WO2004048641A1 - Processus permettant d'ameliorer l'aptitude au façonnage a chaud d'un lingot de superalliage coule - Google Patents

Processus permettant d'ameliorer l'aptitude au façonnage a chaud d'un lingot de superalliage coule Download PDF

Info

Publication number
WO2004048641A1
WO2004048641A1 PCT/US2003/037933 US0337933W WO2004048641A1 WO 2004048641 A1 WO2004048641 A1 WO 2004048641A1 US 0337933 W US0337933 W US 0337933W WO 2004048641 A1 WO2004048641 A1 WO 2004048641A1
Authority
WO
WIPO (PCT)
Prior art keywords
ingot
canister
metal
set forth
metal powder
Prior art date
Application number
PCT/US2003/037933
Other languages
English (en)
Inventor
Gregory J. Del Corso
E. Lance Buck
Mohamed K. Mohamdein
Original Assignee
Crs Holdings, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Crs Holdings, Inc. filed Critical Crs Holdings, Inc.
Priority to AU2003297577A priority Critical patent/AU2003297577A1/en
Priority to EP03812051A priority patent/EP1565594A1/fr
Publication of WO2004048641A1 publication Critical patent/WO2004048641A1/fr

Abstract

La présente invention concerne un processus de préparation de lingot de superalliage à base de Ni, Fe et Co en vue d'un façonnage à chaud et d'un ensemble lingot fabriqué par ce processus. Ce processus consiste à prendre un lingot coulé et à introduire ce lingot dans un récipient d'acier dimensionné de façon à contenir complètement ce lingot. Le lingot est placé à l'intérieur de ce récipient d'acier de manière à laisser un espace entre ce lingot et le récipient d'acier. Après le placement du lingot dans le récipient d'acier, de la poudre de métal est versée dans cet espace. Cette poudre de métal est sélectionnée de façon à se lier immédiatement avec les surfaces du lingot et du récipient d'acier. Puis, le récipient d'acier est refermé avec le lingot et la poudre de métal présents à l'intérieur. Le gaz et l'humidité sont retirés de l'intérieur de ce récipient d'acier. Ce récipient d'acier avec le lingot et la poudre de métal présents à l'intérieur est pressé à chaud ne manière isostatique afin de former un ensemble lingot possédant une chemise tout autour des surfaces longitudinales et des surfaces d'extrémité de ce lingot. L'ensemble lingot produit à partir de ce processus est immédiatement façonné à chaud sans dommages importants causé au lingot par des craquelures ou des craquelures en quadrillages.
PCT/US2003/037933 2002-11-26 2003-11-26 Processus permettant d'ameliorer l'aptitude au façonnage a chaud d'un lingot de superalliage coule WO2004048641A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU2003297577A AU2003297577A1 (en) 2002-11-26 2003-11-26 Process for improving the hot workability of a cast superalloy ingot
EP03812051A EP1565594A1 (fr) 2002-11-26 2003-11-26 Processus permettant d'ameliorer l'aptitude au faconnage a chaud d'un lingot de superalliage coule

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US42920902P 2002-11-26 2002-11-26
US60/429,209 2002-11-26

Publications (1)

Publication Number Publication Date
WO2004048641A1 true WO2004048641A1 (fr) 2004-06-10

Family

ID=32393524

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2003/037933 WO2004048641A1 (fr) 2002-11-26 2003-11-26 Processus permettant d'ameliorer l'aptitude au façonnage a chaud d'un lingot de superalliage coule

Country Status (4)

Country Link
US (1) US20040105774A1 (fr)
EP (1) EP1565594A1 (fr)
AU (1) AU2003297577A1 (fr)
WO (1) WO2004048641A1 (fr)

