WO2004000458A1 - 改質ガス中の一酸化炭素の選択酸化触媒 - Google Patents

改質ガス中の一酸化炭素の選択酸化触媒 Download PDF

Info

Publication number
WO2004000458A1
WO2004000458A1 PCT/JP2002/006278 JP0206278W WO2004000458A1 WO 2004000458 A1 WO2004000458 A1 WO 2004000458A1 JP 0206278 W JP0206278 W JP 0206278W WO 2004000458 A1 WO2004000458 A1 WO 2004000458A1
Authority
WO
WIPO (PCT)
Prior art keywords
alumina
carbon monoxide
selective oxidation
catalyst
reformed gas
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2002/006278
Other languages
English (en)
French (fr)
Inventor
Masaru Kagawa
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tanaka Kikinzoku Kogyo KK
Original Assignee
Tanaka Kikinzoku Kogyo KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tanaka Kikinzoku Kogyo KK filed Critical Tanaka Kikinzoku Kogyo KK
Priority to AU2002315872A priority Critical patent/AU2002315872A1/en
Priority to PCT/JP2002/006278 priority patent/WO2004000458A1/ja
Priority to JP2004515455A priority patent/JPWO2004000458A1/ja
Publication of WO2004000458A1 publication Critical patent/WO2004000458A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

改質ガス中の一酸化炭素を酸素ガスによって選択的に酸化する触媒である。一方の一酸化炭素選択酸化触媒は、ルテニウム及び／又は白金を、αアルミナを含有するアルミナ担体に担持して成り、且つこのアルミナ担体中に含まれるナトリウムがＮａ2Ｏ換算で０．０７％未満である。　他方の一酸化炭素選択酸化触媒は、ルテニウム及び／又は白金をαアルミナを含有するアルミナ担体に担持し、更に、このアルミナ担体を、マグネシウムを含有する支持体に支持して成り、ルテニウム及び／又は白金を担持したアルミナ担体中に含まれるマグネシウムが、ＭｇＯ換算で０．０４％未満である。

Description

明細書 改質ガス中の一酸化炭素の選択酸化触媒
技術分野
本発明は、 改質ガス中の一酸化炭素を選択的に酸化する触媒に係り、 更に詳細には、 低温で作動する燃料電池、 特に固体高分子型燃料電池に 用いられる改質ガス中の一酸化炭素を選択酸化する触媒に関する。
本発明の触媒によれば、 改質ガス中の一酸化炭素が選択的に酸化され るので、 かかる燃料電池を低温においても効果的に作動させることがで きる。 背景技術
従来、 燃料電池用の燃料ガスと しては、 コス ト面を考慮して、 メタン やプロパンなどの天然ガスの炭化水素、 メタノール等のアルコール又は ナフサ等を水蒸気改質して得られる改質ガスが広く用いられている。 か かる改質ガスには、 水素や二酸化炭素など以外にも一酸化炭素が含まれ ており、 シフ ト反応で処理した後であっても、 約 1 V o 1 %の一酸化炭 素が含まれていることが知られている。
