WO2006110100A1 - Boron steel grade for induction hardening and shaft - Google Patents
Boron steel grade for induction hardening and shaftInfo
- Publication number
- WO2006110100A1 WO2006110100A1 PCT/SE2006/050059 SE2006050059W WO2006110100A1 WO 2006110100 A1 WO2006110100 A1 WO 2006110100A1 SE 2006050059 W SE2006050059 W SE 2006050059W WO 2006110100 A1 WO2006110100 A1 WO 2006110100A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- induction hardening
- molybdenum
- nickel
- boron steel
- boron
- Prior art date
Links
- 230000006698 induction Effects 0.000 title claims abstract description 25
- 229910000712 Boron steel Inorganic materials 0.000 title claims abstract description 20
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 claims abstract description 53
- 229910052759 nickel Inorganic materials 0.000 claims abstract description 26
- ZOKXTWBITQBERF-UHFFFAOYSA-N Molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 claims abstract description 24
- 229910052750 molybdenum Inorganic materials 0.000 claims abstract description 24
- 239000011733 molybdenum Substances 0.000 claims abstract description 24
- 239000012535 impurity Substances 0.000 claims abstract description 6
- ZOXJGFHDIHLPTG-UHFFFAOYSA-N Boron Chemical compound [B] ZOXJGFHDIHLPTG-UHFFFAOYSA-N 0.000 claims description 7
- 229910052796 boron Inorganic materials 0.000 claims description 7
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims description 5
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 claims description 5
- NINIDFKCEFEMDL-UHFFFAOYSA-N Sulfur Chemical compound [S] NINIDFKCEFEMDL-UHFFFAOYSA-N 0.000 claims description 5
- 239000005864 Sulphur Substances 0.000 claims description 5
- 239000004411 aluminium Substances 0.000 claims description 5
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims description 5
- 229910052782 aluminium Inorganic materials 0.000 claims description 5
- 229910052799 carbon Inorganic materials 0.000 claims description 5
- 239000011572 manganese Substances 0.000 claims description 5
- 239000010936 titanium Substances 0.000 claims description 5
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 claims description 4
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 claims description 4
- 229910052748 manganese Inorganic materials 0.000 claims description 4
- 229910052719 titanium Inorganic materials 0.000 claims description 4
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 claims description 3
- 229910052698 phosphorus Inorganic materials 0.000 claims description 3
- 239000011574 phosphorus Substances 0.000 claims description 3
- 229910052710 silicon Inorganic materials 0.000 claims description 3
- 239000010703 silicon Substances 0.000 claims description 3
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims 2
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 claims 2
- 229910052742 iron Inorganic materials 0.000 claims 1
- 239000000203 mixture Substances 0.000 abstract description 14
- 229910000831 Steel Inorganic materials 0.000 abstract description 11
- 239000010959 steel Substances 0.000 abstract description 11
- 239000000956 alloy Substances 0.000 abstract description 6
- 229910045601 alloy Inorganic materials 0.000 abstract description 5
- 230000003068 static effect Effects 0.000 abstract description 5
- 230000001965 increasing effect Effects 0.000 abstract description 4
- 230000000750 progressive effect Effects 0.000 abstract description 4
- 238000000034 method Methods 0.000 abstract description 2
- 230000000694 effects Effects 0.000 description 6
- 239000000126 substance Substances 0.000 description 6
- PNEYBMLMFCGWSK-UHFFFAOYSA-N Alumina Chemical compound [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 3
- 238000001816 cooling Methods 0.000 description 3
- 238000002474 experimental method Methods 0.000 description 3
- 238000010438 heat treatment Methods 0.000 description 3
- CADICXFYUNYKGD-UHFFFAOYSA-N sulfanylidenemanganese Chemical compound [Mn]=S CADICXFYUNYKGD-UHFFFAOYSA-N 0.000 description 3
- 239000006104 solid solution Substances 0.000 description 2
- 238000005728 strengthening Methods 0.000 description 2
- 238000002604 ultrasonography Methods 0.000 description 2
- 230000002411 adverse Effects 0.000 description 1
- 238000005275 alloying Methods 0.000 description 1
- 230000015572 biosynthetic process Effects 0.000 description 1
- 230000001419 dependent effect Effects 0.000 description 1
- 238000010586 diagram Methods 0.000 description 1
- 230000001771 impaired effect Effects 0.000 description 1
- 230000001939 inductive effect Effects 0.000 description 1
- 238000011835 investigation Methods 0.000 description 1
- 238000004519 manufacturing process Methods 0.000 description 1
- 239000000463 material Substances 0.000 description 1
- 239000011159 matrix material Substances 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 229920001515 polyalkylene glycol Polymers 0.000 description 1
- 229920002959 polymer blend Polymers 0.000 description 1
- 230000008092 positive effect Effects 0.000 description 1
- 230000002265 prevention Effects 0.000 description 1
- 238000003303 reheating Methods 0.000 description 1
- 239000002344 surface layer Substances 0.000 description 1
- 238000005496 tempering Methods 0.000 description 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 1
- 230000003313 weakening effect Effects 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
Definitions
- the present invention relates to a boron steel grade according to the introductory part of the attached claim 1.
