好ましい。
　上記一般式（３）において、ｍは０または１以上の整数を表す。かかるｍは、好ましくは、０以上４以下の整数であり、より好ましくは、０以上２以下の整数であり、さらに好ましくは、整数０または１である。
　ｍ＝０のとき、上記一般式（３）は、下記一般式（７）となる。
Figure JPOXMLDOC01-appb-C000012
（上記一般式（７）において、Ｘ1、Ｙ、ｎおよびｐは、それぞれ、上記一般式（３）におけるＸ1、Ｙ、ｎおよびｐと同じである。）
　また、上記一般式（３）中の、チエタニル基を含みＳｂ原子に結合する基において、より一層好ましくは、ｍ＝０であり、かつＸ1が硫黄原子である。このとき、上記一般式（３）は、下記一般式（８）で表される。
Figure JPOXMLDOC01-appb-C000013
（上記一般式（８）において、Ｙ、ｎおよびｐは、それぞれ、上記一般式（３）におけるＹ、ｎおよびｐと同じである。）
　なお、上記一般式（８）において、好ましくはｎ＝ｐである。
　次に、上記一般式（３）におけるｎおよびｐについて説明する。
　ｎは、Ｓｂ原子の価数つまり５または３である。後述する重合性組成物中の重合性化合物として用いたときの高屈折率化のために金属の含有率を高める観点では、ｎが３であることが好ましい。
　また、ｐは、Ｓｂ原子の価数以下の正の整数である。よって、Ｓｂ原子の価数ｎが３のとき、ｐは１以上３以下の正の整数であり、Ｓｂ原子の価数ｎが５のとき、ｐは１以上５以下の正の整数である。かかるｐは、好ましくは、ｎ、ｎ－１またはｎ－２であり、より好ましくは、ｎまたはｎ－１である。
　上記一般式（３）において、具体的にはｐ＝３であり、さらに具体的には、Ｘ1が硫黄原子であり、ｎ＝ｐ＝３である。このとき、上記一般式（３）に示される化合物は、下記式（４）に示される化合物となる。
Figure JPOXMLDOC01-appb-C000014
　また、上記一般式（３）において、具体的にはｐ＝５であり、さらに具体的には、Ｘ1が硫黄原子であり、ｎ＝ｐ＝５である。このとき、上記一般式（３）に示される化合物は、下記式（９）に示される化合物となる。
Figure JPOXMLDOC01-appb-C000015
　上記一般式（３）において、Ｙは、１価の無機または有機基を表す。以下、Ｙの具体例を説明する。
　まず、ｎ－ｐ＝１の場合、Ｙは１価の無機または有機基を表す。また、ｎ－ｐが２以上の整数の場合、複数のＹは、各々独立に１価の無機または有機基を表す。複数のＹは、同じ基であってもよいし、全部または一部が異なる基であってもよい。また、複数のＹが互いに結合し、Ｓｂ原子を含む環を形成していてもよい。
　Ｙは特に制限されるものではないが、たとえば、水素原子、ハロゲン原子、水酸基、チオール基、置換または無置換のアルキル基、置換または無置換のアリール基、置換または無置換のアラルキル基、置換または無置換のアルコキシ基、置換または無置換のアルキルチオ基、置換または無置換のアリールオキシ基、置換または無置換のアリールチオ基が挙げられる。
　これらのうち、ハロゲン原子、置換または無置換のアルキル基、置換または無置換のアリール基、置換または無置換のアラルキル基、置換または無置換のアルコキシ（アルキルオキシ）基、置換または無置換のアルキルチオ基、置換または無置換のアリールオキシ基、置換または無置換のアリールチオ基に関して以下説明する。
　ハロゲン原子の具体例として、フッ素原子、塩素原子、臭素原子およびヨウ素原子が挙げられる。
　置換または無置換のアルキル基の具体例として、メチル基、エチル基、ｎ－プロピル基、ｎ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基、等の総炭素数１以上１０以下の直鎖アルキル基；
イソプロピル基、イソブチル基、ｓｅｃ－ブチル基、イソペンチル基、ｓｅｃ－ペンチル基、１－メチルペンチル基、２－メチルペンチル基、３－メチルペンチル基、４－メチルペンチル基、１－エチルブチル基、２－エチルブチル基、１－メチルヘキシル基、２－メチルヘキシル基、３－メチルヘキシル基、４－メチルヘキシル基、５－メチルヘキシル基、１－エチルペンチル基、２－エチルペンチル基、３－エチルペンチル基、１－ｎ－プロピルブチル基、１－ｉｓｏ－プロピルブチル基、１－ｉｓｏ－プロピル－２－メチルプロピル基、１－メチルヘプチル基、２－メチルヘプチル基、３－メチルヘプチル基、４－メチルヘプチル基、５－メチルヘプチル基、６－メチルヘプチル基、１－エチルヘキシル基、２－エチルヘキシル基、３－エチルヘキシル基、４－エチルヘキシル基、１－ｎ－プロピルペンチル基、２－ｎ－プロピルペンチル基、１－ｉｓｏ－プロピルペンチル基、２－ｉｓｏ－プロピルペンチル基、１－ｎ－ブチルブチル基、１－ｉｓｏ－ブチルブチル基、１－ｓｅｃ－ブチルブチル基、１－ｔｅｒｔ－ブチルブチル基、２－ｔｅｒｔ－ブチルブチル基、ｔｅｒｔ－ブチル基、ｔｅｒｔ－ペンチル基、１，１－ジメチルブチル基、１，２－ジメチルブチル基、１，３－ジメチルブチル基、２，３－ジメチルブチル基、１－エチル－２－メチルプロピル基、１，１－ジメチルペンチル基、１，２－ジメチルペンチル基、１，３－ジメチルペンチル基、１，４－ジメチルペンチル基、２，２－ジメチルペンチル基、２，３－ジメチルペンチル基、２，４－ジメチルペンチル基、３，３－ジメチルペンチル基、３，４－ジメチルペンチル基、１－エチル－１－メチルブチル基、１－エチル－２－メチルブチル基、１－エチル－３－メチルブチル基、２－エチル－１－メチルブチル基、２－エチル－３－メチルブチル基、１，１－ジメチルヘキシル基、１，２－ジメチルヘキシル基、１，３－ジメチルヘキシル基、１，４－ジメチルヘキシル基、１，５－ジメチルヘキシル基、２，２－ジメチルヘキシル基、２，３－ジメチルヘキシル基、２，４－ジメチルヘキシル基、２，５－ジメチルヘキシル基、３，３－ジメチルヘキシル基、３，４－ジメチルヘキシル基、３，５－ジメチルヘキシル基、４，４－ジメチルヘキシル基、４，５－ジメチルヘキシル基、１－エチル－２－メチルペンチル基、１－エチル－３－メチルペンチル基、１－エチル－４－メチルペンチル基、２－エチル－１－メチルペンチル基、２－エチル－２－メチルペンチル基、２－エチル－３－メチルペンチル基、２－エチル－４－メチルペンチル基、３－エチル－１－メチルペンチル基、３－エチル－２－メチルペンチル基、３－エチル－３－メチルペンチル基、３－エチル－４－メチルペンチル基、１－ｎ－プロピル－１－メチルブチル基、１－ｎ－プロピル－２－メチルブチル基、１－ｎ－プロピル－３－メチルブチル基、１－ｉｓｏ－プロピル－１－メチルブチル基、１－ｉｓｏ－プロピル－２－メチルブチル基、１－ｉｓｏ－プロピル－３－メチルブチル基、１，１－ジエチルブチル基、１，２－ジエチルブチル基、１，１，２－トリメチルプロピル基、１，２，２－トリメチルプロピル基、１，１，２－トリメチルブチル基、１，１，３－トリメチルブチル基、１，２，３－トリメチルブチル基、１，２，２－トリメチルブチル基、１，３，３－トリメチルブチル基、２，３，３－トリメチルブチル基、１，１，２－トリメチルペンチル基、１，１，３－トリメチルペンチル基、１，１，４－トリメチルペンチル基、１，２，２－トリメチルペンチル基、１，２，３－トリメチルペンチル基、１，２，４－トリメチルペンチル基、１，３，４－トリメチルペンチル基、２，２，３－トリメチルペンチル基、２，２，４－トリメチルペンチル基、２，３，４－トリメチルペンチル基、１，３，３－トリメチルペンチル基、２，３，３－トリメチルペンチル基、３，３，４－トリメチルペンチル基、１，４，４－トリメチルペンチル基、２，４，４－トリメチルペンチル基、３，４，４－トリメチルペンチル基、１－エチル－１，２－ジメチルブチル基、１－エチル－１，３－ジメチルブチル基、１－エチル－２，３－ジメチルブチル基、２－エチル－１，１－ジメチルブチル基、２－エチル－１，２－ジメチルブチル基、２－エチル－１，３－ジメチルブチル基、２－エチル－２，３－ジメチルブチル基等の総炭素数３以上１０以下の分岐アルキル基；および
シクロペンチル基、シクロヘキシル基、メチルシクロペンチル基、メトキシシクロペンチル基、メトキシシクロヘキシル基、メチルシクロヘキシル基、１，２－ジメチルシクロヘキシル基、１，３－ジメチルシクロヘキシル基、１，４－ジメチルシクロヘキシル基、エチルシクロヘキシル基等の総炭素数５以上１０以下の飽和環状アルキル基が挙げられる。
　置換または無置換のアリール基の具体例として、フェニル基、ナフチル基、アンスラニル基、シクロペンタジエニル基等の総炭素数２０以下の芳香族炭化水素；
２－メチルフェニル基、３－メチルフェニル基、４－メチルフェニル基、２－エチルフェニル基、プロピルフェニル基、ブチルフェニル基、ヘキシルフェニル基、シクロヘキシルフェニル基、オクチルフェニル基、２－メチル－１－ナフチル基、３－メチル－１－ナフチル基、４－メチル－１－ナフチル基、５－メチル－１－ナフチル基、６－メチル－１－ナフチル基、７－メチル－１－ナフチル基、８－メチル－１－ナフチル基、１－メチル－２－ナフチル基、３－メチル－２－ナフチル基、４－メチル－２－ナフチル基、５－メチル－２－ナフチル基、６－メチル－２－ナフチル基、７－メチル－２－ナフチル基、８－メチル－２－ナフチル基、２－エチル－１－ナフチル基、２，３－ジメチルフェニル基、２，４－ジメチルフェニル基、２，５－ジメチルフェニル基、２，６－ジメチルフェニル基、３，４－ジメチルフェニル基、３，５－ジメチルフェニル基、３，６－ジメチルフェニル基、２，３，４－トリメチルフェニル基、２，３，５－トリメチルフェニル基、２，３，６－トリメチルフェニル基、２，４，５－トリメチルフェニル基、２，４，６－トリメチルフェニル基、３，４，５－トリメチルフェニル基等の総炭素数２０以下のアルキル置換アリール基；
２－メトキシフェニル基、３－メトキシフェニル基、４－メトキシフェニル基、２－エトキシフェニル基、プロポキシフェニル基、ブトキシフェニル基、ヘキシルオキシフェニル基、シクロヘキシルオキシフェニル基、オクチルオキシフェニル基、２－メトキシ－１－ナフチル基、３－メトキシ－１－ナフチル基、４－メトキシ－１－ナフチル基、５－メトキシ－１－ナフチル基、６－メトキシ－１－ナフチル基、７－メトキシ－１－ナフチル基、８－メトキシ－１－ナフチル基、１－メトキシ－２－ナフチル基、３－メトキシ－２－ナフチル基、４－メトキシ－２－ナフチル基、５－メトキシ－２－ナフチル基、６－メトキシ－２－ナフチル基、７－メトキシ－２－ナフチル基、８－メトキシ－２－ナフチル基、２－エトキシ－１－ナフチル基等の炭素数１０以下の置換または無置換のアルキルオキシ基が置換した総炭素数２０以下のモノアルコキシアリール基；
２，３－ジメトキシフェニル基、２，４－ジメトキシフェニル基、２，５－ジメトキシフェニル基、２，６－ジメトキシフェニル基、３，４－ジメトキシフェニル基、３，５－ジメトキシフェニル基、３，６－ジメトキシフェニル基、４，５－ジメトキシ－１－ナフチル基、４，７－ジメトキシ－１－ナフチル基、４，８－ジメトキシ－１－ナフチル基、５，８－ジメトキシ－１－ナフチル基、５，８－ジメトキシ－２－ナフチル基等の炭素数１０以下の置換または無置換のアルキルオキシ基が置換した総炭素数２０以下のジアルコキシアリール基；
