WO2007037120A1 - 白色発光型ledランプおよびそれを用いたバックライト並びに液晶表示装置 - Google Patents
白色発光型ledランプおよびそれを用いたバックライト並びに液晶表示装置 Download PDFInfo
- Publication number
- WO2007037120A1 WO2007037120A1 PCT/JP2006/318054 JP2006318054W WO2007037120A1 WO 2007037120 A1 WO2007037120 A1 WO 2007037120A1 JP 2006318054 W JP2006318054 W JP 2006318054W WO 2007037120 A1 WO2007037120 A1 WO 2007037120A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- phosphor
- light emitting
- activated
- led lamp
- light
- Prior art date
Abstract
本発明は、紫外発光LEDを用いた白色LEDランプにおいて、青色、緑色、赤色発光の各蛍光体の組合せを改善することによって、高演色性と高輝度とを両立させる。 本発明による白色LEDランプ1は、発光波長が360nm以上440nm以下の範囲のLEDチップ2と、青色発光蛍光体と緑色発光蛍光体と赤色発光蛍光体とが結合した蛍光体を含み、LEDチップ2からの光により励起されて白色光を発光する発光部とを具備する。青色発光蛍光体にはEu付活ハロ燐酸塩蛍光体とEu付活アルミン酸塩蛍光体から選ばれる少なくとも1種、緑色発光蛍光体にはAuおよびAl付活硫化亜鉛蛍光体、赤色発光蛍光体にはEuおよびSm付活酸硫化ランタン蛍光体とCuおよびMn付活硫化亜鉛蛍光体から選ばれる少なくとも1種が用いられる。
Description
明 細 書
白色発光型 LEDランプおよびそれを用いたバックライト並びに液晶表示 装置
技術分野
[0001] 本発明は、光源に発光波長が 360〜440nmの発光ダイオード(LED : Light Emitti ng Diode)を用いた白色発光型 LEDランプおよびそれを用いたバックライト並びに液 晶表示装置に関する。
背景技術
[0002] LEDは電気工ネルギーを紫外光や可視光等の光に変換して放射する半導体素子 であり、このような LEDチップを例えば透明樹脂で封止した LEDランプが各種分野 で使用されている。 LEDチップは半導体素子であるため、長寿命でかつ信頼性が高 ぐ光源として用いた場合に交換作業等が軽減されることから、携帯通信機器、 PC周 辺機器、 OA機器、家庭用電気機器、信号装置、各種スィッチ類、バックライト型表示 板等の各種表示装置の構成部品として広く利用されるようになってきている。
[0003] LEDランプ力 放射される光の色調は LEDチップの発光波長に限られるものでは なぐ例えば LEDチップの表面に蛍光体を塗布したり、あるいは LEDチップを封止 する透明榭脂中に蛍光体を含有させることによって、青色から赤色まで使用用途に 応じた可視光領域の光を得ることができる。特に、白色発光型の LEDランプは携帯 通信機器の表示部のバックライトや車載用ランプ等の用途に急速に普及しており、将 来的には蛍光ランプの代替品として大きく伸張することが期待されている。
[0004] 現在、普及もしくは試行されている白色発光型の LEDランプとしては、青色発光 L EDと黄色発光蛍光体 (YAG等)とを組合せた LEDランプと、紫外発光 LEDと青色、 緑色、赤色発光の各蛍光体の混合物とを組合せた LEDランプとが知られている。現 時点では、前者の青色発光 LEDを用いた白色 LEDランプの方が後者より輝度特性 等に優れることから普及している。しかし、前者は見る方向によっては黄色っぽく見え たり、また白色面に投影したときに黄色や青色のムラが現れるというような難点を有し ている。このため、前者の白色 LEDランプは擬似白色と呼ばれることもある。白色光
の質を表す平均演色指数においても、前者の白色 LEDランプは 70〜75の範囲にと どまっている。