- the invention also relates to a shaft made of boron steel according to the introductory part of the attached claim 6.
- Low-alloy boron steel is used inter alia for shafts which by induction hardening of a surface zone are provided with increased fatigue and static strength but also a wear-resistant surface layer.
- Induction hardening of this kind causes in the surface zone compressive stresses which counteract the occurrence of fatigue cracks in this surface zone and thereby have a positive effect on fatigue strength.
- the relationship between the magnitude of the compressive stresses and the fatigue strength is unambiguous. The greater the compressive stresses, the higher the fatigue strength.
- the compressive stresses in the surface zone are balanced by tensile stresses in central portions (the core).
- Tensile stresses in the core do not normally affect strength, since the level of stresses arising from imposed loads is low in specifically the core.
- stationary induction hardening also called single-shot hardening, i.e. a hardening operation where the total volume to be hardened is first heated to the hardening temperature and is thereafter cooled immediately or after a certain delay
- the compressive stresses in the surface zone become particularly high and the fatigue strength becomes better than is achieved by progressive induction hardening where heating and subsequent cooling are effected during continuous mutual movement between inductor/cooling shower and the workpiece which is to be hardened.
- the stresses, not least the tensile stresses in the core in the case of stationary induction hardening may become so great during the actual hardening process that cracks (central cracks) occur in the core.
- a typical and representative ratio is about 20,000 load cycles at 20 kNm torsional fatigue for progressive induction hardening as against about 80,000 load cycles at 20 kNm torsional fatigue for stationary induction hardening.
- the object of the present invention is to provide low-alloy boron steel which can be induction-hardened statically without central cracks occurring.
- Fig. 1 depicts a compilation in tabular form concerning Hie incidence of cracks as a function of composition, where primarily the molybdenum and nickel contents clearly vary
- Fig. 2 depicts in diagram form the incidence of cracks as a function of molybdenum and nickel contents
- FIG. 3 depicts in an axial section a driveshaft for which experiments with steel grades according to the present invention were carried out.
- the steel grades according to the invention are low-allow boron steel, and steel grades according to the invention with the range of composition according to the invention appear in Table 1 together with a corresponding known steel grade.
- Carbon which has a substantial influence on induction hardening characteristics, is present in contents of between 0.30 and 0.50%, resulting in desired strength after hardening. A carbon content amounting to 0.38-0.45% is preferred.
- Silicon is present in an amount of 0.15-0.40%, preferably more than 0.15% up to 0.40%, and is primarily added as a carrier for other alloying elements, but also has some strengthening effect.
- Manganese is present in an amount of 1.10 up to 1.50%, preferably more than 1.10% up to 1.50%, and has strengthening effects partly by increasing the hardenability, which, where there is great hardness depth, may affect the hardness depth in induction hardening. Manganese is also added in order to bind sulphur which would otherwise have adverse effects on impact strength.