２，３，４－トリメトキシフェニル基、２，３，５－トリメトキシフェニル基、２，３，６－トリメトキシフェニル基、２，４，５－トリメトキシフェニル基、２，４，６－トリメトキシフェニル基、３，４，５－トリメトキシフェニル基等の炭素数１０以下の置換または無置換のアルキルオキシが置換した総炭素数２０以下のトリアルコキシアリール基；および
クロロフェニル基、ジクロロフェニル基、トリクロロフェニル基、ブロモフェニル基、ジブロモフェニル基、ヨードフェニル基、フルオロフェニル基、クロロナフチル基、ブロモナフチル基、ジフルオロフェニル基、トリフルオロフェニル基、テトラフルオロフェニル基、ペンタフルオロフェニル基等のハロゲン原子が置換した総炭素数２０以下のアリール基が挙げられる。
　置換または無置換のアラルキル基の具体例として、ベンジル基、フェネチル基、フェニルプロピル基、ナフチルエチル基等の総炭素数１２以下のアラルキル基が挙げられる。また、他に、置換または無置換のアリール基の具体例で挙げたアリール基を側鎖にもつメチル基、エチル基、プロピル基が挙げられる。
　置換または無置換のアルキルオキシ基の具体例として、メトキシ基、エトキシ基、ｎ－プロポキシ基、ｉｓｏ－プロポキシ基、ｎ－ブトキシ基、ｉｓｏ－ブトキシ基、ｔｅｒｔ－ブトキシ基、ｎ－ペンチルオキシ基、ｉｓｏ－ペンチルオキシ基、ｎ－ヘキシルオキシ基、ｉｓｏ－ヘキシルオキシ基、２－エチルヘキシルオキシ基、３，５，５－トリメチルヘキシルオキシ基、ｎ－ヘプチルオキシ基、ｎ－オクチルオキシ基、ｎ－ノニルオキシ基等の総炭素数１以上１０以下の直鎖または分岐のアルコキシ基；
　シクロペンチルオキシ基、シクロヘキシルオキシ基等の総炭素数５以上１０以下のシクロアルコキシ基；
　メトキシメトキシ基、エトキシメトキシ基、エトキシエトキシ基、ｎ－プロポキシメトキシ基、ｉｓｏ－プロポキシメトキシ基、ｎ－プロポキシエトキシ基、ｉｓｏ－プロポキシエトキシ基、ｎ－ブトキシエトキシ基、ｉｓｏ－ブトキシエトキシ基、ｔｅｒｔ－ブトキシエトキシ基、ｎ－ペンチルオキシエトキシ基、ｉｓｏ－ペンチルオキシエトキシ基、ｎ－ヘキシルオキシエトキシ基、ｉｓｏ－ヘキシルオキシエトキシ基、ｎ－ヘプチルオキシエトキシ基等の総炭素数２以上１０以下のアルコキシアルコキシ基；および
ベンジルオキシ基等のアラルキルオキシ基が挙げられる。
　置換または無置換のアルキルチオ基の具体例として、メチルチオ基、エチルチオ基、ｎ－プロピルチオ基、ｉｓｏ－プロピルチオ基、ｎ－ブチルチオ基、ｉｓｏ－ブチルチオ基、ｓｅｃ－ブチルチオ基、ｔ－ブチルチオ基、ｎ－ペンチルチオ基、ｉｓｏ－ペンチルチオ基、ｎ－ヘキシルチオ基、ｉｓｏ－ヘキシルチオ基、２－エチルヘキシルチオ基、３，５，５－トリメチルヘキシルチオ基、ｎ－ヘプチルチオ基、ｎ－オクチルチオ基、ｎ－ノニルチオ基等の総炭素数１以上１０以下の直鎖または分岐のアルキルチオ基；
シクロペンチルチオ基、シクロヘキシルチオ基等の総炭素数５以上１０以下のシクロアルキルチオ基；
メトキシエチルチオ基、エトキシエチルチオ基、ｎ－プロポキシエチルチオ基、ｉｓｏ－プロポキシエチルチオ基、ｎ－ブトキシエチルチオ基、ｉｓｏ－ブトキシエチルチオ基、ｔｅｒｔ－ブトキシエチルチオ基、ｎ－ペンチルオキシエチルチオ基、ｉｓｏ－ペンチルオキシエチルチオ基、ｎ－ヘキシルオキシエチルチオ基、ｉｓｏ－ヘキシルオキシエチルチオ基、ｎ－ヘプチルオキシエチルチオ基等の総炭素数２以上１０以下のアルコキシアルキルチオ基；
ベンジルチオ基などのアラルキルチオ基；および
メチルチオエチルチオ基、エチルチオエチルチオ基、ｎ－プロピルチオエチルチオ基、ｉｓｏ－プロピルチオエチルチオ基、ｎ－ブチルチオエチルチオ基、ｉｓｏ－ブチルチオエチルチオ基、ｔｅｒｔ－ブチルチオエチルチオ基、ｎ－ペンチルチオエチルチオ基、ｉｓｏ－ペンチルチオエチルチオ基、ｎ－ヘキシルチオエチルチオ基、ｉｓｏ－ヘキシルチオエチルチオ基、ｎ－ヘプチルチオエチルチオ基等の総炭素数２以上１０以下のアルキルチオアルキルチオ基が挙げられる。
　置換または無置換のアリールオキシ基の具体例として、フェニルオキシ基、ナフチルオキシ基、アンスラニルオキシ基、２－メチルフェニルオキシ基、３－メチルフェニルオキシ基、４－メチルフェニルオキシ基、２－エチルフェニルオキシ基、プロピルフェニルオキシ基、ブチルフェニルオキシ基、ヘキシルフェニルオキシ基、シクロヘキシルフェニルオキシ基、オクチルフェニルオキシ基、２－メチル－１－ナフチルオキシ基、３－メチル－１－ナフチルオキシ基、４－メチル－１－ナフチルオキシ基、５－メチル－１－ナフチルオキシ基、６－メチル－１－ナフチルオキシ基、７－メチル－１－ナフチルオキシ基、８－メチル－１－ナフチルオキシ基、１－メチル－２－ナフチルオキシ基、３－メチル－２－ナフチルオキシ基、４－メチル－２－ナフチルオキシ基、５－メチル－２－ナフチルオキシ基、６－メチル－２－ナフチルオキシ基、７－メチル－２－ナフチルオキシ基、８－メチル－２－ナフチルオキシ基、２－エチル－１－ナフチルオキシ基、２，３－ジメチルフェニルオキシ基、２，４－ジメチルフェニルオキシ基、２，５－ジメチルフェニルオキシ基、２，６－ジメチルフェニルオキシ基、３，４－ジメチルフェニルオキシ基、３，５－ジメチルフェニルオキシ基、３，６－ジメチルフェニルオキシ基、２，３，４－トリメチルフェニルオキシ基、２，３，５－トリメチルフェニルオキシ基、２，３，６－トリメチルフェニルオキシ基、２，４，５－トリメチルフェニルオキシ基、２，４，６－トリメチルフェニルオキシ基、３，４，５－トリメチルフェニルオキシ基等の総炭素数２０以下の無置換またはアルキル置換アリールオキシ基；
２－メトキシフェニルオキシ基、３－メトキシフェニルオキシ基、４－メトキシフェニルオキシ基、２－エトキシフェニルオキシ基、プロポキシフェニルオキシ基、ブトキシフェニルオキシ基、ヘキシルオキシフェニルオキシ基、シクロヘキシルオキシフェニルオキシ基、オクチルオキシフェニルオキシ基、２－メトキシ－１－ナフチルオキシ基、３－メトキシ－１－ナフチルオキシ基、４－メトキシ－１－ナフチルオキシ基、５－メトキシ－１－ナフチルオキシ基、６－メトキシ－１－ナフチルオキシ基、７－メトキシ－１－ナフチルオキシ基、８－メトキシ－１－ナフチルオキシ基、１－メトキシ－２－ナフチルオキシ基、３－メトキシ－２－ナフチルオキシ基、４－メトキシ－２－ナフチルオキシ基、５－メトキシ－２－ナフチルオキシ基、６－メトキシ－２－ナフチルオキシ基、７－メトキシ－２－ナフチルオキシ基、８－メトキシ－２－ナフチルオキシ基、２－エトキシ－１－ナフチルオキシ基等の炭素数１０以下の置換または無置換のアルキルオキシ基が置換した総炭素数２０以下のモノアルコキシアリールオキシ基；
２，３－ジメトキシフェニルオキシ基、２，４－ジメトキシフェニルオキシ基、２，５－ジメトキシフェニルオキシ基、２，６－ジメトキシフェニルオキシ基、３，４－ジメトキシフェニルオキシ基、３，５－ジメトキシフェニルオキシ基、３，６－ジメトキシフェニルオキシ基、４，５－ジメトキシ－１－ナフチルオキシ基、４，７－ジメトキシ－１－ナフチルオキシ基、４，８－ジメトキシ－１－ナフチルオキシ基、５，８－ジメトキシ－１－ナフチルオキシ基、５，８－ジメトキシ－２－ナフチルオキシ基等の炭素数１０以下の置換または無置換のアルキルオキシ基が置換した総炭素数２０以下のジアルコキシアリールオキシ基；
２，３，４－トリメトキシフェニルオキシ基、２，３，５－トリメトキシフェニルオキシ基、２，３，６－トリメトキシフェニルオキシ基、２，４，５－トリメトキシフェニルオキシ基、２，４，６－トリメトキシフェニルオキシ基、３，４，５－トリメトキシフェニルオキシ基等の炭素数１０以下の置換または無置換のアルキルオキシ基が置換した総炭素数２０以下のトリアルコキシアリールオキシ基；および
クロロフェニルオキシ基、ジクロロフェニルオキシ基、トリクロロフェニルオキシ基、ブロモフェニルオキシ基、ジブロモフェニルオキシ基、ヨードフェニルオキシ基、フルオロフェニルオキシ基、クロロナフチルオキシ基、ブロモナフチルオキシ基、ジフルオロフェニルオキシ基、トリフルオロフェニルオキシ基、テトラフルオロフェニルオキシ基、ペンタフルオロフェニルオキシ基等のハロゲン原子が置換した総炭素数２０以下のアリールオキシ基が挙げられる。
　置換または無置換のアリールチオ基の具体例として、フェニルチオ基、ナフチルチオ基、アンスラニルチオ基、２－メチルフェニルチオ基、３－メチルフェニルチオ基、４－メチルフェニルチオ基、２－エチルフェニルチオ基、プロピルフェニルチオ基、ブチルフェニルチオ基、ヘキシルフェニルチオ基、シクロヘキシルフェニルチオ基、オクチルフェニルチオ基、２－メチル－１－ナフチルチオ基、３－メチル－１－ナフチルチオ基、４－メチル－１－ナフチルチオ基、５－メチル－１－ナフチルチオ基、６－メチル－１－ナフチルチオ基、７－メチル－１－ナフチルチオ基、８－メチル－１－ナフチルチオ基、１－メチル－２－ナフチルチオ基、３－メチル－２－ナフチルチオ基、４－メチル－２－ナフチルチオ基、５－メチル－２－ナフチルチオ基、６－メチル－２－ナフチルチオ基、７－メチル－２－ナフチルチオ基、８－メチル－２－ナフチルチオ基、２－エチル－１－ナフチルチオ基、２，３－ジメチルフェニルチオ基、２，４－ジメチルフェニルチオ基、２，５－ジメチルフェニルチオ基、２，６－ジメチルフェニルチオ基、３，４－ジメチルフェニルチオ基、３，５－ジメチルフェニルチオ基、３，６－ジメチルフェニルチオ基、２，３，４－トリメチルフェニルチオ基、２，３，５－トリメチルフェニルチオ基、２，３，６－トリメチルフェニルチオ基、２，４，５－トリメチルフェニルチオ基、２，４，６－トリメチルフェニルチオ基、３，４，５－トリメチルフェニルチオ基等の総炭素数２０以下の無置換またはアルキル置換アリールチオ基；
２－メトキシフェニルチオ基、３－メトキシフェニルチオ基、４－メトキシフェニルチオ基、２－エトキシフェニルチオ基、プロポキシフェニルチオ基、ブトキシフェニルチオ基、ヘキシルオキシフェニルチオ基、シクロヘキシルオキシフェニルチオ基、オクチルオキシフェニルチオ基、２－メトキシ－１－ナフチルチオ基、３－メトキシ－１－ナフチルチオ基、４－メトキシ－１－ナフチルチオ基、５－メトキシ－１－ナフチルチオ基、６－メトキシ－１－ナフチルチオ基、７－メトキシ－１－ナフチルチオ基、８－メトキシ－１－ナフチルチオ基、１－メトキシ－２－ナフチルチオ基、３－メトキシ－２－ナフチルチオ基、４－メトキシ－２－ナフチルチオ基、５－メトキシ－２－ナフチルチオ基、６－メトキシ－２－ナフチルチオ基、７－メトキシ－２－ナフチルチオ基、８－メトキシ－２－ナフチルチオ基、２－エトキシ－１－ナフチルチオ基等の炭素数１０以下の置換または無置換のアルキルオキシ基が置換した総炭素数２０以下のモノアルコキシアリールチオ基；
２，３－ジメトキシフェニルチオ基、２，４－ジメトキシフェニルチオ基、２，５－ジメトキシフェニルチオ基、２，６－ジメトキシフェニルチオ基、３，４－ジメトキシフェニルチオ基、３，５－ジメトキシフェニルチオ基、３，６－ジメトキシフェニルチオ基、４，５－ジメトキシ－１－ナフチルチオ基、４，７－ジメトキシ－１－ナフチルチオ基、４，８－ジメトキシ－１－ナフチルチオ基、５，８－ジメトキシ－１－ナフチルチオ基、５，８－ジメトキシ－２－ナフチルチオ基等の炭素数１０以下の置換または無置換のアルキルオキシ基が置換した総炭素数２０以下のジアルコキシアリールチオ基；
