WO2007136495A2 - High efficiency solution polymerization process - Google Patents
High efficiency solution polymerization process Download PDFInfo
- Publication number
- WO2007136495A2 WO2007136495A2 PCT/US2007/009843 US2007009843W WO2007136495A2 WO 2007136495 A2 WO2007136495 A2 WO 2007136495A2 US 2007009843 W US2007009843 W US 2007009843W WO 2007136495 A2 WO2007136495 A2 WO 2007136495A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- phenyl
- methyl
- bis
- oxoyl
- phenoxy
- Prior art date
Abstract
Description
Claims