- the phosphorus content, ⁇ 0.035%, has to be kept low to prevent brittleness and hardness cracks due to grain boundary weakening.
- MnS manganese sulphide
- Chrome is present in an amount ⁇ 0.5%, preferably more than 0.2% and less than 0.5%. Chrome increases hardenability and reduces the risk of decarburisation.
- Molybdenum in an amount of 0.030% and up to 0.15% has according to the invention proved to be able, together with certain contents of nickel as below, to prevent the occurrence of central cracks, inter alia in static induction hardening.
- the molybdenum content is normally not even specified for boron steel of this kind. It is also likely that such an addition of molybdenum in combination with nickel also reduces the risk of hardness cracks in other grades.
- Molybdenum in a quantity of 0.05 up to 0.15% is preferred.
- Nickel in an amount of 0.15% up to 0.40% has proved, together with molybdenum as above, according to the invention, to be able to prevent the occurrence of central cracks, inter alia in static induction hardening.
- the nickel content is likewise not usually specified.
- Nickel is regarded as an impurity. It is also likely that such an addition of molybdenum in combination with nickel also reduces the risk of hardness cracks in other grades.
- Nickel in an amount of more than 0.20 up to 0.40% is preferred.
- Titanium in certain contents is needed for keeping a certain content of boron in solid solution in the steel with a view to improving the hardening characteristics. Titanium should therefore be present in an amount of 0.020-0.050%. Aluminium is a deoxidant and is therefore present in low contents. Aluminium impairs the fatigue strength by forming aluminium oxide, and aluminium contents should be kept ⁇ 0.050%.
- the desirable content in solid solution is at least 0.0005%, while the total content should be limited to less than 0.004%.
- molybdenum and nickel constitute impurities which are not even specified in a standard composition.
- the composition ranges for molybdenum and nickel which result in the crack-eliminating effect according to the invention nevertheless comprise contents which clearly exceed prevailing impurity levels.
- Fig. 1 shows the incidence of cracks on a large number of driveshafts from a large number of charges with mutual varying chemical composition
- "No.” denotes the number of shafts in which cracks were detected
- “Tot.” the total number of shafts examined for each steel charge
- “Incid. %” the ratio between "No.” and “Tot”, i.e. the proportion of shafts with detected cracks.
- Fig. 2 shows the incidence of cracks, "Crack Incidence %", as a function of molybdenum content and nickel content, although for manufacturing reasons the effect of molybdenum content or nickel content would be isolated.
- the minimum contents indicated have been adjusted by a small margin to the respective content combinations of 0.035% molybdenum/0.167% nickel and 0.038 molybdenum/0.188% nickel, which resulted in no cracks.
- the preferred minimum contents have been provided with a margin upwards relative to the minimum contents extracted.
- An upper content limit has also been set for both molybdenum and nickel. This is partly for cost reasons and for preventing disadvantages, e.g. impaired machinability, which occur at increasing molybdenum and nickel contents.
- Scania boron steel TB 1639 as a low-alloy material is specified in Table 1 below.
- Low-alloy compositions are usually stated without contents of molybdenum and nickel, which substances are to be regarded as common impurities.
- a general composition according to the invention, a preferred composition and a detailed composition which in experiments resulted in lack of cracks are also specified.