かかる副生一酸化炭素は、 溶融炭酸塩型などの高温作動型燃料電池で は、 燃料と しても利用されるが、 燐酸型や固体高分子型の低温作動型燃 料電池では、 電極触媒である白金系触媒に対して触媒毒作用を呈し、 特 に燐酸型燃料電池より も低温で運転される固体高分子型燃料電池におい ては、 改質ガス中に共存する一酸化炭素による触媒被毒が著しく、 発電 効率の低下という問題が生じた。
そして、 このような問題に対し、 従来は、 種々の白金族金属を用いた アルミナ触媒が提案されていた。
しかしながら、 かかる白金族金属を用いたアルミナ触媒にあっては、 酸素による酸化反応の選択性や活性が低いため、 改質ガスの主成分であ り燃料ガスとなる水素が同時に酸化浪費されてしまい、 燃料利用効率の 低下を引き起こすという問題点があった。
また、 固体高分子型燃料電池においては、 改質ガスを用いながら要求 される発電効率を得るには、 共存する一酸化炭素を当初の約 1 V o 1 °/0 からその 1 1 0 0程度以下に低減した後に供給する必要があるが、 上 記従来の白金一アルミナ系触媒では、 一酸化炭素の酸化低減が十分でな く、 残留する一酸化炭素により発電効率の劣化を招いていた。
更に、 本発明者らがアルミナを担体とする一酸化炭素選択酸化触媒に つき検討加えたところ、 アルミナ担体に特定元素の酸化物などが一定量 以上含まれると、 かかる選択酸化触媒の活性が著しく減じられることを 知見した。 ' 発明の開示
本発明は、 このよ うな従来技術の有する課題に鑑みてなされたもので あり、 その目的とするところは、 改質ガス中の一酸化炭素を選択的に酸 化して低減し、 良好な燃料利用効率や発電効率を実現し得る一酸化炭素 選択酸化触媒を提供することにある。
本発明者らは、 上記目的を達成すべく鋭意検討を重ねた結果、 ルテニ ゥムゃ白金を、 特定不純物含有量を適切に制御したアルミナ担体に担持 することにより、 酸素ガスが一酸化炭素に対して過剰に存在する条件下 で、 優れた一酸化炭素の選択的酸化を行うことを見出し、 本発明を完成 するに至った。
即ち、 本発明の一酸化炭素選択酸化触媒は、 改質ガス中の一酸化炭素 を酸素ガスによつて選択的に酸化する触媒であって、
ルテニウム及び/又は白金を αアルミナを含有するアルミナ担体に担 持して成り、 且つこのアルミナ担体中に含まれるナ ト リ ゥムが N a 2〇換 算で 0 . 0 7 %未満であることを特徴とする。
更に、 本発明の更に他の一酸化炭素選択酸化触媒は、 改質ガス中の一 酸化炭素を酸素ガスによって選択的に酸化する触媒であって、
ルテェゥム及び Z又は白金をひアルミナを含有するアルミナ担体に担 持し、 更に、 このアルミナ担体をマグネシウムを含有する支持体に支持 して成り、
上記ルテェゥム及び z又は白金を担持したアルミナ担体中に含まれる マグネシウムが、 M g O換算で 0 . 0 4 %未満であることを特徴とする。 更にまた、 本発明の更に他の一酸化炭素選択酸化触媒の好適形態は、 上記ルテニウム及び Z又は白金を担持したアルミナ担体中にナ ト リ ウム が含まれ、 そのナ ト リ ウム含有量が N a 2〇換算で 0 . 0 7 %未満である ことを特徴とする
本発明の選択酸化触媒が、 一酸化炭素 （C O ) の優れた選択酸化性を 発揮する理由の詳細は必ずしも明らかではないが、 現時点では以下のよ うに推察される。
即ち、 本発明では、 アルミナを含有する担体を用いることによ り、 触媒金属であるルテニウム （R u ) と 白金 （P t ) が該担体の最表面近 傍に存在するよ うにした。
このよ うに、 触媒金属を担体表面に局在化させることによって、 C O の酸化が起こる温度を低温側にシフ トさせることができ、 他の反応に対 する選択性を向上でき、 これにより、 反応後の改質ガス中の C O濃度を 低減させ、 且つ水素の消費を防ぐことができるものと思われる。
一般に、 ガス中に水蒸気が混入することによ り水蒸気吸着が起こ り、 c Oの酸化が起こる温度が高温側にシフ トされるが、 αアルミナを用い ることによ り、 その吸着による反応温度の高温側へのシフ トを回避でき る。 この結果、 C ο酸化の選択性を向上させることができ、 反応後の改 質ガス中の C ο濃度を低減させ、 水素の消費を防ぐことができるものと 考えられる。
更に、 本発明の C ο選択酸化触媒では、 極めて高純度のひアルミナを 担体に用いるこ とによ り、 高い C ο酸化活性を発現し得るため、 ひアル ミナに R u及び/又は P t などの触媒活性貴金属種以外の金属、 例えば ナ ト リ ウムや、 その金属酸化物が含有されると、 反応ガスの吸着形態が 変化して活性が大きく阻害されると考えられる。
なお、 本発明の C O選択酸化触媒では、 いわゆるハニカム形状の支持 体を用いるこ と も可能であるが、 かかるハ-カム状支持体に由来するマ グネシゥムなども触媒活性を低減する原因物質となるため、 これらの α アルミナへの混入量を一定値以下に制御することが望ま しい。
以下、 本発明の一酸化炭素選択酸化触媒について詳細に説明する。 な お、 本明細書において、 「％」 は特記しない限り質量百分率を示すもの とする。
上述の如く 、 本発明の一酸化炭素選択酸化触媒は、 改質ガス中の C O を酸素ガスによつて選択的に酸化する触媒である。
ここで、 改質ガスとは、 一般にメタンやプロパン等の炭化水素、 メ タ ノール等のアルコール又はナフサ等を水蒸気改質して得られるガスをい い、 代表的に、 メ タノール改質ガスは水素ガスを主成分と し、 二酸化炭 素 （C 0 2 ) 、 メ タン （C H 4 ) 、 水 （H 2 0 ) 及び C Oを含む。
なお、 本発明の適用対象と して効果的なものは、 これらのうちでもシ フ ト反応後の改質ガスであって、 C O濃度が 1 V o 1 %程度のものであ る。 次に、 酸素ガスは、 c oとの反応当量よ り も過剰に存在すれば特に限 定されるものではないが、 代表的には、 C Oとの反応当量の 1. 1〜 5 倍の酸素を存在させることが好ましい。
1. 1倍未満では、 酸化されない C Oが残留し、 5倍を超えると、 水 素の消費量が増大することがあり、 好ましく ない。
また、 本発明の選択酸化触媒は、 R u と P t を 0. 0 1〜 1 0 %の割 合で含有することが好ましい。 即ち、 R u と P tの混合物の担持量は、 得られる触媒全体の 0. 0 1〜 1 0 %とすることが好ましく、 望ましく は 0. 0 2〜 0. 50/0とすることがよい。
上記混合物の担持量が 0. 0 2 %未満では、 C Oの酸化活性が十分で ないことがあり、 0. 5 %を超えると、 R u、 P tが有効に利用されな いことがある。
更に、 本発明の選択酸化触媒では、 担持されている R u及び P tの少 なく とも一方の粒子径が 200 A以下、 望ましく は 5〜200Aである ことが好ま しい。
粒子径が 20 0 Aを超えると、 c oの酸化活性が十分でなく なること があり、 好ま しく ない。
また、 本発明の選択酸化触媒においては、 アルミナ担体を用いるが、 αアルミナを含有し、 R u、 P t、 R u— P t混合物を、 当該担体を構 成するアルミナ粒子表面から Ι Ο Ο μ πι以内、 好ま しく は 以内 に存在させることができるアルミナ担体であれば、 形状は限定されるも のではない。
R u等をアルミナ粒子表面から 1 0 0 μ m以内に担持できない場合は 触媒表面の R u濃度が薄くなり、 所期の効果が得られないことがある。 本発明の選択酸化触媒においては、 αアルミナを担体と して好適に使 用できるが、 この理由は、 αアルミナは微細な孔を持たないので上 iポの 局在化を容易に実現するからであり、 また、 上述のように水蒸気の影響 を低減できるからである。
なお、 ひアルミナを単独で用いてもよいが、 その他の結晶系のアルミ ナと併用することも可能である。
また、 ·γアルミナは、 1 0 0 0 °C以上の温度で保持すれば αアルミナ に転移するが、 その温度に保つと触媒金属,である R uや P tがシンタリ ングを起こし、 十分な活性が得られなくなるので、 本発明の触媒に単独 で用いるのには適していない。 但し、 触媒活性種である R u、 P tなど を担持する前に γ , θ , などのアルミナを熱処理しひアルミナに相転 換させた後担体して用いることや、 上述の特性を満足する様々な結晶系 の高純度なアルミナと アルミナを併用することは可能である。
