WO2001035511A2 - Materiaux de stockage d'energie thermique - Google Patents

Materiaux de stockage d'energie thermique Download PDF

Info

Publication number
WO2001035511A2
WO2001035511A2 PCT/US2000/030220 US0030220W WO0135511A2 WO 2001035511 A2 WO2001035511 A2 WO 2001035511A2 US 0030220 W US0030220 W US 0030220W WO 0135511 A2 WO0135511 A2 WO 0135511A2
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
phase change
set forth
change material
unit
Prior art date
Application number
PCT/US2000/030220
Other languages
English (en)
Other versions
WO2001035511A3 (fr
Inventor
Shmuel Sternberg
Original Assignee
Baxter International Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baxter International Inc. filed Critical Baxter International Inc.
Priority to EP00976832A priority Critical patent/EP1226397A2/fr
Priority to JP2001537147A priority patent/JP2003514075A/ja
Priority to AU14551/01A priority patent/AU1455101A/en
Publication of WO2001035511A2 publication Critical patent/WO2001035511A2/fr
Publication of WO2001035511A3 publication Critical patent/WO2001035511A3/fr

Abstract

L'invention concerne une structure polymère, les pores de laquelle renfermant un matériau à changement de phase. Cette structure est préparée selon un procédé impliquant la décomposition spinodale. Des unités de stockage d'énergie thermique renferment la structure polymère et un support de cette dernière.
PCT/US2000/030220 1999-11-05 2000-11-02 Materiaux de stockage d'energie thermique WO2001035511A2 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
EP00976832A EP1226397A2 (fr) 1999-11-05 2000-11-02 Materiaux de stockage d'energie thermique
JP2001537147A JP2003514075A (ja) 1999-11-05 2000-11-02 熱エネルギー蓄積材料
AU14551/01A AU1455101A (en) 1999-11-05 2000-11-02 Thermal energy storage materials

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US16372699P 1999-11-05 1999-11-05
US60/163,726 1999-11-05

Publications (2)

Publication Number Publication Date
WO2001035511A2 true WO2001035511A2 (fr) 2001-05-17
WO2001035511A3 WO2001035511A3 (fr) 2001-09-27

Family

ID=22591308

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2000/030220 WO2001035511A2 (fr) 1999-11-05 2000-11-02 Materiaux de stockage d'energie thermique

Country Status (4)

Country Link
EP (1) EP1226397A2 (fr)
JP (1) JP2003514075A (fr)
AU (1) AU1455101A (fr)
WO (1) WO2001035511A2 (fr)

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011098225A1 (fr) * 2010-02-09 2011-08-18 Thüringisches Institut für Textil- und Kunststoff-Forschung e.V. Corps moulés à accumulation de chaleur
US8673448B2 (en) 2011-03-04 2014-03-18 Outlast Technologies Llc Articles containing precisely branched functional polymeric phase change materials
DE102012110330A1 (de) * 2012-10-29 2014-04-30 STS Textiles GmbH & Co. KG Textiles Flächengebilde mit einem Latentwärmespeicher
WO2014070154A1 (fr) * 2012-10-31 2014-05-08 Empire Technology Development Llc Matériaux polymères de stockage d'énergie
US9234059B2 (en) 2008-07-16 2016-01-12 Outlast Technologies, LLC Articles containing functional polymeric phase change materials and methods of manufacturing the same
US9371400B2 (en) 2010-04-16 2016-06-21 Outlast Technologies, LLC Thermal regulating building materials and other construction components containing phase change materials
US9434869B2 (en) 2001-09-21 2016-09-06 Outlast Technologies, LLC Cellulosic fibers having enhanced reversible thermal properties and methods of forming thereof
WO2017004425A1 (fr) * 2015-06-30 2017-01-05 Henderson Engineers, Inc. Système de régulation de température ambiante dans un stade
US9797087B2 (en) 2006-01-26 2017-10-24 Outlast Technologies, LLC Coated articles with microcapsules and other containment structures incorporating functional polymeric phase change materials
US10003053B2 (en) 2015-02-04 2018-06-19 Global Web Horizons, Llc Systems, structures and materials for electrochemical device thermal management
US10431858B2 (en) 2015-02-04 2019-10-01 Global Web Horizons, Llc Systems, structures and materials for electrochemical device thermal management
USD911961S1 (en) 2017-04-03 2021-03-02 Latent Heat Solutions, Llc Battery container
CN112646381A (zh) * 2021-01-22 2021-04-13 西北师范大学 一种高分子防蒸发控温材料的制备及应用
CN113173739A (zh) * 2020-05-09 2021-07-27 中国科学院青海盐湖研究所 一种相变混凝土及其制备方法
CN113173740A (zh) * 2020-05-09 2021-07-27 中国科学院青海盐湖研究所 一种相变保温砂浆及其制备方法
US11970652B1 (en) 2023-02-16 2024-04-30 Microera Power Inc. Thermal energy storage with actively tunable phase change materials