[0005] 一方、後者の紫外発光 LEDを用いた白色 LEDランプは、輝度が前者より劣るもの の、発光並びに投影光のムラが少なぐ将来的には照明用途の白色ランプの主流に なることが期待され、その開発が急速に進められている。このような紫外発光 LEDを 用いた白色 LEDランプでは各色発光の蛍光体の特性に加えて、それら各蛍光体の 組合せが演色性や輝度等のランプ特性に影響を及ぼすことから、青色、緑色、赤色 発光の各蛍光体の選択並びに組合せに関する検討が進められている。
[0006] 例えば、非特許文献 1には紫外発光 LEDと、青色発光蛍光体として Eu付活ハロ燐 酸塩蛍光体または Eu付活アルミン酸塩蛍光体、緑色発光蛍光体として Cuおよび A1 付活硫化亜鉛蛍光体または Euおよび Mn付活アルミン酸塩蛍光体、赤色発光蛍光 体として Eu付活酸硫化イットリウム蛍光体とを組合せた白色 LEDランプが記載されて いる。また、特許文献 1には青色発光蛍光体として Eu付活ハロ燐酸塩蛍光体または Eu付活アルミン酸塩蛍光体、緑色発光蛍光体として Euおよび Mn付活アルミン酸塩 蛍光体、赤色発光蛍光体として Eu付活酸硫ィ匕ランタン蛍光体を用いることが記載さ れている。
非特許文献 1:三菱電線工業時報 2002年 7月第 99号
特許文献 1:特開 2000— 073052号公報
発明の開示
発明が解決しょうとする課題
[0007] 上述した従来の白色 LEDランプは、紫外発光 LEDを用いたランプの特徴である高 ぃ演色性と発光の均一性とを備えているものの、輝度特性の点では不十分であり、さ らなる改善が求められて 、る。紫外発光 LEDを用 、た白色 LEDランプで高演色性と 高輝度とを両立させるためには、白色光のスペクトルにおいて人間の色感度のピーク がある 450nm近辺、 560nm近辺、 620nm近辺の光がバランスよく含まれていること 、さらに青色、緑色、赤色発光成分の各蛍光体の発光効率がバランスよいことが必要 である。
[0008] しかしながら、従来の白色 LEDランプに用いられている各蛍光体のうち、赤色発光
蛍光体は波長 380nm以上の紫外線または紫色光に対する発光効率が他の蛍光体 に比べて劣ることから、白色 LEDランプの輝度特性等を十分に高めることができない ことが分力つてきた。また、発光効率に劣る赤色発光蛍光体に引きずられて、青色お よび緑色発光蛍光体の特性も十分に発揮させることができず、これも輝度特性の劣 化要因となっている。
[0009] 本発明はこのような課題に対処するためになされたもので、紫外発光 LEDを用い た白色発光型の LEDランプにおいて、青色、緑色、赤色発光の各蛍光体の組合せ を改善することによって、高演色性と高輝度とを両立させた白色発光型 LEDランプを 提供することを目的としている。
課題を解決するための手段
[0010] 本発明の白色発光型 LEDランプは、発光波長が 360nm以上 440nm以下の範囲 の発光ダイオードと、青色発光蛍光体と緑色発光蛍光体と赤色発光蛍光体とを含み 、前記発光ダイオードからの光により励起されて白色光を発光する発光部とを具備す る白色発光型 LEDランプにおいて、前記青色発光蛍光体はユーロピウム付活ハロ 燐酸塩蛍光体とユーロピウム付活アルミン酸塩蛍光体力 選ばれる少なくとも 1種か らなり、前記緑色発光蛍光体は金およびアルミニウム付活硫ィ匕亜鉛蛍光体力 なり、 かつ前記赤色発光蛍光体はユーロピウムおよびサマリウム付活酸硫化ランタン蛍光 体と銅およびマンガン付活硫ィ匕亜鉛蛍光体力 選ばれる少なくとも 1種力 なり、 つ、前記青色発光蛍光体、前記緑色発光蛍光体および前記赤色発光蛍光体は予 め結合材により結合されて 、ることを特徴として 、る。
発明の効果
[0011] 本発明の白色発光型 LEDランプは、緑色発光蛍光体として長波長成分をより多く 含む金およびアルミニウム付活硫化亜鉛蛍光体を用いて!/ヽるため、赤色発光蛍光体 による発光成分 (赤色成分)を補強することができる。これによつて、紫外発光 LEDを 用いた白色発光型 LEDランプ本来の高演色性と 、う特徴を損なうことなく、輝度特性 を向上させることができる。従って、高演色性と高輝度とを両立させた白色発光型 LE Dランプを提供することが可能となる。また、本発明の白色発光型 LEDランプは発光 色度差のバラツキが小さ 、ことから、 LEDランプを複数個用いるバックライトおよびそ