２，３，４－トリメトキシフェニルチオ基、２，３，５－トリメトキシフェニルチオ基、２，３，６－トリメトキシフェニルチオ基、２，４，５－トリメトキシフェニルチオ基、２，４，６－トリメトキシフェニルチオ基、３，４，５－トリメトキシフェニルチオ基等の炭素数１０以下の置換または無置換のアルキルオキシ基が置換した総炭素数２０以下のトリアルコキシアリールチオ基；および
クロロフェニルチオ基、ジクロロフェニルチオ基、トリクロロフェニルチオ基、ブロモフェニルチオ基、ジブロモフェニルチオ基、ヨードフェニルチオ基、フルオロフェニルチオ基、クロロナフチルチオ基、ブロモナフチルチオ基、ジフルオロフェニルチオ基、トリフルオロフェニルチオ基、テトラフルオロフェニルチオ基、ペンタフルオロフェニルチオ基等のハロゲン原子が置換した総炭素数２０以下のアリールチオ基等が挙げられる。Ｙはこれらに限定されるものではない。
　かかるＹにおいて、好ましい例を以下に示す。
　好ましい例として、たとえば水素原子が挙げられる。
　また、Ｙの好ましい例のうち、ハロゲン原子として、塩素原子、臭素原子、ヨウ素原子が挙げられる。
　置換または無置換のアルキル基として、メチル基、エチル基、ｎ－プロピル基、ｎ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基、等の総炭素数１以上６以下の直鎖アルキル基；
イソプロピル基、イソブチル基、ｓｅｃ－ブチル基、イソペンチル基、ｓｅｃ－ペンチル基、１－メチルペンチル基、２－メチルペンチル基、３－メチルペンチル基、４－メチルペンチル基、１－エチルブチル基、２－エチルブチル基、ｔｅｒｔ－ブチル基、ｔｅｒｔ－ペンチル基、１，１－ジメチルブチル基、１，２－ジメチルブチル基、１，３－ジメチルブチル基、２，３－ジメチルブチル基、等の総炭素数３以上６以下の分岐アルキル基；および
シクロペンチル基、シクロヘキシル基、等の総炭素数５または６の飽和環状アルキル基が挙げられる。
　置換または無置換のアリール基として、フェニル基、ナフチル基、シクロペンタジエニル基等の総炭素数１２以下の芳香族炭化水素；
２－メチルフェニル基、３－メチルフェニル基、４－メチルフェニル基、２－エチルフェニル基、プロピルフェニル基、ブチルフェニル基、２，３－ジメチルフェニル基、２，４－ジメチルフェニル基、２，５－ジメチルフェニル基、２，６－ジメチルフェニル基、３，４－ジメチルフェニル基、３，５－ジメチルフェニル基、３，６－ジメチルフェニル基、２，３，４－トリメチルフェニル基、２，３，５－トリメチルフェニル基、２，３，６－トリメチルフェニル基、２，４，５－トリメチルフェニル基、２，４，６－トリメチルフェニル基、３，４，５－トリメチルフェニル基等の総炭素数１２以下のアルキル置換アリール基；
２－メトキシフェニル基、３－メトキシフェニル基、４－メトキシフェニル基、２－エトキシフェニル基、プロポキシフェニル基、ブトキシフェニル基、等の炭素数６以下の置換または無置換のアルキルオキシ基が置換した総炭素数１２以下のモノアルコキシアリール基；
２，３－ジメトキシフェニル基、２，４－ジメトキシフェニル基、２，５－ジメトキシフェニル基、２，６－ジメトキシフェニル基、３，４－ジメトキシフェニル基、３，５－ジメトキシフェニル基、３，６－ジメトキシフェニル基等の炭素数６以下の置換または無置換のアルキルオキシ基が置換した総炭素数１２以下のジアルコキシアリール基；および
クロロフェニル基、ジクロロフェニル基、トリクロロフェニル基、ブロモフェニル基、ジブロモフェニル基、ヨードフェニル基、フルオロフェニル基、クロロナフチル基、ブロモナフチル基、ジフルオロフェニル基、トリフルオロフェニル基、テトラフルオロフェニル基、ペンタフルオロフェニル基等のハロゲン原子が置換した総炭素数１２以下のアリール基が挙げられる。
　置換または無置換のアラルキル基として、ベンジル基、フェネチル基、フェニルプロピル基等の総炭素数１２以下のアラルキル基が挙げられる。
　置換または無置換のアルキルオキシ基として、メトキシ基、エトキシ基、ｎ－プロポキシ基、ｉｓｏ－プロポキシ基、ｎ－ブトキシ基、ｉｓｏ－ブトキシ基、ｔｅｒｔ－ブトキシ基、ｎ－ペンチルオキシ基、ｉｓｏ－ペンチルオキシ基、ｎ－ヘキシルオキシ基、ｉｓｏ－ヘキシルオキシ基等の総炭素数１以上６以下の直鎖または分岐のアルコキシ基；
シクロペンチルオキシ基、シクロヘキシルオキシ基等の総炭素数５または６のシクロアルコキシ基；および
メトキシメトキシ基、エトキシメトキシ基、エトキシエトキシ基、ｎ－プロポキシメトキシ基、ｉｓｏ－プロポキシメトキシ基、ｎ－プロポキシエトキシ基、ｉｓｏ－プロポキシエトキシ基、ｎ－ブトキシエトキシ基、ｉｓｏ－ブトキシエトキシ基、ｔｅｒｔ－ブトキシエトキシ基等の総炭素数２以上６以下のアルコキシアルコキシ基が挙げられる。
　置換または無置換のアルキルチオ基として、メチルチオ基、エチルチオ基、ｎ－プロピルチオ基、ｉｓｏ－プロピルチオ基、ｎ－ブチルチオ基、ｉｓｏ－ブチルチオ基、ｓｅｃ－ブチルチオ基、ｔ－ブチルチオ基、ｎ－ペンチルチオ基、ｉｓｏ－ペンチルチオ基、ｎ－ヘキシルチオ基、ｉｓｏ－ヘキシルチオ基等の総炭素数１以上６以下の直鎖または分岐のアルキルチオ基；
　シクロペンチルチオ基、シクロヘキシルチオ基等の総炭素数５または６のシクロアルキルチオ基；
　メトキシエチルチオ基、エトキシエチルチオ基、ｎ－プロポキシエチルチオ基、ｉｓｏ－プロポキシエチルチオ基、ｎ－ブトキシエチルチオ基、ｉｓｏ－ブトキシエチルチオ基、ｔｅｒｔ－ブトキシエチルチオ基等の総炭素数２以上６以下のアルコキシアルキルチオ基；および
　メチルチオエチルチオ基、エチルチオエチルチオ基、ｎ－プロピルチオエチルチオ基、ｉｓｏ－プロピルチオエチルチオ基、ｎ－ブチルチオエチルチオ基、ｉｓｏ－ブチルチオエチルチオ基、ｔｅｒｔ－ブチルチオエチルチオ基等の総炭素数２以上６以下のアルキルチオアルキルチオ基が挙げられる。
　置換または無置換のアリールオキシ基として、フェニルオキシ基、ナフチルオキシ基、２－メチルフェニルオキシ基、３－メチルフェニルオキシ基、４－メチルフェニルオキシ基、２－エチルフェニルオキシ基、プロピルフェニルオキシ基、ブチルフェニルオキシ基、ヘキシルフェニルオキシ基、シクロヘキシルフェニルオキシ基、２，４－ジメチルフェニルオキシ基、２，５－ジメチルフェニルオキシ基、２，６－ジメチルフェニルオキシ基、３，４－ジメチルフェニルオキシ基、３，５－ジメチルフェニルオキシ基、３，６－ジメチルフェニルオキシ基、２，３，４－トリメチルフェニルオキシ基、２，３，５－トリメチルフェニルオキシ基、２，３，６－トリメチルフェニルオキシ基、２，４，５－トリメチルフェニルオキシ基、２，４，６－トリメチルフェニルオキシ基、３，４，５－トリメチルフェニルオキシ基等の総炭素数１２以下の無置換またはアルキル置換アリールオキシ基；
２－メトキシフェニルオキシ基、３－メトキシフェニルオキシ基、４－メトキシフェニルオキシ基、２－エトキシフェニルオキシ基、プロポキシフェニルオキシ基、ブトキシフェニルオキシ基、ヘキシルオキシフェニルオキシ基、シクロヘキシルオキシフェニルオキシ基等の炭素数６以下の置換または無置換のアルキルオキシ基が置換した総炭素数１２以下のモノアルコキシアリールオキシ基；
２，３－ジメトキシフェニルオキシ基、２，４－ジメトキシフェニルオキシ基、２，５－ジメトキシフェニルオキシ基、２，６－ジメトキシフェニルオキシ基、３，４－ジメトキシフェニルオキシ基、３，５－ジメトキシフェニルオキシ基、３，６－ジメトキシフェニルオキシ基等の炭素数６以下の置換または無置換のアルキルオキシ基が置換した総炭素数１２以下のジアルコキシアリールオキシ基；および
クロロフェニルオキシ基、ジクロロフェニルオキシ基、トリクロロフェニルオキシ基、ブロモフェニルオキシ基、ジブロモフェニルオキシ基、ヨードフェニルオキシ基、フルオロフェニルオキシ基、クロロナフチルオキシ基、ブロモナフチルオキシ基、ジフルオロフェニルオキシ基、トリフルオロフェニルオキシ基、テトラフルオロフェニルオキシ基、ペンタフルオロフェニルオキシ基等のハロゲン原子が置換した総炭素数１２以下のアリールオキシ基が挙げられる。
　置換または無置換のアリールチオ基として、フェニルチオ基、ナフチルチオ基、２－メチルフェニルチオ基、３－メチルフェニルチオ基、４－メチルフェニルチオ基、２－エチルフェニルチオ基、プロピルフェニルチオ基、ブチルフェニルチオ基、ヘキシルフェニルチオ基、シクロヘキシルフェニルチオ基、２，４－ジメチルフェニルチオ基、２，５－ジメチルフェニルチオ基、２，６－ジメチルフェニルチオ基、３，４－ジメチルフェニルチオ基、３，５－ジメチルフェニルチオ基、３，６－ジメチルフェニルチオ基、２，３，４－トリメチルフェニルチオ基、２，３，５－トリメチルフェニルチオ基、２，３，６－トリメチルフェニルチオ基、２，４，５－トリメチルフェニルチオ基、２，４，６－トリメチルフェニルチオ基、３，４，５－トリメチルフェニルチオ基等の総炭素数１２以下の無置換またはアルキル置換アリールチオ基；
２－メトキシフェニルチオ基、３－メトキシフェニルチオ基、４－メトキシフェニルチオ基、２－エトキシフェニルチオ基、プロポキシフェニルチオ基、ブトキシフェニルチオ基、ヘキシルオキシフェニルチオ基、シクロヘキシルオキシフェニルチオ基等の炭素数６以下の置換または無置換のアルキルオキシ基が置換した総炭素数１２以下のモノアルコキシアリールチオ基；
２，３－ジメトキシフェニルチオ基、２，４－ジメトキシフェニルチオ基、２，５－ジメトキシフェニルチオ基、２，６－ジメトキシフェニルチオ基、３，４－ジメトキシフェニルチオ基、３，５－ジメトキシフェニルチオ基、３，６－ジメトキシフェニルチオ基、４，５－ジメトキシ－１－ナフチルチオ基、４，７－ジメトキシ－１－ナフチルチオ基、４，８－ジメトキシ－１－ナフチルチオ基、５，８－ジメトキシ－１－ナフチルチオ基、５，８－ジメトキシ－２－ナフチルチオ基等の炭素数６以下の置換または無置換のアルキルオキシ基が置換した総炭素数１２以下のジアルコキシアリールチオ基；
クロロフェニルチオ基、ジクロロフェニルチオ基、トリクロロフェニルチオ基、ブロモフェニルチオ基、ジブロモフェニルチオ基、ヨードフェニルチオ基、フルオロフェニルチオ基、クロロナフチルチオ基、ブロモナフチルチオ基、ジフルオロフェニルチオ基、トリフルオロフェニルチオ基、テトラフルオロフェニルチオ基、ペンタフルオロフェニルチオ基等のハロゲン原子が置換した総炭素数１２以下のアリールチオ基が挙げられる。
　Ｙのより好ましい例を以下に示す。
　Ｙのより好ましい例として、たとえば水素原子が挙げられる。
　また、ハロゲン原子として、塩素原子および臭素原子が挙げられる。
　置換または無置換のアルキル基として、メチル基、エチル基、ｉｓｏ－プロピル基等の総炭素数１以上３以下の直鎖または分岐アルキル基が挙げられる。
　置換または無置換のアリール基として、フェニル基、ナフチル基、シクロペンタジエニル基等の総炭素数１２以下の芳香族炭化水素；
２－メチルフェニル基、３－メチルフェニル基、４－メチルフェニル基、２－エチルフェニル基、プロピルフェニル基、２，３－ジメチルフェニル基、２，４－ジメチルフェニル基、２，５－ジメチルフェニル基、２，６－ジメチルフェニル基、３，４－ジメチルフェニル基、３，５－ジメチルフェニル基、３，６－ジメチルフェニル基等の総炭素数９以下のアルキル置換アリール基；
２－メトキシフェニル基、３－メトキシフェニル基、４－メトキシフェニル基、２－エトキシフェニル基、プロポキシフェニル基等の炭素数３以下の置換または無置換のアルキルオキシ基が置換した総炭素数９以下のモノアルコキシアリール基；および