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4734693B2 (ja) * 2000-06-08 2011-07-27 三菱瓦斯化学株式会社 蓄熱体
JP2008144054A (ja) * 2006-12-11 2008-06-26 Enex Co Ltd 粒子状蓄熱材及びその製造方法
JP5995755B2 (ja) * 2012-03-16 2016-09-21 国立大学法人 東京大学 蓄熱材及びそれを利用した熱利用システム

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4408659A (en) * 1980-10-14 1983-10-11 L. & C. Steinmuller Gmbh Heat storage mass for regenerative heat exchange

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS60134191A (ja) * 1983-12-23 1985-07-17 Matsushita Electric Works Ltd 熱交換装置

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4408659A (en) * 1980-10-14 1983-10-11 L. & C. Steinmuller Gmbh Heat storage mass for regenerative heat exchange

Cited By (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9434869B2 (en) 2001-09-21 2016-09-06 Outlast Technologies, LLC Cellulosic fibers having enhanced reversible thermal properties and methods of forming thereof
US10208403B2 (en) 2001-09-21 2019-02-19 Outlast Technologies, LLC Cellulosic fibers having enhanced reversible thermal properties and methods of forming thereof
US9920455B2 (en) 2001-09-21 2018-03-20 Outlast Technologies, LLC Cellulosic fibers having enhanced reversible thermal properties and methods of forming thereof
US9797087B2 (en) 2006-01-26 2017-10-24 Outlast Technologies, LLC Coated articles with microcapsules and other containment structures incorporating functional polymeric phase change materials
US9234059B2 (en) 2008-07-16 2016-01-12 Outlast Technologies, LLC Articles containing functional polymeric phase change materials and methods of manufacturing the same
US10377936B2 (en) 2008-07-16 2019-08-13 Outlast Technologies, LLC Thermal regulating building materials and other construction components containing phase change materials
AU2011214680B2 (en) * 2010-02-09 2012-12-06 Thueringisches Institut Fuer Textil- Und Kunststoff-Forschung E.V. Heat-storing moldings
US8828530B2 (en) 2010-02-09 2014-09-09 Thueringisches Institut Fuer Textil-Und Kunststoff-Forschung E.V. Heat-storing moldings
WO2011098225A1 (fr) * 2010-02-09 2011-08-18 Thüringisches Institut für Textil- und Kunststoff-Forschung e.V. Corps moulés à accumulation de chaleur
US9371400B2 (en) 2010-04-16 2016-06-21 Outlast Technologies, LLC Thermal regulating building materials and other construction components containing phase change materials
US8673448B2 (en) 2011-03-04 2014-03-18 Outlast Technologies Llc Articles containing precisely branched functional polymeric phase change materials
US9938365B2 (en) 2011-03-04 2018-04-10 Outlast Technologies, LLC Articles containing precisely branched functional polymeric phase change materials
DE102012110330A1 (de) * 2012-10-29 2014-04-30 STS Textiles GmbH & Co. KG Textiles Flächengebilde mit einem Latentwärmespeicher
DE102012110330B4 (de) * 2012-10-29 2014-07-24 STS Textiles GmbH & Co. KG Textiles Flächengebilde mit einem Latentwärmespeicher
US9663605B2 (en) 2012-10-31 2017-05-30 Empire Technology Development Llc Polymeric energy storage materials
WO2014070154A1 (fr) * 2012-10-31 2014-05-08 Empire Technology Development Llc Matériaux polymères de stockage d'énergie
US11411262B2 (en) 2015-02-04 2022-08-09 Latent Heat Solutions, Llc Systems, structures and materials for electrochemical device thermal management
US10431858B2 (en) 2015-02-04 2019-10-01 Global Web Horizons, Llc Systems, structures and materials for electrochemical device thermal management
US10003053B2 (en) 2015-02-04 2018-06-19 Global Web Horizons, Llc Systems, structures and materials for electrochemical device thermal management
WO2017004425A1 (fr) * 2015-06-30 2017-01-05 Henderson Engineers, Inc. Système de régulation de température ambiante dans un stade
US9835343B2 (en) 2015-06-30 2017-12-05 Henderson Engineers, Inc. Stadium ambient temperature control system
USD911961S1 (en) 2017-04-03 2021-03-02 Latent Heat Solutions, Llc Battery container
CN113173739A (zh) * 2020-05-09 2021-07-27 中国科学院青海盐湖研究所 一种相变混凝土及其制备方法
CN113173740A (zh) * 2020-05-09 2021-07-27 中国科学院青海盐湖研究所 一种相变保温砂浆及其制备方法
CN113173739B (zh) * 2020-05-09 2022-12-06 中国科学院青海盐湖研究所 一种相变混凝土及其制备方法
CN113173740B (zh) * 2020-05-09 2022-12-13 中国科学院青海盐湖研究所 一种相变保温砂浆及其制备方法
CN112646381A (zh) * 2021-01-22 2021-04-13 西北师范大学 一种高分子防蒸发控温材料的制备及应用
US11970652B1 (en) 2023-02-16 2024-04-30 Microera Power Inc. Thermal energy storage with actively tunable phase change materials

Also Published As

Publication number Publication date
EP1226397A2 (fr) 2002-07-31
JP2003514075A (ja) 2003-04-15
AU1455101A (en) 2001-06-06
WO2001035511A3 (fr) 2001-09-27

Similar Documents

Publication Publication Date Title
WO2001035511A2 (fr) Materiaux de stockage d'energie thermique
AU651035B2 (en) Wraps comprising phase change materials
US5254380A (en) Dry powder mixes comprising phase change materials
EP1472078B1 (fr) Barrieres thermiques a proprietes thermiques reversibles ameliorees
US5885475A (en) Phase change materials incorporated throughout the structure of polymer fibers
CA1320623C (fr) Polyefines comportant un materiau a changement de phase
US4747240A (en) Encapsulated PCM aggregate
US6652771B2 (en) Phase change material blend, method for making, and devices using same
TWI439499B (zh) 具有提高之可逆的熱性質之聚合複合物及其形成方法
US6615906B1 (en) Latent heat body
US20030124278A1 (en) Thermal barriers with solid/solid phase change materials
US20140113112A1 (en) Microcapillary films containing phase change materials
AU730134B2 (en) Latent heat body
Cao et al. Properties evaluation and applications of thermal energystorage materials in buildings
CN107075794B (zh) 柔性pcm面料
Zhang Heat-storage and thermo-regulated textiles and clothing
US6602592B2 (en) Moisture-retentive cooling gel, moisture-retentive cooling gel laminate, and moisture-retentive cooling plaster
WO2004007631A1 (fr) Dispositif de stockage thermique, composition correspondante et applications correspondantes
Arjun et al. Thermal energy storage materials (PCMs) for textile applications
WO2007058003A1 (fr) Microcapsule en materiau de stockage thermique, dispersion de microcapsule en materiau de stockage thermique et produit solidifie a base de microcapsule en materiau de stockage thermique
CN100580015C (zh) 一种智能透湿聚合物复合薄膜的制备和应用
KR101376343B1 (ko) 단열을 위해 에어로겔이 코팅된 복층 직물지
US20180156546A1 (en) Thermal Energy storage system with enhanced transition array
CN111469505B (zh) 一种导湿快干的吸湿发热纤维海绵材料及其制备方法
JP2008023274A (ja) 冷却袋、冷却材、身体冷却装着体及びその使用方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AU CA JP

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
AK Designated states

Kind code of ref document: A3

Designated state(s): AU CA JP

AL Designated countries for regional patents

Kind code of ref document: A3

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR

WWE Wipo information: entry into national phase

Ref document number: 2000976832

Country of ref document: EP

ENP Entry into the national phase

Ref country code: JP

Ref document number: 2001 537147

Kind code of ref document: A

Format of ref document f/p: F

WWP Wipo information: published in national office

Ref document number: 2000976832

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 2000976832

Country of ref document: EP