れを用いた液晶表示装置に適用したとしても面光源としての色度バラツキを抑えるこ とが可能となる。
図面の簡単な説明
[0012] [図 1]図 1は、本発明の一実施形態による白色 LEDランプの構成を示す断面図であ る。
[図 2]図 2は、本発明に適用される緑色発光蛍光体の発光スペクトルの一例を従来の 緑色発光蛍光体と比較して示す図である。
[図 3]図 3は、本発明に適用される三色蛍光体の発光スペクトルの一例を示す図であ る。
発明を実施するための最良の形態
[0013] 以下、本発明を実施するための形態について、図面を参照して説明する。なお、以 下では本発明の実施形態を図面に基づいて述べるが、それらの図面は図解のみの 目的のために提供されるものであり、本発明はそれらの図面に限定するものではない
[0014] 図 1は本発明の一実施形態による白色発光型 LEDランプ(白色 LEDランプ)の構 成を模式的に示す断面図である。同図に示す白色 LEDランプ 1は、光源として LED チップ 2を有して 、る。この LEDチップ 2はリード端子 3を有する配線基板 4上に接合 されており、 LEDチップ 2とリード端子 3とはボンディングワイヤ 5により電気的に接続 されて!/、る。 LEDチップ 2には波長が 360〜440nmの範囲の紫外線または紫色光 を放射する紫外発光 LEDが用いられる。このような紫外発光タイプの LEDチップ 2と しては、発光層として窒化物系化合物半導体層を有する LEDチップ等が例示される
[0015] 配線基板 4上には円筒状の榭脂枠 6が設けられており、その内壁面には反射層 7が 形成されている。榭脂枠 6内には透明榭脂 8が充填されており、この透明榭脂 8中に LEDチップ 2が埋め込まれている。 LEDチップ 2が埋め込まれた透明榭脂 8は、青色 発光蛍光体と緑色発光蛍光体と赤色発光蛍光体とを含む蛍光体 (三色蛍光体) 9を 含有している。透明榭脂 8中に分散させた三色蛍光体 9は、 LEDチップ 2から放射さ れる紫外線または紫色光により励起されて白色光を発光するものである。
[0016] すなわち、白色 LEDランプ 1に印加された電気エネルギーは LEDチップ 2で紫外 光や紫色光に変換され、それらの光は透明榭脂 8中に分散された三色蛍光体 9でよ り長波長の光に変換される。そして、透明榭脂 8中に含有させた三色蛍光体 9に基づ いて白色の光力 SLEDランプ 1から放出される。三色蛍光体 9を含有する透明榭脂 8は 発光部として機能するものであり、 LEDチップ 2の発光方向前方に配置されている。 このような発光部と光源としての LEDチップ 2とによって、白色 LEDランプ(白色発光 ランプ) 1が構成されている。なお、三色蛍光体 9が含有される透明榭脂 8には、例え ばシリコーン榭脂ゃエポキシ榭脂等を用いることができる。
[0017] 三色蛍光体 9を構成する青色、緑色、赤色発光の各蛍光体には、 LEDチップ 2か ら放射される波長 360〜440nmの範囲の紫外線または紫色光を効率よく吸収する 蛍光体を使用することが好ましい。これら各色発光の蛍光体のうち、青色発光蛍光体 には紫外線や紫色光の吸収効率に優れるユーロピウム (Eu)付活ハロ燐酸塩蛍光体 、およびユーロピウム (Eu)付活アルミン酸塩蛍光体力 選ばれる少なくとも 1種が用 いられる。
[0018] Eu付活ハロ燐酸塩蛍光体としては、
一般式:(Ml , Eu ) (PO ) -CI
l -c c 10 4 6 2
(式中、 Mlは Mg、 Ca、 Srおよび Baから選ばれる少なくとも 1種の元素を示し、 cは 0 . 005≤c≤0. 03を満足する数である)
で表される組成を有する蛍光体が例示される。
Eu付活アルミン酸塩蛍光体としては、
一般式: m(M2 , Eu ) 0 ·ηΑ1 Ο - -- (2)
l -d d 2 3
(式中、 M2は Mg、 Ca、 Sr、 Baおよび Znから選ばれる少なくとも 1種の元素を示し、 d 、 mおよび nは 0. 05≤d≤0. 3、 0<m、 0く n、 0. 2≤m/n≤l. 5を満足する数で ある)
で表される組成を有する蛍光体が例示される。
[0019] また、赤色発光蛍光体にはユーロピウム (Eu)およびサマリウム(Sm)付活酸硫ィ匕ラ ンタン蛍光体、および銅 (Cu)およびマンガン(Mn)付活硫化亜鉛蛍光体から選ば れる少なくとも 1種が用 ヽられる。
Euおよび Sm付活酸硫ィ匕ランタン蛍光体としては、
一般式:(La , Eu , Sm ) O S - -- (3)
1-a-b a b 2 2
(式中、 aおよび bは 0. 01≤a≤0. 15、 0. 0001≤b≤0. 03を満足する数である) で表される組成を有する蛍光体が例示される。
また、 Cuおよび Mn付活硫化亜鉛蛍光体としては、
一般式: ZnS : Cu , Μη · '· (4)
V w
(式中、 vおよび wは 0. 0002≤v≤0. 001、 0. 005≤w≤0. 014を満足する数であ る)
で表される組成を有する蛍光体が例示される。
[0020] (3)式および (4)式で表される赤色発光蛍光体は、 V、ずれも紫外発光タイプの LE Dチップ 2で発光させる赤色発光成分として利用することが可能であるものの、赤色 発光成分の発光特性 (発光強度等)を考慮すると、少なくとも Euおよび Sm付活酸硫 化ランタン蛍光体を赤色発光成分として使用することが好ましい。また、 Euおよび S m付活酸硫ィ匕ランタン蛍光体単独では赤色発光成分が不足することから、 Cuおよび Mn付活硫ィ匕亜鉛蛍光体を併用することが有効である。
[0021] 上述した赤色発光蛍光体は波長 360〜440nmの範囲の紫外線または紫色光に 対する発光効率が必ずしも十分とは言えな!/ヽ。 Euおよび Sm付活酸硫化ランタン蛍 光体と Cuおよび Mn付活硫化亜鉛蛍光体を併用することで赤色発光成分が補強さ れるものの、青色および緑色発光蛍光体に比べると発光効率等が劣る。そこで、この 実施形態の白色 LEDランプ 1においては、従来の緑色発光成分に比べて長波長成 分をより多く含む緑色発光蛍光体を用いている。具体的には、緑色発光蛍光体に金 (Au)およびアルミニウム (A1)付活硫化亜鉛蛍光体を用いる。
[0022] Auおよび A1付活硫ィ匕亜鉛蛍光体としては、例えば
一般式: ZnS :Au , A1 - -- (5)
X y
(式中、 Xおよび yは 0. 0002≤x≤0. 0015、 0. 0001≤y≤0. 0012を満足する数 である)
で表される組成を有する蛍光体が用いられる。(5)式における Xの値(1モルの ZnS に対する Auのモル比)が 0. 0002未満であると発光色度が青色方向にずれて望まし
い色が得られなくなる。一方、 Xの値が 0. 0015を超えると蛍光体の体色が悪くなり輝 度が低下する。また、(5)式における yの値(1モルの ZnSに対する A1のモル比)が 0 . 0001未満であると Auが硫ィ匕亜鉛の中に入らなくなり、これにより輝度が低下する。 一方、 yの値が 0. 0012を超えると蛍光体の体色が悪くなり輝度が低下する。
[0023] 図 2に Auおよび A1付活硫化亜鉛蛍光体 (ZnS: Au, A1蛍光体)の発光スペクトル( a)を、従来の Cuおよび A1付活硫ィ匕亜鉛蛍光体 (ZnS : Cu, A1蛍光体)の発光スぺク トル(b)と Euおよび Mn付活アルミン酸塩蛍光体(3 (Ba, Mg, Eu, Μη) 0· 8Α1 Ο
2 3 蛍光体)の発光スペクトル (c)と比較して示す。図 2から明らかなように、 Auと A1で共 付活した硫ィ匕亜鉛蛍光体は、従来の Cuおよび A1付活硫化亜鉛蛍光体や Euおよび Mn付活アルミン酸塩蛍光体に比べて長波長成分を多く含んでおり、これによつて赤 色発光成分を補強することが可能となる。
[0024] 上述した青色、緑色および赤色発光蛍光体を含む三色蛍光体 9は、 450nm近辺、 560nm近辺、 620nm近辺の光をバランスよく含んでいることから、白色光の演色性 を高めることができる。その上で、従来の緑色発光成分に比べて長波長成分をより多 く含む Auおよび A1付活硫ィ匕亜鉛蛍光体 (ZnS: Au, A1蛍光体)カゝらなる緑色発光 蛍光体を用いているため、赤色発光蛍光体による発光不足等を補強することができ る。これによつて、青色、緑色、赤色の各発光成分の輝度バランスが向上することから 、紫外発光 LEDチップ 2を用いた白色 LEDランプ 1の輝度特性を高めることができる 。従って、高演色性と高輝度とを両立させた白色 LEDランプ 1を実現することが可能 となる。
[0025] 上述した緑色発光蛍光体 (ZnS: Au, A1蛍光体)による白色 LEDランプ 1の輝度特 性の向上効果は、赤色発光蛍光体として Euおよび Sm付活酸硫ィヒランタン蛍光体、 Cuおよび Mn付活硫ィ匕亜鉛蛍光体の 、ずれを用いた場合にお!、ても得ることができ る。さらに、赤色発光蛍光体自体による輝度特性の改善効果を得る上で、赤色発光 蛍光体は前述したように Euおよび Sm付活酸硫ィヒランタン蛍光体と Cuおよび Mn付 活硫ィ匕亜鉛蛍光体とを併用することが好ましい。これによつて、赤色発光成分がさら に補強されることから、白色 LEDランプ 1の輝度特性をより一層高めることが可能とな る。これら赤色発光蛍光体の配合比率は目的とする白色光の色温度等にもよるが、
例えば Euおよび Sm付活酸硫ィ匕ランタン蛍光体と Cuおよび Mn付活硫ィ匕亜鉛蛍光 体との質量比を 3: 7〜7: 3の範囲とすることが好まし 、。
[0026] 図 3は上述した青色、緑色および赤色発光蛍光体を含む三色蛍光体 9を用いた白 色 LEDランプ 1の発光スペクトルの一例を示している。図 3において、 Aの発光スぺク トルは青色発光成分として Eu付活ハロ燐酸塩蛍光体、緑色発光成分として Auおよ び A1付活硫化亜鉛蛍光体、赤色発光成分として Euおよび Sm付活酸硫化ランタン 蛍光体を用いた白色 LEDランプ 1の発光スペクトルであり、 Bの発光スペクトルは Aの 蛍光体の組合せに赤色発光成分として Cuおよび Mn付活硫化亜鉛蛍光体を加えた 白色 LEDランプ 1の発光スペクトルである。
[0027] 上記した蛍光体の組合せ A、 Bの!、ずれにお 、ても、電流値 20mA、ピーク値 400 nmの LEDチップ力もの紫外線を(x=0. 300〜0. 350, y=0. 300〜0. 350)の 色度を有する白色光に変換したとき、青色発光成分のピーク値が 450nm、緑色発光 成分のピーク値が 545nm、赤色発光成分のピーク値が 623nmにそれぞれあり、平 均演色指数で 90以上、輝度で 300mcd以上の特性値が得られている。さらに、 Aと B の発光スペクトルを比較すると、発光スペクトル Bの方が 580nm付近およびそれ以上 の領域における発光成分が増加して 、ることが分かる。これは赤色発光成分として E uおよび Sm付活酸硫ィ匕ランタン蛍光体と Cuおよび Mn付活硫ィ匕亜鉛蛍光体とを併 用したことに基づくものであり、これによつて白色 LEDランプ 1の輝度特性をより一層 高めることが可能となる。
[0028] また、本発明では上述した青色、緑色および赤色発光蛍光体は、透明榭脂 8中に おける各色発光蛍光体の分散状態の均一性を高める上で、予め無機結合剤や有機 結合剤等の結合剤で結合させた状態で透明榭脂 8中に分散させることが好ま 、。 無機結合剤としては微粉ィ匕したアルカリ土類ホウ酸塩等を用いることができ、また有 機結合剤としてはアクリル榭脂ゃシリコーン榭脂等の透明榭脂を用いることができる。 無機結合剤や有機結合剤等を用いて一体化処理を施すことによって、各蛍光体がラ ンダムに結び付いて大粒径ィ匕する。これによつて、透明榭脂 8中での各蛍光体の沈 降速度の差等に基づく分散状態の不均一性等を解消することができ、白色光の再現 性や発光色度の均一性 (色度差のバラツキを小さくする)等を高めることが可能となる
[0029] さらに、白色 LEDランプ 1の輝度特性には各蛍光体の粒径も影響する。このような 点から、青色、緑色および赤色発光蛍光体はそれらの混合物としての平均粒径が 7 m以上であることが好ましい。なお、ここで言う平均粒径は粒度分布の中位値(50 %値)を示すものである。三色蛍光体 9の平均粒径を 7 μ m以上とすることによって、 白色 LEDランプ 1の輝度をさらに高めることが可能となる。三色蛍光体 (混合蛍光体) 9の平均粒径は 8 m以上とすることがより好ましい。なお、三色蛍光体 9の平均粒径 に基づく輝度の向上効果は、上述した一体化処理 (結合工程)を施した蛍光体に対 しても有効である。
このような本発明の白色 LEDランプは個々の LED間で色度バラツキの小さい均一 な LEDを得ることができる。そのため、例えば、液晶表示装置のノ ックライトのように 複数個の LEDを用いる分野に特に有効である。ノ ックライトとしては直下型、サイドラ イト型のいずれのタイプにも有効であり、特に 10個以上並べて使用するものに効果 的である。
実施例
[0030] 次に、本発明の具体的な実施例およびその評価結果について述べる。
[0031] 実施例 1
まず、青色発光蛍光体として Eu付活アルカリ土類クロ口燐酸塩((Sr , Ca , Β
0. 59 0. 01 a , Eu ) (ΡΟ ) 'CI )蛍光体、緑色発光蛍光体として Auおよび Α1付活硫ィ匕
0. 39 0. 01 10 4 6 2
亜鉛 (ZnS: Au , A1 )蛍光体、赤色発光蛍光体として Euおよび Sm付活酸
0. 0008 0. 001
硫化ランタン((La , Eu , Sm ) O S)蛍光体を用意した。
0. 94 0. 058 0. 002 2 2
[0032] 上述した青色発光蛍光体を 1. 74g、緑色発光蛍光体を 2. 17g、赤色発光蛍光体 を 2. 33g計量し、以下に示す結合工程により各色の蛍光体を結合させたものである 。なお、各蛍光体の混合比は LEDランプの CIE色度値(X, y)が x = 0. 30〜0. 31、 y=0. 30-0. 31の範囲に入るように設定したものである。以下の実施例 2〜5およ び比較例 1〜2も同様である。また、各蛍光体の混合物としての平均粒径 (分布中位 径)は 9. 5 mである。
このような混合蛍光体を用いて、図 1に示した LEDランプ 1を作製した。結合工程は
、各色発光の蛍光体を水に投入して懸濁液とした。この懸濁液を撹拌しながらホウ酸 バリウム ·カルシウム(3 (Ba, Ca) 0 -B O )を各蛍光体の合計量に対して 0. 1質量0 /0
2 3
の割合で添加した。撹拌を 30分間継続した後に停止し、蛍光体を沈降させた。これ をろ過してベーキングした後に 200メッシュのナイロン篩にかけて、結合させた 3色混 合蛍光体を得た。
[0033] LEDランプ 1の作製工程は、まず透明榭脂 8を構成するシリコーン榭脂に、混合蛍 光体を 30質量%の割合で添加、混合してスラリーとした。このスラリーを発光ピーク波 長力 00nm、形状が 300 m四方の紫外発光 LEDチップ 2上に滴下し、 140°Cで シリコーン榭脂を硬化させることによって、混合蛍光体 (青色、緑色および赤色の混 合蛍光体)を含有するシリコーン榭脂で紫外発光 LEDチップ 2を封止した。このよう にして作製した LEDランプを後述する特性評価に供した。
[0034] 実施例 2
上記した実施例 1と同一および同量の各蛍光体を用意し、これらを以下に示す方 法で結合させた。結合工程は、まず各蛍光体にアクリル榭脂ェマルジヨンを蛍光体に 対して固形分で 0. 1質量%の割合で添加し、これらを混合した。次いで、この混合物 を 120°Cで乾燥させた後、ナイロンメッシュにかけて一体ィ匕蛍光体を得た。そして、こ のような一体ィ匕蛍光体を用いて、実施例 1と同様にして LEDランプを作製した。この L EDランプを後述する特性評価に供した。
[0035] 実施例 3
上記した実施例 1と同一の緑色発光蛍光体、赤色発光蛍光体に加えて、赤色発光 蛍光体の追加として Cuおよび Mn付活硫化亜鉛 (ZnS : Cu , Mn )蛍光体、
0. 0005 0. 008 青色蛍光体として 3 (Ba0.4,Mg0.5,Eu0.1)O ' 8Al Oを用意した。 Eu付活アルカリ
2 3
土類アルミン酸塩を 2. 10g、 Auおよび A1付活硫化亜鉛蛍光体を 2. 22g、 Euおよ び Sm付活酸硫ィ匕ランタン蛍光体を 2. 10g、 Cuおよび Mn付活硫ィ匕亜鉛蛍光体を 0 . 82g計量し、これらを実施例 1と同様にして混合、結合させた。そして、このような結 合蛍光体を用いて、実施例 1と同様にして LEDランプを作製した。この LEDランプを 後述する特性評価に供した。
[0036] 実施例 4〜5
表 1に示す青色、緑色および赤色発光蛍光体の組合せを適用する以外は、それぞ れ実施例 1または実施例 2と同様にして、混合または一体化蛍光体を作製した。これ ら各混合または一体ィ匕蛍光体を用いて、実施例 1と同様にして LEDランプをそれぞ れ作製した。この LEDランプを後述する特性評価に供した。
[0037] 比較例 1
青色発光蛍光体として Eu付活アルカリ土類クロ口燐酸塩((Sr, Ca, Ba, Eu) (P
10
O ) -CI )蛍光体、緑色発光蛍光体として Euおよび Mn付活アルカリ土類アルミン酸
4 6 2
塩(3 (Ba, Mg, Eu, Μη) 0· 8Α1 Ο )蛍光体、赤色発光蛍光体として Eu付活酸硫
2 3
化ランタン((La, Eu) O S)蛍光体を用意した。上述した青色発光蛍光体を 1. 44g
2 2
、緑色発光蛍光体を 1. 49g、赤色発光蛍光体を 3. 32g計量し、これらを三本ローラ を用いて混合した。このような混合蛍光体を用いて、実施例 1と同様にして LEDラン プを作製した。この LEDランプを後述する特性評価に供した。なお、比較例 1では結 合工程は行わな力つた。
[0038] 比較例 2
青色発光蛍光体として Eu付活アルカリ土類クロ口燐酸塩((Sr, Ca, Ba, Eu) (P
10
O ) -CI )蛍光体、緑色発光蛍光体として Eu付活アルカリ土類珪酸塩((Ba, Sr, C
4 6 2
a, Eu) SiO )蛍光体、赤色発光蛍光体として Eu付活酸硫化ランタン((La, Eu) O
2 4 2
S)蛍光体を用意した。上述した青色発光蛍光体を 2. 71g、緑色発光蛍光体を 0. 4
2
5g、赤色発光蛍光体を 1. 85g計量し、これらを三本ローラを用いて混合した。このよ うな混合蛍光体を用いて、実施例 1と同様にして LEDランプを作製した。この LEDラ ンプを後述する特性評価に供した。なお、比較例 2では結合工程は行わな力つた。
[0039] [表 1]
青色発光蛍光体 緑色発光蛍光体 赤色発光蛍光体 3色蛍光体 の状態 難例 1 (Sr,Ca,Ba,Eu)io(P04 -C ZnS:Au,Al (La,Eu,Sm)202S 結 合 趣例 2 (Sr,Ca,Ba,Eu)io(P04 -Cl2 ZnS:Au,Al (La,Eu,Sm)202S TO 口 麵例 3 3(Ba,Mg}Eu)0-8A 03 ZnS:Au,Al (La,Eu,Sm)202S 結 合
/ ZnS:Cu,Mn
難例 4 3(Ba,Mg,Eu)0-8Al203 ZnS:Au,Al (La,Eu,Sni)202S 結 合
/ ZnS:Cu,Mn
難例 5 (Sr,Ca,BasEu)io(P04 -C (50%) ZnS:Au,Al (La,Eu,Sm)202S 結 合
/ 3(Ba,Mg,Eu)0-8Al203(50%) / ZnS:Cu,Mn
比較例 1 (Sr,Ca,Ba,Eu)io(P04)e-Cl3 3(Ba,Mg,Eu,Mn)0-8Al203 (La,Eu) 02S 混 合 赚例 2 (Sr,Ca,Ba,Eu)io(P04)6-Cl2 (Ba,Sr,Ca,Eu)2Si( (La,Eu)2Q2S 混 合
[0040] 上述した実施例 1〜5および比較例 1〜2の各白色 LEDランプに 20mAの電流を 流して点灯させ、各白色 LEDランプの発光輝度、平均演色指数、色度を測定した。 これらの測定結果を表 2に示す。なお、各白色 LEDランプの発光特性は、 Instrument System社製 CAS 140B COMPACT ARRAY SPECTROMETERおよび大塚電子社製 MCPD装置を用いて測定した。
[0041] [表 2]
表 2から明らかなように、実施例 1〜5による各白色 LEDランプは演色性に優れるこ とにカ卩えて、比較例 1および比較例 2に比べて輝度特性に優れることが分かる。従つ て、紫外発光 LEDを用いた白色 LEDランプにおいて、高演色性と高輝度とを両立さ せることが可能となる。
次に、実施例 1〜5の白色発光 LEDランプの色度バラツキを測定した。色度は各実
施例に力かる白色 LEDを各 20個用意し、各 LEDの真上で色度 (CIE色度座標)を 測定し、 X座標、 y座標の最大値と最小値の差(Δ χ、 Ay)を測定した。なお、参考例 として結合工程を行わない以外は実施例 1と同様のものを用意した。その結果を表 3 に示す。