クロロフェニル基、ジクロロフェニル基、トリクロロフェニル基、ブロモフェニル基、ジブロモフェニル基、クロロナフチル基、ブロモナフチル基等のハロゲン原子が置換した総炭素数１２以下のアリール基が挙げられる。
　置換または無置換のアラルキル基として、ベンジル基、フェネチル基、フェニルプロピル基等の総炭素数９以下のアラルキル基が挙げられる。
　置換または無置換のアルキルオキシ基として、メトキシ基、エトキシ基、ｉｓｏ－プロポキシ基等の総炭素数１以上３以下の直鎖または分岐のアルコキシ基；および
シクロペンチルオキシ基、シクロヘキシルオキシ基等の総炭素数５または６のシクロアルコキシ基が挙げられる。
　置換または無置換のアルキルチオ基として、メチルチオ基、エチルチオ基、ｎ－プロピルチオ基、ｉｓｏ－プロピルチオ基等の総炭素数１以上３以下の直鎖または分岐のアルキルチオ基；
シクロペンチルチオ基、シクロヘキシルチオ基等の総炭素数５または６のシクロアルキルチオ基；および
メチルチオエチルチオ基、エチルチオエチルチオ基、ｎ－プロピルチオエチルチオ基、ｉｓｏ－プロピルチオエチルチオ基、ｎ－ブチルチオエチルチオ基、ｉｓｏ－ブチルチオエチルチオ基、ｔｅｒｔ－ブチルチオエチルチオ基等の総炭素数２以上６以下のアルキルチオアルキルチオ基が挙げられる。
　置換または無置換のアリールオキシ基として、フェニルオキシ基、ナフチルオキシ基、２－メチルフェニルオキシ基、３－メチルフェニルオキシ基、４－メチルフェニルオキシ基、２－エチルフェニルオキシ基、プロピルフェニルオキシ基、２，４－ジメチルフェニルオキシ基、２，５－ジメチルフェニルオキシ基、２，６－ジメチルフェニルオキシ基、３，４－ジメチルフェニルオキシ基、３，５－ジメチルフェニルオキシ基、３，６－ジメチルフェニルオキシ基等の総炭素数９以下の無置換またはアルキル置換アリールオキシ基；
２－メトキシフェニルオキシ基、３－メトキシフェニルオキシ基、４－メトキシフェニルオキシ基、２－エトキシフェニルオキシ基、プロポキシフェニルオキシ基等の炭素数３以下の置換または無置換のアルキルオキシ基が置換した総炭素数９以下のモノアルコキシアリールオキシ基；および
クロロフェニルオキシ基、ジクロロフェニルオキシ基、トリクロロフェニルオキシ基、ブロモフェニルオキシ基、ジブロモフェニルオキシ基、クロロナフチルオキシ基、ブロモナフチルオキシ基等のハロゲン原子が置換した総炭素数１２以下のアリールオキシ基が挙げられる。
　置換または無置換のアリールチオ基として、フェニルチオ基、２－メチルフェニルチオ基、３－メチルフェニルチオ基、４－メチルフェニルチオ基、２－エチルフェニルチオ基、プロピルフェニルチオ基、２，４－ジメチルフェニルチオ基、２，５－ジメチルフェニルチオ基、２，６－ジメチルフェニルチオ基、３，４－ジメチルフェニルチオ基、３，５－ジメチルフェニルチオ基、３，６－ジメチルフェニルチオ基等の総炭素数９以下の無置換またはアルキル置換アリールチオ基；
２－メトキシフェニルチオ基、３－メトキシフェニルチオ基、４－メトキシフェニルチオ基、２－エトキシフェニルチオ基、プロポキシフェニルチオ基等の炭素数３以下の置換または無置換のアルキルオキシ基が置換した総炭素数９以下のモノアルコキシアリールチオ基；および
クロロフェニルチオ基、ジクロロフェニルチオ基、トリクロロフェニルチオ基、ブロモフェニルチオ基、ジブロモフェニルチオ基、クロロナフチルチオ基、ブロモナフチルチオ基等のハロゲン原子が置換した総炭素数１２以下のアリールチオ基が挙げられる。
　Ｙが環を形成しない場合、Ｙとして、さらに具体的には、メチル基、エチル基、プロピル基、イソプロピル基等の炭素数１以上３以下のアルキル基：および
メチルチオ基、エチルチオ基、ｎ－プロピルチオ基、ｉｓｏ－プロピルチオ基等のＳｂ原子に直接結合する硫黄原子を含み総炭素数１以上３以下の直鎖または分岐のアルキルチオ基が挙げられる。
　Ｙがアルキル基であるとき、上記一般式（３）において、Ｙは、好ましくはメチル基である。
　また、Ｙがアルキル基であり、ｎ－ｐが２以上の整数の場合、Ｙは互いに結合し、Ｓｂ原子を介して環状構造となっても構わない。つまり、複数のＹが結合してＳｂ原子を含む環を形成していてもよい。
　環を形成している場合、環を形成するアルキル鎖としては、メチレン基、エチレン基、プロピレン基、つまり炭素数１以上３以下のアルキレン基が挙げられる。環を形成するアルキル鎖は、好ましくは、エチレン基である。なお、Ｓｂ原子を含む環は、具体的には、４員環から６員環であり、環を構成する原子としては、ＳｂおよびＣ（炭素）の他に、後述のようにたとえばＳを含んでもよい。
　また、ＹがＳｂ原子に直接結合する硫黄原子を含むチオアルキル基であるとき、上記一般式（３）に示される化合物の例として、下記一般式（１０）に示される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000016
（上記一般式（１０）中、Ｘ1およびｎは、それぞれ、上記一般式（３）におけるＸ1およびｎと同じである。ｐは２以上（ｎ－１）以下の整数である。
　ｎ－ｐが１の場合、Ｒ2は、置換基を有してもよい炭素数１以上３以下の直鎖状もしくは分岐鎖を有するアルキル基を表す。
　ｎ－ｐが２以上の場合、複数のＲ2は、各々独立に、置換基を有してもよい炭素数１以上３以下の直鎖状もしくは分岐鎖を有するアルキル基または単結合を表す。また、複数のＲ2が互いに結合してＳｂ原子を含む環を形成してもよく、この場合、環を形成するアルキル鎖は炭素数１以上３以下であり、環を構成する部分には、硫黄原子を含まない。）
　上記一般式（１０）においても、樹脂の屈折率を向上させる観点では、Ｘ1が硫黄原子であることが好ましい。このとき、上記一般式（１０）は、下記一般式（１１）となる。
Figure JPOXMLDOC01-appb-C000017
（上記一般式（１１）中、ｐ、ｎおよびＲ2は、それぞれ、上記一般式（１０）におけるｐ、ｎおよびＲ2と同じである。）
　上記一般式（１０）および（１１）において、ｎはＳｂ原子の価数である。また、上記一般式（１０）および（１１）において、ｐは、（Ｓｂ原子の価数－１）以下の正の整数である。つまり、ｐは２以上（ｎ－１）以下の整数である。
　上記一般式（１０）および（１１）において、Ｒ2は、置換基を有してもよい炭素数１以上３以下の直鎖状もしくは分岐鎖を有するアルキル基を表す。
　ｎ－ｐが２以上の場合、Ｒ2は、各々独立に置換基を有してもよい炭素数１以上３以下の直鎖状もしくは分岐鎖を有するアルキル基を表す。複数のＲ2は、同じ基であってもよいし、全部または一部が異なる基であってもよい。また、複数のＲ2が互いに結合し、原子団－Ｓ－Ｓｂ－Ｓ－を含む環を形成してもよい。この場合、環を形成するアルキル鎖は炭素数１以上３以下であり、硫黄原子は、Ｓｂ原子に直接結合しているもののみである。つまり、Ｒ2のうち、環を構成する部分には硫黄原子を含まない。
　上記一般式（１０）および（１１）で表される化合物の中でも好ましい例の一つとして、以下の態様が挙げられる。すなわち、Ｒ2が環を形成しない場合、Ｒ2として、具体的には、メチル基、エチル基、プロピル基、イソプロピル基、つまり炭素数１以上３以下のアルキル基が挙げられる。
　また、上記一般式（１０）および（１１）で表される化合物の別の好ましい例として、ｎ－ｐ＝２であり、二つの－Ｓ－Ｒ2基が、Ｓに隣接するＳｂ原子とともに原子団－Ｓ－Ｓｂ－Ｓ－を含む環を形成しており、環を形成するアルキル鎖が、メチレン基、エチレン基、プロピレン基、つまり炭素数１以上３以下のアルキレン基であるものが挙げられる。Ｓｂ原子を含む環は、具体的には、４員環から６員環である。なお、Ｓｂ原子を含む環が４員環のとき、二つのＲ2のうちの一つは、具体的には単結合である。
　さらに具体的には、環を形成しない場合、Ｒ2はメチル基であり、また環を形成する場合は環を形成するアルキル鎖はエチレン基である。
　次に、上記一般式（６）中、ｒ＝２の場合について、ｒ＝１の場合と異なる点を中心に説明する。以下で特に説明しない基や記号については、ｒ＝１の場合に上記一般式（３）等を参照して前述した場合と同様である。
　ｒ＝２のとき、ｎ－ｐ－ｑ＝１または２であり、Ｙは両端がそれぞれ異なるＳｂ原子に結合する２価の基である。
　Ｙは有機基であることが好ましく、その具体例として、Ｒ1として例示した２価の有機基が挙げられる。また、Ｙとして、他に、－Ｓ－Ｒ3－Ｓ－基が挙げられる。上記基中、Ｒ3は、メチレン基または炭素数２以上５以下のアルキレン基である。なお、ｒ＝２かつｎ－ｐ－ｑ＝２の場合、２つのＹは、同じ基あってもよいし、異なっていてもよい。また、ｒ＝２かつｎ－ｐ－ｑ＝２の場合、２つのＳｂ原子とともに環を形成していてもよい。
　ｒ＝２のとき、上記一般式（６）において、Ｔは、無機または有機基を表す。ｒ＝２かつｑ＝２の場合、複数のＴは、各々独立に無機または有機基を表す。複数のＴは同じ基であってもよいし、異なる基であってもよい。
　Ｔは、有機基であることが好ましく、その具体例としては、ｒ＝１の場合にＹとして例示した１価の基が挙げられる。
　なお、ｒ＝２の場合において、ｍ＝０であることが好ましい。このとき、上記一般式（６）は、下記一般式（１２）に示される。
Figure JPOXMLDOC01-appb-C000018
（上記一般式（１２）において、Ｘ1、Ｙ、Ｔ、ｎ、ｐ、ｑおよびｒは、それぞれ、上記一般式（６）におけるＸ1、Ｙ、Ｔ、ｎ、ｐ、ｑおよびｒと同じである。）
　また、ｒ＝２の場合において、ｍ＝０であり、Ｘ1が硫黄原子であることがさらに好ましい。このとき、上記一般式（６）は、下記一般式（１３）に示される。
Figure JPOXMLDOC01-appb-C000019
（上記一般式（１３）において、Ｙ、Ｔ、ｎ、ｐ、ｑおよびｒは、それぞれ、上記一般式（６）におけるＹ、Ｔ、ｎ、ｐ、ｑおよびｒと同じである。）
　上記一般式（６）に示した化合物の具体例としては、以下の化合物が挙げられる。
　まず、上記一般式（６）において、ｒ＝１の場合、上記式（４）および（９）に示した化合物が挙げられる他、以下の化合物が例示される。
Figure JPOXMLDOC01-appb-C000020
　また、ｒ＝２の場合、以下の化合物が例示される。
Figure JPOXMLDOC01-appb-C000021
　以上、ＭがＳｂ原子である場合を例に説明したが、上記一般式（２）においても、各置換基等は、ＭがＳｂ原子である場合に準じて選択される。
　また、上記一般式（１２）および（１３）は、上記一般式（２）に対応して、それぞれ下記一般式（１４）および（１５）に一般化することができる。
Figure JPOXMLDOC01-appb-C000022
Figure JPOXMLDOC01-appb-C000023
（上記一般式（１４）および（１５）において、Ｍ、Ｘ1、Ｙ、Ｔ、ｎ、ｐ、ｑおよびｒは、それぞれ、上記一般式（２）におけるＭ、Ｘ1、Ｙ、Ｔ、ｎ、ｐ、ｑおよびｒと同じである。）
　上記一般式（１４）で示される化合物として、たとえば以下のものが挙げられる。
Figure JPOXMLDOC01-appb-C000024
　なお、上記一般式（２）～（１５）において、金属原子Ｍの価数ｎは、具体的には、２以上５以下である。
　ｎ＝２のとき、金属原子Ｍの例として、たとえばＴｉ（チタン）、Ｖ（バナジウム）、Ｚｎ（亜鉛）、ＳｎおよびＰｂ（鉛）が挙げられ、ＺｎおよびＳｎが好ましい。