なお、 本発明の選択酸化触媒においては、 上記アルミナ担体が αアル ミナを極めて高濃度で含有することが好ましく、 ナトリ ウム （N a ) や マグネシウム （M g ) などの不純物が一定量以上含まれると触媒活性を 阻害することがある。
例えば、 アルミナ担体中の N aの含有量については、 N a 2〇換算で 0 0 7 %未満に制御することを要する。
また、 本発明の選択酸化触媒は、 粒状やペレッ ト状とすることが可能 で、 更には、 ハニカム状の支持体を用いることが可能であり、 例えば、 コージェライ ト製ゃ金属製などのハニカム状の一体構造型支持体にコー ト して用いることも可能である。
但し、 上述した αアルミナの高濃度ないし高純度を担保して高活性を 発現させるベく、 コージェライ トに由来するマグネシウム （M g ) 上記 アルミナ担体中の含有量は、 それぞれ M g Oで 0. 0 4 %未満に制御さ れていることを要する。
本発明の選択酸化触媒は、 上述のような構成を有し、 優れた C O選択 酸化性を有するが、 代表的には、 改質ガス中に共存する 1 V ο 1 %程度 の C Oを l O O p p m程度に酸化除去する。
なお、 使用条件も特に限定されるものではないが、 空間速度 （ S V) を 3 0 , 0 0 0 h— 1以下、 触媒温度を 1 0 0〜 2 0 0でとすれば、 顕著 な効果が得られる。 図面の簡単な説明
図 1は、 C O選択酸化触媒の触媒性能の N a混入率依存性を示すダラ フ、 図 2は、 M gを含有する C O選択酸化触媒の触媒性能を示すグラフ である。 発明を実施するための最良の形態
以下、 本発明を実施例及び比較例により更に詳細に説明するが、 本発 明はこれら実施例に限定されるものではない。
[性能評価]
以下の実施例及び比較例において、 得られた触媒の性能は下記の手法 で評価した。
(評価条件等）
評価装置 ； 固定床流通型
S V ； 5 0 0 0 0 h ~ 1
C O濃度 ； 1 V o 1 %
O 2/ C O ； 2. 0、 1. 5又は 1. 0 (容量比）
水素濃度 ； 4 0 %
水蒸気濃度 ； 約 3 0 %
二酸化炭素濃度 ； 2 0 %
メタン濃度 ； 2 % 反応温度 ； 1 0 0〜 2 5 0°C
(触媒金属の担持粒子径）
触媒を粉砕して、 透過型電子顕微鏡により担持金属を直接観察して、 その粒径を確認した。
(触媒金属の担体表面局在化）
触媒をほぼ半分に割り、 その断面を E PMAにより観察して担持幅を 確認した。
また触媒の表面を X P Sにより観察し、 アルミナ表面の貴金属濃度を 確認した。
(実施例 1 )
平均粒径が 2 mm程度の高純度ひアルミナ （アルミナ濃度 9 9. 9 9 5 %) に R uを約 0. 2 %担持させて本例の選択酸化触媒 Aを得た。 こ の触媒において、 R uはひアルミナ粒子外表面から 5 0 mまでの深さ に存在していた。 また、 R uの粒子径は平均で 1 0 0 A程度であった。
この選択酸化触媒に、 1 V o 1 %の一酸化炭素を含む改質ガスに同じ く酸素を 1'. 5 V o 1 %分投入した試験ガス （OzZC O l . 5 ) を S V = 5 0 0 0 0 h— 1で通過させ、 触媒温度 （中心温度） 1 0 0 °C〜 2 5 0 °Cの範囲において C O濃度を測定した。 得られた結果を図 1に示す。 (実施例 2 )
上記高純度 αアルミナに N aを N a 20換算で 0. 0 1 4 %の割合で混 入した以外は、 実施例 1 と同様の操作を繰り返し、 本例の選択酸化触媒 を得た。 実施例 1 と同様に C O濃度を測定し、 得られた結果を図 1に示 す。
(比較例 1 )
上記高純度 αアルミナに N aを N a 20換算で 0. 0 7 %の割合で混入 した以外は、 実施例 1 と同様の操作を繰り返して本例の選択酸化触媒を 得た。 実施例 1 と同様に C O濃度を測定し、 得られた結果を図 1に示す。 図 1 より実施例 1、 2の選択酸化触媒は、 優れた C O選択酸化活性を 示すことがわかる。 特に実施例 1の選択酸化触媒においては、 低温から 高温域までの広い温度域において、 C Oを目標とする濃度まで低減する ことができた。 この一方、 比較例 1の選択酸化触媒は、 C O濃度は供給 時と変化無く 1 O O O O p p mで、 1 5 0 °C〜 2 0 0 °Cの範囲で C O濃 度は 3 0 0 0 p p mと活性は低かつた。
