WO2003017266A1 - Support d'enregistrement optique - Google Patents
Support d'enregistrement optique Download PDFInfo
- Publication number
- WO2003017266A1 WO2003017266A1 PCT/JP2002/007763 JP0207763W WO03017266A1 WO 2003017266 A1 WO2003017266 A1 WO 2003017266A1 JP 0207763 W JP0207763 W JP 0207763W WO 03017266 A1 WO03017266 A1 WO 03017266A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- recording medium
- optical recording
- layer
- light transmitting
- amount
- Prior art date
Abstract
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2001244251A JP2003059097A (ja) | 2001-08-10 | 2001-08-10 | 光記録媒体 |
JP2001-244251 | 2001-08-10 | ||
JP2001-324013 | 2001-10-22 | ||
JP2001324013A JP2003132596A (ja) | 2001-10-22 | 2001-10-22 | 光記録媒体の設計方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2003017266A1 true WO2003017266A1 (fr) | 2003-02-27 |
Family
ID=26620401
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2002/007763 WO2003017266A1 (fr) | 2001-08-10 | 2002-07-30 | Support d'enregistrement optique |
Country Status (2)
Country | Link |
---|---|
TW (1) | TWI241579B (fr) |
WO (1) | WO2003017266A1 (fr) |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH01182944A (ja) * | 1988-01-14 | 1989-07-20 | Sanyo Electric Co Ltd | 光学式情報記録ディスクの製造方法 |
JPH0467332A (ja) * | 1990-06-30 | 1992-03-03 | Kyocera Corp | 光ディスクとその製造方法 |
JPH05242527A (ja) * | 1992-02-28 | 1993-09-21 | Teijin Ltd | 光ディスク及びその製造方法 |
WO1999000794A1 (fr) * | 1997-06-27 | 1999-01-07 | Sony Corporation | Support d'enregistrement optique et dispositif de disque optique |
JPH1116211A (ja) * | 1997-06-27 | 1999-01-22 | Hitachi Maxell Ltd | 情報記録媒体及びその製造方法 |
JP2000011449A (ja) * | 1998-06-19 | 2000-01-14 | Sony Corp | 情報記録媒体 |
JP2000067466A (ja) * | 1998-08-21 | 2000-03-03 | Teijin Ltd | 光記録媒体およびその製造方法 |
-
2002
- 2002-07-30 WO PCT/JP2002/007763 patent/WO2003017266A1/fr active Application Filing
- 2002-08-05 TW TW91117587A patent/TWI241579B/zh not_active IP Right Cessation
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH01182944A (ja) * | 1988-01-14 | 1989-07-20 | Sanyo Electric Co Ltd | 光学式情報記録ディスクの製造方法 |
JPH0467332A (ja) * | 1990-06-30 | 1992-03-03 | Kyocera Corp | 光ディスクとその製造方法 |
JPH05242527A (ja) * | 1992-02-28 | 1993-09-21 | Teijin Ltd | 光ディスク及びその製造方法 |
WO1999000794A1 (fr) * | 1997-06-27 | 1999-01-07 | Sony Corporation | Support d'enregistrement optique et dispositif de disque optique |
JPH1116211A (ja) * | 1997-06-27 | 1999-01-22 | Hitachi Maxell Ltd | 情報記録媒体及びその製造方法 |
JP2000011449A (ja) * | 1998-06-19 | 2000-01-14 | Sony Corp | 情報記録媒体 |
JP2000067466A (ja) * | 1998-08-21 | 2000-03-03 | Teijin Ltd | 光記録媒体およびその製造方法 |
Also Published As
Publication number | Publication date |
---|---|
TWI241579B (en) | 2005-10-11 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
KR20010075534A (ko) | 광디스크와 이 광디스크로부터 데이터를 재생하는 방법 및장치 | |
JP2002260280A (ja) | 光情報媒体およびその評価方法 | |
JPH1131337A (ja) | 光記録媒体及び光学ディスク装置 | |
EP1187120A2 (fr) | Medium d'enregistrement optique et procédé pour le tester | |
CN100377237C (zh) | 光信息记录介质 | |
EP1429320B1 (fr) | Disque optique et procede de fabrication associe | |
WO2003017266A1 (fr) | Support d'enregistrement optique | |
JP2003132596A (ja) | 光記録媒体の設計方法 | |
JP2003059097A (ja) | 光記録媒体 | |
JP2003123316A (ja) | 光情報媒体 | |
JP3537701B2 (ja) | 光学記録媒体、光学記録媒体の製造方法、および、光学記録媒体の製造装置 | |
JP2002092969A (ja) | 光ディスクの製造方法および光ディスク | |
WO2003025926A1 (fr) | Procede d'inspection de support d'enregistrement optique | |
US6887547B2 (en) | Optical information recording medium | |
KR20020038503A (ko) | 광정보 기록 매체 | |
JP2003091883A (ja) | 光記録媒体の検査方法 | |
JP4642312B2 (ja) | 情報記録媒体並びに該情報記録媒体を用いた情報処理装置 | |
JP3741375B2 (ja) | 光情報記録媒体 | |
JP2001143319A (ja) | 光ディスク媒体 | |
JPH076408A (ja) | 情報記録媒体 | |
JP2003303444A (ja) | 光ディスクおよびその製造方法 | |
JPH04349241A (ja) | 追記形光記録媒体 | |
JP2009026374A (ja) | 光情報媒体 | |
JPH10269626A (ja) | 相変化型光ディスク | |
JP2003248971A (ja) | 光ディスク及び光磁気ディスク |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TN TR TT TZ UA UG US UZ VN YU ZA ZM ZW Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BY BZ CA CH CN CO CR CU CZ DE DM DZ EC EE ES FI GB GD GE GH HR HU ID IL IN IS KE KG KP KR KZ LK LR LS LT LU LV MA MD MG MK MW MX MZ NO NZ OM PH PL PT RO SD SE SG SI SK SL TJ TM TN TR TT UA UG US UZ VN YU ZA ZM |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR IE IT LU MC NL PT SE SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG Kind code of ref document: A1 Designated state(s): GH GM KE LS MW MZ SD SL SZ UG ZM ZW AM AZ BY KG KZ RU TJ TM AT BE BG CH CY CZ DK EE ES FI FR GB GR IE IT LU MC PT SE SK TR BF BJ CF CG CI GA GN GQ GW ML MR NE SN TD TG |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
122 | Ep: pct application non-entry in european phase |