ｎ＝３のとき、Ｍの例としてＳｃ（スカンジウム）、Ｙ（イットリウム）、Ｌａ（ランタン）、Ｔｉ、Ｖ、Ｎｂ（ニオブ）、Ｔａ（タンタル）、Ｓｂ、Ｂｉ（ビスマス）、Ｉｎ（インジウム）、Ｇａ（ガリウム）およびＡｌ（アルミニウム）が挙げられ、Ｓｂ、Ｙ、Ｌａ、Ｂｉ、ＩｎおよびＡｌが好ましい。
ｎ＝４のとき、Ｍの例としてＴｉ、Ｚｒ（ジルコニウム）、Ｈｆ（ハフニウム）、Ｎｂ、Ｔａ、Ｓｉ（ケイ素）、Ｇｅ（ゲルマニウム）、ＳｎおよびＰｂが挙げられ、Ｓｎ、ＴｉおよびＺｒが好ましい。
また、ｎ＝５のとき、Ｍの例として、Ｎｂ、ＴａおよびＳｂが挙げられる。
　ｎ＝２～５のとき、本発明において用いられる金属チエタン化合物の具体例として、以下のものが挙げられる。
Figure JPOXMLDOC01-appb-C000025
　また、上記一般式（２）に示した化合物の具体例として、ｎ＝ｐ＝４である化合物が挙げられ、さらに具体的には、下記式（５）に示される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000026
　なお、本発明において用いられる金属チエタン化合物の別の態様として、金属原子Ｍに配位子が配位しているものもある。つまり、上記一般式（２）に示した金属チエタン化合物は、さらに配位結合によって金属原子と結合する配位性化合物を含んでもよい。
　配位性化合物は、分子内に１つ以上の金属に配位する配位性官能基を含有する。また、配位性化合物は、たとえば上記一般式（２）で表される化合物に配位するものであればいかなる構造を有する化合物でも使用できるが、好ましくは窒素、酸素、リン、硫黄原子等のヘテロ原子で金属に配位する化合物である。
　窒素原子で配位する配位子の具体的化合物例としてはアンモニア、メチルアミン、エチルアミン、プロピルアミン、イソプロピルアミン、ジメチルアミン、ジエチルアミン、ジ－プロピルアミン、ジ－イソプロピルアミン、トリメチルアミン、トリエチルアミン、エチレンジアミン、プロピレンジアミン、ジメチルエチレンジアミン、テトラメチルエチレンジアミン、ヒドラジン、メチルヒドラジン、ジメチルヒドラジン、アニリン、フェニルヒドラジン、ｏ－フェニレンジアミン、ヒドロキシルアミン、システアミン、アミノエタノール、グリシン等のアンモニアおよびアミン化合物；
ピリジン、２，２'－ビピリジン、１，１０－フェナントロリン等のピリジン化合物；
ピリダジン、ピリミジン、プリン、ピラジン、１，８－ナフチリジン、ピラゾ－ル、イミダゾ－ル等の窒素複素環化合物；
ジメチルホルムアミド、ジメチルイミダゾリジノン等のアミド化合物；
アセトニトリル、プロピオニトリル等のニトリル化合物等を挙げることができる。
　リン原子で配位する配位子の具体的化合物例としてはトリフェニルホスフィン、トリメチルホスフィン、トリエチルホスフィン、１，２－ビス（ジメチルホスフィノ）エタン、ビス（ジメチルホスフィノ）メタン等のホスフィン化合物等を挙げることができる。
　酸素原子で配位する配位子の具体的化合物例としては、水、メタノール、エタノール、プロパノール、イソプロパノール、エチレングリコール、プロピレングリコール、１，３－プロパンジオール等の水およびアルコール化合物；
テトラヒドロフラン、１，４－ジオキサン、ジメトキシエタン、エチレングリコールモノメチルエーテル等のエーテル化合物；
アセトン、メチルエチルケトン等のケトン化合物；
酢酸エチル、酢酸メチル、ギ酸メチル、ギ酸エチル等のエステル化合物；
ジメチルスルホキシド、スルホラン等のスルホキシド化合物およびスルホン化合物等を挙げることができる。
　硫黄原子で配位する配位子の具体的化合物例としては、ジメチルスルフィド、ジエチルスルフィド、テトラヒドロチオフェン等のスルフィド化合物等を挙げることができるが、例示化合物のみに限定されるものではない。
　これら例示した配位性化合物のうち、好ましくはアンモニア、エチレンジアミン、テトラメチルエチレンジアミン、ヒドロキシルアミン等のアンモニアおよびアミン化合物；
ピリジン、２，２'－ビピリジン等のピリジン化合物；
テトラヒドロフラン、ジメトキシエタン等のエーテル化合物等が挙げられる。
　より好ましくはアンモニアおよびエチレンジアミンである。
　次に、本発明において用いられる金属チエタン化合物の製造方法について、上記一般式（６）に示した金属チエタン化合物の製造方法を例に説明する。
　まず、上記一般式（６）においてｒ＝１の場合について説明する。このとき、上記一般式（６）は、上記一般式（３）となる。
　上記一般式（３）に示した金属チエタン化合物は、代表的には、下記一般式（１６）で示されるＳｂ原子を含むハロゲン化物と、下記一般式（１７）で表されるチエタン基を有するヒドロキシ化合物またはチオール化合物との反応により製造される。
Figure JPOXMLDOC01-appb-C000027
（上記一般式（１６）中、ｎ、ｐおよびＹは、それぞれ、上記一般式（３）におけるｎ、ｐおよびＹに同じであり、Ｚはハロゲン原子を表す。）
Figure JPOXMLDOC01-appb-C000028
（上記一般式（１７）中、Ｘ1、Ｘ2、Ｒ1およびｍは、それぞれ、上記一般式（３）におけるＸ1、Ｘ2、Ｒ1およびｍに同じである。）
　また、上記一般式（１１）で表される化合物についても、上記一般式（３）で表される化合物の製造方法に準じた方法で製造できる。
　たとえば、下記一般式（１８）で示されるハロゲン化物と、上記一般式（１７）で表されるチエタン基を有するヒドロキシ化合物またはチオール化合物との反応により製造される。
Figure JPOXMLDOC01-appb-C000029
（上記一般式（１８）中、ｐ、ｎおよびＲ2は、それぞれ、上記一般式（６）におけるｐ、ｎおよびＲ2に同じであり、Ｚはハロゲン原子を表す。）
　また、上記一般式（１８）においてｎ＝ｐであるハロゲン化物と、上記一般式（１７）で表されるチエタン基を有するヒドロキシ化合物またはチオール化合物と、下記一般式（１９）で示されるチオール化合物とを一括混合し、同時に反応させても製造される。
Ｒ2－ＳＨ　（１９）
（上記一般式（１９）中、Ｒ2は、上記一般式（６）におけるＲ2に同じである。）
　また、上記一般式（１８）においてｎ＝ｐであるハロゲン化物と上記一般式（１７）で表されるチエタン基を有するヒドロキシ化合物またはチオール化合物とをあらかじめ反応させて得られた化合物と、上記一般式（１９）で表されるチオール化合物とを反応することによっても製造される。
　なお、上記一般式（３）に示した金属チエタン化合物は、金属ハロゲン化物を用いる方法以外の方法によっても製造できる。たとえば、金属酸化物または金属アミド化物を原料に用いて、上記一般式（１７）で表される化合物を反応させることによっても上記一般式（３）に示した金属チエタン化合物を製造できる。
　上記一般式（１６）、（１８）および（１９）に示した化合物は、工業用原料または研究用試薬として入手可能である。
　また、上記一般式（１７）で表される化合物は公知化合物であって、たとえば、特許文献２（特開２００３－３２７５８３号公報）に記載の方法に準じて製造される。
　上記一般式（１６）で示されるＳｂを含むハロゲン化物と、上記一般式（１７）で表されるチエタン基を有するヒドロキシ化合物またはチオール化合物との反応は無溶媒で行ってもよく、あるいは、反応に不活性な溶媒の存在下に行ってもよい。
　かかる溶媒としては、反応に不活性な溶媒であれば特に限定するものではなく、石油エーテル、ヘキサン、ベンゼン、トルエン、キシレン、メシチレンなどの炭化水素系溶媒；
ジエチルエーテル、テトラヒドロフラン、ジエチレングリコールジメチルエーテルなどのエーテル系溶媒；
アセトン、メチルエチルケトン、メチルイソブチルケトンなどのケトン系溶媒；
酢酸エチル、酢酸ブチル、酢酸アミルなどのエステル系溶媒；
塩化メチレン、クロロホルム、クロルベンゼン、ジクロルベンゼンなどの含塩素系溶媒；
Ｎ，Ｎ－ジメチルホルムアミド、Ｎ，Ｎ－ジメチルアセトアミド、Ｎ，Ｎ－ジメチルイミダゾリジノン、ジメチルスルホキシドなどの非プロトン性極性溶媒；
テトラヒドロチオフェン、チオフェン、スルホラン、トリメチレンスルフィド、ジエチルスルフィド、ジ－ｎ－プロピルスルフィド、ジ－ｔ－ブチルスルフィド、３－メルカプトチエタン、ビス（２－メルカプトエチル）スルフィドなどの含硫系溶媒；および
水などが例示される。
　上記一般式（１６）に示した化合物と上記一般式（１７）に示した化合物の反応温度は、特に制限するものではないが、通常、－７８℃以上２００℃以下の範囲であり、好ましくは、－７８℃以上１００℃以下である。
　また、反応時間は反応温度により影響されるが、通常、数分から１００時間である。
　上記一般式（１６）に示した化合物と上記一般式（１７）に示した化合物の反応における、上記一般式（１６）で表される化合物と上記一般式（１７）で表される化合物の使用量は、特に限定するものではないが、通常、上記一般式（１６）で表される化合物中に含有されるハロゲン原子１モルに対して、上記一般式（１７）で表される化合物の使用量は、０．０１モル以上１００モル以下である。好ましくは、０．１モル以上５０モル以下であり、より好ましくは、０．５モル以上２０モル以下である。
　上記一般式（１６）に示した化合物と上記一般式（１７）に示した化合物の反応を実施するに際し、反応を効率よく行うために、生成するハロゲン化水素の捕捉剤として塩基性化合物を用いることは好ましい。
　かかる塩基性化合物として、たとえば、水酸化ナトリウム、水酸化カリウム、水酸化リチウム、炭酸ナトリウム、炭酸カリウム、炭酸リチウム、重炭酸ナトリウム、重炭酸カリウム、重炭酸リチウム、水酸化マグネシウム、水酸化カルシウムなどの無機塩基；および
ピリジン、トリエチルアミン、ジメチルアニリン、ジエチルアニリン、１，８－ジアザビシクロ［５，４，０］－７－ウンデセンなどの有機塩基が例示される。
　また、上記一般式（６）において、ｒ＝２の場合にも、ｒ＝１の場合について前述した方法に準じて得ることができる。
　以上、金属原子ＭがＳｂ原子である場合を例に挙げて説明したが、本発明において、他の金属原子を含む金属チエタン化合物についても、上述した方法に準じて製造することができる。
　上記一般式（２）に示した金属チエタン化合物は、重合性化合物である。このため、本発明の重合性組成物が、重合性化合物として上記式（３０）および上記一般式（２）に示した化合物を含むとともに、当該重合性化合物が上記一般式（２）に示した金属チエタン化合物から主として構成されていてもよい。たとえば、本発明の重合性組成物中の重合性化合物が、上記一般式（６）に示した金属チエタン化合物から主として構成されていてもよい。
　また、本発明の重合性組成物中の重合性化合物が上記一般式（２）に示した金属チエタン化合物を含むとき、上記一般式（２）に示した金属チエタン化合物に加えて、他の重合性化合物を含んでいてもよい。たとえば、本発明の重合性組成物中の重合性化合物が、上記一般式（６）に示した金属チエタン化合物に加えて、他の重合性化合物を含んでいてもよい。
　本発明の重合性組成物中に含まれる重合性化合物の総重量に占める、上記一般式（２）（たとえば、上記一般式（６））で表される化合物の含有量は、特に限定するものではないが、通常、１０重量％以上であり、高屈折率化の観点から、好ましくは、３０重量％以上であり、より好ましくは、５０重量％以上であり、さらに好ましくは、７０重量％以上である。