本選択酸化触媒に混入した N aは、 C O選択酸化反応に関与するガス の吸着、 脱離に影響を及ぼし、 結果と して C Oの除去能の低下を引き起 こすものと考えているが、 現時点では詳細は不明である。
(実施例 3 )
平均粒径が 2 mm程度の高純度 アルミナ （アルミナ濃度 9 9. 9 9 5 %) に M gを M g O換算で 0. 0 2 %混入し、 更に R uを約 0. 2 % 担持させて本例の選択酸化触媒を得た。 この選択酸化触媒に、 l v o l %の一酸化炭素を含む改質ガスに同じく酸素を 2. 0 V o 1 %, 1. 5 V o 1 %, 1 . O v o l %分投入した試験ガス （〇 2/C O = 2. 0， 1. 5 , 1. 0 ) をそれぞれ S V = 5 0 0 0 0 h一1で通過させ、 触媒温度
(中心温度） 1 0 0 °C〜 2 5 0 °Cの範囲において C O濃度を測定し、 得 られた結果を図 2に示す。
(比較例 2 )
平均粒径が 2 mm程度の高純度ひアルミナ （アルミナ濃度 9 9. 9 9 5 %) に M gを M g O換算で 0. 0 4 %混入し、 更に R uを約 0. 2 % 担持させて本例の選択酸化触媒を得た。
この選択酸化触媒を実施例 3 と同様に試験した。 得られた結果を図 2 に示す。
図 2より、 02/C Oにかかわらず、 比較例 2の選択酸化触媒の C O潠 択酸化能は実施例 3の選択酸化触媒にく らべ大きく低下し、 目標とする C O濃度に到達できる温度域が狭くなっていた。
以上、 本発明を好適実施例により詳細に説明したが、 本発明はこれら 実施例に限定されるものではなく、 本発明の開示の範囲内において種々 の変形実施が可能である。
例えば、 本発明の選択酸化触媒の用途は、 固体高分子型燃科電池に供 給される改質ガスに限定されるものではなく、 他の、 改質ガス中の c o の低減にも利用可能であり、 高純度水素ガスを必要とするアンモエアの 合成などの各種プロセスにも適用可能である。 産業上の利用可能性
以上説明してきたように、 本発明によれば、 ルテニウムや白金を、 特 定不純物含有量を適切に制御したアルミナ担体に担持すること と したた め、 改質ガス中の一酸化炭素を選択的に酸化して低減し、 良好な燃料利 用効率や発電効率を実現し得る一酸化炭素選択酸化触媒を提供すること ができる。
例えば、 本発明の触媒を用いることにより、 改質ガス中に 1 V o 1 % 程度存在する一酸化炭素を過剰量の酸素の存在下 1 5 0 °C程度で反応さ せれば、 一酸化炭素濃度を 0 . 1 V o 1 %以下に低減することができる

Claims

請求の範囲
1 . 改質ガス中の一酸化炭素を酸素ガスによって選択的に酸化する触媒 であって、
ルテニゥム及び 又は白金を、 アルミナを含有するアルミナ担体に 担持して成り、 且つこのアルミナ担体中に含まれるナト リ ゥムが N a 2 0 換算で 0 . 0 7 %未満であることを特徴とする一酸化炭素選択酸化触媒。
2 . 改質ガス中の一酸化炭素を酸素ガスによって選択的に酸化する触媒 であって、
ルテニウム及び/ /又は白金をひアルミナを含有するアルミナ担体に担 持し、 更に、 このアルミナ担体を、 マグネシウムを含有する支持体に支 持して成り、
上記ルテニウム及び/又は白金を担持したアルミナ担体中に含まれる マグネシウムが、 M g O換算で 0 . 0 4 %未満であることを特徴とする 一酸化炭素選択酸化触媒。
3 . 上記ルテニウム及び/又は白金を担持したアルミナ担体中にナト リ ゥムが含まれ、 そのナトリ ウム含有量が N a 2 0換算で 0 . 0 7 %未満で あることを特徴とする請求項 2に記載の一酸化炭素選択酸化触媒。
PCT/JP2002/006278 2002-06-24 2002-06-24 改質ガス中の一酸化炭素の選択酸化触媒 Ceased WO2004000458A1 (ja)