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8230899B2 (en) * 2010-02-05 2012-07-31 Ati Properties, Inc. Systems and methods for forming and processing alloy ingots
US9267184B2 (en) 2010-02-05 2016-02-23 Ati Properties, Inc. Systems and methods for processing alloy ingots
US10207312B2 (en) 2010-06-14 2019-02-19 Ati Properties Llc Lubrication processes for enhanced forgeability
US8789254B2 (en) 2011-01-17 2014-07-29 Ati Properties, Inc. Modifying hot workability of metal alloys via surface coating
US9120150B2 (en) 2011-12-02 2015-09-01 Ati Properties, Inc. Endplate for hot isostatic pressing canister, hot isostatic pressing canister, and hot isostatic pressing method
US9539636B2 (en) 2013-03-15 2017-01-10 Ati Properties Llc Articles, systems, and methods for forging alloys
US9027374B2 (en) 2013-03-15 2015-05-12 Ati Properties, Inc. Methods to improve hot workability of metal alloys
JP6645215B2 (ja) 2016-01-28 2020-02-14 大同特殊鋼株式会社 合金塊の製造方法
CN111014622B (zh) * 2019-12-25 2021-12-31 广西大学 一种低熔点金属和异种高熔点金属扩散偶的制备方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3398448A (en) * 1966-09-12 1968-08-27 Int Nickel Co Process for coating steel with nickel
US4567936A (en) * 1984-08-20 1986-02-04 Kaiser Aluminum & Chemical Corporation Composite ingot casting
GB2239200A (en) * 1989-04-07 1991-06-26 Ici Plc Making explosively clad metal sheet
US5462575A (en) * 1993-12-23 1995-10-31 Crs Holding, Inc. Co-Cr-Mo powder metallurgy articles and process for their manufacture
EP1091021A1 (fr) * 1999-10-04 2001-04-11 General Electric Company Procédé de fabrication d'un revêtement au moyen d'une mousse
WO2002079534A1 (fr) * 2001-03-27 2002-10-10 Crs Holdings, Inc. Acier inoxydable durcissable par precipitation et ultra-resistant et bande allongee produite avec cet acier

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3109602C2 (de) * 1981-01-31 1983-01-13 Klöckner-Werke AG, 4100 Duisburg Verfahren und Vorrichtung zum Herstellen plattierter Blöcke
EP0283877B1 (fr) * 1987-03-25 1993-06-23 Nippon Steel Corporation Procédé pour la fabrication de tubes de métal enrobé.

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3398448A (en) * 1966-09-12 1968-08-27 Int Nickel Co Process for coating steel with nickel
US4567936A (en) * 1984-08-20 1986-02-04 Kaiser Aluminum & Chemical Corporation Composite ingot casting
GB2239200A (en) * 1989-04-07 1991-06-26 Ici Plc Making explosively clad metal sheet
US5462575A (en) * 1993-12-23 1995-10-31 Crs Holding, Inc. Co-Cr-Mo powder metallurgy articles and process for their manufacture
EP1091021A1 (fr) * 1999-10-04 2001-04-11 General Electric Company Procédé de fabrication d'un revêtement au moyen d'une mousse
WO2002079534A1 (fr) * 2001-03-27 2002-10-10 Crs Holdings, Inc. Acier inoxydable durcissable par precipitation et ultra-resistant et bande allongee produite avec cet acier

Also Published As

Publication number Publication date
EP1565594A1 (fr) 2005-08-24
US20040105774A1 (en) 2004-06-03
AU2003297577A1 (en) 2004-06-18

Similar Documents

Publication Publication Date Title
EP0388968B1 (fr) Procédé de production de métaux revêtus
EP2969297B1 (fr) Forgeage d'alliages avec coussin / tampon lubrifiant, résistant thermiquement et réduisant la friction
US4706361A (en) Process for the hot-forming of at least one sheet made of a material that is difficult to work
EP0202735B1 (fr) Procédé pour la fabrication d'une ébauche composite à partir de poudre métallique
EP2531627B1 (fr) Systèmes et procédés de formage et de traitement de lingots d'alliage
EP0283877B1 (fr) Procédé pour la fabrication de tubes de métal enrobé.
US4077109A (en) Hot working of metal powders
US9327349B2 (en) Endplate for hot isostatic pressing canister, hot isostatic pressing canister, and hot isostatic pressing method
US5788142A (en) Process for joining, coating or repairing parts made of intermetallic material
JP2005506200A (ja) クラッドパイプおよびチューブを製造するための複合ビレットおよびその製造方法
US20040105774A1 (en) Process for improving the hot workability of a cast superalloy ingot
US3834003A (en) Method of particle ring-rolling for making metal rings
US3866303A (en) Method of making cross-rolled powder metal discs
US3982904A (en) Metal rings made by the method of particle ring-rolling
US20070092394A1 (en) Supersolvus hot isostatic pressing and ring rolling of hollow powder forms
CN112958626A (zh) 一种适用于TiAl合金轧制的包套及其制备方法
JP4133078B2 (ja) 繊維強化金属の製造方法
JP2580099B2 (ja) 熱間静水圧プレス方法
JP2580100B2 (ja) 熱間静水圧プレス方法
JPS61223106A (ja) 高合金クラツド製品の製造方法
EP0384629A2 (fr) Articles composites et procédé pour leur préparation
US3798742A (en) Method for hot working
AU2012346363B2 (en) Endplate for hot isostatic pressing canister, hot isostatic pressing canister, and hot isostatic pressing method
JPH0421748A (ja) 溶製金属の結晶粒微細化方法
JPH07278610A (ja) 熱間静水圧プレス処理材の熱間押出方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2003812051

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 2003812051

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 2003812051

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP