WO2006133956A2 - Elimination de minces couches polymeriques structurees par du plasma atmospherique - Google Patents
Elimination de minces couches polymeriques structurees par du plasma atmospherique Download PDFInfo
- Publication number
- WO2006133956A2 WO2006133956A2 PCT/EP2006/005801 EP2006005801W WO2006133956A2 WO 2006133956 A2 WO2006133956 A2 WO 2006133956A2 EP 2006005801 W EP2006005801 W EP 2006005801W WO 2006133956 A2 WO2006133956 A2 WO 2006133956A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resist layer
- substrate
- plasma
- mold
- electrode
- Prior art date
Abstract
L'invention concerne des procédés permettant de former une structure dans une couche de résine appliquée sur un substrat par un procédé d'impression par lithographie. Après estampillage et durcissement de la couche de résine dans les creux de la structure, la couche de résine restante est éliminée par l'action de plasma à pression atmosphérique.
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102005027948.1 | 2005-06-16 | ||
DE102005027948 | 2005-06-16 | ||
DE102005045331.7 | 2005-09-22 | ||
DE102005045331A DE102005045331A1 (de) | 2005-06-16 | 2005-09-22 | Entfernen von dünnen strukturierten Polymerschichten durch atmosphärisches Plasma |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2006133956A2 true WO2006133956A2 (fr) | 2006-12-21 |
WO2006133956A3 WO2006133956A3 (fr) | 2007-07-26 |
Family
ID=37309350
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2006/005801 WO2006133956A2 (fr) | 2005-06-16 | 2006-06-16 | Elimination de minces couches polymeriques structurees par du plasma atmospherique |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE102005045331A1 (fr) |
WO (1) | WO2006133956A2 (fr) |
Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5560777A (en) * | 1992-11-09 | 1996-10-01 | Goldstar Co., Ltd. | Apparatus for making a semiconductor |
US5772905A (en) * | 1995-11-15 | 1998-06-30 | Regents Of The University Of Minnesota | Nanoimprint lithography |
WO2000054107A1 (fr) * | 1999-03-11 | 2000-09-14 | Board Of Regents, The University Of Texas System | Lithogravure en photorepetition |
WO2003030252A2 (fr) * | 2001-09-28 | 2003-04-10 | Hrl Laboratories, Llc | Processus de production d'interconnexions |
WO2003087935A2 (fr) * | 2002-04-17 | 2003-10-23 | Clariant Gmbh | Couche de reserve de nanoimpression |
US20040266073A1 (en) * | 2003-02-06 | 2004-12-30 | Semiconductor Energy Laboratory Co., Ltd. | Method of manufacturing semiconductor device and display device |
US20050011752A1 (en) * | 2003-02-05 | 2005-01-20 | Semiconductor Energy Laboratory Co., Ltd. | Manufacturing method for wiring |
US20050100830A1 (en) * | 2003-10-27 | 2005-05-12 | Molecular Imprints, Inc. | Methods for fabricating patterned features utilizing imprint lithography |
EP1594002A2 (fr) * | 2004-01-16 | 2005-11-09 | Lg Electronics Inc. | Méthode pour réaliser un tampon à grande surface pour la nanolithographie par embossage |
-
2005
- 2005-09-22 DE DE102005045331A patent/DE102005045331A1/de not_active Ceased
-
2006
- 2006-06-16 WO PCT/EP2006/005801 patent/WO2006133956A2/fr active Application Filing
Patent Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5560777A (en) * | 1992-11-09 | 1996-10-01 | Goldstar Co., Ltd. | Apparatus for making a semiconductor |
US5772905A (en) * | 1995-11-15 | 1998-06-30 | Regents Of The University Of Minnesota | Nanoimprint lithography |
WO2000054107A1 (fr) * | 1999-03-11 | 2000-09-14 | Board Of Regents, The University Of Texas System | Lithogravure en photorepetition |
WO2003030252A2 (fr) * | 2001-09-28 | 2003-04-10 | Hrl Laboratories, Llc | Processus de production d'interconnexions |
WO2003087935A2 (fr) * | 2002-04-17 | 2003-10-23 | Clariant Gmbh | Couche de reserve de nanoimpression |
US20050011752A1 (en) * | 2003-02-05 | 2005-01-20 | Semiconductor Energy Laboratory Co., Ltd. | Manufacturing method for wiring |
US20040266073A1 (en) * | 2003-02-06 | 2004-12-30 | Semiconductor Energy Laboratory Co., Ltd. | Method of manufacturing semiconductor device and display device |
US20050100830A1 (en) * | 2003-10-27 | 2005-05-12 | Molecular Imprints, Inc. | Methods for fabricating patterned features utilizing imprint lithography |
EP1594002A2 (fr) * | 2004-01-16 | 2005-11-09 | Lg Electronics Inc. | Méthode pour réaliser un tampon à grande surface pour la nanolithographie par embossage |
Non-Patent Citations (2)
Title |
---|
JOHNSON S C ET AL: "Advances in step and flash imprint lithography" PROCEEDINGS OF THE SPIE, SPIE, BELLINGHAM, VA, US, Bd. 5037, 25. Februar 2003 (2003-02-25), Seiten 197-202, XP002314656 ISSN: 0277-786X * |
LE N V ET AL: "Selective dry etch process for step and flash imprint lithography" MICROELECTRONIC ENGINEERING, ELSEVIER PUBLISHERS BV., AMSTERDAM, NL, Bd. 78-79, März 2005 (2005-03), Seiten 464-473, XP004803664 ISSN: 0167-9317 * |
Also Published As
Publication number | Publication date |
---|---|
DE102005045331A1 (de) | 2006-12-28 |
WO2006133956A3 (fr) | 2007-07-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE60029827T2 (de) | Vorrichtung und verfahren in zusammenhang mit der herstellung von strukturen | |
TWI428710B (zh) | 壓印微影術 | |
DE10227054B4 (de) | Wiederverwendbare Druckform, Druckwerk und Druckmaschine damit sowie Verfahren zur Bebilderung der Druckform | |
DE102013206755B4 (de) | Nanoprägelithographieverfahren | |
EP2329319A1 (fr) | Procédé amélioré de nano-impression | |
DE60218755T2 (de) | Verfahren zur herstellung von strukturen auf nanomassstab in lichtaushärtbaren zusammensetzungen mit einem elektrischen feld | |
EP1646507A1 (fr) | Procede pour produire un motif sur une surface avec une haute resolution | |
US8163657B2 (en) | Process for adjusting the size and shape of nanostructures | |
DE19935558B4 (de) | Verfahren zur Erzeugung von Strukturen in einem Substrat im Nanometerbereich | |
DE60307516T2 (de) | Lithografieverfahren durch pressen eines substrats in einem nanoimprint-prozess | |
WO2006133956A2 (fr) | Elimination de minces couches polymeriques structurees par du plasma atmospherique | |
US8163656B2 (en) | Process for adjusting the size and shape of nanostructures | |
EP3134771B1 (fr) | Procédé et dispositif de marquage d'une nanostructure | |
WO2019180031A1 (fr) | Procédé de production et d'utilisation d'un substrat présentant une surface fonctionnalisée | |
DE102009023355A1 (de) | Verfahren zur Herstellung eines optoelektronischen Halbleiterbauteils | |
KR101049218B1 (ko) | 적용 가압력 제거를 이용한 미세 패턴 형성 방법 | |
DE102009018849B4 (de) | Masterstruktur zum Prägen und/oder Bedrucken eines Grundmaterials, Vorrichtung zum kontinuierlichen Prägen und/oder Bedrucken eines Grundmaterials und Verfahren zum Herstellen einer Masterstruktur zum Prägen und/oder Bedrucken eines Grundmaterials | |
DE10144579C2 (de) | Verfahren und Vorrichtung zur Herstellung von Fein- bis Mikrostrukturen und/oder komplexen Mikrosystemen | |
EP3552058B9 (fr) | Procédé, appareil et rouleau d'impression pour imprimer des micro- et/ou nanostructures | |
WO2015091961A1 (fr) | Procédé et dispositif de réalisation de surfaces structurées | |
DE102009046756A1 (de) | Verfahren zur Herstellung von regelmäßigen Nanostrukturen auf Festkörperoberflächen | |
DE102012209371A1 (de) | Siebdruckverfahren und Vorrichtung zum Ausführen eines Siebdruckverfahrens | |
EP2870511A1 (fr) | Procédé et dispositif pour le gaufrage | |
EP2286981A1 (fr) | Dispositif et procédé destinés à l'imprégnation à chaud d'une couche de polymère | |
DE102007044505A1 (de) | Verfahren zum lithographischen Erzeugen von Nano- und/oder Mikrostrukturen, Stempel sowie Substrat |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWW | Wipo information: withdrawn in national office |
Country of ref document: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 06754406 Country of ref document: EP Kind code of ref document: A2 |