- Table 1 Composition of boron steel according to the state of the art and the invention.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Heat Treatment Of Articles (AREA)
- Shafts, Cranks, Connecting Bars, And Related Bearings (AREA)
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN2006800116181A CN101155941B (zh) | 2005-04-12 | 2006-04-06 | 用于感应加热淬火和轴的硼钢种 |
JP2008506416A JP2008537982A (ja) | 2005-04-12 | 2006-04-06 | 誘導硬化用ボロン鋼および軸 |
BRPI0608675-6A BRPI0608675A2 (pt) | 2005-04-12 | 2006-04-06 | grau de aÇo boro para tÊmpera por induÇço e eixo |
EP06717138A EP1871917A1 (en) | 2005-04-12 | 2006-04-06 | Boron steel grade for induction hardening and shaft |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SE0500812A SE527221C2 (sv) | 2005-04-12 | 2005-04-12 | Borstålsort för induktionshärdning jämte axel |
SE0500812-3 | 2005-04-12 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2006110100A1 true WO2006110100A1 (en) | 2006-10-19 |
Family
ID=35653953
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/SE2006/050059 WO2006110100A1 (en) | 2005-04-12 | 2006-04-06 | Boron steel grade for induction hardening and shaft |
Country Status (6)
Country | Link |
---|---|
EP (1) | EP1871917A1 (zh) |
JP (1) | JP2008537982A (zh) |
CN (1) | CN101155941B (zh) |
BR (1) | BRPI0608675A2 (zh) |
SE (1) | SE527221C2 (zh) |
WO (1) | WO2006110100A1 (zh) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN101624675B (zh) * | 2009-07-30 | 2011-02-16 | 莱芜钢铁股份有限公司 | 履带链轨销轴用45bm钢及其制造方法 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH08253842A (ja) * | 1995-03-16 | 1996-10-01 | Nippon Steel Corp | 捩り疲労強度の優れた高周波焼入れ軸部品用鋼材 |
JPH08283910A (ja) * | 1995-04-17 | 1996-10-29 | Nippon Steel Corp | 冷間加工性と捩り疲労強度特性を兼備した高周波焼入れ軸部品用鋼材 |
JPH10195589A (ja) * | 1996-12-26 | 1998-07-28 | Nippon Steel Corp | 高捩り疲労強度高周波焼入れ鋼材 |
JPH11181542A (ja) * | 1997-12-16 | 1999-07-06 | Nippon Steel Corp | 冷間加工性と高周波焼入れ性に優れた高周波焼入れ用鋼材とその製造方法 |
EP1553197A1 (en) * | 2002-10-18 | 2005-07-13 | JFE Steel Corporation | Steel material for mechanical structure excellent in suitability for rolling, quenching crack resistance, and torsional property and drive shaft |
Family Cites Families (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2725747B2 (ja) * | 1990-11-16 | 1998-03-11 | 大同特殊鋼株式会社 | 高周波焼入れ用鋼材 |
JP2916069B2 (ja) * | 1993-09-17 | 1999-07-05 | 新日本製鐵株式会社 | 高強度高周波焼入れ軸部品 |
JP3774697B2 (ja) * | 2002-12-04 | 2006-05-17 | 新日本製鐵株式会社 | 高強度高周波焼き入れ用鋼材及びその製造方法 |
JP2005048211A (ja) * | 2003-07-30 | 2005-02-24 | Jfe Steel Kk | 疲労特性に優れた鋼材の製造方法 |
-
2005
- 2005-04-12 SE SE0500812A patent/SE527221C2/sv not_active IP Right Cessation
-
2006
- 2006-04-06 JP JP2008506416A patent/JP2008537982A/ja active Pending
- 2006-04-06 WO PCT/SE2006/050059 patent/WO2006110100A1/en active Application Filing
- 2006-04-06 CN CN2006800116181A patent/CN101155941B/zh not_active Expired - Fee Related
- 2006-04-06 EP EP06717138A patent/EP1871917A1/en not_active Withdrawn
- 2006-04-06 BR BRPI0608675-6A patent/BRPI0608675A2/pt not_active IP Right Cessation
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH08253842A (ja) * | 1995-03-16 | 1996-10-01 | Nippon Steel Corp | 捩り疲労強度の優れた高周波焼入れ軸部品用鋼材 |