[0043] [表 3]
[0044] 表 3から分力る通り、本実施例にかかる白色 LEDは色度バラツキが小さいことが分 かる。このような白色 LEDランプは、携帯通信機器、 PC周辺機器、 OA機器、家庭用 電気機器、各種スィッチ類、バックライト型表示板等の各種表示装置の構成部品、さ らには一般照明装置等として有効に利用することができる。
特に、色度バラツキが小さいことから白色 LEDランプを複数個用いるバックライトに 用いたとしても均一な白色を有する面光源を得ることができる。従って、それを用いた 液晶表示装置の特性も向上する。
Claims
[1] 発光波長が 360nm以上 440nm以下の範囲の発光ダイオードと、青色発光蛍光体 と緑色発光蛍光体と赤色発光蛍光体とを含み、前記発光ダイオードからの光により 励起されて白色光を発光する発光部とを具備する白色発光型 LEDランプにおいて、 前記青色発光蛍光体はユーロピウム付活ハロ燐酸塩蛍光体とユーロピウム付活ァ ルミン酸塩蛍光体力 選ばれる少なくとも 1種力 なり、前記緑色発光蛍光体は金お よびアルミニウム付活硫化亜鉛蛍光体からなり、かつ前記赤色発光蛍光体はユーロ ピウムおよびサマリウム付活酸硫ィ匕ランタン蛍光体と銅およびマンガン付活硫ィ匕亜鉛 蛍光体力 選ばれる少なくとも 1種力 なり、
かつ、前記青色発光蛍光体、前記緑色発光蛍光体および前記赤色発光蛍光体は 予め結合剤により結合されていることを特徴とする白色発光型 LEDランプ。
[2] 請求項 1記載の白色発光型 LEDランプにおいて、
前記緑色発光蛍光体は、
一般式: ZnS :Au , A1
X y
(式中、 Xおよび yは 0. 0002≤x≤0. 0015、 0. 0001≤y≤0. 0012を満足する数 である)
で表される組成を有する金およびアルミニウム付活硫ィ匕亜鉛蛍光体力 なることを 特徴とする白色発光型 LEDランプ。
[3] 請求項 1または請求項 2記載の白色発光型 LEDランプにぉ 、て、
前記赤色発光蛍光体は、
一般式:(La , Eu , Sm ) O S
1-a-b a b 2 2
(式中、 aおよび bは 0. 01≤a≤0. 15、 0. 0001≤b≤0. 03を満足する数である) で表される糸且成を有するユーロピウムおよびサマリウム付活酸硫ィ匕ランタン蛍光体、 および
一般式: ZnS : Cu , Mn
V w
(式中、 vおよび wは 0. 0002≤v≤0. 001、 0. 005≤w≤0. 014を満足する数であ る)
で表される組成を有する銅およびマンガン付活硫ィ匕亜鉛蛍光体力 選ばれる少な
くとも 1種力 なることを特徴とする白色発光型 LEDランプ。
[4] 請求項 1ないし請求項 3のいずれか 1項記載の白色発光型 LEDランプにおいて、 前記赤色発光蛍光体は前記ユーロピウムおよびサマリウム付活酸硫化ランタン蛍 光体と前記銅およびマンガン付活硫ィ匕亜鉛蛍光体を共に含むことを特徴とする白色 発光型 LEDランプ。
[5] 請求項 1ないし請求項 4のいずれか 1項記載の白色発光型 LEDランプにおいて、 前記青色発光蛍光体は、
一般式:(Ml , Eu ) (PO ) -CI
l -c c 10 4 6 2
(式中、 Mlは Mg、 Ca、 Srおよび Baから選ばれる少なくとも 1種の元素を示し、 cは 0 . 005≤c≤0. 03を満足する数である)
で表される組成を有するユーロピウム付活ハロ燐酸塩蛍光体、および
一般式: m(M2 , Eu ) 0 ·ηΑ1 Ο
l -d d 2 3
(式中、 M2は Mg、 Ca、 Sr、 Baおよび Znから選ばれる少なくとも 1種の元素を示し、 d 、 mおよび nは 0. 05≤d≤0. 3、 0<m、 0く n、 0. 2≤m/n≤l. 5を満足する数で ある)
で表される組成を有するユーロピウム付活アルミン酸塩蛍光体力 選ばれる少なく とも 1種力 なることを特徴とする白色発光型 LEDランプ。
[6] 前記請求項 1な!、し請求項 5の 、ずれか 1項に記載の白色発光型 LEDランプを複 数個用いたことを特徴とするバックライト。
[7] 前記請求項 6のバックライトを用いたことを特徴とする液晶表示装置。