　また、上記一般式（２）（たとえば、上記一般式（６））で表される化合物以外の成分は、重合性組成物を用いた樹脂の屈折率を下げる要因となる場合が多いため、屈折率の高い樹脂を得る観点から、重合性化合物の総重量に占める一般式（２）（たとえば、上記一般式（６））で表される化合物の含有量を５０重量％以上とすることが好ましい。
　また、本発明における重合性組成物は、以下の金属チエタン化合物を含んでもよい。
メチルチオトリス（チエタニルチオ）スズ、エチルチオトリス（チエタニルチオ）スズ、プロピルチオトリス（チエタニルチオ）スズ、イソプロピルチオトリス（チエタニルチオ）スズ等のアルキルチオ（チエタニルチオ）スズ；
ビス（メチルチオ）ビス（チエタニルチオ）スズ、ビス（エチルチオ）ビス（チエタニルチオ）スズ、ビス（プロピルチオ）ビス（チエタニルチオ）スズ、ビス（イソプロピルチオ）ビス（チエタニルチオ）スズ等のビス（アルキルチオ）ビス（チエタニルチオ）スズ；
エチルチオ（メチルチオ）ビス（チエタニルチオ）スズ、メチルチオ（プロピルチオ）ビス（チエタニルチオ）スズ、イソプロピルチオ（メチルチオ）ビス（チエタニルチオ）スズ、エチルチオ（プロピルチオ）ビス（チエタニルチオ）スズ、エチルチオ（イソプロピルチオ）ビス（チエタニルチオ）スズ、イソプロピルチオ（プロピルチオ）ビス（チエタニルチオ）スズ等のアルキルチオ（アルキルチオ）ビス（チエタニルチオ）スズ；
ビス（チエタニルチオ）ジチアスタンネタン、ビス（チエタニルチオ）ジチアスタンノラン、ビス（チエタニルチオ）ジチアスタンニナン、ビス（チエタニルチオ）トリチアスタンノカン等のビス（チエタニルチオ）環状ジチオスズ化合物：
メチルトリス（チエタニルチオ）スズ、ジメチルビス（チエタニルチオ）スズ、ブチルトリス（チエタニルチオ）スズ等のアルキル（チエタニルチオ）スズ化合物：
テトラキス（チエタニルチオ）スズ、テトラキス（チエタニルチオ）ゲルマニウム、トリス（チエタニルチオ）ビスマス等の金属チエタン化合物等。
　また、チエタン化合物として、ビスチエタニルジスルフィド、ビスチエタニルテトラスルフィド、ビス（チエタニルチオ）メタン、３－（（（チエタニルチオ）メチルチオ）メチルチオ）チエタン、テトラキス（チエタニルチオ）スズ、トリス（チエタニルチオ）ビスマス、ビス（チエタニルチオ）ジチアスタンノランからなる群から選択される一種以上を選択することが好ましい。
　また、好ましい化合物としては、ビスチエタニルスルフィド、ビス（チエタニルチオ）メタン、ビスチエタニルジスルフィド、ビスチエタニルテトラスルフィド、ビス（チエタニルチオ）ジチアスタンノランおよびテトラキス（チエタニルチオ）スズであり、より好ましい化合物としてはビスチエタニルジスルフィド、ビス（チエタニルチオ）ジチアスタンノランおよびテトラキス（チエタニルチオ）スズである。
　また、重合性組成物が上記式（３０）に示した化合物と上記一般式（２）に示した化合物を含むとき、さらに、チオール化合物、エポキシ化合物、エピチオ化合物、分子構造中に金属原子を含まない非金属チエタン化合物のうち少なくとも一つを含んでもよい。
　このとき、重合性組成物中に含まれる他の成分の組み合わせの具体例として、チオール化合物が、２－メルカプトチエタン、３－メルカプトチエタン、１，２－エタンジチオール、４－メルカプトメチル－１，８－ジメルカプト－３，６－ジチアオクタン、４，８－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、２，５－ビス（メルカプトメチル）－１，４－ジチアンおよび１，５－ジメルカプト-３－チアペンタンからなる群から選択される一種以上であり、エポキシ化合物が、ビス（２，３－エポキシプロピル）ジスルフィド、エチレングリコールジグリシジルエーテル、イソシアヌル酸トリグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、１，４－シクロヘキサンジメタノールジグリシジルエーテル、トリメチロールプロパントリグリシジルエーテル、ビスフェノールＦジグリシジルエーテル、ビスフェノールＡジグリシジルエーテル、３，４－エポキシシクロヘキシルメチル－３'，４'－エポキシシクロヘキサンカルボキシレートおよび１，５－ビス（グリシジルチオ）－３－チアペンタンからなる群から選択される一種以上であり、エピチオ化合物が、ビス（２，３－エピチオプロピル）スルフィド、ビス（２，３－エピチオプロピル）ジスルフィドからなる群から選択される一種以上であり、非金属チエタン化合物が、ビスチエタニルジスルフィド、ビスチエタニルテトラスルフィド、ビス（チエタニルチオ）メタン、３－（（（チエタニルチオ）メチルチオ）メチルチオ）チエタンからなる群から選択される一種以上である組み合わせが挙げられる。また、このとき、重合性組成物が、テトラキス（チエタニルチオ）スズ、トリス（チエタニルチオ）ビスマス、ビス（チエタニルチオ）ジチアスタンノランを含んでいてもよい。
　また、エポキシ化合物として、下記式に示す化合物の一種以上を用いてもよい。
Figure JPOXMLDOC01-appb-C000030
　重合性組成物において、上記一般式（２）で表される化合物に対するイソシアネート化合物、前記式（３０）に示した化合物以外の活性水素化合物、エポキシ化合物、エピチオ化合物および非金属チエタン化合物の含有量は、屈折率の観点では、エポキシ化合物の含有量は少なく、チオール化合物、エピチオ化合物およびチエタン化合物の含有量は多い方が好ましい場合がある。また樹脂色相の観点では、チオール化合物の含有量が多い方が好ましい場合がある。
　重合性組成物において、上記一般式（２）で表される化合物、イソシアネート化合物、前記式（３０）に示した化合物以外の活性水素化合物、エポキシ化合物、エピチオ化合物および非金属チエタン化合物の合計１００重量部に対する、チオール化合物、エポキシ化合物、エピチオ化合物および非金属チエタン化合物の合計は、たとえば１重量部以上５０重量部以下である。
　また、本発明における重合性組成物に含まれる他の重合性化合物としては、公知の各種重合性モノマーまたは重合性オリゴマーが挙げられ、たとえば、（メタ）アクリル酸エステル化合物、ビニル化合物、オキセタン化合物などが挙げられる。
　また、本発明の重合性組成物は、必要に応じて、重合速度を調整するため公知公用の重合触媒をさらに含んでいてもよい。
　また、本発明の重合性組成物は、必要に応じて、ブルーイング剤を含んでもよい。ブルーイング剤は、可視光領域のうち橙色から黄色の波長域に吸収帯を有し、樹脂の色相を調整する機能を有する。ブルーイング剤は、さらに具体的には、青色から紫色を示す物質を含む。
　本発明の重合性組成物に用いられるブルーイング剤は、特に限定されるものではなく、具体的には、染料、蛍光増白剤、蛍光顔料、無機顔料等が挙げられるが、ブルーイング剤として使用できるものの中からレンズに要求される物性や樹脂色相などに合わせて適宜選択される。これらのブルーイング剤は、それぞれ単独で用いても、２種類以上組み合わせて使用してもよい。
　これらのブルーイング剤のうち、重合性組成物への溶解性の観点および得られる樹脂の透明性の観点からは、染料が好ましい。染料の中でも、ブルー系染料およびバイオレット系の染料から選ばれる１種または２種以上の染料を含む染料であることが好ましいが、場合によっては他の色の染料を混合して用いてもよい。たとえば、ブルー系やバイオレット系のほかに、グレー系やブラウン系やレッド系、オレンジ系の染料も使用することができる。こうしたブルーイング剤の組み合わせの具体例として、ブルー系染料とレッド系染料との組み合わせ、およびバイオレット系染料とレッド系染料の組み合わせ等が挙げられる。
　吸収波長の観点からは、好ましくは、極大吸収波長が５２０ｎｍ以上６００ｎｍ以下の染料であり、さらに好ましくは極大吸収波長が５４０ｎｍ以上５８０ｎｍ以下の染料が挙げられる。
　また、化合物の構造の観点からは、アントラキノン系染料が好ましい。
　染料として、具体的には、「PS Blue RR」、「PS Violet RC」、「PET Blue 2000」、「PS Brilliant Red HEY」、「MLP RED V-1」（それぞれ、ダイスタージャパン社の商品名）等が挙げられる。
　ブルーイング剤の使用量は、モノマーの種類、各種添加剤の使用の有無、使用する添加剤の種類や量、重合方法、重合条件によっても異なるが、一般にはモノマーの全体使用量、つまり重合組成物中に含まれる重合性化合物の総重量に対して０．００１ｐｐｍ以上５００ｐｐｍ以下の割合で、好ましくは０．００５ｐｐｍ以上１００ｐｐｍ以下の割合で、さらに好ましくは０．０１ｐｐｍ以上１０ｐｐｍ以下の割合で使用される。ブルーイング剤の添加量が多すぎると、レンズ全体が青くなりすぎて好ましくない場合があり、また少なすぎると、色相改善効果が十分に発揮されず好ましくない場合がある。
　ブルーイング剤の添加方法については、特に限定されるものではなく、あらかじめモノマー系に添加しておくことが望ましいが、その方法として、モノマーに溶解させておく方法、あるいは、高濃度のブルーイング剤を含有したマスター溶液を調製しておき、そのマスター溶液を使用するモノマーや他の添加剤で希釈して添加する方法など、様々な方法が採用できる。
　さらに、樹脂の改良や取り扱い性を改良する目的で、本発明の重合性組成物に精製や洗浄、保温、保冷、ろ過、減圧処理などの有機化合物を合成する際に一般的に用いられる手法、操作を施したり、また、公知の化合物等を安定剤や樹脂改質剤として加えたりすることは好ましい場合がある。
　樹脂の改良や取り扱い性の改良とは、重合性組成物を硬化してなる樹脂の屈折率、アッベ数等の光学物性のさらなる調整や、色相、耐光性や耐候性、耐熱性、耐衝撃性、硬度、比重、線膨張係数、重合収縮率、吸水性、吸湿性、耐薬品性、粘弾性等の諸物性の調整、透過率や透明性の調整、重合性組成物の粘度の調整、その他保存や輸送方法の取り扱い性を調整することである。
　長期の保存安定性や、重合安定性、熱安定性などの安定性向上のために加えられるものとしては、重合遅延剤や重合禁止剤、脱酸素剤、酸化防止剤などの化合物が挙げられる。
　重合性組成物を精製するのは、硬化して得られる樹脂の透明性を改良したり、色相を改良するためや純度を上げるために用いられる手法である。本発明の重合性組成物を精製する際には、公知の方法、たとえば、再結晶、カラムクロマト法（シリカゲル法や活性炭法、イオン交換樹脂法など）、抽出などのいかなる手法をいかなるタイミングで行ってもよく、一般に精製して得られる組成物を硬化させて得られる樹脂の透明性や色相が改良されていればよい。
　重合性組成物を洗浄する方法は、硬化して得られる樹脂の透明性を改良したり、色相を改良するのに用いられる手法であるが、重合性組成物を合成して取り出す際または合成後の取り出した後などのタイミングで極性および／または非極性溶媒で洗浄し、樹脂の透明性を阻害する物質、たとえば、重合性組成物を合成する際に使用されるまたは、副生する無機塩、たとえば、アンモニウム塩などを取り除くまたは減量する方法が挙げられる。用いる溶媒は、洗浄される重合性組成物そのものや重合性組成物を含有する溶液の極性等により一概に限定はできないが、取り除きたい成分を溶解可能で、かつ、洗浄される重合性組成物そのものや重合性組成物を含有する溶液と相溶しにくいものが好ましく、一種類のみならず、２種類以上を混合して使用してもよい。ここで取り除く成分は目的や用途に応じて異なるが、なるべく少なくしておくことが好ましく、通常５０００ｐｐｍ以下、より好ましくは１０００ｐｐｍ以下とすると良い結果が得られる場合がある。