JPH08283910A (ja) * | 1995-04-17 | 1996-10-29 | Nippon Steel Corp | 冷間加工性と捩り疲労強度特性を兼備した高周波焼入れ軸部品用鋼材 |
JPH10195589A (ja) * | 1996-12-26 | 1998-07-28 | Nippon Steel Corp | 高捩り疲労強度高周波焼入れ鋼材 |
JPH11181542A (ja) * | 1997-12-16 | 1999-07-06 | Nippon Steel Corp | 冷間加工性と高周波焼入れ性に優れた高周波焼入れ用鋼材とその製造方法 |
EP1553197A1 (en) * | 2002-10-18 | 2005-07-13 | JFE Steel Corporation | Steel material for mechanical structure excellent in suitability for rolling, quenching crack resistance, and torsional property and drive shaft |
Non-Patent Citations (4)
Title |
---|
PATENT ABSTRACTS OF JAPAN vol. 198, no. 812 28 July 1998 (1998-07-28) * |
PATENT ABSTRACTS OF JAPAN vol. 199, no. 702 1 October 2001 (2001-10-01) * |
PATENT ABSTRACTS OF JAPAN vol. 199, no. 702 29 October 1996 (1996-10-29) * |
PATENT ABSTRACTS OF JAPAN vol. 199, no. 912 6 July 1999 (1999-07-06) * |
Also Published As
Publication number | Publication date |
---|---|
EP1871917A1 (en) | 2008-01-02 |
CN101155941A (zh) | 2008-04-02 |
SE0500812L (sv) | 2006-01-24 |
BRPI0608675A2 (pt) | 2010-01-19 |
CN101155941B (zh) | 2010-09-08 |
SE527221C2 (sv) | 2006-01-24 |
JP2008537982A (ja) | 2008-10-02 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP3719149B1 (en) | High-hardness steel product and method of manufacturing the same | |
EP0643148B1 (en) | Steel material for induction-hardened shaft part and shaft part made therefrom | |
EP0949340B1 (en) | Steel having excellent outer surface scc resistance for pipeline | |
JP2002256382A (ja) | 耐摩耗鋼板及びその製造方法 | |
KR20090102791A (ko) | 고온 내마모성 및 굽힘 가공성이 우수한 내마모 강판 및 그 제조 방법 | |
US9757780B2 (en) | Electric resistance welded steel pipe excellent in deformability and fatigue properties after quenching | |
US6383311B1 (en) | High strength drive shaft and process for producing the same | |
JP2916069B2 (ja) | 高強度高周波焼入れ軸部品 | |
JP3432950B2 (ja) | 冷間加工性と捩り疲労強度特性を兼備した高周波焼入れ軸部品用鋼材 | |
US6270596B1 (en) | Process for producing high strength shaft | |
JP4728884B2 (ja) | 低サイクル疲労特性に優れた高周波輪郭焼入れ鋼材及び高周波輪郭焼入れ部品 | |
JPH05163563A (ja) | エンドミル用高速度鋼 | |
WO2006110100A1 (en) | Boron steel grade for induction hardening and shaft | |
JP3304550B2 (ja) | 切欠き付き高周波焼入れ部品の製造方法 | |
JP2007332440A (ja) | 低サイクル疲労特性に優れた高周波焼入れ鋼材及び高周波焼入れ部品 | |
JP3432944B2 (ja) | 捩り疲労強度の優れた高周波焼入れ軸部品用鋼材 | |
JPH08311615A (ja) | 高寿命高周波焼入れ軸受用鋼材 | |
JP5505264B2 (ja) | 低サイクル疲労特性に優れた高周波輪郭焼入れ鋼材及び高周波輪郭焼入れ部品 | |
JP2952318B2 (ja) | 高周波焼入用高強度鋼 | |
JPH0796696B2 (ja) | 合金工具鋼 | |
JPH0978127A (ja) | 高強度高靭性機械構造用軸状部品の製造方法 | |
JPH07179988A (ja) | 高温強度の優れた熱間工具鋼 | |
JPH0557350B2 (zh) | ||
JP2004300551A (ja) | 高強度中炭素鋼 | |
JPH0726348A (ja) | 耐ころがり疲労損傷性に優れた高強度レールおよびその製造法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 200680011618.1 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
ENP | Entry into the national phase |
Ref document number: 2008506416 Country of ref document: JP Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2006717138 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
NENP | Non-entry into the national phase |
Ref country code: RU |
|
WWP | Wipo information: published in national office |
Ref document number: 2006717138 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: PI0608675 Country of ref document: BR Kind code of ref document: A2 |