WO2006058585A1 - Kunststoffholkörper, insbesondere kunststoffrohr - Google Patents
Kunststoffholkörper, insbesondere kunststoffrohr Download PDFInfo
- Publication number
- WO2006058585A1 WO2006058585A1 PCT/EP2005/011500 EP2005011500W WO2006058585A1 WO 2006058585 A1 WO2006058585 A1 WO 2006058585A1 EP 2005011500 W EP2005011500 W EP 2005011500W WO 2006058585 A1 WO2006058585 A1 WO 2006058585A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- plastic
- body according
- layers
- layer
- reinforcement
- Prior art date
Abstract
Description
Claims