　重合性組成物を保温・保冷・ろ過する方法は、硬化して得られる樹脂の透明性を改良したり、色相を改良するのに用いられる手法であるが、重合性組成物を合成して取り出す際または合成後の取り出した後などのタイミングで行うのが一般的である。保温方法としては、たとえば、重合性組成物が保管中に結晶化し、ハンドリングが悪くなった場合に、重合性組成物および重合性組成物を硬化させてなる樹脂の性能が低下しない範囲で加熱溶解する方法が挙げられる。加熱する温度範囲や加熱溶解する方法は、取り扱われる重合性組成物を構成する化合物の構造により一概に限定できないが、通常、凝固点＋５０℃以内の温度で行われ、好ましくは＋２０℃以内であり、攪拌可能な装置で機械的に攪拌したり、組成物に不活性なガスでバブリングすることで内液を動かし溶解する方法などが挙げられる。保冷とは重合性組成物の保存安定性を高める目的で通常行われるが、たとえば重合性組成物の融点が高い場合には、結晶化後の取り扱い性を向上させるため、保管温度を考慮するとよい。保冷温度は取り扱われる重合性組成物を構成する化合物の構造、保存安定性により一概に限定できないが、通常は、本発明の重合性組成物の安定性が維持できる温度以下で保存する必要がある。
　また、本発明の重合性組成物が、光学用途に用いる重合性組成物の場合、その非常に高い透明性を要求されることから、通常重合性組成物を孔径の小さいフィルターでろ過するとよい。ここで用いるフィルターの孔径は通常０．０５μｍ以上１０μｍ以下で行われるが、操作性や性能を考慮すれば、好ましくは、０．０５μｍ以上５μｍ以下であり、より好ましくは０．１μｍ以上５μｍ以下である。本発明の重合性組成物も例外でなくろ過すると良い結果が得られる場合が多い。ろ過する温度については、凝固点付近の低温で行うとさらに好ましい結果が得られる場合があるが、ろ過中に凝固が進行するような場合は、ろ過作業に支障を来さない温度で行うと良い場合がある。
　減圧処理は、一般的に重合性組成物を硬化させてなる樹脂の性能を低下させる溶媒や溶存ガス、臭気を取り除くのに行われる手法である。溶存溶媒は一般に得られる樹脂の屈折率低下や耐熱性低下を招くことがあるため、可能な限り取り除くとよい。溶存溶媒の許容値は、取り扱われる重合性組成物を構成する化合物の構造、溶存する溶媒の構造により一概に限定できないが、通常１％以下とするのが好ましく、より好ましくは、５０００ｐｐｍ以下である。溶存ガスは重合の阻害を抑制する観点および得られる樹脂に気泡が混入するのを抑制する観点から、取り除く方が好ましい。特に、水蒸気などの水分を意味するガスについては、とりわけ乾燥ガスでバブリングするなどして除去した方が好ましい。溶存量については、重合性組成物を構成する化合物の構造、溶存するガスの物性および構造、種類に応じて設定できる。
　本発明における重合性組成物の製造方法として、代表的には、上記一般式（２）（たとえば、上記一般式（６））に示した化合物と、必要に応じて上記の他の各種重合性化合物、重合触媒、添加剤等を一括で仕込んだ混合物を加熱溶解調合すれば良い。ただし併用する重合性化合物、重合触媒、添加剤等の種類によっては一括で仕込んで加熱溶解させる過程で混合物が高粘度化して、続く減圧濾過、脱気、成形用モールドへの注型操作が不可能になる場合がある。たとえば、重合性化合物として、エポキシ化合物とチオール化合物を併用する場合などは、上述の一括仕込み加熱溶解調合方法では、加熱溶解時に高粘度化する場合がある。
　このような場合は、たとえば下記（ｉ）（ｉｉ）に示す段階的な調合方法により調合時の高粘度化を回避して重合性組成物の調製が可能である。
（ｉ）エポキシ化合物とチオール化合物を最初に仕込んで混合する。引き続いて、上記一般式（２）（たとえば、上記一般式（６））に示した化合物を添加して加熱溶解する。
（ｉｉ）チオール化合物および上記一般式（２）（たとえば、上記一般式（６））に示した化合物を最初に仕込んで加熱溶解させた後、モノマーが析出することのない温度付近まで冷却してエポキシ化合物を添加する。
　段階的な調合方法は、これらに限られるものではないが、上述（ｉ）（ｉｉ）の調合方法を基本として併用する重合性化合物の物性に応じてモノマー仕込み比、加熱溶解温度、時間条件等を最適化することにより、調合時の高粘度化を回避して安定的に重合性組成物の調製が可能である。
　得られた重合性組成物は、たとえば極めて高い屈折率を有する透明樹脂用の原料モノマー組成物として有用である。
　また、得られた重合性組成物は、通常、公知のチエタン基含有化合物を重合する際の方法に準じて重合し、硬化させることができる。
　硬化樹脂を得るための重合触媒等の種類や量、単量体の種類や割合は、重合性組成物を構成する化合物の構造により設定される。
　本発明の重合性組成物を硬化し成形する際には、目的に応じて、公知の成形法と同様に、安定剤、樹脂改質剤、鎖延長剤、架橋剤、ヒンダードアミン系光安定剤（ＨＡＬＳ）系を代表とする光安定剤、ベンゾトリアゾール系を代表とする紫外線吸収剤、ヒンダードフェノール系を代表とする酸化防止剤、着色防止剤、充填剤、シリコーン系を代表とする外部離型剤または酸性燐酸エステル、４級アンモニウム塩もしくは４級ホスホニウム塩等の界面活性剤を代表とする内部離型剤、密着性向上剤などの種々の物質を添加してもよい。ここで、内部離型剤は、前述の各種触媒のうち離型効果を示すものをも含む。
　上記の添加可能な各種添加剤の添加量は、それぞれの添加剤の種類、構造、効果により異なり一概に限定することはできないが、通常、重合性組成物の総重量に対して０．００１重量％以上１０重量％以下の範囲で用いられ、好ましくは０．０１重量％以上５重量％以下の範囲で使用される。これらの範囲内とすることにより、さらに良好に硬化した樹脂の製造が可能であり、得られる樹脂の透明性、光学物性がさらに良好なものとなる場合がある。
　たとえば、ヒンダードアミン系光安定剤（ＨＡＬＳ）やフェノール系、ホスファイト系、チオエーテル系の酸化防止剤を添加すると樹脂色相が改善される場合がある。特に、ヒンダードアミン系光安定剤（ＨＡＬＳ）を添加すると樹脂色相が大幅に改善される場合がある。このようなヒンダードアミン系光安定剤（ＨＡＬＳ）としては、たとえば、株式会社ＡＤＥＫＡ社製のアデカスタブＬＡ－７７、ＬＡ－５７、ＬＡ－５２、ＬＡ－６７、ＬＡ－６２、ＬＡ－６８、ＬＡ－６３、ＬＡ－８７、ＬＡ－８２等が挙げられるがこれらに限定されるものではない。
　上記重合性組成物を重合することにより、樹脂が得られる。重合方法としては、プラスチックレンズを製造する際に用いられる公知の各種方法が挙げられるが、代表的には、注型重合が挙げられる。
　本発明の重合性組成物を注型重合する際には、必要に応じて、重合性組成物に対して減圧下での脱法処理やフィルターろ過を行った後、成型用モールドに注入し、必要に応じて加熱して重合を行う。この場合、低温から高温へ徐々に加熱して重合することが好ましい。
　上述の成型用モールドは、たとえば、ポリエチレン、エチレン－酢酸ビニル共重合体、ポリ塩化ビニル等からなるガスケットを介した鏡面研磨した二枚の鋳型により構成される。鋳型は、代表的には、ガラスとガラスの組み合わせであり、他にガラスとプラスチック板、ガラスと金属板等の組み合わせの鋳型が挙げられるが、これらに限定されるものではない。また、成型用モールドは２枚の鋳型をポリエステル粘着テープなどのテープ等で固定したものであってもよい。必要に応じて、鋳型に対して離型処理など公知の処理方法を行ってもよい。
　注型重合を行う場合、重合温度は重合開始剤の種類など重合条件によって影響されるので、限定されるものではないが、通常、－５０℃以上２００℃以下であり、好ましくは、－２０℃以上１７０℃以下であり、より好ましくは、０℃以上１５０℃以下である。
　重合時間は、重合温度により影響されるが、通常、０．０１時間以上２００時間以下であり、好ましくは、０．０５時間以上１００時間以下である。また必要に応じて、定温や昇温、降温などを行っていくつかの温度を組み合わせて重合を行うことも可能である。
　また、本発明の重合性組成物は、電子線、紫外線や可視光線などの活性エネルギー線を照射することによっても重合を行うことができる。この際には、必要に応じて、活性エネルギー線によって重合開始するラジカル重合触媒やカチオン重合触媒が用いられる。
　得られた樹脂は、硬化後、必要に応じて、アニール処理を施されてもよい。さらに必要に応じて、反射防止、高硬度付与、耐摩耗性向上、防曇性付与あるいはファッション性付与の目的で、表面研磨、帯電防止処理、ハードコート処理、無反射コート処理、染色処理、調光処理（たとえば、フォトクロミックレンズ化処理など）など公知の各種物理的または化学的処理を施されてもよい。
　本発明の重合性組成物を重合することにより得られる樹脂は、高い透明性、良好な耐熱性と機械的強度を有し、かつ、たとえば高屈折率を有しており、たとえば、プラスチックレンズなどの光学部品に用いられる樹脂として有用である。
　光学部品としては、たとえば、視力矯正用眼鏡レンズ、撮像機器用レンズ、液晶プロジェクター用フレネルレンズ、レンチキュラーレンズ、コンタクトレンズなどの各種プラスチックレンズ；
発光ダイオード（ＬＥＤ）用封止材；
光導波路；
光学レンズや光導波路の接合に用いる光学用接着剤；
光学レンズなどに用いる反射防止膜；
基板、導光板、フィルム、シートなどの液晶表示装置部材に用いる透明性コーティングまたは透明性基板などが挙げられる。
　以下、製造例および実施例により本発明をさらに具体的に説明するが、本発明はこれらの例に限定されるものではない。
　以下の実施例において、製造した樹脂の光学物性（屈折率、アッベ数）、耐熱性、色相、機械物性は以下の試験方法により評価した。
屈折率（ｎｅ），アッベ数（νｅ）：プルフリッヒ屈折計を用い２０℃で測定した。
耐熱性：ＴＭＡペネトレーション法（５０ｇ荷重、ピン先０．５ｍｍφ、昇温速度１０℃／ｍｉｎ）で測定した温度－変位グラフの熱膨張時における極大値を示す温度を「落ち込み開始温度」とし、落ち込み開始温度における接線と、落ち込み時の曲線の接線との交点をＴｇ（℃）とした。
３点曲げ試験：ＳＨＩＭＡＤＺＵ社製オートグラフＡＧＳ－Ｊにより測定した。厚さ３ｍｍ、幅２５ｍｍ、長さ約７０ｍｍの樹脂平板を支点間距離３４ｍｍの支持台上に設置して上部から１．２ｍｍ／ｍｉｎの速度で荷重を掛けて、荷重が最大となった時の応力および変位を最大点応力および最大点変位として試験値とした。
（参考製造例１）
　特許文献２（特開２００３－３２７５８３号公報）に記載の方法に従って、３－チエタノールを合成した。さらに得られた３－チエタノールを用い、３－メルカプトチエタンを合成した。
　すなわち、攪拌装置と温度計を備えた反応器中に、チオ尿素１９０ｇ（２．５０モル）、３５重量％塩酸水２５３ｇおよび水２５０ｇを装入して攪拌して反応液とした。反応液を攪拌しながら、反応液に３－チエタノール１５６ｇ（１．７３モル）を１時間かけて滴下した。滴下終了後、３０℃で２４時間、攪拌して反応を行った後、２４重量％アンモニア水１７７ｇを１時間かけて滴下した。さらに３０℃で１５時間反応を行った後、静置して有機層（下層）を取り出し、粗生成物１３４ｇを得た。得られた粗生成物を減圧下に蒸留して、沸点４０℃／１０６Ｐａの留分を集め、無色透明液体の目的物である３－メルカプトチエタンを得た。
　（参考製造例２）
　本例ではテトラキス（３－チエタニルチオ）スズ（下記式（５）に示す化合物）を合成した。
　参考製造例１で製造した３－メルカプトチエタン１１．２ｇ（０．１１モル）を純水５０ｇ中に装入し、続いて、１０％ＮａＯＨ水溶液４１．２ｇ（０．１０モル）を室温下、４０分かけて滴下装入した。続いて、反応液を３０℃まで昇温し、１０％四塩化スズの水溶液６５．２ｇ（四塩化スズ０．０２５モルに相当）を同温度で４時間かけて滴下装入した。滴下終了後、同温度でさらに２時間攪拌した。この反応混合物にクロロホルム１００ｍｌを加え、有機層と水層に分液した。有機層を１００ｍｌの純水で２回洗浄した後、無水硫酸ナトリウムを用いて乾燥した。この抽出物から溶媒を留去して、下記式（５）に示される化合物１３．４ｇ（収率９９％）を得た。
Figure JPOXMLDOC01-appb-C000031
　（参考製造例３）
　本例では、トリス（チエタニルチオ）アンチモン（下記式（４）に示す化合物）を合成した。
　参考製造例１で製造した３－メルカプトチエタン７１．３ｇ（０．６６モル）を純水１０６．９ｇ中に装入し、１５℃まで冷却した。続いて、３０重量％ＮａＯＨ水溶液８７．７ｇ（０．６６モル）を１時間かけて滴下装入した。続いて、２０．０重量％三塩化アンチモンのエタノール溶液２５０．０ｇ（三塩化アンチモン０．２２モルに相当）を同温度で２時間かけて滴下装入した。滴下終了後、同温度でさらに２時間攪拌した。
　この反応混合物をろ過して固形物をろ取し、２００ｇの水で洗浄を繰り返して副生した塩を除去した。４回洗浄を繰り返した後、固形物をメタノール２００ｇでさらに洗浄して固形物をろ取した。ろ取した固形物を減圧乾燥した。
　乾燥後の反応混合物をクロロホルム５００ｇに溶解し、不溶物をろ過して除去した。ろ過後の有機層を濃縮してヘキサンを装入し、析出物をろ取した後に減圧乾燥して下記式（４）に示す化合物８７．６ｇ（収率９１％）を得た。
Figure JPOXMLDOC01-appb-C000032
　以下に、得られた化合物の同定データを示す。
1Ｈ－ＮＭＲ（溶媒：ＣＤＣｌ3、内部標準物質：ＴＭＳ）：δ３．４０（６Ｈ）、３．５４（６Ｈ）、４．７３（３Ｈ）。
13Ｃ－ＮＭＲ（溶媒：ＣＤＣｌ3）：δ３９．４、４３．３。
ＩＲ（ユニバーサルＡＴＲ法）：２９１６、１４４４、１４１４、１２５２、１２２７、１１７０、９４６、９３３ｃｍ-1。
ＦＤＭＳ：ｍ／ｅ計算値Ｃ9Ｈ15Ｓ6Ｓｂ（Ｍ+）４３６、実測値４３６。
元素分析：計算値Ｃ：２４．７％、Ｈ：３．５％、Ｓ：４４．０％、Ｓｂ：２７．８％、実測値：Ｃ：２４．３％、Ｈ：２．８％、Ｓ：４３．８％、Ｓｂ：２７．５％。
　（実施例１）
　本実施例では、１，３－ビス（３－チエタニルチオ）－２－プロパノール（下記式に示す化合物）を合成した。
Figure JPOXMLDOC01-appb-C000033
　攪拌機と温度計を備えた反応器中に、３－メルカプトチエタン５０ｇ、水６４ｇを装入し、３１％の水酸化ナトリウム水溶液２６ｇを滴下した。これを３５℃に保ちながらエピクロロヒドリン１９ｇを２時間かけて滴下し、１時間熟成した。これにトルエン１００ｇを加えた後、水５０ｇで２回洗浄した。得られたトルエン層を硫酸マグネシウムで脱水して濾過後、減圧濃縮してトルエンを除いてから、濾過し、液体２５ｇを得た。分析の結果、得られた化合物は１，３－ビス（３－チエタニルチオ）－２－プロパノールであった。得られた同定データを以下に示す。以下の同定データ中のａ～ｆおよび１～４は、上記式に対応する。
ＭＳスペクトル（ＥＩ法）
Ｍ＋＝２６８
ＩＲスペクトル
６５１ｃｍ－１：スルフィド、３４２９ｃｍ－１：ヒドロキシル基
１Ｈ－ＮＭＲスペクトル（ＣＤＣｌ３）
ａ：２．６～２．８ｐｐｍ（４Ｈ）
ｂ：２．９ｐｐｍ（１Ｈ）
ｃ、ｄ：３．２～３．５ｐｐｍ（８Ｈ）
ｅ：３．８ｐｐｍ（１Ｈ）
ｆ：４．５ｐｐｍ（２Ｈ）
１３Ｃ－ＮＭＲスペクトル（ＣＤＣｌ３）
１：３４ｐｐｍ
２：３７ｐｐｍ
３：４３ｐｐｍ
４：７０ｐｐｍ
　（実施例２）
　参考製造例２で製造した化合物６０重量部、参考製造例３で製造した化合物２８重量部、１，３－ビス（３－チエタニルチオ）－２－プロパノール（実施例１で製造した化合物）１２重量部を７５℃にて加熱混合溶解させた後、３．９ｋＰａ以下の減圧下で脱気させた後、７５℃、３．９ｋＰａ以下の減圧下で脱気させた。ガラスモールドとテープよりなるモールド中へ該重合性組成物を注入した後、加熱オーブン中へ入れ７０～１３０℃まで徐々に昇温し８６時間重合を行った。
得られた樹脂の成型片は透明性良好であり、歪みのない外観良好なものであった。樹脂物性評価結果を以下に示す。
屈折率ｎｅ：１．７９７
アッベ数νｅ：２４．４
Ｔｇ：１４９．９℃
落ち込み開始温度：１３８．７℃
３点曲げ最大点応力：１０１．７Ｎ／ｍｍ２
３点曲げ最大点変位：１．３７ｍｍ
　（実施例３）
　参考製造例２で製造した化合物４５重量部、参考製造例３で製造した化合物４０重量部、１，３－ビス（３－チエタニルチオ）－２－プロパノール１５重量部を７５℃にて加熱混合溶解させた後、３．９ｋＰａ以下の減圧下で脱気させた後、７５℃、３．９ｋＰａ以下の減圧下で脱気させた。ガラスモールドとテープよりなるモールド中へ該重合性組成物を注入した後、加熱オーブン中へ入れ７０～１３０℃まで徐々に昇温し８６時間重合を行った。
　得られた樹脂の成型片は透明性良好であり、歪みのない外観良好なものであった。樹脂物性評価結果を以下に示す。
屈折率ｎｅ：１．７９８
アッベ数νｅ：２４．２
Ｔｇ：１３３．９℃
落ち込み開始温度：１１９．６℃
３点曲げ最大点応力：１２２．８Ｎ／ｍｍ２
３点曲げ最大点変位：１．８６ｍｍ
（実施例４）
　攪拌機と温度計を備えた反応器中に3－メルカプトチエタン１２１ｇ、メタノール２００ｇを装入し、３１％の水酸化ナトリウム水溶液７８ｇを滴下した。４５℃に保ちながらエピチオクロロヒドリン５６ｇを２時間かけて滴下し、１時間熟成した。トルエン３００ｇを加えた後、水２００ｇで４回洗浄した。得られたトルエン層を硫酸マグネシウムで脱水して濾過後、減圧濃縮してトルエンを除いてから、濾過し、液体１２８ｇを得た。分析の結果、１，３－ビス（３－チエタニルチオ）－２－プロパンチオールであった。得られた同定データおよび構造式を以下に示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-C000034
（実施例５）
　参考製造例２でえたテトラキス（３－チエタニルチオ）スズ８５重量部、実施例４で得た１，３－ビス（３－チエタニルチオ）－２－プロパンチオール１５重量部を８０℃にて加熱混合溶解させた。その後、３．９ｋＰａ以下の減圧下で脱気させ、８０℃、３．９ｋＰａ以下の減圧下で脱気させた。ガラスモールドとテープよりなるモールド中へ該重合性組成物を注入した後、加熱オーブン中へ入れ８０～１３０℃まで徐々に昇温し６１時間重合を行った。
　得られた樹脂の成型片は透明性良好であり、歪みのない外観良好なものであった。樹脂物性評価結果を以下に示す。
Figure JPOXMLDOC01-appb-T000002

Claims (18)

  1. 　下記式（３０）で示される、チエタン化合物。
    Figure JPOXMLDOC01-appb-C000035
     　式（３０）中、Ａは、ＯＨ基あるいは、ＳＨ基を示す。
  2. 　請求項１に記載のチエタン化合物を含む、重合性組成物。
  3. 　請求項２に記載の重合性組成物において、イソシアネート化合物、前記式（３０）に示した化合物以外の活性水素化合物、エポキシ化合物、エピチオ化合物、前記式（３０）に示した化合物以外の非金属チエタン化合物および金属チエタン化合物からなる群から選択される一種以上をさらに含む、重合性組成物。
  4. 　請求項１に記載のチエタン化合物と、下記一般式（２）に示される金属チエタン化合物とを含む、重合性組成物。
    Figure JPOXMLDOC01-appb-C000036
     （上記一般式（２）中、Ｍは金属原子である。Ｘ1およびＸ2は各々独立に硫黄原子または酸素原子である。Ｒ1は２価の有機基である。
    　ｍは０または１以上の整数である。
    　ｎはＭの価数であり、ｐは１以上ｎ以下の整数である。
    　ｑは０または１以上ｎ－２以下の整数である。
    　Ｙは１価または２価の基であり、Ｔは無機または有機基である。
    　ｒは１または２である。
    　ｒ＝１のとき、ｑ＝０であり、Ｙは１価の無機または有機基である。ｒ＝１かつｎ－ｐ－ｑが２以上の場合、複数のＹは、各々独立に１価の無機または有機基である。ｒ＝１かつｎ－ｐ－ｑが２以上の場合、複数のＹが互いに結合し、金属原子を含む環を形成していてもよい。
    　ｒ＝２のとき、ｎ－ｐ－ｑ＝１または２であり、Ｙは２価の基である。ｒ＝２かつｎ－ｐ－ｑ＝２の場合、２つのＹが、２つの金属原子とともに環を形成していてもよい。ｒ＝２かつｑ＝２の場合、複数のＴは、各々独立に無機または有機基である。）
  5. 　請求項４に記載の重合性組成物において、前記一般式（２）においてＭがＳｂまたはＳｎである化合物を含む、重合性組成物。
  6. 　請求項４または５に記載の重合性組成物において、前記一般式（２）に示した化合物として、下記一般式（３）に示される化合物を含む、重合性組成物。
    Figure JPOXMLDOC01-appb-C000037
  7. 　請求項４乃至６いずれかに記載の重合性組成物において、前記一般式（２）においてｍ＝０である化合物を含む、重合性組成物。
  8. 　請求項４乃至７いずれかに記載の重合性組成物において、前記一般式（２）においてＸ1が硫黄原子である化合物を含む、重合性組成物。
  9. 　請求項４乃至８いずれかに記載の重合性組成物において、前記一般式（２）においてｎ＝ｐ＝３である化合物を含む、重合性組成物。
  10. 　請求項４乃至９いずれかに記載の重合性組成物において、前記一般式（２）に示した化合物として、下記式（４）に示される化合物を含む、重合性組成物。
    Figure JPOXMLDOC01-appb-C000038
  11. 　請求項４または５に記載の重合性組成物において、前記一般式（２）においてｎ＝ｐ＝４である化合物を含む、重合性組成物。
  12. 　請求項１１に記載の重合性組成物において、前記一般式（２）に示した化合物として、下記式（５）に示される化合物を含む、重合性組成物。
    Figure JPOXMLDOC01-appb-C000039
  13. 　請求項２乃至１２いずれかに記載の重合性組成物において、ブルーイング剤をさらに含む、重合成組成物。
  14. 　請求項２乃至１３いずれかに記載の重合性組成物を注型重合する工程を含む、樹脂の製造方法。
  15. 　請求項２乃至１３いずれかに記載の重合性組成物を重合して得られる樹脂。
  16. 　請求項１５に記載の樹脂からなる光学部品。
  17. 　請求項２乃至１３いずれかに記載の重合性組成物の光学部品としての使用。
  18. 　請求項２乃至１３いずれかに記載の重合性組成物を重合させた樹脂の光学部品としての使用。
PCT/JP2009/000656 2008-02-19 2009-02-18 チエタン化合物、これを含む重合性組成物、樹脂およびその製造方法ならびに使用 WO2009104385A1 (ja)